WO2021215172A1 - Composition de matériau de revêtement - Google Patents

Composition de matériau de revêtement Download PDF

Info

Publication number
WO2021215172A1
WO2021215172A1 PCT/JP2021/011757 JP2021011757W WO2021215172A1 WO 2021215172 A1 WO2021215172 A1 WO 2021215172A1 JP 2021011757 W JP2021011757 W JP 2021011757W WO 2021215172 A1 WO2021215172 A1 WO 2021215172A1
Authority
WO
WIPO (PCT)
Prior art keywords
coating composition
coating
fine particles
inorganic fine
coating film
Prior art date
Application number
PCT/JP2021/011757
Other languages
English (en)
Japanese (ja)
Inventor
勝彦 杉本
智之 石河
琢也 白石
みずほ 富樫
Original Assignee
日本ペイント・オートモーティブコーティングス株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 日本ペイント・オートモーティブコーティングス株式会社 filed Critical 日本ペイント・オートモーティブコーティングス株式会社
Publication of WO2021215172A1 publication Critical patent/WO2021215172A1/fr

Abstract

Le but de la présente invention concerne une composition de matériau de revêtement contenant des particules fines inorganiques et présentant une adhérence élevée lors d'un nouveau revêtement. La présente invention porte sur une composition de matériau de revêtement contenant une résine contenant un groupe hydroxyle, un agent de durcissement et des particules fines inorganiques, l'énergie surfacique libre d'un film qui est revêtu de la composition de matériau de revêtement et durci étant supérieure à l'énergie surfacique libre d'un film qui est revêtu de la composition de matériau de revêtement à l'exclusion uniquement des particules fines inorganiques et durci.
PCT/JP2021/011757 2020-04-20 2021-03-22 Composition de matériau de revêtement WO2021215172A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2020-074829 2020-04-20
JP2020074829A JP2021172688A (ja) 2020-04-20 2020-04-20 塗料組成物

Publications (1)

Publication Number Publication Date
WO2021215172A1 true WO2021215172A1 (fr) 2021-10-28

Family

ID=78269248

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2021/011757 WO2021215172A1 (fr) 2020-04-20 2021-03-22 Composition de matériau de revêtement

Country Status (2)

Country Link
JP (1) JP2021172688A (fr)
WO (1) WO2021215172A1 (fr)

Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20030190434A1 (en) * 2002-04-05 2003-10-09 Byers Alicia D. Process for applying automotive quality effect coatings to metal substrates
US20090221748A1 (en) * 2008-02-29 2009-09-03 Ppg Industries Ohio, Inc. Coating compositions comprising a polymer containing an oligomeric macromonomer
WO2016089199A1 (fr) * 2014-12-02 2016-06-09 Becker Industrial Coatings (M) Sdn. Bhd. Compositions de stratification rapide
WO2017111112A1 (fr) * 2015-12-25 2017-06-29 関西ペイント株式会社 Procédé de formation de film de revêtement multicouche
CN110499084A (zh) * 2019-09-30 2019-11-26 立邦工业涂料(上海)有限公司 一种水性丙烯酸氨基烤漆及其制备方法
US20200325289A1 (en) * 2019-04-15 2020-10-15 Ppg Industries Ohio, Inc. Curable film-forming compositions containing rheology modifiers comprising non-aqueous dispersions

Patent Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20030190434A1 (en) * 2002-04-05 2003-10-09 Byers Alicia D. Process for applying automotive quality effect coatings to metal substrates
US20090221748A1 (en) * 2008-02-29 2009-09-03 Ppg Industries Ohio, Inc. Coating compositions comprising a polymer containing an oligomeric macromonomer
WO2016089199A1 (fr) * 2014-12-02 2016-06-09 Becker Industrial Coatings (M) Sdn. Bhd. Compositions de stratification rapide
WO2017111112A1 (fr) * 2015-12-25 2017-06-29 関西ペイント株式会社 Procédé de formation de film de revêtement multicouche
US20200325289A1 (en) * 2019-04-15 2020-10-15 Ppg Industries Ohio, Inc. Curable film-forming compositions containing rheology modifiers comprising non-aqueous dispersions
CN110499084A (zh) * 2019-09-30 2019-11-26 立邦工业涂料(上海)有限公司 一种水性丙烯酸氨基烤漆及其制备方法

Also Published As

Publication number Publication date
JP2021172688A (ja) 2021-11-01

Similar Documents

Publication Publication Date Title
JP6587404B2 (ja) 複層塗膜の形成方法
JP3931348B2 (ja) 熱硬化性組成物、塗装仕上げ方法および塗装物品
JP5547398B2 (ja) 塗料組成物
JP2017165955A (ja) 高固形分塗料組成物
JP2009173731A (ja) プライマー及びそれを用いた塗装方法
JP5615704B2 (ja) 塗料組成物及びこれを用いた塗膜形成方法
KR101294443B1 (ko) 코팅 조성물
JPH05309324A (ja) 優れた引っ掻抵抗性および耐衝撃性を有する塗装した鋼板
JP2005042001A (ja) 塗料組成物、塗膜形成方法および塗装物品
JP2005139336A (ja) ２液型塗料組成物、塗装仕上げ方法及び塗装物品
US20070196661A1 (en) Methods for reducing the time to produce a mar and/or scratch resistant coating on a substrate
JP2006008936A (ja) 自動車用クリヤー塗料組成物及びそれを用いた複層塗膜の形成方法
KR101435969B1 (ko) 자동차 보수용 논샌딩 프라이머-서페이서 도료 조성물 및 이를 사용한 자동차 보수 방법
WO2021215172A1 (fr) Composition de matériau de revêtement
JP5362308B2 (ja) 複層塗膜形成方法
JP3801347B2 (ja) 塗装仕上げ方法及び塗装物品
KR101540078B1 (ko) 크롬 도금 표면에 도포되는 이중 경화형 도료 조성물 및 이를 이용한 도장 방법
KR102583106B1 (ko) 클리어 코트 조성물
KR20170085866A (ko) 상도용 유성 무광 1액형 도료 조성물
JPH09131567A (ja) アルミホイ−ルの塗装方法
JP7545561B2 (ja) 塗料組成物及び塗装物品
JP7254012B2 (ja) 自動車用外装部品及び自動車用外装部品の製造方法
JPH11199826A (ja) 加熱硬化性塗料組成物及び上塗り塗膜形成方法
JP2010285549A (ja) 塗料組成物、塗装仕上げ方法および塗装物品
KR101163463B1 (ko) 진공증착용 수용성 클리어 도료

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 21792595

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 21792595

Country of ref document: EP

Kind code of ref document: A1