WO2021085929A1 - 올레핀계 중합체 - Google Patents

올레핀계 중합체 Download PDF

Info

Publication number
WO2021085929A1
WO2021085929A1 PCT/KR2020/014445 KR2020014445W WO2021085929A1 WO 2021085929 A1 WO2021085929 A1 WO 2021085929A1 KR 2020014445 W KR2020014445 W KR 2020014445W WO 2021085929 A1 WO2021085929 A1 WO 2021085929A1
Authority
WO
WIPO (PCT)
Prior art keywords
substituted
unsubstituted
olefin
formula
based polymer
Prior art date
Application number
PCT/KR2020/014445
Other languages
English (en)
French (fr)
Inventor
이문희
김성동
박성연
정욱
정의갑
Original Assignee
한화솔루션 주식회사
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 한화솔루션 주식회사 filed Critical 한화솔루션 주식회사
Publication of WO2021085929A1 publication Critical patent/WO2021085929A1/ko

Abstract

본 발명은 본 발명은 올레핀계 중합체 및 그로부터 제조되는 필름에 관한 것이다. 본 발명의 구체예에 따른 올레핀계 중합체, 구체적으로 선형 저밀도 폴리에틸렌은 분자량 분포가 비교적 넓고 공단량체가 역(reverse)의 분포를 나타내어 가공성과 기계적 강도가 우수하다.

Description

올레핀계 중합체
본 발명은 올레핀계 중합체 및 그로부터 제조되는 필름에 관한 것이다. 구체적으로, 본 발명은 공단량체가 역(reverse)의 분포를 나타내어 기계적 강도가 우수한 올레핀계 중합체, 특히 선형 저밀도 폴리에틸렌 및 그로부터 제조되는 필름에 관한 것이다.
올레핀을 중합하는 데 이용되는 촉매의 하나인 메탈로센 촉매는 전이금속 또는 전이금속 할로겐 화합물에 사이클로펜타디에닐(cycolpentadienyl), 인데닐(indenyl), 사이클로헵타디에닐(cycloheptadienyl) 등의 리간드가 배위 결합된 화합물로서 샌드위치 구조를 기본적인 형태로 갖는다.
올레핀을 중합하는 데 사용되는 다른 촉매인 지글러-나타(Ziegler-Natta) 촉매가 활성점인 금속 성분이 불활성인 고체 표면에 분산되어 활성점의 성질이 균일하지 않은데 반해, 메탈로센 촉매는 일정한 구조를 갖는 하나의 화합물이기 때문에 모든 활성점이 동일한 중합 특성을 갖는 단일 활성점 촉매(single-site catalyst)로 알려져 있다. 이러한 메탈로센 촉매로 중합된 고분자는 분자량 분포가 좁고 공단량체의 분포가 균일하며, 지글러-나타 촉매에 비해 공중합 활성도가 높다.
한편, 선형 저밀도 폴리에틸렌(linear low-density polyethylene; LLDPE)은 중합 촉매를 사용하여 저압에서 에틸렌과 알파-올레핀을 공중합하여 제조되며, 분자량 분포가 좁고 일정한 길이의 단쇄 분지(short chain branch; SCB)를 가지며, 일반적으로 장쇄 분지(long chain branch; LCB)를 갖지 않는다. 선형 저밀도 폴리에틸렌으로 제조된 필름은 일반 폴리에틸렌의 특성과 더불어 파단강도와 신율이 높고, 인열강도, 충격강도 등이 우수하여 기존의 저밀도 폴리에틸렌(low-density polyethylene)이나 고밀도 폴리에틸렌(high-density polyethylene)의 적용이 어려운 스트레치 필름, 오버랩 필름 등에 널리 사용되고 있다.
메탈로센 촉매에 의해 제조되는 선형 저밀도 폴리에틸렌은 가공성과 필름의 헤이즈가 우수한 경우, 필름의 강도가 저하되는 경향이 있다. 반대로, 필름의 강도가 우수한 경우, 가공성과 헤이즈가 저하되는 경향이 있다.
따라서, 가공성과 기계적 강도가 우수한 필름을 제공할 수 있는 올레핀계 중합체, 특히 선형 저밀도 폴리올레핀이 요구되고 있다.
본 발명의 목적은 가공성과 기계적 강도가 우수한 올레핀계 중합체, 특히 선형 저밀도 폴리에틸렌을 제공하는 것이다.
본 발명의 다른 목적은 올레핀계 중합체, 특히 선형 저밀도 폴리에틸렌을 성형하여 제조되며, 기계적 강도가 우수한 필름을 제공하는 것이다.
이러한 목적을 달성하기 위한 본 발명의 일 구체예에 따라서, 아래 수학식 1로 정의되는 공단량체 분포 기울기(comonomer distribution slope; CDS)가 1 이상, 바람직하게는 2~5인 올레핀계 중합체가 제공된다.
[수학식 1]
Figure PCTKR2020014445-appb-img-000001
여기서, C 20과 C 80은 공단량체 분포에서 누적 질량 분율(cumulative weight fraction)이 각각 20%와 80%인 지점에서의 공단량체 함량이고, M 20과 M 80은 공단량체 분포에서 누적 질량 분율이 각각 20%와 80%인 지점에서의 분자량이다.
바람직하게는, 올레핀계 중합체의 (1) 다분산지수(Mw/Mn)에 의한 분자량 분포가 2~20; (2) 밀도가 0.88~0.96 g/㎤; (3) 190℃에서 2.16 kg 하중으로 측정 시 용융지수(melt index; I 2. 16)가 0.01~3.0 g/10분; 및 (4) 190℃에서 21.6 kg의 하중으로 측정되는 용융지수(I 21.6)와 I 2.16의 비(melt flow ratio; MFR)가 25 이상, 바람직하게는 30~100이다.
바람직하게는, 올레핀계 중합체의 중량평균 분자량(Mw)이 100,000~500,000 g/mole이다.
올레핀계 중합체가 올레핀계 단량체와 올레핀계 공단랑체의 공중합체이다. 구체적으로, 올레핀계 단량체가 에틸렌이며, 올레핀계 공단량체가 프로필렌, 1-부텐, 1-펜텐, 4-메틸-1-펜텐, 1-헥센, 1-헵텐, 1-옥텐, 1-데센, 1-운데센, 1-도데센, 1-테트라데센 및 1-헥사데센으로 구성되는 군으로부터 선택되는 하나 이상이다.
바람직하게는, 올레핀계 중합체가 올레핀계 단량체가 에틸렌이고 올레핀계 공단량체가 1-헥센인 선형 저밀도 폴리에틸렌이다.
본 발명의 구체예에 따른 올레핀계 중합체는 아래 화학식 1로 표시되는 적어도 1종의 전이금속 화합물과 적어도 1종의 조촉매 화합물을 포함하는 촉매의 존재하에 제조된다.
[화학식 1]
Figure PCTKR2020014445-appb-img-000002
위 화학식 1에서, n은 각각 독립적으로 1~20의 정수이고,
M은 티타늄(Ti), 지르코늄(Zr) 또는 하프늄(Hf)이며,
X는 각각 독립적으로 할로겐, C 1-20 알킬, C 2-20 알케닐, C 2-20 알키닐, C 6-20 아릴, C 1-20 알킬 C 6-20 아릴, C 6-20 아릴 C 1-20 알킬, C 1-20 알킬아미도, C 6-20 아릴아미도 또는 C 1-20 알킬리덴이고,
R 1 내지 R 4와 R 5 내지 R 8은 각각 독립적으로 수소, 치환 또는 비치환된 C 1-20 알킬, 치환 또는 비치환된 C 2-20 알케닐, 치환 또는 비치환된 C 6-20 아릴, 치환 또는 비치환된 C 1-20 알킬 C 6-20 아릴, 치환 또는 비치환된 C 6-20 아릴 C 1-20 알킬, 치환 또는 비치환된 C 1-20 헤테로알킬, 치환 또는 비치환된 C 3-20 헤테로아릴, 치환 또는 비치환된 C 1-20 알킬아미도, 치환 또는 비치환된 C 6-20 아릴아미도, 치환 또는 비치환된 C 1-20 알킬리덴, 또는 치환 또는 비치환된 C 1-20 실릴이고,
R 9 내지 R 11과 R 12 내지 R 14는 각각 독립적으로 치환 또는 비치환된 C 1-20 알킬, 치환 또는 비치환된 C 2-20 알케닐, 치환 또는 비치환된 C 6-20 아릴, 치환 또는 비치환된 C 1-20 알킬 C 6-20 아릴, 치환 또는 비치환된 C 6-20 아릴 C 1-20 알킬, 치환 또는 비치환된 C 1-20 헤테로알킬, 치환 또는 비치환된 C 3-20 헤테로아릴, 치환 또는 비치환된 C 1-20 알킬아미도, 치환 또는 비치환된 C 6-20 아릴아미도, 치환 또는 비치환된 C 1-20 알킬리덴, 또는 치환 또는 비치환된 C 1-20 실릴이고,
R 1 내지 R 4와 R 5 내지 R 8은 각각 독립적으로 인접한 기가 연결되어 치환 또는 비치환된 포화 또는 불포화 C 4-20 고리를 형성할 수 있다.
이때, 조촉매 화합물은 아래 화학식 2로 표현되는 화합물, 화학식 3으로 표현되는 화합물 및 화학식 4로 표현되는 화합물로 구성되는 군으로부터 선택될 수 있다.
[화학식 2]
Figure PCTKR2020014445-appb-img-000003
[화학식 3]
Figure PCTKR2020014445-appb-img-000004
[화학식 4]
[L-H] +[Z(A) 4] - 또는 [L] +[Z(A) 4] -
위 화학식 2에서, n은 2 이상의 정수이고, R a는 할로겐 원자, C 1-20 탄화수소기 또는 할로겐으로 치환된 C 1-20 탄화수소기이고,
위 화학식 3에서, D는 알루미늄(Al) 또는 보론(B)이고, R b, R c 및 R d는 각각 독립적으로 할로겐 원자, C 1-20 탄화수소기, 할로겐으로 치환된 C 1-20 탄화수소기 또는 C 1-20 알콕시기이며,
위 화학식 4에서, L은 중성 또는 양이온성 루이스 염기이고, [L-H] + 및 [L] +는 브뢴스테드 산이며, Z는 13족 원소이고, A는 각각 독립적으로 치환 또는 비치환된 C 6-20 아릴기이거나 치환 또는 비치환된 C 1-20 알킬기이다.
또한, 촉매가 전이금속 화합물과 조촉매 화합물을 담지하는 담체를 더 포함할 수 있다.
본 발명의 다른 구체예에 따라서, 올레핀계 중합체를 성형하여 제조되는 필름이 제공된다.
구체적으로, 필름은 스트레치 필름, 오버랩 필름, 라미, 사일리지 랩 및 농업용 필름으로 구성되는 군으로부터 선택되는 하나일 수 있다.
본 발명의 구체예에 따른 올레핀계 중합체, 특히 선형 저밀도 폴리에틸렌은 분자량 분포가 비교적 넓고 공단량체가 역(reverse)의 분포를 나타내어 가공성과 기계적 강도가 우수하다.
도 1은 수학식 1로 정의되는 CDS를 측정 방법을 설명하기 위한 GPC-FTIR 그래프이다.
도 2와 3은 각각 실시예 1-1과 실시예 2의 올레핀계 중합체의 CDS 측정을 위한 GPC-FTIR 그래프이다.
도 4와 5는 각각 비교예 1과 비교예 2의 올레핀계 중합체의 CDS 측정을 위한 GPC-FTIR 그래프이다.
올레핀 중합용 촉매
본 발명의 일 구체예에 따른 올레핀계 중합체, 특히 선형 저밀도 폴리에틸렌을 제조하기 위한 촉매는 아래 화학식 1로 표시되는 적어도 1종의 전이금속 화합물과 적어도 1종의 조촉매 화합물을 포함한다.
[화학식 1]
Figure PCTKR2020014445-appb-img-000005
위 화학식 1에서, n은 각각 독립적으로 1~20의 정수, 바람직하게는 1~10의 정수, 더 바람직하게는 1~5의 정수이다. 구체적으로, n은 각각 1 또는 2일 수 있다.
M은 티타늄(Ti), 지르코늄(Zr) 또는 하프늄(Hf)이다. 구체적으로, M은 지르코늄 또는 하프늄일 수 있다.
X는 각각 독립적으로 할로겐, C 1-20 알킬, C 2-20 알케닐, C 2-20 알키닐, C 6-20 아릴, C 1-20 알킬 C 6-20 아릴, C 6-20 아릴 C 1-20 알킬, C 1-20 알킬아미도, C 6-20 아릴아미도 또는 C 1-20 알킬리덴이다. 구체적으로, X는 각각 할로겐 또는 치환 또는 비치환된 C 1-20 알킬일 수 있다. 더 구체적으로, X는 각각 염소 또는 부틸기일 수 있다.
R 1 내지 R 4와 R 5 내지 R 8은 각각 독립적으로 수소, 치환 또는 비치환된 C 1-20 알킬, 치환 또는 비치환된 C 2-20 알케닐, 치환 또는 비치환된 C 6-20 아릴, 치환 또는 비치환된 C 1-20 알킬 C 6-20 아릴, 치환 또는 비치환된 C 6-20 아릴 C 1-20 알킬, 치환 또는 비치환된 C 1-20 헤테로알킬, 치환 또는 비치환된 C 3-20 헤테로아릴, 치환 또는 비치환된 C 1-20 알킬아미도, 치환 또는 비치환된 C 6-20 아릴아미도, 치환 또는 비치환된 C 1-20 알킬리덴, 또는 치환 또는 비치환된 C 1-20 실릴이다. 구체적으로, R 1 내지 R 4와 R 5 내지 R 8은 각각 수소일 수 있다. 또한, R 1 내지 R 4와 R 5 내지 R 8은 각각 독립적으로 인접한 기가 연결되어 치환 또는 비치환된 포화 또는 불포화 C 4-20 고리를 형성할 수 있다.
R 9 내지 R 11과 R 12 내지 R 14는 각각 독립적으로 치환 또는 비치환된 C 1-20 알킬, 치환 또는 비치환된 C 2-20 알케닐, 치환 또는 비치환된 C 6-20 아릴, 치환 또는 비치환된 C 1-20 알킬 C 6-20 아릴, 치환 또는 비치환된 C 6-20 아릴 C 1-20 알킬, 치환 또는 비치환된 C 1-20 헤테로알킬, 치환 또는 비치환된 C 3-20 헤테로아릴, 치환 또는 비치환된 C 1-20 알킬아미도, 치환 또는 비치환된 C 6-20 아릴아미도, 치환 또는 비치환된 C 1-20 알킬리덴, 또는 치환 또는 비치환된 C 1-20 실릴이다.
구체적으로, R 9 내지 R 11과 R 12 내지 R 14는 각각 치환 또는 비치환된 C 1-20 알킬 또는 치환 또는 비치환된 C 6-20 아릴일 수 있다. 더 구체적으로, R 9 내지 R 11과 R 12 내지 R 14는 각각 메틸기 또는 페닐기일 수 있다.
본 발명의 바람직한 구체예에 있어서, 위 화학식 1로 표시되는 화합물이 아래 화학식 1-1 내지 1-8로 표시되는 화합물 중 어느 하나일 수 있다.
[화학식 1-1] [화학식 1-2] [화학식 1-3]
Figure PCTKR2020014445-appb-img-000006
Figure PCTKR2020014445-appb-img-000007
Figure PCTKR2020014445-appb-img-000008
[화학식 1-4] [화학식 1-5] [화학식 1-6]
Figure PCTKR2020014445-appb-img-000009
Figure PCTKR2020014445-appb-img-000010
Figure PCTKR2020014445-appb-img-000011
[화학식 1-7] [화학식 1-8]
Figure PCTKR2020014445-appb-img-000012
Figure PCTKR2020014445-appb-img-000013
위 화학식 1-1 내지 1-8에서, M은 지르코늄 또는 하프늄이고, X는 각각 할로겐 또는 치환 또는 비치환된 C 1-20 알킬, 바람직하게는 염소 또는 메틸기이고, Me는 메틸기이고, Ph는 페닐기이다.
본 발명의 더 바람직한 구체예에 있어서, 위 화학식 1로 표시되는 화합물이 아래 화학식 1-9 또는 1-10으로 표시되는 화합물 중 어느 하나일 수 있다.
[화학식 1-9]
Figure PCTKR2020014445-appb-img-000014
[화학식 1-10]
Figure PCTKR2020014445-appb-img-000015
위 화학식 1-9 및 1-10에서, Me는 메틸기이다.
한편, 조촉매 화합물은 아래 화학식 2로 표현되는 화합물, 화학식 3으로 표현되는 화합물 및 화학식 4로 표현되는 화합물 중 하나 이상을 포함할 수 있다.
[화학식 2]
Figure PCTKR2020014445-appb-img-000016
위 화학식 2에서, n은 2 이상의 정수이고, R a는 할로겐 원자, C 1-20 탄화수소 또는 할로겐으로 치환된 C 1-20 탄화수소일 수 있다. 구체적으로, R a는 메틸, 에틸, n-부틸 또는 이소부틸일 수 있다.
[화학식 3]
Figure PCTKR2020014445-appb-img-000017
위 화학식 3에서, D는 알루미늄(Al) 또는 보론(B)이고, R b, R c 및 R d는 각각 독립적으로 할로겐 원자, C 1-20 탄화수소기, 할로겐으로 치환된 C 1-20 탄화수소기 또는 C 1-20 알콕시기이다. 구체적으로, D가 알루미늄(Al)일 때, R b, R c 및 R d는 각각 독립적으로 메틸 또는 이소부틸일 수 있고, D가 보론(B)일 때, R b, R c 및 R d는 각각 펜타플루오로페닐일 수 있다.
[화학식 4]
[L-H] +[Z(A) 4] - 또는 [L] +[Z(A) 4] -
위 화학식 4에서, L은 중성 또는 양이온성 루이스 염기이고, [L-H] + 및 [L] +는 브뢴스테드 산이며, Z는 13족 원소이고, A는 각각 독립적으로 치환 또는 비치환된 C 6-20 아릴기이거나 치환 또는 비치환된 C 1-20 알킬기이다. 구체적으로, [L-H] +는 디메틸아닐리늄 양이온일 수 있고, [Z(A) 4] -는 [B(C 6F 5) 4] -일 수 있으며, [L] +는 [(C 6H 5) 3C] +일 수 있다.
구체적으로, 위 화학식 2로 표시되는 화합물의 예로는 메틸알루미녹산, 에틸알루미녹산, 이소부틸알루미녹산, 부틸알루미녹산 등을 들 수 있으며, 메틸알루미녹산이 바람직하나, 이들로 제한되는 것은 아니다.
위 화학식 3으로 표시되는 화합물의 예로는 트리메틸알루미늄, 트리에틸알루미늄, 트리이소부틸알루미늄, 트리프로필알루미늄, 트리부틸알루미늄, 디메틸클로로알루미늄, 트리이소프로필알루미늄, 트리- s-부틸알루미늄, 트리사이클로펜틸알루미늄, 트리펜틸알루미늄, 트리이소펜틸알루미늄, 트리헥실알루미늄, 트리옥틸알루미늄, 에틸디메틸알루미늄, 메틸디에틸알루미늄, 트리페닐알루미늄, 트리- p-톨릴알루미늄, 디메틸알루미늄메톡시드, 디메틸알루미늄에톡시드, 트리메틸보론, 트리에틸보론, 트리이소부틸보론, 트리프로필보론, 트리부틸보론 등을 들 수 있으며, 트리메틸알루미늄, 트리에틸알루미늄 및 트리이소부틸알루미늄이 바람직하나, 이들로 제한되는 것은 아니다.
위 화학식 4로 표시되는 화합물의 예로는 트리에틸암모니움테트라페닐보론, 트리부틸암모니움테트라페닐보론, 트리메틸암모니움테트라페닐보론, 트리프로필암모니움테트라페닐보론, 트리메틸암모니움테트라( p-톨릴)보론, 트리메틸암모니움테트라( o, p-디메틸페닐)보론, 트리부틸암모니움테트라( p-트리플로로메틸페닐)보론, 트리메틸암모니움테트라( p-트리플로로메틸페닐)보론, 트리부틸암모니움테트라펜타플로로페닐보론, N,N-디에틸아닐리니움테트라페닐보론, N,N-디에틸아닐리니움테트라펜타플로로페닐보론, 디에틸암모니움테트라펜타플로로페닐보론, 트리페닐포스포늄테트라페닐보론, 트리메틸포스포늄테트라페닐보론, 트리에틸암모니움테트라페닐알루미늄, 트리부틸암모니움테트라페닐알루미늄, 트리메틸암모니움테트라페닐알루미늄, 트리프로필암모니움테트라페닐알루미늄, 트리메틸암모니움테트라( p-톨릴)알루미늄, 트리프로필암모니움테트라( p-톨릴)알루미늄, 트리에틸암모니움테트라( o, p-디메틸페닐)알루미늄, 트리부틸암모니움테트라( p-트리플로로메틸페닐)알루미늄, 트리메틸암모니움테트라( p-트리플로로메틸페닐)알루미늄, 트리부틸암모니움테트라펜타플로로페닐알루미늄, N,N-디에틸아닐리니움테트라페닐알루미늄, N,N-디에틸아닐리니움테트라펜타플로로페닐알루미늄, 디에틸암모니움테트라펜타테트라페닐알루미늄, 트리페닐포스포늄테트라페닐알루미늄, 트리메틸포스포늄테트라페닐알루미늄, 트리프로필암모니움테트라( p-톨릴)보론, 트리에틸암모니움테트라( o, p-디메틸페닐)보론, 트리부틸암모니움테트라( p-트리플로로메틸페닐)보론, 트리페닐카보니움테트라( p-트리플로로메틸페닐)보론, 리페닐카보니움테트라펜타플로로페닐보론 등을 들 수 있다.
본 발명의 바람직한 구체예에 있어서, 올레핀 중합용 촉매가 전이금속 화합물을 담지하는 담체를 더 포함할 수 있다. 구체적으로, 담체가 전이금속 화합물과 조촉매 화합물을 모두 담지할 수 있다.
이때, 담체는 표면에 히드록시기를 함유하는 물질을 포함할 수 있으며, 바람직하게는 건조되어 표면에 수분이 제거된, 반응성이 큰 히드록시기와 실록산기를 갖는 물질이 사용될 수 있다. 예컨대, 담체는 실리카, 알루미나 및 마그네시아로 구성되는 군으로부터 선택되는 적어도 하나를 포함할 수 있다. 구체적으로, 고온에서 건조된 실리카, 실리카-알루미나, 및 실리카-마그네시아 등이 담체로서 사용될 수 있고, 이들은 통상적으로 Na 2O, K 2CO 3, BaSO 4, 및 Mg(NO 3) 2 등의 산화물, 탄산염, 황산염, 및 질산염 성분을 함유할 수 있다. 또한, 이들은 탄소, 제올라이트, 염화 마그네슘 등을 포함할 수도 있다. 다만, 담체가 이들로 제한되는 것은 아니며, 전이금속 화합물과 조촉매 화합물을 담지할 수 있는 것이면 특별히 제한되지 않는다.
담체는 평균 입도가 10~250 ㎛일 수 있으며, 바람직하게는 평균 입도가 10~150 ㎛일 수 있고, 보다 바람직하게는 20~100 ㎛일 수 있다.
담체의 미세기공 부피는 0.1~10 ㎖/g일 수 있으며, 바람직하게는 0.5~5 ㎖/g일 수 있고, 보다 바람직하게는 1.0~3.0 ㎖/g일 수 있다.
담체의 비표면적은 1~1,000 ㎡/g일 수 있으며, 바람직하게는 100~800 ㎡/g일 수 있고, 보다 바람직하게는 200~600 ㎡/g일 수 있다.
바람직한 일 실시예에서, 담체가 실리카일 경우, 실리카는 건조 온도는 200~900℃일 수 있다. 건조 온도는 바람직하게는 300~800℃, 보다 바람직하게는 400~700℃일 수 있다. 건조 온도가 200℃ 미만일 경우에는 수분이 너무 많아서 표면의 수분과 조촉매 화합물이 반응하게 되고, 900℃를 초과하게 되면 담체의 구조가 붕괴될 수 있다.
건조된 실리카 내의 히드록시기의 농도는 0.1~5 mmole/g일 수 있으며, 바람직하게는 0.7~4 mmole/g일 수 있고, 보다 바람직하게는 1.0~2 mmole/g일 수 있다. 히드록시기의 농도가 0.1 mmole/g 미만이면 제1 조촉매 화합물의 담지량이 낮아지며, 5 mmole/g을 초과하면 촉매 성분이 불활성화되는 문제점이 발생할 수 있다.
담체에 담지되는 전이금속 화합물의 양은 담체 1 g을 기준으로 0.001~1 mmole일 수 있다. 전이금속 화합물과 담체의 비가 위 범위를 만족하면, 적절한 담지 촉매 활성을 나타내어 촉매의 활성 유지 및 경제성 측면에서 유리하다.
담체에 담지되는 조촉매 화합물의 양은 담체 1 g을 기준으로 2~15 mmole일 수 있다. 조촉매 화합물과 담체의 비가 위 범위를 만족하면, 촉매의 활성 유지 및 경제성 측면에서 유리하다.
담체는 1종 또는 2종 이상이 사용될 수 있다. 예를 들어, 1종의 담체에 전이금속 화합물과 조촉매 화합물이 모두 담지될 수도 있고, 2종 이상의 담체에 전이금속 화합물과 조촉매 화합물이 각각 담지될 수도 있다. 또한, 전이금속 화합물과 조촉매 화합물 중 하나만이 담체에 담지될 수도 있다.
올레핀 중합용 촉매에 사용될 수 있는 전이금속 화합물 및/또는 조촉매 화합물을 담지하는 방법으로서, 물리적 흡착 방법 또는 화학적 흡착 방법이 사용될 수 있다.
예를 들어, 물리적 흡착 방법은 전이금속 화합물이 용해된 용액을 담체에 접촉시킨 후 건조하는 방법, 전이금속 화합물과 조촉매 화합물이 용해된 용액을 담체에 접촉시킨 후 건조하는 방법, 또는 전이금속 화합물이 용해된 용액을 담체에 접촉시킨 후 건조하여 전이금속 화합물이 담지된 담체를 제조하고, 이와 별개로 조촉매 화합물이 용해된 용액을 담체에 접촉시킨 후 건조하여 조촉매 화합물이 담지된 담체를 제조한 후, 이들을 혼합하는 방법 등일 수 있다.
화학적 흡착 방법은 담체의 표면에 조촉매 화합물을 먼저 담지시킨 후, 조촉매 화합물에 전이금속 화합물을 담지시키는 방법, 또는 담체의 표면의 작용기(예를 들어, 실리카의 경우 실리카 표면의 히드록시기(-OH))와 촉매 화합물을 공유결합시키는 방법 등일 수 있다.
올레핀 중합체
본 발명의 구체예에 따라서, 상술한 올레핀 중합용 촉매의 존재하에 올레핀계 단량체가 중합되어 제조되는 올레핀계 중합체가 제공된다.
본 발명의 구체예에 따른 올레핀계 중합체는 아래 수학식 1로 정의되는 공단량체 분포 기울기(comonomer distribution slope; CDS)가 1 이상, 바람직하게는 2~5이다.
[수학식 1]
Figure PCTKR2020014445-appb-img-000018
위 수학식 1에서, C 20과 C 80은 공단량체 분포에서 누적 질량 분율(cumulative weight fraction)이 각각 20%와 80%인 지점에서의 공단량체 함량이고, M 20과 M 80은 공단량체 분포에서 누적 질량 분율이 각각 20%와 80%인 지점에서의 분자량이다.
여기서, 올레핀계 중합체의 공단량체 분포는 GPC-FTIR 장비를 이용하여 중합체의 분자량, 분자량 분포와 함께 연속적으로 측정할 수 있다.
올레핀계 중합체의 CDS는 공단량체 분포 그래프에서 누적 질량 분율이 각각 20%와 80%인 지점에서의 분자량에 대한 공단량체 함량의 기울기를 나타낸다. 올레핀계 중합체의 CDS가 클수록 분자량이 큰 고분자 사슬에 공중합체가 집중되어 우수한 기계적 강도를 가질 수 있다.
바람직하게는, 본 발명의 구체예에 따른 올레핀계 중합체는 (1) 다분산지수(Mw/Mn)에 의한 분자량 분포가 2~20; (2) 밀도가 0.88~0.96 g/㎤; (3) 190℃에서 2.16 kg 하중으로 측정 시 용융지수(melt index; I 2.16)가 0.01~3.0 g/10분; 및 (4) 190℃에서 21.6 kg의 하중으로 측정되는 용융지수(I 21.6)와 I 2.16의 비(melt flow ratio; MFR)가 25 이상, 바람직하게는 30~100일 수 있다.
구체적으로, 본 발명의 구체예에 따른 올레핀계 중합체는 다분산지수(Mw/Mn)에 의한 분자량 분포(polydispersity index; PDI)가 2~20일 수 있다. 바람직하게는, 올레핀계 중합체의 PDI가 2~8 또는 2~6일 수 있다.
본 발명의 구체예에 따른 올레핀계 중합체는 밀도가 0.88~0.96 g/㎤일 수 있다. 바람직하게는, 올레핀계 중합체의 밀도가 0.90~0.96 g/㎤ 또는 0.92~0.96 g/㎤일 수 있다.
본 발명의 구체예에 따른 올레핀계 중합체는 ASTM D 1238에 따라서 190℃에서 2.16 kg의 하중으로 측정되는 용융지수(I 2.16)가 0.01~3.0 g/10분일 수 있다. 바람직하게는, 올레핀계 중합체의 용융지수(I 2.16)가 0.01~2.5 g/10분 또는 0.01~2.0 g/10분일 수 있다.
또한, 본 발명의 구체예에 따른 올레핀계 중합체는 ASTM D 1238에 따라서 190℃에서 21.6 kg의 하중으로 측정되는 용융지수(I 21.6)와 2.16 kg의 하중으로 측정되는 용융지수(I 2.16)의 비(melt flow ratio; MFR)가 25 이상일 수 있다. 바람직하게는, 올레핀계 중합체의 MFR은 30~100 또는 30~80일 수 있다.
바람직하게는, 올레핀계 중합체의 중량평균 분자량(Mw)이 100,000~500,000 g/mole일 수 있다. 더 바람직하게는, 올레핀계 중합체의 중량평균 분자량(Mw)이 100,000~450,000 g/mole 또는 100,000~400,000 g/mole일 수 있다.
여기서, 올레핀계 중합체는 올레핀계 단량체의 단독 중합체(homopolymer) 또는 올레핀계 단량체와 공단량체의 공중합체(copolymer)일 수 있다.
올레핀계 단량체는 C 2-20 알파-올레핀(α-olefin), C 1-20 디올레핀(diolefin), C 3-20 사이클로올레핀(cycloolefin) 및 C 3-20 사이클로디올레핀(cyclodiolefin)으로 구성되는 군으로부터 선택되는 적어도 하나이다.
예를 들어, 올레핀계 단량체는 에틸렌, 프로필렌, 1-부텐, 1-펜텐, 4-메틸-1-펜텐, 1-헥센, 1-헵텐, 1-옥텐, 1-데센, 1-운데센, 1-도데센, 1-테트라데센 또는 1-헥사데센 등일 수 있고, 올레핀계 중합체는 위에서 예시된 올레핀계 단량체를 1종만 포함하는 단독 중합체이거나 2종 이상 포함하는 공중합체일 수 있다.
예시적인 실시예에서, 올레핀계 중합체는 에틸렌과 C 3-20 알파-올레핀이 공중합된 공중합체일 수 있으며, 에틸렌과 1-헥센이 공중합된 공중합체가 바람직하나, 이들로 제한되는 것은 아니다.
이 경우, 에틸렌의 함량은 55~99.9 중량%인 것이 바람직하고, 90~99.9 중량%인 것이 더욱 바람직하다. 알파-올레핀계 공단량체의 함량은 0.1~45 중량%가 바람 직하고, 0.1~10 중량%인 것이 더욱 바람직하다.
본 발명의 구체예에 따른 올레핀계 중합체는, 예를 들어 자유 라디칼(free radical), 양이온(cationic), 배위(coordination), 축합(condensation), 첨가(addition) 등의 중합반응에 의해 중합될 수 있으나, 이들로 제한되는 것은 아니다.
바람직한 실시예로서, 올레핀계 중합체는 기상 중합법, 용액 중합법 또는 슬러리 중합법 등으로 제조될 수 있다. 올레핀계 중합체가 용액 중합법 또는 슬러리 중합법으로 제조되는 경우, 사용될 수 있는 용매의 예로서, 펜탄, 헥산, 헵탄, 노난, 데칸 및 이들의 이성질체와 같은 C 5-12 지방족 탄화수소 용매; 톨루엔, 벤젠과 같은 방향족 탄화수소 용매; 디클로로메탄, 클로로벤젠과 같은 염소 원자로 치환된 탄화수소 용매; 및 이들의 혼합물 등을 들 수 있으나, 이들로 제한되는 것은 아니다.
올레핀 중합체 필름
본 발명의 또 다른 구체예에 따라서, 올레핀계 중합체를 성형하여 제조되는 필름이 제공된다.
본 발명의 구체예에 따른 필름은 본 발명의 올레핀계 중합체를 포함함으로써, 기계적 물성이 우수하다. 본 발명의 올레핀계 중합체는 비교적 넓은 분자량 분포를 가지며, 고 분자량 성분에 단쇄 분지가 상대적으로 많이 존재하기 때문에, 이로부터 제조되는 필름의 기계적 강도가 우수한 것으로 이해된다.
본 발명의 구체예에 따른 필름의 제조방법은 특별히 제한되지 않으며, 본 발명이 속하는 기술분야에 공지된 방법을 사용할 수 있다. 예를 들어, 본 발명의 구체예에 따른 올레핀계 중합체를 블로운 필름 성형, 압출 성형, 캐스팅 성형 등의 통상적인 방법으로 가공하여 열수축성 폴리프로필렌 필름을 제조할 수 있다. 이 중에서 블로운 필름 성형이 가장 바람직하다.
본 발명의 구체예에 따른 올레핀 중합체 필름은 스트레치 필름, 오버랩 필름, 라미, 사일리지 랩, 농업용 필름 등으로 효과적으로 사용될 수 있다.
실시예
이하, 실시예를 통하여 본 발명을 보다 구체적으로 설명한다. 단, 아래의 실시예는 본 발명을 예시하기 위한 것일 뿐이며, 본 발명의 범위가 이들만으로 한정되는 것은 아니다.
제조예 1: 비스[(2-트리메틸실릴메틸알릴)사이클로펜타디에닐] 하프늄 디클로라이드(bis[(2-trimethylsilylmethylallyl)cyclopentadienyl] hafnium dichloride; 화학식 1-9)의 제조
2-( 트리메틸실릴메틸 )-2- 프로펜 -1-올(2-( trimethylsilylmethyl )-2- propen -1-ol)의 제조
2-(트리메틸실릴메틸)알릴 아세테이트(2-(trimethylsilylmethyl)allyl acetate)(2.69 g, 14.4 mmole)를 메탄올(methanol; 22 ㎖)에 녹인 용액에 탄산칼륨(K 2CO 3) 수용액(6.6 M, 14.4 mmole)을 천천히 투입하였다. 투입 완료 후, 이를 상온에서 4시간 동안 교반하였다. 교반 후, 여기에 물을 넣어 반응을 종결시켰다. 디에틸 에테르(diethyl ether)를 사용하여 유기층을 추출한 후, 황산 마그네슘(MgSO 4)으로 남아 있는 물을 제거하였다. 진공하에서 모든 용매를 제거하여 연미색의 오일 화합물 1.51 g(72%)을 얻었다.
1H-NMR (CDCl 3, 300 MHz): δ 4.90-4.88 (m, 1H), 4.66 (s, 1H), 3.97 (s, 2H), 1.53 (s, 2H), 0.03 (s, 9H).
2-( 트리메틸실릴메틸 ) 메탄설포네이트 (2-( trimethylsilylmethyl ) methanesulfonate)의 제조
2-(트리메틸실릴메틸)-2-프로펜-1-올(1.51 g, 10.5 mmole)과 트리에틸아민(triethylamine)(1.91 g, 18.8 mmole)을 디클로로메탄(dichloromethane)(30 ㎖)에 희석한 용액에 메탄설포닐 클로라이드(methanesulfonyl chloride)(1.8 g, 15.7 mmole)를 0℃에서 천천히 첨가였다. 그 후, 0℃에서 3시간 동안 교반하였다. 0℃에서 탄산수소나트륨(NaHCO 3) 수용액을 넣어 반응을 종결시킨 후, 디클로로메탄으로 추출하여 유기층을 분리하였다. 황산 나트륨(Na 2SO 4)으로 남아 있는 물을 제거한 후, 진공하에서 모든 용매를 제거하여 노란색 오일 화합물 1.9 g(82%)을 얻었다.
1H-NMR (CDCl 3, 300 MHz): δ5.03 (d, 1H), 4.84 (s, 1H), 4.56 (s, 2H), 3.02 (s, 3H), 1.60 (s, 2H), 0.06 (s, 9H).
2-( 트리메틸실릴메틸 )알릴 브로마이드(2-( trimethylsilylmethyl ) allyl bromide)의 제조
2-(트리메틸실릴메틸) 메탄설포네이트(1.9 g, 8.54 mmole)를 테트라하이드로퓨란(tetrahydrofuran)(20 ㎖)에 희석한 용액에 리튬 브로마이드(lithium bromide)를 테트라하이드로퓨란(15 ㎖)에 분산시킨 용액을 상온에서 천천히 첨가한 후, 110℃에서 4시간 동안 교반하였다. 0℃에서 증류수를 넣어 반응을 종결시킨 후, 디에틸 에테르로 추출하여 유기층을 분리하였다. 황산 나트륨으로 남아 있는 물을 제거한 후, 진공하에서 모든 용매를 제거하여 노란색 오일 화합물 1.12 g(65%)을 얻었다.
1H-NMR (CDCl 3, 300 MHz): δ5.04 (s, 1H), 4.74 (d, 1H), 3.90 (d, 2H), 1.72 (d, 2H), 0.05 (s, 9H).
[2-( 사이클로펜타디에닐메틸 )알릴] 트리메틸실란 ([2-(cyclopentadienylmethyl)allyl] trimethylsilane)의 제조
2-(트리메틸실릴메틸)알릴 브로마이드(1.12 g, 5.41 mmole)를 테트라하이드로퓨란(20 ㎖)에 희석한 용액에 나트륨 시클로펜타디엔나이드(sodium cyclopentadienide)(3.04 g, 6.49 mmole, 2M THF 용액)를 -30℃에서 천천히 떨어뜨리고, 온도를 서서히 상온으로 올려 12시간 동안 교반하였다. 0℃에서 증류수를 첨가하여 반응을 종결시킨 후, 디에틸 에테르로 추출하여 유기층을 분리하였다. 황산 마그네슘으로 남아 있는 물을 제거한 후 컬럼 크로마토그래피(hexane)로 분리하여 연미색 오일 화합물 620 mg (60%)을 얻었다.
1H-NMR (CDCl 3, 300 MHz): δ6.42-6.02 (m, 4H), 4.60-4.55 (m, 2H), 3.06-2.97 (m, 2H), 2.87-2.85 (m, 2H), 1.54 (s, 2H), 0.03 (d, 9H).
[2-( 트리메틸실릴메틸 )알릴] 사이클로펜타디에닐 리튬([2-(trimethylsilylmethyl)allyl] cyclopentadienyl lithium)의 제조
[2-(사이클로펜타디에닐메틸)알릴] 트리메틸실란(620 mg, 3.22 mmole)을 테트라하이드로퓨란(10 ㎖)에 희석한 용액에 n-부틸리튬(n-BuLi)(1.44 g, 2.93 mmole, 1.6 M 헥산 용액)을 -30℃에서 천천히 첨가한 후, 온도를 서서히 상온으로 올려 12시간 동안 교반하였다. 반응 용액의 용매를 진공하에서 건조한 후, 헥산을 넣어 15분 동안 교반하였다. 생성된 고체를 여과한 후, 진공하에서 건조하여 연노란색 고체 화합물 528 mg(83%)을 얻었다.
비스 [(2- 트리메틸실릴메틸알릴 ) 사이클로펜타디에닐 ] 하프늄 디클로라이드의 제조
[2-(트리메틸실릴메틸)알릴] 사이클로펜타디에닐 리튬(280 mg, 1.41 mmole)을 톨루엔(3 ㎖)에 희석한 용액에 염화 하프늄(HfCl 4)(226 mg, 0.71 mmole)을 톨루엔(2 ㎖)에 분산시킨 용액을 -30℃에서 천천히 첨가한 후, 온도를 서서히 상온으로 올려 12시간 동안 교반하였다. 반응이 종결되면 반응 용액을 여과한 후, 여과액의 용매를 진공하에서 건조하였다. 생성된 고체를 헥산으로 씻어내고 건조하여 흰색의 고체 화합물 180 mg(41 %)을 얻었다.
1H-NMR (CDCl 3, 300 MHz): δ6.21 (t, 2H), 6.12 (t, 2H), 4.54 (d, 2H), 4.44 (d, 1H), 3.28 (s, 2H), 1.52 (s, 2H), 0.05 (s, 9H).
메탈로센 담지 촉매의 제조
화학식 1-9의 화합물 0.186 g에 10% 메틸알루미녹산의 톨루엔 용액 16.2 g을 투입하여 상온에서 1시간 교반하였다. 반응기 끝난 용액을 4.14 g의 실리카(XPO-2402)에 투입하고, 추가로 톨루엔 30 ㎖를 넣어 70℃에서 2시간 동안 교반하였다. 담지가 끝난 촉매를 20 ㎖의 톨루엔으로 3회 세척하였고, 60℃ 진공에서 밤새 건조시켜 분말 형태의 담지 촉매 6 g을 제조하였다.
제조예 2: 디메틸 비스[(2-트리메틸실릴메틸알릴)사이클로펜타디에닐] 하프늄(dimethyl bis[(2-trimethylsilylmethylallyl)cyclopentadienyl] hafnium; 화학식 1-10)의 제조
제조예 1에서 제조한 비스[2-(트리메틸실릴메틸)알릴]사이클로팬타디에닐 하프늄 디클로라이드(2.4 g, 3.79 mmole)를 톨루엔에 희석한 용액에 MeMgBr(3.0 M의 디에틸 에테르 용액, 11.4 mmole)을 -30℃에서 천천히 첨가한 후, 온도를 서서히 상온으로 올려 12시간 교반하였다. 반응이 종결되면 톨루엔으로 추출하여 여과한 후, 여과액의 용매를 진공하에서 건조하였다. 생성된 고체를 헥산으로 씻어내고 건조하여 흰색의 고체 화합물 2.08 g(93 %)를 얻었다.
위에서 얻은 화학식 1-10의 화합물 0.174 g을 사용하여, 제조예 1과 동일한 방법으로 담지 촉매 6 g을 제조하였다.
제조예 3
sPCI사에서 구매한 아래 화학식 A-1의 화합물을 정제하지 않고 사용하였다. 화학식 A-1의 화합물 0.127 g을 사용하여, 제조예 1과 동일한 방법으로 담지 촉매 6 g을 제조하였다.
[화학식 A-1]
Figure PCTKR2020014445-appb-img-000019
제조예 4
MCN사에서 구매한 아래 화학식 A-2의 화합물을 정제하지 않고 사용하였다. 화학식 A-2의 화합물 0.116 g을 사용하여, 제조예 1과 동일한 방법으로 담지 촉매 6 g을 제조하였다.
[화학식 A-2]
Figure PCTKR2020014445-appb-img-000020
실시예 1
2-리터 오토클레이브 반응기를 이용하여 제조예 1에서 얻어진 담지 촉매의 존재하에 에틸렌/1-헥센 공중합체를 제조하였다. 반응기에 헥산 1 리터, 스캐빈저로서 1M 트리이소부틸 알루미늄(TiBAL) 0.6 ㎖와 함께 제조예 1에서 제조한 담지 촉매 100 ㎎을 투입한 후, 에틸렌 분압을 14 kgf/㎠으로 유지하면서 1-헥센 50 ㎖와 수소 0~5 ㎖/min을 투입하여 1시간 동안 중합 반응을 진행하였다, 반응 결과 그래뉼(granule) 형태의 에틸렌/1-헥센 공중합체 100~200 g을 수득하였다.
실시예 2
제조예 2에서 제조한 담지 촉매를 사용하여 실시예 1과 동일한 방법으로 중합 반응을 실시하여 에틸렌/1-헥센 공중합체를 수득하였다.
비교예 1
제조예 3에서 제조한 담지 촉매를 사용하여 실시예 1과 동일한 방법으로 중합 반응을 실시하여 에틸렌/1-헥센 공중합체를 수득하였다.
비교예 2
제조예 4에서 제조한 담지 촉매를 사용하여 실시예 1과 동일한 방법으로 중합 반응을 실시하여 에틸렌/1-헥센 공중합체를 수득하였다.
위 실시예와 비교예의 중합 조건을 아래 표 1에 나타내었다.
촉매 양
(㎎)
수소 유량
(㎖/min)
1-헥센 양
(㎖)
촉매 활성
(gPE/gCat-hr)
실시예 1-1 100 0 50 1,990
실시예 1-2 100 1 50 2,080
실시예 1-3 100 5 50 2,490
실시예 2 100 0 50 3,080
비교예 1 100 0 50 2,650
비교예 2 100 0 50 3,420
시험예
위 실시예와 비교예에서 얻은 올레핀 중합체의 물성을 아래와 같은 방법 및 기준에 따라서 측정하였다. 그 결과를 아래 표 2에 나타내었다.
(1) 용융지수(melt index) 및 용융지수비(melt flow ratio; MFR)
ASTM D 1238에 의거하여 21.6 kg의 하중과 2.16 kg의 하중으로 190℃에서 각각 용융지수를 측정하고 그 비(MI 21.6/MI 2.16)를 구하였다.
(2) 밀도(density)
ASTM D1505에 의거하여 측정하였다.
(3) 분자량(Mw) 및 분자량 분포(PDI)
겔투과 크로마토그래피-에프티아이알(GPC-FTIR)을 이용하여 측정하였다.
(4) 공단량체 분포 기울기(CDS)
겔투과 크로마토그래피-에프티아이알(GPC-FTIR)을 이용하여 측정하였다.
I 2.16
(g/10분)
I 21.6
(g/10분)
MFR Mw
(g/mole)
PDI CDS 밀도
(g/㎤)
실시예 1-1 0.08 3.26 40.7 224,000 2.60 4.36 0.9290
실시예 1-2 0.12 3.78 31.5 208,000 3.09 3.19 0.9320
실시예 1-3 1.73 105.4 60.9 136,000 7.54 2.99 0.9385
실시예 2 0.04 2.34 58.4 334,000 2.27 3.85 0.9205
비교예 1 0.17 3.28 19.3 299,000 2.03 -0.27 0.9250
비교예 1 2.36 40.4 17.1 184,000 1.78 -0.01 0.9220
본 발명의 구체예에 따른 올레핀계 중합체, 구체적으로 선형 저밀도 폴리에틸렌은 분자량 분포가 비교적 넓고 공단량체가 역(reverse)의 분포를 나타내어 가공성과 기계적 강도가 우수하다.

Claims (11)

  1. 아래 수학식 1로 정의되는 공단량체 분포 기울기(comonomer distribution slope; CDS)가 1 이상인 올레핀계 중합체:
    [수학식 1]
    Figure PCTKR2020014445-appb-img-000021
    여기서, C 20과 C 80은 공단량체 분포에서 누적 질량 분율(cumulative weight fraction)이 각각 20%와 80%인 지점에서의 공단량체 함량이고, M 20과 M 80은 공단량체 분포에서 누적 질량 분율이 각각 20%와 80%인 지점에서의 분자량이다.
  2. 제1항에 있어서, 공단량체 분포 기울기가 2~5인 올레핀계 중합체.
  3. 제1항에 있어서, (1) 다분산지수(Mw/Mn)에 의한 분자량 분포가 2~20; (2) 밀도가 0.88~0.96 g/㎤; (3) 190℃에서 2.16 kg 하중으로 측정 시 용융지수(melt index; I 2. 16)가 0.01~3.0 g/10분; 및 (4) 190℃에서 21.6 kg의 하중으로 측정되는 용융지수(I 21.6)와 I 2.16의 비(melt flow ratio; MFR)가 25 이상인 올레핀계 중합체.
  4. 제1항에 있어서, 중량평균 분자량(Mw)이 100,000~500,000 g/mole인 올레핀계 중합체.
  5. 제1항에 있어서, 올레핀계 단량체가 에틸렌이고, 올레핀계 공단량체가 프로필렌, 1-부텐, 1-펜텐, 4-메틸-1-펜텐, 1-헥센, 1-헵텐, 1-옥텐, 1-데센, 1-운데센, 1-도데센, 1-테트라데센 및 1-헥사데센으로 구성되는 군으로부터 선택되는 하나 이상인 올레핀계 중합체.
  6. 제5항에 있어서, 올레핀계 중합체가 올레핀계 단량체가 에틸렌이고 올레핀계 공단량체가 1-헥센인 선형 저밀도 폴리에틸렌인 올레핀계 중합체.
  7. 제1항에 있어서, 아래 화학식 1로 표시되는 적어도 1종의 전이금속 화합물과 적어도 1종의 조촉매 화합물을 포함하는 촉매의 존재하에 제조되는 올레핀계 중합체:
    [화학식 1]
    Figure PCTKR2020014445-appb-img-000022
    위 화학식 1에서, n은 각각 독립적으로 1~20의 정수이고,
    M은 티타늄(Ti), 지르코늄(Zr) 또는 하프늄(Hf)이며,
    X는 각각 독립적으로 할로겐, C 1-20 알킬, C 2-20 알케닐, C 2-20 알키닐, C 6-20 아릴, C 1-20 알킬 C 6-20 아릴, C 6-20 아릴 C 1-20 알킬, C 1-20 알킬아미도, C 6-20 아릴아미도 또는 C 1-20 알킬리덴이고,
    R 1 내지 R 4와 R 5 내지 R 8은 각각 독립적으로 수소, 치환 또는 비치환된 C 1-20 알킬, 치환 또는 비치환된 C 2-20 알케닐, 치환 또는 비치환된 C 6-20 아릴, 치환 또는 비치환된 C 1-20 알킬 C 6-20 아릴, 치환 또는 비치환된 C 6-20 아릴 C 1-20 알킬, 치환 또는 비치환된 C 1-20 헤테로알킬, 치환 또는 비치환된 C 3-20 헤테로아릴, 치환 또는 비치환된 C 1-20 알킬아미도, 치환 또는 비치환된 C 6-20 아릴아미도, 치환 또는 비치환된 C 1-20 알킬리덴, 또는 치환 또는 비치환된 C 1-20 실릴이고,
    R 9 내지 R 11과 R 12 내지 R 14는 각각 독립적으로 치환 또는 비치환된 C 1-20 알킬, 치환 또는 비치환된 C 2-20 알케닐, 치환 또는 비치환된 C 6-20 아릴, 치환 또는 비치환된 C 1-20 알킬 C 6-20 아릴, 치환 또는 비치환된 C 6-20 아릴 C 1-20 알킬, 치환 또는 비치환된 C 1-20 헤테로알킬, 치환 또는 비치환된 C 3-20 헤테로아릴, 치환 또는 비치환된 C 1-20 알킬아미도, 치환 또는 비치환된 C 6-20 아릴아미도, 치환 또는 비치환된 C 1-20 알킬리덴, 또는 치환 또는 비치환된 C 1-20 실릴이고,
    R 1 내지 R 4와 R 5 내지 R 8은 각각 독립적으로 인접한 기가 연결되어 치환 또는 비치환된 포화 또는 불포화 C 4-20 고리를 형성할 수 있다.
  8. 제7항에 있어서, 조촉매 화합물이 아래 화학식 2로 표현되는 화합물, 화학식 3으로 표현되는 화합물 및 화학식 4로 표현되는 화합물로 구성되는 군으로부터 선택되는 하나 이상인, 올레핀계 중합체:
    [화학식 2]
    Figure PCTKR2020014445-appb-img-000023
    [화학식 3]
    Figure PCTKR2020014445-appb-img-000024
    [화학식 4]
    [L-H] +[Z(A) 4] - 또는 [L] +[Z(A) 4] -
    위 화학식 2에서, n은 2 이상의 정수이고, R a는 할로겐 원자, C 1-20 탄화수소기 또는 할로겐으로 치환된 C 1-20 탄화수소기이고,
    위 화학식 3에서, D는 알루미늄(Al) 또는 보론(B)이고, R b, R c 및 R d는 각각 독립적으로 할로겐 원자, C 1-20 탄화수소기, 할로겐으로 치환된 C 1-20 탄화수소기 또는 C 1-20 알콕시기이며,
    위 화학식 4에서, L은 중성 또는 양이온성 루이스 염기이고, [L-H] + 및 [L] +는 브뢴스테드 산이며, Z는 13족 원소이고, A는 각각 독립적으로 치환 또는 비치환된 C 6-20 아릴기이거나 치환 또는 비치환된 C 1-20 알킬기이다.
  9. 제7항에 있어서, 촉매가 전이금속 화합물과 조촉매 화합물을 담지하는 담체를 더 포함하는, 올레핀계 중합체.
  10. 제1항 내지 제9항 중 어느 한 항에 따른 올레핀계 중합체를 성형하여 제조되는 필름.
  11. 제10항에 있어서, 스트레치 필름, 오버랩 필름, 라미, 사일리지 랩 및 농업용 필름으로 구성되는 군으로부터 선택되는 하나인 필름.
PCT/KR2020/014445 2019-10-29 2020-10-22 올레핀계 중합체 WO2021085929A1 (ko)