WO2021075388A1 - Composition de résine thermodurcissable, matériau de revêtement pour impression, produit durci, stratifié et procédé de production de stratifié - Google Patents

Composition de résine thermodurcissable, matériau de revêtement pour impression, produit durci, stratifié et procédé de production de stratifié Download PDF

Info

Publication number
WO2021075388A1
WO2021075388A1 PCT/JP2020/038382 JP2020038382W WO2021075388A1 WO 2021075388 A1 WO2021075388 A1 WO 2021075388A1 JP 2020038382 W JP2020038382 W JP 2020038382W WO 2021075388 A1 WO2021075388 A1 WO 2021075388A1
Authority
WO
WIPO (PCT)
Prior art keywords
resin composition
thermosetting resin
polymer
radical polymer
composition according
Prior art date
Application number
PCT/JP2020/038382
Other languages
English (en)
Japanese (ja)
Inventor
有人 市原
義人 廣田
Original Assignee
三井化学株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 三井化学株式会社 filed Critical 三井化学株式会社
Priority to JP2021552372A priority Critical patent/JP7247362B2/ja
Publication of WO2021075388A1 publication Critical patent/WO2021075388A1/fr

Abstract

Cette composition de résine thermodurcissable contient (A) une résine aminoplaste éthérifiée par alkyle ayant un paramètre de solubilité δ (valeur SP) d'au plus 10,0, (B) un polymère radicalaire ayant un groupe hydroxyle, et (C) un catalyseur acide.
PCT/JP2020/038382 2019-10-16 2020-10-09 Composition de résine thermodurcissable, matériau de revêtement pour impression, produit durci, stratifié et procédé de production de stratifié WO2021075388A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
JP2021552372A JP7247362B2 (ja) 2019-10-16 2020-10-09 熱硬化性樹脂組成物、印刷用コーティング材、硬化物、積層体および積層体の製造方法

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2019-189402 2019-10-16
JP2019189402 2019-10-16

Publications (1)

Publication Number Publication Date
WO2021075388A1 true WO2021075388A1 (fr) 2021-04-22

Family

ID=75538492

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2020/038382 WO2021075388A1 (fr) 2019-10-16 2020-10-09 Composition de résine thermodurcissable, matériau de revêtement pour impression, produit durci, stratifié et procédé de production de stratifié

Country Status (3)

Country Link
JP (1) JP7247362B2 (fr)
TW (1) TW202130743A (fr)
WO (1) WO2021075388A1 (fr)

Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH1088010A (ja) * 1996-09-17 1998-04-07 Nippon Paint Co Ltd 硬化性樹脂組成物
JP2003221686A (ja) * 2001-11-14 2003-08-08 Jfe Steel Kk 表面処理金属板および表面処理剤
WO2009122934A1 (fr) * 2008-03-31 2009-10-08 コニカミノルタオプト株式会社 Ensemble élément optique et procédé de production d'une unité optique
JP2020084099A (ja) * 2018-11-29 2020-06-04 三井化学株式会社 水性樹脂組成物、塗膜および塗装物品

Family Cites Families (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH1045867A (ja) * 1996-07-30 1998-02-17 Nippon Paint Co Ltd 熱硬化性樹脂組成物
CN101952380B (zh) 2008-03-31 2013-03-20 日立化成高分子株式会社 剥离剂组合物和剥离材
JP6157092B2 (ja) 2012-11-15 2017-07-05 三井化学株式会社 エチル化メラミン樹脂、その製造方法、塗料用硬化剤、樹脂組成物、塗膜および積層体

Patent Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH1088010A (ja) * 1996-09-17 1998-04-07 Nippon Paint Co Ltd 硬化性樹脂組成物
JP2003221686A (ja) * 2001-11-14 2003-08-08 Jfe Steel Kk 表面処理金属板および表面処理剤
WO2009122934A1 (fr) * 2008-03-31 2009-10-08 コニカミノルタオプト株式会社 Ensemble élément optique et procédé de production d'une unité optique
JP2020084099A (ja) * 2018-11-29 2020-06-04 三井化学株式会社 水性樹脂組成物、塗膜および塗装物品

Also Published As

Publication number Publication date
JP7247362B2 (ja) 2023-03-28
TW202130743A (zh) 2021-08-16
JPWO2021075388A1 (fr) 2021-04-22

Similar Documents

Publication Publication Date Title
CN103740251B (zh) 一种光学聚酯薄膜用高附着力水性涂布液
EP1489148B1 (fr) Composition de revetement pouvant etre sechee sous uv et articles revetus
RU2469058C2 (ru) Отслаивающееся временное покрытие
JP6387725B2 (ja) 積層フィルムおよびその製造方法
JP2009544825A (ja) ポリウレタンプライマーを有する自動車用窓パネル
WO2020196223A1 (fr) Feuille anti-adhésive
KR20140138645A (ko) 적층 필름 및 그 제조 방법
US5096954A (en) Aqueous coating composition comprising an acrylic resin and a spiroguanamine resin
JP6183176B2 (ja) 積層フィルムおよびその製造方法
WO2014162956A1 (fr) Film de revêtement dur pour moulage
CN105199496A (zh) 涂料组合物
WO2015046472A1 (fr) Film à revêtement dur pour moulage
WO2021075388A1 (fr) Composition de résine thermodurcissable, matériau de revêtement pour impression, produit durci, stratifié et procédé de production de stratifié
TW202206488A (zh) 表面保護塗層劑、硬化物以及層疊物及所述層疊物的製造方法
JP2020055900A (ja) 塗料組成物
US9234114B2 (en) Resin composition for paint and coating film using the same
TW201940565A (zh) 乾式膜抗蝕劑基材用聚酯膜
US11174392B2 (en) Water-based coatings for improved print performance with multiple print technology
CA3118475A1 (fr) Compositions de revetement contenant des polymeres de polyol a fonction acide phosphoreux et revetements formes a partir de celles-ci
JP2004026912A (ja) 絞り加工缶用上塗り外面塗料組成物及び該組成物の利用
KR102583106B1 (ko) 클리어 코트 조성물
US20240014085A1 (en) Chip protective film and method for manufacturing same, and chip
CN116790174B (zh) 一种不含双酚a的涂料组合物及其制备方法
JP5173205B2 (ja) 輝度向上シート用ポリエステルフィルム
WO2024034362A1 (fr) Composition d'agent démoulant, papier antiadhésif dur et film antiadhésif

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 20877636

Country of ref document: EP

Kind code of ref document: A1

ENP Entry into the national phase

Ref document number: 2021552372

Country of ref document: JP

Kind code of ref document: A

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 20877636

Country of ref document: EP

Kind code of ref document: A1