WO2021060876A1 - 아크릴계 점착제 조성물, 편광판 및 디스플레이 장치 - Google Patents

아크릴계 점착제 조성물, 편광판 및 디스플레이 장치 Download PDF

Info

Publication number
WO2021060876A1
WO2021060876A1 PCT/KR2020/012969 KR2020012969W WO2021060876A1 WO 2021060876 A1 WO2021060876 A1 WO 2021060876A1 KR 2020012969 W KR2020012969 W KR 2020012969W WO 2021060876 A1 WO2021060876 A1 WO 2021060876A1
Authority
WO
WIPO (PCT)
Prior art keywords
weight
acrylate
adhesive composition
parts
sensitive adhesive
Prior art date
Application number
PCT/KR2020/012969
Other languages
English (en)
French (fr)
Inventor
이민기
김기영
류동조
Original Assignee
주식회사 엘지화학
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 주식회사 엘지화학 filed Critical 주식회사 엘지화학
Priority to CN202080021462.5A priority Critical patent/CN113597457B/zh
Priority to US17/438,704 priority patent/US11987733B2/en
Priority to EP20869135.2A priority patent/EP3919580B1/en
Publication of WO2021060876A1 publication Critical patent/WO2021060876A1/ko

Abstract

본 발명은, [화학식 1]로 표시되는 단량체, 가교성 관능기를 갖는 (메트)아크릴계 단량체, 및 알킬 (메트)아크릴레이트계 단량체를 포함하는 단량체 혼합물을 중합하여 형성되고, 가지형(branch) 고분자 구조를 갖는 아크릴계 공중합체; 2개 이상의 라디칼 중합성 관능기를 갖는 다관능성 아크릴레이트; 제1광 개시제; 및 제2광 개시제를 포함하고, 상기 제1광 개시제는 아세토페논계 광 개시제이고, 상기 제2광 개시제는 포스핀 옥사이드계 광 개시제인 를 포함하는 아크릴계 점착제 조성물에 관한 것이다.

Description

아크릴계 점착제 조성물, 편광판 및 디스플레이 장치
<관련출원과의 상호 인용>
본 출원은 2019년 9월 27일에 출원된 한국특허출원 제10-2019-0120028호에 기초한 우선권의 이익을 주장하며, 해당 한국특허출원 문헌에 개시된 모든 내용은 본 명세서의 일부로서 포함된다.
<기술분야>
본 발명은 아크릴계 점착제 조성물, 편광판 및 디스플레이 장치에 관한 것으로, 보다 상세하게는 고형분 함량이 높은 경우에도 낮은 점도 특성을 구현할 수 있으며, 점착층 경시 변화가 작고, 재박리 특성 및 내구성이 우수한 아크릴계 점착제 조성물 및 이를 이용하여 제조되는 편광판 및 디스플레이 장치에 관한 것이다.
일반적으로 액정표시장치(Liquid crystal display device, LCD)는 액정을 포함하고 있는 액정셀과 편광판이 구비되며, 액정셀과 편광판을 부착하기 위해 점착층이 사용된다. 이러한 점착층을 형성하는 편광판 부착용 점착제로는 아크릴계 수지, 고무류, 우레탄계 수지, 실리콘계 수지, 또는 EVA(Ethylene Vinyl Acetate) 등이 사용되고 있으며, 이 중에서도 투명성, 산화 저항성 및 황변 저항성이 있는 아크릴계 수지를 베이스로 하는 점착제가 많이 사용되고 있다.
편광판용 아크릴계 점착제의 경우, 내구성 및 경화 효율 향상을 위해서는 중량평균분자량이 높은 아크릴계 수지를 사용하는 것이 바람직하다. 중량평균분자량이 낮은 아크릴계 수지를 사용하면 경화 효율이 저하되어 경화 속도가 느려질 뿐 아니라, 고온 또는 고온/고습 조건 하에서 점착제의 응집력 및 경화도가 떨어져 내구성이 저하되기 때문이다.
그러나, 중량평균분자량의 높은 아크릴계 수지를 사용할 경우, 코팅액의 점도가 상승하여 작업성이 저하된다는 문제점이 있다. 코팅액 내의 고형분 함량을 낮춰 코팅액의 점도를 조절할 수 있으나, 이와 같이 고형분 함량이 낮은 코팅액을 사용하여 점착층을 형성할 경우, 제조비용이 상승하여 생산성이 떨어지고, 점착층의 두께를 정밀하게 제어하기 어렵다는 문제점이 있다.
따라서, 코팅액 점도를 적정 수준으로 유지하면서 고형분 함량을 증가시키기 위한 방법으로, 저분자량체를 혼합하거나, 경화제의 함량을 증가시키는 방법 등이 제안되었다. 그러나, 저분자량체를 혼합하는 방법의 경우, 점착층의 변형이 쉬워 편광판 제조 공정에서 편광판을 롤(roll) 형태로 보관할 경우, 점착층 눌림 변형(pit)이 발생하기 쉽고, 편광판 절단 시에 절단된 면으로부터 점착제가 돌출되는 현상이 발생하고, 이로 인해 편광판이 오염되기 쉽다는 문제점이 있다. 또한, 경화제의 함량을 증가시킬 경우, 액정 패널에 편광판이 부착된 후 일정 시간이 경과하면 점착력이 크게 증가하여 재박리(Rework)가 어렵고, 잔류 경화제의 영향으로 점착 물성의 경시변화가 발생되기 쉽다는 문제점이 있다.
상기와 같은 문제점을 해결하기 위해, 본 발명자들은 동등 수준의 중량평균분자량을 갖는 선형 공중합체에 비해 낮은 점도 특성을 가지형 고분자 구조를 갖는 공중합체를 이용한 점착제 조성물을 개발하였으며, 이에 대한 특허 출원(한국특허출원 제10-2017-0181616호)을 진행한 바 있다. 상기 특허 출원의 점착제 조성물은 종래의 점착제 조성물에 비해서 낮은 점도를 가져 코팅성이 우수하고, 재박리성 및 경시변화 물성도 우수하였다. 다만, 상기 점착제 조성물의 경우, 80℃ 수준의 고온 조건에서는 양호한 내구성을 나타내었으나, 100℃ 이상의 고온 조건에서는 내구성이 떨어지는 것으로 나타났다.
본 발명은 상기와 같은 문제점을 해결하기 위한 것으로, 코팅성 및 재박리성이 우수하고, 점착층 경시 변화가 작으며, 110℃ 이상의 가혹한 조건에서도 우수한 내구성을 갖는 편광판용 아크릴계 점착제 조성물을 제공하고자 한다.
또한, 본 발명은 상기와 같은 아크릴계 점착제 조성물에 의해 형성된 점착층을 포함하는 편광판 및 이를 포함하는 디스플레이 장치를 제공하고자 한다.
일 측면에서, 본 발명은, 하기 [화학식 1]로 표시되는 단량체, 가교성 관능기를 갖는 (메트)아크릴계 단량체, 및 알킬 (메트)아크릴레이트계 단량체를 포함하는 단량체 혼합물을 중합하여 형성되고, 가지형(branch) 고분자 구조를 갖는 아크릴계 공중합체; 2개 이상의 라디칼 중합성 관능기를 갖는 다관능성 아크릴레이트; 아세토페논계 제1광 개시제 및 포스핀 옥사이드계 제2광 개시제를 포함하는 아크릴계 점착제 조성물을 제공한다.
[화학식 1]
R1-CH=CR2-(C=O)-O-X-Y
상기 화학식 1에서, R1은 수소, C1~C6 알킬기 또는 C2~C6 알켄닐기이고, R2는 수소 또는 C1~C10 알킬기이며, X는 단일결합, C1~C10 알킬렌기, C2~C10 알켄닐렌기, 에테르, 에스테르, 또는 이들의 조합이며, Y는 비닐기, 알릴기(allyl), 또는 C3~C10 사이클로알케닐기이다.
다른 측면에서, 본 발명은, 편광 필름; 및 상기 편광 필름의 일면 또는 양면에 형성되고, 상기 본 발명에 따른 아크릴계 점착제 조성물의 경화물을 포함하는 점착층을 포함하는 편광판을 제공한다.
또 다른 측면에서, 본 발명은 상기 본 발명에 따른 편광판을 포함하는 디스플레이 장치를 제공한다.
본 발명에 따른 아크릴계 점착제 조성물은 가지형 구조의 아크릴계 공중합체를 포함하여, 상대적으로 높은 중량평균분자량을 갖는 아크릴계 공중합체를 사용함에도 불구하고, 낮은 점도를 구현할 수 있다. 이에 따라 본 발명에 따른 아크릴계 점착제 조성물을 사용하면, 코팅액 내의 고형분 함량이 35중량% 이상으로 높은 경우에도 낮은 점도를 구현할 수 있어, 점착층 형성 시에 코팅 작업성이 우수하고, 생산성이 높을 뿐 아니라, 점착층 두께를 정밀하게 제어할 수 있다.
또한, 본 발명에 따른 아크릴계 점착제 조성물은 상기 가지형 구조의 아크릴계 공중합체와 함께 다관능성 아크릴레이트와 특정한 2종의 광 개시제 조합을 포함하여, 점착층 형성 시에 추가적인 가교 구조가 견고하게 형성되며, 이로 인해 110℃ 이상의 가혹한 조건에서도 우수한 내구성을 구현할 수 있다.
또한, 본 발명에 따른 아크릴계 점착제 조성물을 이용하여 형성된 점착층을 포함하는 편광판은 가혹한 조건에서도 우수한 내구성을 가지며, 점착 물성의 경시 변화가 적어 품질이 우수하다.
본 명세서 상에서 언급한 '포함한다', '갖는다', '이루어진다' 등이 사용되는 경우 '~만'이 사용되지 않는 이상 다른 부분이 추가될 수 있다. 구성 요소를 단수로 표현한 경우에 특별히 명시적인 기재 사항이 없는 한 복수를 포함하는 경우를 포함한다.
구성 요소를 해석함에 있어서, 별도의 명시적 기재가 없더라도 오차 범위를 포함하는 것으로 해석한다.
본 명세서에 있어서 「(메트)아크릴」은 아크릴 및 메타크릴의 총칭이다. 예를 들면, (메트)아크릴레이트는 메타크릴레이트와 아크릴레이트를 포함하며, (메트)아크릴산은 아크릴산과 메타크릴산을 포함한다.
본 명세서에 있어서, 범위를 나타내는 「X 내지 Y」는 「X 이상 Y 이하」를 의미한다.
본 명세서에 있어서, 「가지형 고분자 구조」는 서로 다른 방향으로 성장된 2개 이상의 긴 사슬을 갖는 고분자 구조를 의미한다.
이하, 본 발명에 대해 구체적으로 설명한다.
점착제 조성물
본 발명에 따른 아크릴계 점착제 조성물은, (1) 가지형(branch) 고분자 구조를 갖는 아크릴계 공중합체, (2) 2개 이상의 라디칼 중합성 관능기를 갖는 다관능성 아크릴레이트, 및 (3) 2종의 광 개시제를 포함한다.
이하, 본 발명의 점착제 조성물의 각 성분에 대하여 구체적으로 설명한다.
(1) 아크릴계 공중합체
본 발명에 따른 아크릴계 점착제 조성물은, 하기 [화학식 1]로 표시되는 단량체, 가교성 관능기를 갖는 (메트)아크릴계 단량체 및 알킬 (메트)아크릴레이트계 단량체를 포함하는 단량체 혼합물을 중합하여 형성되는, 가지형 고분자 구조의 아크릴계 공중합체를 포함한다.
[화학식 1]
R1-CH=CR2-(C=O)-O-X-Y
상기 화학식 1에서, R1은 수소, C1~C6 알킬기 또는 C2~C6 알켄닐기이고, R2는 수소 또는 C1~C10 알킬기이며, X는 단일결합, C1~C10 알킬렌기, C2~C10 알켄닐렌기, 에테르, 에스테르, 또는 이들의 조합이며, Y는 비닐기, 알릴기(allyl), 또는 C3~C10 사이클로알케닐기임.
상기 [화학식 1]로 표시되는 단량체는 가지형 고분자 구조의 아크릴계 공중합체를 형성하기 위한 것이다. 종래에는 편광판용 점착제에 사용되는 아크릴계 공중합체로 단량체들이 하나의 긴 사슬 형태로 중합되어 있는 선형(Linear) 고분자 구조를 가지는 아크릴계 공중합체들이 주로 사용되었다. 그러나, 이와 같은 선형 고분자 구조를 갖는 아크릴계 공중합체들을 사용할 경우, 중량평균분자량이 커질수록 점도도 함께 증가하여 작업성이 떨어진다는 문제점이 있었다.
그러나, 상기 [화학식 1]로 표시되는 단량체를 첨가하여 아크릴계 공중합체를 형성할 경우, 선형이 아닌 가지형 고분자 구조의 공중합체가 제조되는 것으로 밝혀졌다. 구체적으로는, 상기 [화학식 1]의 단량체는 2개 이상의 에틸렌 기를 가지고 있어 자유 라디칼 중합에서 각각 라디칼 형성이 가능하고 서로 다른 방향으로 사슬이 성장할 수 있어, 성장 방향이 상이한 2개 이상의 사슬을 갖는 가지형 고분자가 형성되게 된다. 이와 같은 가지형 고분자 구조를 갖는 아크릴계 공중합체는 동등 수준의 중량평균분자량을 갖는 선형 고분자 구조의 아크릴계 공중합체에 비해 낮은 점도 특성을 가지기 때문에, 코팅액 내의 고형분 함량을 높여도 우수한 코팅성을 구현할 수 있다.
상기 [화학식 1]로 표시되는 단량체의 구체적인 예로는, 알릴 메타크릴레이트(allyl methacrylate), 알릴 아크릴레이트(allyl acrylate), 메트알릴메타크릴레이트(methallyl methacrylate), 메트알릴아크릴레이트(methallyl acrylate), 3-부텐닐 아크릴레이트(3-butenyl acrylate), 부트-3-에닐-2-메틸프로프-2-에노에이트(but-3-enyl-2-methylprop-2-enoate), 2-알릴옥시에틸 아크릴레이트(2-allyloxyethyl acrylate), 2-알릴옥시에틸 메타크릴레이트(2-allyloxyethyl methacrylate), 3-알릴옥시프로필 메타크릴레이트(3-allyloxypropyl methacrylate), 3-알릴옥시프로필 아크릴레이트, 2-알릴옥시에톡시에틸 메타크릴레이트(2-allyloxyethoxyethyl methacrylate), 2-알릴옥시에톡시에틸 아크릴레이트(2-allyloxyethoxyethyl acrylate), 사이클로헥스-2-에닐아크릴레이트(cyclohex-2-enyl acrylate), 사이클로-헥스-2-엔-1-일-2-메틸프로프-2-에노에이트(cyclohex-2-en-1-yl 2-methylprop-2-enoate) 및 3-비닐사이클로헥스-2-에닐 아크릴레이트(3-vinylcyclohex-2-enyl acrylate)로 이루어진 군으로부터 선택된 1종 이상일 수 있으나, 이에 한정되는 것은 아니다.
상기 [화학식 1]로 표시되는 단량체는, 단량체 혼합물 100중량부에 대하여 0.01 내지 1중량부, 바람직하게는 0.05 내지 0.8중량부, 더 바람직하게는 0.1 내지 0.6중량부로 포함될 수 있다. [화학식 1]로 표시되는 단량체의 함량이 0.01 중량부 미만인 경우에는 낮은 점도 특성을 갖는 공중합체의 제조가 어려우며, 1중량부를 초과하는 경우에는 중합 반응 시에 가교 반응이 진행되어 분자량 및 점도 상승을 제어하기 어렵다.
한편, 상기 가교성 관능기를 갖는 (메트)아크릴계 단량체는 점착제의 내구성, 점착력 및 응집력을 향상시키기 위한 것으로, 예를 들면, 히드록시기 함유 단량체, 카르복시기 함유 단량체 또는 질소 함유 단량체 등을 들 수 있으나, 이에 한정되는 것은 아니다. 상기 히드록시기 함유 단량체의 구체적인 예로는, 2-히드록시에틸 (메트)아크릴레이트, 2-히드록시프로필 (메트)아크릴레이트, 4-히드록시부틸 (메트)아크릴레이트, 6-히드록시헥실 (메트)아크릴레이트, 8-히드록시옥틸 (메트)아크릴레이트, 2-히드록시에틸렌글리콜(메트)아크릴레이트 또는 2-히드록시프로필렌글리콜 (메트)아크릴레이트 등을 들 수 있고, 상기 카복실기 함유 단량체의 예로는 (메트)아크릴산, 2-(메트)아크릴로일옥시 아세트산, 3-(메트)아크릴로일옥시 프로필산, 4-(메트)아크릴로일옥시부틸산, 아크릴산이중체, 이타콘산, 말레산 및 말레산무수물 등을 들 수 있으며, 상기 질소 함유 단량체의 예로는 (메트)아크릴아미드, N-비닐 피롤리돈 또는 N-비닐 카프로락탐 등을 들 수 있으나, 이에 한정되는 것은 아니다.
상기 가교성 관능기를 갖는 (메트)아크릴계 단량체는, 단량체 혼합물 100중량부에 대하여 0.1 내지 15중량부, 바람직하게는 1 내지 10중량부, 더 바람직하게는 1 내지 5중량부의 함량으로 포함될 수 있다. 가교성 관능기를 갖는 (메트)아크릴계 단량체의 함량이 상기 범위를 만족할 때, 보다 우수한 점착력 및 내구성을 얻을 수 있다.
다음으로, 상기 알킬 (메트)아크릴레이트계 단량체는 점착성을 부여하기 위한 것으로, 탄소수 2 내지 14의 알킬기를 포함하는 것이 바람직하다. 알킬 (메트)아크릴레이트계 단량체에 포함되는 알킬기가 지나치게 질어지면 점착제의 응집력이 저하되고, 유리전이온도(Tg)나 점착성 조절이 어려워질 수 있기 때문이다. 예를 들면, 상기 알킬 (메트)아크릴레이트계 단량체의 예로는, 에틸 (메트)아크릴레이트, n-프로필 (메트)아크릴레이트, 이소프로필 (메트)아크릴레이트, n-부틸 (메트)아크릴레이트, t-부틸 (메트)아크릴레이트, sec-부틸 (메트)아크릴레이트, 펜틸 (메트)아크릴레이트, 2-에틸헥실 (메트)아크릴레이트, 2-에틸부틸 (메트)아크릴레이트, n-옥틸 (메트)아크릴레이트, 이소옥틸 (메트)아크릴레이트, 이소노닐 (메트)아크릴레이트, 라우릴 (메트)아크릴레이트 및 테트라데실 (메타)아크릴레이트를 들 수 있으며, 본 발명에서는 상기 중 1종 또는 2종 이상의 혼합을 사용할 수 있다.
상기 알킬 (메트)아크릴레이트계 단량체는 단량체 혼합물 100중량부에 대하여, 84 중량부내지 99.89중량부, 바람직하게는 89.2 내지 96.95중량부, 더 바람직하게는 94.4 내지 98.9중량부의 함량으로 포함될 수 있다. 알킬 (메트)아크릴레이트계 단량체의 함량이 상기 범위를 만족할 때, 우수한 점착력 및 내구성을 얻을 수 있다.
일 구체예에 따르면, 상기 (메트)아크릴계 공중합체는, 단량체 혼합물 100중량부에 대하여, 84중량부 내지 99.89중량부의 알킬 (메트)아크릴레이트계 단량체, 0.1 내지 15중량부의 가교성 관능기를 갖는 (메트)아크릴계 단량체 및 0.01 내지 1중량부의 [화학식 1]로 표시되는 단량체를 포함하는 단량체 혼합물을 중합하여 형성되는 것일 수 있다.
본 발명에 따른 아크릴계 공중합체는 상술한 각각의 단량체들을 혼합하여 단량체 혼합물을 제조한 후, 이를 중합함으로써 제조될 수 있다. 이때, 상기 중합방법은 특별히 한정되지 않으며, 당해 기술 분야에 알려져 있는 다양한 중합 방법들, 예를 들면, 용액중합, 광중합, 벌크 중합, 서스펜션 중합 또는 유화 중합 등과 같은 중합법들이 사용될 수 있다. 상기 중합 시에 중합 개시제, 분자량 조절 등을 추가로 첨가될 수 있으며, 각 성분들의 투입 시기는 특별히 한정되지 않는다. 즉, 상기 성분들은 일괄 투입될 수도 있고, 여러 차례 나누어서 분할 투입될 수도 있다.
본 발명에서는, 특히, 용액 중합법을 사용하여 아크릴계 공중합체를 제조할 수 있으며, 용액 중합은 각각의 단량체가 균일하게 혼합된 상태에서 개시제, 분자량 조절제 등을 첨가하여, 50℃ 내지 140℃의 중합 온도로 수행하는 것이 바람직하다.
이 과정에서 사용될 수 있는 개시제의 예로는 아조비스이소부티로니트릴 또는 아조비스시클로헥산카르보니트릴 등과 같은 아조계개시제; 및/또는 과산화 벤조일 또는 과산화 아세틸 등과 같은 과산화물과 같은 통상의 개시제를 들 수 있고, 상기 중 1종 또는 2종 이상의 혼합을 사용할 수 있으나, 이에 제한되는 것은 아니다.
또한, 상기 분자량 조절제로는 t-도데실머캅탄, 또는 n-도데실머캅탄 등의 머캅탄류, 디펜틴, 또는 t-테르펜의테르펜류, 클로로포름, 또는 사염화탄소의 할로겐화 탄화수소, 또는 펜타에리드리톨테트라키스 (3-머캅토프로피온네이트 등을 사용할 수 있으나, 이에 제한되는 것은 아니다.
본 발명에서 사용되는 상기 아크릴계 공중합체는 중량평균분자량이 300,000 내지 1,000,000g/mol, 바람직하게는 400,000 내지 1,000,000g/mol, 더 바람직하게는 500,000 내지 1,000,000g/mol일 수 있다. 아크릴계 공중합체의 중량평균분자량이 300,000g/mol 미만인 경우에는 응집력, 재박리력 및 내구성 등의 물성 저하가 발생할 수 있으며, 1,000,000g/mol을 초과하는 경우에는, 점도 증가로 인해 코팅성이 저하될 수 있다.
(2) 다관능성 아크릴레이트
본 발명에 따른 아크릴계 점착제 조성물은, 상기 아크릴계 공중합체와 함께 다관능성 아크릴레이트를 포함한다. 상기 다관능성 아크릴레이트는 점착층 경화 시에 가교 구조를 형성함으로써 점착층의 고온 내구성을 개선하기 위한 것으로, 2개 이상의 라디칼 중합성 관능기를 갖는 아크릴레이트이다.
본 발명에서 사용될 수 있는 다관능성 아크릴레이트는, 예를 들면, 1,4-부탄디올 디(메타)아크릴레이트, 1,6-헥산디올 디(메타)아크릴레이트, 네오펜틸글리콜 디(메타)아크릴레이트, 폴리에틸렌글리콜 디(메타)아크릴레이트, 네오펜틸글리콜아디페이트(neopentylglycol adipate) 디(메타)아크릴레이트, 히드록시피발산(hydroxyl puivalic acid) 네오펜틸글리콜 디(메타)아크릴레이트, 디시클로펜타닐(dicyclopentanyl) 디(메타)아크릴레이트, 카프로락톤 변성 디시클로펜테닐 디(메타)아크릴레이트, 에틸렌옥시드 변성 디(메타)아크릴레이트, 디(메타)아크릴록시 에틸 이소시아누레이트, 알릴(allyl)화 시클로헥실 디(메타)아크릴레이트, 트리시클로데칸디메탄올(메타)아크릴레이트, 디메틸롤 디시클로펜탄 디(메타)아크릴레이트, 에틸렌옥시드 변성 헥사히드로프탈산 디(메타)아크릴레이트, 트리시클로데칸 디메탄올(메타)아크릴레이트, 네오펜틸글리콜 변성 트리메틸프로판 디(메타)아크릴레이트, 아다만탄(adamantane) 디(메타)아크릴레이트 또는 9,9-비스[4-(2-아크릴로일옥시에톡시)페닐]플루오렌(fluorine) 등과 같은 2관능성 아크릴레이트; 트리메틸롤프로판 트리(메타)아크릴레이트, 디펜타에리쓰리톨 트리(메타)아크릴레이트, 프로피온산 변성 디펜타에리쓰리톨 트리(메타)아크릴레이트, 펜타에리쓰리톨 트리(메타)아크릴레이트, 프로필렌옥시드 변성 트리메틸롤프로판 트리(메타)아크릴레이트, 3 관능형 우레탄 (메타)아크릴레이트 또는 트리스(메타)아크릴로일록시에틸이소시아누레이트 등의 3관능형 아크릴레이트; 디글리세린 테트라(메타)아크릴레이트 또는 펜타에리쓰리톨 테트라(메타)아크릴레이트 등의 4관능형 아크릴레이트; 프로피온산 변성 디펜타에리쓰리톨 펜타(메타)아크릴레이트 등의 5관능형 아크릴레이트; 및 디펜타에리쓰리톨 헥사(메타)아크릴레이트, 카프로락톤 변성 디펜타에리쓰리톨 헥사(메타)아크릴레이트 또는 우레탄 (메타)아크릴레이트(ex. 이소시아네이트 단량체 및 트리메틸롤프로판 트리(메타)아크릴레이트의 반응물 등의 6관능형 아크릴레이트) 등을 들 수 있으나, 이에 제한되는 것은 아니다.
본 발명에서는 상기와 같은 다관능성 아크릴레이트 중 1종 또는 2종 이상을 혼합하여 사용할 수 있으며, 특히 분자량이 1,000g/mol 미만이며, 3관능성 이상인 아크릴레이트를 사용하는 것이 보다 탁월한 내구성 구현 측면에서 바람직하나, 이에 제한되는 것은 아니다.
또한, 상기 다관능성 아크릴레이트로서, 분자 내에 고리 구조 또는 우레탄 결합을 포함하는 아크릴레이트, 바람직하게는 분자 내에 고리 구조 및 우레탄 결합을 포함하는 아크릴레이트를 사용할 수도 있다. 이와 같은 아크릴레이트를 사용할 경우, 점착제를 보다 하드(hard)한 상태로 형성함과 동시에 점착력 저하를 억제할 수 있고, 이에 따라 빛샘 억제 효과 및 내구성을 추가적으로 증진시킬 수 있다. 상기에서, 아크릴레이트에 포함될 수 있는 고리 구조는 탄소환식 구조 또는 복소환식 구조; 또는 단환식 또는 다환식 구조의 어느 것이어도 된다.
상기와 같은 다관능성 아크릴레이트의 구체적인 예로는, 트리스(메타)아크릴로일록시에틸 이소시아누레이트 등의 이소시아누레이트계 아크릴레이트; 분자 말단 등에 이소시아네이트기를 가지는 화합물, 바람직하게는 분자 내에 고리 구조를 포함하고, 이소시아네이트기를 가지는 화합물(ex. 이소보론 디이소시아네이트)에, 히드록시기 및 아크릴로일(acryloyl)기를 가지는 화합물(ex. 펜타에리스리톨 트리(메타)아크릴레이트 등)을 부가시킨 부가물 등을 들 수 있으나, 이에 제한되는 것은 아니다.
본 발명의 점착제 조성물에서 상기 다관능성 아크릴레이트는, 아크릴계 수지 100 중량부에 대하여, 1 중량부 이상 20 중량부 미만, 바람직하게는 5 내지 15중량부의 함량으로 포함될 수 있다. 다관능성 아크릴레이트의 함량이 1 중량부 미만이면, 내구성 증가 효과가 미미하고, 20 중량부 이상이면 고온 내구성이 오히려 저하될 수 있다.
(3) 광 개시제
본 발명에 따른 점착제 조성물은 상기 다관능성 아크릴레이트를 중합시켜 가교 구조를 형성하기 위한 2종의 광 개시제를 포함한다. 구체적으로는, 상기 광 개시제는 아세토페논계 광 개시제인 제1광 개시제와, 포스핀 옥사이드계 광 개시제인 제2광개시제를 포함한다.
구체적으로는, 상기 제1광개시제는, 예를 들면, 아세토페논, 디메틸아니노 아세토페논, 2,2-디메톡시-2-페닐아세토페논, 2,2-디에톡시-2-페닐아세토페논 등일 수 있다. 이 중에서도 2,2-디메톡시-2-페닐아세토페논은 점착 물성의 경시 변화 및 변색에 대한 우려가 없어 특히 바람직하다.
또한, 상기 제2광개시제는, 예를 들면, 비스(2,4,6-트리메틸벤조일)-4-메틸페닐포스핀 옥사이드, 비스(2,4,6-트리메틸벤조일)-2,5-디이소프로필페닐포스핀 옥사이드, 비스(2,4,6-트리메틸벤조일)-2-메틸페닐포스핀 옥사이드, 비스(2,4,6-트리메틸벤조일)-4-메틸페닐포스핀 옥사이드, 비스(2,4,6-트리메틸벤조일)-2,5-디에틸페닐포스핀 옥사이드, 비스(2,4,6-트리메틸벤조일)-2,3,5,6-테트라메틸페닐포스핀 옥사이드, 2,4,6-트리메틸벤조일-디페닐 포스핀 옥사이드, 비스(2,4,6-트리메틸벤조일)-페닐포스핀 옥사이드 등일 수 있다. 이 중에서도 2,4,6-트리메틸벤조일-디페닐 포스핀 옥사이드는 점착 물성의 경시 변화 및 변색에 대한 우려가 없으며, 360nm~400nm의 장파장의 UV파장 흡수가 가능하여 점착층 내부 경화가 가능하다는 점에서 특히 바람직하다.
본 발명자들의 연구에 따르면, 점착제 조성물에 다관능성 아크릴레이트와 아세토페논계 광 개시제 및 포스핀 옥사이드계 광 개시제를 첨가할 경우, 110℃ 이상에서 고온 내구성이 현저하게 개선되는 것으로 나타났다. 아세토페논계 광 개시제의 경우, 300 ~ 320nm 대역의 광 흡수능이 다소 부족하고, 포스핀 옥사이드계 광 개시제의 경우, 330 ~ 350nm 대역의 광 흡수능이 다소 부족하다. 그러나, 본 발명과 같이, 아세토페논계 광 개시제 및 포스핀 옥사이드계 광 개시제을 함께 사용하면, 파장 흡수에 대한 상호 보완이 이루어져 UV A 영역(315~400nm), UV B 영역(280nm ~ 315nm) 및 UV C영역(200nm ~ 280nm)의 모든 파장을 폭넓게 흡수할 수 있어 경화 효율이 증가하고 이로 인해 점착층의 내부 및 외부의 가교 구조가 균일하고 견고하게 형성되며, 이로 인해 고온 내구성이 현저하게 증가하게 된다. 이에 비해, 다관능성 아크릴레이트와 한 종류의 광 개시제만 사용할 경우나, 2종의 광 개시제를 사용하더라도 아세톤페논계 광 개시제와 포스핀옥사이드계 광 개시제의 조합이 아닌 다른 광 개시제 조합을 사용할 경우, 110℃ 이상에서 고온 내구성을 만족시키지 못하였다. 본 발명의 점착제 조성물에서 상기 제1광 개시제는 상기 아크릴계 공중합체 100중량부에 대하여 1.0 내지 5.0중량부, 바람직하게는 1.0 내지 3.0중량부, 더 바람직하게는 1.0 내지 2.0중량부의 함량으로 포함될 수 있으며, 상기 제2광 개시제는 상기 아크릴계 공중합체 100중량부에 대하여 0.01 내지 1중량부, 바람직하게는 0.01 내지 0.7중량부, 더 바람직하게는 0.1 내지 0.5중량부의 함량으로 포함될 수 있다. 제1광개시제의 함량이 상기 범위를 벗어나면, 다관능 아크릴레이트와의 반응이 원활히 이루어지지 않거나, 반응 후 잔존 성분으로 인해 점착제 물성이 악화될 우려가 있으며, 제2광개시제의 함량이 0.01 중량부 미만이면 고온 내구성 증가 효과가 미미하고, 1 중량부를 초과하면 고온 내구성이 오히려 저하될 수 있다.
(4) 다관능성 가교제
본 발명의 점착제 조성물은 상기 성분들 이외에 다관능성 가교제를 더 포함할 수 있다.
상기 다관능성 가교제는 아크릴계 공중합체와 반응하여 가교 구조를 형성함으로써 점착층의 내구성을 보다 향상시키기 위한 것으로, 예를 들면, 이소시아네이트계 가교제가 사용될 수 있다. 상기 이소시아네이트계 가교제로는 당해 기술 분야에 알려진 통상의 것을 사용할 수 있으며, 예를 들면, 톨루엔디이소시아네이트, 2,4-트릴렌 디이소시아네이트, 2,6-트릴렌 디이소시아네이트, 수소화 트릴렌디이소시아네이트, 이소포름디이소시아네이트, 1,3-크실렌 디이소시아네이트, 1,4-크실렌 디이소시아네이트, 디페닐메탄-4,4-디이소시아네이트, 1,3-비스이소시아나토메틸 시클로헥산, 테트라메틸크실렌디이소시아네이트, 1,5-나프탈렌 디이소시아네이트, 헥사메틸렌디이소시아네이트, 2,2,4-트리메틸 헥사메틸렌디이소시아네이트, 2,4,4-트리메틸 헥사메틸렌디이소시아네이트, 트리메틸올프로판 변성 톨루엔디이소시아네이트, 트리메틸올프로판 변성 톨릴렌디이소시아네이트, 트리메틸올프로판의트릴렌디이소시아네이트어덕트, 트리메틸올프로판의크실렌디오소시아네이트어덕트, 토리페닐메탄토리이소시아네이트, 메틸렌비스 트리 이소시아네이트, 이들의 폴리올(트리메틸올프로판) 및 이들의 혼합물 등을 사용할 수 있다.
상기 다관능성 가교제는 아크릴계 공중합체 100중량부에 대하여 0.01 내지 5중량부, 바람직하게는 0.01 내지 3중량부, 더 바람직하게는 0.1 내지 1중량부로 포함되는 것이 바람직하다. 다관능성 가교제의 함량이 상기 범위를 만족할 경우, 점착성 등의 물성 저하 없이 우수한 내구성을 얻을 수 있다.
(5) 기타 성분
본 발명의 점착제 조성물은, 물성 조절을 위해 상술한 성분들 이외에, 용매, 실란 커플링제, 점착성 부여 수지, 첨가제 등과 다른 성분들을 더 포함할 수 있다.
본 발명의 점착제 조성물은, 점도 조절을 위한 용매를 더 포함할 수 있다. 이때 상기 용매는, 예를 들면, 에틸 아세테이트, n-펜탄, 이소펜탄, 네오펜탄, n-헥산, n-옥탄, n-헵탄, 메틸에틸케톤, 아세톤, 톨루엔 또는 이들의 조합을 들 수 있으나, 이에 한정되는 것은 아니다. 상기 용매는 점착제 조성물 내의 고형분 함량이 30중량% 이상, 바람직하게는 30 내지 60중량%가 되도록 하는 양으로 포함될 수 있다.
또한, 본 발명의 점착제 조성물은 실란 커플링제를 추가로 포함할 수 있다. 실란 커플링제는 점착제와 유리 기판 사이의 밀착성 및 접착 안정성을 향상시켜, 내열성 및 내습성을 개선하고, 또한 고온 및/또는 고습 조건 하에서 점착제가 장기간 방치되었을 경우에 접착 신뢰성을 향상시키는 작용을 한다. 본 발명에서 사용될 수 있는 커플링제의 예로는, γ-글리시독시프로필트리에톡시실란, γ-글리시독시프로필트리메톡시실란, γ-글리시독시프로필메틸디에톡시실란, γ-글리시독시프로필트리에톡시실란, 3-머캅토프로필 트리메톡시실란, 비닐트리메톡시실란, 비닐트리에톡시실란, γ-메타크릴록시프로필트리메톡시실란, γ-메타크릴록시프로필트리에톡시실란, γ-아미노프로필트리메톡시실란, γ-아미노프로필트리에톡시실란, 3-이소시아네이토 프로필 트리에톡시실란, γ-아세토아세테이트프로필트리메톡시실란, γ-아세토아세테이트프로필트리에톡시실란, β-시아노아세틸트리메톡시실란, β-시아노아세틸트리에톡시실란, 아세톡시아세토트리메톡시실란을 들 수 있으며, 상기 중 1종 또는 2종 이상의 혼합을 사용할 수 있다. 본 발명에서는 아세토아세테이트기 또는 β-시아노아세틸기를 갖는 실란 커플링제를 사용하는 것이 바람직하지만, 이에 제한되는 것은 아니다.
본 발명의 조성물에서 실란 커플링제는 아크릴계 공중합체 100 중량부에 대하여 0.01 중량부 내지 5 중량부, 바람직하게는 0.01 중량부 내지 1 중량부의 양으로 포함될 수 있다. 커플링제의 함량이 0.01 중량부 미만이면, 점착력 증가 효과가 미미하며, 5 중량부를 초과하면, 내구성이 저하될 우려가 있다.
본 발명의 점착제 조성물은 또한, 점착 성능의 조절의 관점에서, 아크릴계 공중합체 100 중량부에 대하여 1 중량부 내지 100 중량부의 점착성 부여 수지를 추가로 포함할 수 있다. 이와 같은 점착성 부여 수지의 종류는 특별히 한정되지 않으며, 예를 들면 (수첨) 히드로카본계 수지, (수첨) 로진 수지, (수첨) 로진에스테르 수지, (수첨)테르펜 수지, (수첨) 테르펜 페놀 수지, 중합 로진 수지 또는 중합 로진에스테르 수지 등의 일종 또는 이종 이상의 혼합물을 사용할 수 있다. 상기 점착성 부여 수지의 함량이 1 중량부보다 작으면, 첨가 효과가 미미할 우려가 있고, 100 중량부를 초과하면, 상용성 및/또는 응집력 향상 효과가 저하될 우려가 있다.
본 발명의 점착제 조성물은 또한, 발명의 효과에 영향을 미치지 않는 범위에서, 에폭시 수지, 대전 방지제, 자외선 안정제, 산화 방지제, 조색제, 보강제, 충진제, 소포제, 계면 활성제 및 가소제로 이루어진 군으로부터 선택된 하나 이상의 첨가제를 추가로 포함할 수 있다.
상기와 같은 성분들을 포함하는 본 발명에 따른 점착제 조성물은, 동일 수준의 중량평균분자량을 갖는 선형 고분자 구조의 아크릴계 공중합체를 사용하는 종래의 점착제 조성물에 비해 낮은 점도 특성을 갖는다. 이에 따라, 점착제 조성물 내의 고형분 함량이 높은 경우에도 우수한 코팅성을 구현할 수 있다.
구체적으로는, 본 발명에 따른 점착제 조성물은 고형분 함량이 35중량% 이상, 예를 들면 35중량% 내지 60중량%인 경우에도 23℃에서의 점도가 2,000cP 이하, 바람직하게는 500cP 내지 2,000cP 정도로 낮게 나타난다. 이때, 상기 고형분 함량은 본 발명의 점착제 조성물이 코팅액 등의 형태로 제조되어, 점착제의 제조 과정에 적용되는 시점에서의 고형분 함량을 의미할 수 있다. 이와 같이, 본 발명의 점착제 조성물을 사용하면, 코팅성 저하 없이 코팅액 내에서의 고형분 함량을 높일 수 있어, 생산성이 우수할 뿐 아니라, 두께 등의 정밀 제어가 가능하다.
또한, 본 발명에 따른 점착제 조성물은 다관능성 아크릴레이트 및 2종의 광 개시제를 포함하여, 점착층 경화 시에 견고한 가교 구조가 형성되며, 이로 인해 110℃ 이상의 가혹한 고온 조건에서도 우수한 내구성을 나타낸다.
편광판
다음으로, 본 발명에 따른 편광판에 대해 설명한다.
본 발명에 따른 편광판은, 편광 필름; 및 상기 편광 필름의 일면 또는 양면에 형성되고, 전술한 본 발명에 따른 점착제 조성물의 경화물을 함유하는 점착층을 포함한다.
본 발명에서 사용하는 편광 필름의 종류는 특별히 제한되지 않으며, 이 분야에서 공지된 일반적인 종류를 채용할 수 있다. 예를 들면, 상기 편광 필름은, 편광자; 및 상기 편광자의 일면 또는 양면에 형성된 보호 필름을 포함할 수 있다.
본 발명의 편광판에 포함되는 편광자의 종류는 특별히 제한되지 않으며, 예를 들면, 폴리비닐알코올계 편광자 등과 같이 이 분야에서 공지되어 있는 일반적인 종류를 제한 없이 채용할 수 있다.
편광자는 여러 방향으로 진동하면서 입사되는 빛으로부터 한쪽 방향으로 진동하는 빛만을 추출할 수 있는 기능성 필름 또는 시트이다. 이와 같은 편광자는, 예를 들면, 폴리비닐알코올계 수지 필름에 이색성 색소가 흡착 배향되어 있는 형태일 수 있다. 편광자를 구성하는 폴리비닐알코올계 수지는, 예를 들면, 폴리비닐아세테이트계 수지를 겔화하여 얻을 수 있다. 이 경우, 사용될 수 있는 폴리비닐아세테이트계 수지에는, 비닐 아세테이트의 단독 중합체는 물론, 비닐 아세테이트 및 상기와 공중합 가능한 다른 단량체의 공중합체도 포함될 수 있다. 상기에서 비닐 아세테이트와 공중합 가능한 단량체의 예에는, 불포화 카르본산류, 올레핀류, 비닐에테르류, 불포화 술폰산류 및 암모늄기를 가지는 아크릴아미드류 등의 일종 또는 이종 이상의 혼합을 들 수 있으나, 이에 제한되는 것은 아니다. 폴리비닐알코올계 수지의 겔화도는, 통상 85몰% 내지 100몰% 정도, 바람직하게는 98몰% 이상일 수 있다. 상기 폴리비닐알코올계 수지는 추가로 변성되어 있을 수도 있으며, 예를 들면, 알데히드류로 변성된 폴리비닐포르말 또는 폴리비닐아세탈 등도 사용될 수 있다. 또한 폴리비닐알코올계 수지의 중합도는, 통상 1,000 내지 10,000 정도, 바람직하게는 1,500 내지 5,000 정도일 수 있다.
상기와 같은 폴리비닐알코올계 수지를 제막하여, 편광자의 원반 필름으로서 사용할 수 있다. 폴리비닐알코올계 수지를 제막하는 방법은 특별히 한정되지 않으며, 이 분야에서 공지되어 있는 일반적인 방법을 사용할 수 있다.
폴리비닐알코올계 수지로 제막된 원반 필름의 두께는 특별히 제한되지 않으며, 예를 들면 1 ㎛ 내지 150 ㎛의 범위 내에서 적절히 제어될 수 있다. 연신의 용이성 등을 고려하여, 상기 원반 필름의 두께는 10 ㎛ 이상으로 제어될 수 있다.
편광자는 상기와 같은 폴리비닐알코올계 수지 필름을 연신(ex. 일축 연신)하는 공정, 폴리비닐알코올계 수지 필름을 이색성 색소로 염색하고, 그 이색성 색소를 흡착시키는 공정, 이색성 색소가 흡착된 폴리비닐알코올계 수지 필름을 붕산(boric acid) 수용액으로 처리하는 공정 및 붕산 수용액으로 처리 후에 수세하는 공정 등을 거쳐 제조할 수 있다. 상기에서 이색성 색소로서는, 요오드(iodine)나 이색성의 유기염료 등이 사용될 수 있다.
본 발명의 편광 필름은, 또한, 상기 편광자의 일면 또는 양면에 형성된 보호 필름을 추가로 포함할 수 있다. 본 발명의 편광판에 포함될 수 있는 보호 필름의 종류는 특별히 제한되지 않으며, 예를 들면, 트리아세틸 셀룰로오스와 같은 셀룰로오스계 필름; 폴리카보네이트 필름 또는 폴리에틸렌테레프탈레이트 필름과 같은 폴리에스테르계 필름; 폴리에테르설폰계 필름; 및/또는 폴리에틸렌 필름, 폴리프로필렌 필름 또는 시클로계나노르보르넨 구조를 갖는 폴리올레핀 필름 또는 에틸렌 프로필렌 공중합체와 같은 폴리올레핀계 필름 등으로 구성되는 보호 필름이 적층된 다층 필름으로 형성될 수 있다. 이때 상기 보호 필름의 두께 역시 특별히 제한되지 않으며, 통상적인 두께로 형성할 수 있다.
한편, 본 발명에서 편광 필름에 점착층을 형성하는 방법은 특별히 제한되지 않으며, 예를 들면, 상기 필름 또는 소자에 바코터 등의 통상의 수단으로 점착제 조성물(코팅액)을 도포하고 경화시키는 방법, 또는 점착제 조성물을 일단 박리성 기재의 표면에 도포하고 경화시킨 후에, 형성된 점착층을 편광 필름 또는 소자의 표면에 전사는 방법 등을 사용할 수 있다.
본 발명에서 점착층의 형성 과정은, 또한, 점착제 조성물(코팅액) 내부의 휘발 성분 또는 반응 잔류물과 같은 기포 유발 성분을 충분히 제거한 후, 수행하는 것이 바람직하다. 이에 따라 점착제의 가교 밀도 또는 분자량 등이 지나치게 낮아 탄성률이 떨어지고, 고온 상태에서 유리판 및 점착층 사이에 존재하는 기포들이 커져 내부에서 산란체를 형성하는 문제점 등을 방지할 수 있다.
한편, 상기 편광판의 제조 시에 본 발명의 점착제 조성물을 경화시키는 방법 역시 특별히 한정되지 않으며, 당해 기술 분야에 알려져 있는 통상의 경화 방법을 통해 수행될 수 있다. 예를 들면, 상기 경화는, 가열 등을 통해 도포된 점착제 조성물 내의 가교성 관능기와 다관능성 가교제 사이에 가교 반응이 유발될 수 있는 온도로 유지시키는 방법으로 수행될 수 있다.
본 발명의 편광판은 또한 보호층, 반사층, 방현층, 위상차판, 광시야각 보상 필름 및 휘도 향상 필름으로 이루어진 군으로부터 선택된 하나 이상의 기능성층을 추가로 포함할 수 있다.
상기와 같은 본 발명에 따른 편광판은 점착층의 경시 변화가 적고, 고온 또는 고온/고습 조건 하에서도 내구성이 우수하며, 재박리성(rework)이 우수하다.
디스플레이 장치
다음으로, 본 발명의 디스플레이 장치에 대해 설명한다.
본 발명의 디스플레이 장치는 상기한 본 발명에 따른 편광판을 포함한다.
보다 구체적으로는, 상기 디스플레이 장치는 발명에 따른 편광판이 일면 또는 양면에 접합되어 있는 액정 패널을 포함하는 액정표시장치일 수 있다. 이때, 상기 액정 패널의 종류는 특별히 한정되지 않는다. 본 발명에서는, 예를 들면, 그 종류에 제한되지 않고, TN(Twisted Neumatic)형, STN(Super Twisted Neumatic)형, F(ferroelectric)형 및 PD(polymer dispersed LCD)형 등을 포함한 F 각종 수동행렬 방식; 2단자형(two terminal) 및 3단자형(three terminal)을 포함한 각종 능동행렬 방식; 횡전계형(IPS mode) 패널 및 수직배향형(VA mode) 패널을 포함한 공지의 액정 패널이 모두 적용될 수 있다. 또한, 본 발명의 액정표시장치에 포함되는 그 외의 기타 구성의 종류 및 그 제조 방법도 특별히 한정되지 않으며, 이 분야의 일반적인 구성을 제한 없이 채용하여 사용할 수 있다.
이하, 구체적인 실시예를 통해 본 발명을 보다 자세히 설명한다.
제조예 1: 아크릴계 공중합체(A1) 제조
질소 가스가 환류되고, 온도 조절이 용이하도록 냉각장치를 설치한 3L 반응기에 부틸 아크릴레이트(BA) 97.2중량부 및 히드록시에틸아크릴레이트(HEA) 2.5 중량부, 알릴 메타크릴레이트(AMA) 0.18중량부를 포함하는 단량체 혼합물을 투입하고, 용제로 에틸 아세테이트(EAc) 60중량부를 투입하였다. 이어서, 산소 제거를 위하여 질소 가스를 60분 동안 퍼징(purging)한 후, 온도를 70℃로 유지하였다. 그런 다음, 분자량 조절제로 n-도데실머캅탄(n-DDM) 0.23중량부, 중합개시제로 아조비스(2-4-디메틸발레로니트릴(V-65, 제조사: Wako) 0.15중량부, 알릴 메타크릴레이트(AMA) 0.12중량부를 추가로 투입하면서 10시간동안 반응시켜 아크릴계 공중합체(A1)을 제조하였다. 이때, 상기 알릴 메타크릴레이트는 반응 시간 3시간 후에 투입하였으며, 상기 분자량 조절제는 반응시간 5시간까지 5회로 나누어 투입하였으며, 중합개시제는 발열 정도를 확인하면서 반응 시간 7시간까지 10회에 나누어 투입하였다.
제조예 2: 아크릴계 공중합체 (A2) 제조
질소 가스가 환류되고, 온도 조절이 용이하도록 냉각장치를 설치한 3L 반응기에 부틸 아크릴레이트(BA) 97.0중량부 및 히드록시에틸아크릴레이트(HEA) 2.5 중량부, 알릴 메타크릴레이트(AMA) 0.3 중량부를 포함하는 단량체 혼합물을 투입하고, 용제로 에틸 아세테이트(EAc) 60중량부를 투입하였다. 이어서, 산소 제거를 위하여 질소 가스를 60분 동안 퍼징(purging)한 후, 온도를 70℃로 유지하였다. 그런 다음, 분자량 조절제로 n-도데실머캅탄(n-DDM) 0.185중량부, 중합개시제로 아조비스(2-4-디메틸발레로니트릴(V-65, 제조사: Wako) 0.15중량부, 알릴 메타크릴레이트(AMA) 0.2중량부를 추가로 투입하면서 10시간 동안 반응시켜 아크릴계 공중합체(A2)를 제조하였다. 이때, 상기 알릴 메타크릴레이트는 반응 시간 3시간 후에 투입하였으며, 상기 분자량 조절제는 반응시간 5시간까지 5회로 나누어 투입하였으며, 중합개시제는 발열 정도를 확인하면서 반응 시간 7시간까지 10회에 나누어 투입하였다.
제조예 3: 아크릴계 공중합체 (B1) 제조
질소 가스가 환류되고, 온도 조절이 용이하도록 냉각장치를 설치한 3L 반응기에 부틸 아크릴레이트(BA) 97.5중량부 및 히드록시에틸아크릴레이트(HEA) 2.5 중량부를 포함하는 단량체 혼합물을 투입하고, 용제로 에틸 아세테이트(EAc) 60중량부를 투입하였다. 이어서, 산소 제거를 위하여 질소 가스를 60분 동안 퍼징(purging)한 후, 온도를 70℃로 유지하였다. 그런 다음, 분자량 조절제로 n-도데실머캅탄(n-DDM) 0.147중량부, 중합개시제로 아조비스(2-4-디메틸발레로니트릴(V-65, 제조사: Wako) 0.15중량부를 추가로 투입하고 10시간동안 반응시켜 아크릴계 공중합체(B1)을 제조하였다.
제조예 4: 아크릴계 공중합체 (B2) 제조
질소 가스가 환류되고, 온도 조절이 용이하도록 냉각장치를 설치한 3L 반응기에 부틸 아크릴레이트(BA) 97.5중량부 및 히드록시에틸아크릴레이트(HEA) 2.5 중량부를 포함하는 단량체 혼합물을 투입하고, 용제로 에틸 아세테이트(EAc) 60중량부를 투입하였다. 이어서, 산소 제거를 위하여 질소 가스를 60분 동안 퍼징(purging)한 후, 온도를 70℃로 유지하였다. 그런 다음, 분자량 조절제로 n-도데실머캅탄(n-DDM) 0.112중량부, 중합개시제로 아조비스(2-4-디메틸발레로니트릴(V-65, 제조사: Wako) 0.15중량부를 추가로 투입하고 10시간 동안 반응시켜 아크릴계 공중합체(B2)를 제조하였다.
상기 제조예 1 ~ 4에 의해 제조된 아크릴계 공중합체의 중량평균분자량 및 고분자 구조를 하기와 같이 측정하여 표 1에 나타내었다.
(1) 중량평균분자량은 GPC를 이용하여 하기 조건으로 측정하였다. 검량선 제작에 Agilent system의 표준 폴리스티렌을 사용하여 측정결과를 환산하였다.
<측정 조건>
측정기: Agilent GPC(Agulent 1200 series, 미국)
컬럼: PL Mixed B 2개 연결
컬럼 온도: 40℃
용리액: 테트로하이드로퓨란
유속: 1.0mL/min
농도: ~ 1mg/mL(100μL injection)
(2) 고분자 구조는 하기와 같은 방법으로 평가하였다.
먼저, 고분자 구조를 평가하고자 하는 아크릴계 공중합체(이하, '평가 대상 공중합체'라 함)에서 사용된 것과 동일한 종류의 알킬(메트)아크릴레이트계 단량체 및 가교성 관능기를 갖는 (메트)아크릴계 단량체를 혼합하여 단량체 혼합물을 제조하였다. 이때, 상기 단량체 혼합물 내의 가교성 관능기를 갖는 (메트)아크릴계 단량체의 함량이 평가 대상 공중합체 내의 가교성 관능기를 갖는 (메트)아크릴계 단량체의 함량과 동일하게 되도록 하였다. 그런 다음, 상기 단량체 혼합물을 중합하여 평가 대상 공중합체와 동등 수준의 중량평균 분자량(오차범위 ±5%)을 갖는 아크릴계 공중합체(이하, '기준 공중합체'라 함)를 제조하였다.
이후, 상기 기준 공중합체와 평가 대상 공중합체 각각에 에틸 아세테이트 용매를 첨가하여 고형분 농도가 30중량%가 되도록 조절한 후, 점도를 측정하였다. 상기와 같이 측정된 평가 대상 공중합체의 점도가 기준 공중합체의 점도보다 30% 이상 낮은 점도를 갖는 경우에는 가지형 고분자 구조를 갖는 것으로 평가하고, 그 이외의 경우에는 선형 고분자 구조를 갖는 것으로 평가하였다.
Figure PCTKR2020012969-appb-T000001
실시예 1
제조예 1에 의해 제조된 아크릴계 공중합체 A1 100중량부, 다관능성 아크릴레이트(트리스(메타)아크릴로일록시에틸 이소시아누레이트) 15중량부, 2,2-디메톡시-2-페닐아세토페논(광개시제 1, 상품명: Omnirad BDK, 제조사: IGM Resins社) 1.5중량부, 디페닐(2,4,6-트리메틸벤조일)포스핀 옥사이드(광개시제 2, 상품명: Omnirad TPO, 제조사: IGM Resins社) 0.35중량부, 다관능성 가교제(coronate L, 니폰폴리우레탄사제) 0.2 중량부, 실란커플링제(베타-시아노아세틸기 함유 실란커플링제, LG화학, M812) 0.2중량부를 배합하고, 고형분 함량이 57.2중량%가 되도록 에틸 아세테이트로 희석한 후, 균일하게 혼합하여 점착제 조성물(코팅액)을 제조하였다.
제조된 점착제 조성물을 이형처리된 38㎛의 두께의 폴리에틸렌테레프탈레이트 필름(이형 PET)의 이형 처리면에, 건조 후의 두께가 23 ㎛가 되도록 도포한 후 건조시켜 점착성 코팅층을 형성하였다. 그 후, 점착성 코팅층을 편광판에 라미네이트하여 점착층을 포함하는 편광판을 제조하였다.
실시예 2
제조예 2에 의해 제조된 아크릴계 공중합체 A2 100중량부, 다관능성 아크릴레이트(트리스(메타)아크릴로일록시에틸 이소시아누레이트) 8중량부, 2-디메톡시-2-페닐아세토페논(광 개시제 1) 1.5중량부, 디페닐(2,4,6-트리메틸벤조일)포스핀 옥사이드(광 개시제 2) 0.1중량부, 다관능성 가교제(coronate L, 니폰폴리우레탄사제) 0.2 중량부, 실란커플링제(베타-시아노아세틸기 함유 실란커플링제, LG화학, M812) 0.2중량부를 배합하고, 고형분 함량이 35.0중량%가 되도록 에틸 아세테이트로 희석한 후, 균일하게 혼합하여 점착제 조성물(코팅액)을 제조하였다.
제조된 점착제 조성물을 이형처리된 38㎛의 두께의 폴리에틸렌테레프탈레이트 필름(이형 PET)의 이형 처리면에, 건조 후의 두께가 23 ㎛가 되도록 도포한 후 건조시켜 점착성 코팅층을 형성하였다. 그 후, 점착성 코팅층을 편광판에 라미네이트하여 점착층을 포함하는 편광판을 제조하였다.
실시예 3
제조예 2에 의해 제조된 아크릴계 공중합체 A2 100중량부, 다관능성 아크릴레이트(트리스(메타)아크릴로일록시에틸 이소시아누레이트) 5중량부, 2,2-디메톡시-2-페닐아세토페논(광 개시제 1) 1.5중량부, 디페닐(2,4,6-트리메틸벤조일)포스핀 옥사이드(광 개시제 2) 0.2중량부, 다관능성 가교제(coronate L, 니폰폴리우레탄사제) 0.2 중량부, 실란커플링제(베타-시아노아세틸기 함유 실란커플링제, LG화학, M812) 0.2중량부를 배합하고, 고형분 함량이 35.1중량%가 되도록 에틸 아세테이트로 희석한 후, 균일하게 혼합하여 점착제 조성물(코팅액)을 제조하였다.
제조된 점착제 조성물을 이형처리된 38㎛의 두께의 폴리에틸렌테레프탈레이트 필름(이형 PET)의 이형 처리면에, 건조 후의 두께가 23 ㎛가 되도록 도포한 후 건조시켜 점착성 코팅층을 형성하였다. 그 후, 점착성 코팅층을 편광판에 라미네이트하여 점착층을 포함하는 편광판을 제조하였다.
실시예 4
제조예 2에 의해 제조된 아크릴계 공중합체 A2 100중량부, 다관능성 아크릴레이트(트리스(메타)아크릴로일록시에틸 이소시아누레이트) 15중량부, 2,2-디메톡시-2-페닐아세토페논 (광 개시제 1) 1.5중량부, 디페닐(2,4,6-트리메틸벤조일)포스핀 옥사이드(광 개시제 2) 0.5중량부, 다관능성 가교제(coronate L, 니폰폴리우레탄사제) 0.2 중량부, 실란커플링제(베타-시아노아세틸기 함유 실란커플링제, LG화학, M812) 0.2중량부를 배합하고, 고형분 함량이 35.2중량%가 되도록 에틸 아세테이트로 희석한 후, 균일하게 혼합하여 점착제 조성물(코팅액)을 제조하였다.
제조된 점착제 조성물을 이형처리된 38㎛의 두께의 폴리에틸렌테레프탈레이트 필름(이형 PET)의 이형 처리면에, 건조 후의 두께가 23 ㎛가 되도록 도포한 후 건조시켜 점착성 코팅층을 형성하였다. 그 후, 점착성 코팅층을 편광판에 라미네이트하여 점착층을 포함하는 편광판을 제조하였다.
실시예 5
디페닐(2,4,6-트리메틸벤조일)포스핀 옥사이드를 0.7중량부 사용한 점을 제외하고는 실시예 4와 동일한 방법으로 점착제 조성물 및 편광판을 제조하였다.
실시예 6
다관능성 아크릴레이트를 20중량부로 배합한 점을 제외하고는, 실시예 3과 동일한 방법으로 점착제 조성물 및 편광판을 제조하였다.
비교예 1
디페닐(2,4,6-트리메틸벤조일)포스핀 옥사이드(광 개시제 2)를 사용하지 않은 점을 제외하고는 실시예 1과 동일한 방법으로 점착제 조성물 및 편광판을 제조하였다.
비교예 2
디페닐(2,4,6-트리메틸벤조일)포스핀 옥사이드(광 개시제 2)를 사용하지 않은 점을 제외하고는 실시예 2과 동일한 방법으로 점착제 조성물 및 편광판을 제조하였다.
비교예 3
디페닐(2,4,6-트리메틸벤조일)포스핀 옥사이드(광 개시제 2)를 사용하지 않은 점을 제외하고는 실시예 3과 동일한 방법으로 점착제 조성물 및 편광판을 제조하였다.
비교예 4
제1광개시제를 사용하지 않은 점을 제외하고는 실시예 4과 동일한 방법으로 점착제 조성물 및 편광판을 제조하였다.
비교예 5
제1광개시제로 2,2-디메톡시-2-페닐아세토페논 대신 케톤계 광 개시제인 1-히드록시시클로헥실페닐케톤(광 개시제 3, 상품명: Omnirad 184, 제조사: IGM Resins社)을 사용한 점을 제외하고는 실시예 4과 동일한 방법으로 점착제 조성물 및 편광판을 제조하였다.
비교예 6
제1광개시제로 2,2-디메톡시-2-페닐아세토페논 대신 1-히드록시시클로헥실페닐케톤과 벤조페논의 혼합물(광 개시제 4, 상품명: Omnirad 500, 제조사: IGM Resins社)을 사용한 점을 제외하고는 실시예 4과 동일한 방법으로 점착제 조성물 및 편광판을 제조하였다.
비교예 7
다관능성 아크릴레이트, 2,2-디메톡시-2-페닐아세토페논(광 개시제 1), 디페닐(2,4,6-트리메틸벤조일)포스핀 옥사이드(광 개시제 2)를 사용하지 않고, 고형분 함량이 51.3중량%가 되도록 희석한 점을 제외하고는, 실시예 1과 동일한 방법으로 점착제 조성물 및 편광판을 제조하였다.
비교예 8
다관능성 아크릴레이트, 2,2-디메톡시-2-페닐아세토페논, 디페닐(2,4,6-트리메틸벤조일)포스핀 옥사이드를 사용하지 않고, 고형분 함량이 31.4중량%가 되도록 희석한 점을 제외하고는, 실시예 2와 동일한 방법으로 점착제 조성물 및 편광판을 제조하였다.
비교예 9
다관능성 아크릴레이트를 3중량부로 배합하고, 디페닐(2,4,6-트리메틸벤조일)포스핀 옥사이드(광 개시제 2)를 사용하지 않고, 고형분 함량이 32.8중량%가 되도록 희석한 점을 제외하고는, 실시예 2와 동일한 방법으로 점착제 조성물 및 편광판을 제조하였다.
비교예 10
다관능성 아크릴레이트를 20중량부로 배합하고, 디페닐(2,4,6-트리메틸벤조일)포스핀 옥사이드(광 개시제 2)를 사용하지 않고, 고형분 함량이 57.3중량%가 되도록 희석한 점을 제외하고는, 실시예 1과 동일한 방법으로 점착제 조성물 및 편광판을 제조하였다.
비교예 11
다관능성 아크릴레이트를 20중량부로 배합하고, 디페닐(2,4,6-트리메틸벤조일)포스핀 옥사이드(광 개시제 2)를 사용하지 않은 점을 제외하고는, 실시예 2와 동일한 방법으로 점착제 조성물 및 편광판을 제조하였다.
비교예 12
제조예 1에 의해 제조된 아크릴계 공중합체 A1 대신 제조예 3에 의해 제조된 아크릴계 공중합체 B1을 사용하고, 디페닐(2,4,6-트리메틸벤조일)포스핀 옥사이드를 사용하지 않으며, 고형분 함량이 35.2중량%가 되도록 희석한 점을 제외하고는, 실시예 1과 동일한 방법으로 점착제 조성물 및 편광판을 제조하였다.
비교예 13
제조예 2에 의해 제조된 아크릴계 공중합체 A2 대신 제조예 4에 의해 제조된 아크릴계 공중합체 B2를 사용하고, 디페닐(2,4,6-트리메틸벤조일)포스핀 옥사이드를 사용하지 않으며, 고형분 함량이 35.1중량%가 되도록 희석한 점을 제외하고는, 실시예 4과 동일한 방법으로 점착제 조성물 및 편광판을 제조하였다.
비교예 14
제조예 2에 의해 제조된 아크릴계 공중합체 A2 대신 제조예 4에 의해 제조된 아크릴계 공중합체 B2를 사용하고, 디페닐(2,4,6-트리메틸벤조일)포스핀 옥사이드를 사용하지 않고, 고형분 함량이 24.2중량%가 되도록 희석한 점을 제외하고는 실시예 4와 동일한 방법으로 점착제 조성물 및 편광판을 제조하였다.
상기 실시예 1 ~ 6 및 비교예 1 ~ 14에 의해 제조된 점착제 조성물 및 편광판의 물성을 하기의 방법으로 측정하였으며, 측정 결과는 하기 표 2 ~ 표 4에 나타내었다.
물성 측정방법
1. 코팅 고형분 함량(단위: %)
코팅 고형분은 하기와 같은 방법으로 측정하였다.
먼저, 알루미늄 디쉬(aluminium dish)의 무게(A)를 측정한 다음, 실시예 또는 비교예에서 제조된 점착제 조성물을 0.3 ~ 0.5g 정도의 양(건조 전 시료의 무게: S)으로 채취하여 무게가 측정된 알루미늄 디쉬에 담았다. 이때 알루미늄 디쉬를 포함한 건조 전 시료의 무게 B(A+S)를 측정한다. 그런 다음, 중합금지제(hydroquinone)가 용해된 에틸 아세테이트 용액(중합 금지제 농도 0.5중량%)을 피펫을 사용하여 상기 점착제 조성물에 극소량 첨가하고, 이를 150℃의 오븐에서 30분 정도 건조시켜 용매를 제거하였다. 이후, 상기 건조된 시료를 상온에서 15분 내지 30분 정도 식힌 다음 알루미늄 디쉬 무게 A를 포함한 건조 후 시료의 무게 C를 포함한 무게를 측정하고, 하기 식(3)에 따라 코팅 고형분을 측정하였다.
식 (3): 코팅 고형분(%)= {(C-A)/(B-A)}×100
상기 식 (3)에서 A는 알루미늄 디쉬의 무게(단위: g)이며, C는 알루미늄 디쉬 무게 A를 포함한 건조 후 시료의 무게(단위:g)이고, B는 알루미늄 디쉬의 무게 A를 포함한 건조 전 시료의 무게(단위:g)이다.
2. 코팅 점도(단위: cP)
점착제 조성물의 코팅 점도는 측정기(Brookfield digital viscometer (RV DV2T)를 사용하여 하기 절차에 따라 평가하였다.
250 mL PE bottle에 점착제 조성물을 220mL 정도 넣고, 용제가 휘발되지 않도록뚜껑을 닫고 파라필름 등으로 충분히 밀봉한 이후 항온/항습(23℃, 50% 상대습도) 조건에서 충분히 방치하여 기포를 제거하였다. 그런 다음, 밀봉 및 뚜껑을 제거한 다음 점착제 조성물에 기포가 생기지 않도록 스핀들(spindle)을 비스듬히 넣고, 상기 스핀들을 점도계에 연결하고, 점착제 조성물의 액면이 스핀들의 홈에 맞도록 조절하였다. 이후, 토크(Torque)가 20%(±1%)되는 rpm 조건에서 점도를 측정하였다.
3. 코팅성
실시예 및 비교예에서 제조되는 점착제 조성물을 폴리에틸렌테레프탈레이트 필름 상에 코팅하였을 때 코팅층의 상태를 육안으로 관찰하여 하기 기준에 따라 평가하였다.
<코팅성 평가 기준>
○: 코팅층에서 기포 및 줄 무늬 등이 육안으로 확인되지 않음.
X: 코팅층에서 기포 및/또는 줄 무늬가 육안으로 현저하게 확인됨.
4. 밀림 거리(Creep, 단위: ㎛)
실시예 및 비교예에 의해 제조된 편광판을 폭 10mm, 길이 10mm 사이즈로 재단하여 시편을 제조하였다. 이어서, 점착층에 부착된 이형 PET 필름을 박리하고, JIS Z 0237 규정에 따라 2kg의 롤러를 사용하여 편광판을 무알칼리유리에 부착하여 측정용 시편을 제조하였다. 그런 다음 상기 측정용 시편을 항온항습 조건(23℃, 50% R.H.)에서 각각 1일 및 4일간 보관한 다음, TA 장비(Texture Analyzer, 영국 스테이블 마이크로 시스템사 제)를 사용하여 각각의 밀림 거리를 측정하였다. 구체적으로는 상기 밀림 거리는 1,000g 하중으로 1,000초 동안 측정용 시편의 편광판을 잡아당겼을 때, 상기 편광판이 유리 기판으로부터 밀린 거리(단위: ㎛)로 측정하였다.
5. 점착력 (단위: gf/25mm)
실시예 및 비교예에 의해 제조된 편광판을 항온항습 조건(23℃, 50% R.H.)에서 각각 1일 및 4일간 보관한 후에, 폭 25mm, 길이 100mm가 되도록 재단하여 시편을 제조하였다. 이어서 점착층에 부착된 이형 PET 필름을 박리하고, JIS Z 0237 규정에 따라 2kg의 롤러를 사용하여 편광판을 무알칼리유리에 부착하여 측정용 시편을 제조하였다.
상기 측정용 시편을 항온항습 조건(23℃, 50% R.H.)에서 4시간동안 보관하였다. 그런 다음, TA 장비(Texture Analyzer, 영국 스테이블 마이크로 시스템사 제)를 사용하여 박리속도 300mm/min, 박리각도 180°의 조건으로 상기 편광판을 잡아당겨 유리기판에서 편광판을 완전히 분리시키는데 요구되는 힘을 측정하여 점착력(단위: gf/25mm)을 측정하였다.
6. 재박리력(단위: gf/25mm) 및 재박리성:
실시예 및 비교예에 의해 제조된 편광판을 항온항습 조건(23℃, 50% R.H.)에서 각각 1일 및 4일간 보관한 후에, 폭 25mm, 길이 100mm가 되도록 재단하여 시편을 제조하였다. 이어서 점착층에 부착된 이형 PET 필름을 박리하고, JIS Z 0237 규정에 따라 2kg의 롤러를 사용하여 편광판을 무알칼리유리에 부착하여 측정용 시편을 제조하였다.
그런 다음, 상기 측정용 시편을 80℃에서 1시간동안 보관한 후, 항온항습 조건(23℃, 50% R.H.)에서 1시간동안 보관하였다. 그런 다음, TA 장비(Texture Analyzer, 영국 스테이블 마이크로 시스템사 제)를 사용하여 박리속도 300mm/min, 박리각도 180°의 조건으로 상기 편광판을 잡아당겨 유리기판에서 편광판을 완전히 분리시키는데 요구되는 힘을 측정하여 재박리력(단위: gf/25mm)을 측정하였다.
또한, 재박리 후에 하기 기준으로 재박리성을 평가하였다.
<평가 기준>
○: 재박리력이 1,500gf/25mm 미만이며, 재박리 후 유리 기판 상에 남아있는 점착층이 없는 경우
△: 재박리력이 1,500gf/25mm 이상 2,500gf/25mm 미만인 경우, 또는 재박리 후 유리 기판 상에서 점착층 잔사가 확인되며 잔사 면적이 5% 이하인 경우
Х: 재박리력이 2,500gf/25mm 이상인 경우, 또는 재박리 후 유리 기판 상에서 점착층 잔사가 확인되며 잔사 면적이 5% 를 초과하는 경우
7. 내구성 평가
실시예 및 비교예에 의해 제조된 편광판을 180mm×250mm(길이×폭)의 크기로 재단하여 샘플을 제조하고, 상기 샘플을 19인치 시판 패널에 라미네이터를 이용 부착시켰다. 그 후, 패널을 오토클레이브(50℃ 및 5 기압)에서 약 20분 동안 압착 처리한 다음, 항온항습 조건(23℃ 50% R.H.)에서 24 시간 동안 보관하여 측정용 시편을 제작하였다.
제조된 측정용 시편들의 내습열 내구성은, 시편을 60℃의 온도 및 90% R.H.의 상대습도 조건하에서 500시간 동안 방치한 다음, 기포 또는 박리의 발생 여부를 관찰하여 평가하였다.
한편, 내열 내구성은 시편을 80℃, 100℃ 및 110℃의 온도에서 각각 500시간 동안 방치한 다음, 기포 또는 박리의 발생 여부를 관찰하여 평가하였다.
<평가 기준>
○: 기포 및 박리 발생 없음
△: 기포 및/또는 박리 약간 발생
Х: 기포 및/또는 박리 다량 발생
Figure PCTKR2020012969-appb-T000002
Figure PCTKR2020012969-appb-T000003
Figure PCTKR2020012969-appb-T000004
상기 [표 2]에 나타난 바와 같이, 실시예 1 ~ 6의 점착제 조성물은 고형분 함량이 높은 경우에도 2,000cP 이하의 점도 특성을 나타내었다. 또한, 점착층의 재박리 특성이 우수하고, 점착층 물성의 경시 변화가 적었다. 또한, 고온/고습 조건 및 80℃, 100℃ 및 110℃의 고온 조건에서 모두 우수한 내구성을 나타내었다. 이 중에서도 실시예 1 ~ 4와 같이, 다관능성 아크릴레이트의 함량이 5 ~ 15중량부이고, 제2광 개시제의 함량이 0.1 ~ 0.5 중량부를 만족할 경우에 내구성이 특히 우수한 것으로 나타났다.
이에 비해, 상기 [표 3] 및 [표 4]에 나타난 바와 같이, 본 발명의 조성을 만족하지 못하는 비교예 1 ~ 12 및 14의 점착제 조성물을 사용하는 경우, 110℃ 고온 조건에서의 내구성이 떨어지는 것으로 나타났다.
구체적으로는, 1종의 광 개시제만을 사용한 비교예 1~ 4, 7 ~ 10 및 12와, 2종의 광개시제를 사용하더라도 본 발명의 광 개시제 조합이 아닌 다른 광 개시제 조합을 사용한 비교예 5 및 6의 경우, 110℃ 고온 조건에서의 내구성이 떨어지는 것으로 나타났으며, 다관능성 아크릴레이트를 사용하지 않은 비교예 7 및 8의 경우, 100℃ 및 110℃ 고온 조건에서의 내구성이 떨어지는 것으로 나타났다.

Claims (15)

  1. 하기 [화학식 1]로 표시되는 단량체, 가교성 관능기를 갖는 (메트)아크릴계 단량체, 및 알킬 (메트)아크릴레이트계 단량체를 포함하는 단량체 혼합물을 중합하여 형성되고, 가지형(branch) 고분자 구조를 갖는 아크릴계 공중합체;
    2개 이상의 라디칼 중합성 관능기를 갖는 다관능성 아크릴레이트;
    제1광 개시제; 및
    제2광 개시제를 포함하고,
    상기 제1광 개시제는 아세토페논계 광 개시제이고, 상기 제2광 개시제는 포스핀 옥사이드계 광 개시제인 아크릴계 점착제 조성물:
    [화학식 1]
    R1-CH=CR2-(C=O)-O-X-Y
    상기 화학식 1에서, R1은 수소, C1~C6 알킬기 또는 C2~C6 알켄닐기이고, R2는 수소 또는 C1~C10 알킬기이며, X는 단일결합, C1~C10 알킬렌기, C2~C10 알켄닐렌기, 에테르, 에스테르, 또는 이들의 조합이며, Y는 비닐기, 알릴기(allyl), 또는 C3~C10 사이클로알케닐기임.
  2. 제1항에 있어서,
    상기 아크릴계 공중합체는 중량평균분자량이 300,000 내지 1,000,000g/mol인 아크릴계 점착제 조성물.
  3. 제1항에 있어서,
    상기 [화학식 1]로 표시되는 단량체는, 알릴 메타크릴레이트(allyl methacrylate), 알릴 아크릴레이트(allyl acrylate), 메트알릴메타크릴레이트(methallyl methacrylate), 메트알릴아크릴레이트(methallyl acrylate), 3-부텐닐 아크릴레이트(3-butenyl acrylate), 부트-3-에닐-2-메틸프로프-2-에노에이트(but-3-enyl-2-methylprop-2-enoate), 2-알릴옥시에틸 아크릴레이트(2-allyloxyethyl acrylate), 2-알릴옥시에틸 메타크릴레이트(2-allyloxyethyl methacrylate), 3-알릴옥시프로필 메타크릴레이트(3-allyloxypropyl methacrylate), 3-알릴옥시프로필 아크릴레이트, 2-알릴옥시에톡시에틸 메타크릴레이트(2-allyloxyethoxyethyl methacrylate), 2-알릴옥시에톡시에틸 아크릴레이트(2-allyloxyethoxyethyl acrylate), 사이클로헥스-2-에닐아크릴레이트(cyclohex-2-enyl acrylate), 사이클로-헥스-2-엔-1-일-2-메틸프로프-2-에노에이트(cyclohex-2-en-1-yl 2-methylprop-2-enoate) 및 3-비닐사이클로헥스-2-에닐 아크릴레이트(3-vinylcyclohex-2-enyl acrylate)로 이루어진 군으로부터 선택된 1종 이상인 아크릴계 점착제 조성물.
  4. 제1항에 있어서,
    상기 단량체 혼합물은 상기 [화학식 1]로 표시되는 단량체를 상기 단량체 혼합물 100중량부에 대하여 0.01 내지 1중량부로 포함하는 것인 아크릴계 점착제 조성물.
  5. 제1항에 있어서,
    상기 단량체 혼합물은, 상기 단량체 혼합물 100중량부에 대하여,
    상기 알킬 (메트)아크릴레이트계단량체 84 중량부 내지 99.89중량부;
    가교성 관능기를 갖는 (메트)아크릴계 단량체 0.1 내지 15중량부; 및
    상기 [화학식 1]로 표시되는 단량체 0.01 내지 1중량부를 포함하는 것인 아크릴계 점착제 조성물.
  6. 제1항에 있어서,
    상기 다관능성 아크릴레이트는 상기 아크릴계 공중합체 100중량부에 대하여, 5 내지 15중량부로 포함되는 것인 아크릴계 점착제 조성물.
  7. 제1항에 있어서,
    상기 제1광 개시제는, 아세토페논, 디메틸아니노 아세토페논, 2,2-디메톡시-2-페닐아세토페논, 및 2,2-디에톡시-2-페닐아세토페논 로 이루어진 군으로부터 선택되는 것인 아크릴계 점착제 조성물.
  8. 제1항에 있어서,
    상기 제2광 개시제는 디페닐(2,4,6-트리메틸벤조일)포스핀 옥사이드인 아크릴계 점착제 조성물.
  9. 제1항에 있어서,
    상기 제1광 개시제는 상기 아크릴계 공중합체 100중량부에 대하여 1.0 내지 5.0중량부, 상기 제2광 개시제는 상기 아크릴계 공중합체 100중량부에 대하여 0.01 내지 0.5중량부로 포함되는 것인 아크릴계 점착제 조성물.
  10. 제1항에 있어서,
    상기 점착제 조성물은 고형분 함량이 35중량% 이상이며,
    23℃에서 점도가 500cP 내지 2,000cP인 아크릴계 점착제 조성물.
  11. 제1항에 있어서,
    상기 점착제 조성물은 다관능성 가교제를 추가로 포함하는 것인 아크릴계 점착제 조성물.
  12. 제11항에 있어서,
    상기 다관능성 가교제는 이소시아네이트계 가교제인 아크릴계 점착제 조성물.
  13. 제11항에 있어서,
    상기 다관능성 가교제는 상기 아크릴계 공중합체 100중량부에 대하여 0.01 내지 5중량부로 포함되는 것인 아크릴계 점착제 조성물.
  14. 편광 필름; 및
    상기 편광 필름의 일면 또는 양면에 형성되고, 상기 청구항 1 내지 13 중 어느 한 항의 아크릴계 점착제 조성물의 경화물을 포함하는 점착층을 포함하는 편광판.
  15. 청구항 14의 편광판을 포함하는 디스플레이 장치.
PCT/KR2020/012969 2019-09-27 2020-09-24 아크릴계 점착제 조성물, 편광판 및 디스플레이 장치 WO2021060876A1 (ko)