WO2021060412A1 - Élément de stockage d'énergie et procédé de fabrication d'élément de stockage d'énergie - Google Patents

Élément de stockage d'énergie et procédé de fabrication d'élément de stockage d'énergie Download PDF

Info

Publication number
WO2021060412A1
WO2021060412A1 PCT/JP2020/036128 JP2020036128W WO2021060412A1 WO 2021060412 A1 WO2021060412 A1 WO 2021060412A1 JP 2020036128 W JP2020036128 W JP 2020036128W WO 2021060412 A1 WO2021060412 A1 WO 2021060412A1
Authority
WO
WIPO (PCT)
Prior art keywords
active material
negative electrode
electrode active
material layer
positive electrode
Prior art date
Application number
PCT/JP2020/036128
Other languages
English (en)
Japanese (ja)
Inventor
友章 西野
瀬川　健
Original Assignee
積水化学工業株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 積水化学工業株式会社 filed Critical 積水化学工業株式会社
Priority to CN202080043386.8A priority Critical patent/CN113994502B/zh
Priority to JP2020562229A priority patent/JP6876883B1/ja
Publication of WO2021060412A1 publication Critical patent/WO2021060412A1/fr

Abstract

L'invention concerne un élément de stockage d'énergie 1 comprenant : un boîtier extérieur 7 comprenant un premier matériau de boîtier extérieur 40 et un second matériau de boîtier extérieur 50 ; et un ensemble électrode 5 et un électrolyte logé à l'intérieur d'un espace de logement 7a formé entre le premier matériau de boîtier extérieur 40 et le second matériau de boîtier extérieur 50. L'ensemble électrode 5 comprend de multiples électrodes négatives 20Y et de multiples électrodes positives 10X stratifiées en alternance dans une première direction d1. Chaque électrode négative 20Y comprend : un collecteur de courant d'électrode négative 21Y ; et une couche de matériau actif d'électrode négative 22Y disposée sur au moins l'une des surfaces du collecteur de courant d'électrode négative 21Y et contenant un matériau actif d'électrode négative. Chaque électrode positive 10X comprend : un collecteur de courant d'électrode positive 11X ; et une couche de matériau actif d'électrode positive 12X disposée sur au moins l'une des surfaces du collecteur de courant d'électrode positive 11X et contenant un matériau actif d'électrode positive. Le rapport AC (WA/WC), qui représente la valeur du rapport du poids total WA des couches de matériau actif d'électrode négative 22Y incluses dans l'ensemble électrode 5 au poids total WC des couches de matériau actif d'électrode positive 12X incluses dans l'ensemble électrode 5, est supérieur ou égal à 0,45 et inférieur à 1,0. Les couches de matériau actif d'électrode négative 22Y incluses dans l'ensemble électrode 5 ont un volume solide VA compris entre 50 cm3 et 150 cm3. L'espace de logement 7a possède une capacité permettant de recevoir en outre 20 cm3 ou plus de gaz en plus de l'électrolyte et de l'ensemble électrode 5.
PCT/JP2020/036128 2019-09-25 2020-09-24 Élément de stockage d'énergie et procédé de fabrication d'élément de stockage d'énergie WO2021060412A1 (fr)

Priority Applications (2)

Application Number Priority Date Filing Date Title
CN202080043386.8A CN113994502B (zh) 2019-09-25 2020-09-24 蓄电元件以及蓄电元件的制造方法
JP2020562229A JP6876883B1 (ja) 2019-09-25 2020-09-24 蓄電素子及び蓄電素子の製造方法

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2019174784 2019-09-25
JP2019-174784 2019-09-25

Publications (1)

Publication Number Publication Date
WO2021060412A1 true WO2021060412A1 (fr) 2021-04-01

Family

ID=75166179

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2020/036128 WO2021060412A1 (fr) 2019-09-25 2020-09-24 Élément de stockage d'énergie et procédé de fabrication d'élément de stockage d'énergie

Country Status (3)

Country Link
JP (1) JP6876883B1 (fr)
CN (1) CN113994502B (fr)
WO (1) WO2021060412A1 (fr)

Families Citing this family (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN114975873B (zh) * 2022-06-02 2024-02-09 深圳新宙邦科技股份有限公司 一种正极片及锂离子电池

Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2012127991A1 (fr) * 2011-03-18 2012-09-27 Ｊｍエナジー株式会社 Dispositif de stockage de puissance
JP2016009677A (ja) * 2014-06-26 2016-01-18 株式会社カネカ リチウムイオン二次電池及びその製造方法
WO2017098995A1 (fr) * 2015-12-09 2017-06-15 Ｎｅｃエナジーデバイス株式会社 Dispositif électrochimique et procédé de sa fabrication
WO2017169417A1 (fr) * 2016-03-31 2017-10-05 オートモーティブエナジーサプライ株式会社 Batterie rechargeable au lithium-ion

Family Cites Families (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2008097940A (ja) * 2006-10-10 2008-04-24 Nissan Motor Co Ltd 双極型二次電池
JP6006325B2 (ja) * 2012-10-01 2016-10-12 旭化成株式会社 蓄電素子用電極、及び非水系リチウム型蓄電素子
EP2930728B1 (fr) * 2012-12-06 2020-02-05 Asahi Kasei Kabushiki Kaisha Élément de stockage au lithium non aqueux
JP2014130717A (ja) * 2012-12-28 2014-07-10 Ricoh Co Ltd 非水電解液蓄電素子
CN105103341B (zh) * 2013-03-26 2018-07-10 日产自动车株式会社 非水电解质二次电池
CN107112447A (zh) * 2014-12-26 2017-08-29 株式会社Lg化学 电化学装置
CN109461881B (zh) * 2018-10-17 2020-07-03 宁德时代新能源科技股份有限公司 负极极片及二次电池

Patent Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2012127991A1 (fr) * 2011-03-18 2012-09-27 Ｊｍエナジー株式会社 Dispositif de stockage de puissance
JP2016009677A (ja) * 2014-06-26 2016-01-18 株式会社カネカ リチウムイオン二次電池及びその製造方法
WO2017098995A1 (fr) * 2015-12-09 2017-06-15 Ｎｅｃエナジーデバイス株式会社 Dispositif électrochimique et procédé de sa fabrication
WO2017169417A1 (fr) * 2016-03-31 2017-10-05 オートモーティブエナジーサプライ株式会社 Batterie rechargeable au lithium-ion

Also Published As

Publication number Publication date
CN113994502B (zh) 2023-04-07
JP6876883B1 (ja) 2021-05-26
JPWO2021060412A1 (ja) 2021-10-07
CN113994502A (zh) 2022-01-28

Similar Documents

Publication Publication Date Title
KR101761002B1 (ko) 전극 조립체 및 이를 포함하는 전기화학소자
JP6003041B2 (ja) 耐熱絶縁層付セパレータ
JP5618165B2 (ja) 非水電解質二次電池
JP7069612B2 (ja) 積層電極体、蓄電素子及び積層電極体の製造方法
CN104170151A (zh) 电极组件的制造方法及包括由该方法制造的电极组件的电化学元件
KR20140009037A (ko) 전극조립체 및 이를 포함하는 전기화학소자
JP6587157B2 (ja) 電極組立体及びこれを含む電気化学素子
JP6336703B2 (ja) 耐熱絶縁層付セパレータ
JP2016207576A (ja) 非水電解液二次電池
JP7108052B2 (ja) 蓄電素子及び蓄電素子の製造方法
KR101484369B1 (ko) 이차전지 및 이를 포함하는 전기화학소자
JP6876883B1 (ja) 蓄電素子及び蓄電素子の製造方法
KR20140009047A (ko) 이차전지용 파우치 및 이를 포함하는 이차전지
US10199630B2 (en) Electrode terminal, electro-chemical device and electro-chemical device comprising same
CN113966559A (zh) 叠层型电池和叠层型电池的输送方法
KR101476040B1 (ko) 가스 흡착제가 코팅된 분리막을 포함하는 이차 전지 및 이를 이용한 중대형전지모듈
CN113950766A (zh) 叠层型电池
WO2021060409A1 (fr) Élément de stockage électrique, et procédé de fabrication de celui-ci
JP2008311011A (ja) 非水電解質二次電池
KR101163388B1 (ko) 절연 저항이 우수한 이차전지
JP2020140831A (ja) 蓄電素子及び蓄電素子の製造方法
JP2021057291A (ja) 全固体電池システム
JP7193363B2 (ja) 蓄電素子、蓄電素子の製造方法
KR20140034340A (ko) 전극조립체 및 이를 포함하는 전기화학소자, 전지모듈
KR20130133332A (ko) 신규한 구조의 이차전지

Legal Events

Date Code Title Description
ENP Entry into the national phase

Ref document number: 2020562229

Country of ref document: JP

Kind code of ref document: A

121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 20868080

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 20868080

Country of ref document: EP

Kind code of ref document: A1