WO2020250550A1 - 合成繊維用処理剤及び合成繊維 - Google Patents

合成繊維用処理剤及び合成繊維 Download PDF

Info

Publication number
WO2020250550A1
WO2020250550A1 PCT/JP2020/015208 JP2020015208W WO2020250550A1 WO 2020250550 A1 WO2020250550 A1 WO 2020250550A1 JP 2020015208 W JP2020015208 W JP 2020015208W WO 2020250550 A1 WO2020250550 A1 WO 2020250550A1
Authority
WO
WIPO (PCT)
Prior art keywords
mol
treatment agent
polyoxyethylene
compound
carbon atoms
Prior art date
Application number
PCT/JP2020/015208
Other languages
English (en)
French (fr)
Inventor
智八 岡田
佳典 武田
北原　秀章
利広 小室
Original Assignee
竹本油脂株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 竹本油脂株式会社 filed Critical 竹本油脂株式会社
Priority to KR1020217039630A priority Critical patent/KR102378978B1/ko
Priority to JP2020528367A priority patent/JP6777356B1/ja
Priority to CN202080028557.XA priority patent/CN113785089B/zh
Publication of WO2020250550A1 publication Critical patent/WO2020250550A1/ja

Abstract

本発明は、炭素数１～１６であるジカルボン酸及びそのエステル形成性誘導体から選ばれる少なくとも一つを含むＡ成分、並びに分子中に芳香環を有する１価ヒドロキシ化合物１モルに対し炭素数２～４のアルキレンオキサイドを１０モル超且つ１００モル以下の割合で付加させた化合物、及び分子中に芳香環を有する１価カルボン酸１モルに対し炭素数２～４のアルキレンオキサイドを１０モル超且つ１００モル以下の割合で付加させた化合物から選ばれる少なくとも一つを含むＢ成分、から形成されたジエステル化合物を含むことを特徴とする合成繊維（炭素繊維を除く）用処理剤である。

Description

合成繊維用処理剤及び合成繊維
　本発明は、合成繊維に対して優れた初期親水耐久性を付与し、水系媒体に分散させた際に優れた乳化安定性が得られる合成繊維用処理剤、及びかかる合成繊維用処理剤が付着している合成繊維に関する。
　例えば紙おむつ等の衛生製品として、体液を吸収するために高吸収性高分子の表面を合成繊維で被覆した製品が知られている。高吸収性高分子の表面を被覆する合成繊維には、例えば繰り返し体液をすばやく吸収する初期親水耐久性等の優れた吸収特性が要求される。そのため、特に疎水性の合成繊維に対しては、上記特性を付与するために合成繊維用処理剤が用いられることがある。また、合成繊維用処理剤には、水系媒体に分散させた乳化物の形態で用いられる場合、乳化安定性も必要になる。
　従来、例えば特許文献１～３に開示される合成繊維用処理剤が知られている。
　特許文献１は、１価脂肪族アルコールのアルキレンオキサイド１～１００モルの付加物と２価カルボン酸とのエステル化合物を含有する透水性付与剤について開示する。
　特許文献２は、多環フェノール等のエチレンオキサイド１０モル以下の付加物とジカルボン酸とのエステル化合物を含有する繊維用薬剤について開示する。
　特許文献３は、所定の割合からなる芳香族ジカルボン酸等の構成単位Ａと、エチレングリコール等の構成単位Ｂと、ポリオキシエチレン多環芳香族エーテル等の構成単位Ｃとから構成されたポリエーテルエステル化合物を含有するポリエステル系繊維の処理剤について開示する。
国際公開第２０１１－００４７１３号 特開２００３－１５５６６６号公報 特開２０１６－７５００２号公報
　しかし、従来の処理剤では、水系媒体に分散させた際の乳化安定性と、処理剤を用いて親水化処理された合成繊維に求められる初期親水耐久性という２つの性能の両立を十分に図ることができなかった。
　本発明が解決しようとする課題は、合成繊維に対して優れた初期親水耐久性を付与し、水系媒体に分散させた際に優れた乳化安定性が得られる合成繊維用処理剤を提供することにある。また、本発明が解決しようとする別の課題は、優れた初期親水耐久性を有する合成繊維を提供することにある。
　しかして本発明者らは、前記の課題を解決するべく研究した結果、下記のＡ成分及び下記のＢ成分から形成されたジエステル化合物を含む合成繊維用処理剤がまさしく好適であることを見出した。
　上記課題を解決するために本発明の一態様の合成繊維（ただし炭素繊維を除く）用処理剤では、炭素数１～１６であるジカルボン酸及びそのエステル形成性誘導体から選ばれる少なくとも一つを含むＡ成分と、分子中に芳香環を有する１価ヒドロキシ化合物１モルに対し炭素数２～４のアルキレンオキサイドを１０モル超且つ１００モル以下の割合で付加させた化合物、及び分子中に芳香環を有する１価カルボン酸１モルに対し炭素数２～４のアルキレンオキサイドを１０モル超且つ１００モル以下の割合で付加させた化合物から選ばれる少なくとも一つを含むＢ成分とから形成されたジエステル化合物を含むことを特徴とする。
　前記合成繊維用処理剤において、前記Ａ成分は、炭素数１～１６の不飽和脂肪族ジカルボン酸、芳香族ジカルボン酸、及びこれらのエステル形成性誘導体から選ばれる少なくとも一つを含むことが好ましい。
　前記合成繊維用処理剤において、前記Ｂ成分は、分子中に芳香環を有する１価ヒドロキシ化合物１モルに対し炭素数２～４のアルキレンオキサイドを１０モル超且つ５０モル以下の割合で付加させた化合物、及び分子中に芳香環を有する１価カルボン酸１モルに対し炭素数２～４のアルキレンオキサイドを１０モル超且つ５０モル以下の割合で付加させた化合物から選ばれる少なくとも一つを含むことが好ましい。
　前記合成繊維用処理剤において、前記Ｂ成分は、分子中に芳香環を有する１価ヒドロキシ化合物１モルに対し炭素数２～４のアルキレンオキサイドを１５モル以上且つ２５モル以下の割合で付加させた化合物、及び分子中に芳香環を有する１価カルボン酸１モルに対し炭素数２～４のアルキレンオキサイドを１５モル以上且つ２５モル以下の割合で付加させた化合物から選ばれる少なくとも一つを含むことが好ましい。
　前記合成繊維用処理剤において、前記Ｂ成分を形成することとなる前記分子中に芳香環を有する１価ヒドロキシ化合物は、分子中に２以上の芳香環を有する１価ヒドロキシ化合物であることが好ましい。
　前記合成繊維用処理剤は、更にアニオン界面活性剤、カチオン界面活性剤、非イオン界面活性剤、平滑剤、脂肪族アルコール、及びポリエーテル変性シリコーンから選ばれる少なくとも一つを含むことが好ましい。
　本発明の別の態様の合成繊維は、前記合成繊維用処理剤が付着していることを特徴とする。
　前記合成繊維は、疎水性のものであることが好ましい。
　前記合成繊維は、ポリエステルであることが好ましい。
　本発明によれば、合成繊維に対して優れた初期親水耐久性を付与し、水系媒体に分散させた際に優れた乳化安定性が得られる。
　（第１実施形態）
　以下、本発明の合成繊維用処理剤（以下、単に処理剤という）を具体化した第１実施形態について説明する。本実施形態の処理剤は、下記のＡ成分と下記のＢ成分とがエステル化反応又はエステル交換反応により結合したジエステル化合物を含有する。ジエステル化合物は、１種のジエステル化合物を単独で使用してもよく、２種以上のジエステル化合物を組み合わせて使用してもよい。
　上記ジエステル化合物に供されるＡ成分は、炭素数１～１６であるジカルボン酸及びそのエステル形成性誘導体から選ばれる少なくとも一つを含む成分である。かかるジカルボン酸及びジカルボン酸のエステル形成性誘導体の具体例としては、例えばクエン酸、シュウ酸、マロン酸、コハク酸、グルタル酸、アジピン酸、フマル酸、マレイン酸等の脂肪族ジカルボン酸及びこれらの無水物、シュウ酸ジメチル、マロン酸ジメチル、コハク酸ジメチル、グルタル酸ジメチル、アジピン酸ジメチル、フマル酸ジメチル、マレイン酸ジメチル、マレイン酸ジオクチル、マレイン酸ビス（２－エチルヘキシル）等の脂肪族ジカルボン酸のエステル形成誘導体、フタル酸（ｏ－フタル酸）、テレフタル酸（ｐ－フタル酸）、イソフタル酸（ｍ－フタル酸）、２，６－ナフタレンジカルボン酸、５－スルホイソフタル酸等の芳香族ジカルボン酸及びこれらの無水物、フタル酸ジブチル、テレフタル酸ジメチル、テレフタル酸ジエチル、テレフタル酸ビス（２－エチルヘキシル）、イソフタル酸ジメチル、イソフタル酸ジエチル、イソフタル酸ジオクチル、テレフタル酸ジプロピル、２，６－ナフタレンジカルボン酸ジメチル、５－スルホイソフタル酸－１，３－ジメチル等の芳香族ジカルボン酸のエステル形成性誘導体等が挙げられる。これらの中でもフマル酸、マレイン酸等の不飽和脂肪酸ジカルボン酸、テレフタル酸、イソフタル酸、５－スルホイソフタル酸等の芳香族ジカルボン酸、及びそれらのエステル形成性誘導体が好ましい。これらの化合物を使用した処理剤を用いることにより、合成繊維の耐久親水性、特に初期親水耐久性が向上する。なお、耐久親水性とは、所定の目的で使用される合成繊維に要求される親水性をどれだけ長く持続できるかを示す性能のことであり、特に、合成繊維が有する初期親水性をどれだけ長く持続できるかを示す性能のことを初期親水耐久性という。
　上記ジエステル化合物に供されるＢ成分は、分子中に芳香環を有する１価ヒドロキシ化合物１モルに対し炭素数２～４のアルキレンオキサイドを１０モル超且つ１００モル以下の割合で付加させた化合物、及び分子中に芳香環を有する１価カルボン酸１モルに対し炭素数２～４のアルキレンオキサイドを１０モル超且つ１００モル以下の割合で付加させた化合物から選ばれる少なくとも一つを含む。
　Ｂ成分を構成する分子中に芳香環を有する１価ヒドロキシ化合物は、分子中に１つの芳香環を有する１価ヒドロキシ化合物であってもよく、２つ以上の芳香環を有する１価ヒドロキシ化合物であってもよい。これらの中で、合成繊維の耐久親水性、特に初期親水耐久性を向上させる効果に優れることから、２つ以上の芳香環を有する１価ヒドロキシ化合物が好ましい。１つの芳香環を有する１価ヒドロキシ化合物の具体例としては、例えばフェノール、プロピルフェノール、ブチルフェノール、オクチルフェノール、トリデシルフェノール等の１つの芳香環を有する１価芳香族アルコール等が挙げられる。
　２つ以上の芳香環を有する１価ヒドロキシ化合物の具体例としては、例えばトリスチレン化フェノール、トリ（α－エチルベンジル）フェノール、トリ（α－プロピルベンジル）フェノール、トリ（α－ブチルベンジル）フェノール、ジスチレン化フェノール、ジ（α－エチルベンジル）フェノール、ジ（α－プロピルベンジル）フェノール、ジ（α－ブチルベンジル）フェノール、モノスチレン化フェノール、モノ（α－エチルベンジル）フェノール、モノ（α－プロピルベンジル）フェノール、モノ（α－ブチルベンジル）フェノール、トリベンジルフェノール、ジベンジルフェノール、モノベンジルフェノール等が挙げられる。
　Ｂ成分を構成する分子中に芳香環を有する１価カルボン酸としては、分子中に１つの芳香環を有する１価カルボン酸であってもよく、２つ以上の芳香環を有する１価カルボン酸であってもよい。芳香環を有する１価カルボン酸の具体例としては、例えば安息香酸等の１つの芳香環を有する１価芳香族カルボン酸等が挙げられる。
　Ｂ成分を構成する炭素数２～４のアルキレンオキサイドの具体例としては、エチレンオキサイド、プロピレンオキサイド、ブチレンオキサイド等が挙げられる。これらの中で本発明の効果をより向上させる観点からエチレンオキサイドが好ましい。また、アルキレンオキサイドは、ランダム付加体として構成されても、ブロック付加体として構成されてもよい。
　分子中に芳香環を有する１価ヒドロキシ化合物１モルに対する炭素数２～４のアルキレンオキサイドの付加モル数、又は分子中に芳香環を有する１価カルボン酸１モルに対するアルキレンオキサイドの付加モル数の下限は、１０モルを超え、好ましくは１５モル以上である。１０モルを超える範囲に規定することにより、合成繊維に付与することのできる親水特性、特に初期親水耐久性及び初期親水性が向上する。また、処理剤の乳化安定性、特に高温での乳化安定性が向上する。また、ジエステル化合物の流動性が向上する結果として、処理剤のハンドリング性がより向上する。
　上記付加モル数の上限は、１００モル以下、好ましくは５０モル以下、より好ましくは２５モル以下である。１００モル以下に規定することにより、ジエステル化合物の流動性が向上する結果として、処理剤のハンドリング性がより向上する。また、合成繊維に付与することのできる耐久親水性も向上する。なお、アルキレンオキサイドの付加モル数は平均付加モル数を示す。
　Ｂ成分の具体例としては、例えばポリオキシエチレン（アルキレンオキサイドの付加モル数（以下同じ）が１０．５～５０モル）トリスチレン化フェニルエーテル、ポリオキシエチレン（１０．５～３０モル）ポリオキシプロピレン（１０．５～３０モル）トリスチレン化フェニルエーテル、ポリオキシエチレン（１０．５～３０モル）トリ（α－エチルベンジル）フェニルエーテル、ポリオキシエチレン（１０．５～３０モル）トリ（α－プロピルベンジル）フェニルエーテル、ポリオキシエチレン（１０．５～３０モル）トリ（α－ブチルベンジル）フェニルエーテル、ポリオキシエチレン（１０．５～３０モル）ジスチレン化フェニルエーテル、ポリオキシエチレン（１０．５～３０モル）ジ（α－エチルベンジル）フェニルエーテル、ポリオキシエチレン（１０．５～３０モル）ジ（α－プロピルベンジル）フェニルエーテル、ポリオキシエチレン（１０．５～３０モル）ジ（α－ブチルベンジル）フェニルエーテル、ポリオキシエチレン（１０．５～３０モル）モノスチレン化フェニルエーテル、ポリオキシエチレン（１０．５～３０モル）モノ（α－エチルベンジル）フェニルエーテル、ポリオキシエチレン（１０．５～３０モル）モノ（α－プロピルベンジル）フェニルエーテル、ポリオキシエチレン（１０．５～３０モル）モノ（α－ブチルベンジル）フェニルエーテル、ポリオキシエチレン（１０．５～３０モル）トリベンジルフェニルエーテル、ポリオキシエチレン（１０．５～３０モル）ジベンジルフェニルエーテル、ポリオキシエチレン（１０．５～３０モル）モノベンジルフェニルエーテル、ポリオキシエチレン（１０．５～３０モル）ポリオキシプロピレン（１０．５～３０モル）フェニルエーテル、ポリオキシエチレン（１０．５～３０モル）フェニルエーテル、ポリオキシエチレン（１０．５～３０モル）ｔ－ブチルフェニルエーテル、ポリオキシエチレン（１０．５～３０モル）安息香酸エステル等が挙げられる。
　本実施形態の処理剤が適用される合成繊維は、炭素繊維以外の合成繊維である。炭素繊維以外の合成繊維であれば、特に限定されないが、合成樹脂の表面に親水性を付与するという効果を発揮する観点からすると、疎水性の合成繊維であることが好ましい。
　疎水性の合成繊維の例としては、例えばポリエステル系繊維、ポリオレフィン系繊維、ポリアミド系繊維、ポリアクリロニトリル系繊維等が挙げられる。これらの繊維は、２種以上から成る複合合成繊維であってもよい。ポリエステル系繊維の具体例としては、例えばポリエチレンテレフタレート（ＰＥＴ）、ポリトリメチレンテレフタレート、ポリブチレンテレフタレート、ポリエチレンナフタレート、ポリ乳酸、これらポリエステル系樹脂を含有して成る複合ポリエステル系繊維等が挙げられる。さらにポリエステル系繊維としては、塩基性又は酸性可染性ポリエステル繊維、帯電防止性ポリエステル繊維、難燃性ポリエステル繊維等の改質ポリエステル繊維等が適用されてもよい。ポリオレフィン系繊維の具体例としては、例えばポリエチレン繊維、ポリプロピレン系繊維、ポリブテン系繊維が挙げられる。さらにポリプロピレン系繊維としては、種々の単量体を共重合した改質ポリプロピレン繊維、ポリエチレンとポリプロピレンとの複合ポリプロピレン繊維等が適用されてもよい。
　本実施形態の処理剤は、短繊維及び長繊維のいずれにも適用することができるが、短繊維に適用されることが好ましい。短繊維は、一般にステープルと呼ばれるものが該当し、一般にフィラメントと呼ばれる長繊維を含まないものとする。また、本実施形態における短繊維の長さは、本技術分野において短繊維に該当するものであれば特に限定されないが、例えば１００ｍｍ以下であることが好ましい。
　本実施形態の処理剤は、以上説明したようなジエステル化合物を含有してなるものであるが、更にアニオン界面活性剤、カチオン界面活性剤、非イオン界面活性剤、平滑剤、脂肪族アルコール、及びポリエーテル変性シリコーンから選ばれる少なくとも一つを含むものが好ましい。これらの成分は、１種を単独で使用してもよく、２種以上を組み合わせて使用してもよい。これらの成分は、上記ジエステル化合物の特性を阻害することなく、各成分に応じた特性、例えば合成繊維の製糸工程、延伸工程、又は紡糸工程において摩擦を低減させ、糸切れ等の繊維の損傷を防止する特性を付与する。
　本実施形態の処理剤に供されるアニオン界面活性剤としては、公知のアニオン界面活性剤を適宜採用することができる。アニオン界面活性剤の具体例としては、例えば（１）ラウリルリン酸エステル塩、セチルリン酸エステル塩、オクチルリン酸エステル塩、オレイルリン酸エステル塩、ステアリルリン酸エステル塩等の脂肪族アルコールのリン酸エステル塩、（２）ポリオキシエチレン（５モル）ラウリルエーテルリン酸エステル塩、ポリオキシエチレン（５モル）オレイルエーテルリン酸エステル塩、ポリオキシエチレン（１０モル）ステアリルエーテルリン酸エステル塩等の脂肪族アルコールにエチレンオキサイド及びプロピレンオキサイドから選ばれる少なくとも一種のアルキレンオキサイドを付加したもののリン酸エステル塩、（３）ラウリルスルホン酸エステル塩、ミリスチルスルホン酸エステル塩、セチルスルホン酸エステル塩、オレイルスルホン酸エステル塩、ステアリルスルホン酸エステル塩、テトラデカンスルホン酸塩、Ｃ１４～１６アルキルスルホン酸塩、ドデシルベンゼンスルホン酸塩等の脂肪族アルコール又は芳香族アルコールのスルホン酸エステル塩、（４）ラウリル硫酸エステル塩、オレイル硫酸エステル塩、ステアリル硫酸エステル塩等の脂肪族アルコールの硫酸エステル塩、（５）ポリオキシエチレン（３モル）ラウリルエーテル硫酸エステル塩、ポリオキシエチレン（５モル）ラウリルエーテル硫酸エステル塩、ポリオキシアルキレン（ポリオキシエチレン３モル、ポリオキシプロピレン３モル）ラウリルエーテル硫酸エステル塩、ポリオキシエチレン（３モル）オレイルエーテル硫酸エステル塩、ポリオキシエチレン（５モル）オレイルエーテル硫酸エステル塩等の脂肪族アルコールにエチレンオキサイド及びプロピレンオキサイドから選ばれる少なくとも一種のアルキレンオキサイドを付加したものの硫酸エステル塩、（６）ひまし油脂肪酸硫酸エステル塩、ごま油脂肪酸硫酸エステル塩、トール油脂肪酸硫酸エステル塩、大豆油脂肪酸硫酸エステル塩、なたね油脂肪酸硫酸エステル塩、パーム油脂肪酸硫酸エステル塩、豚脂脂肪酸硫酸エステル塩、牛脂脂肪酸硫酸エステル塩、鯨油脂肪酸硫酸エステル塩等の脂肪酸の硫酸エステル塩、（７）ひまし油の硫酸エステル塩、ごま油の硫酸エステル塩、トール油の硫酸エステル塩、大豆油の硫酸エステル塩、菜種油の硫酸エステル塩、パーム油の硫酸エステル塩、豚脂の硫酸エステル塩、牛脂の硫酸エステル塩、鯨油の硫酸エステル塩等の油脂の硫酸エステル塩、（８）ラウリン酸塩、オレイン酸塩、ステアリン酸塩等の脂肪酸塩、（９）ジオクチルスルホコハク酸塩等の脂肪族アルコールのスルホコハク酸エステル塩等が挙げられる。アニオン界面活性剤の対イオンとしては、例えばカリウム塩、ナトリウム塩等のアルカリ金属塩、アンモニウム塩、トリエタノールアミン等のアルカノールアミン塩等が挙げられる。
　本実施形態の処理剤に供されるカチオン界面活性剤としては、公知のカチオン界面活性剤を適宜採用することができる。カチオン界面活性剤の具体例としては、例えばラウリルトリメチルアンモニウムクロライド、セチルトリメチルアンモニウムクロライド、ステアリルトリメチルアンモニウムクロライド、ベヘニルトリメチルアンモニウムクロライド、ジデシルジメチルアンモニウムクロライド等が挙げられる。
　本実施形態の処理剤に供される非イオン界面活性剤としては、公知の非イオン界面活性剤を適宜採用することができる。非イオン界面活性剤の具体例としては、例えば（１）有機酸、有機アルコール、有機アミン及び／又は有機アミドに炭素数２～４のアルキレンオキサイドを付加した化合物、例えばポリオキシエチレンジラウリン酸エステル、ポリオキシエチレンオレイン酸エステル、ポリオキシエチレンラウリン酸エステルメチルエーテル、ポリオキシエチレンオレイン酸ジエステル、ポリオキシエチレンオクチルエーテル、ポリオキシエチレンラウリルエーテル、ポリオキシエチレンラウリルエーテルメチルエーテル、ポリオキシエチレンポリオキシプロピレンラウリルエーテル、ポリオキシプロピレンラウリルエーテルメチルエーテル、ポリオキシブチレンオレイルエーテル、ポリオキシエチレンポリオキシプロピレンノニルエーテル、ポリオキシプロピレンノニルエーテル、ポリオキシエチレンポリオキシプロピレンオクチルエーテル、ポリオキシエチレンドデシルエーテル、ポリオキシエチレントリデシルエーテル、ポリオキシエチレンラウリルアミノエーテル、ポリオキシエチレンラウロアミドエーテル、ポリオキシエチレントリスチレン化フェニルエーテル等のエーテル型ノニオン界面活性剤、（２）ソルビタントリオレアート、ソルビタンモノオレアート、ソルビタンモノステアレート、グリセリンモノラウレラート等の多価アルコール部分エステル型ノニオン界面活性剤、（３）ポリオキシアルキレンソルビタントリオレアート、ポリオキシアルキレンヤシ油、ポリオキシアルキレンヒマシ油、ポリオキシアルキレン硬化ヒマシ油、ポリオキシアルキレン硬化ヒマシ油トリオクタノアート、ポリオキシアルキレン硬化ヒマシ油のマレイン酸エステル、ステアリン酸エステル、又はオレイン酸エステル等のポリオキシアルキレン多価アルコール脂肪酸エステル型ノニオン界面活性剤、（４）ジエタノールアミンモノラウロアミド等のアルキルアミド型ノニオン界面活性剤、（５）ポリオキシエチレンジエタノールアミンモノオレイルアミド、ポリオキシエチレンラウリルアミン、ポリオキシエチレン牛脂アミン等のポリオキシアルキレン脂肪酸アミド型ノニオン界面活性剤等が挙げられる。
　本実施形態の処理剤に供する平滑剤としては、上述したジエステル化合物以外の公知の平滑剤を適宜採用することができる。平滑剤の具体例としては、例えば（１）ブチルステアラート、オクチルステアラート、オレイルラウラート、オレイルオレアート、イソペンタコサニルイソステアラート、オクチルパルミテート、イソトリデシルステアレート等の、脂肪族モノアルコールと脂肪族モノカルボン酸とのエステル化合物、脂肪族モノアルコールに炭素数２～４のアルキレンオキサイドを付加した（ポリ）オキシアルキレン付加物と脂肪族モノカルボン酸とのエステル化合物、（２）１，６－ヘキサンジオールジデカノエートトリメチロールプロパンモノオレートモノラウレート、ソルビタントリトレアート、ソルビタンモノオレエート、ソルビタンモノステアレート、グリセリンモノラウレラート等の、脂肪族多価アルコールと脂肪族モノカルボン酸との完全エステル化合物、脂肪族多価アルコールに炭素数２～４のアルキレンオキサイドを付加した（ポリ）オキシアルキレン付加物と脂肪族モノカルボン酸との完全エステル化合物、（３）ジラウリルアジペート、ジオレイルアゼレート、ジイソセチルチオジプロピオナート、ビスポリオキシエチレンラウリルアジパート等の、脂肪族モノアルコールと脂肪族多価カルボン酸との完全エステル化合物、脂肪族モノアルコールに炭素数２～４のアルキレンオキサイドを付加した（ポリ）オキシアルキレン付加物と脂肪族多価カルボン酸との完全エステル化合物、（４）ベンジルオレアート、ベンジルラウラート及びポリオキシプロピレンベンジルステアラート等の、芳香族モノアルコールと脂肪族モノカルボン酸とのエステル化合物、芳香族モノアルコールに炭素数２～４のアルキレンオキサイドを付加した（ポリ）オキシアルキレン付加物と脂肪族モノカルボン酸とのエステル化合物、（５）ビスフェノールＡジラウラート、ポリオキシエチレンビスフェノールＡジラウラート等の、芳香族多価アルコールと脂肪族モノカルボン酸との完全エステル化合物、芳香族多価アルコールに炭素数２～４のアルキレンオキサイドを付加した（ポリ）オキシアルキレン付加物と脂肪族モノカルボン酸との完全エステル化合物、（６）ビス２－エチルヘキシルフタラート、ジイソステアリルイソフタレート、トリオクチルトリメリテート等の、脂肪族モノアルコールと芳香族多価カルボン酸との完全エステル化合物、脂肪族モノアルコールに炭素数２～４のアルキレンオキサイドを付加した（ポリ）オキシアルキレン付加物と芳香族多価カルボン酸との完全エステル化合物、（７）ヤシ油、パーム油、ナタネ油、ヒマワリ油、大豆油、ヒマシ油、ゴマ油、魚油、牛脂等の天然油脂等、（８）鉱物油等、処理剤に採用されている公知の平滑剤挙げられる。
　本実施形態の処理剤に供する脂肪族アルコールとしては、公知の脂肪族アルコールを適宜採用することができる。脂肪族アルコールの具体例としては、例えば（１）メチルアルコール、ブチルアルコール、オクチルアルコール、ノナノール、ラウリルアルコール、ステアリルアルコール、セリルアルコール、イソブチルアルコール、２－エチルヘキシルアルコール、イソドデシルアルコール、イソヘキサデシルアルコール、イソステアリルアルコール、イソテトラコサニルアルコール、２－プロピルアルコール、１２－エイコシルアルコール、ビニルアルコール、ブテニルアルコール、ヘキサデセニルアルコール、オレイルアルコール、エイコセニルアルコール、２－メチル－２－プロピレン－１－オール、６－エチル－２－ウンデセン－１－オール、２－オクテン－５－オール、１５－ヘキサデセン－２－オール等の炭素数１～４０の１価の脂肪族アルコール、（２）フェノール、プロピルフェノール、オクチルフェノール、トリデシルフェノール等の１価の芳香族アルコール、（３）エチレングリコール、プロピレングリコール、ブタンジオール、ヘキサンジオール、ネオペンチルグリコール、グリセリン、トリメチロールプロパン、ペンタエリトリット等の２～４価の脂肪族アルコール等が挙げられる。
　本実施形態の処理剤に供するポリエーテル変性シリコーンとしては、公知のポリエーテル変性シリコーンを適宜採用することができ、構成としては、特に制限はなく、例えば、ＡＢｎ型ポリエーテル変性シリコーン、側鎖型ポリエーテル変性シリコーン、両末端型ポリエーテル変性シリコーン、ポリエーテル基とアルキル基の両方が側鎖又は末端に導入されたアルキルポリエーテル変性シリコーン、側鎖型ポリエーテル変性シリコーンのポリエーテル鎖末端部分が脂肪族化合物又は脂肪酸化合物で封鎖されたもの、両末端型ポリエーテル変性シリコーンのポリエーテル鎖末端部分が脂肪族化合物又は脂肪酸化合物で封鎖されたもの等が挙げられる。本実施形態の処理剤に供するポリエーテル変性シリコーンは、例えば以下の構造を有することが好ましい。
Figure JPOXMLDOC01-appb-C000001
 　化１において、
Ｘは、下記の化２で示される有機基を示し、
Ｙは、下記の化３で示される有機基を示し、
Ｘ，Ｙの繰り返しは、それぞれブロック又はランダムのいずれの方法で繰り返されてもよく、
ａ，ｂは、それぞれ１以上の整数を示す。
Figure JPOXMLDOC01-appb-C000002
 　化２において、
Ｒ１は、水素原子、炭素数１～２０のアルキル基又は炭素数２～２０のアルケニル基を示す。
Figure JPOXMLDOC01-appb-C000003
 　化３において、
Ｒ２は、炭素数３～６のアルキレン基を示し、
Ｒ３は、水素原子、炭素数１～２０のアルキル基、炭素数２～２０のアルケニル基、又は炭素数２～８のアシル基を示し、
ｃ，ｄは、ｃ＋ｄ＝１～２００となるような整数（ただし、ｃ≧０、ｄ≧０。）を示す。
　本実施形態の処理剤は、必要により分散媒として水を含んでいてもよい。
　（第２実施形態）
　本発明に係る合成繊維を具体化した第２実施形態について説明する。本実施形態の合成繊維は、第１実施形態の処理剤が付着している合成繊維である。合成繊維の種類としては、第１実施形態の説明の中で挙げたのと同じ炭素繊維以外の合成繊維が適用される。
　第１実施形態の処理剤（溶媒を含まない）を合成繊維に付着させる割合に特に制限はないが、処理剤を合成繊維に対し０．１～３質量％の割合となるよう付着させることが好ましい。また、処理剤を付着させる方法は、例えばローラー給油法、計量ポンプを用いたガイド給油法、浸漬給油法、スプレー給油法等の公知の方法を採用することができる。処理剤を合成繊維に付着させる際の処理剤の形態は、例えば水性液であってもよい。また、本発明の効果を阻害しない範囲内において有機溶媒が処理剤に少量含まれてもよい。
　また、処理剤をどの工程で繊維に付着させるかは特に限定されず、例えば合成繊維の製糸工程、延伸工程、紡糸工程の他、不織布を製造する際の抄紙工程等において付着させてもよい。
　本実施形態の処理剤及び合成繊維の作用及び効果について説明する。
　（１）本実施形態の処理剤では、合成繊維に対して優れた親水特性を付与することができる。特に疎水性の合成繊維に対して優れた耐久親水性、特に初期親水耐久性、及び初期親水性を付与することができる。
　（２）また、処理剤を水系媒体に分散させた際に優れた乳化安定性が得られる。特に２５℃の常温での乳化安定性、及び８０℃等の高温での乳化安定性に優れる。そのため、合成繊維の製糸工程、延伸工程、紡糸工程の他、不織布を製造する際の抄紙工程等において製造特性を向上させることができる。
　（３）本実施形態の処理剤に含まれるジエステル化合物は、常温で流動性又は加熱により流動性を有するため、取扱時に溶媒を用いて希釈する必要がなく、ハンドリング性及び輸送性を著しく向上させることができる。
　なお、上記実施形態は以下のように変更してもよい。
　・本実施形態の処理剤には、本発明の効果を阻害しない範囲内において、処理剤の品質保持のための安定化剤や制電剤として、つなぎ剤、酸化防止剤、紫外線吸収剤等の処理剤に通常用いられる成分をさらに配合してもよい。
　・本実施形態の処理剤は、上記ジエステル化合物を必須成分とすることを特徴とするが、本発明の効果を阻害しない範囲内において、上記Ａ成分と上記Ｂ成分との反応工程で生じる、モノエステル等の反応副生物を含むことを妨げるものではない。
　以下、本発明の構成及び効果をより具体的に説明するため、実施例等を挙げるが、本発明がこれらの実施例に限定されるというものではない。尚、以下の実施例及び比較例の説明において、部は質量部を、また％は質量％を意味する。
　＜試験区分１（ジエステル化合物及び処理剤の調製）＞
　（実施例１）
　ジエステル化合物（Ｅ－１）の合成
　ジカルボン酸である無水フタル酸（１モル）、ポリオキシエチレン（１５モル）トリスチレン化フェニルエーテル（２モル）、及び触媒としてｐ－トルエンスルホン酸（０．１％）を反応容器に仕込み、窒素雰囲気下、１５０～２２０℃でエステル化を１２時間実施した。
　（実施例２）
　ジエステル化合物（Ｅ－２）の合成
　ジカルボン酸のエステル形成誘導体であるマレイン酸ジメチル（２モル）、ポリオキシエチレン（１８モル）トリスチレン化フェニルエーテル（２モル）、及び触媒としてチタンテトラブトキシド（０．１％）を反応容器に仕込み、１０ｈＰａ以下の減圧下、１５０～２２０℃で生成するメタノールを留去しながら、エステル交換反応を８時間実施した。
　（実施例３～３３、比較例１～８）
　ジエステル化合物（Ｅ－３～Ｅ－３３、ｅ－１～ｅ－８）の合成
　原料としてジカルボン酸を使用する実施例９，１０，１３，１５～１８，２０～２２，２４，２６，３２，３３及び比較例２，３，５，７の各ジエステル化合物（Ｅ－９，１０，１３，１５～１８，２０～２２，２４，２６，３２，３３，ｅ－２，３，５，７）は、表１に示される各成分を使用し、実施例１と同様の方法にて調製した。
　原料としてジカルボン酸のエステル形成誘導体を使用する上記以外の実施例及び比較例１，４，６の各エステル化合物は、実施例２と同様の方法にて調製した。
　比較例８は、特許文献３（特開２０１６－７５００２号公報）の実施例１に記載される化合物であり、具体的にはテレフタル酸ジメチルから形成された構成単位Ａ（４２．８モル％）、エチレングリコールから形成された構成単位Ｂ（２８．６モル％）、及びポリオキシエチレン（１８モル）トリスチレン化フェニルエーテルから形成された構成単位Ｃ（２８．６モル％）からなるポリエーテルエステル化合物（ｅ－８）を使用した。
　実施例１～３３及び比較例１～８は、上記各化合物１００質量部からなる処理剤として調製した。
Figure JPOXMLDOC01-appb-T000004
 　表１において
　Ａ－１：無水フタル酸
　Ａ－２：無水マレイン酸
　Ａ－３：マレイン酸
　Ａ－４：イソフタル酸（ｍ－フタル酸）
　Ａ－５：テレフタル酸（ｐ－フタル酸）
　Ａ－６：テレフタル酸ジメチル
　Ａ－７：イソフタル酸ジエチル
　Ａ－８：テレフタル酸ジプロピル
　Ａ－９：フタル酸ジブチル
　Ａ－１０：イソフタル酸ジオクチル
　Ａ－１１：テレフタル酸ビス（２－エチルヘキシル）
　Ａ－１２：マレイン酸ジメチル
　Ａ－１３：マレイン酸ジオクチル
　Ａ－１４：マレイン酸ビス（２－エチルヘキシル）
　Ａ－１５：２，６－ナフタレンジカルボン酸ジメチル
　Ａ－１６：フタル酸（ｏ－フタル酸）
　Ａ－１７：シュウ酸
　Ａ－１８：クエン酸
　Ａ－１９：コハク酸ジメチル
　Ａ－２０：アジピン酸
　Ａ－２１：アジピン酸ジメチル
　ａ－１：安息香酸メチル
　ａ－２：オレイン酸
　Ｂ－１：ポリオキシエチレン（１５モル）トリスチレン化フェニルエーテル
　Ｂ－２：ポリオキシエチレン（１８モル）トリスチレン化フェニルエーテル
　Ｂ－３：ポリオキシエチレン（２０モル）トリスチレン化フェニルエーテル
　Ｂ－４：ポリオキシエチレン（２５モル）モノスチレン化フェニルエーテル
　Ｂ－５：ポリオキシエチレン（２３モル）トリベンジルフェニルエーテル
　Ｂ－６：ポリオキシエチレン（１５モル）ベンジルフェニルエーテル
　Ｂ－７：ポリオキシエチレン（８モル）ポリオキシプロピレン（８モル）ランダム付加型トリスチレン化フェニルエーテル
　Ｂ－８：ポリオキシエチレン（１０．５モル）トリスチレン化フェニルエーテル
　Ｂ－９：ポリオキシエチレン（３０モル）トリスチレン化フェニルエーテル
　Ｂ－１０：ポリオキシエチレン（４０モル）トリスチレン化フェニルエーテル
　Ｂ－１１：ポリオキシエチレン（５０モル）トリスチレン化フェニルエーテル
　Ｂ－１２：ポリオキシエチレン（１５モル）フェニルエーテル
　Ｂ－１３：ポリオキシエチレン（１０モル）ポリオキシプロピレン（５モル）ブロック付加型フェニルエーテル
　Ｂ－１４：ポリオキシエチレン（１５モル）安息香酸エステル
　Ｂ－１５：ポリオキシエチレン（１８モル）安息香酸エステル
　Ｂ－１６：ポリオキシエチレン（１５モル）ｔ－ブチルフェニルエーテル
　Ｂ－１７：ポリオキシエチレン（２５モル）ｔ－ブチルフェニルエーテル
　ｂ－１：ポリオキシエチレン（７モル）トリスチレン化フェニルエーテル
　ｂ－２：ポリオキシエチレン（５モル）トリスチレン化フェニルエーテル
　ｂ－３：ポリオキシエチレン（１０モル）ステアリルエーテル
　ｂ－４：ポリオキシエチレン（７モル）ステアリルエーテル
　ｂ－５：ポリオキシエチレン（１０モル）Ｃ１４～Ｃ６０アルキルエーテル
　※１：２５℃乳化性試験及び８０℃乳化性試験のどちらの方法でも乳化できなかったため、評価未実施
　※２：２５℃乳化性試験及び８０℃乳化性試験において、２５℃及び８０℃にてスポイトでの滴下が行えないため、試験未実施
を示す。
　（実施例３４～６６）
　実施例３４～６６の処理剤の調製
　実施例３４～６６は、ジエステル化合物として実施例１～３３の各ジエステル化合物（Ｅ－１～Ｅ－３３）を使用した。また、その他成分（界面活性剤、平滑剤、脂肪族アルコール、又はポリエーテル変性シリコーン）として下記に示されるＣ－１～Ｃ－３３をそれぞれ使用した。表２に示される各成分を所定の割合で混合することにより、実施例３４～６６の処理剤を調製した。
Figure JPOXMLDOC01-appb-T000005
 　表２において
　Ｃ－１：ポリオキシエチレン（３モル）ラウリルエ一テル硫酸エステルトリエタノールアミン塩
　Ｃ－２：ラウリル硫酸ナトリウム
　Ｃ－３：ラウリルホスフェートカリウム塩
　Ｃ－４：オクチルホスフェートカリウム塩
　Ｃ－５：ステアリルホスフェートカリウム塩
　Ｃ－６：ジオクチルスルホコハク酸ナトリウム
　Ｃ－７：ドデシルベンゼンスルホン酸ナトリウム
　Ｃ－８：牛脂硫酸エステルナトリウム塩
　Ｃ－９：Ｃ１４～１６アルキルスルホン酸ナトリウム
　Ｃ－１０：ポリオキシエチレン（６モル）ラウリルエ一テル
　Ｃ－１１：ポリオキシエチレン（６モル）ラウリルエ一テルのメチルエーテル
　Ｃ－１２：ポリオキシエチレン（２モル）ポリオキシプロピレン（６モル）ラウリルエーテル
　Ｃ－１３：ポリオキシエチレン（６モル）トリスチレン化フェニルエーテル
　Ｃ－１４：ポリオキシエチレン（２０モル）硬化ヒマシ油エステル
　Ｃ－１５：ポリオキシエチレン（３０モル）ひまし油エステル
　Ｃ－１６：ポリオキシエチレン（２０モル）硬化ヒマシ油エステルのマレイン酸及びステアリン酸エステル
　Ｃ－１７：ポリオキシエチレン（２５モル）硬化ひまし油エステルのオレイン酸エステル
　Ｃ－１８：ポリオキシエチレン（１０モル）ひまし油脂肪酸
　Ｃ－１９：ポリオキシエチレン（１０モル）ヤシ油脂肪酸
　Ｃ－２０：ポリオキシエチレン（１０モル）ラウリルアミン
　Ｃ－２１：ポリオキシエチレン（１５モル）牛脂アミン
　Ｃ－２２：ポリオキシエチレン（２０モル）ソルビタンモノオレエート
　Ｃ－２３：ポリオキシエチレン（２０モル）ソルビタンモノステアレート
　Ｃ－２４：ポリオキシエチレン（２０モル）ソルビタントリオレエート
　Ｃ－２５：ソルビタンモノオレエート
　Ｃ－２６：ソルビタンモノステアレート
　Ｃ－２７：パーム油
　Ｃ－２８：オレイン酸カリウム
　Ｃ－２９：オレイルアルコール
　Ｃ－３０：オクチルアルコール
　Ｃ－３１：２－エチルヘキサノール
　Ｃ－３２：プロピレングリコール
　Ｃ－３３：ポリエーテル変性シリコーン
を示す。
　＜試験区分２（５％水溶液の調製）＞
　２００ｍＬのビーカーに２５℃の水９５ｇを秤量した。これを４５０ｒｐｍで撹拌しつつ、２５℃の各実施例及び各比較例記載のエステル化合物を含む処理剤を５ｇ加えた後、５分間撹拌して５％水溶液を調製した。
　＜試験区分３（短繊維の調製）＞
　原料繊維（繊度１．３ｄｔｅｘ、長さ３８ｍｍのポリエチレンテレフタレート短繊維）５ｇに対して、試験区分２で調製した各例の５％水溶液をさらに水で希釈して調製した０．２％水溶液５ｇをスプレーを用いて均一に付着させ、８０℃の乾燥機で１時間乾燥した。
　得られた短繊維試料について、下記に示されるように耐久親水性、初期親水性、初期親水耐久性の評価を行った。
　＜試験区分４（評価）＞
　・耐久親水性
（１）試験区分３で得た短繊維試料５ｇを、「ＮＯＮＷＯＶＥＮＳ　ＳＴＡＮＤＡＲＤ　ＰＲＯＣＥＤＵＲＥＳ　２０１５　ＥＤＩＴＩＯＮ」（ＥＤＡＮＡ（Ｅｕｒｏｐｅａｎ　Ｄｉｓｐｏｓａｂｌｅｓ　Ａｎｄ　Ｎｏｎｗｏｖｅｎｓ　Ａｓｓｏｃｉａｔｉｏｎ）発行）中のＳＴＡＮＤＡＲＤ　ＰＲＯＣＥＤＵＲＥ：ＮＷＳＰ　０１０．１．Ｒ０（１５）の５．１項記載のワイヤーバスケットに均一に詰める。
（２）１Ｌビーカーに１０００ｇの２５℃±１℃の水を秤量する。
（３）短繊維試料が入ったワイヤーバスケットを液面２５ｍｍの高さから水中へ落とす。
（４）ワイヤーバスケット全体が液面より下へ沈むまでの時間を測定する。
（５）ワイヤーバスケットから短繊維試料を取り出し、水分率が５０％になるまで脱水後、８０℃で１時間乾燥する。
（６）（２）～（５）の工程を、ワイヤーバスケットが６０秒以内に沈まなくなるまで繰り返す。
　下記評価基準に基づく結果を表１，２の「耐久親水性」欄に示した。
　・耐久親水性の評価基準
　◎（優）：６０秒以内にワイヤーバスケット全体が水中へ沈む回数が１０回以上の場合
　○（良）：６０秒以内にワイヤーバスケット全体が水中へ沈む回数が５回以上且つ１０回未満の場合
　×（不良）：６０秒以内にワイヤーバスケット全体が水中へ沈む回数が５回未満の場合
　・初期親水性
（１）試験区分３で得た短繊維試料５ｇを、上記「ＳＴＡＮＤＡＲＤ　ＰＲＯＣＥＤＵＲＥ：ＮＷＳＰ　０１０．１．Ｒ０（１５）」の５．１項記載のワイヤーバスケットに均一に詰める。
（２）１Ｌビーカーに１０００ｇの２５℃±１℃の水を秤量する。
（３）短繊維試料が入ったワイヤーバスケットを液面２５ｍｍの高さから水中へ落とす。
（４）ワイヤーバスケット全体が液面より下へ沈むまでの時間を測定する。
　下記評価基準に基づく結果を表１，２の「初期親水性」欄に示した。
　・初期親水性の評価基準
　◎（優）：５秒以内にワイヤーバスケット全体が水中へ沈む場合
　×（不良）：ワイヤーバスケット全体が水中へ沈むのに５秒超かかる場合
　・初期親水耐久性
（１）試験区分３で得た短繊維試料５ｇを、上記「ＳＴＡＮＤＡＲＤ　ＰＲＯＣＥＤＵＲＥ：ＮＷＳＰ　０１０．１．Ｒ０（１５）」の５．１項記載のワイヤーバスケットに均一に詰める。
（２）１Ｌビーカーに１０００ｇの２５℃±１℃の水を秤量する。
（３）短繊維試料が入ったワイヤーバスケットを液面２５ｍｍの高さから水中へ落とす。
（４）ワイヤーバスケット全体が液面より下へ沈むまでの時間を測定する。
（５）ワイヤーバスケットから短繊維試料を取り出し、水分率が５０％になるまで脱水後、８０℃で１時間乾燥する。
（６）（２）～（５）の工程を、ワイヤーバスケットが１０秒以内に沈まなくなるまで繰り返す。
　下記評価基準に基づく結果を表１，２の「初期親水耐久性」欄に示した。
　・初期親水耐久性の評価基準
　◎（優）：１０秒以内にワイヤーバスケット全体が水中へ沈む回数が８回以上の場合
　○（良）：１０秒以内にワイヤーバスケット全体が水中へ沈む回数が４回以上且つ８回未満の場合
　×（不良）：１０秒以内にワイヤーバスケット全体が水中へ沈む回数が４回未満の場合
　・２５℃乳化性
（１）２５℃の水９５ｇを２００ｍＬビーカーに加え、２５℃のウォーターバスで保温しつつ、４５０ｒｐｍで撹拌する。
（２）５ｇの２５℃又は８０℃に加温した、各例記載の処理剤をスポイトで滴下する。
（３）滴下後、５分間撹拌を行い、撹拌直後の乳化状態を確認する。
　下記評価基準に基づく結果を表１，２の「２５℃乳化性」欄に示した。
　・２５℃乳化性の評価基準
　◎（優）：均一に分散又は乳化し、浮遊物又は沈殿物が無い場合
　×（不良）：均一に分散又は乳化しておらず、浮遊物又は沈殿物が残っている場合
　・８０℃乳化性
（１）８０℃の水９５ｇを２００ｍＬビーカーに加え、８０℃の湯煎で保温しつつ、４５０ｒｐｍで撹拌する。
（２）５ｇの２５℃又は８０℃に加温した、各例記載の処理剤をスポイトで滴下する。
（３）滴下後、５分間撹拌を行い、攪拌直後の乳化状態を確認する。
　下記評価基準に基づく結果を表１，２の「８０℃乳化性」欄に示した。
　・８０℃乳化性の評価基準
　◎（優）：均一に分散又は乳化し、浮遊物又は沈殿物が無い場合
　×（不良）：均一に分散又は乳化しておらず、浮遊物又は沈殿物が残っている場合
　・ハンドリング性
（１）２５℃又は８０℃の各例記載の処理剤２０ｇを１００ｍＬビーカーに加える。
（２）１０ｃｍの高さでビーカーを持ち、ビーカーの口を９０度傾ける。
（３）２０秒以内にビーカーから各例の処理剤がビーカーから流出するか確認し、流出した場合は、流動性ありと判断する。
　下記評価基準に基づく結果を表１，２の「ハンドリング性」欄に示した。
　・ハンドリング性の評価基準
　◎（優）：２５℃及び８０℃の両方の条件で、流動性がある場合
　○（良）：８０℃の条件でのみ、流動性がある場合
　×（不良）：２５℃及び８０℃の両方の条件において、流動性が無い場合
　以上表１，２の結果からも明らかなように、本発明によれば、合成繊維に対して優れた初期親水耐久性等の親水性特性を付与することができる。また、水系媒体に分散させた際に優れた乳化安定性が得られる。また、取扱時の流動性に優れ、ハンドリング性を向上できる。

Claims (9)

  1. 　炭素繊維以外の合成繊維の処理に使用される合成繊維用処理剤であって、
    　炭素数１～１６であるジカルボン酸及びそのエステル形成性誘導体から選ばれる少なくとも一つを含むＡ成分と、
    　分子中に芳香環を有する１価ヒドロキシ化合物１モルに対し炭素数２～４のアルキレンオキサイドを１０モル超且つ１００モル以下の割合で付加させた化合物、及び分子中に芳香環を有する１価カルボン酸１モルに対し炭素数２～４のアルキレンオキサイドを１０モル超且つ１００モル以下の割合で付加させた化合物から選ばれる少なくとも一つを含むＢ成分と
    から形成されたジエステル化合物を含むことを特徴とする合成繊維用処理剤。
  2. 　前記Ａ成分が、炭素数１～１６の不飽和脂肪族ジカルボン酸、芳香族ジカルボン酸、及びこれらのエステル形成性誘導体から選ばれる少なくとも一つを含む請求項１に記載の合成繊維用処理剤。
  3. 　前記Ｂ成分が、分子中に芳香環を有する１価ヒドロキシ化合物１モルに対し炭素数２～４のアルキレンオキサイドを１０モル超且つ５０モル以下の割合で付加させた化合物、及び分子中に芳香環を有する１価カルボン酸１モルに対し炭素数２～４のアルキレンオキサイドを１０モル超且つ５０モル以下の割合で付加させた化合物から選ばれる少なくとも一つを含む請求項１又は２に記載の合成繊維用処理剤。
  4. 　前記Ｂ成分が、分子中に芳香環を有する１価ヒドロキシ化合物１モルに対し炭素数２～４のアルキレンオキサイドを１５モル以上且つ２５モル以下の割合で付加させた化合物、及び分子中に芳香環を有する１価カルボン酸１モルに対し炭素数２～４のアルキレンオキサイドを１５モル以上且つ２５モル以下の割合で付加させた化合物から選ばれる少なくとも一つを含む請求項１～３のいずれか一項に記載の合成繊維用処理剤。
  5. 　前記Ｂ成分を形成することとなる前記分子中に芳香環を有する１価ヒドロキシ化合物が、分子中に２以上の芳香環を有する１価ヒドロキシ化合物である請求項１～４のいずれか一項に記載の合成繊維用処理剤。
  6. 　更にアニオン界面活性剤、カチオン界面活性剤、非イオン界面活性剤、平滑剤、脂肪族アルコール、及びポリエーテル変性シリコーンから選ばれる少なくとも一つを含む請求項１～５のいずれか一項に記載の合成繊維用処理剤。
  7. 　請求項１～６のいずれか一項に記載の合成繊維用処理剤が付着していることを特徴とする合成繊維。
  8. 　前記合成繊維が、疎水性のものである請求項７に記載の合成繊維。
  9. 　前記合成繊維が、ポリエステルである請求項８に記載の合成繊維。
PCT/JP2020/015208 2019-06-13 2020-04-02 合成繊維用処理剤及び合成繊維 WO2020250550A1 (ja)