WO2020115028A1 - Électrode pour l'évolution électrolytique d'un gaz - Google Patents
Électrode pour l'évolution électrolytique d'un gaz Download PDFInfo
- Publication number
- WO2020115028A1 WO2020115028A1 PCT/EP2019/083448 EP2019083448W WO2020115028A1 WO 2020115028 A1 WO2020115028 A1 WO 2020115028A1 EP 2019083448 W EP2019083448 W EP 2019083448W WO 2020115028 A1 WO2020115028 A1 WO 2020115028A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- catalytic layer
- tin
- platinum
- oxides
- metal
- Prior art date
Abstract
Priority Applications (11)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
AU2019391296A AU2019391296A1 (en) | 2018-12-03 | 2019-12-03 | Electrode for electrolytic evolution of gas |
IL283404A IL283404B2 (en) | 2018-12-03 | 2019-12-03 | Electrode for electrolytic evolution of gas |
BR112021010421-6A BR112021010421A2 (pt) | 2018-12-03 | 2019-12-03 | Eletrodo para evolução eletrolítica de gás |
CN201980079027.5A CN113166956A (zh) | 2018-12-03 | 2019-12-03 | 用于电解析出气体的电极 |
JP2021531113A JP2022514211A (ja) | 2018-12-03 | 2019-12-03 | ガスの電解発生用の電極 |
US17/292,885 US20210404076A1 (en) | 2018-12-03 | 2019-12-03 | Electrode for electrolytic evolution of gas |
MX2021006438A MX2021006438A (es) | 2018-12-03 | 2019-12-03 | Electrodo para el desprendimiento electrolitico de gas. |
KR1020217020705A KR20210096661A (ko) | 2018-12-03 | 2019-12-03 | 가스의 전해 발생용 전극 |
EP19812784.7A EP3891322A1 (fr) | 2018-12-03 | 2019-12-03 | Électrode pour l'évolution électrolytique d'un gaz |
CA3120540A CA3120540A1 (fr) | 2018-12-03 | 2019-12-03 | Electrode pour l'evolution electrolytique d'un gaz |
ZA2021/03111A ZA202103111B (en) | 2018-12-03 | 2021-05-07 | Electrode for electrolytic evolution of gas |
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
IT102018000010760A IT201800010760A1 (it) | 2018-12-03 | 2018-12-03 | Elettrodo per evoluzione elettrolitica di gas |
IT102018000010760 | 2018-12-03 |
Publications (1)
Publication Number | Publication Date |
---|---|
WO2020115028A1 true WO2020115028A1 (fr) | 2020-06-11 |
Family
ID=65685882
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/EP2019/083448 WO2020115028A1 (fr) | 2018-12-03 | 2019-12-03 | Électrode pour l'évolution électrolytique d'un gaz |
Country Status (15)
Country | Link |
---|---|
US (1) | US20210404076A1 (fr) |
EP (1) | EP3891322A1 (fr) |
JP (1) | JP2022514211A (fr) |
KR (1) | KR20210096661A (fr) |
CN (1) | CN113166956A (fr) |
AU (1) | AU2019391296A1 (fr) |
BR (1) | BR112021010421A2 (fr) |
CA (1) | CA3120540A1 (fr) |
IL (1) | IL283404B2 (fr) |
IT (1) | IT201800010760A1 (fr) |
MX (1) | MX2021006438A (fr) |
SA (1) | SA521422103B1 (fr) |
TW (1) | TW202022166A (fr) |
WO (1) | WO2020115028A1 (fr) |
ZA (1) | ZA202103111B (fr) |
Cited By (1)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
EP4245890A4 (fr) * | 2020-11-12 | 2024-10-09 | Lg Chem Ltd | Électrode pour électrolyse |
Families Citing this family (1)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
CN113151885B (zh) * | 2021-03-15 | 2023-03-21 | 广州鸿葳科技股份有限公司 | 一种电镀用钛阳极及其制备方法 |
Citations (7)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
EP0153586A1 (fr) | 1984-01-31 | 1985-09-04 | TDK Corporation | Electrode pour électrolyse |
JPS62243790A (ja) | 1986-04-15 | 1987-10-24 | Osaka Soda Co Ltd | 塩化アルカリ電解用陽極 |
JPS62260088A (ja) * | 1986-03-31 | 1987-11-12 | Permelec Electrode Ltd | 電解用電極及びその製造方法 |
JP2008050675A (ja) * | 2006-08-28 | 2008-03-06 | Ishifuku Metal Ind Co Ltd | 電解用電極 |
WO2012081635A1 (fr) | 2010-12-15 | 2012-06-21 | 旭化成ケミカルズ株式会社 | Électrode pour électrolyse, cellule électrolytique et procédé de production d'électrode pour électrolyse |
US20130186750A1 (en) | 2010-11-26 | 2013-07-25 | Industrie De Nora S.P.A. | Anode for electrolytic evolution of chlorine |
WO2016083319A1 (fr) | 2014-11-24 | 2016-06-02 | Industrie De Nora S.P.A. | Anode de dégagement électrolytique de chlore |
Family Cites Families (4)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
ITMI20031543A1 (it) * | 2003-07-28 | 2005-01-29 | De Nora Elettrodi Spa | Elettrodo per processi elettrochimici e metodo per il suo ottenimento |
JP4476759B2 (ja) * | 2004-09-17 | 2010-06-09 | 多摩化学工業株式会社 | 電解用電極の製造方法、及びこの電解用電極を用いた水酸化第四アンモニウム水溶液の製造方法 |
IT1391767B1 (it) * | 2008-11-12 | 2012-01-27 | Industrie De Nora Spa | Elettrodo per cella elettrolitica |
CN108603296A (zh) * | 2015-12-14 | 2018-09-28 | 奥克海德莱克斯控股有限公司 | 用于高效地操作电化学电池的方法和系统 |
-
2018
- 2018-12-03 IT IT102018000010760A patent/IT201800010760A1/it unknown
-
2019
- 2019-12-02 TW TW108143844A patent/TW202022166A/zh unknown
- 2019-12-03 BR BR112021010421-6A patent/BR112021010421A2/pt unknown
- 2019-12-03 JP JP2021531113A patent/JP2022514211A/ja active Pending
- 2019-12-03 IL IL283404A patent/IL283404B2/en unknown
- 2019-12-03 WO PCT/EP2019/083448 patent/WO2020115028A1/fr active Application Filing
- 2019-12-03 AU AU2019391296A patent/AU2019391296A1/en active Pending
- 2019-12-03 EP EP19812784.7A patent/EP3891322A1/fr active Pending
- 2019-12-03 CN CN201980079027.5A patent/CN113166956A/zh active Pending
- 2019-12-03 KR KR1020217020705A patent/KR20210096661A/ko unknown
- 2019-12-03 MX MX2021006438A patent/MX2021006438A/es unknown
- 2019-12-03 US US17/292,885 patent/US20210404076A1/en active Pending
- 2019-12-03 CA CA3120540A patent/CA3120540A1/fr active Pending
-
2021
- 2021-05-07 ZA ZA2021/03111A patent/ZA202103111B/en unknown
- 2021-05-25 SA SA521422103A patent/SA521422103B1/ar unknown
Patent Citations (9)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
EP0153586A1 (fr) | 1984-01-31 | 1985-09-04 | TDK Corporation | Electrode pour électrolyse |
US4626334A (en) | 1984-01-31 | 1986-12-02 | Tdk Corporation | Electrode for electrolysis |
JPS62260088A (ja) * | 1986-03-31 | 1987-11-12 | Permelec Electrode Ltd | 電解用電極及びその製造方法 |
JPS62243790A (ja) | 1986-04-15 | 1987-10-24 | Osaka Soda Co Ltd | 塩化アルカリ電解用陽極 |
JP2008050675A (ja) * | 2006-08-28 | 2008-03-06 | Ishifuku Metal Ind Co Ltd | 電解用電極 |
US20130186750A1 (en) | 2010-11-26 | 2013-07-25 | Industrie De Nora S.P.A. | Anode for electrolytic evolution of chlorine |
WO2012081635A1 (fr) | 2010-12-15 | 2012-06-21 | 旭化成ケミカルズ株式会社 | Électrode pour électrolyse, cellule électrolytique et procédé de production d'électrode pour électrolyse |
US20130334037A1 (en) | 2010-12-15 | 2013-12-19 | Asahi Kasei Chemicals Corporation | Electrode for electrolysis, electrolytic cell and production method for electrode for electrolysis |
WO2016083319A1 (fr) | 2014-11-24 | 2016-06-02 | Industrie De Nora S.P.A. | Anode de dégagement électrolytique de chlore |
Cited By (1)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
EP4245890A4 (fr) * | 2020-11-12 | 2024-10-09 | Lg Chem Ltd | Électrode pour électrolyse |
Also Published As
Publication number | Publication date |
---|---|
IL283404B1 (en) | 2024-06-01 |
BR112021010421A2 (pt) | 2021-08-24 |
MX2021006438A (es) | 2021-07-02 |
IT201800010760A1 (it) | 2020-06-03 |
JP2022514211A (ja) | 2022-02-10 |
CN113166956A (zh) | 2021-07-23 |
ZA202103111B (en) | 2022-10-26 |
CA3120540A1 (fr) | 2020-06-11 |
IL283404A (en) | 2021-07-29 |
IL283404B2 (en) | 2024-10-01 |
AU2019391296A1 (en) | 2021-06-03 |
TW202022166A (zh) | 2020-06-16 |
EP3891322A1 (fr) | 2021-10-13 |
SA521422103B1 (ar) | 2024-03-24 |
KR20210096661A (ko) | 2021-08-05 |
US20210404076A1 (en) | 2021-12-30 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
US4297195A (en) | Electrode for use in electrolysis and process for production thereof | |
EA034359B1 (ru) | Электрод для электролитических процессов | |
EP0715002B1 (fr) | Solutions de revêtement stables pour la préparation de revêtements électrocatalytiques d'oxydes mixtes sur des substrats métalliques ou revêtus de métaux et procédé pour la préparation des anodes dimensionnellement stables utilitsant ces solutions | |
AU2019391296A1 (en) | Electrode for electrolytic evolution of gas | |
US9090983B2 (en) | Electrode for electrochemical processes and method for obtaining the same | |
KR20220091502A (ko) | 수소의 전기화학적 발생을 위한 전극 | |
IT201800006544A1 (it) | Anodo per evoluzione elettrolitica di cloro | |
RU2789597C2 (ru) | Электрод для электролитического выделения газа | |
EP4146844B1 (fr) | Électrode pour l'évolution électrochimique d'hydrogène | |
WO2024008895A2 (fr) | Électrode pour évolution électrolytique de gaz | |
NO138664B (no) | Elektrode til bruk ved elektrokjemiske prosesser, spesielt som anode ved kloralkalielektrolyse |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
121 | Ep: the epo has been informed by wipo that ep was designated in this application |
Ref document number: 19812784 Country of ref document: EP Kind code of ref document: A1 |
|
DPE1 | Request for preliminary examination filed after expiration of 19th month from priority date (pct application filed from 20040101) | ||
ENP | Entry into the national phase |
Ref document number: 3120540 Country of ref document: CA |
|
ENP | Entry into the national phase |
Ref document number: 2021531113 Country of ref document: JP Kind code of ref document: A |
|
ENP | Entry into the national phase |
Ref document number: 2019391296 Country of ref document: AU Date of ref document: 20191203 Kind code of ref document: A |
|
NENP | Non-entry into the national phase |
Ref country code: DE |
|
REG | Reference to national code |
Ref country code: BR Ref legal event code: B01A Ref document number: 112021010421 Country of ref document: BR |
|
ENP | Entry into the national phase |
Ref document number: 20217020705 Country of ref document: KR Kind code of ref document: A |
|
ENP | Entry into the national phase |
Ref document number: 2019812784 Country of ref document: EP Effective date: 20210705 |
|
ENP | Entry into the national phase |
Ref document number: 112021010421 Country of ref document: BR Kind code of ref document: A2 Effective date: 20210528 |
|
WWE | Wipo information: entry into national phase |
Ref document number: 521422103 Country of ref document: SA |