WO2019213192A1 - Films multi-couches - Google Patents
Films multi-couches Download PDFInfo
- Publication number
- WO2019213192A1 WO2019213192A1 PCT/US2019/030105 US2019030105W WO2019213192A1 WO 2019213192 A1 WO2019213192 A1 WO 2019213192A1 US 2019030105 W US2019030105 W US 2019030105W WO 2019213192 A1 WO2019213192 A1 WO 2019213192A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- multilayer film
- skin layer
- polypropylene
- thickness
- layer
- Prior art date
Abstract
La présente invention concerne un film multi-couches comprenant une première couche de peau en polypropylène et une seconde couche de peau en polypropylène. Le film multi-couches comprend une couche centrale entre la première couche de peau en polypropylène et la seconde couche de peau en polypropylène. La couche centrale comprend du polypropylène et un agent moussant.
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
US201862665625P | 2018-05-02 | 2018-05-02 | |
US62/665,625 | 2018-05-02 |
Publications (1)
Publication Number | Publication Date |
---|---|
WO2019213192A1 true WO2019213192A1 (fr) | 2019-11-07 |
Family
ID=68386596
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/US2019/030105 WO2019213192A1 (fr) | 2018-05-02 | 2019-05-01 | Films multi-couches |
Country Status (2)
Country | Link |
---|---|
TW (1) | TW201946782A (fr) |
WO (1) | WO2019213192A1 (fr) |
Citations (5)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US4828915A (en) * | 1981-08-05 | 1989-05-09 | American National Can Company | Oriented evoh/nylon blend film |
US5858552A (en) * | 1996-03-15 | 1999-01-12 | Mobil Oil Corporation | Film structure |
WO2005032815A1 (fr) * | 2003-10-01 | 2005-04-14 | Toray Plastics (America), Inc. | Films barrieres multicouches de polypropylene |
US20050136235A1 (en) * | 2003-06-30 | 2005-06-23 | Rockwell Anthony L. | Multilayer densified surface to improve air flow resistance and structural properties |
US20130327476A1 (en) * | 2011-04-12 | 2013-12-12 | The Procter & Gamble Company | Multi-Layer Films And Methods Of Forming Same |
-
2019
- 2019-05-01 WO PCT/US2019/030105 patent/WO2019213192A1/fr active Application Filing
- 2019-05-02 TW TW108115207A patent/TW201946782A/zh unknown
Patent Citations (5)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US4828915A (en) * | 1981-08-05 | 1989-05-09 | American National Can Company | Oriented evoh/nylon blend film |
US5858552A (en) * | 1996-03-15 | 1999-01-12 | Mobil Oil Corporation | Film structure |
US20050136235A1 (en) * | 2003-06-30 | 2005-06-23 | Rockwell Anthony L. | Multilayer densified surface to improve air flow resistance and structural properties |
WO2005032815A1 (fr) * | 2003-10-01 | 2005-04-14 | Toray Plastics (America), Inc. | Films barrieres multicouches de polypropylene |
US20130327476A1 (en) * | 2011-04-12 | 2013-12-12 | The Procter & Gamble Company | Multi-Layer Films And Methods Of Forming Same |
Also Published As
Publication number | Publication date |
---|---|
TW201946782A (zh) | 2019-12-16 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
EP2551754A2 (fr) | Feuille de protection pour panneau tactile et son procédé de fabrication | |
JPH08276527A (ja) | 包装用クリ−ンフィルムおよびそれを使用した包装用袋 | |
KR102039919B1 (ko) | 가스 배리어성 필름 | |
JP2015096877A (ja) | ハードコートフィルムおよびハードコートフィルムの製造方法 | |
EP2447177A1 (fr) | Sac de conditionnement antistatique pour module à cristaux liquides et procédé de conditionnement de modules à cristaux liquides | |
WO2019213192A1 (fr) | Films multi-couches | |
KR101316705B1 (ko) | 디스플레이 제품 포장용 폼 합지 폴리에틸렌 필름 | |
JP5628132B2 (ja) | 易滑及び離型性熱可塑性樹脂フィルム並びに該熱可塑性樹脂フィルムからなる包装体及び離型又は加工プロセス用支持体フィルム | |
JP2609779B2 (ja) | チップ型電子部品包装用カバーテープ | |
KR100737617B1 (ko) | 웨이퍼용 곤포체 | |
BRPI0504204A (pt) | aperfeiçoamento introduzido em produtos laminados para utilização em embalagens contendo partìculas anti-blocantes | |
CN214032317U (zh) | 防碰oca光学胶膜及其结构 | |
KR101209194B1 (ko) | 자동차 도막 보호필름용 이형필름 | |
JPH0767774B2 (ja) | チップ型電子部品包装用カバーテープ | |
JP2008020856A (ja) | 液晶表示パネルの保護フィルム及び液晶表示パネルの保護方法 | |
US10933610B2 (en) | Display screen and screen body cutting method | |
CN217863171U (zh) | 一种高透光性双抗离型膜 | |
JP6789213B2 (ja) | 紫外線吸収層を有する包装用積層体 | |
JP2901857B2 (ja) | チップ型電子部品包装用カバーテープ | |
JP3030448B2 (ja) | 包装方法 | |
CN219637140U (zh) | 一种抗静电硅胶保护膜 | |
JP3055187U (ja) | 合成樹脂製機器カバー | |
JP5428184B2 (ja) | 包装材及びそれを用いた包装袋 | |
CN210103807U (zh) | 一种无硅离型膜 | |
KR101867878B1 (ko) | 투과성 필름과 이를 포함하는 포장필름 및 그 제조방법 |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
121 | Ep: the epo has been informed by wipo that ep was designated in this application |
Ref document number: 19796840 Country of ref document: EP Kind code of ref document: A1 |
|
NENP | Non-entry into the national phase |
Ref country code: DE |
|
122 | Ep: pct application non-entry in european phase |
Ref document number: 19796840 Country of ref document: EP Kind code of ref document: A1 |