WO2019188277A1 - カーペット - Google Patents

カーペット Download PDF

Info

Publication number
WO2019188277A1
WO2019188277A1 PCT/JP2019/010194 JP2019010194W WO2019188277A1 WO 2019188277 A1 WO2019188277 A1 WO 2019188277A1 JP 2019010194 W JP2019010194 W JP 2019010194W WO 2019188277 A1 WO2019188277 A1 WO 2019188277A1
Authority
WO
WIPO (PCT)
Prior art keywords
fiber
base fabric
carpet
fibers
layer
Prior art date
Application number
PCT/JP2019/010194
Other languages
English (en)
French (fr)
Inventor
原田大
土倉弘至
Original Assignee
東レ株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 東レ株式会社 filed Critical 東レ株式会社
Priority to EP19774612.6A priority Critical patent/EP3777617A4/en
Priority to JP2019519426A priority patent/JP7251475B2/ja
Publication of WO2019188277A1 publication Critical patent/WO2019188277A1/ja

Abstract

高い難燃性を備えたカーペットを提供するため、 ｉ）パイル層と、ｉｉ）高温収縮率が３％以下で、且つＩＳＯ２２００７－３（２００８年）に準拠する熱伝導率が０．０６０Ｗ／ｍ・Ｋ以下である非溶融繊維Ａと、ＪＩＳ　Ｋ７２０１－２（２００７年）に準拠するＬＯＩ値が２５以上である炭化型熱可塑性繊維Ｂとを含む基布層から成る表皮層と、ｉｉｉ）裏打ち層を備えたカーペットとする。

Description

カーペット
　本発明は、カーペットに関する。
　鉄道車輌、自動車、船舶等の乗物用座席や、家庭、オフィス等のフロアなどに、タフテッドカーペットは多く使用されている。一方、火災時の安全性を高めるために、これらのインテリア製品において難燃化が強く要望されている。その難燃性を付与するために、特許文献１で、パイルの表面を難燃剤により処理したものが開示されている。また、特許文献２では、パイルに難燃剤を練り込む方法として、ナイロン６とナイロン６６の混合物に無機難燃化剤を添加した糸を用いたカーペットが開示されている。さらに、特許文献３では、メタアラミドと難燃レーヨンを有する難燃性繊維を用いたタフトカーペット基布用不織布にする方法が開示されている。
　一方、特許文献４、５では、裏面に設けられる裏貼層に難燃剤を含有せしめる方法が開示されている。さらに、特許文献６では、予め基布に難燃剤を含浸する方法が開示されている。
特開平５－３３２７０号公報 特開昭５８－１０４２１８号公報 特開昭５０－６５６４８号公報 特開平６－１６６１４８号公報 特開２００１－７３２７５号公報 特開２０１２－２２３３６６号公報
　しかし、特許文献１記載のような表面処理では、カーペットのパイル表面の風合いが低下し、カーペットを靴等で使用する際に、表面処理剤が落脱するため、難燃性が持続できないという問題があった。また、特許文献２記載の方法では、パイルとなる原糸に練り込むため設備が大がかりとなるほか、練り込む粒子の濃度が高い場合には、曳糸性が低下し、糸品質が安定しない問題があった。特許文献３記載の方法では、１５ｍｍ高さの炎で１０秒という短時間の接炎時での難燃効果しか確認されておらず、単に基布を難燃性の高い繊維としたのみでは難燃性の効果は十分とはいえなかった。特許文献４、５記載の方法では、裏面だけの難燃性付与であるため、表面パイルの燃焼は抑えられず、難燃性としては不十分なものであった。さらに、特許文献６記載の方法では、難燃剤の種類と含浸量を規定することによって経時的なブリードアウト等の問題を改善できることが記載されているが、長期保管や、移送中の高温多湿条件下でのブリードアウトの問題を解決する余地があるうえ、難燃剤と含浸樹脂を付与することによってカーペット全体が重くなるという問題もあり、適度な重さのカーペットを得ようとすれば難燃性が不十分であった。
　したがって本発明は、高い難燃性を備えたカーペットを提供することを課題とする。
　本発明は上記課題を解決するために、次のような手段を採用する。
　（１）ｉ）パイル層と、
ｉｉ）高温収縮率が３％以下で、且つＩＳＯ２２００７－３（２００８年）に準拠する熱伝導率が０．０６０Ｗ／ｍ・Ｋ以下である非溶融繊維Ａと、ＪＩＳ　Ｋ　７２０１－２（２００７年）に準拠するＬＯＩ値が２５以上である炭化型熱可塑性繊維Ｂとを含む基布層
から成る表皮層と、
ｉｉｉ）裏打ち層を備えたカーペット。
　（２）前記基布層の非溶融繊維Ａの含有率が２０～８０重量％である（１）に記載のカーペット。
　（３）前記基布層の炭化型熱可塑性繊維Ｂの含有率が２０～８０重量％である（１）または（２）に記載のカーペット。
　（４）前記基布層の非溶融繊維Ａが、耐炎化繊維またはメタアラミド系繊維である（１）～（３）の何れかに記載のカーペット。
　（５）前記基布層の炭化型熱可塑性繊維Ｂが、異方性溶融ポリエステル、難燃性ポリ（アルキレンテレフタレート）、難燃性ポリ（アクリロニトリルブタジエンスチレン）、難燃性ポリスルホン、ポリ（エーテル－エーテル－ケトン）、ポリ（エーテル－ケトン－ケトン）、ポリエーテルスルホン、ポリアリレート、ポリアリーレンスルフィド、ポリフェニルスルホン、ポリエーテルイミド、ポリアミドイミドおよびこれらの混合物の群から選択される樹脂からなる繊維である（１）～（４）の何れかに記載のカーペット。
　（６）前記基布層の炭化型熱可塑性繊維Ｂの融点が３００℃以下である（１）～（５）の何れかに記載のカーペット。
　（７）前記パイル層はポリエステル繊維、ナイロン繊維、アクリル繊維、セルロース繊維、天然繊維およびこれらの混合物の群から選択される繊維を含む（１）～（６）の何れかに記載のカーペット。
　（８）前記パイル層の基布層に対する重量比が５以下である（１）～（７）の何れかに記載の難燃カーペット。
　（９）目付が３００～２５００ｇ／ｍ２の範囲である（１）～（８）の何れかに記載の難燃カーペット。
　本発明の難燃カーペットは、上記の構成を備えることにより、優れた難燃性を有している。
本発明の難燃カーペットの一例を示す概略断面図である。
　本発明は、ｉ）パイル層１と、ｉｉ）高温収縮率が３％以下で、且つＩＳＯ２２００７－３（２００８年）に準拠する熱伝導率が０．０６０Ｗ／ｍ・Ｋ以下である非溶融繊維Ａと、ＪＩＳ　Ｋ　７２０１－２（２００７年）に準拠するＬＯＩ値が２５以上である炭化型熱可塑性繊維Ｂとを含む基布層２から成る表皮層３と、ｉｉｉ）裏打ち層４を備えたカーペットである。図１は本発明の難燃カーペットの一例を示す概略断面図である。
　《高温収縮率》
　本発明において高温収縮率とは、不織布の原料となる繊維を標準状態（２０℃、相対湿度６５％）中で１２時間放置後、０．１ｃＮ／ｄｔｅｘの張力を与えて原長Ｌ０を測定し、その繊維に対して荷重を付加せずに２９０℃の乾熱雰囲気に３０分間暴露し、標準状態（２０℃、相対湿度６５％）中で十分冷却したうえで、さらに繊維に対して０．１ｃＮ／ｄｔｅｘの張力を与えて長さＬ１を測定し、Ｌ０およびＬ１から以下の式で求められる数値である。
高温収縮率＝〔（Ｌ０－Ｌ１）／Ｌ０〕×１００（％）　
　炎が近づき、熱が加わると熱可塑性繊維が溶融し、溶融した熱可塑性繊維が非溶融繊維（骨材）の表面に沿って薄膜状に広がる。さらに温度が上がると、やがて、両繊維は炭化するが、非溶融繊維の高温収縮率が３％以下であるから、高温となった接炎部近辺は収縮しにくく、炎の接していない低温部と高温度部の間で生じる熱応力による基布の破断が生じにくいので、優れた難燃性を維持することができる。この点で、高温収縮率は低いことが好ましいが、縮まずとも熱によって大幅に膨張しても、熱応力による基布の破断を生じる原因となるので、高温収縮率は－５％以上であることが好ましい。なかでも高温収縮率が０～２％であることが好ましい。
　《熱伝導率》
　熱伝導率とは、熱の伝導のしやすさを数値化したものであり、熱伝導率が小さいとは、一方の面から材料が加熱された際の、加熱されていない部分の温度上昇が小さくなることを意味する。目付２００ｇ／ｍ２、ＪＩＳ　Ｌ１９１３（２０１０）に準拠する方法で測定した厚さが２ｍｍ（密度１００ｋｇ／ｍ３）の不織布を試験体とし、ＩＳＯ２２００７－３（２００８年）に準拠する方法で測定した熱伝導率が０．０６０Ｗ／ｍ・Ｋ以下である素材は、熱を伝えにくく、カーペットの表皮層から熱した際に裏打ち層の温度上昇を抑制することができるため、カーペットの難燃性を向上できる。熱伝導率は低い方が好ましいが、入手可能な繊維材料では、０．０２０Ｗ／ｍ・Ｋ程度が上限である。
　《ＬＯＩ値》
　ＬＯＩ値は、窒素と酸素の混合気体において、物質の燃焼を持続させるのに必要な最小酸素量の容積百分率であり、ＬＯＩ値が高いほど燃え難いと言える。そこで、ＪＩＳ　Ｋ７２０１－２（２００７年）に準拠するＬＯＩ値が２５以上である熱可塑性繊維は燃えにくく、たとえ、着火しても火源を離せばすぐに消火し、通常わずかに燃え広がった部分に炭化膜を形成し、この炭化部分が延焼を防ぐことができる。ＬＯＩ値は高い方が好ましいが、現実に入手可能な物質のＬＯＩ値の上限は６５程度である。
　《発火温度》
　発火温度は、ＪＩＳ　Ｋ７１９３（２０１０年）に準拠した方法で測定した自然発火温度である。
　《融点》
　融点は、ＪＩＳ　Ｋ７１２１（２０１２年）に準拠した方法で測定した値である。１０℃／分で加熱した際の融解ピーク温度の値をいう。
　《非溶融繊維Ａ》
　本発明において、非溶融繊維Ａとは炎にさらされた際に液化せずに繊維形状を保つ繊維をいい、７００℃の温度で液化および発火しないものが好ましく、８００℃以上の温度で液化および発火しないものがさらに好ましい。上記高温収縮率が本発明で規定する範囲にある非溶融繊維として、例えば、耐炎化繊維、メタアラミド系繊維およびガラス繊維を挙げることができる。耐炎化繊維は、アクリロニトリル系、ピッチ系、セルロース系、フェノール系繊維等から選択される繊維を原料として耐炎化処理を行った繊維である。これらは単独で使用しても２種類以上を同時に使用してもよい。なかでも、高温収縮率が低くかつ、後述する炭化型熱可塑性繊維Ｂが接炎時に形成する皮膜による酸素遮断効果によって、炭素化が進行し、高温下での耐熱性がさらに向上する耐炎化繊維が好ましく、各種の耐炎化繊維の中で比重が小さく柔軟で難燃性に優れる繊維としてアクリロニトリル系耐炎化繊維がより好ましく用いられ、かかる耐炎化繊維は前駆体としてのアクリル系繊維を高温の空気中で加熱、酸化することによって得られる。市販品としては、後記する実施例および比較例で使用した、Ｚｏｌｔｅｋ社製耐炎化繊維ＰＹＲＯＮ(登録商標)の他、東邦テナックス(株)パイロメックス(Ｐｙｒｏｍｅｘ)（登録商標）等が挙げられる。また、一般にメタアラミド系繊維は高温収縮率が高く、本発明で規定する高温収縮率を満たさないが、高温収縮率を抑制処理することにより本発明の高温収縮率の範囲内としたメタアラミド系繊維であれば、好ましく使用することができる。また本発明で好ましく用いられる非溶融繊維は、非溶融繊維単独あるいは異素材と複合する方法で用いられ、繊維長は３０～１２０ｍｍの範囲内にあることが好ましく、３８～７０ｍｍの範囲内にあることがより好ましい。繊維長が３８～７０ｍｍの範囲内であれば、一般的なニードルパンチ法や水流交絡法で不織布とすることが可能であり、異素材と複合することが容易である。また、紡績糸とし、織物や編物の形態とする場合には、繊維長が３８～５１ｍｍの範囲内であれば、一般的な紡績工程で防錆糸とすることが可能である。非溶融繊維の単繊維の太さについても、特に限定されるものではないが、カード工程の通過性の点から、単繊維繊度は０．１～１０ｄｔｅｘの範囲内にあるものが好ましい。
　基布における非溶融繊維Ａの含有率が低すぎると、骨材としての機能が不十分となるためカーペットとしたときに十分な難燃性を得られなくなる傾向にある。一方、非溶融繊維Ａの含有率が高すぎても、すなわち、炭化型熱可塑性繊維Ｂの含有量が低すぎても接炎時に十分な炭化膜を形成できないため、難燃性が低下する傾向となる。そのため、基布層における非溶融繊維Ａの混率は、２０～８０重量％であるのが好ましく、３０～７０重量％であるのがより好ましい。
　《炭化型熱可塑性繊維Ｂ》
　本発明で用いる炭化型熱可塑性繊維Ｂとしては、前記ＬＯＩ値が本発明で規定する範囲にあり、かつ融点が非溶融繊維Ａの発火温度よりも低い融点を有するものであるが、具体例としては例えば、異方性溶融ポリエステル、難燃性ポリ（アルキレンテレフタレート）、難燃性ポリ（アクリロニトリルブタジエンスチレン）、難燃性ポリスルホン、ポリ（エーテル－エーテル－ケトン）、ポリ（エーテル－ケトン－ケトン）、ポリエーテルスルホン、ポリアリレート、ポリアリーレンスルフィド、ポリフェニルスルホン、ポリエーテルイミド、ポリアミドイミドおよびこれらの混合物の群から選択される熱可塑性樹脂で構成される繊維を挙げることができる。これらは単独で使用しても、２種類以上を同時に使用してもよい。ＬＯＩ値が本発明で規定する範囲にあることで、空気中での燃焼を抑制し、ポリマーが炭化しやすくなる。また、融点が非溶融繊維Ａの発火温度よりも低いことで、溶融したポリマーが非溶融繊維Ａの表面および繊維間で皮膜を形成し、さらにそれが炭化されることで酸素を遮断する効果が高くなり、非溶融繊維Ａの酸化劣化を抑制でき、また、その炭化膜が優れた難燃性を有する。炭化型熱可塑性繊維Ｂの融点は、非溶融繊維Ａの発火温度よりも２００℃以上低いことが好ましく、３００℃以上低いことがさらに好ましい。具体的には融点は３００℃以下であることが好ましい。これらの中で、ＬＯＩ値の高さおよび融点の範囲および入手の容易さの点から、最も好ましいのはポリフェニレンスルフィド繊維（以下、ＰＰＳ繊維ともいう）である。ＰＰＳ繊維は加熱されて溶融する際、架橋物を形成し、炭化しやすい。よって、カーペットが加熱されたときに、パイル層が熱可塑性繊維の場合には、溶融したＰＰＳ繊維と混溶して架橋を形成するためドリップ抑制効果を発揮する。一方、パイル層が非溶融性のセルロース系繊維であっても、ＰＰＳ繊維が熱分解する際に発生する硫酸でセルロース系繊維の炭化を促進するため、パイル層で炭化膜を形成し、カーペットとしての難燃性が向上する。また、ＬＯＩ値が本発明で規定する範囲にないポリマーであっても、難燃剤で処理することによって、処理後のＬＯＩ値が本発明で規定する範囲内であれば好ましく用いることができる。ポリマー構造中あるいは、難燃剤中に硫黄原子を含むことにより、ポリマーあるいは難燃の熱分解時にリン酸あるいは硫酸を生成し、ポリマー基材を脱水炭化させる機構を発現するため、加熱されたときにパイル層を炭化し、カーペットとしての難燃性が向上する。難燃剤を用いる場合には、リン系や硫黄系の難燃剤が好ましい。
　また本発明で用いられる炭化型熱可塑性繊維Ｂは、上記熱可塑性樹脂単独あるいは異素材と複合する方法で用いられ、繊維長は３０～１２０ｍｍの範囲内にあることが好ましく、３８～７０ｍｍの範囲内にあることがより好ましい。繊維長が３８～７０ｍｍの範囲内であれば、一般的なニードルパンチ法や水流交絡法で不織布とすることが可能であり、異素材と複合することが容易である。また、紡績糸とする場合には、一般的な紡績工程で紡績糸とするために、繊維長が３８～５１ｍｍの範囲であることが好ましい。炭化型熱可塑性繊維Ｂの単繊維の太さについても、特に限定されるものではないが、カード工程の通過性の点から、単繊維繊度は０．１～１０ｄｔｅｘの範囲内にあるものが好ましい。
　本発明で好ましく用いられるＰＰＳ繊維は、ポリマー構成単位が－（Ｃ６Ｈ４－Ｓ）－を主な構造単位とする重合体からなる合成繊維である。これらＰＰＳ重合体の代表例としては、ポリフェニレンスルフィド、ポリフェニレンスルフィドスルホン、ポリフェニレンスルフィドケトン、これらのランダム共重合体、ブロック共重合体およびそれらの混合物などが挙げられる。特に好ましいＰＰＳ重合体としては、ポリマーの主要構造単位として、－（Ｃ６Ｈ４－Ｓ）－で表されるｐ－フェニレンスルフィド単位を、好ましくは９０モル％以上含有するポリフェニレンスルフィドが望ましい。質量の観点からは、ｐ－フェニレンスルフィド単位を８０重量％、さらには９０重量％以上含有するポリフェニレンスルフィドが望ましい。
　また本発明で好ましく用いられるＰＰＳ繊維は、ＰＰＳ繊維単独あるいは異素材と複合する方法で用いられ、フィラメント、ステープルのいずれの形態であってもよい。ステープルを紡績して用いる場合には、繊維長は３０～１２０ｍｍの範囲内にあることが好ましく、３８～７０ｍｍの範囲内にあることがより好ましい。繊維長が３８～７０ｍｍの範囲内であれば、一般的なニードルパンチ法や水流交絡法で不織布とすることが可能であり、異素材と複合することが容易である。また、また、紡績糸とする場合には、一般的な紡績工程で紡績糸とするために、繊維長が３８～５１ｍｍの範囲であることが好ましい。ＰＰＳの単繊維の太さについても、特に限定されるものではないが、カード工程の通過性の点から、単繊維繊度は０．１～１０ｄｔｅｘの範囲内にあるものが好ましい。
　本発明で用いられるＰＰＳ繊維の製造方法は、上述のフェニレンスルフィド構造単位を有するポリマーをその融点以上で溶融し、紡糸口金から紡出することにより繊維状にする方法が好ましい。紡出された繊維は、そのままでは未延伸のＰＰＳ繊維である。未延伸のＰＰＳ繊維は、その大部分が非晶構造であり、破断伸度は高い。一方、このような繊維は熱による寸法安定性が乏しいので、紡出に続いて熱延伸して配向させ、繊維の強力と熱寸法安定性を向上させた延伸糸が市販されている。ＰＰＳ繊維としては、“トルコン”（登録商標）（東レ製）、“プロコン”（登録商標）（東洋紡績製）など、複数のものが流通している。
　本発明においては、本発明の範囲を満たす範囲で上記未延伸のＰＰＳ繊維と延伸糸を併用することができる。なお、ＰＰＳ繊維の代わりに本発明の範囲を満たす繊維の延伸糸と未延伸糸を併用することでももちろん構わない。
　基布における炭化型熱可塑性繊維Ｂの混率が低すぎると、骨材の非溶融繊維の間に熱可塑性繊維が十分膜状に広がりにくくなる傾向にあるため、カーペットとしたときに難燃性が低下する。一方、炭化型熱可塑性繊維Ｂの混率が高すぎると、接炎部分の基布が脆くなり、脆化した部分から割れが発生しやすくなり、難燃性が低下する傾向にある。基布層における炭化型熱可塑性繊維Ｂの混率は、２０～８０重量％であるのが好ましく、３０～７０重量％であるのがより好ましい。
　本発明において、基布に用いる繊維の形態として、繊維同士の絡合性を十分得るために、繊維のけん縮数は７個／２．５４ｃｍ以上であることが好ましく、さらには１２個／２．５４ｃｍ以上であることが好ましい。非溶融繊維Ａおよび炭化型熱可塑性繊維Ｂの短繊維の長さは、より均一な不織布を得るため、あるいは、安定して紡績糸とするために同じ長さとすることが好ましい。なお同じ長さは厳密に同じでなくてもよく、非溶融繊維Ａの長さに対し±５％程度の差異があってもよい。かかる観点から、非溶融繊維の繊維長も、溶融繊維の繊維長も繊維長は３０～１２０ｍｍの範囲内にあることが好ましく、不織布の場合には、３８～７０ｍｍ、紡績糸の場合には３８～５１ｍｍの範囲内にあることがより好ましい。
　本発明で用いる基布は、パイルの把持力があれば、組織は限定されるものではない。上記短繊維を用いて、不織布とする場合には、ニードルパンチ法や水流交絡法などで製造される。不織布の場合、タフティング機のニードルの貫通の際に抵抗が少なく、クッション性のあるものが好適である。一方、織物や編物の形態とする場合には、一般的な製造方法で紡績糸とした後、紡績糸を用いて織物や編物とする。織物の場合は、特に織物組織に限定はない。また、編物についても編組織は限定されるものではなく、横編み、丸編み、経編のいずれであってもよいが、カーペットを製造する工程での加工張力による基布の伸びを抑制する点で経編が好ましい。
　基布は、不織布あるいは織編物とした後、テンターを用いて熱セットしてもよいし、カレンダー加工をおこなってもよい。当然、生機のまま使用してもよい。セット温度は高温収縮率を抑制する効果が得られる温度がよく、好ましくは１６０～２４０℃、より好ましくは１９０～２３０℃である。カレンダー加工は、基布の厚さや密度を調整するものであり、カーペットのパイルを打ち込む際の加工性に影響のない範囲で実施されるものであるので、カレンダーの速度、圧力、温度は制限されるものではない。基布の目付としては５０～４００ｇ／ｍ２の範囲が好ましい。目付が軽すぎるとタフト性を確保できず、逆に目付が重すぎると、タフトを打ち込めなかったり、カーペット全体が重くなりすぎる。
　このようにして得られる基布層は、ハロゲン系難燃剤やリン系難燃剤等の有機難燃剤、金属水酸化物やアンチモン系難燃剤等の無機難燃剤等いわゆる難燃剤を含まなくとも優れた難燃性を有する。ここでいう「難燃剤を含まなくとも」における難燃剤は、基布層を構成する前記炭化型熱可塑性繊維Ｂにおいて、ＬＯＩ値を調整するために含まれる難燃剤ではなく、基布層中、非溶融繊維Ａと炭化型熱可塑性繊維Ｂとを含む以外に別途難燃剤を含まなくてもよいという意味である。　本発明におけるパイルはタフティング機により基布に植設される。パイル層の形態としては、カットパイル、ループパイル、カットアンドループ等どの様な形態でも用いることができる。
　パイルを構成するパイル素材としては、一般的にカーペット素材として使用しているものを用いればよく、ウール、麻、コットン等の天然繊維やポリアミド系繊維、ポリエステル系繊維、ポリアクリル系繊維、ポリプロピレン系繊維等の合成樹脂繊維等が挙げられる。なかでもパイル層にはポリエステル系繊維、ポリアミド系繊維、アクリル系繊維、セルロース系繊維、天然繊維およびこれらの混合物を用いることが好ましい。
　パイルの繊度は８００～４０００ｄｔｅｘのパイル糸を用いることが好ましい。上記範囲のパイルを用いれば、良好な見栄えとなり、踏み心地の良好なカーペットとなる。８００ｄｔｅｘを下回れば、透けが発生し見苦しい表情のカーペットとなり、４０００ｄｔｅｘを上回れば経済的にも不利となり、重量が嵩み運搬、収納等に問題が生じる。
　本発明においては、基布層の炭化作用によって、パイル層側から接炎させたときのパイル層の難燃化および裏打ち層への延焼防止を達成するが、パイル層の基布層に対する重量比は５以下であることが好ましい。パイル層の重量比が大きくなりすぎると、パイル層による空気遮断効果で難燃性が向上する場合もある。特にパイル素材が熱可塑性繊維の場合には、燃焼中にドリップを生じ、ドリップ物に引火して難燃性が悪化する場合があるうえ、重量が嵩み運搬、収納等に問題が生じる。
　タフト表面で延焼が生じてしまう場合には、ハロゲン系難燃剤やリン系難燃剤等の有機難燃剤、または金属水酸化物やアンチモン系難燃剤等の無機難燃剤等を、スプレー加工などの方法を用いてパイル層に付与してもよい。
　上記有機難燃剤としては、ハロゲン化ジフェニルスルフィド類などのハロゲン系難燃剤、ポリリン酸アンモニウム、トリフェニルホスフェート等のリン系難燃剤、テトラブロモビスフェノールＡおよびその誘導体、ヘキサブロモベンゼン、デカブロモジフェニルエーテル、テトラブロモエタン、テトラブロモブタン、ヘキサブロモシクロデカン等の臭素系難燃剤、塩素化パラフィン、塩化ジフェニル、パークロロペンタシクロデカン、塩素化ナフタレン等の塩素系難燃剤等が主に挙げられる。上記無機難燃剤としては、水酸化アルミニウム、水酸化マグネシウム、水酸化ジルコニウム、塩基性炭酸マグネシウム、ドロマイト、ハイドロタルサイト、水酸化カルシウム、水酸化バリウム、酸化スズの水和物、ホウ砂等の無機金属化合物の水和物、五酸化アンチモン等のアンチモン系難燃剤が挙げられる。難燃剤の付与量は、風合いやブリードアウト等の品質面で問題のない範囲とすればよい。
　裏打ち層は、タフテッドカーペットの用途によって異なるが、形態として、ペーストによるコーティング、シートラミネート等が使用できる。使用する樹脂として、例えば樹脂としてはアクリル系、ウレタン系、ポリ塩化ビニル、ポリエチレン、ポリプロピレン、エチレン－酢酸ビニル共重合体（ＥＶＡ）等の樹脂が挙げられる。あるいは、ゴムラテックスとして、ゴム成分はＳＢＲ（スチレン－ブタジエンゴム）、ＮＢＲ（アクリロニトリル－ブタジエンゴム）、ＭＢＲ（メチルメタクリレート－ブタジエンゴム）あるいは天然ゴム等が挙げられる。
　本発明におけるカーペットは、基布にタフティング機で、パイル糸を植え込んで表面パイル層を形成して表皮層と成し、該表皮層の裏面に裏打ち層を積層一体化することで得られる。
　本発明のカーペットの目付は、難燃性と、収納性や持ち運び性の両立の点から３００～２５００ｇ／ｍ２の範囲であることが好ましく、３５０～２３００ｇ／ｍ２であることがより好ましい。
　かくして得られる本発明の難燃カーペットは難燃性に優れ、自動車、鉄道、航空機などの高い難燃性が求められる用途に好適である。
　次に、実施例に基づき本発明を具体的に説明する。ただし、本発明はこれらの実施例のみに限定されるものではない。本発明の技術的範囲を逸脱しない範囲において、様々な変形や修正が可能である。なお、本実施例で用いる各種特性の測定方法は、以下のとおりである。
　［目付］
　３０ｃｍ角のサンプルの重量を測定し、１ｍ２当たりの重量(ｇ／ｍ２)で表した。
　 [難燃性評価]
　（１）車輌材料試験
　鉄道車輌用非金属材料の燃焼試験方法として規定されている、国土交通省令第８３条　アルコールランプ燃焼試験を実施し、「難燃性」以上、すなわち、「難燃性」、「極難燃性」、「不燃性」のいずれかの基準を満たすものを合格とし、合格をＡ、不合格をＦとした。
　（２）消防法４５度ミクロバーナー試験
　日本国の消防法の４５度ミクロバーナー試験方法に準拠し、炭化面積３０ｃｍ２以下、残炎時間３秒以下、残じん時間５秒以下を合格とし、合格をＢ、炭化面積２０ｃｍ２ 以下、残炎時間３秒以下でとくに良好な難燃性であるものをＡ、規格を不合格であったものをＦとした。
　（３）自動車内装材燃焼試験
　ＪＩＳ　Ｄ　１２０１（１９９８年）に規定される、自動車内装材用の水平燃焼試験ＦＭＶＳＳＮｏ．３０２に準拠し、燃焼速度４インチ（１０２ｍｍ）／分以下を合格とし、４インチ（１０２ｍｍ）／分以下をＢ、３インチ（７６ｍｍ）／分以下をＡ、不合格をＦとした。
　次に、以下の実施例および比較例における用語について説明する。
　《ＰＰＳ繊維の延伸糸》
　延伸されたＰＰＳ繊維として、単繊維繊度２．２ｄｔｅｘ（直径１４μｍ）、カット長５１ｍｍの東レ製“トルコン”（登録商標）、品番Ｓ３７１を用いた。このＰＰＳ繊維のＬＯＩ値は３４、融点は２８４℃である。
　《耐炎化繊維》
　１．７ｄｔｅｘのＺｏｌｔｅｋ社製耐炎化繊維ＰＹＲＯＮを５１ｍｍにカットしたものを用いた。ＰＹＲＯＮの高温収縮率は１．６％であった。ＪＩＳ　Ｋ７１９３（２０１０年）に準拠した方法で加熱したところ、８００℃でも発火は認められず、発火温度は８００℃以上である。また、熱伝導率は、０．０４２Ｗ／ｍ・Ｋであった。
　《ポリエチレンテレフタレート（ＰＥＴ）繊維》
　延伸されたＰＥＴ繊維として、単繊維繊度２．２ｄｔｅｘ（直径１４μｍ）、カット長５１ｍｍの東レ製“テトロン”（登録商標）を用いた。このＰＥＴ繊維のＬＯＩ値は２２、融点は２６７℃である。
　《炭素繊維》
　直径３０ミクロンの東レ製“トレカ”（登録商標）を５１ｍｍにカットしたものを用いた。熱伝導率は、８．４Ｗ／ｍ・Ｋであった。
　《ポリエステル繊維の延伸糸》
　延伸されたポリエステル繊維として、単繊維繊度２．２ｄｔｅｘ（直径１４μｍ）のポリエチレンテレフタレート繊維である東レ製“テトロン”（登録商標）、品番Ｔ９６１５を５１ｍｍにカットして用いた。このポリエステル繊維のＬＯＩ値は２２、融点は２５６℃である。
　［実施例１］
　（基布作製）
　ＰＰＳ繊維の延伸糸および耐炎化繊維を開繊機によって混合し、次いで混打綿機によって更に混合し、次いで梳綿機に通じてスライバーとした。得られたスライバーの重量は、３１０ゲレン／ ６ ヤード（ １ ゲレン＝ １ ／ ７ ０ ０ ０ ポンド）（２０．０９ｇ／５．４８６ｍ） であった。次いで練条機でトータルドラフトを８ 倍に設定して延伸し、２９０ ゲレン／ ６ ヤード（１８．７９ｇ／５．４８６ｍ）のスライバーとした。次いで粗紡機で０ ． ５５Ｔ ／ ２ ． ５ ４ ｃ ｍ に加撚して７.４ 倍に延伸し、２ ５ ０ ゲレン／ ６ ヤード（１６．２０ｇ／５．４８６ｍ）の粗糸を得た。次いで精紡機で１６．４Ｔ ／ ２ ． ５ ４ ｃ ｍ に加撚してトータルドラフト３０倍に延伸して加撚し、綿番手で３０番の紡績糸を得た。得られた紡績糸をダブルツイスターで６４．７Ｔ／２．５４ｃｍで上撚をかけ、３０番双糸とした。紡績糸のＰＰＳ繊維の延伸糸と耐炎化繊維の重量混率は、６０対４０であった。
　得られた紡績糸を、レピア織機で経５０本／インチ（２．５４ｃｍ）、緯５０本／インチ（２．５４ｃｍ）の平織りで製織した。
　次いで、界面活性剤を含む８０℃の温水中で、２０分間精練をおこなったのち、１３０℃のテンターで乾燥させ、さらに２３０℃のテンターで熱セットをおこなうことで、経５４本／インチ（２．５４ｃｍ）、緯５３本／インチ（２．５４ｃｍ）、目付１８７ｇ／ｍ２の基布を得た。
　（カーペット作製）
　得られた基布にタフティングカットパイル機を用いて、単繊維繊度４０ｄｔｅｘのトータル繊度２４００ｄｔｅｘのナイロン（ナイロン６６）フィラメントを、ヨコ密度：３５本／１０ｃｍ、タテ密度：３０本／１０ｃｍ、パイル長８ｍｍでタフティングをおこない、パイル重量５５７ｇ／ｍ２のカットパイルから成るパイル層を形成した。次いで、コーティング加工機で、カーペット原反の裏面にスチレンブタジエンラテックスを７６３ｇ／ｍ２塗布し、カーペットとした。
　（難燃性評価）
　得られたカーペットの難燃性は良好で、車輌材料試験、消防法４５度ミクロバーナー試験、自動車内装材燃焼試験ともに合格であった。
　［実施例２］
　（基布作製）
　ＰＰＳ繊維の延伸糸および耐炎化繊維を開繊機によって混合し、次いで混打綿機によって更に混合し、次いでカード機に通じてウェブを作成した。得られたウェブをクロスラップ機にて積層したのち、ニードルパンチマシンで不織布化し、ＰＰＳ繊維の延伸糸および耐炎化繊維からなる不織布を得た。不織布のＰＰＳ繊維の延伸糸と耐炎化繊維の重量混率は、６０対４０、目付は１７３ｇ／ｍ２であった。
　（カーペット作製）
　実施例１と同様の方法でタフティングをおこない、パイル重量５５３ｇ／ｍ２のカットパイルから成るパイル層を形成した。次いで、実施例１と同様の方法でカーペット原反の裏面にスチレンブタジエンラテックスを７４１ｇ／ｍ２塗布し、カーペットとした。
　（難燃性評価）
　得られたカーペットの難燃性は良好で、車輌材料試験、消防法４５度ミクロバーナー試験、自動車内装材燃焼試験ともに合格であった。
　［実施例３］
　実施例１で、パイル密度をヨコ密度：５０本／１０ｃｍ、タテ密度：４５本／１０ｃｍに変更し、パイル重量１１８７ｇ／ｍ２とした。次いで、コーティング加工機で、カーペット原反の裏面にスチレンブタジエンラテックスを８２５ｇ／ｍ２塗布し、カーペットとした。さらに、得られたカーペットのパイル側に、リン系難燃剤をスプレーした。
　（難燃性評価）
　得られたカーペットの難燃性は良好で、車輌材料試験、消防法４５度ミクロバーナー試験、自動車内装材燃焼試験ともに合格であった。
　［比較例１］
　実施例１で、基布を構成する紡績糸を耐炎化繊維の紡績糸に変更して、目付１８０ｇ／ｍ２の基布とした。得られた基布を用いて実施例１と同様の方法でカーペットを作製した。パイル重量５５０ｇ／ｍ２、裏打ち層のスチレンブタジエンラテックス塗布量は７５８ｇ／ｍ２であった。
　得られたカーペットは、すべての試験で不合格であった。
　［比較例２］
　実施例１で、基布を構成する紡績糸をＰＰＳ繊維の延伸糸を用いた紡績糸に変更して、目付１７７ｇ／ｍ２の基布とした。得られた基布を用いて実施例１と同様の方法でカーペットを作製した。パイル重量５５０ｇ／ｍ２、裏打ち層のスチレンブタジエンラテックス塗布量は７８７ｇ／ｍ２であった。
　得られたカーペットは、自動車内装材燃焼試験は合格であったものの、車輌材料試験、消防法４５度ミクロバーナー試験は不合格であった。
　［比較例３］
　実施例１で、基布を構成する紡績糸を炭素繊維を用いた紡績糸に変更して、目付１６３ｇ／ｍ２の基布とした。得られた基布を用いて実施例１と同様の方法でカーペットを作製した。パイル重量５８９ｇ／ｍ２、裏打ち層のスチレンブタジエンラテックス塗布量は７６０ｇ／ｍ２であった。
　得られたカーペットは、自動車内装材燃焼試験は合格であったものの、車輌材料試験、消防法４５度ミクロバーナー試験は不合格であった。
　［比較例４］
　実施例１で、基布を構成する紡績糸をポリエステル繊維の延伸糸を用いた紡績糸に変更して、目付１７９ｇ／ｍ２の基布とした。得られた基布を用いて実施例１と同様の方法でカーペットを作製した。パイル重量５８０ｇ／ｍ２、裏打ち層のスチレンブタジエンラテックス塗布量は７５５ｇ／ｍ２であった。
　得られたカーペットは、すべての試験で不合格であった。
Figure JPOXMLDOC01-appb-T000001
　本発明は、優れた難燃性を有しており、鉄道車輌、自動車、船舶等の乗物用座席や、家庭、オフィス等のフロアなどのカーペットとして使用するのに好適である。
　１　パイル層
　２　基布層
　３　表皮層
　４　裏打ち層
 
 

Claims (9)

  1. ｉ）パイル層と、
    ｉｉ）高温収縮率が３％以下で、且つＩＳＯ２２００７－３（２００８年）に準拠する熱伝導率が０．０６０Ｗ／ｍ・Ｋ以下である非溶融繊維Ａと、ＪＩＳ　Ｋ７２０１－２（２００７年）に準拠するＬＯＩ値が２５以上である炭化型熱可塑性繊維Ｂとを含む基布層
    から成る表皮層と、
    ｉｉｉ）裏打ち層を備えたカーペット。
  2. 前記基布層の非溶融繊維Ａの含有率が２０～８０重量％である請求項１に記載のカーペット。
  3. 前記基布層の炭化型熱可塑性繊維Ｂの含有率が２０～８０重量％である請求項１または２に記載のカーペット。
  4. 前記基布層の非溶融繊維Ａが、耐炎化繊維またはメタアラミド系繊維である請求項１～３の何れかに記載のカーペット。
  5. 前記基布層の炭化型熱可塑性繊維Ｂが、異方性溶融ポリエステル、難燃性ポリ（アルキレンテレフタレート）、難燃性ポリ（アクリロニトリルブタジエンスチレン）、難燃性ポリスルホン、ポリ（エーテル－エーテル－ケトン）、ポリ（エーテル－ケトン－ケトン）、ポリエーテルスルホン、ポリアリレート、ポリアリーレンスルフィド、ポリフェニルスルホン、ポリエーテルイミド、ポリアミドイミドおよびこれらの混合物の群から選択される樹脂からなる繊維である請求項１～４の何れかに記載のカーペット。
  6. 前記基布層の炭化型熱可塑性繊維Ｂの融点が３００℃以下である請求項１～５の何れかに記載のカーペット。
  7. 前記パイル層はポリエステル系繊維、ポリアミド系繊維、アクリル系繊維、セルロース系繊維、天然繊維およびこれらの混合物の群から選択される繊維を含む請求項１～６の何れかに記載のカーペット。
  8. 前記パイル層の基布層に対する重量比が５以下である請求項１～７の何れかに記載の難燃カーペット。
  9. 目付が３００～２５００ｇ／ｍ２の範囲である請求項１～８の何れかに記載の難燃カーペット。
PCT/JP2019/010194 2018-03-30 2019-03-13 カーペット WO2019188277A1 (ja)