WO2019130567A1 - Procédé de fabrication de plaque de guidage de lumière - Google Patents

Procédé de fabrication de plaque de guidage de lumière Download PDF

Info

Publication number
WO2019130567A1
WO2019130567A1 PCT/JP2017/047325 JP2017047325W WO2019130567A1 WO 2019130567 A1 WO2019130567 A1 WO 2019130567A1 JP 2017047325 W JP2017047325 W JP 2017047325W WO 2019130567 A1 WO2019130567 A1 WO 2019130567A1
Authority
WO
WIPO (PCT)
Prior art keywords
transfer
stampers
transferred object
light guide
temperature
Prior art date
Application number
PCT/JP2017/047325
Other languages
English (en)
Japanese (ja)
Inventor
博司 岡田
耕治 岡田
厚史 長尾
Original Assignee
日東樹脂工業株式会社
住化ポリカーボネート株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 日東樹脂工業株式会社, 住化ポリカーボネート株式会社 filed Critical 日東樹脂工業株式会社
Priority to PCT/JP2017/047325 priority Critical patent/WO2019130567A1/fr
Priority to JP2018521133A priority patent/JP6356375B1/ja
Priority to TW107147393A priority patent/TWI777012B/zh
Publication of WO2019130567A1 publication Critical patent/WO2019130567A1/fr

Abstract

La présente invention concerne un procédé de fabrication d'une plaque de guidage de lumière, qui permet une production à faible volume de mélange élevé des plaques de guidage de lumière faciles à manipuler destinée à des applications réelles sur lesquelles des formes telles qu'un motif de points ont été appliquées à une précision élevée. Le procédé de fabrication d'une plaque de guidage de lumière comprend : une première étape de transfert consistant à chauffer un objet de réception de transfert entre deux matrices de pressage à partir de l'extérieur de deux supports, à appliquer une pression à l'objet à l'aide d'une presse à membrane, et ainsi à transférer la forme de surface des matrices de pressage à la surface de l'objet ; une seconde étape de transfert consistant à continuer à transférer la forme de surface des matrices de pressage à la surface de l'objet de réception de transfert en maintenant la température de l'objet entre les deux matrices de pressage à partir de l'extérieur des deux supports et à maintenir la pression appliquée sur l'objet ; et une étape consistant à transporter l'objet de réception de transfert entre les deux matrices de pressage de la première étape de transfert à la seconde étape de transfert pendant que l'objet est maintenu par les deux supports dans une condition sensiblement étanche.
PCT/JP2017/047325 2017-12-28 2017-12-28 Procédé de fabrication de plaque de guidage de lumière WO2019130567A1 (fr)

Priority Applications (3)

Application Number Priority Date Filing Date Title
PCT/JP2017/047325 WO2019130567A1 (fr) 2017-12-28 2017-12-28 Procédé de fabrication de plaque de guidage de lumière
JP2018521133A JP6356375B1 (ja) 2017-12-28 2017-12-28 導光板の製造方法
TW107147393A TWI777012B (zh) 2017-12-28 2018-12-27 導光板之製造方法及製造裝置

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
PCT/JP2017/047325 WO2019130567A1 (fr) 2017-12-28 2017-12-28 Procédé de fabrication de plaque de guidage de lumière

Publications (1)

Publication Number Publication Date
WO2019130567A1 true WO2019130567A1 (fr) 2019-07-04

Family

ID=62843728

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2017/047325 WO2019130567A1 (fr) 2017-12-28 2017-12-28 Procédé de fabrication de plaque de guidage de lumière

Country Status (3)

Country Link
JP (1) JP6356375B1 (fr)
TW (1) TWI777012B (fr)
WO (1) WO2019130567A1 (fr)

Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH07287864A (ja) * 1994-04-14 1995-10-31 Pioneer Electron Corp 光ディスクの製造方法
JP2003109254A (ja) * 2001-09-27 2003-04-11 Nissei Plastics Ind Co 光記録基板および光記録媒体並びにその製造法
JP2013082085A (ja) * 2011-10-06 2013-05-09 Yasuda Koki Kk 熱転写成形装置
WO2014054242A1 (fr) * 2012-10-01 2014-04-10 出光ユニテック株式会社 Dispositif de moulage par transfert et procédé de moulage par transfert
US9770875B2 (en) * 2013-08-16 2017-09-26 New Optics, Ltd. Apparatus and method for forming serration pattern

Family Cites Families (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20080070998A1 (en) * 2004-09-30 2008-03-20 Oji Paper Co., Ltd. Foam Production Method
CN103802307B (zh) * 2012-11-05 2016-12-28 欧姆龙株式会社 导光板及其制造方法、模型构造、转印成形装置、面光源装置、液晶显示装置及移动设备
WO2017033290A1 (fr) * 2015-08-25 2017-03-02 日東樹脂工業株式会社 Procédé de production pour plaque de guidage de lumière

Patent Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH07287864A (ja) * 1994-04-14 1995-10-31 Pioneer Electron Corp 光ディスクの製造方法
JP2003109254A (ja) * 2001-09-27 2003-04-11 Nissei Plastics Ind Co 光記録基板および光記録媒体並びにその製造法
JP2013082085A (ja) * 2011-10-06 2013-05-09 Yasuda Koki Kk 熱転写成形装置
WO2014054242A1 (fr) * 2012-10-01 2014-04-10 出光ユニテック株式会社 Dispositif de moulage par transfert et procédé de moulage par transfert
US9770875B2 (en) * 2013-08-16 2017-09-26 New Optics, Ltd. Apparatus and method for forming serration pattern

Also Published As

Publication number Publication date
TW201930780A (zh) 2019-08-01
TWI777012B (zh) 2022-09-11
JPWO2019130567A1 (ja) 2019-12-26
JP6356375B1 (ja) 2018-07-11

Similar Documents

Publication Publication Date Title
US7670131B2 (en) Imprinting jig and imprinting apparatus
US8485811B2 (en) Fine structure formation apparatus
US10421218B2 (en) Roller-type depressing device, imprinting device, and roller-type depressing method
TWI707770B (zh) 導光板之製造方法
WO2019130567A1 (fr) Procédé de fabrication de plaque de guidage de lumière
EP2783833B1 (fr) Dispositif d'impression et procédé d'impression
JP4893240B2 (ja) 耐熱離型シート
EP2889895A1 (fr) Dispositif d'empreinte et procédé d'empreinte
JP2012031016A (ja) 光学素子の製造方法、及び、光学素子の製造装置
WO2007029715A1 (fr) Dispositif de moulage d’elements optiques
JPWO2010095402A1 (ja) 表面形状付き光学部材の製造方法及びその製造装置
KR20220100583A (ko) 보상 재료를 가지는 플레이트 캐리어를 포함하는 롤-투-플레이트 임프린팅 공정을 위한 장치
JP5479787B2 (ja) 光学素子の製造方法および光学素子の製造装置
JP2014162111A (ja) パターン転写用金型とこれを用いたパターン転写装置
JP2021020332A (ja) 成形体の製造方法
JP5731838B2 (ja) トレイ式基板搬送システム、成膜方法及び電子装置の製造方法
JP2020121333A (ja) 熱プレス装置および成形体の製造方法
JP6374809B2 (ja) 光学素子の製造装置、及び、光学素子の製造方法
JP7379983B2 (ja) 成形体の製造方法
CN109895440B (zh) 气密式连续热压成型装置的加压装置
US20190168467A1 (en) Press forming method and press forming apparatus for continuous fiber composite sheet
JP2004157452A (ja) 電気光学装置及びその製造装置
TW202337669A (zh) 積層裝置及積層方法
KR20120067775A (ko) 도광판 제조장치 및 제조방법
JP2020104348A (ja) フィルム状部材の製造方法

Legal Events

Date Code Title Description
ENP Entry into the national phase

Ref document number: 2018521133

Country of ref document: JP

Kind code of ref document: A

121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 17935891

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 17935891

Country of ref document: EP

Kind code of ref document: A1