WO2019082385A1 - Agent antiadhésif, matériau de moulage et article moulé - Google Patents

Agent antiadhésif, matériau de moulage et article moulé

Info

Publication number
WO2019082385A1
WO2019082385A1 PCT/JP2017/038935 JP2017038935W WO2019082385A1 WO 2019082385 A1 WO2019082385 A1 WO 2019082385A1 JP 2017038935 W JP2017038935 W JP 2017038935W WO 2019082385 A1 WO2019082385 A1 WO 2019082385A1
Authority
WO
WIPO (PCT)
Prior art keywords
polymer
block copolymer
hydride
mass
parts
Prior art date
Application number
PCT/JP2017/038935
Other languages
English (en)
Japanese (ja)
Inventor
竜太 栗原
小原　禎二
Original Assignee
日本ゼオン株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 日本ゼオン株式会社 filed Critical 日本ゼオン株式会社
Priority to PCT/JP2017/038935 priority Critical patent/WO2019082385A1/fr
Priority to JP2019549970A priority patent/JPWO2019082385A1/ja
Publication of WO2019082385A1 publication Critical patent/WO2019082385A1/fr

Abstract

L'invention concerne un agent antiadhésif, caractérisé en ce qu'il comprend une poudre d'un hydrure de (co)polymère obtenue par hydrogénation d'un (co)polymère présentant, en tant que constituant principal, un motif structural dérivé d'un composé aromatique de vinyle, la température de ramollissement de l'hydrure de (co)polymère étant de 120°C ou plus.
PCT/JP2017/038935 2017-10-27 2017-10-27 Agent antiadhésif, matériau de moulage et article moulé WO2019082385A1 (fr)

Priority Applications (2)

Application Number Priority Date Filing Date Title
PCT/JP2017/038935 WO2019082385A1 (fr) 2017-10-27 2017-10-27 Agent antiadhésif, matériau de moulage et article moulé
JP2019549970A JPWO2019082385A1 (ja) 2017-10-27 2017-10-27 ブロッキング防止剤、成形材料、および成形体

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
PCT/JP2017/038935 WO2019082385A1 (fr) 2017-10-27 2017-10-27 Agent antiadhésif, matériau de moulage et article moulé

Publications (1)

Publication Number Publication Date
WO2019082385A1 true WO2019082385A1 (fr) 2019-05-02

Family

ID=66246321

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2017/038935 WO2019082385A1 (fr) 2017-10-27 2017-10-27 Agent antiadhésif, matériau de moulage et article moulé

Country Status (2)

Country Link
JP (1) JPWO2019082385A1 (fr)
WO (1) WO2019082385A1 (fr)

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2020205145A (ja) * 2019-06-14 2020-12-24 パナソニックＩｐマネジメント株式会社 照明装置及び導光部材
JP2021022513A (ja) * 2019-07-29 2021-02-18 パナソニックＩｐマネジメント株式会社 照明装置

Citations (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH10176012A (ja) * 1996-12-17 1998-06-30 Idemitsu Petrochem Co Ltd 耐ブロッキング性共重合体水素添加物
JP2005126546A (ja) * 2003-10-23 2005-05-19 Asahi Kasei Chemicals Corp ブロック共重合体水添物、又はフィルム
JP2006117879A (ja) * 2004-10-25 2006-05-11 Asahi Kasei Chemicals Corp 水添共重合体及びその組成物
WO2006109743A1 (fr) * 2005-04-07 2006-10-19 Asahi Kasei Chemicals Corporation Produit d'hydrogénation d'un copolymère en blocs ou feuille ou film de celui-ci
JP2007126569A (ja) * 2005-11-04 2007-05-24 Sekisui Chem Co Ltd 粘着剤及び表面保護フィルム
JP2009073930A (ja) * 2007-09-20 2009-04-09 Kaneka Corp スチレン系エラストマー樹脂ペレットのブロッキング防止方法
JP2009197049A (ja) * 2008-02-19 2009-09-03 Kaneka Corp スチレン系エラストマー樹脂ペレットのブロッキング防止方法
WO2017155068A1 (fr) * 2016-03-10 2017-09-14 日本ゼオン株式会社 Pastilles comprenant un copolymère en bloc hydrogéné spécifique, procédé permettant d'empêcher que les pastilles ne souffrent d'une adhérence de contact, et procédé de production d'objet moulé

Patent Citations (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH10176012A (ja) * 1996-12-17 1998-06-30 Idemitsu Petrochem Co Ltd 耐ブロッキング性共重合体水素添加物
JP2005126546A (ja) * 2003-10-23 2005-05-19 Asahi Kasei Chemicals Corp ブロック共重合体水添物、又はフィルム
JP2006117879A (ja) * 2004-10-25 2006-05-11 Asahi Kasei Chemicals Corp 水添共重合体及びその組成物
WO2006109743A1 (fr) * 2005-04-07 2006-10-19 Asahi Kasei Chemicals Corporation Produit d'hydrogénation d'un copolymère en blocs ou feuille ou film de celui-ci
JP2007126569A (ja) * 2005-11-04 2007-05-24 Sekisui Chem Co Ltd 粘着剤及び表面保護フィルム
JP2009073930A (ja) * 2007-09-20 2009-04-09 Kaneka Corp スチレン系エラストマー樹脂ペレットのブロッキング防止方法
JP2009197049A (ja) * 2008-02-19 2009-09-03 Kaneka Corp スチレン系エラストマー樹脂ペレットのブロッキング防止方法
WO2017155068A1 (fr) * 2016-03-10 2017-09-14 日本ゼオン株式会社 Pastilles comprenant un copolymère en bloc hydrogéné spécifique, procédé permettant d'empêcher que les pastilles ne souffrent d'une adhérence de contact, et procédé de production d'objet moulé

Cited By (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2020205145A (ja) * 2019-06-14 2020-12-24 パナソニックＩｐマネジメント株式会社 照明装置及び導光部材
JP7236701B2 (ja) 2019-06-14 2023-03-10 パナソニックＩｐマネジメント株式会社 照明装置及び導光部材
JP2021022513A (ja) * 2019-07-29 2021-02-18 パナソニックＩｐマネジメント株式会社 照明装置
JP7382593B2 (ja) 2019-07-29 2023-11-17 パナソニックＩｐマネジメント株式会社 照明装置

Also Published As

Publication number Publication date
JPWO2019082385A1 (ja) 2020-11-05

Similar Documents

Publication Publication Date Title
JP6423276B2 (ja) 熱可塑性重合体組成物、シューズおよびアウターソール
US20180171057A1 (en) Hydrogenated block copolymer and laminated glass
EP3112431B1 (fr) Feuille adhésive transparente
TWI711658B (zh) 特定的嵌段共聚物氫化物構成的粒料、粒料的成塊防止方法及成形體的製造方法
WO2001048079A1 (fr) Compositions thermoplastiques de caoutchouc reticule
JP2018048236A (ja) ブロッキング防止剤、成形材料、および成形体
WO2019082385A1 (fr) Agent antiadhésif, matériau de moulage et article moulé
TW201837112A (zh) 樹脂組成物及成形體以及其成形方法
JP7420070B2 (ja) 接着性樹脂の製造方法
JP6435733B2 (ja) 変性ブロック共重合体水素化物の製造方法
JPWO2019159672A1 (ja) 酸無水物基含有ブロック共重合体、樹脂組成物、樹脂シート、および合わせガラス
TWI733830B (zh) 熱塑性樹脂摻合組成物、母料及雙軸延伸聚烯烴類膜成形用組成物
TW201917192A (zh) 抗沾黏劑、成形材料及成形體
JP7196604B2 (ja) 成形材料
JPWO2020080202A1 (ja) 共重合体水素化物およびその製造方法、共重合体水素化物含有組成物、合わせガラス用中間膜、合わせガラス用中間膜積層体、封止材、光学フィルム、医療用成形体およびその製造方法、接着剤、ならびに、接合体およびその製造方法
JP2019065097A (ja) 熱可塑性樹脂成形体の製造方法
JPWO2019044267A1 (ja) 合わせガラス
JP7207313B2 (ja) 熱可塑性樹脂シートおよび積層体
JP2018002763A (ja) アルコキシシリル基を有する変性ブロック共重合体水素化物及びその利用
JP2022146935A (ja) シラン官能化スチレンブロックコポリマー
JP2020066161A (ja) 接合体の製造方法
TW201420624A (zh) 纖維強化樹脂組合物
TW202344524A (zh) 樹脂組成物及光學薄膜
JP2021037641A (ja) 接合体の製造方法

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 17930081

Country of ref document: EP

Kind code of ref document: A1

ENP Entry into the national phase

Ref document number: 2019549970

Country of ref document: JP

Kind code of ref document: A

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 17930081

Country of ref document: EP

Kind code of ref document: A1