WO2019010662A1 - Manufacturing method for blended woven fabric - Google Patents

Manufacturing method for blended woven fabric Download PDF

Info

Publication number
WO2019010662A1
WO2019010662A1 PCT/CN2017/092735 CN2017092735W WO2019010662A1 WO 2019010662 A1 WO2019010662 A1 WO 2019010662A1 CN 2017092735 W CN2017092735 W CN 2017092735W WO 2019010662 A1 WO2019010662 A1 WO 2019010662A1
Authority
WO
WIPO (PCT)
Prior art keywords
woven fabric
weaving
yarn
blended
finishing
Prior art date
Application number
PCT/CN2017/092735
Other languages
French (fr)
Chinese (zh)
Inventor
阚军
Original Assignee
阚军
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 阚军 filed Critical 阚军
Priority to PCT/CN2017/092735 priority Critical patent/WO2019010662A1/en
Publication of WO2019010662A1 publication Critical patent/WO2019010662A1/en

Abstract

A manufacturing method for a blended woven fabric, comprising the steps of material selection, weaving, dyeing, and finishing, the raw material selected being a yarn of 90 Nm in which silk and nylon are blended; when weaving, a warp knitting machine being employed for weaving; and, the setting temperature when finishing being 150°C. A product manufactured per the present invention provides strong wool imitating effects, a rich texture, soft touch, strong draping performance and free from laddering, and easiness to cut. A product wetting apparatus for feather-smoothing processing of the raw material and increasing the strength of the yarn, thus mitigating the problem of skipped stitches, broken needles, and patterned stitches caused by the yarn being wrapped by feathers, and increasing product quality and productivity.

Description

混纺编织物的制造方法  Method for producing blended woven fabric
技术领域  Technical field
[0001] 本发明涉及一种混纺编织物的制造方法。  [0001] The present invention relates to a method of making a blended woven fabric.
背景技术  Background technique
[0002] 经编产品基本上以化学长丝原料为主， 产品主要用于产业、 装饰、 家纺、 运动 服装为主， 贴身保暖内衣面料应用很少， 主要由于化学长丝穿着舒适性不能完 全适应人们的不同需求。  [0002] Warp knitting products are mainly made of chemical filament raw materials. The products are mainly used in industry, decoration, home textiles and sportswear. The application of close-fitting thermal underwear fabrics is rare, mainly due to the wearing comfort of chemical filaments. Different needs of people.
技术问题  technical problem
[0003] 本发明的目的在于提供一种仿毛效果好， 质地丰满、 手感柔软的混纺编织物的 制造方法。  [0003] An object of the present invention is to provide a method for producing a blended woven fabric having a good hair-like effect, a rich texture, and a soft hand.
问题的解决方案  Problem solution
技术解决方案  Technical solution
[0004] 一种混纺编织物的制造方法， 包括选料、 织造、 染色、 后整理步骤， 其特征是 ： 选择原料为丝毛锦纶混纺的 90Nm纱； 织造吋， 采用经编机进行织造； 后整理 吋的定型温度为 105°C。  [0004] A method for manufacturing a blended woven fabric, comprising the steps of: selecting, weaving, dyeing, and finishing, wherein: the raw material is a 90Nm yarn blended with silky nylon; the weaving woven fabric is woven by a warp knitting machine; The setting temperature of the finishing crucible was 105 °C.
[0005] 后整理吋， 进行柔软处理， 柔软处理液中柔软剂的重量百分比为 3%。  [0005] After finishing, the softening treatment was carried out, and the weight percentage of the softening agent in the softening treatment liquid was 3%.
[0006] 所述经编机为 KS经编机。  [0006] The warp knitting machine is a KS warp knitting machine.
[0007] 经编机上装给湿装置， 使纱线能沾上给湿装置的润滑液。  [0007] The warp knitting machine is attached to the wet device so that the yarn can be wetted with the lubricating fluid of the wet device.
发明的有益效果  Advantageous effects of the invention
有益效果  Beneficial effect
[0008] 本发明制得的产品仿毛效果强、 质地丰满、 手感柔软、 悬垂性强不脱散、 易裁 剪。 采用给湿装置， 给原料进行顺羽绒处理， 并增加了纱线的强力， 减少了毛 羽缠纱造成的漏针、 断头、 花针等问题， 提高了产品质量和生产效率。  [0008] The product obtained by the invention has strong hair-like effect, full texture, soft handfeel, strong drape and no detachment, and easy cutting. The wetting device is used to process the raw materials, and the strength of the yarn is increased, and the problems such as missing needles, broken ends, and needles caused by the winding of the hairs are reduced, and the product quality and production efficiency are improved.
实施该发明的最佳实施例  BEST MODE FOR CARRYING OUT THE INVENTION
本发明的最佳实施方式 [0009] 一种混纺编织物的制造方法， 包括选料、 织造、 染色、 后整理步骤， 选择原料 为丝毛锦纶混纺的 90Nm纱； 织造吋， 采用经编机进行织造； 后整理吋的定型温 度为 105°C。 BEST MODE FOR CARRYING OUT THE INVENTION [0009] A method for manufacturing a blended woven fabric, comprising the steps of: selecting, weaving, dyeing, and finishing, selecting a 90Nm yarn of a raw material of a silky nylon blend; weaving weaving, weaving with a warp knitting machine; The temperature was 105 °C.
[0010] 后整理吋， 进行柔软处理， 柔软处理液中柔软剂的重量百分比为 3%。  [0010] After finishing, the softening treatment is carried out, and the weight percentage of the softening agent in the softening treatment liquid is 3%.
[0011] 所述经编机为 KS经编机。 [0011] The warp knitting machine is a KS warp knitting machine.
[0012] 经编机上装给湿装置， 使纱线能沾上给湿装置的润滑液。  [0012] The warp knitting machine is attached to the wet device so that the yarn can be wetted with the lubricating fluid of the wet device.

Claims

权利要求书 Claim
[权利要求 1] 一种混纺编织物的制造方法， 包括选料、 织造、 染色、 后整理步骤， 其特征是： 选择原料为丝毛锦纶混纺的 90Nm纱； 织造吋， 采用经编 机进行织造； 后整理吋的定型温度为 105°C。  [Claim 1] A method for producing a blended woven fabric, comprising the steps of: selecting, weaving, dyeing, and finishing, wherein: the raw material is a 90Nm yarn blended with silky nylon; the weaving woven fabric is woven by a warp knitting machine. The finishing temperature of the finishing 为 is 105 °C.
[权利要求 2] 根据权利要求 1所述的混纺编织物的制造方法， 其特征是： 后整理吋[Claim 2] The method for producing a blended woven fabric according to claim 1, wherein:
， 进行柔软处理， 柔软处理液中柔软剂的重量百分比为 3%。 For softening treatment, the softener in the softening treatment solution is 3% by weight.
[权利要求 3] 根据权利要求 1或 2所述的混纺编织物的制造方法， 其特征是： 所述经 编机为 KS经编机。 [Claim 3] The method for producing a blended woven fabric according to claim 1 or 2, wherein the warp knitting machine is a KS warp knitting machine.
[权利要求 4] 根据权利要求 3所述的混纺编织物的制造方法， 其特征是： 经编机上 装给湿装置， 使纱线能沾上给湿装置的润滑液。  [Claim 4] The method for producing a blended woven fabric according to claim 3, wherein the warp knitting machine is attached to the wet device to allow the yarn to be wetted with the lubricating liquid of the wet device.
PCT/CN2017/092735 2017-07-13 2017-07-13 Manufacturing method for blended woven fabric WO2019010662A1 (en)