CN110029434A - A kind of Cashmere knitting fabric and its production technology - Google Patents
A kind of Cashmere knitting fabric and its production technology Download PDFInfo
- Publication number
- CN110029434A CN110029434A CN201910268041.1A CN201910268041A CN110029434A CN 110029434 A CN110029434 A CN 110029434A CN 201910268041 A CN201910268041 A CN 201910268041A CN 110029434 A CN110029434 A CN 110029434A
- Authority
- CN
- China
- Prior art keywords
- cashmere
- fabric
- knitting fabric
- mixed yarn
- carries
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to textile technology fields, more particularly to a kind of Cashmere knitting fabric and its production technology, the Cashmere knitting fabric, it is made of mixed yarn and spandex filament, mixed yarn is formed by Modal fibre and cashmere fiber are blended, since cashmere fiber first carries out blended obtained mixed yarn with Modal fibre, it carries out weaving obtained Cashmere knitting fabric with spandex filament again, pass through Modal fibre, the combination of spandex filament and cashmere fiber, good improvement result is played to cashmere fiber, and then sufficiently overcome in the prior art cashmere fiber fabric it is at high price, washing nursing is troublesome and is easy damaged disadvantage.Therefore, the Cashmere knitting fabric have the advantages that washing nursing is convenient, validity period is long, feel it is fluffy it is soft it is glutinous, warmth retention property is excellent, moisture absorption is ventilative, it is comfortable and easy to wear to paste skin.The production technology of the Cashmere knitting fabric has process simple, and production cost is low, and can be suitble to the characteristics of being mass produced.
Description
Technical field
The present invention relates to textile technology fields, and in particular to a kind of Cashmere knitting fabric and its production technology.
Background technique
Cashmere is to be grown in goat outer skin, covers a thin layer of fine fleece in goat coarse wool root, is entering cold
It is grown when cold, is used for resistance to colds, the beginning of spring turns to fall off after warming up, and with natural adaptation weather, belongs to rare special animal fiber.Sheep
Why very precious suede is, is not only due to yield rareness, it is often more important that its excellent quality and characteristic, feature really seem
The skin of " baby ", soft, fine and smooth, smooth flexible, therefore, cashmere is by it is believed that be " fiber jewel " and " fiber emperor
Afterwards ".
But there is also deficiency, low output and at high price, cashmere fiber knittings especially in the prior art for cashmere fiber
Fabric is there are process complexity, washing nursing also very troublesome defect, due to the delicate easy breakage of cashmere, improper use,
It is easy to shorten validity period.
Summary of the invention
It is an object of the present invention in view of the deficiencies of the prior art, providing a kind of Cashmere knitting fabric, the cashmere needle
Knitted fabric has the advantages that washing nursing is convenient and long-lived, and feel it is fluffy it is soft it is glutinous, warmth retention property is excellent, moisture absorption is ventilative,
Soft skin care, patch skin advantage comfortable and easy to wear, and have effects that skin-protection and health-care.
The second object of the present invention is to provide a kind of production work of Cashmere knitting fabric in view of the deficiencies of the prior art
Skill, the production technology of the Cashmere knitting fabric have the advantages that process is simple.
One of to achieve the goals above, the present invention adopts the following technical scheme:
A kind of Cashmere knitting fabric is provided, is made of the raw material of following weight percent:
Mixed yarn 85%~98%
Spandex filament 2%~15%；
Wherein, the mixed yarn blended is made of the raw material of following weight percent:
Modal fibre 25%~75%
Cashmere fiber 25%~75%.
Preferably, a kind of Cashmere knitting fabric, is made of the raw material of following weight percent:
Mixed yarn 90%~95%
Spandex filament 5%~10%；
Wherein, the mixed yarn blended is made of the raw material of following weight percent:
Modal fibre 35%~65%
Cashmere fiber 35%~65%.
More preferably, a kind of Cashmere knitting fabric, is made of the raw material of following weight percent:
Mixed yarn 92%
Spandex filament 8%；
Wherein, the mixed yarn blended is made of the raw material of following weight percent:
Modal fibre 45%
Cashmere fiber 55%.
The count of yarn of the mixed yarn is 40S~50S.
The fineness of the spandex filament is 10D~30D.
To achieve the goals above two, the present invention adopts the following technical scheme:
A kind of production technology of Cashmere knitting fabric is provided, it the following steps are included:
Spinning: the Modal fibre of formula ratio and cashmere fiber are carried out blended, obtained mixed yarn by step 1；
Weaving: step 2 is weaved mixed yarn made from step 1 and spandex filament using circular knitting machine, obtained
Weave fabric；
The predetermined embryo of open-width: step 3 carries out open-width to the weaving fabric that step 2 obtains, and uses high temperature open width dryer
Carry out predetermined embryo；
Step 4, dyeing: step 3 dyes fabric after completing predetermined embryo, obtains dyed shell fabrics；
Dry cloth: step 5 carries out the dry cloth of tentering using high temperature open width dryer to the dyed shell fabrics that step 4 obtains；
Sanding: step 6 carries out sanding using patch skin face of the diamond dust roller roughing-up machine to the fabric after dry cloth；
Cropping: step 7 carries out cropping processing to the face for completing sanding using rotary knife shearing machine；
Finished product of being formed: step 8 is used high temperature open width dryer to carry out tentering and is made after completing sizing with finished product of being formed
Obtain the Cashmere knitting fabric.
In above-mentioned technical proposal, in the step 1, the blended mode is match network compact spinning.
In above-mentioned technical proposal, in the step 4, the dyeing for reactive dye and acid dyes carries out it is double contaminate or
Person carries out single dye with acid dyes or carries out single dye with reactive dye.
In above-mentioned technical proposal, the process for carrying out double dyes with reactive dye and acid dyes are as follows:
A, single dye Modal fibre is first carried out at 50 DEG C~85 DEG C with reactive dye, then carries out soap washing；
B, carried out at 95 DEG C with acid dyes again it is single contaminate cashmere fiber, then soaped, make soft wash water and go out cylinder；
The process singly contaminated with acid dyes are as follows:
Carried out at 95 DEG C using acid dyes it is single contaminate cashmere fiber, then soaped, make soft wash water and go out cylinder process；
The process singly contaminated with reactive dye are as follows:
Single dye Modal fibre is carried out at 50 DEG C~85 DEG C using reactive dye, it is soft then to carry out soap washing, system
Wash water goes out cylinder process.
In above-mentioned technical proposal, in the step 8, the setting temperature is 150 DEG C~170 DEG C.
Beneficial effects of the present invention:
(1) a kind of Cashmere knitting fabric of the invention, is made of mixed yarn and spandex filament, wherein mixed yarn be by
Modal fibre and cashmere fiber is blended forms, since cashmere fiber first carries out blended obtained mixed yarn with Modal fibre, leads to
The combination for crossing Modal fibre and cashmere fiber is played good improvement result to cashmere fiber, and then is overcome in the prior art
The washing of cashmere fiber fabric nurse troublesome defect, and cashmere fiber fabric can reduce by the combination of Modal fibre
Price, in addition, softness, exquisiteness, smooth characteristic that cashmere fiber itself has, soft well in conjunction with Modal fibre
Property and excellent hygroscopicity, further such that fabric obtained is more soft, comfortable ventilative with moisture absorption.In addition, Modal fibre
With cashmere fiber it is blended at mixed yarn after, then carry out weaving obtained Cashmere knitting fabric with spandex filament, by spandex filament into
One step improve cashmere fiber, and then substantially overcome cashmere fiber fabric in the prior art it is at high price, washing nursing trouble and
The disadvantage of the delicate easy breakage of cashmere.Therefore, through Modal fibre and cashmere fiber it is blended made of mixed yarn, then it is long with spandex
Silk cooperate with Cashmere knitting fabric obtained have washing nursing is convenient, validity period is long, feel it is fluffy it is soft it is glutinous, warmth retention property is excellent, inhales
Advantage penetrable ventilated, patch skin is comfortable and easy to wear.
(2) production technology of a kind of Cashmere knitting fabric provided by the invention has process simple, production cost
It is low, and the characteristics of being mass produced can be suitble to.
Specific embodiment
Below in conjunction with specific embodiment, the present invention is described in detail.
Embodiment 1.
A kind of Cashmere knitting fabric of the present embodiment, is made of the raw material of following weight percent:
Mixed yarn 92%
Spandex filament 8%；
Wherein, the mixed yarn blended is made of the raw material of following weight percent:
Modal fibre 45%
Cashmere fiber 55%.
In the present embodiment, the count of yarn of mixed yarn is 45S.
In the present embodiment, the fineness of spandex filament is 20D.
A kind of production technology of above-mentioned Cashmere knitting fabric, it the following steps are included:
Spinning: the Modal fibre of formula ratio and cashmere fiber are carried out blended, obtained mixed yarn by step 1；Wherein, it mixes
The mode of spinning is match network compact spinning；
Weaving: step 2 is weaved mixed yarn made from step 1 and spandex filament using circular knitting machine, obtained
Weave fabric；
The predetermined embryo of open-width: step 3 carries out open-width to the weaving fabric that step 2 obtains, and uses high temperature open width dryer
Carry out predetermined embryo；
Step 4, dyeing: step 3 dyes fabric after completing predetermined embryo, obtains dyed shell fabrics；
Wherein, it in step 4, dyes to carry out double dyes with reactive dye and acid dyes；
The process for carrying out double dyes with reactive dye and acid dyes are as follows:
A, single dye Modal fibre is first carried out at 70 DEG C with reactive dye, then carries out soap washing；
B, carried out at 95 DEG C with acid dyes again it is single contaminate cashmere fiber, then soaped, make soft wash water and go out cylinder；
Dry cloth: step 5 carries out the dry cloth of tentering using high temperature open width dryer to the dyed shell fabrics that step 4 obtains；
Sanding: step 6 carries out sanding using patch skin face of the diamond dust roller roughing-up machine to the fabric after dry cloth；
Cropping: step 7 carries out cropping processing to the face for completing sanding using rotary knife shearing machine；
Finished product of being formed: step 8 is used high temperature open width dryer to carry out tentering and is made after completing sizing with finished product of being formed
Obtain the Cashmere knitting fabric.In the present embodiment, setting temperature is 160 DEG C.
Embodiment 2.
A kind of Cashmere knitting fabric of the present embodiment, is made of the raw material of following weight percent:
Mixed yarn 85%
Spandex filament 15%；
Wherein, mixed yarn blended is made of the raw material of following weight percent:
Modal fibre 25%
Cashmere fiber 75%.
In the present embodiment, the count of yarn of mixed yarn is 40S.
In the present embodiment, the fineness of spandex filament is 10D.
A kind of production technology of above-mentioned Cashmere knitting fabric, it the following steps are included:
Spinning: the Modal fibre of formula ratio and cashmere fiber are carried out blended, obtained mixed yarn by step 1；Wherein, it mixes
The mode of spinning is match network compact spinning；
Weaving: step 2 is weaved mixed yarn made from step 1 and spandex filament using circular knitting machine, obtained
Weave fabric；
The predetermined embryo of open-width: step 3 carries out open-width to the weaving fabric that step 2 obtains, and uses high temperature open width dryer
Carry out predetermined embryo；
Step 4, dyeing: step 3 dyes fabric after completing predetermined embryo, obtains dyed shell fabrics；
Wherein, it in step 4, dyes to carry out double dyes with reactive dye and acid dyes；
The process for carrying out double dyes with reactive dye and acid dyes are as follows:
A, single dye Modal fibre is first carried out at 50 DEG C with reactive dye, then carries out soap washing；
B, carried out at 95 DEG C with acid dyes again it is single contaminate cashmere fiber, then soaped, make soft wash water and go out cylinder；
Dry cloth: step 5 carries out the dry cloth of tentering using high temperature open width dryer to the dyed shell fabrics that step 4 obtains；
Sanding: step 6 carries out sanding using patch skin face of the diamond dust roller roughing-up machine to the fabric after dry cloth；
Cropping: step 7 carries out cropping processing to the face for completing sanding using rotary knife shearing machine；
Finished product of being formed: step 8 is used high temperature open width dryer to carry out tentering and is made after completing sizing with finished product of being formed
Obtain the Cashmere knitting fabric.In the present embodiment, setting temperature is 150 DEG C.
Embodiment 3.
A kind of Cashmere knitting fabric of the present embodiment, is made of the raw material of following weight percent:
Mixed yarn 98%
Spandex filament 2%；
Wherein, mixed yarn blended is made of the raw material of following weight percent:
Modal fibre 75%
Cashmere fiber 25%.
In the present embodiment, the count of yarn of mixed yarn is 50S.
In the present embodiment, the fineness of spandex filament is 30D.
A kind of production technology of above-mentioned Cashmere knitting fabric, it the following steps are included:
Spinning: the Modal fibre of formula ratio and cashmere fiber are carried out blended, obtained mixed yarn by step 1；Wherein, it mixes
The mode of spinning is match network compact spinning；
Weaving: step 2 is weaved mixed yarn made from step 1 and spandex filament using circular knitting machine, obtained
Weave fabric；
The predetermined embryo of open-width: step 3 carries out open-width to the weaving fabric that step 2 obtains, and uses high temperature open width dryer
Carry out predetermined embryo；
Step 4, dyeing: step 3 dyes fabric after completing predetermined embryo, obtains dyed shell fabrics；
Wherein, it in step 4, dyes to carry out double dyes with reactive dye and acid dyes；
The process for carrying out double dyes with reactive dye and acid dyes are as follows:
A, single dye Modal fibre is first carried out at 85 DEG C with reactive dye, then carries out soap washing；
B, carried out at 95 DEG C with acid dyes again it is single contaminate cashmere fiber, then soaped, make soft wash water and go out cylinder；
Dry cloth: step 5 carries out the dry cloth of tentering using high temperature open width dryer to the dyed shell fabrics that step 4 obtains；
Sanding: step 6 carries out sanding using patch skin face of the diamond dust roller roughing-up machine to the fabric after dry cloth；
Cropping: step 7 carries out cropping processing to the face for completing sanding using rotary knife shearing machine；
Finished product of being formed: step 8 is used high temperature open width dryer to carry out tentering and is made after completing sizing with finished product of being formed
Obtain the Cashmere knitting fabric.In the present embodiment, setting temperature is 170 DEG C.
Embodiment 4.
A kind of Cashmere knitting fabric of the present embodiment, is made of the raw material of following weight percent:
Mixed yarn 90%
Spandex filament 10%；
Wherein, mixed yarn blended is made of the raw material of following weight percent:
Modal fibre 35%
Cashmere fiber 65%.
In the present embodiment, the count of yarn of mixed yarn is 42S.
In the present embodiment, the fineness of spandex filament is 15D.
A kind of production technology of above-mentioned Cashmere knitting fabric, it the following steps are included:
Spinning: the Modal fibre of formula ratio and cashmere fiber are carried out blended, obtained mixed yarn by step 1；Wherein, it mixes
The mode of spinning is match network compact spinning；
Weaving: step 2 is weaved mixed yarn made from step 1 and spandex filament using circular knitting machine, obtained
Weave fabric；
The predetermined embryo of open-width: step 3 carries out open-width to the weaving fabric that step 2 obtains, and uses high temperature open width dryer
Carry out predetermined embryo；
Step 4, dyeing: step 3 dyes fabric after completing predetermined embryo, obtains dyed shell fabrics；
Wherein, it in step 4, dyes to carry out single dye with acid dyes；
The process singly contaminated with acid dyes are as follows:
Carried out at 95 DEG C using acid dyes it is single contaminate cashmere fiber, then soaped, make soft wash water and go out cylinder process；
Dry cloth: step 5 carries out the dry cloth of tentering using high temperature open width dryer to the dyed shell fabrics that step 4 obtains；
Sanding: step 6 carries out sanding using patch skin face of the diamond dust roller roughing-up machine to the fabric after dry cloth；
Cropping: step 7 carries out cropping processing to the face for completing sanding using rotary knife shearing machine；
Finished product of being formed: step 8 is used high temperature open width dryer to carry out tentering and is made after completing sizing with finished product of being formed
Obtain the Cashmere knitting fabric.In the present embodiment, setting temperature is 155 DEG C.
Embodiment 5.
A kind of Cashmere knitting fabric of the present embodiment, is made of the raw material of following weight percent:
Mixed yarn 95%
Spandex filament 5%；
Wherein, mixed yarn blended is made of the raw material of following weight percent:
Modal fibre 65%
Cashmere fiber 35%.
In the present embodiment, the count of yarn of mixed yarn is 48S.
In the present embodiment, the fineness of spandex filament is 25D.
A kind of production technology of above-mentioned Cashmere knitting fabric, it the following steps are included:
Spinning: the Modal fibre of formula ratio and cashmere fiber are carried out blended, obtained mixed yarn by step 1；Wherein, it mixes
The mode of spinning is match network compact spinning；
Weaving: step 2 is weaved mixed yarn made from step 1 and spandex filament using circular knitting machine, obtained
Weave fabric；
The predetermined embryo of open-width: step 3 carries out open-width to the weaving fabric that step 2 obtains, and uses high temperature open width dryer
Carry out predetermined embryo；
Step 4, dyeing: step 3 dyes fabric after completing predetermined embryo, obtains dyed shell fabrics；
Wherein, it in step 4, dyes to carry out single dye with reactive dye；
The process singly contaminated with reactive dye are as follows:
Single dye Modal fibre is carried out at 50 DEG C~85 DEG C using reactive dye, it is soft then to carry out soap washing, system
Wash water goes out cylinder process；
Dry cloth: step 5 carries out the dry cloth of tentering using high temperature open width dryer to the dyed shell fabrics that step 4 obtains；
Sanding: step 6 carries out sanding using patch skin face of the diamond dust roller roughing-up machine to the fabric after dry cloth；
Cropping: step 7 carries out cropping processing to the face for completing sanding using rotary knife shearing machine；
Finished product of being formed: step 8 is used high temperature open width dryer to carry out tentering and is made after completing sizing with finished product of being formed
Obtain the Cashmere knitting fabric.In the present embodiment, setting temperature is 165 DEG C.
Finally it should be noted that the above embodiments are merely illustrative of the technical solutions of the present invention, rather than the present invention is protected
The limitation of range is protected, although explaining in detail referring to preferred embodiment to the present invention, those skilled in the art are answered
Work as understanding, it can be with modification or equivalent replacement of the technical solution of the present invention are made, without departing from the reality of technical solution of the present invention
Matter and range.
Claims (10)
1. a kind of Cashmere knitting fabric, it is characterised in that: be made of the raw material of following weight percent:
Mixed yarn 85%~98%
Spandex filament 2%~15%；
Wherein, the mixed yarn blended is made of the raw material of following weight percent:
Modal fibre 25%~75%
Cashmere fiber 25%~75%.
2. a kind of Cashmere knitting fabric according to claim 1, it is characterised in that: be by the raw material of following weight percent
It is made:
Mixed yarn 90%~95%
Spandex filament 5%~10%；
Wherein, the mixed yarn blended is made of the raw material of following weight percent:
Modal fibre 35%~65%
Cashmere fiber 35%~65%.
3. a kind of Cashmere knitting fabric according to claim 1, it is characterised in that: be by the raw material of following weight percent
It is made:
Mixed yarn 92%
Spandex filament 8%；
Wherein, the mixed yarn blended is made of the raw material of following weight percent:
Modal fibre 45%
Cashmere fiber 55%.
4. a kind of Cashmere knitting fabric according to claim 1, it is characterised in that: the count of yarn of the mixed yarn is
40S~50S.
5. a kind of Cashmere knitting fabric according to claim 1, it is characterised in that: the fineness of the spandex filament is 10D
~30D.
6. a kind of production technology of Cashmere knitting fabric described in claim 1 to 5 any one, it is characterised in that: it includes
Following steps:
Spinning: the Modal fibre of formula ratio and cashmere fiber are carried out blended, obtained mixed yarn by step 1；
Weaving: step 2 is weaved mixed yarn made from step 1 and spandex filament using circular knitting machine, is weaved
Fabric；
The predetermined embryo of open-width: step 3 is carried out open-width to the weaving fabric that step 2 obtains, and is carried out using high temperature open width dryer
Predetermined embryo；
Step 4, dyeing: step 3 dyes fabric after completing predetermined embryo, obtains dyed shell fabrics；
Dry cloth: step 5 carries out the dry cloth of tentering using high temperature open width dryer to the dyed shell fabrics that step 4 obtains；
Sanding: step 6 carries out sanding using patch skin face of the diamond dust roller roughing-up machine to the fabric after dry cloth；
Cropping: step 7 carries out cropping processing to the face for completing sanding using rotary knife shearing machine；
Finished product of being formed: step 8 uses high temperature open width dryer to carry out tentering and obtains institute after completing sizing with finished product of being formed
State Cashmere knitting fabric.
7. a kind of production technology of Cashmere knitting fabric according to claim 6, it is characterised in that: in the step 1,
The blended mode is match network compact spinning.
8. a kind of production technology of Cashmere knitting fabric according to claim 6, it is characterised in that: in the step 4,
The dyeing is to carry out double dyes with reactive dye and acid dyes or carry out single dye with acid dyes or carried out with reactive dye
Single dye.
9. a kind of production technology of Cashmere knitting fabric according to claim 8, it is characterised in that: described to use reactive dye
The process for carrying out double dyes with acid dyes are as follows:
A, single dye Modal fibre is first carried out at 50 DEG C~85 DEG C with reactive dye, then carries out soap washing；
B, carried out at 95 DEG C with acid dyes again it is single contaminate cashmere fiber, then soaped, make soft wash water and go out cylinder；
The process singly contaminated with acid dyes are as follows:
Carried out at 95 DEG C using acid dyes it is single contaminate cashmere fiber, then soaped, make soft wash water and go out cylinder process；
The process singly contaminated with reactive dye are as follows:
Single dye Modal fibre is carried out at 50 DEG C~85 DEG C using reactive dye, then carries out soap washing, the soft wash water of system
Cylinder process out.
10. a kind of production technology of Cashmere knitting fabric according to claim 6, it is characterised in that: in the step 8,
The setting temperature is 150 DEG C~170 DEG C.