CN108301162A - A kind of production technology of spun silk cotton blending coloured-woven mercerising knitting fabric - Google Patents
A kind of production technology of spun silk cotton blending coloured-woven mercerising knitting fabric Download PDFInfo
- Publication number
- CN108301162A CN108301162A CN201711108402.3A CN201711108402A CN108301162A CN 108301162 A CN108301162 A CN 108301162A CN 201711108402 A CN201711108402 A CN 201711108402A CN 108301162 A CN108301162 A CN 108301162A
- Authority
- CN
- China
- Prior art keywords
- mercerising
- spun silk
- fabric
- woven
- production technology
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses the production technologies that a kind of spun silk cotton blending coloured-woven mercerising is knitted fabric, it is related to garment material manufacture field, using spun silk tampon blank yarn as raw material, pass through pretreatment, yarn dyeing, weaving, it singes, half mercerising, washing neutralizes, seven steps of sizing are made, the present invention takes into account the excellent performance and chemicals-resistant effect of natural fiber of spun silk fabric and blended yarn weaved fabric, provide a kind of production technology of spun silk cotton blending coloured-woven mercerising knitting fabric, the product produced wears refrigerant absorbing sweat, it is soft smooth, quality is strong, elasticity is good, there is preferable affinity with human body.
Description
Technical field
The present invention relates to garment material manufacture fields, and fabric is knitted more particularly to a kind of spun silk cotton blending coloured-woven mercerising
Production technology.
Background technology
Silk spinning is the spinning process process for the damaged cocoon, the waste silk that are generated in sericulture, throwing, silk weaving being processed into yarn.According to
Raw material and end product properties, it includes spun silk and silk that silk spinning, which has carbaso and silk spinning two major classes, product,.Natural silk fibers are elongated, it is soft,
Rich in gloss, good hygroscopicity, high-count spun silk yarn can be spinned, weaves frivolous silk spinning silk fabric, is advanced clothing materials；It also can be with chemistry
Fiber, raw silk or wool yarn etc. are woven into attractive appearance, fabric comfortable and easy to wear；Knitted fabric, and sewing can be also manufactured with spun silk
Silk thread, art silk etc..The fabric made of spun silk, soft and full, the more continuous grains in surface are that the dress ornament of classification tool style is used
Material.Since spun silk is different from the chemical resistance of cotton fiber, to determine that suitable spun silk cotton blending coloured-woven mercerising is knitted fabric
Production technology, based on production practices, especially by pre-treatment, yarn dyeing, weave, singe, half mercerising, washing, setting
Etc. processes analysis, formulated corresponding technology preparation and condition, technological process, product inspection is qualified.Two can be taken into account by having obtained
Kind of fibre property, the production technology for being suitble to such knitting fabric processing for keeping its respective advantage.
Invention content
To overcome the shortcomings of in the prior art, it is an object of the present invention to provide a kind of spun silk cotton blending coloured-woven mercerisings to be knitted fabric
Production technology.
To achieve the purpose of the present invention, technical scheme is as follows：
A kind of production technology of spun silk cotton blending coloured-woven mercerising knitting fabric, includes the following steps：
A. it pre-processes：It selects the spun silk tampon blank yarns of 10tex × 2 as raw material, spun silk cotton embryo yarn is done at refining and bleaching
Reason；
B. yarn dyeing：Spun silk cotton embryo yarn is put into reactive dyes with double active group, processes and is dyed, wherein double-active radical activity contaminates
The constituent of material is：EVERZOL reactive dye 8%, levelling agent 1%, sodium sulphate 40%~45%, sodium carbonate 5%~15%,
Remaining ingredient is water；
C. it weaves：It is selected on S3P172 plectrum small jacquard single side circular knitting machines and weaves, workshop temperature is at 25~30 DEG C, relative humidity
65%~70%, blank gram mass 132g/m2；
D. it singes：Fabric tube is strutted by circular expander, fabric coil is made uniformly to open, cloth cover when processing
Below temperature 50 C；
E. half mercerising：Fabric is put into Dornier tubular fabric mercerizing machines and carries out half mercerising, the constituent of half mercerizing agent
For caustic soda 1.6%~1.8%, mercerising oil 3%, remaining ingredient is water；
F. washing neutralizes：Fabric is put into rinsing agent and is neutralized, the constituent of rinsing agent is dispersion chelating agent
1.0%, lubricant 1.0% in bath, acetic acid 6%~7%, remaining ingredient is water；
G. it shapes：Fabric is put into sizing dressing liquid and is carried out shaping, the constituent for dressing liquid of shaping is：Without urea formaldehyde
30%~35%, catalyst 15%, rest part is softening agent.
The production technology of above-mentioned a kind of spun silk cotton blending coloured-woven mercerising knitting fabric, wherein the dispersion chelating agent is the Chinese
It is high by 540.
A kind of production technology of above-mentioned spun silk cotton blending coloured-woven mercerising knitting fabric, wherein the Dornier tubular fabrics
The pick-up rate of mercerizing machine is 140%, and machine speed is 11~15m/min.
The production technology of above-mentioned a kind of spun silk cotton blending coloured-woven mercerising knitting fabric, wherein the sizing is in hot wind tentering
It is carried out in formula boarding machine.
A kind of production technology of above-mentioned spun silk cotton blending coloured-woven mercerising knitting fabric, wherein the hot wind tentering formula setting
Machine machine speed is 10~15m/min.
The production technology of above-mentioned a kind of spun silk cotton blending coloured-woven mercerising knitting fabric, wherein corresponding soap is carried out after dyeing
It boils, fixation and soft treatment.
Beneficial effects of the present invention：Take into account the natural fiber of spun silk fabric and blended yarn weaved fabric excellent performance and chemically-resistant
Product effect, provide it is a kind of wearing refrigerant absorbing sweat, soft smooth, quality is strong, elasticity is good, there have with human body to be preferable affine
The production technology of the spun silk cotton blending coloured-woven mercerising knitting fabric of power.
Specific implementation mode
To make the technical means, the creative features, the aims and the efficiencies achieved by the present invention be easy to understand, with reference to
Specific implementation mode, the present invention is further explained.
Embodiment 1：A kind of production technology of spun silk cotton blending coloured-woven mercerising knitting fabric, includes the following steps：
A. it pre-processes：It selects the spun silk tampon blank yarns of 10tex × 2 as raw material, spun silk cotton embryo yarn is done at refining and bleaching
Reason；
B. yarn dyeing：Spun silk cotton embryo yarn is put into reactive dyes with double active group, processes and is dyed, wherein double-active radical activity contaminates
The constituent of material is：EVERZOL reactive dye 8%, levelling agent 1%, sodium sulphate 41%, sodium carbonate 10%, remaining ingredient are
Water；
C. it weaves：It is selected on S3P172 plectrum small jacquard single side circular knitting machines and weaves, workshop temperature is at 25~30 DEG C, relative humidity
65%, blank gram mass 132g/m2；
D. it singes：Fabric tube is strutted by circular expander, fabric coil is made uniformly to open, cloth cover when processing
48 DEG C of temperature；
E. half mercerising：Fabric is put into Dornier tubular fabric mercerizing machines and carries out half mercerising, the constituent of half mercerizing agent
For caustic soda 1.6%, mercerising oil 3%, remaining ingredient is water；
F. washing neutralizes：Fabric is put into rinsing agent and is neutralized, the constituent of rinsing agent is dispersion chelating agent
1.0%, lubricant 1.0% in bath, acetic acid 6%, remaining ingredient is water；
G. it shapes：Fabric is put into sizing dressing liquid and is carried out shaping, the constituent for dressing liquid of shaping is：Without urea formaldehyde
30%, catalyst 15%, rest part is softening agent.
The production technology of above-mentioned a kind of spun silk cotton blending coloured-woven mercerising knitting fabric, wherein the dispersion chelating agent is the Chinese
It is high by 540.
Embodiment 2：A kind of production technology of spun silk cotton blending coloured-woven mercerising knitting fabric, includes the following steps：
A. it pre-processes：It selects the spun silk tampon blank yarns of 10tex × 2 as raw material, spun silk cotton embryo yarn is done at refining and bleaching
Reason；
B. yarn dyeing：Spun silk cotton embryo yarn is put into reactive dyes with double active group, processes and is dyed, wherein double-active radical activity contaminates
The constituent of material is：EVERZOL reactive dye 8%, levelling agent 1%, sodium sulphate 41%, sodium carbonate 5%%, remaining ingredient are
Water；
C. it weaves：It is selected on S3P172 plectrum small jacquard single side circular knitting machines and weaves, workshop temperature is at 25~30 DEG C, relative humidity
67%, blank gram mass 132g/m2；
D. it singes：Fabric tube is strutted by circular expander, fabric coil is made uniformly to open, cloth cover when processing
Temperature 45 C；
E. half mercerising：Fabric is put into Dornier tubular fabric mercerizing machines and carries out half mercerising, the constituent of half mercerizing agent
For caustic soda 1.6%, mercerising oil 3%, remaining ingredient is water；
F. washing neutralizes：Fabric is put into rinsing agent and is neutralized, the constituent of rinsing agent is dispersion chelating agent
1.0%, lubricant 1.0% in bath, acetic acid 7%, remaining ingredient is water；
G. it shapes：Fabric is put into sizing dressing liquid and is carried out shaping, the constituent for dressing liquid of shaping is：Without urea formaldehyde
35%, catalyst 15%, rest part is softening agent.
A kind of production technology of above-mentioned spun silk cotton blending coloured-woven mercerising knitting fabric, wherein the Dornier tubular fabrics
The pick-up rate of mercerizing machine is 140%, and machine speed is 13m/min.
The production technology of above-mentioned a kind of spun silk cotton blending coloured-woven mercerising knitting fabric, wherein corresponding soap is carried out after dyeing
It boils, fixation and soft treatment.
Embodiment 3：A kind of production technology of spun silk cotton blending coloured-woven mercerising knitting fabric, includes the following steps：
A. it pre-processes：It selects the spun silk tampon blank yarns of 10tex × 2 as raw material, spun silk cotton embryo yarn is done at refining and bleaching
Reason；
B. yarn dyeing：Spun silk cotton embryo yarn is put into reactive dyes with double active group, processes and is dyed, wherein double-active radical activity contaminates
The constituent of material is：EVERZOL reactive dye 8%, levelling agent 1%, sodium sulphate 45%, sodium carbonate 7%, remaining ingredient are
Water；
C. it weaves：It is selected on S3P172 plectrum small jacquard single side circular knitting machines and weaves, at 30 DEG C, relative humidity exists workshop temperature
70%, blank gram mass 132g/m2；
D. it singes：Fabric tube is strutted by circular expander, fabric coil is made uniformly to open, cloth cover when processing
40 DEG C of temperature；
E. half mercerising：Fabric is put into Dornier tubular fabric mercerizing machines and carries out half mercerising, the constituent of half mercerizing agent
For caustic soda 1.8%, mercerising oil 3%, remaining ingredient is water；
F. washing neutralizes：Fabric is put into rinsing agent and is neutralized, the constituent of rinsing agent is dispersion chelating agent
1.0%, lubricant 1.0% in bath, acetic acid 7%, remaining ingredient is water；
G. it shapes：Fabric is put into sizing dressing liquid and is carried out shaping, the constituent for dressing liquid of shaping is：Without urea formaldehyde
33%g/L, catalyst 15%, rest part are softening agent.
A kind of production technology of above-mentioned spun silk cotton blending coloured-woven mercerising knitting fabric, wherein the Dornier tubular fabrics
The pick-up rate of mercerizing machine is 140%, and machine speed is 14m/min.
The production technology of above-mentioned a kind of spun silk cotton blending coloured-woven mercerising knitting fabric, wherein the sizing is in hot wind tentering
It is carried out in formula boarding machine.
The natural fiber of spun silk fabric and blended yarn weaved fabric excellent performance and chemicals-resistant effect are taken into account in the present invention, are carried
A kind of production technology of spun silk cotton blending coloured-woven mercerising knitting fabric is supplied, it is soft that the product produced wears refrigerant absorbing sweat, feel
Smooth refreshing, quality is strong, elasticity is good, has preferable affinity with human body.
Example the above is only the implementation of the present invention is not intended to limit the scope of the invention, every to utilize this hair
Equivalent structure or equivalent flow shift made by bright specification is applied directly or indirectly in other relevant technical fields,
Similarly it is included within the scope of the present invention.
Claims (6)
1. a kind of production technology of spun silk cotton blending coloured-woven mercerising knitting fabric, it is characterised in that：Include the following steps：
A. it pre-processes：It selects the spun silk tampon blank yarns of 10tex × 2 as raw material, refining and bleaching is done to spun silk cotton embryo yarn；
B. yarn dyeing：Spun silk cotton embryo yarn is put into reactive dyes with double active group, processes and is dyed, wherein reactive dyes with double active group, processes
Constituent is：EVERZOL reactive dye 8%, levelling agent 1%, sodium sulphate 40%~45%, sodium carbonate 5%~15%, remaining
Ingredient is water；
C. it weaves：It is selected on S3P172 plectrum small jacquard single side circular knitting machines and weaves, at 25~30 DEG C, relative humidity exists workshop temperature
65%~70%, blank gram mass 132g/m2；
D. it singes：Fabric tube is strutted by circular expander, fabric coil is made uniformly to open, cloth cover temperature when processing
50 DEG C or less；
E. half mercerising：Fabric is put into Dornier tubular fabric mercerizing machines and carries out half mercerising, the constituent of half mercerizing agent is to burn
Alkali 1.6%~1.8%, mercerising oil 3%, remaining ingredient are water；
F. washing neutralizes：Fabric is put into rinsing agent and is neutralized, the constituent of rinsing agent is dispersion chelating agent 1.0%,
Lubricant 1.0% in bath, acetic acid 6%~7%, remaining ingredient are water；
G. it shapes：Fabric is put into sizing dressing liquid and is carried out shaping, the constituent for dressing liquid of shaping is：Without urea formaldehyde 30%
~35%, catalyst 15%, rest part is softening agent.
2. a kind of production technology of spun silk cotton blending coloured-woven mercerising knitting fabric according to claim 1, which is characterized in that
The dispersion chelating agent is Henkel 540.
3. a kind of production technology of spun silk cotton blending coloured-woven mercerising knitting fabric according to claim 1, which is characterized in that
The pick-up rate of the Dornier tubular fabrics mercerizing machine is 140%, and machine speed is 11~15m/min.
4. a kind of production technology of spun silk cotton blending coloured-woven mercerising knitting fabric according to claim 1, which is characterized in that
The sizing carries out in hot wind tentering formula boarding machine.
5. a kind of production technology of spun silk cotton blending coloured-woven mercerising knitting fabric according to claim 4, which is characterized in that
The hot wind tentering formula boarding machine machine speed is 10~15m/min.
6. a kind of production technology of spun silk cotton blending coloured-woven mercerising knitting fabric according to claim 1, which is characterized in that
Corresponding soap boiling, fixation and soft treatment are carried out after dyeing.