WO2018181305A1 - 発光性曲面ガラス及び曲面デジタルサイネージ - Google Patents

発光性曲面ガラス及び曲面デジタルサイネージ Download PDF

Info

Publication number
WO2018181305A1
WO2018181305A1 PCT/JP2018/012422 JP2018012422W WO2018181305A1 WO 2018181305 A1 WO2018181305 A1 WO 2018181305A1 JP 2018012422 W JP2018012422 W JP 2018012422W WO 2018181305 A1 WO2018181305 A1 WO 2018181305A1
Authority
WO
WIPO (PCT)
Prior art keywords
light
curved
luminescent
glass
curved glass
Prior art date
Application number
PCT/JP2018/012422
Other languages
English (en)
French (fr)
Inventor
祐輔 太田
康之 伊豆
中島　大輔
Original Assignee
積水化学工業株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 積水化学工業株式会社 filed Critical 積水化学工業株式会社
Priority to CN201880004076.8A priority Critical patent/CN109890775A/zh
Priority to US16/477,569 priority patent/US11545056B2/en
Priority to EP18775218.3A priority patent/EP3604248B1/en
Priority to KR1020197008222A priority patent/KR102500390B1/ko
Priority to MX2019010762A priority patent/MX2019010762A/es
Priority to JP2018517653A priority patent/JP7010814B2/ja
Publication of WO2018181305A1 publication Critical patent/WO2018181305A1/ja

Abstract

本発明は、曲率半径が小さい曲面状にもかかわらず、光線が照射されることにより全面において鮮明な表示を行うことができる発光性曲面ガラス、及び、該発光性曲面ガラスを用いた曲面デジタルサイネージを提供することを目的とする。 本発明は、曲率半径が３０００ｍｍ以下の透明板と発光シートとの積層体からなる発光性曲面ガラスであって、前記発光シートは、熱可塑性樹脂と、励起光によって波長３８０～７５０ｎｍの可視光を発光する発光材料とを含有する発光性曲面ガラスである。

Description

発光性曲面ガラス及び曲面デジタルサイネージ
本発明は、曲率半径が小さい曲面状にもかかわらず、光線が照射されることにより全面において鮮明な表示を行うことができる発光性曲面ガラス、及び、該発光性曲面ガラスを用いた曲面デジタルサイネージに関する。
駅や空港等の公共施設やデパート等の商業施設には、ディスプレイに動画や静止画で種々の情報を表示するデジタルサイネージが設置されている。これらのデジタルサイネージにおいては、液晶ディスプレイやプラズマディスプレイが用いられるのが一般的であるが（例えば、特許文献１等）、大型のデジタルサイネージに液晶ディスプレイ等を用いた場合、極めて高価なものとなる。
これに対して、特殊な加工を施したガラス等をスクリーンとして、映像プロジェクタから映像を投影する方法が採用されるようになってきている。
しかしながら、近年では、より高い意匠性を発揮した、複雑な形状のデジタルサイネージが求められるようになってきている。また、建築物の柱を利用してデジタルサイネージのスクリーンを設置することも行われている。このような複雑な形状や柱状等の曲率半径の小さな曲面状のスクリーンに映像を投影した場合、スクリーンの全面において鮮明な表示を行うことが困難であるという問題があった。
特表平４－５０２５２５号公報
本発明は、上記現状に鑑み、曲率半径が小さい曲面状にもかかわらず、光線が照射されることにより全面において鮮明な表示を行うことができる発光性曲面ガラス、及び、該発光性曲面ガラスを用いた曲面デジタルサイネージを提供することを目的とする。
本発明は、曲率半径が３０００ｍｍ以下の透明板と発光シートとの積層体からなる発光性曲面ガラスであって、前記発光シートは、熱可塑性樹脂と、励起光によって波長３８０～７５０ｎｍの可視光を発光する発光材料とを含有する発光性曲面ガラスである。
以下に本発明を詳述する。
本発明者らは、鋭意検討の結果、熱可塑性樹脂と、励起光によって波長３８０～７５０ｎｍの可視光を発光する発光材料とを含有する発光シートを透明板に積層した積層体に、該励起光を照射することにより、種々の画像を表示することができることを見出した。該画像は、映像プロジェクタから投影されたものではなく、積層体自体が発光することにより表示されるものである。従って、映像プロジェクタから投影する場合とは異なり、たとえ積層体が曲率半径の小さい曲面状であっても、全面において鮮明な表示を行うことができる。
本発明の発光性曲面ガラスは、透明板と発光シートとの積層体からなる。
上記透明板は、本発明の発光性曲面ガラスに強度を付与し、取り扱い性を向上させる役割を有する。上記積層体としては、なかでも一対の透明板の間に上記発光シートが積層されている構造（合わせガラス構造）を採ることが好ましい。
上記透明板は、一般に使用されている透明板ガラスを使用することができる。例えば、フロート板ガラス、磨き板ガラス、型板ガラス、網入りガラス、線入り板ガラス、着色された板ガラス、熱線吸収ガラス、熱線反射ガラス、グリーンガラス等の無機ガラスが挙げられる。また、ガラスの表面に紫外線遮蔽コート層が形成された紫外線遮蔽ガラスも用いることができるが、特定の波長の光線を照射する側とは反対のガラス板として用いることが好ましい。更に、上記透明板としてポリエチレンテレフタレート、ポリカーボネート、ポリアクリレート等の有機プラスチックス板を用いることもできる。
上記透明板として、２種類以上の透明板を用いてもよい。また、上記透明板として、２種以上の厚さの異なる透明板を用いてもよい。
上記透明板は、曲率半径が３０００ｍｍ以下の曲面状である。曲率半径が３０００ｍｍ以下であれば、意匠性の高い複雑な形状のデジタルサイネージや、建築物の柱を利用してデジタルサイネージに好適に用いることができる。上記透明板は、曲率半径が２０００ｍｍ以下の曲面状であることが好ましく、曲率半径が１０００ｍｍ以下の曲面状であることがより好ましい。
本発明の発光性曲面ガラスは、透明板の曲率半径が３０００ｍｍを超える場合であっても、励起光を照射することにより、種々の画像を表示することはできる。しかしながら、本発明は、曲率半径が３０００ｍｍ以下の曲面状であっても、光線が照射されることにより全面において鮮明な表示を行うことができる点において大きな利点がある。
上記透明板の厚みは特に限定されないが、好ましい下限は１．５ｍｍ、好ましい上限は１５ｍｍである。上記透明板の厚みが上記範囲内であると、充分な強度と取り扱い性とを両立することができる。上記透明板の厚みのより好ましい下限は２．０ｍｍ、より好ましい上限は１２ｍｍである。
上記発光シートは、熱可塑性樹脂と、励起光によって波長３８０～７５０ｎｍの可視光を発光する発光材料とを含有する。このような発光シートを有する発光性曲面ガラスに励起光を照射することにより、発光性曲面ガラス自体が発光して、種々の画像を表示することができる。
上記熱可塑性樹脂は特に限定されず、例えば、ポリビニルアセタール樹脂、エチレン－酢酸ビニル共重合体樹脂、エチレン－アクリル共重合体樹脂、ポリウレタン樹脂、硫黄元素を含有するポリウレタン樹脂、ポリビニルアルコール樹脂、塩化ビニル樹脂、ポリエチレンテレフタレート樹脂等が挙げられる。なかでも、可塑剤と併用することにより上記透明板に対して優れた接着性を発揮できることからポリビニルアセタール樹脂が好適である。
上記ポリビニルアセタール樹脂は、ポリビニルアルコールをアルデヒドでアセタール化して得られるポリビニルアセタール樹脂であれば特に限定されないが、ポリビニルブチラールが好適である。また、必要に応じて２種以上のポリビニルアセタールを併用してもよい。
上記ポリビニルアセタール樹脂のアセタール化度の好ましい下限は４０モル％、好ましい上限は８５モル％であり、より好ましい下限は６０モル％、より好ましい上限は７５モル％である。
上記ポリビニルアセタール樹脂は、水酸基量の好ましい下限が１５モル％、好ましい上限が３５モル％である。水酸基量が１５モル％以上であると、合わせガラス用中間膜の成形が容易になる。水酸基量が３５モル％以下であると、得られる発光シートの取り扱いが容易になる。
なお、上記アセタール化度及び水酸基量は、例えば、ＪＩＳ　Ｋ６７２８「ポリビニルブチラール試験方法」に準拠して測定できる。
上記ポリビニルアセタール樹脂は、ポリビニルアルコールをアルデヒドでアセタール化することにより調製することができる。上記ポリビニルアルコールは、通常、ポリ酢酸ビニルを鹸化することにより得られ、鹸化度７０～９９．８モル％のポリビニルアルコールが一般的に用いられる。
上記ポリビニルアルコールの重合度の好ましい下限は５００、好ましい上限は４０００である。上記ポリビニルアルコールの重合度が５００以上であると、得られる発光シートを用いた合わせガラスの耐貫通性が高くなる。上記ポリビニルアルコールの重合度が４０００以下であると、発光シートの成形が容易になる。上記ポリビニルアルコールの重合度のより好ましい下限は１０００、より好ましい上限は３６００である。
上記アルデヒドは特に限定されないが、一般には、炭素数が１～１０のアルデヒドが好適に用いられる。上記炭素数が１～１０のアルデヒドは特に限定されず、例えば、ｎ－ブチルアルデヒド、イソブチルアルデヒド、ｎ－バレルアルデヒド、２－エチルブチルアルデヒド、ｎ－ヘキシルアルデヒド、ｎ－オクチルアルデヒド、ｎ－ノニルアルデヒド、ｎ－デシルアルデヒド、ホルムアルデヒド、アセトアルデヒド、ベンズアルデヒド等が挙げられる。なかでも、ｎ－ブチルアルデヒド、ｎ－ヘキシルアルデヒド、ｎ－バレルアルデヒドが好ましく、ｎ－ブチルアルデヒドがより好ましい。これらのアルデヒドは単独で用いてもよく、２種以上を併用してもよい。
上記発光材料は、励起光により波長３８０～７５０ｎｍの可視光を発光する発光材料である。このような発光材料を用いることにより、発光性曲面ガラスに励起光を照射することにより、発光性曲面ガラス自体が発光して、種々の画像を表示することができる。
上記発光材料としては励起光により波長３８０～７５０ｎｍの可視光を発光するものであれば特に限定されず、従来公知の発光材料を用いることができる。発光材料は単独で用いてもよく、２種以上を併用してもよい。なかでも、高い輝度で発光させることができることから、ハロゲン原子を含む多座配位子を有するランタノイド錯体や、テレフタル酸エステル構造を有する発光材料が好適である。
ランタノイド錯体のなかでも、ハロゲン原子を含む多座配位子を有するランタノイド錯体は光線を照射することにより高い発光強度で発光する。上記ハロゲン原子を含む多座配位子を有するランタノイド錯体としては、ハロゲン原子を含む二座配位子を有するランタノイド錯体、ハロゲン原子を含む三座配位子を有するランタノイド錯体、ハロゲン原子を含む四座配位子を有するランタノイド錯体、ハロゲン原子を含む五座配位子を有するランタノイド錯体、ハロゲン原子を含む六座配位子を有するランタノイド錯体等が挙げられる。
なかでも、ハロゲン原子を含む二座配位子を有するランタノイド錯体又はハロゲン原子を含む三座配位子を有するランタノイド錯体は、３００～４１０ｎｍの波長の光を照射することにより、５８０～７８０ｎｍの波長の光を極めて高い発光強度で発光する。この発光は極めて高強度であることから、これを含有する発光シートは、ごく弱い励起光でも充分に発光して、「暈し発光」による極めて優れた美観を呈することができる。
しかも、上記ハロゲン原子を含む二座配位子を有するランタノイド錯体又はハロゲン原子を含む三座配位子を有するランタノイド錯体は、耐熱性にも優れる。従って、発光シートを太陽光の赤外線が照射される屋外で使用したときにも、高温によって発光材料が劣化してしまうのを防止することができる。
本明細書においてランタノイドとは、ランタン、セリウム、プラセオジム、ネオジム、プロメチウム、サマリウム、ユーロピウム、ガドリニウム、テルビウム、ジスプロシウム、ホルミウム、エルビウム、ツリウム、イッテルビウム又はルテチウムを含む。より一層高い発光強度が得られることから、ランタノイドは、ネオジム、ユーロピウム又はテルビウムが好ましく、ユーロピウム又はテルビウムがより好ましく、ユーロピウムが更に好ましい。
上記ハロゲン原子を含む二座配位子を有するランタノイド錯体は、例えば、トリス（トリフルオロアセチルアセトン）フェナントロリンユーロピウム、トリス（トリフルオロアセチルアセトン）ジフェニルフェナントロリンユーロピウム、トリス（ヘキサフルオロアセチルアセトン）ジフェニルフェナントロリンユーロピウム、トリス（ヘキサフルオロアセチルアセトン）ビス（トリフェニルホスフィン）ユーロピウム、トリス（トリフルオロアセチルアセトン）２，２’－ビピリジンユーロピウム、トリス（ヘキサフルオロアセチルアセトン）２，２’－ビピリジンユーロピウム等が挙げられる。
上記ハロゲン原子を含む三座配位子を有するランタノイド錯体は、例えば、ターピリジントリフルオロアセチルアセトンユーロピウム、ターピリジンヘキサフルオロアセチルアセトンユーロピウム等が挙げられる。
上記ハロゲン原子を含む二座配位子を有するランタノイド錯体又はハロゲン原子を含む三座配位子を有するランタノイド錯体のハロゲン原子としては、フッ素原子、塩素原子、臭素原子、ヨウ素原子を用いることができる。なかでも、配位子の構造を安定化させることから、フッ素原子が好適である。
上記ハロゲン原子を含む二座配位子を有するランタノイド錯体又はハロゲン原子を含む三座配位子を有するランタノイド錯体のなかでも、特に初期発光性に優れることから、ハロゲン原子を含むアセチルアセトン骨格を有する二座配位子を有するランタノイド錯体が好適である。
上記ハロゲン原子を含むアセチルアセトン骨格を有する二座配位子を有するランタノイド錯体は、例えば、Ｅｕ（ＴＦＡ）３ｐｈｅｎ、Ｅｕ（ＴＦＡ）３ｄｐｐｈｅｎ、Ｅｕ（ＨＦＡ）３ｐｈｅｎ、［Ｅｕ（ＦＯＤ）３］ｂｐｙ、［Ｅｕ（ＴＦＡ）３］ｔｍｐｈｅｎ、［Ｅｕ（ＦＯＤ）３］ｐｈｅｎ等が挙げられる。これらのハロゲン原子を含むアセチルアセトン骨格を有する二座配位子を有するランタノイド錯体の構造を示す。
Figure JPOXMLDOC01-appb-C000001
上記ハロゲン原子を含む二座配位子を有するランタノイド錯体又はハロゲン原子を含む三座配位子を有するランタノイド錯体は、粒子状であることが好ましい。粒子状であることにより、上記ハロゲン原子を含む二座配位子を有するランタノイド錯体又はハロゲン原子を含む三座配位子を有するランタノイド錯体を発光シート中に微分散させることがより容易となる。
上記ハロゲン原子を含む二座配位子を有するランタノイド錯体又はハロゲン原子を含む三座配位子を有するランタノイド錯体が粒子状である場合、ランタノイド錯体の平均粒子径の好ましい下限は０．０１μｍ、好ましい上限は１０μｍであり、より好ましい下限は０．０３μｍ、より好ましい上限は１μｍである。
上記テレフタル酸エステル構造を有する発光材料は、例えば、下記一般式（１）で表される構造を有する化合物や下記一般式（２）で表される構造を有する化合物が挙げられる。
これらは単独で用いてもよく、２種以上を用いてもよい。
Figure JPOXMLDOC01-appb-C000002
上記一般式（１）中、Ｒ１は有機基を表し、ｘは１、２、３又は４である。
発光シートの透明性がより一層高くなることから、ｘは１又は２であることが好ましく、ベンゼン環の２位又は５位に水酸基を有することがより好ましく、ベンゼン環の２位及び５位に水酸基を有することが更に好ましい。
上記Ｒ１の有機基は炭化水素基であることが好ましく、炭素数が１～１０の炭化水素基であることがより好ましく、炭素数が１～５の炭化水素基であることが更に好ましく、炭素数が１～３の炭化水素基であることが特に好ましい。
上記炭化水素基の炭素数が１０以下であると、上記テレフタル酸エステル構造を有する発光材料を発光シートに容易に分散させることができる。
上記炭化水素基はアルキル基であることが好ましい。
上記一般式（１）で表される構造を有する化合物として、例えば、ジエチル－２，５－ジヒドロキシテレフタレート、ジメチル－２，５－ジヒドロキシテレフタレート等が挙げられる。
なかでも、コントラストがより一層高い画像を表示できることから、上記一般式（１）で表される構造を有する化合物はジエチル－２，５－ジヒドロキシルテレフタレート（Ａｌｄｒｉｃｈ社製「２，５－ジヒドロキシテレフタル酸ジエチル」）であることが好ましい。
上記一般式（２）中、Ｒ２は有機基を表し、Ｒ３及びＲ４は水素原子又は有機基を表し、ｙは１、２、３又は４である。
上記Ｒ２の有機基は炭化水素基であることが好ましく、炭素数が１～１０の炭化水素基であることがより好ましく、炭素数が１～５の炭化水素基であることが更に好ましく、炭素数が１～３の炭化水素基であることが特に好ましい。
上記炭化水素基の炭素数が上記上限以下であると、上記テレフタル酸エステル構造を有する発光材料を発光シートに容易に分散させることができる。
上記炭化水素基はアルキル基であることが好ましい。
上記一般式（２）中、ＮＲ３Ｒ４はアミノ基である。
Ｒ３及びＲ４は、水素原子であることが好ましい。
上記一般式（２）で表される構造を有する化合物のベンゼン環の水素原子のうち、一つの水素原子が上記アミノ基であってもよく、二つの水素原子が上記アミノ基であってもよく、三つの水素原子が上記アミノ基であってもよく、四つの水素原子が上記アミノ基であってもよい。
上記一般式（２）で表される構造を有する化合物として、コントラストがより一層高い画像を表示できることから、ジエチル－２，５－ジアミノテレフタレート（Ａｌｄｒｉｃｈ社製）が好ましい。
上記発光シートにおける上記発光材料の含有量は、発光材料の種類に応じて適宜調整すればよいが、上記熱可塑性樹脂１００重量部に対する好ましい下限は０．００１重量部、好ましい上限は１０重量部である。上記発光材料の含有量がこの範囲内であると、上記顔料と併用することにより優れた美観を呈することができる。上記発光材料の含有量のより好ましい下限は０．０１重量部、より好ましい上限は８重量部、更に好ましい下限は０．１重量部、更に好ましい上限は５重量部である。
上記発光シートは、更に、可塑剤を含有してもよい。
上記可塑剤は特に限定されず、例えば、一塩基性有機酸エステル、多塩基性有機酸エステル等の有機エステル可塑剤、有機リン酸可塑剤、有機亜リン酸可塑剤等のリン酸可塑剤等が挙げられる。上記可塑剤は液状可塑剤であることが好ましい。
上記一塩基性有機酸エステルは特に限定されないが、例えば、グリコールと一塩基性有機酸との反応によって得られたグリコールエステル等が挙げられる。上記グリコールとしては、例えば、トリエチレングリコール、テトラエチレングリコール、トリプロピレングリコール等が挙げられる。上記一塩基性有機酸としては、例えば、酪酸、イソ酪酸、カプロン酸、２－エチル酪酸、ヘプチル酸、ｎ－オクチル酸、２－エチルヘキシル酸、ペラルゴン酸（ｎ－ノニル酸）、デシル酸等が挙げられる。なかでも、トリエチレングリコールジカプロン酸エステル、トリエチレングリコールジ－２－エチル酪酸エステル、トリエチレングリコールジ－ｎ－オクチル酸エステル、トリエチレングリコールジ－２－エチルヘキシル酸エステル等が好適である。
上記多塩基性有機酸エステルは特に限定されないが、例えば、アジピン酸、セバシン酸、アゼライン酸等の多塩基性有機酸と、炭素数４～８の直鎖又は分岐構造を有するアルコールとのエステル化合物が挙げられる。なかでも、ジブチルセバシン酸エステル、ジオクチルアゼライン酸エステル、ジブチルカルビトールアジピン酸エステル等が好適である。
上記有機エステル可塑剤は特に限定されず、トリエチレングリコールジ－２－エチルブチレート、トリエチレングリコールジ－２－エチルヘキサノエート、トリエチレングリコールジカプリレート、トリエチレングリコールジ－ｎ－オクタノエート、トリエチレングリコールジ－ｎ－ヘプタノエート、テトラエチレングリコールジ－ｎ－ヘプタノエート、テトラエチレングリコールジ－２－エチルヘキサノエート、ジブチルセバケート、ジオクチルアゼレート、ジブチルカルビトールアジペート、エチレングリコールジ－２－エチルブチレート、１，３－プロピレングリコールジ－２－エチルブチレート、１，４－ブチレングリコールジ－２－エチルブチレート、ジエチレングリコールジ－２－エチルブチレート、ジエチレングリコールジ－２－エチルヘキサノエート、ジプロピレングリコールジ－２－エチルブチレート、トリエチレングリコールジ－２－エチルペンタノエート、テトラエチレングリコールジ－２－エチルブチレート、ジエチレングリコールジカプリエート、アジピン酸ジヘキシル、アジピン酸ジオクチル、アジピン酸ヘキシルシクロヘキシル、アジピン酸ジイソノニル、アジピン酸ヘプチルノニル、セバシン酸ジブチル、油変性セバシン酸アルキド、リン酸エステルとアジピン酸エステルとの混合物、アジピン酸エステル、炭素数４～９のアルキルアルコール及び炭素数４～９の環状アルコールから作製された混合型アジピン酸エステル、アジピン酸ヘキシル等の炭素数６～８のアジピン酸エステル等が挙げられる。
上記有機リン酸可塑剤は特に限定されず、例えば、トリブトキシエチルホスフェート、イソデシルフェニルホスフェート、トリイソプロピルホスフェート等が挙げられる。
上記可塑剤のなかでも、ジヘキシルアジペート（ＤＨＡ）、トリエチレングリコールジ－２－エチルヘキサノエート（３ＧＯ）、テトラエチレングリコールジ－２－エチルヘキサノエート（４ＧＯ）、トリエチレングリコールジ－２－エチルブチレート（３ＧＨ）、テトラエチレングリコールジ－２－エチルブチレート（４ＧＨ）、テトラエチレングリコールジ－ｎ－ヘプタノエート（４Ｇ７）及びトリエチレングリコールジ－ｎ－ヘプタノエート（３Ｇ７）からなる群より選択される少なくとも１種であることが好ましい。
更に、上記可塑剤として、加水分解を起こしにくいため、トリエチレングリコールジ－２－エチルヘキサノエート（３ＧＯ）、トリエチレングリコールジ－２－エチルブチレート（３ＧＨ）、テトラエチレングリコールジ－２－エチルヘキサノエート（４ＧＯ）、ジヘキシルアジペート（ＤＨＡ）を含有することが好ましい。テトラエチレングリコールジ－２－エチルヘキサノエート（４ＧＯ）、トリエチレングリコールジ－２－エチルヘキサノエート（３ＧＯ）を含有することがより好ましい。トリエチレングリコールジ－２－エチルヘキサノエートを含有することが更に好ましい。
上記発光シートにおける上記可塑剤の含有量は特に限定されないが、上記熱可塑性樹脂１００重量部に対する好ましい下限が３０重量部、好ましい上限が１００重量部である。上記可塑剤の含有量がこの範囲内であると、発光シートの美観を損ねることなく、成形を容易にすることができる。上記可塑剤の含有量のより好ましい下限は３５重量部、より好ましい上限は８０重量部、更に好ましい下限は４５重量部、更に好ましい上限は７０重量部、特に好ましい下限は５０重量部、特に好ましい上限は６３重量部である。
上記発光シートは接着力調整剤を含有することが好ましい。
上記接着力調整剤としては、例えば、アルカリ金属塩又はアルカリ土類金属塩が好適に用いられる。上記接着力調整剤として、例えば、カリウム、ナトリウム、マグネシウム等の塩が挙げられる。
上記塩を構成する酸としては、例えば、オクチル酸、ヘキシル酸、２－エチル酪酸、酪酸、酢酸、蟻酸等のカルボン酸の有機酸、又は、塩酸、硝酸等の無機酸が挙げられる。
なお、上記発光シートには、上記接着力調整剤の他に、熱可塑性樹脂製造時に用いた中和剤等の原料に由来するカリウム、ナトリウム、マグネシウムが含まれ得る。これらの金属の含有量が多い場合には、発光材料の発光性が低下することがある。このような発光性の低下は、発光材料が上記ハロゲン原子を含む二座配位子を有するランタノイド錯体又はハロゲン原子を含む三座配位子を有するランタノイド錯体である場合に特に顕著である。
そこで、発光シートに含まれるカリウム、ナトリウム及びマグネシウムの合計の含有量は５０ｐｐｍ以下であることが好ましい。カリウム、ナトリウム及びマグネシウムの合計の含有量を５０ｐｐｍ以下とすることにより、発光材料の発光性が低下するのを防止することができる。
上記発光シートは、更に分散剤を含有することが好ましい。分散剤を含有することにより、上記発光材料の凝集を抑制できる。
上記分散剤は、例えば、直鎖アルキルベンゼンスルホン酸塩等のスルホン酸構造を有する化合物や、ジエステル化合物、リシノール酸アルキルエステル、フタル酸エステル、アジピン酸エステル、セバシン酸エステル、リン酸エステル等のエステル構造を有する化合物や、ポリオキシエチレングリコール、ポリオキシプロピレングリコールやアルキルフェニル－ポリオキシエチレン－エーテル等のエーテル構造を有する化合物や、ポリカルボン酸等のカルボン酸構造を有する化合物や、ラウリルアミン、ジメチルラウリルアミン、オレイルプロピレンジアミン、ポリオキシエチレンの２級アミン、ポリオキシエチレンの３級アミン、ポリオキシエチレンのジアミン等のアミン構造を有する化合物や、ポリアルキレンポリアミンアルキレンオキシド等のポリアミン構造を有する化合物や、オレイン酸ジエタノールアミド、アルカノール脂肪酸アミド等のアミド構造を有する化合物や、ポリビニルピロリドン、ポリエステル酸アマイドアミン塩等の高分子量型アミド構造を有する化合物等の分散剤を用いることができる。また、ポリオキシエチレンアルキルエーテルリン酸（塩）や高分子ポリカルボン酸、縮合リシノール酸エステル等の高分子量分散剤を用いてもよい。なお、高分子量分散剤とは、その分子量が１万以上である分散剤と定義される。
上記発光材料が上記ハロゲン原子を含む二座配位子を有するランタノイド錯体又はハロゲン原子を含む三座配位子を有するランタノイド錯体である場合、上記発光シート中における発光材料１００重量部に対する上記分散剤の含有量の好ましい下限は１重量部、好ましい上限は５０重量部である。上記分散剤の含有量がこの範囲内であると、上記ハロゲン原子を含む二座配位子を有するランタノイド錯体又はハロゲン原子を含む三座配位子を有するランタノイド錯体を発光シート中に均一に分散させることができる。上記分散剤の含有量のより好ましい下限は３重量部、より好ましい上限は３０重量部であり、更に好ましい下限は５重量部、更に好ましい上限は２５重量部である。
上記発光シートは、必要に応じて、紫外線吸収剤、酸化防止剤、光安定剤、帯電防止剤、青色顔料、青色染料、緑色顔料、緑色染料等の添加剤を含有してもよい。
本発明の発光性曲面ガラスは、曲率半径が小さい曲面状にもかかわらず、上記発光材料の励起光が照射されることにより全面において鮮明な表示を行うことができる。従って、意匠性の高い複雑な形状のデジタルサイネージや、建築物の柱を利用してデジタルサイネージに好適に用いることができる。
光源と、本発明の発光性曲面ガラスとからなる曲面デジタルサイネージもまた、本発明の１つである。
本発明によれば、曲率半径が小さい曲面状にもかかわらず、光線が照射されることにより全面において鮮明な表示を行うことができる発光性曲面ガラス、及び、該発光性曲面ガラスを用いた曲面デジタルサイネージを提供できる。
実施例、比較例の評価において文字情報を表示させる方法を説明する模式図である。
以下に実施例を挙げて本発明の態様を更に詳しく説明するが、本発明はこれら実施例にのみ限定されるものではない。
（実施例１）
（１）Ｅｕ（ＴＦＡ）３ｐｈｅｎの調製
酢酸ユーロピウム（Ｅｕ（ＣＨ３ＣＯＯ）３）１２．５ｍｍｏｌを５０ｍＬの蒸留水へ溶かし、トリフルオロアセチルアセトン（ＴＦＡ、ＣＨ３ＣＯＣＨ２ＣＯＣＦ３）３３．６ｍｍｏｌを加え、室温で３時間撹拌した。沈殿した固体を濾過、水洗後、メタノールと蒸留水で再結晶を行なってＥｕ（ＴＦＡ）３（Ｈ２Ｏ）２を得た。得られた錯体Ｅｕ（ＴＦＡ）３（Ｈ２Ｏ）２５．７７ｇと１，１０－フェナントロリン（ｐｈｅｎ）２．５ｇを１００ｍＬのメタノールに溶かし、１２時間加熱還流を行なった。１２時間後、メタノールを減圧留去により取り除き、白色生成物を得た。この粉末をトルエンで洗浄し、未反応の原料を吸引濾過により取り除いた後、トルエンを減圧留去し、紛体を得た。トルエン、ヘキサンの混合溶媒により再結晶を行なうことにより、Ｅｕ（ＴＦＡ）３ｐｈｅｎを得た。
（２）発光シートの調製
可塑剤であるトリエチレングリコールジ－２－エチルヘキサノエート（３ＧＯ）４０重量部に、発光材料としてＥｕ（ＴＦＡ）３ｐｈｅｎ０．２重量部と、接着力調整剤として最終的な濃度が０．０３６ｐｈｒとなるようにアセチルアセトンマグネシウムを加え、発光性の可塑剤溶液を調製した。得られた可塑剤溶液の全量と、ポリビニルブチラール（ＰＶＢ、重合度１７００）１００重量部とをミキシングロールで充分に混練して樹脂組成物を調製した。
得られた樹脂組成物を、押出機を用いて押出し、厚み７６０μｍの発光シートを得た。
（３）発光性曲面ガラスの製造
得られた発光シートを、縦３０ｃｍ×横３０ｃｍの一対のクリアガラス（厚み２．５ｍｍ、曲率半径が３０００ｍｍの曲面状）の間に積層し、積層体を得た。得られた積層体を、真空ラミネーターにて９０℃下、３０分保持しつつ真空プレスを行い圧着した。圧着後１４０℃、１４ＭＰａの条件でオートクレーブを用いて２０分間圧着を行い、合わせガラス構造の発光性曲面ガラスを得た。
（実施例２）
一対のクリアガラスとして厚み２．５ｍｍ、曲率半径２０００ｍｍのものを用いた以外は実施例１と同様にして発光シート、発光性曲面ガラスを製造した。
（実施例３）
一対のクリアガラスとして厚み２．５ｍｍ、曲率半径１０００ｍｍのものを用いた以外は実施例１と同様にして発光シート、発光性曲面ガラスを製造した。
（実施例４）
酢酸テリビウム（Ｔｂ（ＣＨ３ＣＯＯ）３）１２．５ｍｍｏｌを５０ｍＬの蒸留水へ溶かし、トリフルオロアセチルアセトン（ＴＦＡ、ＣＨ３ＣＯＣＨ２ＣＯＣＦ３）３３．６ｍｍｏｌを加え、室温で３時間撹拌した。沈殿した固体を濾過、水洗後、メタノールと蒸留水で再結晶を行なってＴｂ（ＴＦＡ）３（Ｈ２Ｏ）２を得た。得られた錯体Ｔｂ（ＴＦＡ）３（Ｈ２Ｏ）２５．７７ｇと１，１０－フェナントロリン（ｐｈｅｎ）２．５ｇを１００ｍＬのメタノールに溶かし、１２時間加熱還流を行なった。１２時間後、メタノールを減圧留去により取り除き、白色生成物を得た。この粉末をトルエンで洗浄し、未反応の原料を吸引濾過により取り除いた後、トルエンを減圧留去し、紛体を得た。トルエン、ヘキサンの混合溶媒により再結晶を行なうことにより、Ｔｂ（ＴＦＡ）３ｐｈｅｎを得た。
Ｅｕ（ＴＦＡ）３ｐｈｅｎに代えてＴｂ（ＴＦＡ）３ｐｈｅｎを用いた以外は実施例１と同様にして発光シート、発光性曲面ガラスを製造した。
（実施例５）
Ｅｕ（ＴＦＡ）３ｐｈｅｎに代えてジエチル－２，５－ジヒドロキシテレフタレート（アルドリッチ社製、「２，５－ジヒドロキシテレフタル酸ジエチル」）を用いた以外は実施例１と同様にして発光シート、発光性曲面ガラスを製造した。
（比較例１）
発光材料を用いなかった以外は実施例１と同様にして樹脂シート、曲面ガラスを製造した。
（評価）
実施例及び比較例で得られた発光性曲面ガラスについて、以下の方法で評価を行った。
結果を表１に示した。
図１に示したように、実施例で得られた発光性曲面ガラスの曲面の中心点側から、映像プロジェクタ（ＯＰＵＳ社製、ｅＰｒｏ－２０００）を励起光源として波長４０５ｎｍ、出力１ｍＷの光を照射して、発光材料を発光させることにより文字情報として「Ａ」を９カ所に表示させた。
一方、比較例１で得られた曲面ガラスの曲面の中心点から、映像プロジェクタ（ＯＰＵＳ社製、ｅＰｒｏ－２０００）を用いて波長５１５ｎｍの緑色光を照射して、文字情報として「Ａ」を９カ所に表示させた。
目視にて各「Ａ」を観察して、歪みが認められた「Ａ」が５つ未満であった場合を「○」と、歪みが認められた「Ａ」が５つ以上であった場合を「×」と評価した。
Figure JPOXMLDOC01-appb-T000003
本発明によれば、曲率半径が小さい曲面状にもかかわらず、光線が照射されることにより全面において鮮明な表示を行うことができる発光性曲面ガラス、及び、該発光性曲面ガラスを用いた曲面デジタルサイネージを提供できる。 

Claims (5)

  1. 曲率半径が３０００ｍｍ以下の透明板と発光シートとの積層体からなる発光性曲面ガラスであって、
    前記発光シートは、熱可塑性樹脂と、励起光によって波長３８０～７５０ｎｍの可視光を発光する発光材料とを含有する
    ことを特徴とする発光性曲面ガラス。
  2. 透明板の曲率半径が２０００ｍｍ以下であることを特徴とする請求項１記載の発光性曲面ガラス。
  3. 透明板の曲率半径が１０００ｍｍ以下であることを特徴とする請求項１記載の発光性曲面ガラス。
  4. 一対の透明板の間に発光シートが積層されている積層体からなることを特徴とする請求項１、２又は３記載の発光性曲面ガラス。
  5. 光源と、請求項１、２、３又は４記載の発光性曲面ガラスとからなることを特徴とする曲面デジタルサイネージ。
PCT/JP2018/012422 2017-03-29 2018-03-27 発光性曲面ガラス及び曲面デジタルサイネージ WO2018181305A1 (ja)