WO2018062438A1 - Agent d'alignement de cristaux liquides, film d'alignement de cristaux liquides et élément d'écran à cristaux liquides - Google Patents

Agent d'alignement de cristaux liquides, film d'alignement de cristaux liquides et élément d'écran à cristaux liquides Download PDF

Info

Publication number
WO2018062438A1
WO2018062438A1 PCT/JP2017/035348 JP2017035348W WO2018062438A1 WO 2018062438 A1 WO2018062438 A1 WO 2018062438A1 JP 2017035348 W JP2017035348 W JP 2017035348W WO 2018062438 A1 WO2018062438 A1 WO 2018062438A1
Authority
WO
WIPO (PCT)
Prior art keywords
group
liquid crystal
formula
carbon atoms
aligning agent
Prior art date
Application number
PCT/JP2017/035348
Other languages
English (en)
Japanese (ja)
Inventor
アルム 金
Original Assignee
日産化学工業株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 日産化学工業株式会社 filed Critical 日産化学工業株式会社
Priority to CN201780060270.3A priority Critical patent/CN109791329B/zh
Priority to JP2018542891A priority patent/JP7089229B2/ja
Priority to KR1020197011769A priority patent/KR102453433B1/ko
Priority to CN202111009465.XA priority patent/CN113805386B/zh
Publication of WO2018062438A1 publication Critical patent/WO2018062438A1/fr

Abstract

Cet agent d'alignement de cristaux liquides est caractérisé en ce qu'il contient : (A) au moins un polymère choisi parmi un acide polyamique et un polymère imidisé de celui-ci, ledit acide polyamique obtenu à l'aide d'un composant dianhydride d'acide tétracarboxylique, qui contient un dianhydride d'acide tétracarboxylique représenté par l'expression (1) et un dianhydride d'acide tétracarboxylique aliphatique dans un rapport de 10 : 90 à 90 : 10, et un composant diamine, qui contient une diamine représentée par l'expression (2); (B) au moins un polymère choisi dans le groupe constitué par un précurseur de polyimide, un polymère imidisé dudit précurseur de polyimide, et un polymère acrylique à chaîne latérale photosensible qui présente une cristallinité liquide dans une plage de température prescrite; et un solvant organique.
PCT/JP2017/035348 2016-09-29 2017-09-28 Agent d'alignement de cristaux liquides, film d'alignement de cristaux liquides et élément d'écran à cristaux liquides WO2018062438A1 (fr)

Priority Applications (4)

Application Number Priority Date Filing Date Title
CN201780060270.3A CN109791329B (zh) 2016-09-29 2017-09-28 液晶取向剂、液晶取向膜和液晶表示元件
JP2018542891A JP7089229B2 (ja) 2016-09-29 2017-09-28 液晶配向剤、液晶配向膜、及び液晶表示素子
KR1020197011769A KR102453433B1 (ko) 2016-09-29 2017-09-28 액정 배향제, 액정 배향막, 및 액정 표시 소자
CN202111009465.XA CN113805386B (zh) 2016-09-29 2017-09-28 液晶取向剂、液晶取向膜和液晶表示元件

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2016191843 2016-09-29
JP2016-191843 2016-09-29

Publications (1)

Publication Number Publication Date
WO2018062438A1 true WO2018062438A1 (fr) 2018-04-05

Family

ID=61762740

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2017/035348 WO2018062438A1 (fr) 2016-09-29 2017-09-28 Agent d'alignement de cristaux liquides, film d'alignement de cristaux liquides et élément d'écran à cristaux liquides

Country Status (5)

Country Link
JP (1) JP7089229B2 (fr)
KR (1) KR102453433B1 (fr)
CN (1) CN109791329B (fr)
TW (2) TWI817934B (fr)
WO (1) WO2018062438A1 (fr)

Cited By (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN111196929A (zh) * 2018-11-19 2020-05-26 捷恩智株式会社 用以形成液晶取向膜的液晶取向剂、液晶取向膜的形成方法及液晶显示元件的制造方法
WO2020116459A1 (fr) * 2018-12-04 2020-06-11 日産化学株式会社 Agent d'alignement à cristaux liquides, film d'alignement à cristaux liquides et élément d'affichage à cristaux liquides
WO2020158819A1 (fr) * 2019-01-30 2020-08-06 日産化学株式会社 Agent d'alignment de cristaux liquides, film d'alignment de cristaux liquides et élément d'affichage à cristaux liquides
CN111971617A (zh) * 2018-04-09 2020-11-20 日产化学株式会社 液晶取向剂、液晶取向膜和使用其的液晶表示元件
CN113728270A (zh) * 2019-04-24 2021-11-30 日产化学株式会社 液晶取向剂、液晶取向膜以及使用了该液晶取向膜的液晶显示元件

Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2016080985A (ja) * 2014-10-21 2016-05-16 Jnc株式会社 ポリアミック酸またはその誘導体を含む液晶配向剤、液晶配向膜および液晶表示素子
WO2016125870A1 (fr) * 2015-02-06 2016-08-11 日産化学工業株式会社 Agent d'alignement de cristaux liquides, élément d'affichage à cristaux liquides, et procédé de fabrication d'élément d'affichage à cristaux liquides
JP2016170409A (ja) * 2015-03-11 2016-09-23 Jnc株式会社 液晶配向膜を形成するための液晶配向剤、液晶配向膜およびこれを用いた液晶表示素子

Family Cites Families (11)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
TW556029B (en) 2000-10-16 2003-10-01 Nissan Chemical Ind Ltd Aligning agent for liquid crystal for in-plane switching, liquid-crystal alignment film, and liquid-crystal display element
JP4052308B2 (ja) 2002-12-11 2008-02-27 日産化学工業株式会社 液晶配向剤およびそれを用いた液晶表示素子
KR101589322B1 (ko) * 2008-01-25 2016-01-27 닛산 가가쿠 고교 가부시키 가이샤 액정 배향제, 액정 배향막 및 액정 표시 소자
JP5961880B2 (ja) 2012-02-16 2016-08-03 株式会社ジャパンディスプレイ 液晶表示装置
JP6233309B2 (ja) * 2012-08-29 2017-11-22 日産化学工業株式会社 液晶配向剤、液晶配向膜、及び液晶表示素子
JPWO2014092170A1 (ja) * 2012-12-13 2017-01-12 日産化学工業株式会社 液晶配向剤、液晶配向膜及び液晶表示素子
CN105492965B (zh) * 2013-06-25 2019-04-09 日产化学工业株式会社 液晶取向剂、液晶取向膜、液晶表示元件
US10011772B2 (en) 2013-10-23 2018-07-03 Nissan Chemical Industries, Ltd. Liquid crystal aligning agent, liquid crystal alignment film and liquid crystal display device
KR102278975B1 (ko) * 2013-11-28 2021-07-16 닛산 가가쿠 가부시키가이샤 액정 배향제 및 그것을 사용한 액정 표시 소자
KR102421827B1 (ko) 2014-06-25 2022-07-15 닛산 가가쿠 가부시키가이샤 액정 배향제, 액정 배향막 및 액정 표시 소자
KR102227960B1 (ko) * 2014-10-21 2021-03-15 삼성디스플레이 주식회사 광배향제, 광배향막, 액정 표시 장치 및 그 제조 방법

Patent Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2016080985A (ja) * 2014-10-21 2016-05-16 Jnc株式会社 ポリアミック酸またはその誘導体を含む液晶配向剤、液晶配向膜および液晶表示素子
WO2016125870A1 (fr) * 2015-02-06 2016-08-11 日産化学工業株式会社 Agent d'alignement de cristaux liquides, élément d'affichage à cristaux liquides, et procédé de fabrication d'élément d'affichage à cristaux liquides
JP2016170409A (ja) * 2015-03-11 2016-09-23 Jnc株式会社 液晶配向膜を形成するための液晶配向剤、液晶配向膜およびこれを用いた液晶表示素子

Cited By (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN111971617A (zh) * 2018-04-09 2020-11-20 日产化学株式会社 液晶取向剂、液晶取向膜和使用其的液晶表示元件
CN111196929A (zh) * 2018-11-19 2020-05-26 捷恩智株式会社 用以形成液晶取向膜的液晶取向剂、液晶取向膜的形成方法及液晶显示元件的制造方法
WO2020116459A1 (fr) * 2018-12-04 2020-06-11 日産化学株式会社 Agent d'alignement à cristaux liquides, film d'alignement à cristaux liquides et élément d'affichage à cristaux liquides
CN113168053A (zh) * 2018-12-04 2021-07-23 日产化学株式会社 液晶取向剂、液晶取向膜以及液晶显示元件
JPWO2020116459A1 (ja) * 2018-12-04 2021-10-21 日産化学株式会社 液晶配向剤、液晶配向膜及び液晶表示素子
JP7428138B2 (ja) 2018-12-04 2024-02-06 日産化学株式会社 液晶配向剤、液晶配向膜及び液晶表示素子
WO2020158819A1 (fr) * 2019-01-30 2020-08-06 日産化学株式会社 Agent d'alignment de cristaux liquides, film d'alignment de cristaux liquides et élément d'affichage à cristaux liquides
CN113728270A (zh) * 2019-04-24 2021-11-30 日产化学株式会社 液晶取向剂、液晶取向膜以及使用了该液晶取向膜的液晶显示元件

Also Published As

Publication number Publication date
CN109791329A (zh) 2019-05-21
CN113805386A (zh) 2021-12-17
TW201827578A (zh) 2018-08-01
KR102453433B1 (ko) 2022-10-11
TWI817934B (zh) 2023-10-11
TWI813994B (zh) 2023-09-01
CN109791329B (zh) 2022-05-17
JPWO2018062438A1 (ja) 2019-08-08
JP7089229B2 (ja) 2022-06-22
KR20190058569A (ko) 2019-05-29
TW202132549A (zh) 2021-09-01

Similar Documents

Publication Publication Date Title
JP6582988B2 (ja) 液晶配向剤、液晶配向膜、及び液晶配向素子
JP7089231B2 (ja) 液晶配向剤、液晶配向膜、及び液晶表示素子
JP6578948B2 (ja) 熱脱離性基を有するポリイミド前駆体及び／又はポリイミドを含む液晶配向剤
JP7089229B2 (ja) 液晶配向剤、液晶配向膜、及び液晶表示素子
JP2017106941A (ja) アルコキシシリル基を有するウレア化合物及び液晶配向剤
JP7196847B2 (ja) 液晶配向剤、液晶配向膜及び液晶表示素子
JP7131384B2 (ja) 液晶配向剤、液晶配向膜及び液晶表示素子
JP7334723B2 (ja) 液晶配向剤、液晶配向膜及び液晶表示素子
WO2018062437A1 (fr) Agent d'alignement de cristaux liquides, film d'alignement de cristaux liquides et élément d'écran à cristaux liquides
WO2018062439A1 (fr) Agent d'alignement de cristaux liquides, film d'alignement de cristaux liquides et élément d'écran à cristaux liquides
CN113805386B (zh) 液晶取向剂、液晶取向膜和液晶表示元件
JPWO2020171128A1 (ja) 液晶配向剤及びそれを用いた液晶表示素子
CN112969959A (zh) 液晶取向剂、液晶取向膜及液晶表示元件

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 17856387

Country of ref document: EP

Kind code of ref document: A1

ENP Entry into the national phase

Ref document number: 2018542891

Country of ref document: JP

Kind code of ref document: A

NENP Non-entry into the national phase

Ref country code: DE

ENP Entry into the national phase

Ref document number: 20197011769

Country of ref document: KR

Kind code of ref document: A

122 Ep: pct application non-entry in european phase

Ref document number: 17856387

Country of ref document: EP

Kind code of ref document: A1