WO2017175569A1 - Plaque de titane, plaque d'échangeur de chaleur et séparateur de pile à combustible - Google Patents

Plaque de titane, plaque d'échangeur de chaleur et séparateur de pile à combustible Download PDF

Info

Publication number
WO2017175569A1
WO2017175569A1 PCT/JP2017/011020 JP2017011020W WO2017175569A1 WO 2017175569 A1 WO2017175569 A1 WO 2017175569A1 JP 2017011020 W JP2017011020 W JP 2017011020W WO 2017175569 A1 WO2017175569 A1 WO 2017175569A1
Authority
WO
WIPO (PCT)
Prior art keywords
orientation
titanium plate
plate
titanium
mass
Prior art date
Application number
PCT/JP2017/011020
Other languages
English (en)
Japanese (ja)
Inventor
良規 伊藤
浩司 山下
賢 野原
Original Assignee
株式会社神戸製鋼所
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 株式会社神戸製鋼所 filed Critical 株式会社神戸製鋼所
Publication of WO2017175569A1 publication Critical patent/WO2017175569A1/fr

Abstract

La présente invention concerne une plaque de titane et elle est caractérisée en ce que cette plaque de titane : contient de 0,020 à 1,000 % en masse de Fe et de 0,020 à 0,200 % en masse d'O ; contient une structure de grains cristallins de phase alpha qui est une structure HCP ; satisfait à la relation ([Fe] - 0,020)/[O] ≥ 0,68 ; satisfait à la relation 1,5 ≤ (A3 + A4 + A5)/(A1 + A2) ≤ 30 où A1, A2, A3, A4 et A5 sont, respectivement, les rapports de surface pour les grains cristallins centrés sur des orientations respectives — une orientation 1 où φ1 = 0°, Φ = 35°, φ2 = 0°, une orientation 2 où φ1 = 0°, Φ = 35°, φ2 = 30°, une orientation 3 où φ1 = 90°, Φ = 35°, φ2 = 30°, une orientation 4 où φ1 = 65°, Φ = 30°, φ2 = 0°, et une orientation 5 où φ1 = 90°, Φ = 90°, φ2 = 0° — dans la représentation des orientations cristallines des grains cristallins de phase alpha par une fonction de distribution d'orientation cristalline ; et présente une valeur moyenne de 5 à 80 µm et une valeur maximale n'excédant pas 300 µm pour le diamètre de cercle équivalent des grains cristallins de phase alpha.
PCT/JP2017/011020 2016-04-05 2017-03-17 Plaque de titane, plaque d'échangeur de chaleur et séparateur de pile à combustible WO2017175569A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2016076121 2016-04-05
JP2016-076121 2016-04-05

Publications (1)

Publication Number Publication Date
WO2017175569A1 true WO2017175569A1 (fr) 2017-10-12

Family

ID=60001018

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2017/011020 WO2017175569A1 (fr) 2016-04-05 2017-03-17 Plaque de titane, plaque d'échangeur de chaleur et séparateur de pile à combustible

Country Status (2)

Country Link
JP (1) JP2017186672A (fr)
WO (1) WO2017175569A1 (fr)

Cited By (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2022157842A1 (fr) * 2021-01-20 2022-07-28 日本製鉄株式会社 Plaque de titane
WO2023084746A1 (fr) * 2021-11-12 2023-05-19 日本製鉄株式会社 Plaque de titane
WO2024048002A1 (fr) * 2022-08-30 2024-03-07 日本製鉄株式会社 Tôle d'alliage de titane et lunettes
JP7495645B2 (ja) 2021-01-20 2024-06-05 日本製鉄株式会社 チタン板

Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2002285267A (ja) * 2001-03-23 2002-10-03 Nippon Steel Corp 表層部組織に優れた銅箔製造ドラム用チタンおよびその製造方法
WO2015046084A1 (fr) * 2013-09-24 2015-04-02 株式会社神戸製鋼所 Plaque de titane
JP2016108652A (ja) * 2014-11-28 2016-06-20 株式会社神戸製鋼所 チタン板、熱交換器用プレートおよび燃料電池用セパレータ
WO2016152935A1 (fr) * 2015-03-23 2016-09-29 株式会社神戸製鋼所 Plaque de titane, plaque pour échangeur de chaleur et séparateur pour pile à combustible

Patent Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2002285267A (ja) * 2001-03-23 2002-10-03 Nippon Steel Corp 表層部組織に優れた銅箔製造ドラム用チタンおよびその製造方法
WO2015046084A1 (fr) * 2013-09-24 2015-04-02 株式会社神戸製鋼所 Plaque de titane
JP2016108652A (ja) * 2014-11-28 2016-06-20 株式会社神戸製鋼所 チタン板、熱交換器用プレートおよび燃料電池用セパレータ
WO2016152935A1 (fr) * 2015-03-23 2016-09-29 株式会社神戸製鋼所 Plaque de titane, plaque pour échangeur de chaleur et séparateur pour pile à combustible

Cited By (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2022157842A1 (fr) * 2021-01-20 2022-07-28 日本製鉄株式会社 Plaque de titane
JP7495645B2 (ja) 2021-01-20 2024-06-05 日本製鉄株式会社 チタン板
WO2023084746A1 (fr) * 2021-11-12 2023-05-19 日本製鉄株式会社 Plaque de titane
WO2024048002A1 (fr) * 2022-08-30 2024-03-07 日本製鉄株式会社 Tôle d'alliage de titane et lunettes

Also Published As

Publication number Publication date
JP2017186672A (ja) 2017-10-12

Similar Documents

Publication Publication Date Title
WO2016152935A1 (fr) Plaque de titane, plaque pour échangeur de chaleur et séparateur pour pile à combustible
JP5700650B2 (ja) プレス成形性と強度のバランスに優れた純チタン板
TWI732529B (zh) 鈦合金板、鈦合金板之製造方法、製造銅箔的滾筒及製造銅箔的滾筒之製造方法
JP6263040B2 (ja) チタン板
JP5625646B2 (ja) 圧延幅方向の剛性に優れたチタン板及びその製造方法
JP7448776B2 (ja) チタン合金薄板およびチタン合金薄板の製造方法
WO2015046084A1 (fr) Plaque de titane
WO2017175569A1 (fr) Plaque de titane, plaque d'échangeur de chaleur et séparateur de pile à combustible
JP5988899B2 (ja) チタン板およびチタン板の製造方法
JP6577707B2 (ja) チタン板、熱交換器用プレート、燃料電池用セパレータおよびチタン板の製造方法
JP2017190480A (ja) チタン板
JP5531931B2 (ja) 板面集合組織の発達した電解Ｃｕ箔製造ドラム用チタン合金板とその製造方法
JP2016108652A (ja) チタン板、熱交換器用プレートおよび燃料電池用セパレータ
JP6673121B2 (ja) α＋β型チタン合金棒およびその製造方法
JP2016023315A (ja) チタン板およびその製造方法
TWI796118B (zh) 鈦合金板及鈦合金捲材暨鈦合金板之製造方法及鈦合金捲材之製造方法
JP6623950B2 (ja) 耐力と延性のバランスに優れるチタン板とその製造方法
JP2006241584A (ja) 強化α黄銅及びその製造方法
WO2023127073A1 (fr) MATÉRIAU FORMÉ EN ALLIAGE DE TITANE DE TYPE α+β ET SON PROCÉDÉ DE FABRICATION
WO2023145050A1 (fr) Plaque en alliage de titane
JP3951564B2 (ja) 電解析出ドラムの表面部材用熱延チタン板およびその製造方法
WO2020261436A1 (fr) Plaque d'alliage de titane et tête de club de golf
CN116724136A (zh) 钛合金薄板和钛合金薄板的制造方法
JP2023162898A (ja) β型チタン合金
JP2023040457A (ja) チタン合金板およびその製造方法

Legal Events

Date Code Title Description
NENP Non-entry into the national phase

Ref country code: DE

121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 17778948

Country of ref document: EP

Kind code of ref document: A1

122 Ep: pct application non-entry in european phase

Ref document number: 17778948

Country of ref document: EP

Kind code of ref document: A1