WO2017168869A1 - Composition adhésive autocollante pour film optique et film optique - Google Patents

Composition adhésive autocollante pour film optique et film optique Download PDF

Info

Publication number
WO2017168869A1
WO2017168869A1 PCT/JP2016/087304 JP2016087304W WO2017168869A1 WO 2017168869 A1 WO2017168869 A1 WO 2017168869A1 JP 2016087304 W JP2016087304 W JP 2016087304W WO 2017168869 A1 WO2017168869 A1 WO 2017168869A1
Authority
WO
WIPO (PCT)
Prior art keywords
film
layer
optical film
thin film
sensitive adhesive
Prior art date
Application number
PCT/JP2016/087304
Other languages
English (en)
Japanese (ja)
Inventor
善丈 鈴木
良則 鈴木
吉田　勝彦
片山　和孝
竹内　哲也
改森　信吾
雅晃 山内
Original Assignee
住友理工株式会社
住友電気工業株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 住友理工株式会社, 住友電気工業株式会社 filed Critical 住友理工株式会社
Priority to JP2018508390A priority Critical patent/JPWO2017168869A1/ja
Publication of WO2017168869A1 publication Critical patent/WO2017168869A1/fr

Abstract

L'invention concerne une composition adhésive autocollante pour des films optiques et un film optique, qui, même après avoir été placé dans un environnement à température élevée, a une excellente aptitude au refaçonnage et une durabilité satisfaisante. La composition adhésive autocollante pour films optiques comprend (A) un copolymère séquencé acrylique, (B) un agent anti-bloquant et (C) une résine collante. Lorsqu'on laisse le film optique à 80 °C pendant 72 heures, puis qu'on l'applique ensuite à une partie adhérée, et qu'on examine sa force d'adhérence après un mois conformément à JIS-K-6854-2 dans les conditions d'une vitesse de traction de 50 mm/min, on obtient une force d'adhérence de 4,0 N/25 mm ou plus. Le film optique (10) présente, sur une surface d'un film, une couche adhésive autocollante (22) formée à partir de la composition adhésive autocollante pour des films optiques.
PCT/JP2016/087304 2016-03-30 2016-12-14 Composition adhésive autocollante pour film optique et film optique WO2017168869A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
JP2018508390A JPWO2017168869A1 (ja) 2016-03-30 2016-12-14 光学フィルム用粘着剤組成物および光学フィルム

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2016-069265 2016-03-30
JP2016069265 2016-03-30

Publications (1)

Publication Number Publication Date
WO2017168869A1 true WO2017168869A1 (fr) 2017-10-05

Family

ID=59963917

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2016/087304 WO2017168869A1 (fr) 2016-03-30 2016-12-14 Composition adhésive autocollante pour film optique et film optique

Country Status (2)

Country Link
JP (1) JPWO2017168869A1 (fr)
WO (1) WO2017168869A1 (fr)

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2019130682A (ja) * 2018-01-29 2019-08-08 リンテック株式会社 赤外線反射フィルムおよび赤外線反射フィルムの被着体への貼付方法
JPWO2019142809A1 (ja) * 2018-01-22 2021-01-28 三井・ダウポリケミカル株式会社 シール性樹脂組成物、シール材、包装材、包装容器および包装体
US20220380640A1 (en) * 2020-01-21 2022-12-01 Dic Corporation Pressure-sensitive adhesive tape

Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2002338935A (ja) * 2001-05-18 2002-11-27 Daicel Chem Ind Ltd 感熱性粘着剤組成物、感熱性粘着剤積層体及び感熱性粘着剤積層体の製造方法
WO2007029783A1 (fr) * 2005-09-07 2007-03-15 Kuraray Co., Ltd. Composition adhésive acrylique et produit adhésif
JP2009185138A (ja) * 2008-02-05 2009-08-20 Toagosei Co Ltd 接着剤組成物
JP2015520774A (ja) * 2012-04-27 2015-07-23 株式会社クラレ アクリル系粘着剤組成物および粘着製品
JP2015140379A (ja) * 2014-01-28 2015-08-03 住友理工株式会社 フィルム用粘着剤組成物およびこれを用いた粘着フィルムならびに遮熱性粘着フィルム、粘着フィルムの施工方法ならびに遮熱性粘着フィルムの施工方法

Patent Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2002338935A (ja) * 2001-05-18 2002-11-27 Daicel Chem Ind Ltd 感熱性粘着剤組成物、感熱性粘着剤積層体及び感熱性粘着剤積層体の製造方法
WO2007029783A1 (fr) * 2005-09-07 2007-03-15 Kuraray Co., Ltd. Composition adhésive acrylique et produit adhésif
JP2009185138A (ja) * 2008-02-05 2009-08-20 Toagosei Co Ltd 接着剤組成物
JP2015520774A (ja) * 2012-04-27 2015-07-23 株式会社クラレ アクリル系粘着剤組成物および粘着製品
JP2015140379A (ja) * 2014-01-28 2015-08-03 住友理工株式会社 フィルム用粘着剤組成物およびこれを用いた粘着フィルムならびに遮熱性粘着フィルム、粘着フィルムの施工方法ならびに遮熱性粘着フィルムの施工方法

Cited By (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPWO2019142809A1 (ja) * 2018-01-22 2021-01-28 三井・ダウポリケミカル株式会社 シール性樹脂組成物、シール材、包装材、包装容器および包装体
JP7051908B2 (ja) 2018-01-22 2022-04-11 三井・ダウポリケミカル株式会社 シール性樹脂組成物、シール材、包装材、包装容器および包装体
JP2019130682A (ja) * 2018-01-29 2019-08-08 リンテック株式会社 赤外線反射フィルムおよび赤外線反射フィルムの被着体への貼付方法
US20220380640A1 (en) * 2020-01-21 2022-12-01 Dic Corporation Pressure-sensitive adhesive tape

Also Published As

Publication number Publication date
JPWO2017168869A1 (ja) 2019-02-21

Similar Documents

Publication Publication Date Title
WO2016135997A1 (fr) Film adhésif sensible à la pression pour application sur une fenêtre
JP7019659B2 (ja) 偏光フィルムおよびその製造方法
EP2281023B1 (fr) Matière auto-adhésive
US9804305B2 (en) Methods for sealing the edges of multi-layer articles
WO2017168869A1 (fr) Composition adhésive autocollante pour film optique et film optique
JP2015140379A (ja) フィルム用粘着剤組成物およびこれを用いた粘着フィルムならびに遮熱性粘着フィルム、粘着フィルムの施工方法ならびに遮熱性粘着フィルムの施工方法
JP5959746B2 (ja) 光透過性積層体
DE102008047965A1 (de) Haftklebeband für Solar Panels
WO2014049891A1 (fr) Film stratifié transparent
CN110542943A (zh) 带粘合剂层的偏振膜、其制造方法、以及图像显示装置
DE102007045168A1 (de) Transparentes Klebeband
JP6926506B2 (ja) バリアフィルム及びそれを用いた波長変換シート
TW201434662A (zh) 阻氣薄膜
JP6181981B2 (ja) 透明積層フィルム
JP2015140378A (ja) フィルム用粘着剤組成物およびこれを用いた粘着フィルムならびに遮熱性粘着フィルム、粘着フィルムの施工方法ならびに遮熱性粘着フィルムの施工方法
JP2013151103A (ja) 透明積層フィルム
JP2010155923A (ja) 保護用粘着フィルム
JP2012017407A (ja) フッ素樹脂系粘着フィルム
CN109073800B (zh) 阻隔膜及其制造方法、波长转换片及其制造方法、以及光学层叠体及其制造方法
JP2011133721A (ja) 透明積層フィルム
JP6297290B2 (ja) 光透過性積層体
WO2017043288A1 (fr) Film de réflexion optique
JP6800060B2 (ja) 光学積層体
EP3427942A1 (fr) Stratifié transmettant la lumière et procédé pour produire un stratifié transmettant la lumière
WO2023190740A1 (fr) Film de fenêtre de fixation externe

Legal Events

Date Code Title Description
WWE Wipo information: entry into national phase

Ref document number: 2018508390

Country of ref document: JP

NENP Non-entry into the national phase

Ref country code: DE

121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 16897085

Country of ref document: EP

Kind code of ref document: A1

122 Ep: pct application non-entry in european phase

Ref document number: 16897085

Country of ref document: EP

Kind code of ref document: A1