WO2017111428A8 - 연성, 구멍가공성 및 표면처리 특성이 우수한 고강도 냉연강판, 용융아연도금강판 및 이들의 제조방법 - Google Patents

연성, 구멍가공성 및 표면처리 특성이 우수한 고강도 냉연강판, 용융아연도금강판 및 이들의 제조방법 Download PDF

Info

Publication number
WO2017111428A8
WO2017111428A8 PCT/KR2016/014934 KR2016014934W WO2017111428A8 WO 2017111428 A8 WO2017111428 A8 WO 2017111428A8 KR 2016014934 W KR2016014934 W KR 2016014934W WO 2017111428 A8 WO2017111428 A8 WO 2017111428A8
Authority
WO
WIPO (PCT)
Prior art keywords
steel sheet
surface treatment
rolled steel
dip galvanized
hot dip
Prior art date
Application number
PCT/KR2016/014934
Other languages
English (en)
French (fr)
Other versions
WO2017111428A1 (ko
Inventor
곽재현
조항식
신동석
Original Assignee
주식회사 포스코
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from KR1020150185458A external-priority patent/KR101736634B1/ko
Priority claimed from KR1020150185462A external-priority patent/KR101736635B1/ko
Application filed by 주식회사 포스코 filed Critical 주식회사 포스코
Priority to US15/781,619 priority Critical patent/US11091818B2/en
Priority to JP2018532467A priority patent/JP6694511B2/ja
Priority to CN201680075989.XA priority patent/CN108431268B/zh
Priority to EP16879295.0A priority patent/EP3395977B1/en
Publication of WO2017111428A1 publication Critical patent/WO2017111428A1/ko
Publication of WO2017111428A8 publication Critical patent/WO2017111428A8/ko

Abstract

연성, 구멍가공성 및 표면처리 특성이 우수한 고강도 냉연강판, 용융아연도금강판 및 이들의 제조방법이 제공된다. 본 발명의 냉연강판은, 중량%로, 탄소(C):0.05~0.3%, 실리콘(Si):0.6~2.5%, 알루미늄(Al): 0.01~0.5%, 망간(Mn):1.5~3.0%, 잔부 Fe 및 불가피한 불순물을 포함하고, 강 미세조직이, 면적분율로, 페라이트 60%이하, 침상 베이나이트 25%이상, 마르텐사이트 5%이상 및 침상 잔류 오스테나이트 5%이상을 함유하며, 상기 페라이트는 평균 직경 2 ㎛ 이하이고, 상기 페라이트는, [관계식 1]에 의해 정의되는 Fn2가 89%이상, 그리고 [관계식 2]에 의해 정의되는 Fa5가 70%이하를 만족한다.
PCT/KR2016/014934 2015-12-23 2016-12-20 연성, 구멍가공성 및 표면처리 특성이 우수한 고강도 냉연강판, 용융아연도금강판 및 이들의 제조방법 WO2017111428A1 (ko)

Priority Applications (4)

Application Number Priority Date Filing Date Title
US15/781,619 US11091818B2 (en) 2015-12-23 2016-12-20 High strength cold-rolled steel sheet and hot-dip galvanized steel sheet having excellent hole expansion, ductility and surface treatment properties, and method for manufacturing same
JP2018532467A JP6694511B2 (ja) 2015-12-23 2016-12-20 延性、穴加工性、及び表面処理特性に優れた高強度冷延鋼板、溶融亜鉛めっき鋼板、並びにそれらの製造方法
CN201680075989.XA CN108431268B (zh) 2015-12-23 2016-12-20 延展性、孔加工性和表面处理特性优异的高强度冷轧钢板、热浸镀锌钢板及其制造方法
EP16879295.0A EP3395977B1 (en) 2015-12-23 2016-12-20 High strength cold-rolled steel sheet and hot dip galvanized steel sheet having excellent hole expansion, ductility and surface treatment properties, and method for manufacturing same

Applications Claiming Priority (4)

Application Number Priority Date Filing Date Title
KR1020150185458A KR101736634B1 (ko) 2015-12-23 2015-12-23 연성과 구멍가공성이 우수한 고강도 냉연강판, 용융아연도금강판 및 이들의 제조방법
KR10-2015-0185462 2015-12-23
KR10-2015-0185458 2015-12-23
KR1020150185462A KR101736635B1 (ko) 2015-12-23 2015-12-23 표면처리 특성 및 용접성이 우수한 고강도 냉연강판, 용융아연도금강판 및 이들의 제조방법

Publications (2)

Publication Number Publication Date
WO2017111428A1 WO2017111428A1 (ko) 2017-06-29
WO2017111428A8 true WO2017111428A8 (ko) 2017-12-21

Family

ID=59089566

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/KR2016/014934 WO2017111428A1 (ko) 2015-12-23 2016-12-20 연성, 구멍가공성 및 표면처리 특성이 우수한 고강도 냉연강판, 용융아연도금강판 및 이들의 제조방법

Country Status (5)

Country Link
US (1) US11091818B2 (ko)
EP (1) EP3395977B1 (ko)
JP (1) JP6694511B2 (ko)
CN (1) CN108431268B (ko)
WO (1) WO2017111428A1 (ko)

Families Citing this family (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
KR102153200B1 (ko) * 2018-12-19 2020-09-08 주식회사 포스코 굽힘 가공성이 우수한 고강도 냉연강판 및 그 제조방법
KR102326687B1 (ko) * 2019-12-17 2021-11-17 주식회사 포스코 인산염 처리성이 우수한 고강도 냉연강판 및 그 제조방법
CN114807737B (zh) * 2021-01-21 2023-06-13 宝山钢铁股份有限公司 一种热镀锌钢及其制造方法

Family Cites Families (22)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE4406052A1 (de) * 1993-11-30 1995-06-01 Nippon Kokan Kk Rostfreies Stahlblech und Verfahren zu dessen Herstellung
US6030714A (en) 1995-07-13 2000-02-29 Kawasaki Steel Corporation Zinc and zinc-alloy hot-dip-coated steel sheet having decreased bare spots and excellent coating adhesion and a method for manufacturing the same
KR100325755B1 (ko) 1997-01-13 2002-07-18 에모토 간지 도금이안된결함이적고코팅밀착성이우수한아연및아연-합금용융도금강판및이의제조방법
KR100360095B1 (ko) * 1998-08-28 2003-10-22 주식회사 포스코 성형성이 우수한 고밀착 법랑강판의 제조방법
JP3716718B2 (ja) * 2000-07-31 2005-11-16 住友金属工業株式会社 合金化溶融亜鉛めっき鋼板とその製造方法
WO2003078668A1 (fr) 2002-03-18 2003-09-25 Jfe Steel Corporation Procede pour fabriquer une feuille d'acier galvanisee a chaud de haute resistance, presentant une excellente ductilite et une grande resistance a la fatigue
JP4528191B2 (ja) 2005-04-15 2010-08-18 新日本製鐵株式会社 スポット溶接性、塗装性、加工性に優れた溶融亜鉛メッキ鋼板およびその製造方法
JP2007138216A (ja) 2005-11-16 2007-06-07 Jfe Steel Kk 化成処理性および耐型かじり性に優れた冷延鋼板およびその製造方法
JP5058769B2 (ja) * 2007-01-09 2012-10-24 新日本製鐵株式会社 化成処理性に優れた高強度冷延鋼板の製造方法および製造設備
JP5493986B2 (ja) 2009-04-27 2014-05-14 Ｊｆｅスチール株式会社 加工性に優れた高強度鋼板および高強度溶融亜鉛めっき鋼板並びにそれらの製造方法
JP4737319B2 (ja) 2009-06-17 2011-07-27 Ｊｆｅスチール株式会社 加工性および耐疲労特性に優れた高強度合金化溶融亜鉛めっき鋼板およびその製造方法
CA2805834C (en) 2010-08-12 2016-06-07 Jfe Steel Corporation High-strength cold rolled sheet having excellent formability and crashworthiness and method for manufacturing the same
KR20130027794A (ko) * 2011-09-08 2013-03-18 현대하이스코 주식회사 저항복비형 초고강도 냉연강판, 용융도금강판 및 그 제조 방법
KR101353787B1 (ko) * 2011-12-26 2014-01-22 주식회사 포스코 용접성 및 굽힘가공성이 우수한 초고강도 냉연강판 및 그 제조방법
KR20130076589A (ko) 2011-12-28 2013-07-08 주식회사 포스코 도금표면 품질 및 도금밀착성이 우수한 고강도 용융아연도금강판 및 그 제조방법
JP5880235B2 (ja) 2012-04-10 2016-03-08 新日鐵住金株式会社 鋼板の製造方法
JP5949253B2 (ja) 2012-07-18 2016-07-06 新日鐵住金株式会社 溶融亜鉛めっき鋼板とその製造方法
WO2015015239A1 (en) 2013-08-02 2015-02-05 ArcelorMittal Investigación y Desarrollo, S.L. Cold rolled, coated and post tempered steel sheet and method of manufacturing thereof
JP5821912B2 (ja) * 2013-08-09 2015-11-24 Ｊｆｅスチール株式会社 高強度冷延鋼板およびその製造方法
JP6079726B2 (ja) * 2013-09-04 2017-02-15 Ｊｆｅスチール株式会社 高強度鋼板の製造方法
CN104726770B (zh) * 2013-12-20 2017-04-12 Posco公司 扩孔性优异的析出强化型钢板及其制造方法
KR101594670B1 (ko) 2014-05-13 2016-02-17 주식회사 포스코 연성이 우수한 고강도 냉연강판, 용융아연도금강판 및 이들의 제조방법

Also Published As

Publication number Publication date
EP3395977A1 (en) 2018-10-31
CN108431268B (zh) 2020-12-18
JP2019504203A (ja) 2019-02-14
WO2017111428A1 (ko) 2017-06-29
EP3395977A4 (en) 2018-10-31
JP6694511B2 (ja) 2020-05-13
CN108431268A (zh) 2018-08-21
US20180371569A1 (en) 2018-12-27
EP3395977B1 (en) 2021-02-03
US11091818B2 (en) 2021-08-17

Similar Documents

Publication Publication Date Title
MX2018008561A (es) Lamina de acero de alta resistencia que tiene excelente conformabilidad y un metodo de fabricacion de la misma.
WO2016098964A8 (ko) 재질 불균일이 작고 성형성이 우수한 고강도 냉연강판, 용융아연도금강판, 및 그 제조 방법
MX2019007165A (es) Lamina de acero templada y recubierta que tiene excelente conformabilidad y metodo para fabricar la misma.
MX2019007169A (es) Hoja de acero revestida y templada con excelente capacidad de formacion y un metodo para fabricar la misma.
MX2018009643A (es) Lamina de acero de alta resistencia y metodo para la produccion de la misma.
MX2018001082A (es) Lamina de acero laminada en caliente de alta resistencia y metodo para la fabricacion de la misma.
WO2015162939A8 (ja) 厚鋼板及びその製造方法
MX2018007347A (es) Amina de acero galvanizada por inmersion en caliente de alta resistencia que tiene excelente calidad de superficie y soldabilidad por puntos, y metodo de manufactura para la misma.
MX2016009745A (es) Lamina de acero laminada en frio de alta resistencia y metodo para la fabricacion de la misma.
MX2017012438A (es) Lamina de acero laminada en frio de alta resistencia que tiene excelentes caracteristicas de capacidad de trabajo y colision y que tiene resistencia a la tension de 980 mpa o mas, y un metodo para producir el mismo.
UA117134C2 (uk) Холоднокатаний сталевий лист, спосіб його виробництва і автотранспортний засіб
MX2017012442A (es) Lamina de acero laminada en frio de alta resistencia que tiene excelentes caracteristicas de capacidad trabajo y colision y que tiene una resistencia a la tension de 980 mpa o mas, y metodo para producir el mismo.
MX2018011688A (es) Lamina de acero y lamina de acero enchapada, metodo para producir lamina de acero laminada en caliente, metodo para producir lamina de acero de dureza completa laminada en frio, metodo para producir lamina termicamente tratada, metodo para producir lamina de acero, y metodo para producir lamina de acero enchapada.
MX2020006507A (es) Hoja de acero que tiene excelente tenacidad, ductilidad y resistencia, y metodo de fabricacion de la misma.
IN2014DN11262A (ko)
MX2019008167A (es) Lamina de acero y proceso para producir la misma.
UA113404C2 (xx) Гарячекатаний сталевий лист та спосіб його виготовлення
MY183438A (en) High-strength cold-rolled steel sheet and method for manufacturing the same
MX356054B (es) Lámina de acero laminada en frío, de alta resistencia y método para la fabricación de la misma.
MX2016007664A (es) Acero de elevada resistencia y procedimiento de fabricacion.
MX2018007641A (es) Metodo para producir una lamina de acero de alta resistencia que tiene resistencia y formabilidad mejoradas, y la lamina de acero de alta resistencia obtenida.
MX366776B (es) Lamina de acero, laminada en caliente, recocida y galvanizada por inmersion en caliente, y proceso para producir la misma.
MX2017008295A (es) Laminas de acero galvanizado de alta resistencia y metodos para fabricar las mismas.
IN2014DN09576A (ko)
WO2016001895A3 (en) Method for producing a high strength coated steel sheet having improved strength, ductility and formability

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 16879295

Country of ref document: EP

Kind code of ref document: A1

ENP Entry into the national phase

Ref document number: 2018532467

Country of ref document: JP

Kind code of ref document: A

NENP Non-entry into the national phase

Ref country code: DE

WWE Wipo information: entry into national phase

Ref document number: 2016879295

Country of ref document: EP

ENP Entry into the national phase

Ref document number: 2016879295

Country of ref document: EP

Effective date: 20180723