WO2017105026A8 - 화성처리성 및 구멍확장성이 우수한 초고강도 강판 및 이의 제조방법 - Google Patents
화성처리성 및 구멍확장성이 우수한 초고강도 강판 및 이의 제조방법 Download PDFInfo
- Publication number
- WO2017105026A8 WO2017105026A8 PCT/KR2016/014289 KR2016014289W WO2017105026A8 WO 2017105026 A8 WO2017105026 A8 WO 2017105026A8 KR 2016014289 W KR2016014289 W KR 2016014289W WO 2017105026 A8 WO2017105026 A8 WO 2017105026A8
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- ultra
- high strength
- steel sheet
- strength steel
- hole expansibility
- Prior art date
Abstract
본 발명은 자동차용 강판 등으로 사용되는 초고강도 강판에 관한 것으로서, 강판은 중량%로, 탄소(C): 0.08~0.2%, 실리콘(Si): 0.05~1.3%, 망간(Mn): 2.0~3.0%, 인(P): 0.001~0.10%, 황(S): 0.010% 이하, 알루미늄(Al): 0.01~0.1%, 크롬(Cr): 0.3~1.2%, 보론(B): 0.0010~0.0030%, 티타늄(Ti): 0.01~0.05%, 질소(N): 0.001~0.01%,잔부 Fe 및 기타 불가피한 불순물을 포함하고, 상기 Ti 및 N은 [관계식 1] 3.4≤Ti/N≤10 을 만족하고, 상기 Mn, Si 및 Cr은 [관계식 2] 1.0≤Mn/(Si+Cr)를 만족하며, 표층(표면으로부터 두께방향 0.1㎛까지) 내 Mn, Si 및 Cr의 함량이 [관계식 3] 0.7≤Mn/(Si+Cr)≤Mn/(Si+Cr)을 만족하는 화성처리성 및 구멍확장성이 뛰어난 초고강도 강판을 제공한다.
Priority Applications (3)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
CN201680073487.3A CN108463570B (zh) | 2015-12-15 | 2016-12-07 | 化学转化处理性及扩孔性优异的超高强度钢板及其制造方法 |
US15/781,911 US20180355453A1 (en) | 2015-12-15 | 2016-12-07 | Ultra-high strength steel sheet having excellent phosphatability and hole expandability and method for manufacturing same |
JP2018530888A JP6689384B2 (ja) | 2015-12-15 | 2016-12-07 | 化成処理性及び穴拡げ性に優れた超高強度鋼板及びその製造方法 |
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
KR10-2015-0179002 | 2015-12-15 | ||
KR1020150179002A KR101736620B1 (ko) | 2015-12-15 | 2015-12-15 | 화성처리성 및 구멍확장성이 우수한 초고강도 강판 및 이의 제조방법 |
Publications (2)
Publication Number | Publication Date |
---|---|
WO2017105026A1 WO2017105026A1 (ko) | 2017-06-22 |
WO2017105026A8 true WO2017105026A8 (ko) | 2017-10-19 |
Family
ID=59048559
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/KR2016/014289 WO2017105026A1 (ko) | 2015-12-15 | 2016-12-07 | 화성처리성 및 구멍확장성이 우수한 초고강도 강판 및 이의 제조방법 |
Country Status (5)
Country | Link |
---|---|
US (1) | US20180355453A1 (ko) |
JP (1) | JP6689384B2 (ko) |
KR (1) | KR101736620B1 (ko) |
CN (1) | CN108463570B (ko) |
WO (1) | WO2017105026A1 (ko) |
Families Citing this family (10)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
KR101736619B1 (ko) | 2015-12-15 | 2017-05-17 | 주식회사 포스코 | 화성처리성 및 굽힘가공성이 우수한 초고강도 강판 및 이의 제조방법 |
BR112022010401A2 (pt) * | 2019-12-13 | 2022-08-23 | Arcelormittal | Chapa de aço, método de produção de chapa de aço, uso de uma chapa de aço e veículo |
JP7264090B2 (ja) * | 2020-03-06 | 2023-04-25 | Jfeスチール株式会社 | プレス用鋼板の製造方法、プレス部品の製造方法、及び伸びフランジ成形性の評価方法 |
CN111676421B (zh) * | 2020-05-20 | 2021-09-28 | 樟树市兴隆高新材料有限公司 | 一种马氏体气阀钢轧制坯的轧制方法 |
KR20230016218A (ko) * | 2020-07-20 | 2023-02-01 | 아르셀러미탈 | 열처리 냉연 강판 및 그 제조 방법 |
KR102440772B1 (ko) * | 2020-09-22 | 2022-09-08 | 주식회사 포스코 | 성형성이 우수한 고강도강판 및 그 제조방법 |
KR102494555B1 (ko) * | 2020-12-21 | 2023-02-07 | 주식회사 포스코 | 열적 안정성이 우수한 고항복비 초고강도 강판 및 그 제조방법 |
KR102487306B1 (ko) * | 2020-12-21 | 2023-01-13 | 현대제철 주식회사 | 점용접성 및 성형성이 우수한 초고장력 냉연강판, 초고장력 도금강판 및 그 제조방법 |
JP7332062B1 (ja) | 2021-09-30 | 2023-08-23 | Jfeスチール株式会社 | 鋼板、部材およびそれらの製造方法 |
WO2023053908A1 (ja) * | 2021-09-30 | 2023-04-06 | Jfeスチール株式会社 | 鋼板、部材およびそれらの製造方法 |
Family Cites Families (17)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JP4315844B2 (ja) | 2004-03-05 | 2009-08-19 | 株式会社神戸製鋼所 | 塗膜密着性に優れた高強度冷延鋼板 |
JP4772497B2 (ja) * | 2005-12-27 | 2011-09-14 | 新日本製鐵株式会社 | 穴拡げ性に優れた高強度冷延薄鋼板及びその製造方法 |
PL2031081T3 (pl) * | 2007-08-15 | 2011-11-30 | Thyssenkrupp Steel Europe Ag | Stal dwufazowa, produkt płaski z takiej stali dwufazowej i sposób wytwarzania produktu płaskiego |
MY154273A (en) * | 2009-03-31 | 2015-05-29 | Nissha Printing | A film for sliced veneer insert, a method of manufacturing same, and a method of manufacturing a sliced veneer insert molded article |
JP5779847B2 (ja) * | 2009-07-29 | 2015-09-16 | Jfeスチール株式会社 | 化成処理性に優れた高強度冷延鋼板の製造方法 |
WO2011065591A1 (ja) * | 2009-11-30 | 2011-06-03 | 新日本製鐵株式会社 | 耐水素脆化特性に優れた引張最大強度900MPa以上の高強度鋼板及びその製造方法 |
JP5636727B2 (ja) * | 2010-04-27 | 2014-12-10 | 新日鐵住金株式会社 | 溶融亜鉛めっき鋼板およびその製造方法 |
KR101220619B1 (ko) * | 2010-11-09 | 2013-01-10 | 주식회사 포스코 | 초고강도 냉연강판, 용융아연도금강판 및 이들의 제조방법 |
MX2014008430A (es) * | 2012-01-13 | 2014-10-06 | Nippon Steel & Sumitomo Metal Corp | Articulo moldeado estampado en caliente y metodo para la produccion de articulo moldeado estampado en caliente. |
CN104040010B (zh) * | 2012-01-13 | 2016-06-15 | 新日铁住金株式会社 | 冷轧钢板及冷轧钢板的制造方法 |
DE102012002079B4 (de) * | 2012-01-30 | 2015-05-13 | Salzgitter Flachstahl Gmbh | Verfahren zur Herstellung eines kalt- oder warmgewalzten Stahlbandes aus einem höchstfesten Mehrphasenstahl |
CN104271787A (zh) * | 2012-09-27 | 2015-01-07 | 日立金属株式会社 | 析出强化型马氏体钢及其制造方法 |
JP5862651B2 (ja) * | 2013-12-18 | 2016-02-16 | Jfeスチール株式会社 | 耐衝撃性および曲げ加工性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法 |
CN105814227B (zh) * | 2013-12-18 | 2018-02-27 | 杰富意钢铁株式会社 | 高强度热浸镀锌钢板及其制造方法 |
JP6102902B2 (ja) * | 2014-03-05 | 2017-03-29 | Jfeスチール株式会社 | 冷延鋼板、その製造方法、高強度溶融亜鉛めっき鋼板及び高強度合金化溶融亜鉛めっき鋼板 |
WO2016001706A1 (en) * | 2014-07-03 | 2016-01-07 | Arcelormittal | Method for producing a high strength steel sheet having improved strength and formability and obtained sheet |
KR101736619B1 (ko) * | 2015-12-15 | 2017-05-17 | 주식회사 포스코 | 화성처리성 및 굽힘가공성이 우수한 초고강도 강판 및 이의 제조방법 |
-
2015
- 2015-12-15 KR KR1020150179002A patent/KR101736620B1/ko active IP Right Grant
-
2016
- 2016-12-07 CN CN201680073487.3A patent/CN108463570B/zh active Active
- 2016-12-07 WO PCT/KR2016/014289 patent/WO2017105026A1/ko active Application Filing
- 2016-12-07 US US15/781,911 patent/US20180355453A1/en not_active Abandoned
- 2016-12-07 JP JP2018530888A patent/JP6689384B2/ja active Active
Also Published As
Publication number | Publication date |
---|---|
JP2019502819A (ja) | 2019-01-31 |
CN108463570A (zh) | 2018-08-28 |
KR101736620B1 (ko) | 2017-05-17 |
WO2017105026A1 (ko) | 2017-06-22 |
CN108463570B (zh) | 2020-09-18 |
JP6689384B2 (ja) | 2020-04-28 |
US20180355453A1 (en) | 2018-12-13 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
WO2017105026A8 (ko) | 화성처리성 및 구멍확장성이 우수한 초고강도 강판 및 이의 제조방법 | |
WO2017105025A8 (ko) | 화성처리성 및 굽힘가공성이 우수한 초고강도 강판 및 이의 제조방법 | |
WO2016105089A8 (ko) | 열처리 강재, 내구특성이 우수한 초고강도 성형품 및 그 제조방법 | |
MX2018007347A (es) | Amina de acero galvanizada por inmersion en caliente de alta resistencia que tiene excelente calidad de superficie y soldabilidad por puntos, y metodo de manufactura para la misma. | |
IN2014DN10254A (ko) | ||
MX2018008561A (es) | Lamina de acero de alta resistencia que tiene excelente conformabilidad y un metodo de fabricacion de la misma. | |
MX2019007165A (es) | Lamina de acero templada y recubierta que tiene excelente conformabilidad y metodo para fabricar la misma. | |
UA107519C2 (uk) | Гаряче- або холоднокатаний сталевий лист, спосіб його виготовлення та його застосування в автомобільній промисловості | |
WO2015039763A3 (en) | Steel for hot forming | |
UA124354C2 (uk) | Відпущена листова сталь з покриттям, яка характеризується чудовою деформованістю, і спосіб її виготовлення | |
MX2016009745A (es) | Lamina de acero laminada en frio de alta resistencia y metodo para la fabricacion de la misma. | |
MX370910B (es) | Tubos de acero sin costura revenidos y templados de pared media de alta resistencia y metodo relacionado para la fabricacion de dichos tubos de acero. | |
BR112017007999A2 (pt) | ?processo para fabricar chapas de aço para endurecimento por prensagem e peças obtidas por esse processo? | |
MX363739B (es) | Hoja de acero laminada en frio de alta resistencia y metodo para fabricar la misma. | |
MX2016001013A (es) | Hoja de acero que tiene propiedades mecanicas de resistencia y ductibilidad muy altas, metodo de fabricacion y uso de tales hojas. | |
MX2019004458A (es) | Sustrato de acero para partes pintadas. | |
WO2016105115A8 (ko) | 표면품질, 도금밀착성 및 성형성이 우수한 고강도 용융아연도금강판 및 그 제조방법 | |
MX2016014990A (es) | Hoja de acero doblemente recocida que tiene resistencia mecanica alta y caracteristicas de ductilidad, metodo de fabricacion y uso de tales hojas. | |
MX2019006232A (es) | Acero para nitrocarburacion, y componente. | |
IN2014DN09528A (ko) | ||
WO2017027085A3 (en) | Low alloy high performance steel | |
MX2018011694A (es) | Lamina de acero y lamina de acero enchapada, metodo para producir una lamina de acero laminada en caliente, metodo para producir una lamina de acero de dureza completa laminada en frio, metodo para producir una lamina de acero, y metodo para producir una lamina de acero enchapada. | |
MY153967A (en) | High-strength hot rolled steel sheet having good formability and method for manufacturing the same | |
WO2017111322A8 (ko) | 연성이 우수한 초고강도 열연강판 및 그 제조방법 | |
MY163017A (en) | High strength cold rolled steel sheet having excellent formability, and method for manufacturing the same |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
121 | Ep: the epo has been informed by wipo that ep was designated in this application |
Ref document number: 16875968 Country of ref document: EP Kind code of ref document: A1 |
|
ENP | Entry into the national phase |
Ref document number: 2018530888 Country of ref document: JP Kind code of ref document: A |
|
NENP | Non-entry into the national phase |
Ref country code: DE |
|
122 | Ep: pct application non-entry in european phase |
Ref document number: 16875968 Country of ref document: EP Kind code of ref document: A1 |