CN108463570B - 化学转化处理性及扩孔性优异的超高强度钢板及其制造方法 - Google Patents
化学转化处理性及扩孔性优异的超高强度钢板及其制造方法 Download PDFInfo
- Publication number
- CN108463570B CN108463570B CN201680073487.3A CN201680073487A CN108463570B CN 108463570 B CN108463570 B CN 108463570B CN 201680073487 A CN201680073487 A CN 201680073487A CN 108463570 B CN108463570 B CN 108463570B
- Authority
- CN
- China
- Prior art keywords
- relational expression
- steel sheet
- hole expansibility
- chemical conversion
- ultra
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Links
Classifications
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D9/00—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor
- C21D9/46—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for sheet metals
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D1/00—General methods or devices for heat treatment, e.g. annealing, hardening, quenching or tempering
- C21D1/18—Hardening; Quenching with or without subsequent tempering
- C21D1/19—Hardening; Quenching with or without subsequent tempering by interrupted quenching
- C21D1/20—Isothermal quenching, e.g. bainitic hardening
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D6/00—Heat treatment of ferrous alloys
- C21D6/002—Heat treatment of ferrous alloys containing Cr
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D6/00—Heat treatment of ferrous alloys
- C21D6/005—Heat treatment of ferrous alloys containing Mn
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D6/00—Heat treatment of ferrous alloys
- C21D6/008—Heat treatment of ferrous alloys containing Si
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
- C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
- C21D8/0205—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips of ferrous alloys
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
- C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
- C21D8/0247—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the heat treatment
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/001—Ferrous alloys, e.g. steel alloys containing N
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/002—Ferrous alloys, e.g. steel alloys containing In, Mg, or other elements not provided for in one single group C22C38/001 - C22C38/60
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/02—Ferrous alloys, e.g. steel alloys containing silicon
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/06—Ferrous alloys, e.g. steel alloys containing aluminium
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
- C22C38/22—Ferrous alloys, e.g. steel alloys containing chromium with molybdenum or tungsten
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
- C22C38/24—Ferrous alloys, e.g. steel alloys containing chromium with vanadium
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
- C22C38/26—Ferrous alloys, e.g. steel alloys containing chromium with niobium or tantalum
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
- C22C38/28—Ferrous alloys, e.g. steel alloys containing chromium with titanium or zirconium
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
- C22C38/32—Ferrous alloys, e.g. steel alloys containing chromium with boron
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
- C22C38/38—Ferrous alloys, e.g. steel alloys containing chromium with more than 1.5% by weight of manganese
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
- C23C2/04—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor characterised by the coating material
- C23C2/06—Zinc or cadmium or alloys based thereon
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
- C23C2/26—After-treatment
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
- C23C2/26—After-treatment
- C23C2/261—After-treatment in a gas atmosphere, e.g. inert or reducing atmosphere
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
- C23C2/26—After-treatment
- C23C2/28—Thermal after-treatment, e.g. treatment in oil bath
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
- C23C2/26—After-treatment
- C23C2/28—Thermal after-treatment, e.g. treatment in oil bath
- C23C2/29—Cooling or quenching
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
- C23C2/34—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor characterised by the shape of the material to be treated
- C23C2/36—Elongated material
- C23C2/40—Plates; Strips
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23G—CLEANING OR DE-GREASING OF METALLIC MATERIAL BY CHEMICAL METHODS OTHER THAN ELECTROLYSIS
- C23G1/00—Cleaning or pickling metallic material with solutions or molten salts
- C23G1/02—Cleaning or pickling metallic material with solutions or molten salts with acid solutions
- C23G1/08—Iron or steel
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D2211/00—Microstructure comprising significant phases
- C21D2211/001—Austenite
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D2211/00—Microstructure comprising significant phases
- C21D2211/002—Bainite
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D2211/00—Microstructure comprising significant phases
- C21D2211/005—Ferrite
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D2211/00—Microstructure comprising significant phases
- C21D2211/008—Martensite
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
- C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
- C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
- C21D8/0221—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the working steps
- C21D8/0226—Hot rolling
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
- C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
- C21D8/0221—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the working steps
- C21D8/0236—Cold rolling
Landscapes
- Chemical & Material Sciences (AREA)
- Engineering & Computer Science (AREA)
- Materials Engineering (AREA)
- Mechanical Engineering (AREA)
- Metallurgy (AREA)
- Organic Chemistry (AREA)
- Thermal Sciences (AREA)
- Physics & Mathematics (AREA)
- Crystallography & Structural Chemistry (AREA)
- Chemical Kinetics & Catalysis (AREA)
- Oil, Petroleum & Natural Gas (AREA)
- General Chemical & Material Sciences (AREA)
- Heat Treatment Of Sheet Steel (AREA)
Applications Claiming Priority (3)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
KR1020150179002A KR101736620B1 (ko) | 2015-12-15 | 2015-12-15 | 화성처리성 및 구멍확장성이 우수한 초고강도 강판 및 이의 제조방법 |
KR10-2015-0179002 | 2015-12-15 | ||
PCT/KR2016/014289 WO2017105026A1 (ko) | 2015-12-15 | 2016-12-07 | 화성처리성 및 구멍확장성이 우수한 초고강도 강판 및 이의 제조방법 |
Publications (2)
Publication Number | Publication Date |
---|---|
CN108463570A CN108463570A (zh) | 2018-08-28 |
CN108463570B true CN108463570B (zh) | 2020-09-18 |
Family
ID=59048559
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
CN201680073487.3A Active CN108463570B (zh) | 2015-12-15 | 2016-12-07 | 化学转化处理性及扩孔性优异的超高强度钢板及其制造方法 |
Country Status (5)
Country | Link |
---|---|
US (1) | US20180355453A1 (ko) |
JP (1) | JP6689384B2 (ko) |
KR (1) | KR101736620B1 (ko) |
CN (1) | CN108463570B (ko) |
WO (1) | WO2017105026A1 (ko) |
Families Citing this family (10)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
KR101736619B1 (ko) * | 2015-12-15 | 2017-05-17 | 주식회사 포스코 | 화성처리성 및 굽힘가공성이 우수한 초고강도 강판 및 이의 제조방법 |
MX2022007053A (es) * | 2019-12-13 | 2022-07-11 | Arcelormittal | Hoja de acero laminada en frio tratada termicamente y un metodo de fabricacion de la misma. |
JP7264090B2 (ja) * | 2020-03-06 | 2023-04-25 | Jfeスチール株式会社 | プレス用鋼板の製造方法、プレス部品の製造方法、及び伸びフランジ成形性の評価方法 |
CN111676421B (zh) * | 2020-05-20 | 2021-09-28 | 樟树市兴隆高新材料有限公司 | 一种马氏体气阀钢轧制坯的轧制方法 |
KR20230016218A (ko) * | 2020-07-20 | 2023-02-01 | 아르셀러미탈 | 열처리 냉연 강판 및 그 제조 방법 |
KR102440772B1 (ko) * | 2020-09-22 | 2022-09-08 | 주식회사 포스코 | 성형성이 우수한 고강도강판 및 그 제조방법 |
KR102494555B1 (ko) * | 2020-12-21 | 2023-02-07 | 주식회사 포스코 | 열적 안정성이 우수한 고항복비 초고강도 강판 및 그 제조방법 |
KR102487306B1 (ko) * | 2020-12-21 | 2023-01-13 | 현대제철 주식회사 | 점용접성 및 성형성이 우수한 초고장력 냉연강판, 초고장력 도금강판 및 그 제조방법 |
KR20240051975A (ko) * | 2021-09-30 | 2024-04-22 | 제이에프이 스틸 가부시키가이샤 | 강판, 부재 및 그들의 제조 방법 |
EP4372119A1 (en) * | 2021-09-30 | 2024-05-22 | JFE Steel Corporation | Steel sheet, member, and manufacturing methods therefor |
Citations (3)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
CN102639739A (zh) * | 2009-11-30 | 2012-08-15 | 新日本制铁株式会社 | 耐氢脆化特性优异的最大拉伸强度为900MPa以上的高强度钢板及其制造方法 |
CN104040011A (zh) * | 2012-01-13 | 2014-09-10 | 新日铁住金株式会社 | 热冲压成型体以及热冲压成型体的制造方法 |
JP2015180766A (ja) * | 2014-03-05 | 2015-10-15 | Jfeスチール株式会社 | 冷延鋼板、その製造方法、高強度溶融亜鉛めっき鋼板及び高強度合金化溶融亜鉛めっき鋼板 |
Family Cites Families (14)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JP4315844B2 (ja) | 2004-03-05 | 2009-08-19 | 株式会社神戸製鋼所 | 塗膜密着性に優れた高強度冷延鋼板 |
JP4772497B2 (ja) * | 2005-12-27 | 2011-09-14 | 新日本製鐵株式会社 | 穴拡げ性に優れた高強度冷延薄鋼板及びその製造方法 |
PL2031081T3 (pl) * | 2007-08-15 | 2011-11-30 | Thyssenkrupp Steel Europe Ag | Stal dwufazowa, produkt płaski z takiej stali dwufazowej i sposób wytwarzania produktu płaskiego |
CN102369093B (zh) * | 2009-03-31 | 2013-07-03 | 日本写真印刷株式会社 | 突板嵌入用膜及其制造方法、突板嵌入成形品的制造方法 |
JP5779847B2 (ja) * | 2009-07-29 | 2015-09-16 | Jfeスチール株式会社 | 化成処理性に優れた高強度冷延鋼板の製造方法 |
JP5636727B2 (ja) * | 2010-04-27 | 2014-12-10 | 新日鐵住金株式会社 | 溶融亜鉛めっき鋼板およびその製造方法 |
KR101220619B1 (ko) * | 2010-11-09 | 2013-01-10 | 주식회사 포스코 | 초고강도 냉연강판, 용융아연도금강판 및 이들의 제조방법 |
TWI524953B (zh) * | 2012-01-13 | 2016-03-11 | 新日鐵住金股份有限公司 | 冷軋鋼板及冷軋鋼板之製造方法 |
DE102012002079B4 (de) * | 2012-01-30 | 2015-05-13 | Salzgitter Flachstahl Gmbh | Verfahren zur Herstellung eines kalt- oder warmgewalzten Stahlbandes aus einem höchstfesten Mehrphasenstahl |
KR101521071B1 (ko) * | 2012-09-27 | 2015-05-15 | 히타치 긴조쿠 가부시키가이샤 | 석출 강화형 마르텐사이트강 및 그의 제조방법 |
JP5862651B2 (ja) * | 2013-12-18 | 2016-02-16 | Jfeスチール株式会社 | 耐衝撃性および曲げ加工性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法 |
KR101813974B1 (ko) * | 2013-12-18 | 2018-01-02 | 제이에프이 스틸 가부시키가이샤 | 고강도 용융 아연 도금 강판 및 그의 제조 방법 |
WO2016001706A1 (en) * | 2014-07-03 | 2016-01-07 | Arcelormittal | Method for producing a high strength steel sheet having improved strength and formability and obtained sheet |
KR101736619B1 (ko) * | 2015-12-15 | 2017-05-17 | 주식회사 포스코 | 화성처리성 및 굽힘가공성이 우수한 초고강도 강판 및 이의 제조방법 |
-
2015
- 2015-12-15 KR KR1020150179002A patent/KR101736620B1/ko active IP Right Grant
-
2016
- 2016-12-07 US US15/781,911 patent/US20180355453A1/en not_active Abandoned
- 2016-12-07 CN CN201680073487.3A patent/CN108463570B/zh active Active
- 2016-12-07 JP JP2018530888A patent/JP6689384B2/ja active Active
- 2016-12-07 WO PCT/KR2016/014289 patent/WO2017105026A1/ko active Application Filing
Patent Citations (3)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
CN102639739A (zh) * | 2009-11-30 | 2012-08-15 | 新日本制铁株式会社 | 耐氢脆化特性优异的最大拉伸强度为900MPa以上的高强度钢板及其制造方法 |
CN104040011A (zh) * | 2012-01-13 | 2014-09-10 | 新日铁住金株式会社 | 热冲压成型体以及热冲压成型体的制造方法 |
JP2015180766A (ja) * | 2014-03-05 | 2015-10-15 | Jfeスチール株式会社 | 冷延鋼板、その製造方法、高強度溶融亜鉛めっき鋼板及び高強度合金化溶融亜鉛めっき鋼板 |
Also Published As
Publication number | Publication date |
---|---|
JP6689384B2 (ja) | 2020-04-28 |
JP2019502819A (ja) | 2019-01-31 |
WO2017105026A1 (ko) | 2017-06-22 |
CN108463570A (zh) | 2018-08-28 |
US20180355453A1 (en) | 2018-12-13 |
WO2017105026A8 (ko) | 2017-10-19 |
KR101736620B1 (ko) | 2017-05-17 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
CN108463570B (zh) | 化学转化处理性及扩孔性优异的超高强度钢板及其制造方法 | |
CN108368590B (zh) | 化学转化处理性及弯曲加工性优异的超高强度钢板及其制造方法 | |
JP6043801B2 (ja) | 温間プレス成形用鋼板、温間プレス成形部材、及びこれらの製造方法 | |
CN111448332B (zh) | 加工性优异的高强度钢板及其制造方法 | |
JP6700398B2 (ja) | 高降伏比型高強度冷延鋼板及びその製造方法 | |
WO2013100485A1 (ko) | 용접성 및 굽힘가공성이 우수한 초고강도 냉연강판 및 그 제조방법 | |
KR20140047960A (ko) | 용접성 및 굽힘가공성이 우수한 초고강도 냉연강판 및 그 제조방법 | |
KR20230024905A (ko) | 가소성이 우수한 초고강도 강 및 이의 제조 방법 | |
CN116635556A (zh) | 延展性和成型性优异的高强度热浸镀锌钢板及其制造方法 | |
JP2010126808A (ja) | 冷延鋼板およびその製造方法 | |
KR101382908B1 (ko) | 초고강도 박강판 및 그 제조방법 | |
JP6843245B2 (ja) | 曲げ性及び伸びフランジ性に優れた高張力亜鉛系めっき鋼板及びその製造方法 | |
KR101228753B1 (ko) | 형상 품질이 우수한 초고강도 냉연강판 및 그 제조방법 | |
KR102468051B1 (ko) | 연성이 우수한 초고강도 강판 및 그 제조방법 | |
US20240060161A1 (en) | High strength steel sheet having excellent workability, and method for manufacturing same | |
CN115698346A (zh) | 经热处理的冷轧钢板及其制造方法 | |
KR101428375B1 (ko) | 표면품질이 우수한 초고강도 냉연강판, 용융아연도금강판 및 이들의 제조방법 | |
CN113195773A (zh) | 冲缘加工性优异的高强度冷轧钢板和合金化热浸镀锌钢板及其制造方法 | |
KR20130056051A (ko) | 슬라브 코너크랙이 없는 초고강도 강판 및 그 제조방법 | |
KR20130056052A (ko) | 합금화 특성이 우수한 초고강도 합금화 용융아연도금강판 및 그 제조방법 | |
KR101406478B1 (ko) | 고항복비 및 냉연형상이 우수한 초고강도 냉연강판 및 그 제조방법 | |
KR20120063196A (ko) | 표면품질이 우수한 초고강도 냉연강판, 용융아연도금강판 및 이들의 제조방법 | |
CN118202081A (zh) | 耐碰撞性能和成型性优异的高强度钢板及其制造方法 | |
US20240011118A1 (en) | High strength steel sheet having excellent workability and method for manufacturing same | |
KR20230014121A (ko) | 구멍확장성 및 연성이 우수한 고강도 강판 및 이의 제조방법 |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
PB01 | Publication | ||
PB01 | Publication | ||
SE01 | Entry into force of request for substantive examination | ||
SE01 | Entry into force of request for substantive examination | ||
GR01 | Patent grant | ||
GR01 | Patent grant | ||
CP03 | Change of name, title or address |
Address after: Seoul, South Kerean Patentee after: POSCO Holdings Co.,Ltd. Address before: Gyeongbuk, South Korea Patentee before: POSCO |
|
CP03 | Change of name, title or address | ||
TR01 | Transfer of patent right |
Effective date of registration: 20230505 Address after: Gyeongbuk, South Korea Patentee after: POSCO Co.,Ltd. Address before: Seoul, South Kerean Patentee before: POSCO Holdings Co.,Ltd. |
|
TR01 | Transfer of patent right |