WO2017057636A1 - Nanoparticules d'oxyde de zirconium - Google Patents

Nanoparticules d'oxyde de zirconium Download PDF

Info

Publication number
WO2017057636A1
WO2017057636A1 PCT/JP2016/078932 JP2016078932W WO2017057636A1 WO 2017057636 A1 WO2017057636 A1 WO 2017057636A1 JP 2016078932 W JP2016078932 W JP 2016078932W WO 2017057636 A1 WO2017057636 A1 WO 2017057636A1
Authority
WO
WIPO (PCT)
Prior art keywords
zirconium oxide
group
oxide nanoparticles
mass
zirconium
Prior art date
Application number
PCT/JP2016/078932
Other languages
English (en)
Japanese (ja)
Inventor
朋侑 八尾
純也 木村
高橋　邦夫
威夫 赤塚
Original Assignee
株式会社日本触媒
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from JP2016039323A external-priority patent/JP6742761B2/ja
Priority claimed from JP2016039322A external-priority patent/JP6796386B2/ja
Application filed by 株式会社日本触媒 filed Critical 株式会社日本触媒
Priority to US15/764,048 priority Critical patent/US20180265372A1/en
Priority to EP16851807.4A priority patent/EP3357866A4/fr
Publication of WO2017057636A1 publication Critical patent/WO2017057636A1/fr

Abstract

L'objectif de la présente invention est d'obtenir facilement, sans utiliser ou en utilisant une plus petite quantité d'une solution aqueuse de sulfate, telle qu'une solution aqueuse de MgSO4, des particules d'oxyde de zirconium qui comprennent des éléments métalliques tels que des oxydes de terres rares (de préférence stabilisés à l'aide d'un élément métallique) et qui présentent une bonne dispersabilité par rapport à un milieu organique. Ces nanoparticules d'oxyde de zirconium sont revêtues d'un premier acide carboxylique qui possède trois ou plus de trois atomes de carbone et qui est du type acide carboxylique primaire et/ou du type acide carboxylique secondaire. Les nanoparticules d'oxyde de zirconium comprennent au moins un type d'élément métallique M choisi dans le groupe constitué des éléments des terres rares, Al, Fe, Co, Sn, Zn, In, Bi, Mn, Ni, et Cu.
PCT/JP2016/078932 2015-09-30 2016-09-29 Nanoparticules d'oxyde de zirconium WO2017057636A1 (fr)

Priority Applications (2)

Application Number Priority Date Filing Date Title
US15/764,048 US20180265372A1 (en) 2015-09-30 2016-09-29 Zirconium oxide nanoparticles
EP16851807.4A EP3357866A4 (fr) 2015-09-30 2016-09-29 Nanoparticules d'oxyde de zirconium

Applications Claiming Priority (8)

Application Number Priority Date Filing Date Title
JP2015-194172 2015-09-30
JP2015194172 2015-09-30
JP2016039323A JP6742761B2 (ja) 2015-09-30 2016-03-01 酸化ジルコニウムナノ粒子
JP2016-039323 2016-03-01
JP2016-039322 2016-03-01
JP2016039322A JP6796386B2 (ja) 2016-03-01 2016-03-01 酸化ジルコニウムナノ粒子
JP2016108539 2016-05-31
JP2016-108539 2016-05-31

Publications (1)

Publication Number Publication Date
WO2017057636A1 true WO2017057636A1 (fr) 2017-04-06

Family

ID=58427651

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2016/078932 WO2017057636A1 (fr) 2015-09-30 2016-09-29 Nanoparticules d'oxyde de zirconium

Country Status (1)

Country Link
WO (1) WO2017057636A1 (fr)

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2019026811A1 (fr) * 2017-07-31 2019-02-07 クラレノリタケデンタル株式会社 Procédé de fabrication de poudre contenant des particules de zircone
CN111233468A (zh) * 2020-02-12 2020-06-05 长裕控股集团有限公司 结构件用钇稳定锆粉的制备方法

Citations (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2000185916A (ja) * 1998-10-14 2000-07-04 Nippon Shokubai Co Ltd 金属酸化物系粒子、その製造方法および用途
JP2003506309A (ja) * 1999-08-16 2003-02-18 スリーエム エスペ アクチェンゲゼルシャフト 酸化添加物を含んだ酸化ジルコニウムセラミックから成る未加工品及びその使用
WO2008010533A1 (fr) * 2006-07-18 2008-01-24 Nippon Shokubai Co., Ltd. Nanoparticule d'oxyde métallique et son procédé de production
JP2008515747A (ja) * 2004-10-04 2008-05-15 ライプニッツ−インスティトゥート フィア ノイエ マテリアーリエン ゲマインニュッツィゲ ゲゼルシャフト ミット ベシュレンクタ ハフトゥンク カスタムな表面化学を有するナノ粒子及び対応するコロイドの製造方法
JP2010132494A (ja) * 2008-12-04 2010-06-17 Sakai Chem Ind Co Ltd 酸化ジルコニウム分散液とその製造方法とそれを含む樹脂組成物
JP2010150066A (ja) * 2008-12-24 2010-07-08 Sakai Chem Ind Co Ltd 酸化ジルコニウム分散液とその製造方法
JP2011190148A (ja) * 2010-03-15 2011-09-29 Sumitomo Osaka Cement Co Ltd 複合セラミックス粉体及びその製造方法並びに固体酸化物形燃料電池
JP2012250894A (ja) * 2011-06-06 2012-12-20 Nippon Shokubai Co Ltd 有機基で被覆された金属酸化物ナノ粒子の製造方法
JP2016028998A (ja) * 2014-07-18 2016-03-03 東京インキ株式会社 正方晶酸化ジルコニウムナノ粒子、その製造方法、分散体および樹脂複合体

Patent Citations (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2000185916A (ja) * 1998-10-14 2000-07-04 Nippon Shokubai Co Ltd 金属酸化物系粒子、その製造方法および用途
JP2003506309A (ja) * 1999-08-16 2003-02-18 スリーエム エスペ アクチェンゲゼルシャフト 酸化添加物を含んだ酸化ジルコニウムセラミックから成る未加工品及びその使用
JP2008515747A (ja) * 2004-10-04 2008-05-15 ライプニッツ−インスティトゥート フィア ノイエ マテリアーリエン ゲマインニュッツィゲ ゲゼルシャフト ミット ベシュレンクタ ハフトゥンク カスタムな表面化学を有するナノ粒子及び対応するコロイドの製造方法
WO2008010533A1 (fr) * 2006-07-18 2008-01-24 Nippon Shokubai Co., Ltd. Nanoparticule d'oxyde métallique et son procédé de production
JP2010132494A (ja) * 2008-12-04 2010-06-17 Sakai Chem Ind Co Ltd 酸化ジルコニウム分散液とその製造方法とそれを含む樹脂組成物
JP2010150066A (ja) * 2008-12-24 2010-07-08 Sakai Chem Ind Co Ltd 酸化ジルコニウム分散液とその製造方法
JP2011190148A (ja) * 2010-03-15 2011-09-29 Sumitomo Osaka Cement Co Ltd 複合セラミックス粉体及びその製造方法並びに固体酸化物形燃料電池
JP2012250894A (ja) * 2011-06-06 2012-12-20 Nippon Shokubai Co Ltd 有機基で被覆された金属酸化物ナノ粒子の製造方法
JP2016028998A (ja) * 2014-07-18 2016-03-03 東京インキ株式会社 正方晶酸化ジルコニウムナノ粒子、その製造方法、分散体および樹脂複合体

Non-Patent Citations (1)

* Cited by examiner, † Cited by third party
Title
See also references of EP3357866A4 *

Cited By (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2019026811A1 (fr) * 2017-07-31 2019-02-07 クラレノリタケデンタル株式会社 Procédé de fabrication de poudre contenant des particules de zircone
CN110891903A (zh) * 2017-07-31 2020-03-17 可乐丽则武齿科株式会社 包含氧化锆颗粒的粉末的制造方法
US11479510B2 (en) 2017-07-31 2022-10-25 Kuraray Noritake Dental Inc. Method for producing zirconia particle-containing powder
CN111233468A (zh) * 2020-02-12 2020-06-05 长裕控股集团有限公司 结构件用钇稳定锆粉的制备方法
CN111233468B (zh) * 2020-02-12 2023-09-15 长裕控股集团股份有限公司 结构件用钇稳定锆粉的制备方法

Similar Documents

Publication Publication Date Title
KR102351339B1 (ko) 금속산화물 입자를 포함하는 분산체
JP6742761B2 (ja) 酸化ジルコニウムナノ粒子
US20180265372A1 (en) Zirconium oxide nanoparticles
JP6796386B2 (ja) 酸化ジルコニウムナノ粒子
WO2017057636A1 (fr) Nanoparticules d'oxyde de zirconium
KR102575562B1 (ko) 산화지르코늄 나노 입자
JPWO2019017305A1 (ja) 被覆無機微粒子及びその製造方法
JP2017214277A (ja) 酸化ジルコニウムナノ粒子
WO2017163610A1 (fr) Nanoparticule d'oxyde de zirconium
JP6517106B2 (ja) 分散液
JP6417528B2 (ja) 化合物、金属酸化物粒子及び金属酸化物粒子の製造方法
JP2022033609A (ja) 金属酸化物ナノ粒子、金属酸化物ナノ粒子を含む組成物及びその硬化物
JP2016040355A (ja) 金属酸化物粒子含有組成物および光学部材
CN114829304A (zh) 包覆的氧化锆微粒和其制造方法
JP6826899B2 (ja) 無機粒子分散体
JP6219627B2 (ja) 金属酸化物粒子、金属酸化物粒子含有組成物および光学部材
JP2013184933A (ja) 金属酸化物粒子
JP6293836B2 (ja) Ｚｒ酸化物粒子及びこれを含む組成物
JP6030844B2 (ja) 精製金属カルボン酸化合物の製造方法、及びこれを用いた金属酸化物粒子の製造方法
JP2020100692A (ja) 被覆された酸化ジルコニウムナノ粒子と極性溶媒と親水性樹脂を含む組成物

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 16851807

Country of ref document: EP

Kind code of ref document: A1

WWE Wipo information: entry into national phase

Ref document number: 15764048

Country of ref document: US

NENP Non-entry into the national phase

Ref country code: DE

WWE Wipo information: entry into national phase

Ref document number: 2016851807

Country of ref document: EP