WO2017018774A1 - 절연필름 및 플렉서블 플랫 케이블 - Google Patents

절연필름 및 플렉서블 플랫 케이블 Download PDF

Info

Publication number
WO2017018774A1
WO2017018774A1 PCT/KR2016/008152 KR2016008152W WO2017018774A1 WO 2017018774 A1 WO2017018774 A1 WO 2017018774A1 KR 2016008152 W KR2016008152 W KR 2016008152W WO 2017018774 A1 WO2017018774 A1 WO 2017018774A1
Authority
WO
WIPO (PCT)
Prior art keywords
insulating film
flame retardant
adhesive layer
resin
polyester
Prior art date
Application number
PCT/KR2016/008152
Other languages
English (en)
French (fr)
Inventor
김성문
박광석
유의덕
정인기
박수병
Original Assignee
주식회사 두산
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 주식회사 두산 filed Critical 주식회사 두산
Priority to US15/329,121 priority Critical patent/US10074458B2/en
Priority to CN201680001785.1A priority patent/CN107995891B/zh
Priority to EP16830807.0A priority patent/EP3179484A4/en
Publication of WO2017018774A1 publication Critical patent/WO2017018774A1/ko

Abstract

본 발명은 플렉서블 플랫 케이블(FFC)에 사용될 수 있으며, 굴곡성 및 기계적 특성이 우수한 절연필름과 상기 절연필름을 이용한 플렉서블 플랫 케이블(FFC)에 관한 것이다. 본 발명에서 제공하는 절연필름은 인장 강도, 신장율 및 굴곡성 등의 기계적 특성이 매우 우수하고, 열에 의한 수축성, 변성 등의 내열 특성 또한 매우 우수하다. 또한, 본 발명에서 제공하는 플렉서블 플랫 케이블 역시 상기한 절연필름을 사용함으로써 기계적 특성과 내열 특성이 매우 우수하다.

Description

절연필름 및 플렉서블 플랫 케이블
본 발명은 플렉서블 플랫 케이블(FFC)(flexible flat cable)에 사용될 수 있으며, 기계적 특성 및 열적 특성이 우수한 절연필름과 상기 절연필름을 이용한 플렉서블 플랫 케이블(FFC)에 관한 것이다.
종래부터 컴퓨터, 액정 표시 장치, 휴대 전화, 프린터, 자동차, 가전제품, 복사기 및 그 외 각종 전자, 전기, 기계 제품에서 굴곡성 또는 유동성이 필요한 전기적인 접속이나 다양한 형태의 배선을 위하여 플렉서블 플랫 케이블(FFC)이 많이 사용되고 있다. 이러한 플렉서블 플랫 케이블(FFC)은 일반적으로 단수 또는 복수의 도체에 접착제가 도포된 기재 필름 등을 도체의 단면 또는 양면에 부착하여 피복하는 구조를 갖는다.
플렉서블 플랫 케이블(FFC)은 회전, 미끄럼 이동 등 운동을 하는 전자기기 또는 기계 장치에 적용하여 전자기기 또는 기계 장치의 운동에 따른 구조의 변화에 유연하게 변형하면서, 전자기기의 동작 또는 기계 장치의 운동에 의한 발열 환경에서도 원활하게 전기적 신호를 전달하는데 사용된다. 이 때문에 플렉서블 플랫 케이블(FFC)을 피복하고 있는 플렉서블 플랫 케이블(FFC)용 절연필름은 회전 또는 미끄럼 이동 등의 운동에 대한 인장강도와 유연성이 요구되고 고온에 대한 높은 안정성 및 난연성이 요구된다.
이러한 플렉서블 플랫 케이블(FFC)용 절연필름으로는 일본 특허 공개 평성8-60108호 공보에는, 폴리이미드 필름과 인 변성 포화 폴리에스테르 공중합체로 이루어지는 접착층에 의한 비할로겐의 난연성 플랫 케이블이 제안되어 있다.
하지만 이러한 절연필름도 충분한 인장응력 및 유연성의 특성을 갖지 못해 문제되고 있다.
본 발명의 목적은 인장 강도, 신장율 및 굴곡성 등의 기계적 특성과 열에 의한 수축성, 변성 등의 내열 특성이 우수한 절연필름과 상기 절연필름을 이용한 플렉서블 플랫 케이블(FFC)을 제공하고자 한다.
본 발명의 일 구현 예에 따르면, 접착층, 중간층 및 수지층이 순서대로 적층된 절연필름으로서, 상기 절연필름의 온도 85℃, 습도 85%의 조건 하에서 1000hr 유지한 후의 인장응력(TH)에 대한 상온에서의 인장응력(TR)의 비율(TH /TR)은 0.9 ~ 1.0일 수 있다.
본 발명에서 온도 85℃, 습도 85%의 조건 하에서 1000hr 유지한 후의 상기 절연필름의 인장응력(TH)은 115 ~ 135MPa일 수 있다.
본 발명에서 상온 조건 하에서의 상기 절연필름의 인장응력(TR)은 130 ~ 140MPa일 수 있다.
본 발명에서 상기 절연필름의 길이 방향(MD) 수축율은 0.20 ~ 0.35%이고, 폭 방향(TD) 수축율은 0.08 ~ 0.13%일 수 있다.
본 발명에서 상기 절연필름의 길이 방향 수축율에 대한 폭 방향 수축율의 비율(MD/TD)은 2.5 ~ 3.0일 수 있다.
본 발명에서 상기 접착층은 고분자 수지를 포함할 수 있다.
본 발명에서 상기 고분자 수지는 폴리에스터(PE) 수지를 포함할 수 있다.
본 발명에서 상기 고분자 수지는 2종 이상의 폴리에스터(PE) 수지를 포함하고, 상기 폴리에스터(PE) 수지는 분자량이 1,000 내지 15,000인 제1폴리에스터(PE) 수지와 분자량이 20,000 내지 35,000인 제2폴리에스터(PE) 수지를 혼합하여 사용할 수 있다.
본 발명에서 상기 접착층은 1종 이상의 경화제를 포함할 수 있다.
본 발명에서 상기 경화제는 이소시아네이트기, 블록이소시아네이트기, 및 카르보디이미드기 중 적어도 하나의 작용기를 포함하는 화합물일 수 있다.
본 발명에서 상기 경화제는 고분자 수지 50 중량부에 대하여 6 내지 60 중량부의 양으로 포함될 수 있다.
본 발명에서 상기 접착층은 1종 이상의 난연제 필러를 더 포함할 수 있다.
본 발명에서 상기 난연제 필러는 할로겐 난연제, 인계 난연제, 질소계 난연제, 금속계 난연제 및 안티몬계 난연제로 이루어진 군에서 선택된 1종 이상일 수 있다.
본 발명의 다른 구현 예에 따르면, 접착층, 중간층 및 수지층이 순서대로 적층된 절연필름으로서, 상기 절연필름의 온도 85℃, 습도 85%의 조건 하에서 1000hr 유지한 후의 신장율(EH)은 85 ~ 105%인 절연필름을 제공한다.
본 발명에서 온도 85℃, 습도 85%의 조건 하에서 1000hr 유지한 후의 상기 절연필름의 인장응력(TH)은 115 ~ 135MPa일 수 있다.
본 발명에서 상온 조건 하에서의 상기 절연필름의 인장응력(TR)은 130 ~ 140MPa일 수 있다.
본 발명에서 상기 절연필름의 길이 방향(MD) 수축율은 0.20~0.35%이고, 폭 방향(TD) 수축율은 0.08 ~ 0.13%일 수 있다.
본 발명에서 상기 절연필름의 길이 방향 수축율에 대한 폭 방향 수축율의 비율(MD/TD)은 2.5 ~ 3.0일 수 있다.
본 발명에서 상기 접착층은 고분자 수지를 포함할 수 있다.
본 발명에서 상기 고분자 수지는 폴리에스터(PE) 수지를 포함할 수 있다.
본 발명에서 상기 고분자 수지는 2종 이상의 폴리에스터(PE) 수지를 포함하고, 상기 폴리에스터(PE) 수지는 분자량이 1,000 내지 15,000인 제1폴리에스터(PE) 수지와 분자량이 20,000 내지 35,000인 제2폴리에스터(PE) 수지를 포함할 수 있다.
본 발명에서 상기 접착층 1종 이상의 경화제를 포함할 수 있다.
본 발명에서 상기 경화제는 이소시아네이트기, 블록이소시아네이트기 및 카르보디이미드기 중 적어도 하나의 작용기를 포함하는 화합물일 수 있다.
본 발명에서 상기 경화제는 고분자 50 중량부 대비 6 내지 60 중량부의 양으로 포함될 수 있다.
본 발명에서 상기 접착층은 1종 이상의 난연제 필러를 더 포함할 수 있다.
본 발명에서 상기 난연제 필러는 할로겐 난연제, 인계 난연제, 질소계 난연제 및 금속계 난연제로 이루어진 군에서 선택된 1종 이상일 수 있다.
본 발명의 또 다른 구현 예에 따르면, 도체; 및 상기 도체의 적어도 일면에 본 발명의 일 구현 예 또는 다른 구현 예에 따른 절연필름이 적층된, 플렉서블 플랫 케이블(FFC)을 제공한다.
본 발명의 플렉서블 플랫 케이블(FFC)에서 온도 85℃, 습도 85%의 조건 하에서 1000hr 유지한 후의 상기 접착층에 대한 도체의 박리 강도(Peel Strength) 값은 0.75 ~ 1.00kg/cm일 수 있다.
본 발명에서 제공하는 절연필름은 인장 강도, 신장율 및 굴곡성 등의 기계적 특성이 매우 우수하고, 열에 의한 수축성, 변성 등의 내열 특성 또한 매우 우수하다.
또한, 본 발명에서 제공하는 플렉서블 플랫 케이블 역시 상기한 절연필름을 사용함으로써 기계적 특성과 내열 특성이 매우 우수하다.
도 1은 본 발명의 일 실시예에 따른 절연 필름의 단면 구조를 개략적으로 도시한 것이다.
도 2는 본 발명의 일 실시예에 따른 플렉서블 플랫 케이블의 단면 구조를 개략적으로 도시한 것이다.
도 3은 실험예 1에서 실시예 1 내지 6 및 비교예 1 내지 4에서 경화제 함량과 TH/TR의 관계를 그래프로 나타내었다.
도 4는 실험예 2에서 실시예 1 내지 6 및 비교예 1 내지 4에서 경화제 함량과 EH의 관계를 그래프로 나타내었다.
본 발명은 접착층, 중간층 및 수지층이 순서대로 적층된 절연필름으로서, 상기 절연필름의 온도 85℃, 습도 85%의 조건 하에서 1000hr 유지한 후의 인장응력(TH)에 대한 상온에서의 인장응력(TR)의 비율(TH /TR)은 0.9 ~ 1.0일 수 있다.
이하, 본 발명의 바람직한 실시형태들을 설명한다. 그러나 본 발명의 실시형태는 여러 가지 다른 형태로 변형될 수 있으며, 본 발명의 범위가 이하 설명하는 실시 형태로 한정되는 것은 아니다. 또한, 본 발명의 실시형태는 당해 기술분야에서 평균적인 지식을 가진 자에게 본 발명을 더욱 완전하게 설명하기 위해서 제공되는 것이다.
최근 각종 전자 기기나 자동차 분야에서 사용되는 플렉서블 플랫 케이블(FFC)은 전자 부품의 발열에 따라 고온의 환경 하에서 주로 사용되므로, 고온 및 고습 등의 가혹 조건 하에서 높은 인장 강도 및 신장율 등의 특성이 요구된다.
본 발명의 발명자들은 상기와 같이 가혹 조건 하에서 높은 인장 강도와 신장율 등의 기계적 특성 및 유연성을 유지할 수 있는 절연필름을 발견하여 본 발명에 이르게 되었다.
구체적으로, 본 발명은 접착층, 중간층 및 수지층이 순서대로 적층된 절연필름으로서, 도 1은 본 발명의 일 실시예에 따른 절연필름의 단면 구조를 개략적으로 도시한 것으로, 상기한 바와 같이 수지층(3) 상에 중간층(2)이 적층되고, 중간층(2) 상에 접착층(1)이 적층되는 것을 볼 수 있다.
여기서 상기 접착층(1)은 절연필름이 도전체에 접착하여 결합하게 해주는 역할을 하고, 상기 중간층(2)은 접착층(1)과 수지층(3) 사이에 위치하여 접착층(1)과 수지층(3)이 직접 결합했을 때의 부족한 결합력을 보완해 주는 역할을 하며, 상기 수지층(3)은 절연필름의 최외각에 위치하며 도전체가 외부와 절연이 될 수 있도록 한다.
본 발명의 일 구현 예에 따르면, 상기 절연필름의 온도 85℃, 습도 85%의 조건 하에서 1000hr 유지한 후의 인장응력(TH)에 대한 상온에서의 인장응력(TR)의 비율(TH /TR)은 0.9 ~ 1.0, 보다 바람직하게는 0.93 ~ 1.0인 것을 특징으로 한다.
단, 본 명세서에서 용어 '상온'은 가온 또는 감온되지 않은 자연 그대로의 온도를 의미하고, 예를 들면, 약 15 내지 35℃, 약 20 내지 25℃, 약 25 또는 23℃의 온도를 의미할 수 있다.
본 발명에서 상기 절연필름의 온도 85℃ 및 습도 85%의 가혹 조건 하에서 1000hr 유지한 후의 인장응력(TH)에 대한 상온에서의 인장응력(TR)의 비율(TH /TR)은 0.9 이상으로 가혹 조건에서도 상온 조건과 동일 및 유사한 기계적 특성이 유지될 수 있다. 반면 상기 TH /TR 비율이 0.9 미만인 경우, 접착층 또는 중간층에 포함되는 고분자 수지 내 가교 체인의 절단이 발생하고, 이로 인하여 기계적 강도 및 굴곡성이 현저히 저하될 수 있다. 따라서, 본 발명에서는 상기 절연필름의 온도 85℃, 습도 85%의 조건 하에서 1000hr 유지한 후의 인장응력(TH)에 대한 상온에서의 인장응력(TR)의 비율(TH/TR)을 0.9 이상으로 제어하는 것이 바람직하나, 실현 가능성 및 경제적 상황을 고려할 때 1.0 이하로 제어하는 것이 바람직하다.
또한, 본 발명의 다른 구현 예에 따르면, 상기 절연필름의 온도 85℃, 습도 85%의 조건 하에서 1000hr 유지한 후, 즉 가혹 조건 하에서 신장율(EH)이 85 ~ 105%의 높은 값을 갖는 것을 특징으로 한다.
본 발명에서 상기 절연필름의 상온에서의 인장응력(TR)은 130 ~ 140MPa의 높은 값을 가질 수 있다.
뿐만 아니라, 본 발명에서 상기 절연필름을 온도 85℃, 습도 85%의 가혹 조건 하에서 1000hr 유지한 후의 상기 절연필름의 인장응력(TH) 역시 115 ~ 135MPa의 매우 높은 값을 가질 수 있다.
또한, 본 발명에서 상기와 같이 제공하는 절연필름은 그 길이 방향(MD)의 수축율이 0.20 ~ 0.35%이고, 폭 방향(TD)의 수축율은 0.08 ~ 0.13%이며, 길이 방향의 수축율에 대한 폭 방향의 수축율의 비율(MD/TD)을 2.5 ~ 3.0로 제어함으로써 열 수축율의 특성을 더욱 향상시킬 수 있다.
또한, 본 발명의 절연필름에서 상기 접착층은 고분자 수지를 포함할 수 있고, 이때 상기 고분자 수지로는 폴리에스터(PE)계 수지, 폴리이미드계 수지, 폴리에틸렌계 수지, 폴리우레탄계 수지 및 폴리페닐렌설파이드계 수지로 이루어진 군으로부터 선택된 1종 이상을 사용할 수 있으나, 바람직하게는 폴리에스터(PE) 수지를 필수적으로 포함할 수 있다.
본 발명에서 상기 고분자 수지로 사용될 수 있는 폴리에스터 수지로는, 바람직하게는 2종 이상의 폴리에스터 수지를 사용할 수 있고, 보다 바람직하게는 분자량이 1,000 내지 15,000인 제1폴리에스터(PE) 수지, 분자량이 20,000 내지 35,000인 제2폴리에스터(PE) 수지 또는 이들의 혼합물을 사용할 수 있으며, 더욱 바람직하게는 2종 이상의 제1폴리에스터(PE) 수지, 2종 이상의 제2폴리에스터(PE) 수지 또는, 1종 이상의 제1폴리에스터(PE) 수지와 1종 이상의 제2폴리에스터(PE) 수지의 혼합물을 사용할 수 있으나, 가장 바람직하게는 1종 이상의 제1폴리에스터(PE) 수지와 1종 이상의 제2폴리에스터(PE) 수지의 혼합물을 사용할 수 있다.
단, 본 발명에서 사용할 수 있는 폴리에스터 수지의 종류는 상기한 종류로 한정되는 것은 아니고, 구현하고자 하는 제품의 특성에 따라 선택적으로 사용할 수 있다.
또한, 본 발명의 절연필름에서 상기 접착층은 1종 이상의 경화제를 포함하는 것이 바람직하다.
이때 상기 경화제의 종류로는 이소시아네이트기, 블록이소시아네이트기, 및 카르보디이미드기 중 적어도 하나의 작용기를 포함하는 화합물일 수 있다. 보다 상세하게는 2,4-톨릴렌 디이소시아네이트, 2,6-톨릴렌 디이소시아네이트, 디페닐메탄-4,4'-디이소시아네이트, 크실렌 디이소시아네이트, 이소포론 디이소시아네이트, 폴리에틸렌 페닐 디이소시아네이트 및 헥사메틸렌디이소시아네이트 등의 다관능 이소시아네이트, 이들의 이소시아네이트의 폴리올 변성물, 카르보디이미드 변성물, 이들의 이소시아네이트를 알코올, 페놀, 락탐, 아민 등으로 마스크한 블록형 이소시아네이트 등을 사용할 수 있으나, 이에 제한되는 것은 아니다.
또한, 본 발명에서 상기 경화제는 상기 접착층에 포함되는 고분자 수지 50 중량부에 대하여 6 ~ 60 중량부, 바람직하게는 6 ~ 26 중량부, 보다 바람직하게는 8 ~ 22 중량부, 더욱 바람직하게는 8 ~ 18 중량부의 양으로 포함되는 것이 인장 강도, 신장율 및 열 수축율 등의 기계적 물성과 굴곡성을 보다 향상시킬 수 있다. 고분자 수지의 함량이 100 중량부일 때는 경화제의 함량이 2배 증가할 수 있다.
본 발명에서 상기 고분자 수지 50 중량부 대비 경화제를 최소 6 중량부 이상 사용하여야 상기한 효과를 얻을 수 있고, 보다 바람직하게는 8 중량부 이상 사용하여야 경화제가 폴리에스테르 간에 가교역할(Cross-Linking)을 충분히 하여 가혹 조건 하에서도 우수한 기계적 특성을 발휘할 수 있다. 다만, 상기 경화제를 26 중량부 초과하여 사용할 경우 접착층이 딱딱해 져서 굴곡성과 유연성이 떨어지고 신장율도 낮아질 수 있다.
또한, 본 발명에서는 상기 접착층에 난연성을 부여하기 위하여 1종 이상의 난연제 필러를 더 포함할 수 있다.
여기서 상기 난연제 필러의 종류는 특별히 한정하지는 않으나, 상기한 난연제 필러의 첨가로 인하여 본 발명에 따르는 플렉서블 플랫 케이블(FFC)은 UL 규격의 수직 연소 시험(VW-1시험)에 합격하는 난연성을 부여하는 것이 바람직하다.
보다 상세하게는, 상기 난연제 필러로는 할로겐 난연제, 인계 난연제, 질소계 난연제, 금속계 난연제 및 안티몬계 난연제로 이루어진 군에서 선택된 1종 이상을 사용할 수 있고, 바람직하게는 1종 이상 7종 이하를 혼합하여 사용할 수 있으며, 보다 바람직하게는 적절하게는 3종 이상 5종 이하의 화합물을 혼합하여 사용할 수 있다.
본 발명에서 상기 난연제의 구체적인 예를 들면, 염소화파라핀, 염소화폴리에틸렌, 염소화폴리페닐, 퍼클로로펜타시클로데칸 등의 염소계 난연제; 에틸렌비스펜타브로모벤젠, 에틸렌비스펜타브로모디페닐, 테트라브로모에탄, 테트라브로모비스페놀 A, 헥사브로모벤젠, 데카브로모비페닐에테르, 테트라브로모무수프탈산, 폴리디브로모페닐렌옥사이드, 헥사브로모시클로데칸, 브롬화암모늄 등의 브롬계 난연제; 트리알릴포스페이트, 알킬알릴포스페이트, 알킬포스페이트, 디메틸포스포네이트, 포스폴리네이트, 할로겐화포스폴리네이트에스테르, 트리메틸포스페이트, 트리부틸포스페이트, 트리옥틸포스페이트, 트리부톡시에틸포스페이트, 옥틸디페닐포스페이트, 트리크레딜포스페이트, 크레딜페닐포스페이트, 트리페닐포스페이트, 트리스(클로로에틸)포스페이트, 트리스(2-클로로프로필)포스페이트, 트리스(2,3-디클로로프로필)포스페이트, 트리스(2,3-디브로모프로필)포스페이트, 트리스(브로모클로로프로필)포스페이트, 비스(2,3디브로모프로필)2,3디클로로프로필포스페이트, 비스(클로로프로필)모노옥틸포스페이트, 폴리포스포네이트, 폴리포스페이트, 방향족폴리포스페이트, 디브로모네오펜틸글리콜, 트리스(디에틸포스핀산)알루미늄 등의 인산에스테르 또는 인 화합물; 포스포네이트형 폴리올, 포스페이트형 폴리올, 할로겐 원소 함유 폴리올 등의 폴리올류; 수산화알루미늄, 수산화마그네슘, 탄산마그네슘, 삼산화안티몬, 삼염화안티몬, 붕산아연, 붕산안티몬, 붕산, 몰리부텐산안티몬, 산화몰리부텐, 인·질소 화합물, 칼슘·알루미늄 실리케이트, 티타늄 다이옥사이드, 지르코늄 화합물, 주석 화합물, 도오소나이트, 알루민산칼슘 수화물, 산화구리, 금속 구리분, 탄산칼슘, 메타붕산바륨 등의 금속분 또는 무기 화합물; 멜라민시아누레이트, 트리아진, 이소시아누레이트, 요소, 구아니딘 등의 질소 화합물; 및 실리콘계 폴리머, 페로센, 푸마르산, 말레산 등의 그 밖의 화합물 등을 들 수 있다. 그 중에서도, 브롬계 난연제, 염소계 난연제 등의 할로겐계 난연제가 바람직하다.
본 발명에서 상기 난연제 필러의 함량은 특별히 한정하지 않으나, 고분자 수지 50 중량부에 대하여 5 중량부 이상, 바람직하게는 10 중량부 이상, 보다 바람직하게는 15 중량부 이상으로 포함되는 것이 접착제층에 충분한 난연성을 부여할 수 있어 바람직하고, 그 상한으로는, 75 중량부, 바람직하게는 65 중량부, 보다 바람직하게는 60 중량부일 수 있다. 난연제 필러의 함량이 상기한 상한 값을 초과하는 경우, 첨가량 증가에 비하여 충분한 난연성 개선의 효과를 볼 수 없어 경제적으로 문제될 수 있고, 필러 함량 증가로 인해 유연성이 떨어지고 신장율도 낮아질 수 있다.
본 발명에서 필요에 따라서는 절연필름의 기계적 물성, 굴곡성 및 난연성 등의 특성을 손상시키지 않는 범위 하에서 상기한 접착층에 난연조제, 안료, 산화방지제, 은폐제, 윤활제, 가공 안정제, 가소제, 발포제 보강제, 착색제, 충전제, 과립제, 금속 불활성제, 실란 커플링제 등을 추가로 더 포함할 수 있다.
본 발명의 또 다른 구현 예에 따르면, 도체; 및 상기 도체의 적어도 일면에 본 발명의 일 구현 예 또는 다른 구현 예에 따른 절연필름이 적층되어 기계적 특성, 굴곡성 및 난연성이 매우 우수한 플렉서블 플랫 케이블(Flexible flat cable, FFC)을 제공한다.
도 2는 본 발명의 일 실시예에 따른 플렉서블 플랫 케이블의 단면 구조를 개략적으로 도시한 것으로, 도체(10)의 양면에 접착층(1)이 적층되고, 접착층(1)의 다른 일면 상에 중간층(2)이 적층되며, 중간층(2)의 다른 이면에 수지층(3)이 적층된다.
본 발명의 플렉서블 플랫 케이블(FFC)에서 온도 85℃, 습도 85%의 조건 하에서 상기 접착층에 대한 도체의 박리 강도(Peel Strength) 값은 0.75 ~ 1.00kg/cm일 수 있다.
본 발명에서 상기 도체의 종류는 특별히 한정하지는 않으나, 예를 들어, 구리, 주석 도금 구리, 니켈 도금 구리 등의 도전성 금속으로 이루어질 수 있다. 도체로서는 박 형상의 도전성 금속이 바람직하다.
본 발명의 또 다른 구현 예에 따르면, 1종 이상의 폴리에스터 수지, 1종 이상의 경화제 및 1종 이상의 난연성 필러를 배합 및 합성하여 제1용매를 제조하는 단계; 1종 이상의 폴리에스터 수지, 1종 이상의 경화제 및 무기필러를 배합 및 합성하여 제2용매를 제조하는 단계; 수지층에 상기 제2용매를 코팅하여 중간층을 형성하는 단계; 및 상기 중간층 상에 상기 제1용매를 코팅하고 건조하여 접착층을 형성하는 단계를 포함하는 절연필름의 제조방법을 제공한다.
본 발명의 절연필름의 제조방법에서 상기 폴리에스터 수지, 경화제 및 난연성 필러는 상기 절연필름에 기재한 바와 중복되어 이하에서는 그 구체적인 기재를 생략한다.
본 발명에서 상기 제2용매의 제조에 사용되는 무기필러의 종류를 특별히 한정하지는 않으나, 예를 들어 실리카(SiO2)를 사용할 수 있다.
본 발명의 또 다른 구현 예에 따르면, 본 발명에 따른 절연필름을 2개 준비하는 단계; 및 2개의 절연필름의 접착층 사이에 도체를 개재시킨 뒤 합지하는 단계를 포함하는, 플렉서블 플랫 케이블의 제조방법을 제공한다.
본 발명에서는 절연필름을 도체에 부착시키기에 앞서, 절연필름을 원하는 크기로 절단하는 단계를 추가로 수행할 수 있다.
실시예
이하, 구체적인 실시예를 통해 본 발명을 보다 구체적으로 설명한다. 하기 실시예는 본 발명의 이해를 돕기 위한 예시에 불과하며, 본 발명의 범위가 이에 한정되는 것은 아니다.
[실시예 1 내지 6 및 비교예 1 내지 6]
반응형 폴리에스터 수지 (분자량 8,000 / 유리전이온도 61℃)와 반응형 폴리에스터 수지 (분자량 30,000 / 유리전이온도 80℃) 각각 25중량부를 톨루엔 80 중량부, 메틸에틸케톤 90 중량부로 구성되는 용제 중에 용해해 수지 용액을 제조하고, 난연 특성 개선을 위한 난연제 필러 50 중량부를 첨가해 혼합한 후, 이소시아네이트 경화제를 하기 표 1에 나타난 함량으로 첨가하여 2,000cps 이상의 접착층용 제1용매를 제조하였다. 이소시아네이트 경화제는 수지 조성물의 경시에 영향을 미치는 인자로 코팅하기 직전에 투입하여 혼합물을 제조하였다. 또한, 폴리에스터 수지(분자량 5,000/유리전이온도 51℃)와 반응형 폴리에스터 수지(분자량 20,000/유리전이온도 35℃)의 혼합 수지 80 중량부에 대하여 실리카 20 중량부를 첨가하여 중간층용 제2용매를 제조하였다. 연신 폴리에틸렌 필름의 일 면에 콤마 코트 방식으로 제2용매를 10g/m2의 코팅량으로 코팅한 후 건조하여 중간층을 형성한 뒤, 상기 중간층 상에 제1용매를 100g/m2의 코팅량으로 코팅하고 건조하여 두께 20㎛의 접착층을 형성하였다.
구분 조성(중량부)
제1 폴리에스터(분자량 1,000 ~ 15,000) 제2 폴리에스터(분자량 20,000 ~ 35,000) 경화제 난연제 필러
실시예 1 25 25 8 50
실시예 2 25 25 10 50
실시예 3 25 25 14 50
실시예 4 25 25 18 50
실시예 5 25 25 22 50
실시예 6 25 25 26 50
비교예 1 25 25 1 50
비교예 2 25 25 3 50
비교예 3 25 25 5 50
비교예 4 25 25 - 50
비교예 5 50 - 14 50
비교예 6 - 50 14 50
[실험예 1]
상기 실시예 1 내지 6 및 비교예 1 내지 6에서 제조된 절연필름에 대하여 상온 조건(TR) 및 온도 85℃, 습도 85%의 조건(TH) 하에서 1000hr 유지한 후 각 샘플의 절연필름을 인장 시험기로 인장응력을 평가하여 그 결과를 하기 표 2에 나타내었고, 실시예 1 내지 6 및 비교예 1 내지 4에서 경화제 함량과 TH/TR의 관계를 도 3에 그래프로 나타내었다.
구분 경화제 함량(중량부) TR(MPa) TH(MPa) TH/TR
실시예 1 8 134 128 0.96
실시예 2 10 138 131 0.95
실시예 3 14 139 129 0.93
실시예 4 18 135 125 0.93
실시예 5 22 131 118 0.90
실시예 6 26 130 117 0.90
비교예 1 1 115 88 0.77
비교예 2 3 119 94 0.79
비교예 3 5 128 108 0.84
비교예 4 - 112 75 0.67
비교예 5 14 89 72 0.81
비교예 6 14 111 90 0.81
상기 표 2 및 도 3에서 보는 바와 같이, 본 발명에 따른 실시예 1 내지 6의 절연필름은 TH/TR이 0.90 ~ 0.96의 범위로 상온 조건 대비 가혹 조건에서의 특성이 매우 우수한 것을 볼 수 있다. 하지만, 비교예 1 내지 6는 상온 조건 대비 가혹 조건에서의 기계적 특성이 매우 저하된 것을 볼 수 있다.
[실험예 2]
실시예 1 내지 6 및 비교예 1 내지 6에서 제조된 절연필름에 대하여 상온 조건에서의 신장율(ER) 및 온도 85℃, 습도 85%에서 1000hr 유지한 후의 신장율(EH)을 평가하여 그 결과를 하기 표 3에 나타내었고, 실시예 1 내지 6 및 비교예 1 내지 4에서 경화제 함량과 EH의 관계를 도 4에 그래프로 나타내었다.
구분 경화제 함량(중량부) ER(%) EH(%)
실시예 1 8 120 92
실시예 2 10 123 97
실시예 3 14 125 103
실시예 4 18 121 105
실시예 5 22 104 89
실시예 6 26 109 85
비교예 1 1 104 77
비교예 2 3 109 78
비교예 3 5 117 82
비교예 4 - 98 75
비교예 5 14 85 75
비교예 6 14 88 76
상기 표 3 및 도 4에서 보는 바와 같이, 본 발명에 따른 실시예 1 내지 6의 절연필름은 온도 85℃, 습도 85%에서 1000hr 유지한 후의 신장율(EH)이 85 ~ 105%로 높은 값을 갖는 것을 볼 수 있다. 반면, 비교예 1 내지 6의 절연 필름은 온도 85℃, 습도 85%에서 1000hr 유지한 후의 가혹 조건에서의 신장율(EH)이 75 ~ 82% 정도의 수준에 불과한 것을 볼 수 있다.
[실험예 3]
실시예 1 내지 6 및 비교예 1 내지 6에서 제조된 절연필름에 대하여 열 수축율, 온도 85℃, 습도 95%의 조건 하에서 1000hr 유지한 후의 유연성과 온도 85℃, 습도 85%의 조건 하에서 1000hr 유지한 후의 외관성을 평가하여 그 결과를 하기 표 4에 나타내었다.
단, 상기 유연성 및 외관성의 구체적인 평가 기준은 다음과 같다.
1. 유연성 평가
온도 85℃, 습도 95%의 조건 하에서 도체 저항이 기존대비 10% 이상 증가할 때까지 절연필름을 미끄럼 이동 방식으로 횟수를 측정하였다.
◎ : 10만회 이상 , ○ : 7~10만회, △ : 5~7만회, X : 5만회 이하
2. 외관성 평가
온도 85℃, 습도 85%의 조건 하에서 층간박리(Delamination) 발생 여부로 평가하였다.
◎ : 2,000시간이상 층간박리 발생 無, ○ : 1,500~2,000시간 층간박리 발생, △ : 1,000~1,500시간 층간박리 발생, X : 1,000시간이하 층간박리 발생
구분 경화제 함량(중량부) MD(%) TD(%) MD/TD 유연성 외관성
실시예 1 8 0.30 0.10 3 ◎ ◎
실시예 2 10 0.20 0.08 2.5 ◎ ◎
실시예 3 14 0.20 0.08 2.5 ◎ ◎
실시예 4 18 0.20 0.08 2.5 ○ ○
실시예 5 22 0.20 0.08 2.5 ○ ○
실시예 6 26 0.20 0.08 2.5 ○ ○
비교예 1 1 0.75 0.25 3 △ △
비교예 2 3 0.60 0.20 3 ○ ○
비교예 3 5 0.40 0.15 2.67 ○ ○
비교예 4 - 0.80 0.30 2.67 △ △
비교예 5 14 0.35 0.13 2.69 △ △
비교예 6 14 0.35 0.12 2.92 △ △
상기 표 4에서 보는 바와 같이, 본 발명에 따른 실시예 1 내지 6의 절연필름은 MD가 0.2 ~ 0.3% 정도의 수준이고, TD가 0.08 ~ 0.10%의 수준으로 비교예 1 내지 6의 절연필름보다 열 수축율이 현저히 낮은 값을 갖는 것을 볼 수 있고, 유연성 및 외관성의 특성 또한 매우 우수한 것을 볼 수 있다.
[실험예 4]
상기 실시예 1 내지 6 및 비교예 1 내지 6에서 제조된 절연필름 2개의 접착층 사이에 두께 35㎛의 도체를 개재시킨 뒤, 0.8m/min의 속도로 라미네이팅 하여 플렉서블 플랫 케이블을 제조하였다. 이 후, 온도 85℃, 습도 85%의 조건 하에서 1000hr 유지한 후의 박리하는 강도(Peel strength, P/S)를 측정하여 그 결과를 하기 표 5에 나타내었다.
구분 경화제 함량(중량부) 고온고습P/S(kg/cm)
실시예 1 8 0.80
실시예 2 10 0.90
실시예 3 14 1.00
실시예 4 18 0.90
실시예 5 22 0.82
실시예 6 26 0.75
비교예 1 1 0.30
비교예 2 3 0.50
비교예 3 5 0.70
비교예 4 - 0.30
비교예 5 14 0.20
비교예 6 14 0.35
상기 표 5에서 보는 바와 같이, 본 발명에 따른 실시예 1 내지 6의 절연필름은 가혹 조건 하에서도 비교예 1 내지 6의 절연필름보다 박리 강도가 매우 높은 값을 갖는 것을 볼 수 있다.
이상에서 본 발명의 실시예에 대하여 상세하게 설명하였지만 본 발명의 권리범위는 이에 한정되는 것은 아니고, 청구범위에 기재된 본 발명의 기술적 사상을 벗어나지 않는 범위 내에서 다양한 수정 및 변형이 가능하다는 것은 당 기술분야의 통상의 지식을 가진 자에게는 자명할 것이다.
[부호의 설명]
1: 접착층, 2: 중간층, 3: 수지층, 10: 도체
본 발명은 절연필름과 상기 절연필름을 이용한 플렉서블 플랫 케이블(FFC)에 관한 것이다.

Claims (21)

  1. 접착층, 중간층 및 수지층이 순서대로 적층된 절연필름으로서,
    상기 절연필름의 온도 85℃, 습도 85%의 조건 하에서 1000hr 유지한 후의 인장응력(TH)에 대한 상온에서의 인장응력(TR)의 비율(TH /TR)은 0.9 ~ 1.0인 절연필름.
  2. 제1항에 있어서,
    상기 절연필름의 온도 85℃, 습도 85%의 조건 하에서 1000hr 유지한 후의 인장응력(TH)은 115 ~ 135Mpa인 절연필름.
  3. 제1항에 있어서,
    상기 절연필름의 상온에서의 인장응력(TR)은 130 ~ 140MPa인 절연필름.
  4. 제1항에 있어서,
    상기 절연필름의 길이 방향(MD) 수축율은 0.20~0.35%이고, 폭 방향(TD) 수축율은 0.08~0.13%이며,
    상기 절연필름의 길이 방향 수축율에 대한 폭 방향 수축율의 비율(MD/TD)은 2.5 ~ 3.0인 절연필름.
  5. 제1항에 있어서,
    상기 접착층은 고분자 수지를 포함하는 절연필름.
  6. 제5항에 있어서,
    상기 고분자 수지는 폴리에스터(PE) 수지를 포함하는 절연필름.
  7. 제6항에 있어서,
    상기 고분자 수지는 2종 이상의 폴리에스터(PE) 수지를 포함하고, 상기 폴리에스터(PE) 수지는 분자량이 1,000 내지 15,000인 제1폴리에스터(PE) 수지와 분자량이 20,000 내지 35,000인 제2폴리에스터(PE) 수지를 포함하는 절연필름.
  8. 제1항에 있어서,
    상기 접착층은 적어도 1종 이상의 경화제를 포함하고,
    상기 경화제는 이소시아네이트기, 블록이소시아네이트기, 및 카르보디이미드기 중 적어도 하나의 작용기를 포함하는 화합물인 절연필름.
  9. 제8항에 있어서,
    상기 경화제는 고분자 수지 50 중량부에 대하여 6 내지 60 중량부의 양으로 포함되는 절연필름.
  10. 제1항에 있어서,
    상기 접착층은 1종 이상의 난연제 필러를 더 포함하고,
    상기 난연제 필러는 할로겐 난연제, 인계 난연제, 질소계 난연제, 금속계 난연제 및 안티몬계 난연제로 이루어진 군에서 선택된 1종 이상인 절연필름.
  11. 접착층, 중간층 및 수지층이 순서대로 적층된 절연필름으로서,
    상기 절연필름의 온도 85℃, 습도 85%의 조건 하에서 1000hr 유지한 후의 신장율(EH)은 85~105%인 절연필름.
  12. 제11항에 있어서,
    상기 절연 필름의 길이 방향(MD) 수축율(%)은 0.20~0.35%이고, 폭 방향(TD) 수축율(%)은 0.08~0.13%이며,
    상기 절연 필름의 길이 방향 수축율(%)에 대한 폭 방향 수축율(%)의 비율(MD/TD)은 2.5 ~ 3.0인 것을 특징으로 하는 절연필름.
  13. 제11항에 있어서,
    상기 접착층은 폴리에스터 수지를 포함하는, 절연필름.
  14. 제13항에 있어서,
    상기 접착층은 2종 이상의 폴리에스터 수지를 포함하고, 상기 폴리에스터 수지는 분자량이 1,000~15,000인 제1폴리에스터 수지와 분자량이 20,000~35,000인 제2폴리에스터 수지를 포함하는, 절연필름.
  15. 제11항에 있어서,
    상기 접착층은 적어도 1종 이상의 경화제를 포함하고,
    상기 경화제는 이소시아네이트기, 블록이소시아네이트기, 및 카르보디이미드기 중 적어도 하나의 작용기를 포함하는 화합물인, 절연필름.
  16. 제15항에 있어서,
    상기 경화제는 고분자 수지 50 중량부에 대하여 6 내지 60 중량부로 포함되는, 절연필름.
  17. 제11항에 있어서,
    상기 접착층은 1종 이상의 난연제 필러를 더 포함하고,
    상기 난연제 필러는 할로겐 난연제, 인계 난연제, 질소계 난연제, 금속계 난연제 및 안티몬계 난연제로 이루어진 군에서 선택된 1종 이상인, 절연필름.
  18. 도체; 및
    상기 도체의 적어도 일면에 청구항 제1항 내지 제10항 중 어느 한 항에 따른 절연필름이 적층된 플렉서블 플랫 케이블(FFC).
  19. 제18항에 있어서,
    온도 85℃, 습도 85%의 조건 하에서 1000hr 유지한 후의 상기 접착층에 대한 도체의 박리 강도(Peel Strength) 값은 0.75 ~ 1.00kg/cm인 플렉서블 플랫 케이블(FFC).
  20. 도체; 및
    상기 도체의 적어도 일면에 청구항 제11항 내지 제17항 중 어느 한 항에 따른 절연필름이 적층된 플렉서블 플랫 케이블(FFC).
  21. 제20항에 있어서,
    온도 85℃, 습도 85%의 조건 하에서 1000hr 유지한 후의 상기 접착층에 대한 도체의 박리 강도(Peel Strength) 값은 0.75 ~ 1.00kg/cm인 플렉서블 플랫 케이블(FFC).
PCT/KR2016/008152 2015-07-28 2016-07-26 절연필름 및 플렉서블 플랫 케이블 WO2017018774A1 (ko)