WO2016076057A1 - Procédé de fabrication d'un film de résine - Google Patents

Procédé de fabrication d'un film de résine Download PDF

Info

Publication number
WO2016076057A1
WO2016076057A1 PCT/JP2015/079041 JP2015079041W WO2016076057A1 WO 2016076057 A1 WO2016076057 A1 WO 2016076057A1 JP 2015079041 W JP2015079041 W JP 2015079041W WO 2016076057 A1 WO2016076057 A1 WO 2016076057A1
Authority
WO
WIPO (PCT)
Prior art keywords
casting
film
drying
resin
resin film
Prior art date
Application number
PCT/JP2015/079041
Other languages
English (en)
Japanese (ja)
Inventor
田中　博文
Original Assignee
コニカミノルタ株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by コニカミノルタ株式会社 filed Critical コニカミノルタ株式会社
Priority to JP2016558935A priority Critical patent/JP6601414B2/ja
Publication of WO2016076057A1 publication Critical patent/WO2016076057A1/fr

Abstract

La présente invention concerne, selon un aspect, un procédé de fabrication d'un film de résine, qui comprend une étape de coulage pour former un film coulé en coulant une solution de résine contenant une résine transparente provenant d'une filière de coulage sur un support continu, une étape de séchage pour sécher le film coulé en dirigeant un courant d'air sec projeté à partir d'un dispositif de séchage sur le film coulé sur le support, ainsi qu'une étape de pelage pour peler le film coulé séché à partir du support et qui utilise un mécanisme de prévention pour empêcher l'écoulement du courant d'air sec vers le ruban de coulage au-dessus du film coulé entre la filière de coulage et le dispositif de séchage.
PCT/JP2015/079041 2014-11-10 2015-10-14 Procédé de fabrication d'un film de résine WO2016076057A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
JP2016558935A JP6601414B2 (ja) 2014-11-10 2015-10-14 樹脂フィルムの製造方法

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2014228253 2014-11-10
JP2014-228253 2014-11-10

Publications (1)

Publication Number Publication Date
WO2016076057A1 true WO2016076057A1 (fr) 2016-05-19

Family

ID=55954149

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2015/079041 WO2016076057A1 (fr) 2014-11-10 2015-10-14 Procédé de fabrication d'un film de résine

Country Status (2)

Country Link
JP (1) JP6601414B2 (fr)
WO (1) WO2016076057A1 (fr)

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2018074020A1 (fr) * 2016-10-20 2018-04-26 コニカミノルタ株式会社 Procédé de fabrication de film optique
WO2018074019A1 (fr) * 2016-10-20 2018-04-26 コニカミノルタ株式会社 Procédé de fabrication d'un film optique

Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2008307730A (ja) * 2007-06-13 2008-12-25 Konica Minolta Opto Inc 光学用フィルムの製造方法、光学用フィルム、偏光板及び液晶表示装置
WO2014141616A1 (fr) * 2013-03-12 2014-09-18 コニカミノルタ株式会社 Procédé de fabrication de film de résine

Patent Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2008307730A (ja) * 2007-06-13 2008-12-25 Konica Minolta Opto Inc 光学用フィルムの製造方法、光学用フィルム、偏光板及び液晶表示装置
WO2014141616A1 (fr) * 2013-03-12 2014-09-18 コニカミノルタ株式会社 Procédé de fabrication de film de résine

Cited By (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2018074020A1 (fr) * 2016-10-20 2018-04-26 コニカミノルタ株式会社 Procédé de fabrication de film optique
WO2018074019A1 (fr) * 2016-10-20 2018-04-26 コニカミノルタ株式会社 Procédé de fabrication d'un film optique
KR20190056399A (ko) * 2016-10-20 2019-05-24 코니카 미놀타 가부시키가이샤 광학 필름의 제조 방법
KR102184070B1 (ko) 2016-10-20 2020-11-27 코니카 미놀타 가부시키가이샤 광학 필름의 제조 방법

Also Published As

Publication number Publication date
JPWO2016076057A1 (ja) 2017-08-17
JP6601414B2 (ja) 2019-11-06

Similar Documents

Publication Publication Date Title
JP5708654B2 (ja) 樹脂フィルムの製造方法、樹脂フィルム、偏光板、及び液晶表示装置
TWI659055B (zh) 光學薄膜之製造方法
JP6601414B2 (ja) 樹脂フィルムの製造方法
JP6586787B2 (ja) 樹脂フィルムの製造方法
WO2016076070A1 (fr) Procédé de fabrication d'un film de résine
KR20160148455A (ko) 수지 필름의 제조 방법
JP6252581B2 (ja) 樹脂フィルムの製造方法
JP5708655B2 (ja) 樹脂フィルムの製造方法、流延ダイ、樹脂フィルムの製造装置、樹脂フィルム、偏光板、及び液晶表示装置
JP5907178B2 (ja) 光学フィルムの製造方法
JP6217744B2 (ja) 樹脂フィルムの製造方法
JP5692095B2 (ja) 樹脂フィルムの製造方法、樹脂フィルム、偏光板、及び液晶表示装置
JP6733543B2 (ja) 偏光膜の製造方法
JP2010023312A (ja) フィルムおよびその製造方法
JP6558092B2 (ja) 樹脂フィルムの製造方法
JP6733542B2 (ja) 偏光膜の製造方法
JP5082998B2 (ja) 樹脂フィルムの製造方法
JP4710160B2 (ja) 液晶表示装置用光学補償セルロースエステルフィルムの製造装置
JP5682749B2 (ja) 光学フィルムの製造方法
JP5682522B2 (ja) 液晶表示装置用光学フィルムの製造方法
JP5678813B2 (ja) 液晶表示装置用光学フィルムの製造方法

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 15859077

Country of ref document: EP

Kind code of ref document: A1

ENP Entry into the national phase

Ref document number: 2016558935

Country of ref document: JP

Kind code of ref document: A

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 15859077

Country of ref document: EP

Kind code of ref document: A1