WO2016047200A1 - Matériau de formation d'image et procédé de formation d'image - Google Patents

Matériau de formation d'image et procédé de formation d'image Download PDF

Info

Publication number
WO2016047200A1
WO2016047200A1 PCT/JP2015/064936 JP2015064936W WO2016047200A1 WO 2016047200 A1 WO2016047200 A1 WO 2016047200A1 JP 2015064936 W JP2015064936 W JP 2015064936W WO 2016047200 A1 WO2016047200 A1 WO 2016047200A1
Authority
WO
WIPO (PCT)
Prior art keywords
image forming
pigment
parts
mass
layer
Prior art date
Application number
PCT/JP2015/064936
Other languages
English (en)
Japanese (ja)
Inventor
陽平 有年
孝太郎 岡部
Original Assignee
富士フイルム株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 富士フイルム株式会社 filed Critical 富士フイルム株式会社
Publication of WO2016047200A1 publication Critical patent/WO2016047200A1/fr

Abstract

L'invention concerne un matériau de formation d'image qui forme une image à l'aide d'une lumière laser et comprend, sur un corps de support, une couche de conversion photothermique et une couche de formation d'image qui contient, sur la base de 100 parties en masse de la teneur totale en solides, de 20 parties en masse à 60 parties en masse (inclus) de particules de pigment ayant un diamètre de particule moyen en nombre de 30 nm à 100 nm (inclus), de 4 parties en masse à 40 parties en masse (inclus) d'au moins une résine qui est sélectionnée parmi des résines acryliques ayant une masse moléculaire moyenne en poids de 10 000 ou moins et des résines de colophane, et de 4 parties en masse à 40 parties en masse (inclus) d'un composé polymérisable ayant au moins deux doubles liaisons éthyléniquement insaturées ; et un procédé de formation d'image.
PCT/JP2015/064936 2014-09-26 2015-05-25 Matériau de formation d'image et procédé de formation d'image WO2016047200A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2014-197313 2014-09-26
JP2014197313A JP6204897B2 (ja) 2014-09-26 2014-09-26 画像形成材料及び画像形成方法

Publications (1)

Publication Number Publication Date
WO2016047200A1 true WO2016047200A1 (fr) 2016-03-31

Family

ID=55580741

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2015/064936 WO2016047200A1 (fr) 2014-09-26 2015-05-25 Matériau de formation d'image et procédé de formation d'image

Country Status (3)

Country Link
JP (1) JP6204897B2 (fr)
TW (1) TW201612023A (fr)
WO (1) WO2016047200A1 (fr)

Citations (12)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH08310124A (ja) * 1995-05-19 1996-11-26 Konica Corp 画像形成材料
JPH08337056A (ja) * 1995-04-10 1996-12-24 Konica Corp 画像形成材料及びそれを用いる画像形成方法
JPH1114979A (ja) * 1997-05-23 1999-01-22 Samsung Display Devices Co Ltd カラーフィルター用ドナーフィルム
JP2000098599A (ja) * 1998-09-22 2000-04-07 Fuji Photo Film Co Ltd 感光性転写材料
JP2001010244A (ja) * 1999-06-30 2001-01-16 Fuji Photo Film Co Ltd 熱転写シート
JP2002264551A (ja) * 2001-03-09 2002-09-18 Fuji Photo Film Co Ltd 画像形成材料、カラーフィルター形成材料、画像形成方法並びにカラーフィルター形成方法
JP2002274051A (ja) * 2001-03-16 2002-09-25 Fuji Photo Film Co Ltd 熱転写シート、受像シート、及び多色画像形成方法
JP2002347358A (ja) * 2001-01-24 2002-12-04 Fuji Photo Film Co Ltd 多色画像形成材料
JP2003341244A (ja) * 2002-05-24 2003-12-03 Fuji Photo Film Co Ltd 熱転写シート、画像形成材料及び画像形成方法
JP2008516262A (ja) * 2004-10-08 2008-05-15 富士フイルム株式会社 カラーフィルター、カラーフィルターの製造方法、及び液晶表示装置
JP2008250023A (ja) * 2007-03-30 2008-10-16 Dainippon Printing Co Ltd カラーフィルター用顔料分散液、カラーフィルター用硬化性樹脂組成物、カラーフィルター、及び表示装置
JP2008276255A (ja) * 2008-07-14 2008-11-13 Fujifilm Corp カラーフィルターの形成方法及びそれに用いるカラーフィルター形成材料並びにカラーフィルター

Patent Citations (12)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH08337056A (ja) * 1995-04-10 1996-12-24 Konica Corp 画像形成材料及びそれを用いる画像形成方法
JPH08310124A (ja) * 1995-05-19 1996-11-26 Konica Corp 画像形成材料
JPH1114979A (ja) * 1997-05-23 1999-01-22 Samsung Display Devices Co Ltd カラーフィルター用ドナーフィルム
JP2000098599A (ja) * 1998-09-22 2000-04-07 Fuji Photo Film Co Ltd 感光性転写材料
JP2001010244A (ja) * 1999-06-30 2001-01-16 Fuji Photo Film Co Ltd 熱転写シート
JP2002347358A (ja) * 2001-01-24 2002-12-04 Fuji Photo Film Co Ltd 多色画像形成材料
JP2002264551A (ja) * 2001-03-09 2002-09-18 Fuji Photo Film Co Ltd 画像形成材料、カラーフィルター形成材料、画像形成方法並びにカラーフィルター形成方法
JP2002274051A (ja) * 2001-03-16 2002-09-25 Fuji Photo Film Co Ltd 熱転写シート、受像シート、及び多色画像形成方法
JP2003341244A (ja) * 2002-05-24 2003-12-03 Fuji Photo Film Co Ltd 熱転写シート、画像形成材料及び画像形成方法
JP2008516262A (ja) * 2004-10-08 2008-05-15 富士フイルム株式会社 カラーフィルター、カラーフィルターの製造方法、及び液晶表示装置
JP2008250023A (ja) * 2007-03-30 2008-10-16 Dainippon Printing Co Ltd カラーフィルター用顔料分散液、カラーフィルター用硬化性樹脂組成物、カラーフィルター、及び表示装置
JP2008276255A (ja) * 2008-07-14 2008-11-13 Fujifilm Corp カラーフィルターの形成方法及びそれに用いるカラーフィルター形成材料並びにカラーフィルター

Also Published As

Publication number Publication date
JP6204897B2 (ja) 2017-09-27
JP2016068283A (ja) 2016-05-09
TW201612023A (en) 2016-04-01

Similar Documents

Publication Publication Date Title
US7368148B2 (en) Fabrication process of color filters, inks, color filters, and image displays using the color filters
JP4623500B2 (ja) カラーフィルターの製造方法
JP2005534046A (ja) カラーフィルタのサーマルプリンティングのドナー要素用の低分子量アクリルコポリマーラテックス
WO2016039272A1 (fr) Matériau de formation d'image et procédé de formation d'image
WO2003050575A1 (fr) Filtre couleur, materiau de formation d'un filtre couleur, procede de formation d'un filtre couleur, carte de circuit imprime pourvue d'un filtre couleur, procede de formation de ladite carte et element a cristaux liquides
JP2004505292A (ja) レーザー誘起熱転写記録プロセス
JP2004525808A (ja) レーザー誘起熱画像転写用高分解能レーザー誘起型集合体
JP6204897B2 (ja) 画像形成材料及び画像形成方法
JP6204868B2 (ja) 画像形成材料、及び画像形成方法
JP2008276255A (ja) カラーフィルターの形成方法及びそれに用いるカラーフィルター形成材料並びにカラーフィルター
JP4734380B2 (ja) カラーフィルターの形成方法及びカラーフィルター
JP2012203374A (ja) カラーフィルタの製造方法
US20020168579A1 (en) Image-forming material, color filter-forming material, and method of forming images and color filters
KR101058977B1 (ko) 내구성 어셈블리지를 제공하는 화상형성 방법 및 생산물
JP2005526293A (ja) カラーフィルタのサーマルプリンティング用平坦化要素
JP3792953B2 (ja) レーザ熱転写材料
JP3425564B2 (ja) 多色画像形成材料及び多色画像形成方法
JP2016182684A (ja) 画像形成材料及び画像形成方法
JP2003177229A (ja) カラーフィルター付回路基板の形成方法及びカラーフィルター付回路基板
JP2004268290A (ja) 熱転写シート、画像形成材料及び画像形成方法
JP2002264551A (ja) 画像形成材料、カラーフィルター形成材料、画像形成方法並びにカラーフィルター形成方法
JP2002219878A (ja) 画像形成材料、カラーフィルター形成材料、画像形成方法並びにカラーフィルター形成方法
KR20030019305A (ko) 레이저 유도 열 전사 기록 방법
JP2008064960A (ja) カラーフィルタ及び表示装置
JP2005103893A (ja) 画像形成材料及び画像形成方法

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 15845290

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase