WO2016035972A1 - 광고지 부착 방지용 코팅시트 - Google Patents

광고지 부착 방지용 코팅시트 Download PDF

Info

Publication number
WO2016035972A1
WO2016035972A1 PCT/KR2015/004843 KR2015004843W WO2016035972A1 WO 2016035972 A1 WO2016035972 A1 WO 2016035972A1 KR 2015004843 W KR2015004843 W KR 2015004843W WO 2016035972 A1 WO2016035972 A1 WO 2016035972A1
Authority
WO
WIPO (PCT)
Prior art keywords
coating
coating layer
sheet
weight
parts
Prior art date
Application number
PCT/KR2015/004843
Other languages
English (en)
French (fr)
Inventor
류영옥
Original Assignee
주식회사 신도디앤텍
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 주식회사 신도디앤텍 filed Critical 주식회사 신도디앤텍
Priority to CA2951518A priority Critical patent/CA2951518C/en
Priority to US15/318,355 priority patent/US10519346B2/en
Priority to CN201580000327.1A priority patent/CN105517799A/zh
Publication of WO2016035972A1 publication Critical patent/WO2016035972A1/ko

Abstract

본 발명은 광고지 부착 방지용 코팅시트에 관한 것이다. 본 발명에 따른 광고지 부착 방지용 코팅시트는, 합성수지재로 형성되는 연질시트; 상기 연질시트의 일측면 상부에 위치하고, 태양에서 방사되는 자외선에 의한 탈색, 변색을 방지하는 보호층; 상기 보호층 상부에 위치하고 미세 요철 또는 돌기가 형성된 제1 코팅층; 상기 제1 코팅층 상에 위치하고 상기 제1 코팅층 상에 필름막으로 형성된 제2 코팅층; 상기 연질시트 타측면 하부에 위치하고, 상기 연질시트를 고정 부착하기 위한 점착제층; 및 상기 점착제층 하부에 위치하고, 상기 점착제층이 외부로부터 오염되는 것을 방지하여 점착력을 보호, 유지시키기 위한 이형지층을 포함한다. 상기한 구성에 의해 본 발명에 따른 광고지 부착 방지용 코팅시트는 벽이나 전신주, 가로등, 신호등과 같은 공공시설물 또는 개인시설물에 부착되어 불법 광고지 등이 무단 부착되는 것을 방지할 수 있다.

Description

광고지 부착 방지용 코팅시트
본 발명은 광고지 부착 방지용 코팅시트에 관한 것으로서, 보다 상세하게는 벽이나 전신주, 가로등, 신호등과 같은 공공시설물 또는 개인시설물에 부착되어 불법 광고지 등이 무단 부착되는 것을 방지할 수 있는 광고지 부착 방지용 코팅시트에 관한 것이다.
일반적으로 도로의 교통시설물인 가로등이나 도로표지판 및 신호등의 지주(支柱)와 전신주는 시계(視界)가 우수한 장소에 주로 설치되어 있어 광고의 효과가 뛰어나고, 그로 인하여 각종 불법 광고 전단지의 부착이 늘어나고 있는 실정이다.
이와 같이 시계(視界)가 우수한 장소에 설치되어지는 또 다른 도로 시설물로는 휀스 및 옹벽 등의 시설물들을 예로 들을 수 있고, 이 또한 불법 광고전단지의 부착으로부터 자유로울 수 없었다.
상기와 같이 불법적으로 부착되는 광고 전단지는 거리 환경을 오염시키는 주된 요인으로 대두 되고 있는데, 상기와 같이 각종 개인 또는 공공시설물의 표면에 무분별하게 불법 부착되는 부착물은 미관을 해치며, 특히 교통 표지판의 표면 또는 기둥 등에 부착된 불법 부착물은 운전자의 집중력을 떨어뜨리거나, 도로 상황에 대한 전달력을 저하시켜 사고의 원인이 되는 문제점이 발생하였다.
한편, 이와 같이 불법적으로 부착되는 광고지를 지속적으로 제거하기 위하여 정부 또는 지방자치단체에서는 전담관리부서를 설치하여 이러한 불법 광고지를 제거하고 있는데, 이러한 방법은 근본적인 해결책이 되지 못하고 있을 뿐만 아니라 이러한 제거방법은 많은 인력과 막대한 비용이 소요되는 문제점이 있었다.
상기한 문제점을 감안하여 도로변에 설치되는 각종 가로등이나 도로표지판, 신호등의 지주 표면에 불법 광고지의 부착을 미연에 방지할 수 있도록 하기 위한 광고지 부착방지판이 제안되고 있다.
이와 같은 불법 광고지 부착방지판의 일 예를 들면, 이는 가로등이나 도로표지판, 신호등의 지주 표면을 둥글게 감싸서 상호 연결할 수 있도록 고무, 합성수지 재질의 판체를 형성함과 동시에 광고지 부착방지판의 표면에는 원뿔, 사각뿔 등의 다양한 형태를 가지는 부착방지 돌기를 형성하여 별도의 체결밴드로서 고정토록 하는 구성이다.
그러나, 이와 같은 구성은 전체적으로 하나의 판체로 형성하면서도 별도의 체결밴드 등으로 설치하는 구성이므로 설치에 따른 구성이 복잡할 뿐만 아니라 체결밴드가 외부로 노출되어 외관이 좋지 못한 문제점이 있었다.
[선행기술문헌]
[특허문헌]
(특허문헌 1) 국내등록특허 제10-1412870호(2014년 06월 20일 등록)
(특허문헌 2) 국내등록실용 제20-0411629호(2006년 03월 09일 등록)
본 발명은 벽이나 전신주, 가로등, 신호등과 같은 공공시설물 또는 개인시설물에 부착되어 불법 광고지 등이 무단 부착되는 것을 방지할 수 있는 광고지 부착 방지용 코팅시트를 제공하는데 있다.
또한, 본 발명은 시설물의 표면이나 인쇄물 상에 도포되어 접착력을 저하시킴과 동시에 접착제를 이용한 광고지 등이 부착된 경우에도 접착제 성분이 잔류하지 않고, 스크레이퍼와 같은 기계적인 도움없이도 광고지 등을 손쉽게 제거할 수 있는 광고지 부착 방지용 코팅시트를 제공하는데 있다.
또한, 본 발명은 전기절연 특성이 있어 가로등이나 신호등에 사용되는 경우에도 누전에 의한 사고를 방지할 수 있는 광고지 부착 방지용 코팅시트를 제공하는데 있다.
본 발명이 해결하고자 하는 다양한 과제들은 이상에서 언급한 과제들에 제한되지 않으며, 언급되지 않은 또 다른 과제들은 아래의 기재로부터 당업자에게 명확하게 이해될 수 있을 것이다.
본 발명에 따른 광고지 부착 방지용 코팅시트는, 합성수지재로 형성되는 연질시트; 상기 연질시트의 일측면 상부에 위치하고, 태양에서 방사되는 자외선에 의한 탈색, 변색을 방지하는 보호층; 상기 보호층 상부에 위치하고 미세 요철 또는 돌기가 형성된 제1 코팅층; 상기 제1 코팅층 상에 위치하고 상기 제1 코팅층 상에 필름막으로 형성된 제2 코팅층; 상기 연질시트 타측면 하부에 위치하고, 상기 연질시트를 고정 부착하기 위한 점착제층; 및 상기 점착제층 하부에 위치하고, 상기 점착제층이 외부로부터 오염되는 것을 방지하여 점착력을 보호, 유지시키기 위한 이형지층을 포함한다.
상기 보호층은 자외선 보호 잉크를 상기 연질시트 상에 실사인쇄 또는 실크인쇄하여 형성될 수 있다.
상기 제1 코팅층은, 우레탄 합성수지, 아크릴계 수지용액 또는 에폭시계 수지용액 25 내지 35 중량부와, PE-열가소성 수지, 페놀수지, 멜라민수지, 에폭시수지, 폴리스티렌수지 비드 또는 유리 비드 10 내지 20 중량부와, 우레탄 신너 및 톨루엔 40 내지 52 중량부와, 경화제 2 내지 4 중량부가 상기 연질시트 상에 도포된 후 건조되어 형성될 수 있다.
상기 경화제는 이소시아네트 TDI(toluene d-iso cyanate), MDI(Michelson Doppler Imager) 우레탄 합성수지 경화제나, 디에틸렌트리아민(DETA), TET(Tetramethylthiurammonosulfide), 아크릴계 또는 에폭시계 경화제가 사용될 수 있다.
상기 제1 코팅층은 10 내지 500㎛ 범위의 직경을 가지는 PE-열가소성 수지, 페놀수지, 멜라민수지, 에폭시수지, 폴리스티렌수지 비드 또는 유리 비드가 사용될 수 있다.
상기 제1 코팅층은 실리카 경화제가 더 포함될 수 있다.
상기 제2 코팅층은 실리콘 이형제 8 내지 12 중량부, 헥세인 40 내지 55 중량부, 톨루엔 20 내지 25 중량부 및 백금촉매 0.08 내지 0.18 중량부로 혼합된 용액이 상기 제1 코팅층 상에 도포된 후 건조되어 형성될 수 있다.
상기 제2 코팅층은 상기 제1 코팅층 상에 에어스프레이 도장 방식이나 로울러 도색 방식으로 도포될 수 있다.
상기 제2 코팅층은 10 내지 35℃의 온도에서 1시간 30분 내지 2시간 30분 동안 자연 건조되어 형성될 수 있다.
상기 제1 코팅층 또는 제2 코팅층은 오일 성분을 더 포함할 수 있다.
상기 오일 성분은 실리콘 오일, 파라핀 오일, 테라핀 오일 또는 페트롤 오일 중에서 선택되는 어느 하나일 수 있다.
상기 제2 코팅층은 상기 백금촉매와 초산형 또는 무초산형 실리콘을 혼합하여 사용할 수 있다.
또한, 본 발명에 따른 광고지 부착 방지용 코팅시트는, 시설물 상부에 도포되고 미세 요철 또는 돌기가 형성된 제1 코팅층; 및 상기 제1 코팅층 상에 도포되고 상기 제1 코팅층 상에 필름막으로 형성된 제2 코팅층을 포함하되, 상기 제1 코팅층은 우레탄 합성수지, 아크릴계 수지용액 또는 에폭시계 수지용액 25 내지 35 중량부와, PE-열가소성 수지, 페놀수지, 멜라민수지, 에폭시수지, 폴리스티렌수지 비드 또는 유리 비드 10 내지 20 중량부와, 우레탄 신너 및 톨루엔 40 내지 52 중량부와, 경화제 2 내지 4 중량부가 상기 시설물 상에 도포된 후 건조되어 형성되며, 상기 제2 코팅층은 실리콘 이형제 8 내지 12 중량부, 헥세인 40 내지 55 중량부, 톨루엔 20 내지 25 중량부 및 백금촉매 0.08 내지 0.18 중량부로 혼합된 용액이 상기 제1 코팅층 상에 도포된 후 건조되어 형성된다.
상기 제1 코팅층 또는 제2 코팅층은 오일 성분을 더 포함하되, 상기 오일 성분은 실리콘 오일, 파라핀 오일, 테라핀 오일 또는 페트롤 오일 중에서 선택될 수 있다.
상기 제1 코팅층 또는 제2 코팅층은 에어스프레이 도장 방식이나 로울러 도색 방식으로 도포될 수 있다.
상기 PE-열가소성 수지, 페놀수지, 멜라민수지, 에폭시수지, 폴리스티렌수지 비드 또는 유리 비드는 10 내지 500㎛ 범위의 직경을 가질 수 있다.
상기 제2 코팅층은 상기 백금촉매와 초산형 또는 무초산형 실리콘을 혼합하여 사용할 수 있다.
본 발명에 따른 광고지 부착 방지용 코팅시트는 벽이나 전신주, 가로등, 신호등과 같은 공공시설물 또는 개인시설물에 부착되어 불법 광고지 등이 무단 부착되는 것을 방지할 수 있다.
또한, 본 발명에 따른 광고지 부착 방지용 코팅시트는 시설물의 표면이나 인쇄물 상에 도포되어 접착력을 저하시킴과 동시에 접착제를 이용한 광고지 등이 부착된 경우에도 접착제 성분이 잔류하지 않고, 스크레이퍼와 같은 기계적인 도움없이도 광고지 등을 손쉽게 제거할 수 있다.
또한, 본 발명에 따른 광고지 부착 방지용 코팅시트는 전기절연 특성이 있어 가로등이나 신호등에 사용되는 경우에도 누전에 의한 사고를 방지할 수 있다.
본 발명의 기술적 사상의 실시예는, 구체적으로 언급되지 않은 다양한 효과를 제공할 수 있다는 것이 충분히 이해될 수 있을 것이다.
도 1은 본 발명에 따른 광고지 부착 방지용 코팅시트의 일부를 분해하여 도시한 사시도이다.
도 2는 본 발명에 따른 광고지 부착 방지용 코팅시트에서 제1 코팅층 상에 존재하는 미세 요철 입자의 주사현미경(SEM) 사진이다.
본 발명의 이점 및 특징, 그리고 그것들을 달성하는 방법은 첨부되는 도면과 함께 상세하게 후술되어 있는 실시예를 참조하면 명확해질 것이다. 그러나 본 발명은 여기서 설명되는 실시예들에 한정되지 않고 다른 형태로 구체화될 수도 있다. 오히려, 여기서 소개되는 실시예들은 개시된 내용이 철저하고 완전해질 수 있도록 그리고 당업자에게 본 발명의 사상이 충분히 전달될 수 있도록 하기 위해 제공되는 것이다. 도면들에 있어서, 층 및 영역들의 두께는 명확성을 기하기 위하여 과장된 것이다.
상단, 하단, 상면, 하면, 또는 상부, 하부 등의 용어는 구성요소에 있어 상대적인 위치를 구별하기 위해 사용되는 것이다. 예를 들어, 편의상 도면상의 위쪽을 상부, 도면상의 아래쪽을 하부로 명명하는 경우, 실제에 있어서는 본 발명의 권리 범위를 벗어나지 않으면서 상부는 하부로 명명될 수 있고, 하부는 상부로 명명될 수 있다.
본 출원에서 사용한 용어는 단지 특정한 실시예를 설명하기 위해 사용된 것으로, 본 발명을 한정하려는 의도가 아니다. 단수의 표현은 문맥상 명백하게 다르게 뜻하지 않는 한, 복수의 표현을 포함한다. 본 출원에서, "포함하다" 또는 "가지다" 등의 용어는 명세서상에 기재된 특징, 숫자, 단계, 동작, 구성요소, 부분품 또는 이들을 조합한 것이 존재함을 지정하려는 것이지, 하나 또는 그 이상의 다른 특징들이나 숫자, 단계, 동작, 구성요소, 부분품 또는 이들을 조합한 것들의 존재 또는 부가 가능성을 미리 배제하지 않는 것으로 이해되어야 한다.
다르게 정의되지 않는 한, 기술적이거나 과학적인 용어를 포함해서 여기서 사용되는 모든 용어들은 본 발명이 속하는 기술 분야에서 통상의 지식을 가진 자에 의해 일반적으로 이해되는 것과 동일한 의미가 있다. 일반적으로 사용되는 사전에 정의되어 있는 것과 같은 용어들은 관련 기술의 문맥상 가지는 의미와 일치하는 의미가 있는 것으로 해석되어야 하며, 본 출원에서 명백하게 정의하지 않는 한, 이상적이거나 과도하게 형식적인 의미로 해석되지 않는다.
이하, 첨부된 도면을 참조하여 본 발명의 기술적 사상의 일 실시예에 따른 광고지 부착 방지용 코팅시트에 대한 바람직한 실시예를 더욱 상세하게 설명한다.
도 1은 본 발명에 따른 광고지 부착 방지용 코팅시트의 일부를 분해하여 도시한 사시도이고, 도 2는 본 발명에 따른 광고지 부착 방지용 코팅시트에서 제1 코팅층 상에 존재하는 미세 요철 입자의 주사현미경(SEM) 사진이다.
본 발명에 따른 광고지 부착 방지용 코팅시트는 벽이나 전신주, 가로등, 신호등과 같은 공공시설물 또는 개인시설물에 부착되어 불법 광고지 등이 무단 부착되는 것을 방지할 수 있는 것으로, 본 발명에서 상기 광고지는 접착제를 이용한 전단지, 스티커 등 옥외 구조물에 불법적으로 부착되는 각종 부착물들을 포함한다.
도 1 및 도 2를 참조하면, 본 발명에 따른 광고지 부착 방지용 코팅시트는 연질시트(4), 보호층(3), 제1 코팅층(2), 제2 코팅층(1), 점착제층(5) 및 이형지층(6)을 포함한다.
상기 연질시트(4)는 합성수지재인 PVC, 플렉스 패브릭(FLEX Fabric), PP, PET 등과 같은 연질의 합성수지재가 사용되고, 연질시트(4)가 부착되는 대상물의 표면에 따라 곡선, 원형 또는 일정 범위의 각도로 손쉽게 휘어질 수 있는 휨 성질을 가질 수 있다. 상기 연질시트(4)는 휨 성질을 가진 판재나 필름 형태로 구성될 수 있다.
상기 보호층(3)은 상기 연질시트(4)의 일측면 상부에 위치하고, 태양으로부터 방사되는 자외선으로부터 연질시트(4)의 표면을 보호하기 위하여 구비될 수 있다. 즉, 상기 보호층(3)은 연질시트(4) 표면에 도포되어 상기 연질시트(4)가 태양에서 방사되는 자외선에 의해 탈색 및 변색되는 것을 방지할 수 있다.
상기 보호층(3)은 자외선으로부터 상기 연질시트(4)를 보호하는 자외선 보호 잉크를 사용할 수 있는데, 상기 자외선 보호 잉크는 상기 연질시트(4) 상에 실사인쇄, 실크인쇄 또는 다양한 인쇄, 도포 방식이 이용될 수 있다.
상기 제1 코팅층(2)은 무색 투명하며 상기 보호층(3) 상에 도포되고, 광고지와의 접착성을 저하시킬 수 있다. 상기 제1 코팅층(2)은 미세 요철 표면을 형성함으로써, 스크레이퍼와 같은 기계적인 도움없이도 본 발명에 따른 코팅시트 상에 부착된 광고지 등을 손쉽게 분리될 수 있게 한다. 상기 제1 코팅층(2)은 에어스프레이 도장 방식이나 로울러 도색 방식에 의해 상기 보호층(3) 상에 도포됨으로써 형성될 수 있다.
상기 제1 코팅층(2)은 우레탄 합성수지, 아크릴계 수지용액 또는 에폭시계 수지용액 25 내지 35 중량부와, 10 내지 500㎛ 범위의 다양한 직경을 가지는 PE-열가소성 수지, 페놀수지, 멜라민수지, 에폭시수지, 폴리스티렌수지 비드 또는 유리 비드 10 내지 20 중량부, 희석을 위한 유기 용매제로 사용되는 우레탄 신너 및 톨루엔 40 내지 52 중량부, 경도를 높이거나 경화를 촉진하기 위한 경화제 2 내지 4 중량부가 포함될 수 있다. 상기 경화제는 이소시아네트 TDI(toluene d-iso cyanate), MDI(Michelson Doppler Imager) 우레탄 합성수지 경화제나, 디에틸렌트리아민(DETA(Diethylenetriamine)), TET(Tetramethylthiurammonosulfide), 아크릴계 또는 에폭시계 경화제가 사용될 수 있다.
본 발명에 따른 광고지 부착 방지용 코팅시트에서 상기 제1 코팅층(2)을 형성하는 조성물은 실리카(Silica) 경화제를 더 포함할 수 있다. 상기 실리카 경화제는 주위 온도가 낮은 동절기에 사용될 수 있는 것으로, 외부 온도가 -1 내지 -20℃ 범위의 온도에서 상기 제1 코팅 조성물의 경화 속도 및 건조 속도를 증대시키기 위하여 첨가될 수 있다. 본 발명에서 상기 실리카 경화제는 4 내지 8 중량부가 포함될 수 있다.
상기 제2 코팅층(1)은 상기 제1 코팅층(2) 상에 도포되고, 상기 제1 코팅층(2)이 도포되어 건조된 후 형성될 수 있다. 상기 제2 코팅층(1)은 에어스프레이 도장 방식이나 로울러 도색 방식에 의해 상기 제1 코팅층(2) 상에 도포될 수 있고, 얇은 필름막을 형성하여 이형 효과를 증대시킬 수 있고 광고지의 접착제가 부착되는 것을 방지할 수 있다.
상기 제2 코팅층(1)은 실리콘 이형제(Silicone release agent) 8 내지 12 중량부, 헥세인(Hexane) 40 내지 55 중량부, 톨루엔 20 내지 25 중량부를 포함되고, 경화를 촉진시키기 위하여 백금촉매(Platinum catalyst) 0.08 내지 0.18 중량부가 포함될 수 있다.
본 발명에서 상기 제2 코팅층(1)은 경화를 촉진시키기 위하여 초산형 또는 무초산형 실리콘이 더 포함될 수 있다. 본 발명에서 경화를 촉진시키기 위한 물질로 백금촉매를 사용하였는데, 조금 더 빠른 경화를 위하여 백금촉매와 초산형 또는 무초산형 실리콘을 혼합하여 사용할 수 있다.
상기 초산형 실리콘은 초산 재질의 실리콘으로 산성을 띠고 굳는 속도가 빠르며 가격이 저렴한 특성이 있고 유리나 도기 재질에 대한 접착력이 우수하다. 또한, 상기 무초산형 실리콘은 초산 성분이 실리콘 내에 혼합되지 않은 것으로 주로 거울이나 알루미늄 새시, 나무, 석재 등에 접착력이 좋고 건조 속도는 초산형에 비해 조금 느리나 초산형에 비해 지속적인 접착력을 유지할 수 있다.
본 발명에 따른 광고지 부착 방지용 코팅시트는 제1 코팅층(2)에 PE-열가소성 수지, 페놀수지, 멜라민수지, 에폭시수지, 폴리스티렌수지 비드 또는 유리 비드가 포함되고, 제2 코팅층(1)에 실리콘 이형제가 포함되는데, 상기한 제1 코팅층(2) 및 제2 코팅층(1)은 경화시 절연 기능이 있으므로, 본 발명에 따라 제조된 광고지 부착 방지용 코팅시트는 가로등이나 신호등에 사용되는 경우에도 누전에 의한 사고를 방지할 수 있다.
상기 제1 코팅층(2) 및 제2 코팅층(1)은 광고지와의 이형성을 증대시키기 위하여 오일이 더 포함될 수 있다.
상기 오일은 실리콘 오일, 파라핀 오일, 테라핀 오일 또는 페트롤 오일이 선택될 수 있고, 상기 제1 코팅액 및 제2 코팅액 혼합시 상기 오일을 더 첨가하여 제1 코팅액 및 제2 코팅액의 이형성을 더욱 증대시킬 수 있다.
상기 점착제층(5)은 상기 연질시트(4) 타측면 하부에 위치하고, 벽이나 전신주, 가로등, 이정표, 신호등과 같은 구조물에 상기 연질시트(4)를 고정 부착하기 위하여 구비될 수 있다. 상기 점착제층(5)은 벽이나 전신주, 가로등, 이정표, 신호등과 같은 구조물에 견고하게 부착되기 위하여 10N/cm 이상의 접착 강도를 가지도록 구성할 수 있다. 본 발명에서 상기 점착제층(5)은 부직포 합성의 양면테이프가 사용되거나 아크릴 모노머의 필름타입 테이프가 사용될 수 있다.
상기 이형지층(6)은 상기 점착제층(5) 타측면 하부에 위치하고, 상기 점착제층(5)이 외부로부터 오염되는 것을 방지하여 점착력을 보호, 유지시키기 위하여 구비될 수 있다. 상기 이형지층(6)은 상기 점착제층(5)으로부터 쉽게 박리될 수 있도록 표면 가공될 수 있다.
이하, 첨부된 도면을 참조하여 본 발명에 따른 광고지 부착 방지용 코팅시트의 제조방법에 대하여 더욱 상세히 설명하기로 한다.
먼저, 작업자는 연질시트(4)를 준비할 수 있다. 상기 연질시트(4)는 PVC, 플렉스 패브릭(FLEX Fabric), PP, PET 등과 같은 연질의 합성수지재일 수 있고, 연질시트(4)가 부착되는 대상물의 표면에 따라 곡선, 원형 또는 일정 범위의 각도로 손쉽게 휘어질 수 있는 휨 성질을 가질 수 있다.
다음으로, 상기 연질시트(4) 일측면 상부에 보호층(3)을 형성할 수 있다. 상기 보호층(3)은 연질시트(4) 표면에 도포되어 상기 연질시트(4)가 태양에서 방사되는 자외선에 의해 탈색 및 변색되는 것을 방지할 수 있는데, 상기 보호층(3)은 자외선 보호 잉크를 도포하여 형성할 수 있다. 작업자는 상기 연질시트(4) 상에 상기 자외선 보호 잉크를 실사인쇄, 실크인쇄 또는 다양한 인쇄, 도포 방식을 이용하여 보호층(3)을 형성할 수 있다.
그 다음으로, 상기 보호층(3) 상에 제1 코팅층(2)을 형성할 수 있다. 상기 제1 코팅층(2)은 우레탄 합성수지, 아크릴계 수지용액 또는 에폭시계 수지용액 25 내지 35 중량부와, 직경이 10 내지 500㎛인 범위 내의 PE-열가소성 수지, 페놀수지, 멜라민수지, 에폭시수지, 폴리스티렌수지 비드 또는 유리 비드 입자 10 내지 20 중량부와, 우레탄 신너 및 톨루엔 40 내지 52 중량부, 이소시아네트 TDI(toluene d-iso cyanate), MDI(Michelson Doppler Imager) 우레탄 합성수지 경화제나, 디에틸렌트리아민(DETA), TET(Tetramethylthiurammonosulfide), 아크릴계 또는 에폭시계 경화제 2 내지 4 중량부의 비율로 혼합된 조성물을 에어스프레이 도장 방식이나 로울러 도색 방식으로 도포한 후, 10 내지 35℃의 온도에서 1시간 30분 내지 2시간 30분 자연건조할 수 있다. 이때 상기의 조성물이 경화되면서 도 2에 도시된 바와 같이 미세 크기의 요철이나 돌기를 형성하게 된다.
여기서, 작업자는 주위 기온이 낮은 동절기에는 상기 제1 코팅층(2)을 형성하는 조성물에 실리카 경화제를 더 첨가할 수 있다.
이어서, 제1 코팅층(2)을 형성한 후 상기 제1 코팅층(2) 상에 제2 코팅층(1)을 형성할 수 있다. 상기 제2 코팅층(1)은 실리콘 이형제 8 내지 12 중량부, 헥세인 40 내지 55 중량부, 톨루엔 20 내지 25 중량부 및 백금촉매 0.08 내지 0.18 중량부의 비율로 혼합된 조성물을 상기 제1 코팅층(2) 상에 에어스프레이 도장 방식이나 로울러 도색 방식으로 도포한 후, 10 내지 35℃의 온도에서 1시간 30분 내지 2시간 30분 자연건조할 수 있다. 상기 제2 코팅층(1)은 제1 코팅층(2) 상에 도포되어 얇은 필름막을 형성하고, 이러한 제2 코팅층(1)은 이형 효과를 증대시킬 수 있고 광고지의 접착제가 부착되는 것을 방지할 수 있다.
한편, 본 발명에 따른 광고지 부착 방지용 코팅시트의 제조방법에서는 빠른 경화를 위하여 백금촉매를 사용한 것을 일 예로 들어 설명하였는데, 상기 백금촉매에 초산형 또는 무초산형 실리콘을 혼합하여 사용함으로써 경화를 촉진시킬 수 있다.
다음으로, 상기 연질시트(4)의 일측면 상부에 보호층(3), 제1 코팅층(2) 및 제2 코팅층(1)을 차례로 도포하여 코팅한 후, 연질시트(4)의 타측면에 벽이나 전신주, 가로등, 이정표, 신호등과 같은 구조물에 부착 고정하기 위해 점착제층(5) 및 상기 점착제층(5)이 외부로부터 오염되는 것을 방지하여 점착력을 보호, 유지시키기 위한 이형지층(6)을 차례로 적층함으로써, 본 발명에 따른 광고지 부착 방지용 코팅시트를 완성할 수 있다.
또한, 본 발명에 따른 광고지 부착 방지용 코팅시트의 제조방법에서는 상기 제1 코팅층(2) 및 제2 코팅층(1)과 광고지와의 이형성을 증대시키기 위하여 오일을 더 첨가하여 제조할 수 있다. 상기 오일은 실리콘 오일, 파라핀 오일, 테라핀 오일 또는 페트롤 오일 중에서 선택될 수 있고, 원활한 혼합을 위하여 상기 제1 코팅층(2) 조성물 또는 제2 코팅용 조성물과 상기 오일을 교반기를 이용하여 5분 내지 15분간 강제 교반하여 제1 코팅층(2) 또는 제2 코팅층(1)을 형성하기 위한 조성물로 사용할 수 있다.
또한, 본 발명에 따른 광고지 부착 방지용 코팅시트에서는 상기 제1 코팅층(2) 및 제2 코팅층(1)을 상기 보호층(3)이 형성된 연질시트(4) 상에 도포하여 적층함으로써 제조되는 것을 일 예로 들어 설명하였는데, 시설물의 표면 상에 상기 제1 코팅층(2) 및 제2 코팅층(1)을 도포하여 적층함으로써 본 발명의 광고지 부착 방지용 코팅시트를 제조할 수도 있다. 즉, 상기 시설물은 벽이나 전신주, 가로등, 이정표, 신호등과 같은 구조물을 포함할 수 있고, 상기 제1 코팅층(2) 및 제2 코팅층(1)을 상기 시설물 상에 도포하여 코팅함으로써, 상기 시설물 상에 불법 광고지 등이 무단 부착되는 것을 방지할 수도 있다.
이상, 첨부된 도면을 참조하여 본 발명의 바람직한 일 실시예를 설명하였지만, 본 발명이 속하는 기술분야에서 통상의 지식을 가진 자라면 본 발명이 그 기술적 사상이나 필수적인 특징을 변경하지 않고서 다른 구체적인 형태로 실시될 수 있다는 것을 이해할 수 있을 것이다. 그러므로 이상에서 기술한 일 실시예는 모든 면에서 예시적인 것이며 한정적이 아닌 것으로 이해해야만 한다.

Claims (17)

  1. 합성수지재로 형성되는 연질시트;
    상기 연질시트의 일측면 상부에 위치하고, 태양에서 방사되는 자외선에 의한 탈색, 변색을 방지하는 보호층;
    상기 보호층 상부에 위치하고 미세 요철 또는 돌기가 형성된 제1 코팅층;
    상기 제1 코팅층 상에 위치하고 상기 제1 코팅층 상에 필름막으로 형성된 제2 코팅층;
    상기 연질시트 타측면 하부에 위치하고, 상기 연질시트를 고정 부착하기 위한 점착제층; 및
    상기 점착제층 하부에 위치하고, 상기 점착제층이 외부로부터 오염되는 것을 방지하여 점착력을 보호, 유지시키기 위한 이형지층을 포함하는 것을 특징으로 하는 광고지 부착 방지용 코팅시트.
  2. 제 1항에 있어서,
    상기 보호층은 자외선 보호 잉크를 상기 연질시트 상에 실사인쇄 또는 실크인쇄하여 형성되는 것을 특징으로 하는 광고지 부착 방지용 코팅시트.
  3. 제 1항에 있어서,
    상기 제1 코팅층은,
    우레탄 합성수지, 아크릴계 수지용액 또는 에폭시계 수지용액 25 내지 35 중량부와,
    PE-열가소성 수지, 페놀수지, 멜라민수지, 에폭시수지, 폴리스티렌수지 비드 또는 유리 비드 10 내지 20 중량부와,
    우레탄 신너 및 톨루엔 40 내지 52 중량부와,
    경화제 2 내지 4 중량부가 상기 연질시트 상에 도포된 후 건조되어 형성되는 것을 특징으로 하는 광고지 부착 방지용 코팅시트.
  4. 제 3항에 있어서,
    상기 경화제는 이소시아네트 TDI(toluene d-iso cyanate), MDI(Michelson Doppler Imager) 우레탄 합성수지 경화제나, 디에틸렌트리아민(DETA), TET(Tetramethylthiurammonosulfide), 아크릴계 또는 에폭시계 경화제가 사용되는 것을 특징으로 하는 광고지 부착 방지용 코팅시트.
  5. 제 3항에 있어서,
    상기 제1 코팅층은 10 내지 500㎛ 범위의 직경을 가지는 PE-열가소성 수지, 페놀수지, 멜라민수지, 에폭시수지, 폴리스티렌수지 비드 또는 유리 비드가 사용되는 것을 특징으로 하는 광고지 부착 방지용 코팅시트.
  6. 제 3항에 있어서,
    상기 제1 코팅층은 실리카 경화제가 더 포함되는 것을 특징으로 하는 광고지 부착 방지용 코팅시트.
  7. 제 1항에 있어서,
    상기 제2 코팅층은 실리콘 이형제 8 내지 12 중량부, 헥세인 40 내지 55 중량부, 톨루엔 20 내지 25 중량부 및 백금촉매 0.08 내지 0.18 중량부로 혼합된 용액이 상기 제1 코팅층 상에 도포된 후 건조되어 형성되는 것을 특징으로 하는 광고지 부착 방지용 코팅시트.
  8. 제 7항에 있어서,
    상기 제2 코팅층은 상기 제1 코팅층 상에 에어스프레이 도장 방식이나 로울러 도색 방식으로 도포되는 것을 특징으로 하는 광고지 부착 방지용 코팅시트.
  9. 제 7항에 있어서,
    상기 제2 코팅층은 10 내지 35℃의 온도에서 1시간 30분 내지 2시간 30분 동안 자연 건조되어 형성되는 것을 특징으로 하는 광고지 부착 방지용 코팅시트.
  10. 제 1항에 있어서,
    상기 제1 코팅층 또는 제2 코팅층은 오일 성분을 더 포함하는 것을 특징으로 하는 광고지 부착 방지용 코팅시트.
  11. 제 10항에 있어서,
    상기 오일 성분은 실리콘 오일, 파라핀 오일, 테라핀 오일 또는 페트롤 오일 중에서 선택되는 어느 하나인 것을 특징으로 하는 광고지 부착 방지용 코팅시트.
  12. 제 7항에 있어서,
    상기 제2 코팅층은 상기 백금촉매와 초산형 또는 무초산형 실리콘을 혼합하여 사용하는 것을 특징으로 하는 광고지 부착 방지용 코팅시트.
  13. 시설물 상부에 도포되고 미세 요철 또는 돌기가 형성된 제1 코팅층; 및
    상기 제1 코팅층 상에 도포되고 상기 제1 코팅층 상에 필름막으로 형성된 제2 코팅층을 포함하되,
    상기 제1 코팅층은 우레탄 합성수지, 아크릴계 수지용액 또는 에폭시계 수지용액 25 내지 35 중량부와, PE-열가소성 수지, 페놀수지, 멜라민수지, 에폭시수지, 폴리스티렌수지 비드 또는 유리 비드 10 내지 20 중량부와, 우레탄 신너 및 톨루엔 40 내지 52 중량부와, 경화제 2 내지 4 중량부가 상기 시설물 상에 도포된 후 건조되어 형성되며,
    상기 제2 코팅층은 실리콘 이형제 8 내지 12 중량부, 헥세인 40 내지 55 중량부, 톨루엔 20 내지 25 중량부 및 백금촉매 0.08 내지 0.18 중량부로 혼합된 용액이 상기 제1 코팅층 상에 도포된 후 건조되어 형성되는 것을 특징으로 하는 광고지 부착 방지용 코팅시트.
  14. 제 13항에 있어서,
    상기 제1 코팅층 또는 제2 코팅층은 오일 성분을 더 포함하되,
    상기 오일 성분은 실리콘 오일, 파라핀 오일, 테라핀 오일 또는 페트롤 오일 중에서 선택되는 것을 특징으로 하는 광고지 부착 방지용 코팅시트.
  15. 제 13항에 있어서,
    상기 제1 코팅층 또는 제2 코팅층은 에어스프레이 도장 방식이나 로울러 도색 방식으로 도포되는 것을 특징으로 하는 광고지 부착 방지용 코팅시트.
  16. 제 13항에 있어서,
    상기 PE-열가소성 수지, 페놀수지, 멜라민수지, 에폭시수지, 폴리스티렌수지 비드 또는 유리 비드는 10 내지 500㎛ 범위의 직경을 가지는 것을 특징으로 하는 광고지 부착 방지용 코팅시트.
  17. 제 13항에 있어서,
    상기 제2 코팅층은 상기 백금촉매와 초산형 또는 무초산형 실리콘을 혼합하여 사용하는 것을 특징으로 하는 광고지 부착 방지용 코팅시트.
PCT/KR2015/004843 2014-09-03 2015-05-14 광고지 부착 방지용 코팅시트 WO2016035972A1 (ko)