WO2016027864A1 - Procédé de fabrication de polariseur - Google Patents

Procédé de fabrication de polariseur Download PDF

Info

Publication number
WO2016027864A1
WO2016027864A1 PCT/JP2015/073413 JP2015073413W WO2016027864A1 WO 2016027864 A1 WO2016027864 A1 WO 2016027864A1 JP 2015073413 W JP2015073413 W JP 2015073413W WO 2016027864 A1 WO2016027864 A1 WO 2016027864A1
Authority
WO
WIPO (PCT)
Prior art keywords
polarizer
film
complementary color
crosslinking
boric acid
Prior art date
Application number
PCT/JP2015/073413
Other languages
English (en)
Japanese (ja)
Inventor
勇介 松岡
英樹 松久
公彦 矢可部
佑介 北河
天煕 趙
容鉉 權
崔　允碩
正寧 崔
Original Assignee
住友化学株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 住友化学株式会社 filed Critical 住友化学株式会社
Priority to CN201580044385.4A priority Critical patent/CN106662696A/zh
Priority to KR1020177007333A priority patent/KR20170045265A/ko
Priority to JP2016544252A priority patent/JPWO2016027864A1/ja
Publication of WO2016027864A1 publication Critical patent/WO2016027864A1/fr

Abstract

L'invention concerne un procédé de fabrication de polariseur. Plus précisément, l'invention concerne un procédé de fabrication de polariseur qui inclut des étapes d'expansion, de coloration, de réticulation, de compensation de couleur et de première extension d'un film pour formation de polariseur. L'étape d'expansion, l'étape de coloration, l'étape de réticulation et l'étape de compensation de couleur sont effectuées dans cet ordre. L'étape de première extension est effectuée avant l'étape de compensation de couleur. Le film pour formation de polariseur est soumis à une seconde extension selon un rapport d'extension de 1,010 à 1,100 fois lors de l'étape de compensation de couleur. Ainsi, il est possible de fabriquer un polariseur dont les variations de tonalité chromatique sont minimisées, y compris en cas de blanchiment sur une longue durée sous des conditions de hautes températures.
PCT/JP2015/073413 2014-08-22 2015-08-20 Procédé de fabrication de polariseur WO2016027864A1 (fr)

Priority Applications (3)

Application Number Priority Date Filing Date Title
CN201580044385.4A CN106662696A (zh) 2014-08-22 2015-08-20 偏振片的制造方法
KR1020177007333A KR20170045265A (ko) 2014-08-22 2015-08-20 편광자의 제조 방법
JP2016544252A JPWO2016027864A1 (ja) 2014-08-22 2015-08-20 偏光子の製造方法

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
KR10-2014-0109837 2014-08-22
KR1020140109837A KR20160023429A (ko) 2014-08-22 2014-08-22 편광자의 제조 방법

Publications (1)

Publication Number Publication Date
WO2016027864A1 true WO2016027864A1 (fr) 2016-02-25

Family

ID=55350805

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2015/073413 WO2016027864A1 (fr) 2014-08-22 2015-08-20 Procédé de fabrication de polariseur

Country Status (5)

Country Link
JP (1) JPWO2016027864A1 (fr)
KR (2) KR20160023429A (fr)
CN (1) CN106662696A (fr)
TW (1) TW201613992A (fr)
WO (1) WO2016027864A1 (fr)

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2018025764A (ja) * 2016-07-29 2018-02-15 住友化学株式会社 光学積層体
JP2018025765A (ja) * 2016-07-29 2018-02-15 住友化学株式会社 光学積層体
JP7495416B2 (ja) 2019-01-23 2024-06-04 住友化学株式会社 偏光子及びその製造方法

Families Citing this family (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN107987213B (zh) * 2017-12-28 2020-07-21 深圳市华星光电技术有限公司 偏光膜材料及其制备方法、偏光膜及其制作方法
EP3670146B1 (fr) * 2018-12-21 2023-04-12 Essilor International Procede et systeme de production d'un film a gradient de polarisation
KR20200091741A (ko) * 2019-01-23 2020-07-31 동우 화인켐 주식회사 편광자 및 이의 제조방법

Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2001296428A (ja) * 2000-04-17 2001-10-26 Nitto Denko Corp 偏光板の製造方法及び液晶表示装置
JP2005084505A (ja) * 2003-09-10 2005-03-31 Sumitomo Chemical Co Ltd 偏光フィルムとその製造方法、偏光板および光学積層体
JP2005114990A (ja) * 2003-10-07 2005-04-28 Sumitomo Chemical Co Ltd 偏光フィルムの製造方法、偏光板の製造方法および光学積層体の製造方法
JP2009015314A (ja) * 2007-06-05 2009-01-22 Japan Steel Works Ltd:The 偏光フィルムの製造方法および製造装置
JP2011164553A (ja) * 2010-02-15 2011-08-25 Sumitomo Chemical Co Ltd 偏光フィルムの製造方法

Family Cites Families (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2009069375A (ja) * 2007-09-12 2009-04-02 Sumitomo Chemical Co Ltd 偏光板の製造方法
KR100947939B1 (ko) 2007-12-26 2010-03-15 주식회사 에이스 디지텍 편광자의 제조방법
CN103149620B (zh) * 2011-12-06 2017-04-12 日东电工株式会社 偏振片的制造方法及偏光板的制造方法

Patent Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2001296428A (ja) * 2000-04-17 2001-10-26 Nitto Denko Corp 偏光板の製造方法及び液晶表示装置
JP2005084505A (ja) * 2003-09-10 2005-03-31 Sumitomo Chemical Co Ltd 偏光フィルムとその製造方法、偏光板および光学積層体
JP2005114990A (ja) * 2003-10-07 2005-04-28 Sumitomo Chemical Co Ltd 偏光フィルムの製造方法、偏光板の製造方法および光学積層体の製造方法
JP2009015314A (ja) * 2007-06-05 2009-01-22 Japan Steel Works Ltd:The 偏光フィルムの製造方法および製造装置
JP2011164553A (ja) * 2010-02-15 2011-08-25 Sumitomo Chemical Co Ltd 偏光フィルムの製造方法

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2018025764A (ja) * 2016-07-29 2018-02-15 住友化学株式会社 光学積層体
JP2018025765A (ja) * 2016-07-29 2018-02-15 住友化学株式会社 光学積層体
JP7495416B2 (ja) 2019-01-23 2024-06-04 住友化学株式会社 偏光子及びその製造方法

Also Published As

Publication number Publication date
KR20160023429A (ko) 2016-03-03
KR20170045265A (ko) 2017-04-26
CN106662696A (zh) 2017-05-10
JPWO2016027864A1 (ja) 2017-06-01
TW201613992A (en) 2016-04-16

Similar Documents

Publication Publication Date Title
JP6685915B2 (ja) 偏光子及び偏光子の製造方法
JP2015075762A (ja) 偏光子の製造方法
JP6942055B2 (ja) 偏光子及びその製造方法
WO2016027864A1 (fr) Procédé de fabrication de polariseur
JP6694821B2 (ja) 偏光子の製造方法
KR20120002815A (ko) 편광자의 제조방법
KR20110135321A (ko) 편광자의 제조방법
JP6197146B1 (ja) 偏光子の製造方法
KR20130030990A (ko) 편광자의 제조방법
JP6712595B2 (ja) 偏光子の製造方法
JP6723240B2 (ja) 偏光子の製造方法
JP2017536562A (ja) 偏光子の製造方法、これを用いて製造された偏光子及び偏光板
KR20120124903A (ko) 편광자의 제조방법
KR20210069893A (ko) 편광자의 제조방법
KR20160096385A (ko) 편광자의 제조방법

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 15834390

Country of ref document: EP

Kind code of ref document: A1

ENP Entry into the national phase

Ref document number: 2016544252

Country of ref document: JP

Kind code of ref document: A

NENP Non-entry into the national phase

Ref country code: DE

ENP Entry into the national phase

Ref document number: 20177007333

Country of ref document: KR

Kind code of ref document: A

122 Ep: pct application non-entry in european phase

Ref document number: 15834390

Country of ref document: EP

Kind code of ref document: A1