WO2015123851A1 - Procede de broyage a boulets par voie humide pour la poudre de tantale et poudre de tantale preparee par ce procede - Google Patents

Procede de broyage a boulets par voie humide pour la poudre de tantale et poudre de tantale preparee par ce procede Download PDF

Info

Publication number
WO2015123851A1
WO2015123851A1 PCT/CN2014/072353 CN2014072353W WO2015123851A1 WO 2015123851 A1 WO2015123851 A1 WO 2015123851A1 CN 2014072353 W CN2014072353 W CN 2014072353W WO 2015123851 A1 WO2015123851 A1 WO 2015123851A1
Authority
WO
WIPO (PCT)
Prior art keywords
powder
ball milling
surfactant
weight
tantalum powder
Prior art date
Application number
PCT/CN2014/072353
Other languages
English (en)
Chinese (zh)
Inventor
李仲香
程越伟
师德军
王葶
王治道
童泽堃
李霞
魏军祥
赵忠环
Original Assignee
宁夏东方钽业股份有限公司
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 宁夏东方钽业股份有限公司 filed Critical 宁夏东方钽业股份有限公司
Priority to CN201480018132.5A priority Critical patent/CN105051225A/zh
Priority to PCT/CN2014/072353 priority patent/WO2015123851A1/fr
Publication of WO2015123851A1 publication Critical patent/WO2015123851A1/fr

Abstract

La présente invention concerne un procédé de broyage à boulets par voie humide pour une poudre de tantale, ledit procédé utilisant un adjuvant de broyage contenant un milieu de broyage à boulets et un tensioactif. Le procédé présente un processus simple et une forte contrôlabilité, et le produit obtenu possède une teneur inférieure en impuretés métalliques.
PCT/CN2014/072353 2014-02-21 2014-02-21 Procede de broyage a boulets par voie humide pour la poudre de tantale et poudre de tantale preparee par ce procede WO2015123851A1 (fr)

Priority Applications (2)

Application Number Priority Date Filing Date Title
CN201480018132.5A CN105051225A (zh) 2014-02-21 2014-02-21 一种钽粉的湿式球磨方法及由该方法制备的钽粉
PCT/CN2014/072353 WO2015123851A1 (fr) 2014-02-21 2014-02-21 Procede de broyage a boulets par voie humide pour la poudre de tantale et poudre de tantale preparee par ce procede

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
PCT/CN2014/072353 WO2015123851A1 (fr) 2014-02-21 2014-02-21 Procede de broyage a boulets par voie humide pour la poudre de tantale et poudre de tantale preparee par ce procede

Publications (1)

Publication Number Publication Date
WO2015123851A1 true WO2015123851A1 (fr) 2015-08-27

Family

ID=53877538

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/CN2014/072353 WO2015123851A1 (fr) 2014-02-21 2014-02-21 Procede de broyage a boulets par voie humide pour la poudre de tantale et poudre de tantale preparee par ce procede

Country Status (2)

Country Link
CN (1) CN105051225A (fr)
WO (1) WO2015123851A1 (fr)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN114410276A (zh) * 2021-12-13 2022-04-29 长安大学 一种球磨过程控制剂的制备方法

Families Citing this family (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN112404439A (zh) * 2020-11-18 2021-02-26 贵州振华电子信息产业技术研究有限公司 一种电容器用高压钽粉及其制备方法和电容器
CN112317754A (zh) * 2020-11-18 2021-02-05 贵州振华电子信息产业技术研究有限公司 一种片状球磨钽粉及其制备方法和应用

Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20040252445A1 (en) * 2003-06-10 2004-12-16 Duan-Fan Wang Tantalum powders and methods of producing same
CN101010160A (zh) * 2004-06-28 2007-08-01 卡伯特公司 高电容钽片及其制备方法
US20090095130A1 (en) * 2007-10-15 2009-04-16 Joseph Smokovich Method for the production of tantalum powder using reclaimed scrap as source material
CN101514405A (zh) * 2009-03-09 2009-08-26 江西稀有稀土金属钨业集团有限公司 一种硬质合金混合料的制备方法

Family Cites Families (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN100560507C (zh) * 2003-05-19 2009-11-18 卡伯特公司 生产铌金属氧化物的方法和氧还原的铌氧化物

Patent Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20040252445A1 (en) * 2003-06-10 2004-12-16 Duan-Fan Wang Tantalum powders and methods of producing same
CN101010160A (zh) * 2004-06-28 2007-08-01 卡伯特公司 高电容钽片及其制备方法
US20090095130A1 (en) * 2007-10-15 2009-04-16 Joseph Smokovich Method for the production of tantalum powder using reclaimed scrap as source material
CN101514405A (zh) * 2009-03-09 2009-08-26 江西稀有稀土金属钨业集团有限公司 一种硬质合金混合料的制备方法

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN114410276A (zh) * 2021-12-13 2022-04-29 长安大学 一种球磨过程控制剂的制备方法

Also Published As

Publication number Publication date
CN105051225A (zh) 2015-11-11

Similar Documents

Publication Publication Date Title
JP4972249B2 (ja) 窒素化ニオブ粉末及びニオブ電解キャパシター
CN104841929B (zh) 一种微细铌粉及其制造方法
TWI596215B (zh) A fine tantalum powder and its preparation method
WO2015124094A1 (fr) Procédé de préparation d'une poudre de tantale pour condensateur électrolytique de fiabilité élevée et de capacité spécifique élevée
JP6211961B2 (ja) 蓄電デバイスの負極材料
CN107073575B (zh) 一种复合钽粉及其制备方法及该钽粉制备的电容器阳极
JP2019090117A (ja) 薄片粉末を製造するための低エネルギーの粉砕
CN100339172C (zh) 球化造粒凝聚金属粉末的方法,金属粉末和电解电容器阳极
WO2015096048A1 (fr) Poudre de tantale à haut volume spécifique pour condensateur améliorant les performances électriques et son procédé de préparation
WO2015123851A1 (fr) Procede de broyage a boulets par voie humide pour la poudre de tantale et poudre de tantale preparee par ce procede
JP6231760B2 (ja) リチウムイオン二次電池負極活物質用Ｓｉ合金粉末およびその製造方法
JP2014058712A (ja) タンタル粒子の製造方法
CN103934452A (zh) 一种超高比容钽粉末的团化方法及由该方法制备的钽粉末
JP6242814B2 (ja) ニオブコンデンサ陽極用化成体及びその製造方法
EP3056299A1 (fr) Procédé de production de poudre granulée de niobium
JP6977021B2 (ja) 薄片状タンタル粉末およびその調製方法
WO2012073879A1 (fr) Cible de pulvérisation
JP6258222B2 (ja) ニオブコンデンサ陽極用化成体及びその製造方法
CN103878364B (zh) 一种改善了耐电压性能的中压钽粉的制备方法
JP2003299977A (ja) タンタル粉末またはニオブ粉末の製造方法
JP2018100426A (ja) 金属造粒粒子の製造方法
JP2000294235A (ja) 電池用水素吸蔵合金粉末及びその製造方法

Legal Events

Date Code Title Description
WWE Wipo information: entry into national phase

Ref document number: 201480018132.5

Country of ref document: CN

121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 14882901

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 14882901

Country of ref document: EP

Kind code of ref document: A1