WO2015064575A1 - Corps moulé en forme de plaque - Google Patents

Corps moulé en forme de plaque Download PDF

Info

Publication number
WO2015064575A1
WO2015064575A1 PCT/JP2014/078637 JP2014078637W WO2015064575A1 WO 2015064575 A1 WO2015064575 A1 WO 2015064575A1 JP 2014078637 W JP2014078637 W JP 2014078637W WO 2015064575 A1 WO2015064575 A1 WO 2015064575A1
Authority
WO
WIPO (PCT)
Prior art keywords
methacrylic
mass
plate
ester
resin composition
Prior art date
Application number
PCT/JP2014/078637
Other languages
English (en)
Japanese (ja)
Inventor
卓郎 新村
淳裕 中原
敦 松村
宙 小澤
Original Assignee
株式会社クラレ
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 株式会社クラレ filed Critical 株式会社クラレ
Priority to JP2015545007A priority Critical patent/JP6360490B2/ja
Publication of WO2015064575A1 publication Critical patent/WO2015064575A1/fr

Abstract

Cette invention concerne un corps moulé en forme de plaque obtenu par moulage d'une composition de résine méthacrylique qui contient de 50 à 90 % en poids de motifs structuraux dérivés du méthacrylate de méthyle et de 10 à 50 % en poids de motifs structuraux dérivés d'un ester hydrocarboné alicyclique d'acide méthacrylique, la composition de résine méthacrylique ayant un indice de jaunissement (YI) de 10 ou moins à une longueur de trajet optique de 200 mm, et contenant 1,0 % en poids ou moins dudit ester hydrocarboné alicyclique d'acide méthacrylique. Une plaque de type conduit de lumière constituée par le corps moulé en forme de plaque est en outre décrite.
PCT/JP2014/078637 2013-10-28 2014-10-28 Corps moulé en forme de plaque WO2015064575A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
JP2015545007A JP6360490B2 (ja) 2013-10-28 2014-10-28 板状成形体

Applications Claiming Priority (4)

Application Number Priority Date Filing Date Title
JP2013223772 2013-10-28
JP2013-223772 2013-10-28
JP2014012852 2014-01-27
JP2014-012852 2014-01-27

Publications (1)

Publication Number Publication Date
WO2015064575A1 true WO2015064575A1 (fr) 2015-05-07

Family

ID=53004177

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2014/078637 WO2015064575A1 (fr) 2013-10-28 2014-10-28 Corps moulé en forme de plaque

Country Status (3)

Country Link
JP (1) JP6360490B2 (fr)
TW (1) TWI646139B (fr)
WO (1) WO2015064575A1 (fr)

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2018124069A1 (fr) * 2016-12-27 2018-07-05 株式会社クラレ Copolymère méthacrylique et article moulé
EP3760675A1 (fr) * 2019-07-05 2021-01-06 Trinseo Europe GmbH Compositions polymérisables et copolymères d'esters de (méth)acrylate avec de l'alkyle (méthacrylates) et/ou des monomères polymérisable de radicaux libres
US11649347B2 (en) 2019-10-08 2023-05-16 Trinseo Europe Gmbh Impact modified copolymers of (meth)acrylate esters and/or free radically polymerizable monomers containing nucleophilic groups

Citations (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS6317909A (ja) * 1986-07-09 1988-01-25 Hitachi Chem Co Ltd 重合体からなる光学機器
JP2003128707A (ja) * 2001-10-29 2003-05-08 Mitsubishi Gas Chem Co Inc 光学材料用メタクリル樹脂及びその製造方法
JP2005308781A (ja) * 2004-04-16 2005-11-04 Mitsubishi Rayon Co Ltd 短波長型半導体レーザー用ピックアップレンズ
WO2012141453A2 (fr) * 2011-04-13 2012-10-18 Lg Chem, Ltd. Procédé de préparation d'une composition de résine pour film optique par polymérisation en masse continue et procédés de préparation d'un film optique et d'une plaque de polarisation utilisant ladite composition de résine
WO2012165918A2 (fr) * 2011-06-01 2012-12-06 주식회사 엘지화학 Composition de résine pour film optique et film optique l'employant
WO2013161266A1 (fr) * 2012-04-27 2013-10-31 株式会社クラレ Composition de résine (méth)acrylique
WO2013161267A1 (fr) * 2012-04-27 2013-10-31 株式会社クラレ Composition de résine méthacrylique
WO2014073215A1 (fr) * 2012-11-09 2014-05-15 株式会社クラレ Composition de résine méthacrylique

Family Cites Families (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS59227909A (ja) * 1983-06-09 1984-12-21 Sumitomo Chem Co Ltd 低吸湿性メタクリル系樹脂製の光学機器
JPS62151805A (ja) * 1985-12-26 1987-07-06 Mitsubishi Rayon Co Ltd プラスチツク光伝送性繊維
JP2752458B2 (ja) * 1989-09-27 1998-05-18 株式会社クラレ メタクリル系ポリマーの製造方法
KR101508038B1 (ko) * 2011-06-01 2015-04-08 주식회사 엘지화학 광학 필름용 수지 조성물 및 이를 이용한 광학 필름
JP2013203840A (ja) * 2012-03-28 2013-10-07 Sumitomo Chemical Co Ltd 連続重合装置の操作方法
JP2014012781A (ja) * 2012-07-05 2014-01-23 Sumitomo Chemical Co Ltd メタクリル系重合体組成物の製造方法
JP6002017B2 (ja) * 2012-12-03 2016-10-05 住友化学株式会社 メタクリル系重合体組成物の製造方法

Patent Citations (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS6317909A (ja) * 1986-07-09 1988-01-25 Hitachi Chem Co Ltd 重合体からなる光学機器
JP2003128707A (ja) * 2001-10-29 2003-05-08 Mitsubishi Gas Chem Co Inc 光学材料用メタクリル樹脂及びその製造方法
JP2005308781A (ja) * 2004-04-16 2005-11-04 Mitsubishi Rayon Co Ltd 短波長型半導体レーザー用ピックアップレンズ
WO2012141453A2 (fr) * 2011-04-13 2012-10-18 Lg Chem, Ltd. Procédé de préparation d'une composition de résine pour film optique par polymérisation en masse continue et procédés de préparation d'un film optique et d'une plaque de polarisation utilisant ladite composition de résine
WO2012165918A2 (fr) * 2011-06-01 2012-12-06 주식회사 엘지화학 Composition de résine pour film optique et film optique l'employant
WO2013161266A1 (fr) * 2012-04-27 2013-10-31 株式会社クラレ Composition de résine (méth)acrylique
WO2013161267A1 (fr) * 2012-04-27 2013-10-31 株式会社クラレ Composition de résine méthacrylique
WO2014073215A1 (fr) * 2012-11-09 2014-05-15 株式会社クラレ Composition de résine méthacrylique

Cited By (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2018124069A1 (fr) * 2016-12-27 2018-07-05 株式会社クラレ Copolymère méthacrylique et article moulé
CN110036047A (zh) * 2016-12-27 2019-07-19 株式会社可乐丽 甲基丙烯酸类共聚物和成型体
JPWO2018124069A1 (ja) * 2016-12-27 2019-10-31 株式会社クラレ メタクリル共重合体および成形体
US10875996B2 (en) 2016-12-27 2020-12-29 Kuraray Co., Ltd. Methacrylic copolymer and molded article
CN110036047B (zh) * 2016-12-27 2021-01-05 株式会社可乐丽 甲基丙烯酸类共聚物和成型体
EP3760675A1 (fr) * 2019-07-05 2021-01-06 Trinseo Europe GmbH Compositions polymérisables et copolymères d'esters de (méth)acrylate avec de l'alkyle (méthacrylates) et/ou des monomères polymérisable de radicaux libres
WO2021004996A1 (fr) * 2019-07-05 2021-01-14 Trinseo Europe Gmbh Compositions polymérisables et copolymères d'esters de (méth)acrylate cycliques et de (méthacrylates) d'alkyle et/ou de monomères polymérisables par voie radicalaire
US11649347B2 (en) 2019-10-08 2023-05-16 Trinseo Europe Gmbh Impact modified copolymers of (meth)acrylate esters and/or free radically polymerizable monomers containing nucleophilic groups

Also Published As

Publication number Publication date
TW201527390A (zh) 2015-07-16
JP6360490B2 (ja) 2018-07-18
JPWO2015064575A1 (ja) 2017-03-09
TWI646139B (zh) 2019-01-01

Similar Documents

Publication Publication Date Title
JP6228225B2 (ja) メタクリル樹脂組成物の製造方法
KR102164738B1 (ko) (메트)아크릴 수지 조성물의 제조 방법
KR101958051B1 (ko) (메트)아크릴 수지 조성물
KR102005135B1 (ko) (메트)아크릴 수지 조성물의 제조 방법
JP6259400B2 (ja) メタクリル樹脂組成物
JP6230532B2 (ja) メタクリル樹脂組成物並びにその成形品および製造方法
JP6360490B2 (ja) 板状成形体
JP6097741B2 (ja) （メタ）アクリル樹脂組成物からなる成形品の製造方法
JP7184793B2 (ja) メタクリル樹脂、メタクリル樹脂組成物及び成形体
JP6046707B2 (ja) メタクリル樹脂組成物
JP7442520B2 (ja) メタクリル共重合体および成形品
WO2018124069A1 (fr) Copolymère méthacrylique et article moulé

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 14857496

Country of ref document: EP

Kind code of ref document: A1

ENP Entry into the national phase

Ref document number: 2015545007

Country of ref document: JP

Kind code of ref document: A

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 14857496

Country of ref document: EP

Kind code of ref document: A1