WO2014163299A1 - 터치패널용 점착제 조성물, 점착 필름 및 터치 패널 - Google Patents

터치패널용 점착제 조성물, 점착 필름 및 터치 패널 Download PDF

Info

Publication number
WO2014163299A1
WO2014163299A1 PCT/KR2014/001622 KR2014001622W WO2014163299A1 WO 2014163299 A1 WO2014163299 A1 WO 2014163299A1 KR 2014001622 W KR2014001622 W KR 2014001622W WO 2014163299 A1 WO2014163299 A1 WO 2014163299A1
Authority
WO
WIPO (PCT)
Prior art keywords
meth
acrylate
adhesive composition
group
containing monomer
Prior art date
Application number
PCT/KR2014/001622
Other languages
English (en)
French (fr)
Inventor
윤찬오
박은경
정부기
이재관
김장순
박성찬
김원호
Original Assignee
(주)엘지하우시스
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by (주)엘지하우시스 filed Critical (주)엘지하우시스
Priority to JP2016506223A priority Critical patent/JP6545659B2/ja
Priority to EP14778676.8A priority patent/EP2982723B1/en
Priority to US14/782,329 priority patent/US20160152868A1/en
Priority to CN201480020301.9A priority patent/CN105102564B/zh
Publication of WO2014163299A1 publication Critical patent/WO2014163299A1/ko

Abstract

친수성 관능기 함유 단량체를 포함하고, 100kHz 내지 2MHz 영역의 주파수에서 유전율이 3.5이하인 터치패널용 점착제 조성물 및 상기 터치패널용 점착제 조성물의 경화물을 포함하는 점착제층을 포함하는 점착필름을 제공한다. 또한, 일면에 도전층이 형성된 전도성 플라스틱 필름; 및 상기 도전층에 부착되고, 상기 터치패널용 점착제 조성물의 경화물을 포함하는 점착제층을 포함하는 터치패널을 제공한다.

Description

터치패널용 점착제 조성물, 점착 필름 및 터치 패널
터치패널용 점착제 조성물, 점착 필름 및 터치 패널에 관한 것이다.
근래, PDA, 이동통신 단말기 또는 차량용 네비게이션 등과 같은 전자 기기가 큰 시장을 형성하고 있다. 이와 같은 전자 기기에 있어서, 추구되는 기술적 목표는 주로 박형화, 경량화, 저전력 소비화, 고해상도화 및 고휘도화 등을 들 수 있다.
한편, 입력 조작부에 터치스크린 또는 터치패널 스위치가 설치된 전자 기기는, 경량화 및 깨짐 방지 등을 위하여, 투명 도전성 플라스틱 필름이 사용되고 있다. 그 예로는, 폴리에틸렌테레프탈레이트(PolyEthylenTerephthalate, PET) 필름을 기재로 하고, 그 일면에 인듐 주석 산화물(Indium Tin Oxide, ITO) 등의 도전층을 형성한 필름이 있으며, 상기 필름은 점착제층에 의해 전도성 유리, 보강재 또는 데코 필름 등에 적층되어 있다.
터치스크린 또는 터치패널에서 투명 도전성 필름의 부착에 사용되는 점착제에는 터치패널의 민감도 개선을 위해 유전율이 낮고, 고온 또는 고습조건과 같은 가혹 조건에 노출되었을 경우 백탁현상의 발생을 억제할 수 있는 내구성 등의 다양한 물성이 요구된다.
본 발명의 일 구현예는 터치패널에 대한 민감도 및 백탁현상에 대한 신뢰성이 우수한 터치패널용 점착제 조성물을 제공한다.
본 발명의 다른 구현예는 상기 터치패널용 점착제 조성물을 이용한 점착 필름을 제공한다.
본 발명의 또 다른 구현예는 상기 점착 필름을 적용한 터치 패널을 제공한다.
본 발명의 일 구현예에서, 친수성 관능기 함유 단량체를 포함하고, 100kHz 내지 2MHz 영역의 주파수에서 유전율이 3.5이하인 터치패널용 점착제 조성물 제공한다.
상기 친수성 관능기 함유 단량체가 수산기 함유 단량체, 아미노기 함유 단량체, 카르복실기 함유 단량체, 설폰기 함유 단량체, 모르폴린기 함유 단량체, 글리시딜기 함유 단량체 및 이들의 조합으로 이루어진 군으로부터 선택된 하나 이상일 수 있다.
상기 친수성 관능기 함유 단량체가 (메타) 아크릴산 에스테르계 단량체 100중량부에 대해서 약 30중량부 이하일 수 있다.
상기 (메타) 아크릴산 에스테르계 단량체 및 상기 친수성 관능기 함유 단량체의 중합체 분자량이 각각 약 60만 내지 약 120만일 수 있다.
상기 (메타)아크릴산 에스테르계 단량체가 알킬(메타)아크릴레이트이고, 상기 알킬(메타)아크릴레이트의 알킬은 선형 또는 분지형 C1 내지 C14 알킬일 수 있다.
상기 (메타) 아크릴산 에스테르계 단량체가 메틸 (메타)아크릴레이트, 에틸 (메타)아크릴레이트, n-프로필 (메타)아크릴레이트, 이소프로필 (메타)아크릴레이트, n-부틸 (메타)아크릴레이트, t-부틸 (메타)아크릴레이트, sec-부틸 (메타)아크릴레이트, 펜틸 (메타)아크릴레이트, 2-에틸헥실 (메타)아크릴레이트, 2-에틸부틸 (메타)아크릴레이트, n-옥틸 (메타)아크릴레이트, 이소옥틸 (메타)아크릴레이트, 이소노닐 (메타)아크릴레이트, 라우릴 (메타)아크릴레이트, 테트라데실 (메타)아크릴레이트 및 이들의 조합으로 이루어진 군으로부터 선택된 하나 이상일 수 있다.
점착증진제를 더 포함할 수 있다.
상기 점착증진제는 아민계 액상 고분자, 폴리 아민, 석유수지, 폴리부텐, 아크릴계 변성수지, 아크릴로일 모폴라인 수지 및 이들의 조합으로 이루어진 군으로부터 선택된 하나 이상일 수 있다.
광개시제를 더 포함할 수 있다.
상기 광개시제는 벤조인계 개시제, 히드록시 케톤계 개시제, 아미노 케톤계 개시제 카프로락탐 및 이들의 조합으로 이루어진 군으로부터 선택된 하나 이상일 수 있다.
본 발명의 다른 구현예에서, 상기 터치패널용 점착제 조성물의 경화물을 포함하는 점착제층을 포함하는 점착필름 제공한다.
상기 점착제층의 유전율은 약 100kHz 내지 약 2MHz 영역의 주파수에서 약 3.5이하일 수 있다.
상기 점착제층의 두께가 약 50㎛ 내지 약 300㎛일 수 있다.
본 발명의 또 다른 구현예에서, 일면에 도전층이 형성된 전도성 플라스틱 필름; 및 상기 도전층에 부착되고, 상기 터치패널용 점착제 조성물의 경화물을 포함하는 점착제층을 포함하는 터치패널을 제공한다.
상기 전도성 필라스틱 필름이 ITO(도전성 금속 산화물)층이 일면에 형성된 폴리에틸렌테레프탈레이트 필름일 수 있다.
상기 터치패널용 점착제 조성물은 터치패널에 대한 민감도 및 백탁현상에 대한 신뢰성이 우수한 점착필름을 제공할 수 있다.
도 1은 본 발명의 일 구현예에 따른 점착 필름의 개략적인 단면도이다.
도 2은 본 발명의 다른 구현예들에 따른 터치 패널의 개략적인 단면도이다.
도 3은 본 발명의 또 다른 구현예들에 따른 터치 패널의 개략적인 단면도이다.
도 4는 실시예 및 비교예에서 제조된 점착필름에 대하여 주파수에 대한 유전율을 도시한 그래프이다.
도 5는 실시예 및 비교예에서 제조된 점착필름에 대하여 박리력을 측정하여 도시한 그래프이다.
도 6은 실시예 및 비교예에서 제조된 점착필름의 백탁현상여부를 측정하여 도시한 그래프이다.
이하, 본 발명의 구현예를 상세히 설명하기로 한다. 다만, 이는 예시로서 제시되는 것으로, 이에 의해 본 발명이 제한되지는 않으며 본 발명은 후술할 청구항의 범주에 의해 정의될 뿐이다.
본 발명을 명확하게 설명하기 위해서 설명과 관계없는 부분은 생략하였으며, 명세서 전체를 통하여 동일 또는 유사한 구성요소에 대해서는 동일한 참조 부호를 붙이도록 한다.
도면에서 여러 층 및 영역을 명확하게 표현하기 위하여 두께를 확대하여 나타내었다. 그리고 도면에서, 설명의 편의를 위해, 일부 층 및 영역의 두께를 과장되게 나타내었다.
이하에서 기재의 “상부 (또는 하부)” 또는 기재의 “상 (또는 하)”에 임의의 구성이 형성된다는 것은, 임의의 구성이 상기 기재의 상면 (또는 하면)에 접하여 형성되는 것을 의미할 뿐만 아니라, 상기 기재와 기재 상에 (또는 하에) 형성된 임의의 구성 사이에 다른 구성을 포함하지 않는 것으로 한정하는 것은 아니다.
터치패널용 점착제 조성물
본 발명의 일 구현예에서, 친수성 관능기 함유 단량체를 포함하고, 100kHz 내지 2MHz 영역의 주파수에서 유전율이 약 3.5이하인 터치패널용 점착제 조성물을 제공한다.
이 때, 상기 유전율은 부도체의 전기적인 특성을 나타내는 값으로, 구체적으로 초기 전기장을 기준으로 전기장이 얼마나 약해졌는지를 의미한다. 용매 및 공중합체의 극성 정도를 유전율로 표현할 수 있는바, 유극성으로 극성이 높은 경우는 유전율이 높게, 무극성으로 극성이 낮은 경우는 유전율이 낮게 측정된다.
터치패널용 점착제 조성물을 형성하는 통상의 3차원 공중합체 등은 대부분 아크릴계 조성물로써 대체로 유전율이 높았으며 유전율을 조절하기에는 어려움이 있었다. 유전율이 높은 경우 초기전기장에 비해 전기장이 많이 약해진 것을 의미하는 것으로 점착제 조성물을 터치패널에 적용하여 터치등의 자극이 있는 경우에도 약해진 전기장에 의해 신호인식이 되지 않아 민감도가 떨어질 수 있다. 이에, 본 발명의 일 구현예에서는 통상의 점착제 조성물과 대비하여 터치등의 자극에 대한 점착제 조성물의 민감도를 개선하기 위해 일정수준 이하의 유전율을 확보할 수 있게 하였다.
상기 점착제 조성물에 있어서 친수성 관능기 함유 단량체를 포함함으로써, 터치패널용 점착제 조성물의 유전율은 100kHz 내지 2MHz 영역의 주파수에서 3.5이하로 측정될 수 있다. 상기 유전율이 100kHz 내지 2MHz 영역의 주파수에서 3.5이하를 나타내는 것은 종래에 비해 낮은 유전율을 확보하는 것으로 상기 점착제 조성물이 터치 등의 자극에 대한 신호향상으로 인해 민감도가 상승할 수 있고, 민감도 개선으로 인해 빠른 반응속도를 나타내는 점착필름을 확보할 수 있다.
상기 친수성 관능기 함유 단량체가 수산기 함유 단량체, 아미노기 함유 단량체, 카르복실기 함유 단량체, 설폰기 함유 단량체, 모르폴린기 함유 단량체, 글리시딜기 함유 단량체 및 이들의 조합으로 이루어진 군으로부터 선택된 하나 이상일 수 있다.
상기 수산기 함유 단량체로서는 예컨대, 2-히드록시에틸(메타)아크릴레이트, 4-히드록시부틸(메타)아크릴레이트, 5-히드록시펜틸(메타)아크릴레이트, 6-히드록시헥실(메타)아크릴레이트, 8-히드록시옥틸(메타)아크릴레이트, 10-히드록시데실(메타)아크릴레이트, (4-히드록시메틸시클로헥실)메틸(메타) 아크릴레이트 등의 (메타)아크릴산히드록시알킬에스테르, 카프로락톤 변성 2-히드록시에틸(메타)아크릴레이트 등의 카프로락톤 변성 모노머, 2-아크릴로일옥시에틸-2-히드록시에틸프탈산, N-메틸올(메타)아크릴아미드, N-히드록시에틸(메타)아크릴아미드 등의 1급 수산기 함유 모노머; 2-히드록시프로필(메타)아크릴레이트, 2-히드록시부틸(메타)아크릴레이트, 2-히드록시-3-페녹시프로필(메타)아크릴레이트, 3-클로로-2-히드록시프로필(메타)아크릴레이트, 2-히드록시-3-페녹시프로필(메타)아크릴레이트 등의 2급 수산기 함유 모노머; 2,2-디메틸-2-히드록시에틸(메타)아크릴레이트 등의 3급 수산기 함유 모노머를 들 수 있다.
상기 수산기 함유 단량체 중에서도, 2-히드록시에틸(메타)아크릴레이트를 사용하는 것이, 디(메타)아크릴레이트 등의 불순물이 적고, 제조하기 쉬운 점에서 특히 바람직하다.
상기 아미노기 함유 단량체로서는, 예컨대, 디메틸아미노에틸(메타) 아크릴레이트, 디에틸아미노에틸(메타)아크릴레이트 등을 들 수 있다.
상기 카르복실기 함유 단량체로서는, 예컨대, 아크릴산, 메타크릴산, 크로톤산, 말레산, 무수말레산, 이타콘산, 푸마르산, 아크릴아미드 N-글리콜산, 계피산, (메타)아크릴산의 마이클 부가물(예컨대, 아크릴산 다이머, 메타크릴산 다이머, 아크릴산 트라이머, 메타크릴산 트라이머, 아크릴산 테트라머, 메타크릴산 테트라머 등), 2-(메타)아크릴로일옥시에틸디카르복실산모노에스테르(예컨대, 2-아크릴로일옥시에틸숙신산모노에스테르, 2-메타크릴로일옥시에틸숙신산모노에스테르, 2-아크릴로일옥시에틸프탈산모노에스테르, 2-메타크릴로일옥시에틸프탈산모노 에스테르, 2-아크릴로일옥시에틸헥사히드로프탈산모노에스테르, 2-메타크릴로일옥시에틸헥사히드로프탈산모노에스테르 등) 등을 들 수 있다.
상기 설폰기 함유 단량체로서는, 예컨대, 에틸렌설폰, 알릴설폰, 메타알릴설폰 등의 올레핀설폰, 2-아크릴아미드-2-메틸프로판설폰, 스티렌설폰 또는 그의 염 등을 들 수 있다. 상기 모르필린기 함유 단량체로서는 4-메틸모르필린(4-Methylmorpholine), 상기 글리시딜기 함유 단량체로서는, 예컨대, 글리시딜(메타) 아크릴레이트, 알릴글리시딜에테르 등을 들 수 있다.
상기 친수성 관능기 함유 단량체는 (메타) 아크릴산 에스테르계 단량체 100중량부에 대하여 약 30중량부 이하를 포함할 수 있다. 상기 점착제 조성물의 극성을 낮추기 위해 극성이 큰 친수성 관능기 함유 단량체의 함량을 한정할 수 있는바, 구체적으로, (메타) 아크릴산 에스테르계 단량체 100중량부에 대하여, 친수성 관능기 함유 단량체를 약 30중량부 이하, 보다 구체적으로는 약 20중량부 이하를 포함하는 점착제 조성물을 제공할 수 있다.
상기 친수성 관능기 함유 단량체는 수산기(-OH), 카르복실기(-COOH)등을 포함하고 있어 대부분의 경우 큰 극성을 유지하는 바, 상기 친수성 관능기 함유 단량체를 30중량부 이하로 포함함으로써 상기 점착제 조성물의 전체적인 극성이 감소되고, 이로 인해 유전율이 감소될 수 있다.
상기 (메타) 아크릴산 에스테르계 단량체 및 상기 친수성 관능기 함유 단량체의 중합체 분자량이 각각 약 60만 내지 약 120만일 수 있다. 상기 중합체 분자량이 120만을 초과하는 경우 점착제 조성물의 비중이 커지는 문제점이 있고, 60만 미만인 경우 내구성이 취약할 우려가 있다. 그러므로 상기 중합체의 분자량이 상기 범위를 유지함으로써 점도유지를 통한 가공 안정성 및 내구성 확보라는 점에서 장점이 있다.
상기 (메타)아크릴산 에스테르 단량체는, 예를 들어, 알킬(메타) 아크릴레이트일 수 있고, 이에 한정되지 않는다. 상기 알킬(메타)아크릴레이트의 알킬은 선형 또는 분지형 C1-C14 알킬일 수 있고, 구체적으로 C1-C8 알킬일 수 있다. 상기 범위의 탄소수의 알킬 (메타)아크릴레이트를 사용하여 상기 터치패널용 점착제 조성물의 경화물이 적절한 응집력, 박리력 및 점착 특성을 가지도록 조절할 수 있다.
상기 (메타) 아크릴산 에스테르계 단량체가 메틸 (메타)아크릴레이트, 에틸 (메타)아크릴레이트, n-프로필 (메타)아크릴레이트, 이소프로필 (메타)아크릴레이트, n-부틸 (메타)아크릴레이트, t-부틸 (메타)아크릴레이트, sec-부틸 (메타)아크릴레이트, 펜틸 (메타)아크릴레이트, 2-에틸헥실 (메타)아크릴레이트, 2-에틸부틸 (메타)아크릴레이트, n-옥틸 (메타)아크릴레이트, 이소옥틸 (메타)아크릴레이트, 이소노닐 (메타)아크릴레이트, 라우릴 (메타)아크릴레이트, 테트라데실 (메타)아크릴레이트 및 이들의 조합으로 이루어진 군으로부터 선택된 하나 이상일 수 있다.
상기 터치패널용 점착제 조성물은 점착증진제를 더 포함할 수 있다. 상기 점착증진제는 점착제 조성물이 포함하는 단량체가 서로 잘 중합되게 하고 점착수준을 향상시키기 위해 추가될 수 있다. 또한, 점착증진제를 추가함으로써 친수성 관능기 함유 단량체들의 함량을 한정하였는바 점착물성이 저하될 수 있고, 극성이 감소되어 고온고습등의 외부환경에서 액정표시장치등에 적용된 점착제 조성물의 백탁현상을 억제할 수 있다.
점착증진제의 함유 함량에 제한이 있는 것은 아니나, 구체적으로, 점착증진제는 (메타) 아크릴산 에스테르계 단량체 100중량부에 대하여 약 1중량부 내지 약 20중량부일 수 있다. 상기 점착증진제가 상기 (메타) 아크릴산 에스테르계 단량체 100중량부에 대하여, 약 1중량부 미만인 경우 점착증진효과가 미흡한 문제점이 있고, 약 20중량부를 초과하는 경우 상기 점착제 조성물의 자체 응집 현상이 발생하거나 미반응물이 이동할 우려가 있다. 그러므로, 점착증진제가 상기 범위의 함량을 유지함으로써 상기 점착제 조성물과의 상용성을 유지하고, 물성을 안정적이게 구현하는데에 장점이 있다.
상기 점착증진제의 종류에는 제한이 없으나, 아민계 액상 고분자, 폴리 아민, 석유수지, 폴리부텐, 아크릴계 변성수지, 아크릴로일 모폴라인(acryloyl morpholine) 수지 및 이들의 조합으로 이루어진 군으로부터 선택된 하나를 이상을 포함할 수 있다.
상기 터치패널용 점착제 조성물은 광개시제를 더 포함할 수 있다. 구체적으로, 상기 (메타) 아크릴산 에스테르계 단량체 100중량부에 대하여, 광중합 개시제 약 0.5 내지 약 1.0중량부를 추가로 포함할 수 있다. 상기 광중합 개시제가 상기 범위를 벗어나는 경우, 결합길이가 짧은 분자들이 많이 생성되어 내구성이 취약할 우려가 있다. 상기 광개시제의 종류에는 제한이 없으나, 벤조인계 개시제, 히드록시 케톤계 개시제, 아미노 케톤계 개시제 카프로락탐 및 이들의 조합으로 이루어진 군으로부터 선택된 하나를 포함할 수 있다.
점착필름
본 발명의 다른 구현예에서, 친수성 관능기 함유 단량체를 포함하고, 100kHz 내지 2MHz 영역의 주파수에서 유전율이 3.5이하인 터치패널용 점착제 조성물의 경화물을 포함하는 점착제층으로 이루어진 점착필름을 제공한다.
상기 터치패널용 점착제 조성물을 경화함에 있어서, 원자외선, 자외선, 근자외선, 적외선 등의 광선, X선, γ선 등의 전자파외에, 전자선, 프로톤선, 중성 자선 등을 이용할 수 있으나, 경화 속도, 조사 장치의 입수의 용이성, 가격 등으로부터 자외선 조사에 의한 경화가 유리하다.
그리고, 상기 자외선 조사를 행할 때의 광원으로서는, 고압 수은등, 무전극 램프, 초고압 수은등 카본 아크등, 크세논등, 메탈핼라이드 램프, 케미컬 램프, 블랙라이트 등이 이용된다. 상기 고압 수은 램프의 경우에는, 예컨대, 약 5mJ/㎠ 내지 3000mJ/㎠, 바람직하게는 약 10mJ/㎠ 내지 약 1000mJ/㎠의 조건에서 행해진다. 또한, 상기 무전극 램프의 경우에는, 예컨대, 약 2mJ/㎠ 내지 약 1500mJ/㎠, 바람직하게는 약 5 mJ/㎠ 내지 약 500mJ/㎠의 조건에서 행해진다.
그리고, 조사시간은, 광원의 종류, 광원과 도포면과의 거리, 도공 두께, 그 외의 조건에 따라서도 다르지만, 통상은, 수초 내지 수십초, 경우에 따라서는 수분의 1초여도 된다.
전술한 경화방법에 의해 경화된 상기 터치패널용 점착제 조성물의 경화물을 포함하는 점착제층의 유전율은 100kHz 내지 2MHz 영역의 주파수에서 3.5이하일 수 있다. 상기 유전율이 100kHz 내지 2MHz 영역의 주파수에서 3.5이하를 나타내는 것은 종래에 비해 낮은 유전율을 확보하는 것으로 상기 점착제 조성물이 터치 등의 자극에 대한 신호향상으로 인해 민감도가 상승할 수 있고, 민감도 개선으로 인해 빠른 반응속도를 나타내는 점착필름을 제공할 수 있다.
도 1은 본 발명의 일 구현예에 따른 점착필름의 개략적인 단면도로, 점착필름(100)은 위로부터 기재층(20), 점착제층(10), 기재층(20)을 포함할 수 있다. 상기 점착제층(10)의 두께는 약 50 ㎛ 내지 약 300 ㎛, 구체적으로 약 50 ㎛ 내지 약 150 ㎛일 수 있다. 상기 점착제층(10)이 상기 범위의 두께를 갖도록 하여, 박형의 터치 패널 또는 터치 스크린에 적용 가능하면서도, 내구성이 우수한 점착 필름(100)을 구현할 수 있다.
상기 기재층(10)의 구체적인 종류는 특별히 한정되지 않으며, 예를 들면, 이 분야의 일반적인 플라스틱 필름을 사용할 수 있다. 예를 들면, 상기 기재층(10)으로서, 폴리에틸렌테레프탈레이트, 폴리테트라플루오르에틸렌, 폴리에틸렌, 폴리프로필렌, 폴리부텐, 폴리부타디엔, 염화비닐 공중합체, 폴리우레탄, 에틸렌-비닐아세테이트, 에틸렌-프로필렌 공중합체, 에틸렌-아크릴산 에틸 공중합체, 에틸렌-아크릴산 메틸 공중합체, 폴리이미드 및 이들의 조합으로 이루어진 군으로부터 선택된 하나를 사용할 수 있다. 구체적으로, 상기 기재층(11)은 폴리에틸렌테레프탈레이트 필름을 사용할 수 있으나, 이에 제한되는 것은 아니다.
상기 기재층(10)의 두께는 약 25 ㎛ 내지 약 300 ㎛, 구체적으로 약 30 ㎛ 내지 약 200㎛일 수 있다. 상기 기재층(10)이 상기 범위의 두께를 갖도록 하여, 박형의 터치 패널 또는 터치 스크린에 적용 가능하면서도, 내구성이 우수한 점착 필름(100)을 구현할 수 있다.
터치패널
본 발명의 또다른 구현예에서, 일면에 도전층이 형성된 전도성 플라스틱 필름; 및 상기 도전층에 부착되고, 친수성 관능기 함유 단량체를 포함하고, 1100kHz 내지 2MHz 영역의 주파수에서 유전율이 3.5이하인 터치패널용 점착제 조성물의 경화물을 포함하는 점착제층으로 이루어지는 터치패널을 제공한다.
도 2를 참고하면, 상기 터치 패널(200)은, 플라스틱 기재층(40) 및 상기 플라스틱 기재층(40)의 일면에 형성된 도전층(30)을 포함하는 전도성 플라스틱 필름(50)을 포함하고, 상기 점착제층(10)이 상기 전도성 플라스틱 필름(50)의 도전층(30)의 일면에 부착된 구조를 가질 수 있다. 또한, 도 3과 같이, 상기 점착제층(10)이 상기 전도성 플라스틱 필름(50)의 도전층(30)의 양면에 부착된 구조를 가질 수 있다.
상기 터치 패널은, 예를 들면, 정전용량 방식의 터치 패널일 수 있다. 또한, 상기 터치 패널의 구체적인 구조 또는 그 형성 방법은, 전술한 상기 터치패널용 점착제 조성물이 적용되는 한, 특별히 제한되지 않고, 이 분야의 일반적인 구성이 채용될 수 있다.
상기 전도성 플라스틱 필름(50)의 구체적인 종류는 특별히 제한되지 않고, 이 분야의 공지의 전도성 필름을 사용할 수 있다. 예를 들어, 상기 전도성 필름(50)으로, 일면에 ITO 전극층이 형성된 투명 플라스틱 필름일 수 있다. 구체적으로, 상기 플라스틱 기재층(40)을 형성하는 상기 투명 플라스틱 필름으로는, 폴리에틸렌테레프탈레이트 필름, 폴리테트라플로오루에틸렌 필름, 폴리에틸렌 필름, 폴리프로필렌 필름, 폴리부텐 필름, 폴리부타디엔 필름, 염화비닐 공중합체 필름, 폴리우레탄 필름, 에틸렌-비닐 아세테이트 필름, 에틸렌-프로필렌 공중합체 필름, 에틸렌-아크릴산 에틸 공중합체 필름, 에틸렌-아크릴산 메틸 공중합체 필름 또는 폴리이미드 필름 등을 사용할 수 있고, 이에 제한되지 않는다. 보다 구체적으로, 상기 플라스틱 기재층(40)은 폴리에틸렌테레프탈레이트(PET) 필름일 수 있다.
이하에서는 본 발명의 구체적인 실시예들을 제시한다. 다만, 하기에 기재된 실시예들은 본 발명을 구체적으로 예시하거나 설명하기 위한 것에 불과하며, 이로서 본 발명이 제한되어서는 아니된다.
<실시예 및 비교예>
실시예 1
2-EHA(에틸헥실아크릴레이트) 60중량부, IBOA(이소보닐아크릴레이트) 22중량부 및 HEA(히드록시에틸아크릴레이트) 18중량부의 함량비로 혼합하고, 여기에 광개시제로서 1-히드록시 시클로헥실 페닐 케톤(Irgacure 184, HCPK) 및 기타 첨가제로 커플링제를 포함하는 점착제 조성물을 제조하였다. 용제로서 톨루엔을 혼합하여 코팅액을 준비하고, 상기 코팅액이 이형처리된 폴리에틸렌테레프탈레이트 필름(두께: 75 ㎛)에 UV 경화 후 점착제층의 두께가 100㎛가 되도록 바코터를 이용하여 코팅하였다. 이 후, UV 램프를 이용하여 자외선을 10 분 동안 조사하여 경화시킴으로써 점착 필름을 제조하였다.
실시예 2
점착증진제로서 아크릴로일 모폴라인 수지를 추가로 포함하는 점착제 조성물을 제조한 것을 제외하고 상기 실시예 1과 동일한 방법으로 점착필름을 제조하였다.
실시예 3 및 4
하기 표 1에서와 같이 점착제 조성물의 함량비 및 점착증진제의 함량비를 변경한 점을 제외하고 실시예 2에서와 동일한 방법으로 점착 필름을 제조하였다.
비교예 1 내지 3
하기 표 1에서와 같이 점착제 조성물의 함량비를 변경한 점을 제외하고 실시예 1에서와 동일한 방법으로 점착 필름을 제조하였다.
표 1
Figure PCTKR2014001622-appb-T000001
<실험예1>- 점착필름의 물리적 특성
상기 실시예 및 비교예에서 제작된 점착필름에 대하여 하기 물성을 측정하고, 표 2에 기재하였다.
1) 유전율 측정: 상기 점착필름을 지름 5mm의 사이즈로 측정하여 Agilent사에서 제조한 E4980 LCR Meter를 이용하여 유전율을 측정하였다.
2) 박리력 측정: 상기 점착필름을 25mmX40mm(가로X세로)로 제작하여, 상기 점착필름을 유리 Glass상, 무처리 PET상에 2kg 롤러로 1 왕복하여 부착하고, 상기 부착된 점착 필름면에 대하여 180°방향으로 300mm/분으로 잡아당겨 박리시킬 때의 박리력을 측정하였다.
3) 백탁현상 측정: 85℃, 85% RH의 조건에서 유리에 부착된 상기 점착필름을 3일간 보관하여 흰 반점이 관찰되는지 여부를 관찰하였다.
표 2
Figure PCTKR2014001622-appb-T000002
상기 실시예 1 내지 4의 경우 (메타) 아크릴산 에스테르계 단량체 100중량부에 대하여, 친수성 관능기 함유 단량체를 30중량부 이하로 포함하는 점착제 조성물을 사용하여 점착필름을 형성하였는바, 100kHz에서 유전율이 모두 3.5이하로 측정되었다. 이는 친수성 관능기 함유 단량체를 30중량부를 초과하여 포함하는 점착제 조성물을 사용한 비교예 1 및 2의 점착필름에 비해 유전율이 낮아진 것으로 실시예의 점착필름이 터치에 대한 민감도가 개선된 것을 알 수 있었다(도4). 또한, 친수성 관능기를 함유하지 않은 점착제 조성물을 사용한 비교예3의 점착필름의 경우는 유전율의 측정에 어려움이 있었다.
박리력의 경우, 점착필름이 부착된 기재에 따라 측정값에 차이가 있긴 하였으나, 실시예가 비교예에 비해 더 높은 박리력을 확보하였고, 이로 인해 기재들의 리워크성 또한 더 우수함을 알 수 있었다(도5).
구체적으로, 실시예 1의 경우 친수성 관능기 함유 단량체의 조절로 인해 점착필름의 전체적인 극성이 감소되어 유전율을 감소시키는 효과는 있었으나 백탁현상이 발생할 수 있었다. 이에 실시예 2 내지 4와 같이 일정함량의 점착증진제를 추가로 포함하는 점착제 조성물을 사용함으로써 고온, 고습의 외부 환경에 있어서도 백탁현상의 발생을 억제할 수 있었다.
<실험예2>- 점착제층의 두께에 따른 물리적, 광학적 특성
상기 실시예 3에서 제조된 점착필름의 점착제층 두께를 50㎛(실시예5), 75㎛(실시예6), 125㎛(실시예7), 150㎛(실시예8)로 하여 박리력 및 광학적 특성을 측정하고, 표 3에 기재하였다.
1) 박리력: 상기 점착필름을 25mmX40mm(가로X세로)로 제작하여, 상기 점착필름을 무처리 PET상에 2kg 롤러로 1 왕복하여 부착하고, 상기 부착된 점착 필름면에 대하여 180°방향으로 300mm/분으로 잡아당겨 박리시킬 때의 박리력을 측정하였다.
2) 투과율: 상기 점착필름을 유리 Glass상에 부착하고, 상기 부착된 점착필름 면에 대하여 Conika minolta사의 CM-5를 이용하여 투과율을 측정하였다.
3) 색지수 및 헤이즈: 상기 점착필름을 유리 Glass상에 부착하고, 상기 부착된 점착필름 면에 대하여 BYK사의 Guard-Plus를 이용하여 색지수 및 헤이즈를 측정하였다.
표 3
Figure PCTKR2014001622-appb-T000003
상기 실험예 1에서 유전율이 낮고, 백탁현상이 발생하지 않아 가장 실험결과가 좋은 실시예 3의 점착제층의 두께를 다르게 하여 점착필름의 물리적 특성을 측정하였는바, 상기 실시예 5 내지 8의 경우, 일정수준이상의 박리력을 확보함을 알 수 있었다.
또한, 점착필름이 액정표시장치에 부착되어 활용되는 경우, 투과율 및 헤이즈등의 광학성능을 확보하여야 한다. 도 6를 참고하면, 상기 실시예 5 내지 8의 경우 400nm이상의 파장에 대하여 100%T 이상의 투과율을 가짐을 확인하였는바 다양한 점착제층의 두께에 대해서도 일정수준이상의 광학특성을 나타냄을 알 수 있었다.
나아가, 통상의 경우 색지수는 L* 약 97, a* 약 -0.2, b* 약 0.20, 헤이즈는 0.3%로 측정되는 경우 광학특성을 나타내는 것으로 파악되는바, 상기 실시예 5 내지 8의 경우 통상의 경우와 마찬가지의 수준으로 측정된 것으로 보아 다양한 점착제층의 두께에 대해서도 일정수준이상의 광학특성을 확보함을 확인하였다.

Claims (15)

  1. 친수성 관능기 함유 단량체를 포함하고,
    100kHz 내지 2MHz 영역의 주파수에서 유전율이 3.5이하인
    터치패널용 점착제 조성물.
  2. 제 1항에 있어서,
    상기 친수성 관능기 함유 단량체가 수산기 함유 단량체, 아미노기 함유 단량체, 카르복실기 함유 단량체, 설폰기 함유 단량체, 모르폴린기 함유 단량체, 글리시딜기 함유 단량체 및 이들의 조합으로 이루어진 군으로부터 선택된 하나 이상인
    터치패널용 점착제 조성물.
  3. 제 1항에 있어서,
    상기 친수성 관능기 함유 단량체가 (메타) 아크릴산 에스테르계 단량체 100중량부에 대해서 30중량부 이하인
    터치패널용 점착제 조성물.
  4. 제 3항에 있어서,
    상기 (메타) 아크릴산 에스테르계 단량체 및 상기 친수성 관능기 함유 단량체의 중합체 분자량이 각각 60만 내지 120만인
    터치패널용 점착제 조성물.
  5. 제 3항에 있어서,
    상기 (메타)아크릴산 에스테르계 단량체가 알킬(메타)아크릴레이트이고, 상기 알킬(메타)아크릴레이트의 알킬은 선형 또는 분지형 C1 내지 C14 알킬인
    터치패널용 점착제 조성물.
  6. 제 3항에 있어서,
    상기 (메타) 아크릴산 에스테르계 단량체가 메틸 (메타)아크릴레이트, 에틸 (메타)아크릴레이트, n-프로필 (메타)아크릴레이트, 이소프로필 (메타)아크릴레이트, n-부틸 (메타)아크릴레이트, t-부틸 (메타)아크릴레이트, sec-부틸 (메타)아크릴레이트, 펜틸 (메타)아크릴레이트, 2-에틸헥실 (메타)아크릴레이트, 2-에틸부틸 (메타)아크릴레이트, n-옥틸 (메타)아크릴레이트, 이소옥틸 (메타)아크릴레이트, 이소노닐 (메타)아크릴레이트, 라우릴 (메타)아크릴레이트, 테트라데실 (메타)아크릴레이트 및 이들의 조합으로 이루어진 군으로부터 선택된 하나 이상인
    터치패널용 점착제 조성물.
  7. 제 1항에 있어서,
    점착증진제를 더 포함하는
    터치패널용 점착제 조성물.
  8. 제 7항에 있어서,
    상기 점착증진제는 아민계 액상 고분자, 폴리 아민, 석유수지, 폴리부텐, 아크릴계 변성수지, 아크릴로일 모폴라인 수지 및 이들의 조합으로 이루어진 군으로부터 선택된 하나 이상인
    터치패널용 점착제 조성물.
  9. 제 1항에 있어서,
    광개시제를 더 포함하는
    터치패널용 점착제 조성물.
  10. 제 9항에 있어서,
    상기 광개시제는 벤조인계 개시제, 히드록시 케톤계 개시제, 아미노 케톤계 개시제 카프로락탐 및 이들의 조합으로 이루어진 군으로부터 선택된 하나 이상인
    터치패널용 점착제 조성물.
  11. 제 1항 내지 제 10항 중 어느 한 항에 따른 터치패널용 점착제 조성물의 경화물을 포함하는 점착제층을 포함하는 점착필름.
  12. 제 11항에 있어서,
    상기 점착제층의 유전율은 100kHz 내지 2MHz 영역의 주파수에서 3.5이하인
    점착필름.
  13. 제 11항에 있어서,
    상기 점착제층의 두께가 50㎛ 내지 300㎛인
    점착필름.
  14. 일면에 도전층이 형성된 전도성 플라스틱 필름; 및
    상기 도전층에 부착되고, 제 1항 내지 제 10항 중 어느 한 항에 따른 터치패널용 점착제 조성물의 경화물을 포함하는 점착제층을 포함하는
    터치패널.
  15. 제 14항에 있어서,
    상기 전도성 필라스틱 필름이 ITO(도전성 금속 산화물)층이 일면에 형성된 폴리에틸렌테레프탈레이트 필름인
    터치 패널.
PCT/KR2014/001622 2013-04-05 2014-02-27 터치패널용 점착제 조성물, 점착 필름 및 터치 패널 WO2014163299A1 (ko)