WO2014156421A1 - 光拡散フィルムおよび光拡散フィルムの製造方法 - Google Patents

光拡散フィルムおよび光拡散フィルムの製造方法 Download PDF

Info

Publication number
WO2014156421A1
WO2014156421A1 PCT/JP2014/054397 JP2014054397W WO2014156421A1 WO 2014156421 A1 WO2014156421 A1 WO 2014156421A1 JP 2014054397 W JP2014054397 W JP 2014054397W WO 2014156421 A1 WO2014156421 A1 WO 2014156421A1
Authority
WO
WIPO (PCT)
Prior art keywords
component
light
film
light diffusion
column structure
Prior art date
Application number
PCT/JP2014/054397
Other languages
English (en)
French (fr)
Inventor
健太郎 草間
片桐 麦
知生 大類
所司 悟
Original Assignee
リンテック株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by リンテック株式会社 filed Critical リンテック株式会社
Priority to US14/775,522 priority Critical patent/US9945990B2/en
Priority to JP2015508191A priority patent/JP5914752B2/ja
Priority to CN201480018408.XA priority patent/CN105074508B/zh
Publication of WO2014156421A1 publication Critical patent/WO2014156421A1/ja

Abstract

 フィルム内に、屈曲部を有する柱状物および屈折率が相対的に低い領域からなる所定のカラム構造を形成することにより、拡散光の開き角を効果的に拡大した光拡散フィルムおよびその製造方法を提供する。 屈折率が相対的に低い領域中に、屈折率が相対的に高い複数の柱状物をフィルム膜厚方向に林立させてなるカラム構造を有する光拡散フィルム等であって、屈折率が相対的に高い複数の柱状物が、当該柱状物の途中において屈曲部を有している。

Description

光拡散フィルムおよび光拡散フィルムの製造方法
 本発明は、光拡散フィルムおよび光拡散フィルムの製造方法に関する。
 特に、フィルム内に、屈曲部を有する柱状物等からなる所定のカラム構造を有することにより、拡散光の開き角を効果的に拡大した光拡散フィルムおよびその製造方法に関する。
 従来、例えば、液晶表示装置等が属する光学技術分野において、特定の方向からの入射光については特定の方向へ拡散させ、それ以外の方向からの入射光についてはそのまま直進透過させることができる光拡散フィルムの使用が提案されている。
 このような光拡散フィルムとしては、様々な態様が知られているが、特に、フィルム内において、屈折率が異なる複数の板状領域をフィルム面(フィルムの端面以外の面を意味する。以下において同じ。)に沿った任意の一方向に沿って交互に配置してなるルーバー構造を有する光拡散フィルムが広く使用されている。
 また、別のタイプの光拡散フィルムとしては、フィルム内において、屈折率が相対的に低い領域中に屈折率が相対的に高い複数の柱状物を林立させてなるカラム構造を有する光拡散フィルムが広く使用されている。
 ところで、このようなルーバー構造やカラム構造を有する光拡散フィルムは、屈折率が異なる2種以上の重合性化合物を含む光拡散フィルム用組成物を膜状に塗布してなる塗布層に対して、所定の方法にて活性エネルギー線を照射することにより得られることが知られている。
 すなわち、塗布層に対して進行方向や平行性を制御した所定の活性エネルギー線を照射することで、塗布層における2種以上の重合性化合物を相分離させながら硬化することにより所定の内部構造を有する光拡散フィルムを得ることができる。
 したがって、より明確な内部構造を有し、光の透過と拡散において良好な入射角度依存性を有する高品質な光拡散フィルムを得るために、2種以上の重合性化合物をより効率的に相分離させることができ、かつ、より安定的に光硬化させることができる光拡散フィルム用組成物が提案されている(例えば、特許文献1~2)。
 すなわち、特許文献1には、(A)成分としての下記一般式(11)で表わされるビフェニル化合物と、(B)成分としての重量平均分子量が3,000~20,000の範囲内の値である重合性化合物と、を含む異方性光拡散フィルム用組成物であって、(A)成分の含有量を、(B)成分100重量部に対して、25~400重量部の範囲内の値とすることを特徴とする異方性光拡散フィルム用組成物が開示されている。
Figure JPOXMLDOC01-appb-C000001
(一般式(11)中、Ra1~Ra10は、それぞれ独立しており、Ra1~Ra10の少なくとも1つは、下記一般式(12)で表わされる置換基であり、残りは、水素原子、水酸基、カルボキシル基、アルキル基、アルコキシ基、ハロゲン化アルキル基、ヒドロキシアルキル基、カルボキシアルキル基およびハロゲン原子のいずれかの置換基である。)
Figure JPOXMLDOC01-appb-C000002
(一般式(12)中、Ra11は、水素原子またはメチル基であり、炭素数pは1~4の整数であり、繰り返し数qは1~10の整数である。)
 また、特許文献2には、(A)成分としての複数の芳香環を含有する(メタ)アクリル酸エステルと、(B)成分としての重量平均分子量が3,000~20,000の範囲内の値であるウレタン(メタ)アクリレートと、を含む異方性光拡散フィルム用組成物であって、(B)成分としてのウレタン(メタ)アクリレートが、構成成分として下記(a)~(c)成分に由来し、かつ、モル比にて(a)成分:(b)成分:(c)成分=1~5:1:1~5の割合で構成された化合物であるとともに、(A)成分の含有量を、(B)成分100重量部に対して、25~400重量部の範囲内の値とすることを特徴とする異方性光拡散フィルム用組成物が開示されている。
(a)脂肪族環を介してイソシアナート基を2つ含有する化合物
(b)ポリアルキレングリコール
(c)ヒドロキシアルキル(メタ)アクリレート
特開2012-141591号公報(特許請求の範囲) 特開2012-141592号公報(特許請求の範囲)
 しかしながら、特許文献1~2に記載の異方性光拡散フィルム用組成物を光硬化させてなる異方性光拡散フィルムは、ルーバー構造による異方性光拡散の特徴であるが、光拡散入射角度領域と、非光拡散入射角度領域との間において光の拡散具合に急峻な切り替わりが生じてしまうという問題が見られた。
 一方、特許文献1~2に記載の異方性光拡散フィルム用組成物は、所定の方法にて活性エネルギー線を照射することにより、カラム構造を有する等方性光拡散フィルムを得ることもできることが確認されている。
 したがって、特許文献1~2に記載の異方性光拡散フィルム用組成物であっても、カラム構造を有する等方性光拡散フィルムとすることにより、上述した光拡散入射角度領域と、非光拡散入射角度領域との間における光の拡散具合の急峻な切り替わりについては解決することができる。
 しかしながら、この場合であっても、(B)成分としてのウレタン(メタ)アクリレートの重量平均分子量、あるいは塗布層の温度といった条件にもよるが、得られる光拡散フィルムにおける拡散光の開き角が不十分であるという問題が見られた。
 そこで、本発明者らは、以上のような事情に鑑み、鋭意努力したところ、フィルム内に、屈曲部を有する柱状物等からなる所定のカラム構造を形成することにより、拡散光の開き角を効果的に拡大できることを見出し、本発明を完成させたものである。
 すなわち、本発明の目的は、フィルム内に、屈曲部を有する柱状物等からなる所定のカラム構造を有することにより、拡散光の開き角を効果的に拡大した光拡散フィルムおよびその製造方法を提供することにある。
 本発明によれば、屈折率が相対的に低い領域中に、屈折率が相対的に高い複数の柱状物をフィルム膜厚方向に林立させてなるカラム構造を有する光拡散フィルムであって、屈折率が相対的に高い複数の柱状物が、当該柱状物の途中において屈曲部を有していることを特徴とする光拡散フィルムが提供され、上述した問題を解決することができる。
 すなわち、本発明の光拡散フィルムであれば、フィルム内に、屈曲部を有する柱状物等からなる所定のカラム構造(以下、屈曲カラム構造と称する場合がある。)を有することから、拡散光の開き角を効果的に拡大することができる。
 また、フィルム内に、ルーバー構造を有する光拡散フィルムに特有の、光拡散入射角度領域と、非光拡散入射角度領域との間において光の拡散具合に急峻な切り替わりが生じる問題についても根本的に解決することができる。
 なお、本発明において、「拡散光の開き角」とは、光拡散フィルムに対して、入射光が最も拡散される角度に点光源を固定し、この状態で得られる拡散光の角度範囲(以下、「光拡散角度領域」と称する場合がある。)の幅を意味する。
 また、本発明において、「光拡散入射角度領域」とは、光拡散フィルムに対し、点光源からの入射光の角度を変化させた場合に、拡散光を出光するのに対応する入射光の角度範囲を意味する。
 また、本発明の光拡散フィルムを構成するにあたり、カラム構造のうち、屈曲部よりも上方部分における柱状物のフィルム面の法線に対する傾斜角θaを0~30°の範囲内の値とするとともに、屈曲部よりも下方部分における柱状物のフィルム面の法線に対する傾斜角θbを1~60°の範囲内の値とすることが好ましい。
 このように構成することにより、拡散光の開き角を、より効率的に拡大することができる。
 なお、「屈曲部よりも上方部分」とは、光拡散フィルムを製造する際に活性エネルギー線が照射される側の部分を意味し、「屈曲部分よりも下方部分」とは、その反対側の部分を意味する。
 また、本発明の光拡散フィルムを構成するにあたり、傾斜角θaおよびθbが、下記関係式(1)を満足することが好ましい。
1≦|θb-θa|≦30    (1)
 このように構成することにより、拡散光の開き角を、さらに効率的に拡大することができる。
 また、本発明の光拡散フィルムを構成するにあたり、カラム構造の厚さLを50~700μmの範囲内の値とすることが好ましい。
 このように構成することにより、光拡散角度領域内における拡散光の強度の均一性を向上させることができる。
 また、本発明の光拡散フィルムを構成するにあたり、カラム構造のうち、屈曲部よりも上方部分における柱状物の長さLaを5~200μmの範囲内の値とするとともに、屈曲部よりも下方部分における柱状物の長さLbを20~400μmの範囲内の値とすることが好ましい。
 このように構成することにより、拡散光の開き角をさらに効率的に拡大しつつ、光拡散角度領域内における拡散光の強度の均一性を向上させることができる。
 また、本発明の光拡散フィルムを構成するにあたり、長さLaおよびLbが、下記関係式(2)を満足することが好ましい。
0.01≦La/Lb≦10    (2)
 このように構成することにより、拡散光の開き角を一段と効率的に拡大しつつ、光拡散角度領域内における拡散光の強度の均一性を向上させることができる。
 また、本発明の別の態様は、屈折率が相対的に低い領域中に、屈折率が相対的に高い複数の柱状物をフィルム膜厚方向に林立させてなるカラム構造であって、屈折率が相対的に高い複数の柱状物が、当該柱状物の途中において屈曲部を有するカラム構造を有する光拡散フィルムの製造方法であって、下記工程(a)~(c)を含むことを特徴とする光拡散フィルムの製造方法である。
(a)(A)成分としての複数の芳香環を含有する(メタ)アクリル酸エステルと、(B)成分としてのウレタン(メタ)アクリレートと、(C)成分としての光重合開始剤と、(D)成分としての紫外線吸収剤と、を含む光拡散フィルム用組成物であって、(A)成分の含有量を、(B)成分100重量部に対して、25~400重量部の範囲内の値とするとともに、(C)成分の含有量を、(A)成分および(B)成分の合計量(100重量部)に対して、0.2~20重量部の範囲内の値とし、かつ、(D)成分の含有量を、(A)成分および(B)成分の合計量(100重量部)に対して、2重量部未満の値(但し、0重量部を除く。)とする光拡散フィルム用組成物を準備する工程
(b)光拡散フィルム用組成物を工程シートに対して塗布し、塗布層を形成する工程
(c)塗布層に対して活性エネルギー線を照射する工程
 すなわち、本発明の光拡散フィルムの製造方法であれば、所定の光拡散フィルム用組成物からなる塗布層に対して活性エネルギー線を照射することから、フィルム内において、容易かつ安定的に屈曲カラム構造を形成することができる。
 また、本発明の光拡散フィルムの製造方法を実施するにあたり、(D)成分として、波長330~380nmの光に対して吸収ピークを有する紫外線吸収剤を用いることが好ましい。
 このように実施することにより、より明確な屈曲カラム構造を形成することができる。
 また、本発明の光拡散フィルムの製造方法を実施するにあたり、(D)成分として、ヒドロキシフェニルトリアジン系紫外線吸収剤、ベンゾトリアゾール系紫外線吸収剤、ベンゾフェノン系紫外線吸収剤およびヒドロキシベンゾエート系紫外線吸収剤からなる群から選択される少なくとも一種を用いることが好ましい。
 このように実施することにより、さらに明確な屈曲カラム構造を形成することができる。
図1(a)~(b)は、フィルム内にカラム構造を有する光拡散フィルムの概略を説明するために供する図である。 図2(a)~(b)は、フィルム内にカラム構造を有する光拡散フィルムにおける入射角度依存性および等方性光拡散を説明するために供する図である。 図3(a)~(b)は、フィルム内に屈曲カラム構造を有する光拡散フィルムにおける入射角度依存性および等方性光拡散を説明するために供する図である。 図4(a)~(b)は、屈曲カラム構造を説明するために供する図である。 図5(a)~(b)は、光拡散フィルムの製造方法における各工程を説明するために供する図である。 図6(a)~(d)は、活性エネルギー線照射工程を説明するために供する図である。 図7は、活性エネルギー線照射工程を説明するために供する別の図である。 図8は、(A)成分および(B)成分の波長-透過率チャートを示すために供する図である。 図9は、(C)成分の波長-吸光度チャートを示すために供する図である。 図10(a)~(c)は、(D)成分の波長-吸光度チャートを示すために供する図である。 図11(a)~(c)は、実施例1の光拡散フィルムの断面を示すために供する模式図および写真である。 図12(a)~(b)は、実施例1の光拡散フィルムの断面を示すために供する写真である。 図13は、光拡散特性を測定する際の光拡散フィルムに対する入射角θ1を説明するために供する図である。 図14(a)~(p)は、実施例1~3および比較例1の光拡散フィルムの光拡散特性を比較するために供する写真である。 図15(a)~(p)は、実施例1~3および比較例1の光拡散フィルムの光拡散特性を比較するために供する別の写真である。 図16(a)~(p)は、実施例1~3および比較例1の光拡散フィルムの光拡散特性を比較するために供するさらに別の写真である。 図17は、実施例1~3および比較例1の光拡散フィルムの光拡散特性を比較するために供する図である。 図18(a)~(c)は、実施例2の光拡散フィルムの断面を示すために供する模式図および写真である。 図19(a)~(b)は、実施例2の光拡散フィルムの断面を示すために供する写真である。 図20(a)~(c)は、実施例3の光拡散フィルムの断面を示すために供する模式図および写真である。 図21(a)~(b)は、実施例3の光拡散フィルムの断面を示すために供する写真である。 図22(a)~(c)は、実施例4の光拡散フィルムの断面を示すために供する模式図および写真である。 図23(a)~(b)は、実施例4の光拡散フィルムの断面を示すために供する写真である。 図24(a)~(l)は、実施例4~5および比較例1の光拡散フィルムの光拡散特性を比較するために供する写真である。 図25(a)~(l)は、実施例4~5および比較例1の光拡散フィルムの光拡散特性を比較するために供する別の写真である。 図26(a)~(l)は、実施例4~5および比較例1の光拡散フィルムの光拡散特性を比較するために供するさらに別の写真である。 図27は、実施例4~5および比較例1の光拡散フィルムの光拡散特性を比較するために供する図である。 図28(a)~(c)は、実施例5の光拡散フィルムの断面を示すために供する模式図および写真である。 図29(a)~(b)は、実施例5の光拡散フィルムの断面を示すために供する写真である。 図30(a)~(c)は、実施例6の光拡散フィルムの断面を示すために供する模式図および写真である。 図31(a)~(b)は、実施例6の光拡散フィルムの断面を示すために供する写真である。 図32(a)~(l)は、実施例6~7および比較例1の光拡散フィルムの光拡散特性を比較するために供する写真である。 図33(a)~(l)は、実施例6~7および比較例1の光拡散フィルムの光拡散特性を比較するために供する別の写真である。 図34(a)~(l)は、実施例6~7および比較例1の光拡散フィルムの光拡散特性を比較するために供するさらに別の写真である。 図35は、実施例6~7および比較例1の光拡散フィルムの光拡散特性を比較するために供する図である。 図36(a)~(c)は、実施例7の光拡散フィルムの断面を示すために供する模式図および写真である。 図37(a)~(b)は、実施例7の光拡散フィルムの断面を示すために供する写真である。 図38(a)~(b)は、実施例8の光拡散フィルムの断面を示すために供する模式図および写真である。 図39(a)~(l)は、実施例8、実施例1および比較例1の光拡散フィルムの光拡散特性を比較するために供する写真である。 図40(a)~(l)は、実施例8、実施例1および比較例1の光拡散フィルムの光拡散特性を比較するために供する別の写真である。 図41(a)~(l)は、実施例8、実施例1および比較例1の光拡散フィルムの光拡散特性を比較するために供するさらに別の写真である。 図42(a)~(c)は、比較例1の光拡散フィルムの断面を示すために供する模式図および写真である。 図43(a)~(b)は、比較例3の光拡散フィルムの断面を示すために供する模式図および写真である。 図44(a)~(l)は、比較例3、実施例1および比較例1の光拡散フィルムの光拡散特性を比較するために供する写真である。 図45(a)~(l)は、比較例3、実施例1および比較例1の光拡散フィルムの光拡散特性を比較するために供する別の写真である。 図46(a)~(l)は、比較例3、実施例1および比較例1の光拡散フィルムの光拡散特性を比較するために供するさらに別の写真である。 図47は、バンドパスフィルターの波長-透過率チャートを示すために供する図である。 図48は、比較例4の光拡散フィルムの様子を説明するために供する写真である。 図49(a)~(c)は、参考例1の光拡散フィルムの断面を示すために供する模式図および写真である。 図50(a)~(f)は、参考例1および実施例1の光拡散フィルムの光拡散特性を比較するために供する写真である。 図51(a)~(d)は、参考例1および実施例1の光拡散フィルムの光拡散特性を比較するために供する別の写真である。
[第1の実施形態]
 第1の実施形態は、屈折率が相対的に低い領域中に、屈折率が相対的に高い複数の柱状物をフィルム膜厚方向に林立させてなるカラム構造を有する光拡散フィルムであって、屈折率が相対的に高い複数の柱状物が、当該柱状物の途中において屈曲部を有していることを特徴とする光拡散フィルムである。
 以下、本発明の第1の実施形態を、図面を適宜参照して、具体的に説明するが、かかる説明の理解を容易にするため、まず、光拡散フィルムにおける光拡散の基本原理について説明する。
1.光拡散フィルムにおける光拡散の基本原理
 最初に、図1~2を用いて光拡散フィルムにおける光拡散の基本原理について説明する。
 まず、図1(a)には、光拡散フィルム10の上面図(平面図)が示してあり、図1(b)には、図1(a)に示す光拡散フィルム10を、点線A-Aに沿って垂直方向に切断して、切断面を矢印に沿った方向から眺めた場合の光拡散フィルム10の断面図が示してある。
 また、図2(a)には、光拡散フィルム10の全体図を示し、図2(b)には、図2(a)の光拡散フィルム10をX方向から見た場合の断面図を示す。
 かかる図1(a)の平面図に示すように、光拡散フィルム10は、屈折率が相対的に高い柱状物12と、屈折率が相対的に低い領域14とからなるカラム構造13を有している。
 また、図1(b)の断面図に示すように、光拡散フィルム10の垂直方向においては、屈折率が相対的に高い柱状物12と、屈折率が相対的に低い領域14は、それぞれ所定の幅を有して交互に配置された状態となっている。
 これにより、図2(a)に示すように、入射角が光拡散入射角度領域内である場合には、入射光が光拡散フィルム10によって拡散されると推定される。
 すなわち、図1(b)に示すように、光拡散フィルム10に対する入射光の入射角が、カラム構造13の境界面13aに対し、平行から所定の角度範囲の値、つまり、光拡散入射角度領域内の値である場合には、入射光(52、54)は、カラム構造内の相対的に高屈折率の柱状物12の内部を、方向を変化させながら膜厚方向に沿って通り抜けることにより、出光面側での光の進行方向が一様でなくなるものと推定される。
 その結果、入射角が光拡散入射角度領域内である場合には、入射光が光拡散フィルム10によって拡散され、拡散光(52´、54´)になると推定される。
 一方、光拡散フィルム10に対する入射光の入射角が、光拡散入射角度領域から外れる場合には、図1(b)に示すように、入射光56は、光拡散フィルムによって拡散されることなく、そのまま光拡散フィルム10を透過し、透過光56´になるものと推定される。
 なお、本発明において、「光拡散入射角度領域」とは、光拡散フィルムに対し、点光源からの入射光の角度を変化させた場合に、拡散光を出光するのに対応する入射光の角度範囲を意味する。
 また、かかる「光拡散入射角度領域」は、図2(a)に示すように、光拡散フィルムにおけるカラム構造の屈折率差や傾斜角等によって、その光拡散フィルムごとに決定される角度領域である。
 以上の基本原理により、カラム構造13を備えた光拡散フィルム10は、例えば、図2(a)に示すように、光の透過と拡散において入射角度依存性を発揮することが可能となる。
 また、図1~図2に示すように、カラム構造13を有する光拡散フィルムは、通常、「等方性」を有することになる。
 ここで、本発明において「等方性」とは、図2(a)に示すように、入射光がフィルムによって拡散された場合に、拡散された出射光におけるフィルムと平行な面(フィルムの端面以外の面と平行な面を意味する。以下において同じ。)内での、その光の拡散具合(拡散光の広がりの形状)が、同面内での方向によって変化しない性質を有することを意味する。
 より具体的には、図2(a)に示すように、入射光がフィルムによって拡散された場合に、拡散された出射光の拡散具合は、フィルムと平行な面内において円状になる。
 また、図2(b)に示すように、本発明において、入射光の「入射角θ1」と言った場合、入射角θ1は、光拡散フィルムの入射側表面の法線の角度を0°とした場合の角度(°)を意味するものとする。
 また、本発明において、「光拡散角度領域」とは、光拡散フィルムに対して、入射光が最も拡散される角度に点光源を固定し、この状態で得られる拡散光の角度範囲を意味するものとする。
 さらに、本発明において、「拡散光の開き角」とは、上述した「光拡散角度領域」の角度幅(°)であり、図2(b)に示すように、フィルムの断面を矢印Xに沿った方向から眺めた場合における拡散光の開き角θ2を意味するものとする。
 なお、光拡散角度領域の角度幅(°)と、光拡散入射角度領域の幅は、略同一になることが確認されている。
 また、図2(a)に示すように、光拡散フィルムは、入射光の入射角が光拡散入射角度領域に含まれる場合には、その入射角が異なる場合であっても、出光面側においてほぼ同様の光拡散をさせることができる。
 したがって、得られた光拡散フィルムは、光を所定箇所に集中させる集光作用を有すると言うことができる。
 なお、カラム構造内の柱状物12の内部における入射光の方向変化は、図1(b)に示すような全反射により直線状にジグザグに方向変化するステップインデックス型となる場合の他、曲線状に方向変化するグラディエントインデックス型となる場合も考えられる。
 また、図1(a)および(b)では、相対的に屈折率が高い柱状物12と、相対的に屈折率が低い領域14と、の境界面を簡単のために直線で表わしたが、実際には、界面は僅かに蛇行しており、それぞれの柱状物は分岐や消滅を伴った複雑な屈折率分布構造を形成している。
 その結果、一様でない光学特性の分布が光拡散性を高めているものと推定される。
2.基本的構成
 次いで、図面を用いて、本発明の光拡散フィルムの基本的構成について説明する。
 図3(a)~(b)に示すように、本発明の光拡散フィルム10´は、屈折率が相対的に低い領域中に、屈折率が相対的に高い複数の柱状物をフィルム膜厚方向に林立させてなるカラム構造13´を有する光拡散フィルム10´であって、屈曲率が相対的に高い複数の柱状物が、当該柱状物の途中において屈曲部を有していることを特徴としている。
 すなわち、本発明の光拡散フィルム10´は、フィルム内に、屈曲カラム構造13´を有することを特徴としている。
 ここで、図3(a)には、本発明の光拡散フィルム10´の全体図を示し、図3(b)には、図3(a)の光拡散フィルム10´をX方向から見た場合の断面図を示す。
 このような屈曲カラム構造13´を有する光拡散フィルム10´は、屈曲を有さない通常のカラム構造を有する光拡散フィルムと同様の原理により、その光拡散特性として、入射角度依存性および等方性を有する。
 但し、屈曲カラム構造13´を有する本発明の光拡散フィルム10´では、図3(b)に示すように、通常のカラム構造を有する光拡散フィルムと比較して、拡散光の開き角θ2が大きくなる。
 これは、屈曲カラム構造は、屈曲を境として、1枚のフィルムの中に柱状物の傾斜角が異なる2種類のカラム構造を有していると解釈することができるためである。
 したがって、入射した光が上方に存在するカラム構造で拡散し、その拡散光が下方に存在するカラム構造でさらに拡散することにより、拡散光の開き角θ2が拡大することになるためである。
3.屈曲カラム構造
 本発明の光拡散フィルムにおける内部構造は、上述した屈曲カラム構造であることを特徴とする。
 なお、本発明の光拡散フィルムは、後述するように、単一の塗布層に由来する単一層のフィルム内に屈曲カラム構造が形成されており、しかも、かかる屈曲カラム構造は、一度の活性エネルギー線照射によって形成されるものである。
 以下、屈曲カラム構造について具体的に説明する。
(1)屈折率
 屈曲カラム構造において、屈折率が相対的に高い柱状物の屈折率と、屈折率が相対的に低い領域の屈折率との差を0.01以上の値とすることが好ましい。
 この理由は、かかる屈折率の差を0.01以上の値とすることにより、屈曲カラム構造内において入射光を安定的に反射させて、屈曲カラム構造に由来した入射角度依存性をより高め、光拡散入射角度領域と、非光拡散入射角度領域との区別を明確に制御することができるためである。
 より具体的には、かかる屈折率の差が0.01未満の値となると、入射光が屈曲カラム構造内で全反射する角度域が狭くなることから、入射角度依存性が過度に低下する場合があるためである。
 したがって、屈曲カラム構造における屈折率が相対的に高い柱状物の屈折率と、屈折率が相対的に低い領域の屈折率との差を0.05以上の値とすることがより好ましく、0.1以上の値とすることがさらに好ましい。
 なお、屈折率が相対的に高い柱状物の屈折率と、屈折率が相対的に低い領域の屈折率との差は大きい程好ましいが、屈曲カラム構造を形成可能な材料を選定する観点から、0.3程度が上限であると考えられる。
(2)最大径
 また、図4(a)に示すように、屈曲カラム構造において、柱状物の断面における最大径Sを0.1~15μmの範囲内の値とすることが好ましい。
 この理由は、かかる最大径を0.1~15μmの範囲内の値とすることにより、屈曲カラム構造内において入射光をより安定的に反射させて、屈曲カラム構造に由来した入射角度依存性を、より効果的に向上させることができるためである。
 すなわち、かかる最大径が0.1μm未満の値となると、入射光の入射角度にかかわらず、光拡散性を示すことが困難になる場合があるためである。一方、かかる最大径が15μmを超えた値となると、屈曲カラム構造内を直進する光が増加し、拡散光の均一性が悪化する場合があるためである。
 したがって、屈曲カラム構造において、柱状物の断面における最大径を0.5~10μmの範囲内の値とすることがより好ましく、1~5μmの範囲内の値とすることがさらに好ましい。
 なお、柱状物の断面形状については、特に限定されるものではないが、例えば、円、楕円、多角形、異形等とすることが好ましい。
 また、柱状物の断面とは、フィルム表面と平行な面によって切断された断面を意味する。
 なお、柱状物の最大径や長さ等は、光学デジタル顕微鏡にて観察することにより計測することができる。
(3)柱状物間の距離
 また、図4(a)に示すように、屈曲カラム構造において、柱状物間における距離、すなわち、隣接する柱状物におけるスペースPを0.1~15μmの範囲内の値とすることが好ましい。
 この理由は、かかる距離を0.1~15μmの範囲内の値とすることにより、屈曲カラム構造内において入射光をより安定的に反射させて、屈曲カラム構造に由来した入射角度依存性を、さらに向上させることができるためである。
 すなわち、かかる距離が0.1μm未満の値となると、入射光の入射角度にかかわらず、光拡散性を示すことが困難になる場合があるためである。一方、かかる距離が15μmを超えた値となると、屈曲カラム構造内を直進する光が増加し、拡散光の均一性が悪化する場合があるためである。
 したがって、屈曲カラム構造において、柱状物間における距離を0.5~10μmの範囲内の値とすることがより好ましく、1~5μmの範囲内の値とすることがさらに好ましい。
(4)厚さ
 また、屈曲カラム構造の厚さ、すなわち、図4(b)に示すように、フィルム面の法線方向における柱状物の長さLを50~700μmの範囲内の値とすることが好ましい。
 この理由は、屈曲カラム構造の厚さをかかる範囲内の値とすることにより、膜厚方向に沿った柱状物の長さを安定的に確保して、屈曲カラム構造内において入射光をより安定的に反射させて、屈曲カラム構造に由来した光拡散角度領域内における拡散光の強度の均一性をさらに向上させることができるためである。
 すなわち、かかる屈曲カラム構造の厚さLが50μm未満の値となると、柱状物の長さが不足して、屈曲カラム構造内を直進してしまう入射光が増加し、光拡散角度領域内における拡散光の強度の均一性を得ることが困難になる場合があるためである。一方、かかる屈曲カラム構造の厚さLが700μmを超えた値となると、光拡散フィルム用組成物に対して活性エネルギー線を照射して屈曲カラム構造を形成する際に、初期に形成されたカラム構造によって光重合の進行方向が拡散してしまい、所望の屈曲カラム構造を形成することが困難になる場合があるためである。
 したがって、屈曲カラム構造の厚さLを70~300μmの範囲内の値とすることがより好ましく、80~200μmの範囲内の値とすることがさらに好ましい。
 また、本発明の光拡散フィルムは、図4(b)に示すように膜厚方向全体に屈曲カラム構造(膜厚方向長さL)が形成されていてもよいし、フィルムの上端部、下端部の少なくともいずれか一方にカラム構造未形成部分を有していてもよい。
 また、図4(b)に示すように、屈曲カラム構造13´のうち、屈曲部よりも上方部分(光拡散フィルムを製造する際に活性エネルギー線が照射される側の部分)における柱状物の長さLaを5~200μmの範囲内の値とすることが好ましい。
 この理由は、長さLaをかかる範囲内の値とすることにより、拡散光の開き角をさらに効率的に拡大しつつ、光拡散角度領域内における拡散光の強度の均一性を向上させることができるためである。
 すなわち、長さLaが5μm未満の値となると、上方部分のカラム構造に由来する拡散が弱くなりすぎ、拡散光の開き角を効果的に拡大することが困難になる場合があるためである。なお、光拡散フィルム用組成物における紫外線吸収剤の含有量が多い程、長さLaが短くなる傾向がある。したがって、逆に言えば、長さLaが過度に短いということは、紫外線吸収剤の含有量が非常に多いことになり、その場合、光拡散フィルム用組成物を光硬化させる際に、フィルムの収縮シワが発生する可能性が高くなり、制御が困難になる。
 一方、長さLaが200μmを超えた値となると、上方部分のカラム構造に由来する拡散は十分に得ることができる。但し、光拡散フィルム用組成物における紫外線吸収剤の含有量が少ない程、長さLaが長くなる傾向がある。したがって、逆に言えば、長さLaが過度に長いということは、紫外線吸収剤の含有量が非常に少ないことになり、その場合、下方部分のカラム構造が十分に形成されず、拡散光の開き角を拡大する効果を十分に得られない可能性がある。
 したがって、屈曲カラム構造のうち、屈曲部よりも上方部分における柱状物の長さLaを10~170μmの範囲内の値とすることがより好ましく、20~140μmの範囲内の値とすることがさらに好ましい。
 また、図4(b)に示すように、屈曲カラム構造13´のうち、屈曲部よりも下方部分における柱状物の長さLbを20~400μmの範囲内の値とすることが好ましい。
 この理由は、長さLbをかかる範囲内の値とすることにより、拡散光の開き角をさらに効率的に拡大しつつ、光拡散角度領域内における拡散光の強度の均一性を向上させることができるためである。
 すなわち、長さLbが20μm未満の値となると、下方部分のカラム構造に由来する拡散が弱くなりすぎ、拡散光の開き角を効果的に拡大することが困難になる場合があるためである。一方、長さLbが400μmを超えた値となると、下方部分のカラム構造に有来する拡散は十分に得られるが、光拡散フィルムの膜厚が過度に厚くなってディスプレイ用途としての適用が困難になる場合があるためである。
 したがって、屈曲カラム構造のうち、屈曲部よりも下方部分における柱状物の長さLbを30~300μmの範囲内の値とすることがより好ましく、40~200μmの範囲内の値とすることがさらに好ましい。
 また、上述した長さLaおよびLbが、下記関係式(2)を満足することが好ましい。
0.01≦La/Lb≦10    (2)
 この理由は、長さLaおよびLbがかかる関係式を満足することにより、拡散光の開き角を一段と効率的に拡大しつつ、光拡散角度領域内における拡散光の強度の均一性を向上させることができるためである。
 すなわち、La/Lbが0.01未満の値となると、長さLaが過度に短くなり、カラム構造の屈曲による拡散光の開き角を拡大する効果を十分に得ることができない場合があるためである。一方、La/Lbが10を超えた値となると、長さLbが過度に短くなり、カラム構造の屈曲による拡散光の開き角を拡大する効果を十分に得ることができない場合があるためである。
 したがって、長さLaおよびLbが、下記関係式(2´)を満足することがより好ましく、下記関係式(2´´)を満足することがさらに好ましい。
0.1≦La/Lb≦8    (2´)
0.2≦La/Lb≦6    (2´´)
(5)傾斜角
 また、図4(b)に示すように、屈曲カラム構造において、柱状物12が膜厚方向に対して一定の傾斜角にて林立してなることが好ましい。
 この理由は、柱状物の傾斜角を一定とすることにより、屈曲カラム構造内において入射光をより安定的に反射させて、屈曲カラム構造に由来した入射角度依存性をさらに向上させることができるためである。
 より具体的には、図4(b)に示すように、屈曲カラム構造13´のうち、屈曲部よりも上方部分における柱状物のフィルム面の法線に対する傾斜角θaを0~30°の範囲内の値とすることが好ましい。
 この理由は、傾斜角θaをかかる範囲内の値とすることにより、拡散光の開き角を、より効率的に拡大することができるためである。
 すなわち、傾斜角θaが30°を超えた値となると、それに伴い活性エネルギー線の入射角度の絶対値も大きくなることから、空気と塗布層との界面における活性エネルギー線の反射の割合が増加してしまい、屈曲カラム構造を形成するにあたり、より高照度の活性エネルギー線を照射する必要が生じるためである。一方、活性エネルギー線が真に0°で入射した場合、屈曲が生じる方向を決定することができなくなって、結果的に屈曲が生じない可能性がある。
 したがって、屈曲カラム構造のうち、屈曲部よりも上方部分における柱状物の傾斜角θaを0.5~25°の範囲内の値とすることがより好ましく、1~20°の範囲内の値とすることがさらに好ましい。
 なお、傾斜角θaは、フィルム面に垂直な面であって、1本の柱状物全体を軸線に沿って2つに切断する面によってフィルムを切断した場合の断面において測定されるフィルム表面に対する法線の角度を0°とした場合の屈曲部よりも上方部分における柱状物の傾斜角(°)を意味する。
 より具体的には、図4(b)に示す通り、傾斜角θaは、屈曲カラム構造の上端面の法線と、屈曲部よりも上方部分における柱状物の最上部との為す角度のうち狭い側の角度を意味する。
 また、図4(b)に示す通り、柱状物が左側に傾いているときの傾斜角を基準とし、柱状物が右側に傾いているときの傾斜角をマイナスで表記する。
 また、図4(b)に示すように、屈曲カラム構造13´のうち、屈曲部よりも下方部分における柱状物のフィルム面の法線に対する傾斜角θbを1~60°の範囲内の値とすることが好ましい。
 この理由は、傾斜角θbをかかる範囲内の値とすることにより、拡散光の開き角を、より効率的に拡大することができるためである。
 すなわち、傾斜角θbが1°未満の値となると、上方部分のカラム構造との相乗効果を考慮しても、拡散光の開き角を拡大する効果を十分に得ることが困難になる場合があるためである。一方、傾斜角θbが60°を超えた値となると、それに伴い活性エネルギー線の入射角度の絶対値も大きくなることから、空気と塗布層との界面における活性エネルギー線の反射の割合が増加してしまい、屈曲カラム構造を形成するにあたり、より高照度の活性エネルギー線を照射する必要が生じるためである。また、上方部分のカラム構造との相乗効果を考慮すれば、敢えてこれ以上の傾斜角とせずとも、拡散光の開き角を十分に拡大することができるためである。
 したがって、屈曲カラム構造のうち、屈曲部よりも下方部分における柱状物の傾斜角θbを3~55°の範囲内の値とすることがより好ましく、5~50°の範囲内の値とすることがさらに好ましい。
 なお、傾斜角θbの定義は、基本的に傾斜角θaと同様である。
 但し、傾斜角θbは、屈曲カラム構造の屈曲面の法線と、屈曲部よりも下方部分における柱状物との為す角度のうち狭い側の角度を意味する。
 また、上述した傾斜角θaおよびθbが、下記関係式(1)を満足することが好ましい。
1≦|θb-θa|≦30    (1)
 この理由は、傾斜角θaおよびθbがかかる関係式を満足することにより、拡散光の開き角を、さらに効率的に拡大することができるためである。
 すなわち、|θb-θa|が1°未満の値となると、カラム構造に屈曲が生じていない場合と同然であり、拡散光の開き角を拡大する効果を得ることが困難になる場合があるためである。一方、|θb-θa|が30°を超えた値となると、上方部分のカラム構造と、下方部分のカラム構造と、のそれぞれに由来する拡散領域が離れすぎてしまい、却って拡散光の開き角を拡大する効果を得ることが困難になる場合があるためである。
 したがって、傾斜角θaおよびθbが、下記関係式(1´)を満足することがより好ましく、下記関係式(1´´)を満足することがさらに好ましい。
3≦|θb-θa|≦25    (1´)
5≦|θb-θa|≦20    (1´´)
4.膜厚
 また、本発明の光拡散フィルムの膜厚を60~700μmの範囲内の値とすることが好ましい。
 この理由は、光拡散フィルムの膜厚が60μm未満の値となると、屈曲カラム構造内を直進する入射光が増加し、光拡散を示すことが困難になる場合があるためである。一方、光拡散フィルムの膜厚が700μmを超えた値となると、光拡散フィルム用組成物に対して活性エネルギー線を照射して屈曲カラム構造を形成する際に、初期に形成されたカラム構造によって光重合の進行方向が拡散してしまい、所望の屈曲カラム構造を形成することが困難になる場合があるためである。
 したがって、光拡散フィルムの膜厚を90~450μmの範囲内の値とすることがより好ましく、120~250μmの範囲内の値とすることがさらに好ましい。
5.拡散光の開き角
 また、本発明の光拡散フィルムは、拡散光の開き角を45°以上の値とすることが好ましい。
 この理由は、カラム構造が屈曲を有さない場合であっても、45°未満の拡散光の開き角であれば、達成することができるためである。
 すなわち、拡散光の開き角が45°未満の値となると、光拡散フィルムをディスプレイに適用した場合に、拡散光の開き角が不十分であるため、1枚の光拡散フィルムでは十分な性能が得られず、複数枚の光拡散フィルムを使用する必要が生じるためである。一方、拡散光の開き角が過度に大きくなると、光拡散フィルムを反射型液晶ディスプレイやプロジェクションスクリーンといった用途に使用した場合に、拡散光が広がりすぎることにより、画像表示光が全体的に暗くなってしまう場合があるためである。
 したがって、本発明の光拡散フィルムにおける拡散光の開き角を、5~90°の範囲内の値とすることがより好ましく、55~80°の範囲内の値とすることがさらに好ましい。
6.粘着剤層
 また、本発明の光拡散フィルムは、その片面または両面に、被着体に対して積層するための粘着剤層を備えていてもよい。
 かかる粘着剤層を構成する粘着剤としては、特に制限されるものではなく、従来公知のアクリル系、シリコーン系、ウレタン系、ゴム系等の粘着剤を使用することができる。
[第2の実施形態]
 本発明の第2の実施形態は、屈折率が相対的に低い領域中に、屈折率が相対的に高い複数の柱状物をフィルム膜厚方向に林立させてなるカラム構造であって、屈折率が相対的に高い複数の柱状物が、当該柱状物の途中において屈曲部を有するカラム構造を有する光拡散フィルムの製造方法であって、下記工程(a)~(c)を含むことを特徴とする光拡散フィルムの製造方法である。
(a)(A)成分としての複数の芳香環を含有する(メタ)アクリル酸エステルと、(B)成分としてのウレタン(メタ)アクリレートと、(C)成分としての光重合開始剤と、(D)成分としての紫外線吸収剤と、を含む光拡散フィルム用組成物であって、(A)成分の含有量を、(B)成分100重量部に対して、25~400重量部の範囲内の値とするとともに、(C)成分の含有量を、(A)成分および(B)成分の合計量(100重量部)に対して、0.2~20重量部の範囲内の値とし、かつ、(D)成分の含有量を、(A)成分および(B)成分の合計量(100重量部)に対して、2重量部未満の値(但し、0重量部を除く。)とする光拡散フィルム用組成物を準備する工程
(b)光拡散フィルム用組成物を工程シートに対して塗布し、塗布層を形成する工程
(c)塗布層に対して活性エネルギー線を照射する工程
 以下、本発明の第2の実施形態を、第1の実施形態と異なる点を中心に、図面を参照しつつ、具体的に説明する。
1.工程(a):光拡散フィルムの準備工程
 かかる工程は、所定の光拡散フィルム用組成物を準備する工程である。
 より具体的には、(A)~(D)成分および所望によりその他の添加剤を混合する工程である。
 また、混合に際しては、室温下でそのまま撹拌してもよいが、均一性を向上させる観点からは、例えば、40~80℃の加温条件下にて撹拌して、均一な混合液とすることが好ましい。
 また、塗工に適した所望の粘度となるように、希釈溶剤をさらに加えることも好ましい。
 以下、光拡散フィルム用組成物について、より具体的に説明する。
(1)(A)成分
(1)-1 種類
 本発明における光拡散フィルム用組成物は、(A)成分として、複数の芳香環を含有する(メタ)アクリル酸エステルを含むことを特徴とする。
 この理由は、(A)成分として、特定の(メタ)アクリル酸エステルを含むことにより、(A)成分の重合速度を、(B)成分の重合速度よりも速くして、これらの成分間における重合速度に所定の差を生じさせ、両成分の共重合性を効果的に低下させることができるものと推定されるためである。
 その結果、光硬化させた際に、(B)成分に由来した屈折率が相対的に低い領域中に、(A)成分に由来した屈折率が相対的に高い複数の柱状物を林立させてなるカラム構造を効率よく形成することができる。
 また、(A)成分として、特定の(メタ)アクリル酸エステルを含むことにより、単量体の段階では(B)成分と十分な相溶性を有しつつも、重合の過程において複数繋がった段階では(B)成分との相溶性を所定の範囲にまで低下させて、カラム構造をさらに効率よく形成することができるものと推定される。
 さらに、(A)成分として、特定の(メタ)アクリル酸エステルを含むことにより、カラム構造における(A)成分に由来した領域の屈折率を高くして、(B)成分に由来した領域の屈折率との差を、所定以上の値に調節することができる。
 したがって、(A)成分として、特定の(メタ)アクリル酸エステルを含むことにより、後述する(B)成分の特性と相まって、(A)成分に由来した屈折率が相対的に高い領域と、(B)成分に由来した屈折率が相対的に低い領域とからなるカラム構造を効率的に得ることができる。
 なお、「複数の芳香環を含有する(メタ)アクリル酸エステル」とは、(メタ)アクリル酸エステルのエステル残基部分に複数の芳香環を有する化合物を意味する。
 また、「(メタ)アクリル酸」とは、アクリル酸とメタクリル酸の両方を意味する。
 また、このような(A)成分としての複数の芳香環を含有する(メタ)アクリル酸エステルとしては、例えば、(メタ)アクリル酸ビフェニル、(メタ)アクリル酸ナフチル、(メタ)アクリル酸アントラシル、(メタ)アクリル酸ベンジルフェニル、(メタ)アクリル酸ビフェニルオキシアルキル、(メタ)アクリル酸ナフチルオキシアルキル、(メタ)アクリル酸アントラシルオキシアルキル、(メタ)アクリル酸ベンジルフェニルオキシアルキル等、若しくは、芳香環上の水素原子の一部がハロゲン、アルキル、アルコキシ、ハロゲン化アルキル等によって置換されたもの等を挙げることができる。
 また、(A)成分としての複数の芳香環を含有する(メタ)アクリル酸エステルとして、ビフェニル環を含有する化合物を含むことが好ましく、特に、下記一般式(1)で表わされるビフェニル化合物を含むことが好ましい。
Figure JPOXMLDOC01-appb-C000003
(一般式(1)中、R~R10は、それぞれ独立しており、R1~R10の少なくとも1つは、下記一般式(2)で表わされる置換基であり、残りは、水素原子、水酸基、カルボキシル基、アルキル基、アルコキシ基、フッ素以外のハロゲン化アルキル基、ヒドロキシアルキル基、カルボキシアルキル基およびフッ素以外のハロゲン原子のいずれかの置換基である。)
Figure JPOXMLDOC01-appb-C000004
(一般式(2)中、R11は、水素原子またはメチル基であり、炭素数nは1~4の整数であり、繰り返し数mは1~10の整数である。)
 この理由は、(A)成分として、特定の構造を有するビフェニル化合物を含むことにより、(A)成分および(B)成分の重合速度に所定の差を生じさせ、(A)成分と、(B)成分との相溶性を所定の範囲にまで低下させて、両成分同士の共重合性をさらに低下させることができると推定されるためである。
 また、カラム構造における(A)成分に由来した領域の屈折率を高くして、(B)成分に由来した領域の屈折率との差を、所定以上の値に、より容易に調節することができる。
 また、一般式(1)におけるR1~R10が、アルキル基、アルコキシ基、ハロゲン化アルキル基、ヒドロキシアルキル基、およびカルボキシアルキル基のいずれかを含む場合には、そのアルキル部分の炭素数を1~4の範囲内の値とすることが好ましい。
 この理由は、かかる炭素数が4を超えた値となると、(A)成分の重合速度が低下したり、(A)成分に由来した領域の屈折率が低くなり過ぎたりして、カラム構造を効率的に形成することが困難になる場合があるためである。
 したがって、一般式(1)におけるR1~R10が、アルキル基、アルコキシ基、ハロゲン化アルキル基、ヒドロキシアルキル基、およびカルボキシアルキル基のいずれかを含む場合には、そのアルキル部分の炭素数を1~3の範囲内の値とすることがより好ましく、1~2の範囲内の値とすることがさらに好ましい。
 また、一般式(1)におけるR~R10が、ハロゲン化アルキル基またはハロゲン原子以外の置換基、すなわち、ハロゲンを含まない置換基であることが好ましい。
 この理由は、光拡散フィルムを焼却等する際に、ダイオキシンが発生することを防止して、環境保護の観点から好ましいためである。
 なお、従来の光拡散フィルムにおいては、所定のカラム構造を得るにあたり、モノマー成分を高屈折率化する目的で、モノマー成分においてハロゲン置換が行われることが一般的であった。
 この点、一般式(1)で表わされるビフェニル化合物であれば、ハロゲン置換を行わない場合であっても、高い屈折率とすることができる。
 したがって、本発明における光拡散フィルム用組成物を光硬化してなる光拡散フィルムであれば、ハロゲンを含まない場合であっても、良好な入射角度依存性を発揮することができる。
 また、一般式(1)におけるR2~R9のいずれか一つが、一般式(2)で表わされる置換基であることが好ましい。
 この理由は、一般式(2)で表わされる置換基の位置を、R1およびR10以外の位置とすることにより、光硬化させる前の段階において、(A)成分同士が配向し、結晶化することを効果的に防止することができるためである。
 さらに、光硬化させる前のモノマー段階で液状であり、希釈溶媒等を使用しなくとも、見掛け上(B)成分と均一に混合することができる。
 これにより、光硬化の段階において、(A)成分および(B)成分の微細なレベルでの凝集・相分離を可能とし、カラム構造を備えた光拡散フィルムを、より効率的に得ることができるためである。
 さらに、同様の観点から、一般式(1)におけるR3、R5、R6およびR8のいずれか一つが、一般式(2)で表わされる置換基であることが特に好ましい。
 また、一般式(2)で表わされる置換基における繰り返し数mを、通常1~10の整数とすることが好ましい。
 この理由は、繰り返し数mが10を超えた値となると、重合部位と、ビフェニル環とをつなぐオキシアルキレン鎖が長くなりすぎて、重合部位における(A)成分同士の重合を阻害する場合があるためである。
 したがって、一般式(2)で表わされる置換基における繰り返し数mを、1~4の整数とすることがより好ましく、1~2の整数とすることが特に好ましい。
 なお、同様の観点から、一般式(2)で表わされる置換基における炭素数nを、通常1~4の整数とすることが好ましい。
 また、重合部位である重合性炭素-炭素二重結合の位置が、ビフェニル環に対して近すぎて、ビフェニル環が立体障害となり、(A)成分の重合速度が低下する場合をも考慮すると、一般式(2)で表わされる置換基における炭素数nを、2~4の整数とすることがより好ましく、2~3の整数とすることが特に好ましい。
 また、一般式(1)で表わされるビフェニル化合物の具体例としては、下記式(3)~(4)で表わされる化合物を好ましく挙げることができる。
Figure JPOXMLDOC01-appb-C000005
Figure JPOXMLDOC01-appb-C000006
(1)-2 分子量
 また、(A)成分の分子量を、200~2,500の範囲内の値とすることが好ましい。
 この理由は、(A)成分の分子量を所定の範囲とすることにより、(A)成分の重合速度をさらに速くして、(A)成分および(B)成分の共重合性をより効果的に低下させることができるものと推定されるためである。
 その結果、光硬化させた際に、(B)成分に由来した屈折率が相対的に低い領域中に、(A)成分に由来した屈折率が相対的に高い複数の柱状物を林立させてなるカラム構造を、より効率よく形成することができる。
 すなわち、(A)成分の分子量が200未満の値となると、立体障害が小さくなるため(B)成分との共重合が生じ易くなるものと推定され、その結果、カラム構造を効率よく形成することが困難になる場合があるためである。一方、(A)成分の分子量が2,500を超えた値となると、(B)成分との分子量の差が小さくなるのにともなって、(A)成分の重合速度が低下して(B)成分の重合速度に近くなり、(B)成分との共重合が生じ易くなるものと推定され、その結果、カラム構造を効率よく形成することが困難になる場合があるためである。
 したがって、(A)成分の分子量を、240~1,500の範囲内の値とすることがより好ましく、260~1,000の範囲内の値とすることがさらに好ましい。
 なお、(A)成分の分子量は、分子の組成と、構成原子の原子量から得られる計算値から求めることができる。
(1)-3 単独使用
 また、本発明における光拡散フィルム用組成物は、カラム構造における屈折率が相対的に高い領域を形成するモノマー成分として、(A)成分を含むことを特徴とするが、(A)成分は単独成分で構成されることが好ましい。
 この理由は、このように構成することにより、(A)成分に由来した領域における屈折率のばらつきを効果的に抑制して、カラム構造を備えた光拡散フィルムを、より効率的に得ることができるためである。
 すなわち、(A)成分における(B)成分に対する相溶性が低い場合、例えば、(A)成分がハロゲン系化合物等の場合、(A)成分を(B)成分に相溶させるための第3成分として、他の(A)成分(例えば、非ハロゲン系化合物等)を併用する場合がある。
 しかしながら、この場合、かかる第3成分の影響により、(A)成分に由来した屈折率が相対的に高い領域における屈折率がばらついたり、低下し易くなったりすることがある。
 その結果、(B)成分に由来した屈折率が相対的に低い領域との屈折率差が不均一になったり、過度に低下し易くなったりする場合がある。
 したがって、(B)成分との相溶性を有する高屈折率なモノマー成分を選択し、それを単独の(A)成分として用いることが好ましい。
 なお、例えば、(A)成分としての式(3)で表わされるビフェニル化合物であれば、低粘度であることから、(B)成分との相溶性を有するため、単独の(A)成分として使用することができる。
(1)-4 屈折率
 また、(A)成分の屈折率を1.5~1.65の範囲内の値とすることが好ましい。
 この理由は、(A)成分の屈折率をかかる範囲内の値とすることにより、(A)成分に由来した領域の屈折率と、(B)成分に由来した領域の屈折率との差を、より容易に調節して、カラム構造を備えた光拡散フィルムを、より効率的に得ることができるためである。
 すなわち、(A)成分の屈折率が1.5未満の値となると、(B)成分の屈折率との差が小さくなり過ぎて、有効な光拡散角度領域を得ることが困難になる場合があるためである。一方、(A)成分の屈折率が1.65を超えた値となると、(B)成分の屈折率との差は大きくなるものの、(B)成分との見かけ上の相溶状態さえも形成することが困難になる場合があるためである。
 したがって、(A)成分の屈折率を、1.52~1.62の範囲内の値とすることがより好ましく、1.56~1.6の範囲内の値とすることがさらに好ましい。
 なお、上述した(A)成分の屈折率とは、光照射により硬化する前の(A)成分の屈折率を意味する。
 また、屈折率は、例えば、JIS K0062に準じて測定することができる。
(1)-5 含有量
 また、光拡散フィルム用組成物における(A)成分の含有量を、後述する(B)成分100重量部に対して、25~400重量部の範囲内の値とすることを特徴とする。
 この理由は、(A)成分の含有量が25重量部未満の値となると、(B)成分に対する(A)成分の存在割合が少なくなって、図1(b)の断面図に示すカラム構造における(A)成分に由来した部分の幅が、(B)成分に由来した部分の幅と比較して過度に小さくなり、屈曲が得られたとしても十分な拡散光の開き角を有するカラム構造を得ることが困難になる場合があるためである。一方、(A)成分の含有量が400重量部を超えた値となると、(B)成分に対する(A)成分の存在割合が多くなって、カラム構造における(A)成分に由来した部分の幅が、(B)成分に由来した部分の幅と比較して過度に大きくなり、屈曲が得られたとしても十分な拡散光の開き角を有するカラム構造を得ることが困難になる場合があるためである。
 したがって、(A)成分の含有量を、(B)成分100重量部に対して40~300重量部の範囲内の値とすることがより好ましく、50~200重量部の範囲内の値とすることがさらに好ましい。
(2)(B)成分
(2)-1 種類
 本発明における光拡散フィルム用組成物は、(B)成分として、ウレタン(メタ)アクリレートを含むことを特徴とする。
 この理由は、ウレタン(メタ)アクリレートであれば、(A)成分に由来した領域の屈折率と、(B)成分に由来した領域の屈折率との差を、より容易に調節できるばかりか、(B)成分に由来した領域の屈折率のばらつきを有効に抑制し、カラム構造を備えた光拡散フィルムを、より効率的に得ることができるためである。
 なお、(メタ)アクリレートとは、アクリレートおよびメタクリレートの両方を意味する。
 まず、ウレタン(メタ)アクリレートは、(B1)イソシアナート基を少なくとも2つ含有する化合物、(B2)ポリオール化合物、好ましくはジオール化合物、特に好ましくはポリアルキレングリコール、および(B3)ヒドロキシアルキル(メタ)アクリレートから形成される。
 なお、(B)成分には、ウレタン結合の繰り返し単位を有するオリゴマーも含むものとする。
 このうち、(B1)成分であるイソシアナート基を少なくとも2つ含有する化合物としては、例えば、2,4-トリレンジイソシアナート、2,6-トリレンジイソシアナート、1,3-キシリレンジイソシアナート、1,4-キシリレンジイソシアナート等の芳香族ポリイソシアナート、ヘキサメチレンジイソシアナート等の脂肪族ポリイソシアナート、イソホロンジイソシアナート(IPDI)、水素添加ジフェニルメタンジイソシアナート等の脂環式ポリイソシアナート、およびこれらのビウレット体、イソシアヌレート体、さらにはエチレングリコール、プロピレングリコール、ネオペンチルグリコール、トリメチロールプロパン、ヒマシ油等の低分子活性水素含有化合物との反応物であるアダクト体(例えば、キシリレンジイソシアナート系3官能アダクト体)等を挙げることができる。
 また、上述した中でも、脂環式ポリイソシアナートであることが、特に好ましい。
 この理由は、脂環式ポリイソシアナートであれば、脂肪族ポリイソシアナートと比較して、立体配座等の関係で各イソシアナート基の反応速度に差を設けやすいためである。
 これにより、(B1)成分が(B2)成分とのみ反応したり、(B1)成分が(B3)成分とのみ反応したりすることを抑制して、(B1)成分を、(B2)成分および(B3)成分と確実に反応させることができ、余分な副生成物の発生を防止することができる。
 その結果、カラム構造における(B)成分に由来した領域、すなわち、低屈折率領域の屈折率のばらつきを効果的に抑制することができる。
 また、脂環式ポリイソシアナートであれば、芳香族ポリイソシアナートと比較して、得られる(B)成分と、(A)成分との相溶性を所定の範囲に低下させて、カラム構造をより効率よく形成することができる。
 さらに、脂環式ポリイソシアナートであれば、芳香族ポリイソシアナートと比較して、得られる(B)成分の屈折率を小さくすることができることから、(A)成分の屈折率との差を大きくし、光拡散性をより確実に発現するとともに、光拡散角度領域内における拡散光の均一性の高いカラム構造をさらに効率よく形成することができる。
 また、このような脂環式ポリイソシアナートの中でも、脂肪族環を介してイソシアナート基を2つ含有する化合物が好ましい。
 この理由は、このような脂環式ジイソシアナートであれば、(B2)成分および(B3)成分と定量的に反応し、単一の(B)成分を得ることができるためである。
 このような脂環式ジイソシアナートとしては、イソホロンジイソシアナート(IPDI)を特に好ましく挙げることができる。
 この理由は、2つのイソシアナート基の反応性に有効な差異を設けることができるためである。
 また、ウレタン(メタ)アクリレートを形成する成分のうち、(B2)成分であるポリアルキレングリコールとしては、例えば、ポリエチレングリコール、ポリプロピレングリコール、ポリブチレングリコール、ポリへキシレングリコール等が挙げられ、中でも、ポリプロピレングリコールであることが、特に好ましい。
 この理由は、ポリプロピレングリコールであれば、(B)成分を硬化させた際に、当該硬化物における良好なソフトセグメントとなり、光拡散フィルムのハンドリング性や実装性を、効果的に向上させることができるためである。
 なお、(B)成分の重量平均分子量は、主に、(B2)成分の重量平均分子量により調節することができる。ここで、(B2)成分の重量平均分子量は、通常、2,300~19,500であり、好ましくは4,300~14,300であり、特に好ましくは6,300~12,300である。
 また、ウレタン(メタ)アクリレートを形成する成分のうち、(B3)成分であるヒドロキシアルキル(メタ)アクリレートとしては、例えば、2-ヒドロキシエチル(メタ)アクリレート、2-ヒドロキシプロピル(メタ)アクリレート、3-ヒドロキシプロピル(メタ)アクリレート、2-ヒドロキシブチル(メタ)アクリレート、3-ヒドロキシブチル(メタ)アクリレート、4-ヒドロキシブチル(メタ)アクリレート等が挙げられる。
 また、得られるウレタン(メタ)アクリレートの重合速度を低下させ、カラム構造をより効率的に形成する観点から、特に、ヒドロキシアルキルメタクリレートであることがより好ましく、2-ヒドロキシエチルメタクリレートであることがさらに好ましい。
 また、(B1)~(B3)成分によるウレタン(メタ)アクリレートの合成は、常法に従って実施することができる。
 このとき(B1)~(B3)成分の配合割合を、モル比にて(B1)成分:(B2)成分:(B3)成分=1~5:1:1~5の割合とすることが好ましい。
 この理由は、かかる配合割合とすることにより、(B2)成分の有する2つの水酸基に対してそれぞれ(B1)成分の有する一方のイソシアナート基が反応して結合し、さらに2つの(B1)成分がそれぞれ有するもう一方のイソシアナート基に対して、(B3)成分の有する水酸基が反応して結合したウレタン(メタ)アクリレートを効率的に合成することができるためである。
 したがって、(B1)~(B3)成分の配合割合を、モル比にて(B1)成分:(B2)成分:(B3)成分=1~3:1:1~3の割合とすることがより好ましく、2:1:2の割合とすることがさらに好ましい。
(2)-2 重量平均分子量
 また、(B)成分の重量平均分子量を、3,000~20,000の範囲内の値とすることが好ましい。
 この理由は、(B)成分の重量平均分子量を所定の範囲とすることにより、(A)成分および(B)成分の重合速度に所定の差を生じさせ、両成分の共重合性を効果的に低下させることができると推定されるためである。
 その結果、光硬化させた際に、(B)成分に由来した屈折率が相対的に低い領域中に、(A)成分に由来した屈折率が相対的に高い複数の柱状物を林立させてなるカラム構造を効率よく形成することができる。
 すなわち、(B)成分の重量平均分子量が3,000未満の値となると、(B)成分の重合速度が速くなって、(A)成分の重合速度に近くなり、(A)成分との共重合が生じ易くなる結果、カラム構造を効率よく形成することが困難になる場合があるためである。一方、(B)成分の重量平均分子量が20,000を超えた値となると、カラム構造を形成することが困難になったり、(A)成分との相溶性が過度に低下して、塗布段階で(A)成分が析出したりする場合があるためである。
 したがって、(B)成分の重量平均分子量を、5,000~15,000の範囲内の値とすることがより好ましく、7,000~13,000の範囲内の値とすることがさらに好ましい。
 なお、(B)成分の重量平均分子量は、ゲルパーミエーションクロマトグラフィー(GPC)を用いて測定することができる。
(2)-3 単独使用
 また、(B)成分は、分子構造や重量平均分子量が異なる2種以上を併用してもよいが、カラム構造における(B)成分に由来した領域の屈折率のばらつきを抑制する観点からは、1種類のみを用いることが好ましい。
 すなわち、(B)成分を複数用いた場合、(B)成分に由来した屈折率が相対的に低い領域における屈折率がばらついたり、高くなったりして、(A)成分に由来した屈折率が相対的に高い領域との屈折率差が不均一になったり、過度に低下する場合があるためである。
(2)-4 屈折率
 また、(B)成分の屈折率を1.4~1.55の範囲内の値とすることが好ましい。
 この理由は、(B)成分の屈折率をかかる範囲内の値とすることにより、(A)成分に由来した領域の屈折率と、(B)成分に由来した領域の屈折率との差を、より容易に調節して、カラム構造を備えた光拡散フィルムを、より効率的に得ることができるためである。
 すなわち、(B)成分の屈折率が1.4未満の値となると、(A)成分の屈折率との差は大きくなるものの、(A)成分との相溶性が極端に悪化し、カラム構造を形成することができないおそれがあるためである。一方、(B)成分の屈折率が1.55を超えた値となると、(A)成分の屈折率との差が小さくなり過ぎて、所望の入射角度依存性を得ることが困難になる場合があるためである。
 したがって、(B)成分の屈折率を、1.45~1.54の範囲内の値とすることがより好ましく、1.46~1.52の範囲内の値とすることがさらに好ましい。
 なお、上述した(B)成分の屈折率とは、光照射により硬化する前の(B)成分の屈折率を意味する。
 そして、屈折率は、例えば、JIS K0062に準じて測定することができる。
 また、上述した(A)成分の屈折率と、(B)成分の屈折率との差を、0.01以上の値とすることが好ましい。
 この理由は、かかる屈折率の差を所定の範囲内の値とすることにより、光の透過と拡散におけるより良好な入射角度依存性、およびより広い光拡散入射角度領域を有する光拡散フィルムを得ることができるためである。
 すなわち、かかる屈折率の差が0.01未満の値となると、入射光がカラム構造内で全反射する角度域が狭くなることから、光拡散における開き角が過度に狭くなる場合があるためである。一方、かかる屈折率の差が過度に大きな値となると、(A)成分と(B)成分の相溶性が悪化しすぎて、カラム構造を形成できないおそれがあるためである。
 したがって、(A)成分の屈折率と、(B)成分の屈折率との差を、0.05~0.5の範囲内の値とすることがより好ましく、0.1~0.2の範囲内の値とすることがさらに好ましい。
 なお、ここでいう(A)成分および(B)成分の屈折率とは、光照射により硬化する前の(A)成分および(B)成分の屈折率を意味する。
(2)-5 含有量
 また、光拡散フィルム用組成物における(B)成分の含有量を、光拡散フィルム用組成物の全体量100重量部に対して、10~80重量部の範囲内の値とすることが好ましい。
 この理由は、(B)成分の含有量が10重量部未満の値となると、(A)成分に対する(B)成分の存在割合が少なくなって、カラム構造における(B)成分に由来した部分の幅が、(A)成分に由来した部分の幅と比較して過度に小さくなり、屈曲が得られたとしても十分な拡散光の開き角を有するカラム構造を得ることが困難になる場合があるためである。一方、(B)成分の含有量が80重量部を超えた値となると、(A)成分に対する(B)成分の存在割合が多くなって、カラム構造における(B)成分に由来した部分の幅が、(A)成分に由来した部分の幅と比較して過度に大きくなり、屈曲が得られたとしても十分な拡散光の開き角を有するカラム構造を得ることが困難になる場合があるためである。
 したがって、(B)成分の含有量を、光拡散フィルム用組成物の全体量100重量部に対して、20~70重量部の範囲内の値とすることがより好ましく、30~60重量部の範囲内の値とすることがさらに好ましい。
(3)(C)成分
(3)-1 種類
 また、本発明における光拡散フィルム用組成物は、(C)成分として、光重合開始剤を含有させることを特徴とする。
 この理由は、光拡散フィルム用組成物に対して活性エネルギー線を照射した際に、効率的に、(B)成分に由来した屈折率が相対的に低い領域中に、(A)成分に由来した屈折率が相対的に高い複数の柱状物を林立させてなるカラム構造を形成することができるためである。
 ここで、光重合開始剤とは、紫外線等の活性エネルギー線の照射により、ラジカル種を発生させる化合物をいう。
 かかる(C)成分としての光重合開始剤は、α-ヒドロキシアセトフェノン型光重合開始剤、α-アミノアセトフェノン型光重合開始剤およびアシルフォスフィンオキサイド型重合開始剤からなる群から選択される少なくとも一種であることが好ましい。
 この理由は、これらの光重合開始剤であれば、カラム構造に、より明確に屈曲を生じさせることができることから、得られる光拡散フィルムにおける拡散光の開き角を、より効果的に拡大することができるためである。
 すなわち、これらの光重合開始剤であれば、屈曲したカラム構造の形成に際し、(A)成分および(B)成分に由来した領域の屈折率差がより大きくなるよう、これらの成分の分離を促しつつ硬化させることに寄与していると推測されるためである。
 光重合開始剤の具体例として、例えば、ベンゾイン、ベンゾインメチルエーテル、ベンゾインエチルエーテル、ベンゾインイソプロピルエーテル、ベンゾイン-n-ブチルエーテル、ベンゾインイソブチルエーテル、アセトフェノン、ジメチルアミノアセトフェノン、2,2-ジメトキシ-2-フェニルアセトフェノン、2,2-ジエトキシ-2-フェニルアセトフェノン、2-ヒドロキシ-2-メチル-1-フェニルプロパン-1-オン、1-ヒドロキシシクロヘキシルフェニルケトン、2-メチル-1-[4-(メチルチオ)フェニル]-2-モルフォリノ-プロパン-1-オン、4-(2-ヒドロキシエトキシ)フェニル-2-(ヒドロキシ-2-プロピル)ケトン、ベンゾフェノン、p-フェニルベンゾフェノン、4,4-ジエチルアミノベンゾフェノン、ジクロロベンゾフェノン、2-メチルアントラキノン、2-エチルアントラキノン、2-ターシャリーブチルアントラキノン、2-アミノアントラキノン、2-メチルチオキサントン、2-エチルチオキサントン、2-クロロチオキサントン、2,4-ジメチルチオキサントン、2,4-ジエチルチオキサントン、ベンジルジメチルケタール、アセトフェノンジメチルケタール、p-ジメチルアミン安息香酸エステル、オリゴ[2-ヒドロキシ-2-メチル-1-[4-(1-メチルビニル)フェニル]プロパン]等が挙げられ、これらのうち1種を単独で用いてもよいし、2種以上を組み合わせて用いてもよい。中でも、α-ヒドロキシアセトフェノン型光重合開始剤としては、2-ヒドロキシ-2-メチル-1-フェニルプロパン-1-オンであることが好ましい。
(3)-2 含有量
 また、光拡散フィルム用組成物における(C)成分の含有量を、(A)成分および(B)成分の合計量(100重量部)に対して、0.2~20重量部の範囲内の値とすることを特徴とする。
 この理由は、(C)成分の含有量をかかる範囲内の値とすることにより、後述する(D)成分の作用と相まって、光拡散フィルム用組成物の硬化を阻害することなく、フィルム内に形成されるカラム構造に屈曲を生じさせることができ、これにより、得られる光拡散フィルムにおける拡散光の開き角を効果的に拡大することができるためである。
 すなわち、(C)成分の含有量が0.2重量部未満の値となると、重合開始点が乏しくなることから、十分にフィルムを硬化させることが困難になる場合があるためである。一方、(C)成分の含有量が20重量部を超えた値となると、拡散光の開き角を十分に拡大することはできるものの、フィルムの黄変や耐久性の低下が生じ易くなる場合があるためである。また、塗布層の表層での紫外線吸収が過度に強くなって、却って硬化が阻害されたり、光拡散フィルム用組成物の臭気が強くなったり、得られるフィルムにおける初期の黄色味が強くなったりといった問題が生じ易くなる場合があるためである。
 したがって、(C)成分の含有量を、(A)成分および(B)成分の合計量(100重量部)に対して、0.5~15重量部の範囲内の値とすることがより好ましく、1~10重量部の範囲内の値とすることがさらに好ましい。
(4)(D)成分
(4)-1 種類
 また、本発明における光拡散フィルム用組成物は、(D)成分として、紫外線吸収剤を含むことを特徴とする。
 この理由は、(D)成分として、紫外線吸収剤を含むことにより、活性エネルギー線を照射した際に、所定波長の活性エネルギー線を、所定の範囲で選択的に吸収することができるためである。
 その結果、光拡散フィルム用組成物の硬化を阻害することなく、図3(a)~(b)に示すように、フィルム内に形成されるカラム構造に屈曲を生じさせることができ、これにより、得られる光拡散フィルムにおける拡散光の開き角を効果的に拡大することができる。
 ここで、現時点では、紫外線吸収剤が、フィルム内に形成されるカラム構造に屈曲を生じさせる具体的な機構について、十分には解明されていない。
 但し、以下のような機構であると推測される。
 すなわち、経験的には、紫外線吸収剤の添加量が少ない程、屈曲する角度が小さくなり、拡散光の開き角が小さくなることが確認されている。
 また、高圧水銀ランプの主波長である365nmの波長により近い箇所にピークを持つ紫外線吸収剤程、少ない添加量で屈曲が生じることが確認されている。
 したがって、紫外線吸収剤により、高圧水銀ランプから発生られる紫外線の波長が制御される程、すなわち、高圧水銀ランプから発せられる紫外線における各波長の強度比が変化する程、塗布層における膜厚方向下方への重合進行が遅くなり、ある程度重合が進行した深さで重合の進行方向が変化しているものと推定される。
 なお、重合の進行方向を変化させる因子としては、(A)成分と(B)成分における屈折率差が考えられるが、かかる屈折率差では計算上、実際に確認されている程の屈曲は生じないことになる。
 よって、重合の進行方向を変化させる因子の解明が急がれる。
 また、(D)成分が、ヒドロキシフェニルトリアジン系紫外線吸収剤、ベンゾトリアゾール系紫外線吸収剤、ベンゾフェノン系紫外線吸収剤およびヒドロキシベンゾエート系紫外線吸収剤からなる群から選択される少なくとも一種であることが好ましい。
 この理由は、これらの紫外線吸収剤であれば、カラム構造に、より明確に屈曲を生じさせることができることから、得られる光拡散フィルムにおける拡散光の開き角を、より効果的に拡大することができるためである。
 すなわち、高圧水銀ランプの主波長である365nmの波長により近い箇所にピークを持つこれらの紫外線吸収剤であれば、少ない添加量で屈曲を生じさせることが確認されているためである。
 また、ヒドロキシフェニルトリアジン系紫外線吸収剤の具体例としては、下記式(5)~(9)で表わされる化合物が好ましく挙げられる。
Figure JPOXMLDOC01-appb-C000007
Figure JPOXMLDOC01-appb-C000008
Figure JPOXMLDOC01-appb-C000009
Figure JPOXMLDOC01-appb-C000010
Figure JPOXMLDOC01-appb-C000011
 また、ベンゾトリアゾール系紫外線吸収剤の具体例としては、下記式(10)で表わされる化合物が好ましく挙げられる。
Figure JPOXMLDOC01-appb-C000012
(4)-2 吸収波長
 また、(D)成分が、波長330~380nmの光に対して吸収ピークを有することが好ましい。
 この理由は、(D)成分がこのような光吸収特性を有することにより、カラム構造に、さらに明確に屈曲を生じさせることができることから、得られる光拡散フィルムにおける拡散光の開き角を、さらに効果的に拡大することができるためである。
 すなわち、吸収ピークが波長330nm未満の値となると、高圧水銀ランプから発せられる主波長365nmの紫外線における各波長の強度比への影響が低く、カラム構造の屈曲、ひいては拡散光の開き角の拡大を十分に達成することが困難になる場合があるためである。一方、吸収ピークが波長380nmを超えた値となると、高圧水銀ランプから発せられる紫外線の全波長領域にわたって吸収が強くなり、フィルムを十分に硬化させることが困難になる場合があるためである。
 したがって、(D)成分における吸収ピークを、波長335~375nmの範囲内の値とすることがより好ましく、波長340~370nmの範囲内の値とすることがさらに好ましい。
(4)-3 含有量
 また、光拡散フィルム用組成物における(D)成分の含有量を、(A)成分および(B)成分の合計量(100重量部)に対して、2重量部未満の値(但し、0重量部を除く。)とすることを特徴とする。
 この理由は、(D)成分の含有量をかかる範囲内の値とすることにより、光拡散フィルム用組成物の硬化を阻害することなく、フィルム内に形成されるカラム構造に屈曲を生じさせることができ、これにより、得られる光拡散フィルムにおける拡散光の開き角を効果的に拡大することができるためである。
 すなわち、(D)成分の含有量が2重量部以上の値となると、光拡散フィルム用組成物の硬化が阻害されて、フィルム表面に収縮シワが生じたり、全く硬化しなくなったりする場合があるためである。一方、(D)成分の含有量が過度に少なくなると、フィルム内に形成されるカラム構造に対し、十分な屈曲を生じさせることが困難になり、得られる光拡散フィルムにおける拡散光の開き角を効果的に拡大することが困難になる場合があるためである。
 したがって、(D)成分の含有量を、(A)成分および(B)成分の合計量(100重量部)に対して、0.01~1.5重量部の範囲内の値とすることがより好ましく、0.02~1重量部の範囲内の値とすることがさらに好ましい。
(5)他の添加剤
 また、本発明の効果を損なわない範囲で、適宜、上述した化合物以外の添加剤を添加することができる。
 このような添加剤としては、例えば、ヒンダードアミン系光安定化剤、酸化防止剤、帯電防止剤、重合促進剤、重合禁止剤、赤外線吸収剤、可塑剤、希釈溶剤、およびレベリング剤等が挙げられる。
 なお、このような添加剤の含有量は、一般に、(A)成分および(B)成分の合計量(100重量部)に対して、0.01~5重量部の範囲内の値とすることが好ましく、0.02~3重量部の範囲内の値とすることがより好ましく、0.05~2重量部の範囲内の値とすることがさらに好ましい。
2.工程(b):塗布工程
 かかる工程は、図5(a)に示すように、光拡散フィルム用組成物を工程シート2に対して塗布し、塗布層1を形成する工程である。
 工程シートとしては、プラスチックフィルム、紙のいずれも使用することができる。
 このうち、プラスチックフィルムとしては、ポリエチレンテレフタレートフィルム等のポリエステル系フィルム、ポリエチレンフィルム、ポリプロピレンフィルム等のポリオレフィン系フィルム、トリアセチルセルロースフィルム等のセルロース系フィルム、およびポリイミド系フィルム等が挙げられる。
 また、紙としては、例えば、グラシン紙、コート紙、およびラミネート紙等が挙げられる。
 また、後述する工程を考慮すると、工程シート2としては、熱や活性エネルギー線に対する寸法安定性に優れたプラスチックフィルムであることが好ましい。
 このようなプラスチックフィルムとしては、上述したもののうち、ポリエステル系フィルム、ポリオレフィン系フィルムおよびポリイミド系フィルムが好ましく挙げられる。
 また、工程シートに対しては、光硬化後に、得られた光拡散フィルムを工程シートから剥離し易くするために、工程シートにおける光拡散フィルム用組成物の塗布面側に、剥離層を設けることが好ましい。
 かかる剥離層は、シリコーン系剥離剤、フッ素系剥離剤、アルキッド系剥離剤、オレフィン系剥離剤等、従来公知の剥離剤を用いて形成することができる。
 なお、工程シートの厚さは、通常、25~200μmの範囲内の値とすることが好ましい。
 また、工程シート上に光拡散フィルム用組成物を塗布する方法としては、例えば、ナイフコート法、ロールコート法、バーコート法、ブレードコート法、ダイコート法、およびグラビアコート法等、従来公知の方法により行うことができる。
 なお、このとき、塗布層の膜厚を80~700μmの範囲内の値とすることが好ましい。
3.工程(c):活性エネルギー線の照射工程
 かかる工程は、図5(b)に示すように、塗布層1に対して活性エネルギー線照射を行い、フィルム内に屈曲カラム構造を形成し、光拡散フィルムとする工程である。
 より具体的には、活性エネルギー線の照射工程においては、工程シートの上に形成された塗布層に対し、光線の平行度が高い平行光を照射する。
 ここで、平行光とは、発せられる光の方向が、いずれの方向から見た場合であっても広がりを持たない略平行な光を意味する。
 より具体的には、例えば、図6(a)に示すように、点光源202からの照射光50をレンズ204によって平行光60とした後、塗布層に照射したり、図6(b)~(c)に示すように、線状光源125からの照射光50を、照射光平行化部材200(200a、200b)によって平行光60とした後、塗布層に照射したりすることが好ましい。
 なお、図6(d)に示すように、照射光平行化部材200は、線状光源125による直接光のうち、光の向きがランダムとなる線状光源125の軸線方向と平行な方向において、例えば、板状部材210aや筒状部材210b等の遮光部材210を用いて光の向きを統一することにより、線状光源125による直接光を平行光に変換することができる。
 より具体的には、線状光源125による直接光のうち、板状部材210aや筒状部材210b等の遮光部材210に対する平行度が低い光は、これらに接触し、吸収される。
 したがって、板状部材210aや筒状部材210b等の遮光部材210に対する平行度が高い光、すなわち、平行光のみが、照射光平行化部材200を通過することになり、結果として、線状光源125による直接光が、照射光平行化部材200により平行光に変換されることになる。
 なお、板状部材210aや筒状部材210b等の遮光部材210の材料物質としては、遮光部材210に対する平行度の低い光を吸収できるものであれば特に制限されるものではなく、例えば、耐熱黒塗装を施したアルスター鋼板等を用いることができる。
 また、照射光の平行度を10°以下の値とすることが好ましい。
 この理由は、照射光の平行度をかかる範囲内の値とすることにより、カラム構造を効率的、かつ、安定的に形成することができるためである。
 したがって、照射光の平行度を5°以下の値とすることがより好ましく、2°以下の値とすることがさらに好ましい。
 また、照射光の照射角としては、図7に示すように、塗布層1の表面に対する法線の角度を0°とした場合の照射角θ3を、通常、-80~80°の範囲内の値とすることが好ましい。
 この理由は、照射角が-80~80°の範囲外の値となると、塗布層1の表面での反射等の影響が大きくなって、十分なカラム構造を形成することが困難になる場合があるためである。
 また、照射光としては、紫外線を用いることが好ましい。
 この理由は、電子線の場合、重合速度が非常に速いため、重合過程で(A)成分と(B)成分が十分に相分離できず、カラム構造を形成することが困難になる場合があるためである。一方、可視光等と比較した場合、紫外線の方が、その照射により硬化する紫外線硬化樹脂や、使用可能な光重合開始剤のバリエーションが豊富であることから、(A)成分および(B)成分の選択の幅を広げることができるためである。
 また、紫外線の照射条件としては、塗布層表面におけるピーク照度を0.5~10mW/cm2の範囲内の値とすることが好ましい。
 この理由は、かかるピーク照度が0.5mW/cm2未満の値となると、光拡散フィルム用組成物が紫外線吸収剤を含んでいるため、塗布層表面での紫外線吸収が生じ、重合によるカラム構造の形成が膜厚方向に沿って上方から下方に向かって進行せず、フィルムを硬化させることが困難となる場合があるためである。一方、かかるピーク照度が10mW/cm2を超えた値となると、重合によるカラム構造の形成が膜厚方向に沿って上方から下方に向かって瞬時に進んでしまい、屈曲が生じない場合があるためである。
 したがって、紫外線照射における塗布層表面のピーク照度を0.5~8mW/cm2の範囲内の値とすることがより好ましく、0.7~6mW/cm2の範囲内の値とすることがさらに好ましい。
 また、紫外線照射における塗布層表面における積算光量を10~200mJ/cm2の範囲内の値とすることが好ましい。
 この理由は、かかる積算光量が10mJ/cm2未満の値となると、光量不足により塗布層が硬化しなかったり、重合によるカラム構造の形成が膜厚方向に沿って上方から下方に向かって十分に進行せず、所定の屈曲が得られなくなったりする場合があるためである。一方、かかる積算光量が200mJ/cm2を超えた値となると、過度に紫外線が照射され、フィルムが黄変劣化、つまりフィルムの黄色味が強くなってしまう場合があるためである。
 したがって、紫外線照射における塗布層表面における積算光量を15~150mJ/cm2の範囲内の値とすることがより好ましく、20~100mJ/cm2の範囲内の値とすることがさらに好ましい。
 また、紫外線照射の際に、工程シート上に形成された塗布層を、0.1~10m/分の速度にて移動させることが好ましい。
 この理由は、かかる速度が0.1m/分未満の値となると、量産性が過度に低下する場合があるためである。一方、かかる速度が10m/分を超えた値となると、塗布層の硬化、言い換えれば、カラム構造の形成よりも速く、塗布層に対する紫外線の入射角度が変化してしまい、カラム構造の形成が不十分になる場合があるためである。
 したがって、紫外線照射の際に、工程シート上に形成された塗布層を、0.2~5m/分の範囲内の速度にて移動させることがより好ましく、0.3~3m/分の範囲内の速度にて移動させることがさらに好ましい。
 また、塗布層の温度を0~60℃の範囲内の値に制御しながら紫外線を照射することも好ましい。
 この理由は、塗布層の温度を制御することにより、(D)成分を光拡散フィルム用組成物中に完全に溶解させ、得られる内部構造をより大きく屈曲させることができるためである。
 したがって、塗布層の温度を5~50℃の範囲内の値とすることがより好ましく、15~30℃の範囲内の値とすることがさらに好ましい。
 なお、紫外線照射工程後の光拡散フィルムは、工程シートを剥離することによって、最終的に使用可能な状態となる。
 ここで、本発明においては、光拡散フィルム用組成物が(D)成分として所定量の紫外線吸収剤を含むことから、紫外線を照射した際に、所定波長の活性エネルギー線を、所定の範囲で選択的に吸収することができる。
 それ故、本発明においては、例えば、バンドパスフィルター等によって紫外線における波長分布を調節する必要は無い。
 したがって、本発明においては、バンドパスフィルター等を介することなく、紫外線光源から照射される光をそのまま塗布層に照射することが好ましい。
 すなわち、バンドパスフィルターは、長時間の紫外線照射に耐え得るべく、一般に石英ガラスを基材として用いているばかりでなく、多層スパッタ層を有することから、非常に高価である。
 また、屈曲を有するカラム構造を形成するにあたり、最適なものを検討する段階で、複数のバンドパスフィルターを試すことになり、さらに経済的に不利である。
 一方、紫外線吸収剤により屈曲を有するカラム構造を形成する場合、バンドパスフィルターと比較して格段に安価であるばかりか、種類と添加量の組み合わせを調節することで、より容易に最適なものを検討することができ、経済的に著しく有利である。
 また、バンドパスフィルターと紫外線吸収剤の両方により、紫外線の波長制御を行うことも想定されるが、その場合、過度の波長制御となり、塗布層を硬化させるのに十分な照度および光量を得ることが困難になる場合がある。
 また、紫外線の照度および光量を補うために光源強度を高くすることは、エネルギー損失が大きく、生産コストの上昇に繋がる。
 したがって、バンドパスフィルターと紫外線吸収剤を両方用いる利点は乏しいため、バンドパスフィルターを用いることなく紫外線の波長と、光重合開始剤やその他の成分の吸収波長を考慮した上で、紫外線吸収剤の種類と添加量を最適化することにより、屈曲を有するカラム構造を形成することが好ましい。
 以下、実施例を参照して、本発明をさらに詳細に説明する。
[実施例1]
1.低屈折率重合性化合物(B)成分の合成
 容器内に、(B2)成分としての重量平均分子量9,200のポリプロピレングリコール(PPG)1モルに対して、(B1)成分としてのイソホロンジイソシアナート(IPDI)2モル、および(B3)成分としての2-ヒドロキシエチルメタクリレート(HEMA)2モルを収容した後、常法に従って反応させ、重量平均分子量9,900のポリエーテルウレタンメタクリレートを得た。
 なお、ポリプロピレングリコールおよびポリエーテルウレタンメタクリレートの重量平均分子量は、ゲルパーミエーションクロマトグラフィー(GPC)にて、下記条件に沿って測定したポリスチレン換算値である。
・GPC測定装置:東ソー(株)製、HLC-8020
・GPCカラム :東ソー(株)製(以下、通過順に記載)
  TSK guard column HXL-H
  TSK gel GMHXL(×2)
  TSK gel G2000HXL
・測定溶媒   :テトラヒドロフラン
・測定温度   :40℃
2.光拡散フィルム用組成物の調製
 次いで、得られた(B)成分としての重量平均分子量9,900のポリエーテルウレタンメタクリレート100重量部に対し、(A)成分としての前記式(3)で表わされる分子量268のo-フェニルフェノキシエトキシエチルアクリレート(新中村化学(株)製、NKエステル A-LEN-10)150重量部と、(D)成分としての前記式(5)~(7)で表わされる紫外線吸収剤の混合品(BASF(株)製、TINUVIN 477)0.25重量部((A)成分および(B)成分の合計量(100重量部)に対して0.1重量部)と、(C)成分としての2-ヒドロキシ-2-メチル-1-フェニルプロパン-1-オン20重量部((A)成分および(B)成分の合計量(100重量部)に対して8重量部)とを添加した後、80℃の条件下にて加熱混合を行い、光拡散フィルム用組成物を得た。
 なお、(A)成分および(B)成分の屈折率は、アッベ屈折率(アタゴ(株)製、アッベ屈折計DR-M2、Na光源、波長589nm)を用いてJIS K0062に準じて測定したところ、それぞれ1.58および1.46であった。
 また、光拡散フィルム用組成物を構成する各成分の光吸収特性を測定した。
 すなわち、紫外可視近赤外分光光度計(島津製作所(株)製、UV-3600)を用いて、使用した(A)成分、(B)成分、(C)成分および(D)成分の各波長(nm)に対する透過率(%)または吸光度(-)を測定した。得られた波長-透過率チャートまたは波長-吸光度チャートを図8~10に示す。
 なお、図8における特性曲線Aは、使用した(A)成分の波長-透過率チャートであり、特性曲線Bは、使用した(B)成分の波長-透過率チャートであり、図9は、使用した(C)成分の波長-吸光度チャートであり、図10(a)は、使用した(D)成分の波長-吸光度チャートである。
 また、図10(b)は、実施例4~5で使用した(D)成分の波長-吸光度チャートであり、図10(c)は、実施例6~7で使用した(D)成分の波長-吸光度チャートである。
3.塗布工程
 次いで、得られた光拡散フィルム用組成物を、工程シートとしてのフィルム状の透明ポリエチレンテレフタレート(以下、PETと称する。)に対して塗布し、膜厚170μmの塗布層を形成した。
4.活性エネルギー線照射
 次いで、塗布層を図5(b)におけるB方向に移動させながら、中心光線平行度を±3°以内に制御した紫外線スポット平行光源(ジャテック(株)製)を用い、平行度が2°以下の平行光(主ピーク波長365nm、その他254、303、313nmにピークを有する高圧水銀ランプからの紫外線)を、照射角(図7のθ3)がほぼ10°となるように塗布層に照射した。
 その際のピーク照度は2.00mW/cm2、積算光量は53.13mJ/cm2、ランプ高さは240mmとし、塗布層の移動速度は0.2m/分とした。
 なお、このとき、塗布層の温度を23℃に維持した。
 次いで、確実な硬化を図るべく、塗布層の露出面側に、厚さ38μmの紫外線透過性を有する剥離フィルム(リンテック(株)製、SP-PET382050;紫外線照射側の表面における中心線平均粗さ0.01μm、ヘーズ値1.80%、像鮮明度425、波長360nmの透過率84.3%)をラミネートした。
 次いで、剥離フィルムの上から、上述した平行光の進行方向をランダムにした散乱光をピーク照度10mW/cm2、積算光量150mJ/cm2となるように照射して塗布層を完全硬化させ、工程シートと剥離フィルムを除いた状態での膜厚が170μmである光拡散フィルムを得た。
 なお、上述したピーク照度および積算光量は、受光器を取り付けたUV METER(アイグラフィックス(株)製、アイ紫外線積算照度計UVPF-A1)を塗布層の位置に設置して測定した。
 また、得られた光拡散フィルムの膜厚は、定圧厚さ測定器(宝製作所(株)製、テクロック PG-02J)を用いて測定した。
 また、得られた光拡散フィルムを、塗布層の移動方向に平行かつフィルム面と直交する面で切断した断面の模式図を図11(a)に示し、その断面写真を図11(b)に示す。
 また、得られた光拡散フィルムを、塗布層の移動方向に垂直かつフィルム面と直交する面で切断した断面の断面写真を図11(c)に示す。
 さらに、図11(b)に示す断面写真における屈曲部付近を拡大した写真を図12(a)に示し、屈曲部よりも下方部分を拡大した写真を図12(b)に示す。
 なお、光拡散フィルムの切断は剃刀を用いて行い、断面の写真の撮影はデジタルマイクロスコープ(キーエンス(株)製、VHX-2000)を用いて反射観察により行った。
5.光拡散特性の評価
 得られた光拡散フィルムの光拡散特性を評価した。
 すなわち、PETと剥離フィルムにより挟まれた状態で得られた光拡散フィルムのPET表面に粘着剤層を設け、厚さ1.1mmのソーダガラスに対して貼合し、評価用試験片とした。
 次いで、コノスコープ(autronic-MELCHERS GmbH社製)を用いて、図13に示すように、試験片のガラス側より、光拡散フィルムに対して、入射角θ1(°)を0°、5°、10°、15°、20°、25°、30°、35°、40°、45°、50°、55°に変えながら光を入射した。得られたコノスコープ画像を図14(a)~(d)、図15(a)~(d)および図16(a)~(d)に示す。
 また、比較のために、実施例2((D)成分の添加量:(A)成分および(B)成分の合計量100重量部に対して0.067重量部)のコノスコープ画像を図14(e)~(h)、図15(e)~(h)および図16(e)~(h)に示し、実施例3((D)成分の添加量:(A)成分および(B)成分の合計量100重量部に対して0.33重量部)のコノスコープ画像を図14(i)~(l)、図15(i)~(l)および図16(i)~(l)に示し、比較例1((D)成分の添加量:0重量部)のコノスコープ画像を図14(m)~(p)、図15(m)~(p)および図16(m)~(p)に示す。
 また、コノスコープを用いて、入射角θ1=5°の光を入射した場合における拡散光の出射角(°)に対応する輝度(cd/cm2)を測定した。得られた出射角-輝度チャートを図17に示す。
 なお、図17における特性曲線Aが実施例1((D)成分の添加量:(A)成分および(B)成分の合計量100重量部に対して0.1重量部)における出射角-輝度チャートであり、特性曲線Bが実施例2((D)成分の添加量:(A)成分および(B)成分の合計量100重量部に対して0.067重量部)における出射角-輝度チャートであり、特性曲線Cが実施例3((D)成分の添加量:(A)成分および(B)成分の合計量100重量部に対して0.033重量部)における出射角-輝度チャートであり、特性曲線Dが比較例1((D)成分の添加量:0重量部)における出射角-輝度チャートである。
 なお、各実施例、比較例等における紫外線吸収剤の添加量、フィルムの製造条件、フィルム内に形成された内部構造の種類等を表1に示す。
[実施例2]
 実施例2では、光拡散フィルム用組成物を調製する際に、(D)成分としての紫外線吸収剤の添加量を0.167重量部((A)成分および(B)成分の合計量(100重量部)に対して0.067重量部)に変えたほかは、実施例1と同様に光拡散フィルムを製造し、評価した。得られた結果を、表1、図18~19および図14~17に示す。
 なお、図18(a)は、得られた光拡散フィルムを、塗布層の移動方向に平行かつフィルム面と直交する面で切断した断面の模式図であり、図18(b)は、その断面写真である。
 また、図18(c)は、得られた光拡散フィルムを、塗布層の移動方向に垂直かつフィルム面と直交する面で切断した断面の断面写真である。
 また、図19(a)は、図18(b)に示す断面写真における屈曲部付近を拡大した写真であり、図19(b)は、屈曲部よりも下方部分を拡大した写真である。
 また、図14(e)~(h)、図15(e)~(h)および図16(e)~(h)が実施例2におけるコノスコープ画像であり、図17における特性曲線Bが実施例2における出射角-輝度チャートである。
[実施例3]
 実施例3では、光拡散フィルム用組成物を調製する際に、(D)成分としての紫外線吸収剤の添加量を0.083重量部((A)成分および(B)成分の合計量(100重量部)に対して0.033重量部)に変えたほかは、実施例1と同様に光拡散フィルムを製造し、評価した。得られた結果を、表1、図20~21および図14~17に示す。
 なお、図20(a)は、得られた光拡散フィルムを、塗布層の移動方向に平行かつフィルム面と直交する面で切断した断面の模式図であり、図20(b)は、その断面写真である。
 また、図20(c)は、得られた光拡散フィルムを、塗布層の移動方向に垂直かつフィルム面と直交する面で切断した断面の断面写真である。
 また、図21(a)は、図20(b)に示す断面写真における屈曲部付近を拡大した写真であり、図21(b)は、屈曲部よりも下方部分を拡大した写真である。
 また、図14(i)~(l)、図15(i)~(l)および図16(i)~(l)が実施例3におけるコノスコープ画像であり、図17における特性曲線Cが実施例3における出射角-輝度チャートである。
[実施例4]
 実施例4では、光拡散フィルム用組成物を調製する際に、(D)成分としての紫外線吸収剤を前記式(8)~(9)で表わされる化合物の混合品であるBASF(株)製のTINUVIN 400に変えるとともに、その添加量を1.5重量部((A)成分および(B)成分の合計量(100重量部)に対して0.6重量部)としたほかは、実施例1と同様に光拡散フィルムを製造し、評価した。得られた結果を、表1および図22~27に示す。
 なお、図22(a)は、得られた光拡散フィルムを、塗布層の移動方向に平行かつフィルム面と直交する面で切断した断面の模式図であり、図22(b)は、その断面写真である。
 また、図22(c)は、得られた光拡散フィルムを、塗布層の移動方向に垂直かつフィルム面と直交する面で切断した断面の断面写真である。
 また、図23(a)は、図22(b)に示す断面写真における屈曲部付近を拡大した写真であり、図23(b)は、屈曲部よりも下方部分を拡大した写真である。
 また、図24(a)~(d)、図25(a)~(d)および図26(a)~(d)が実施例4におけるコノスコープ画像である。
 また、比較のために、実施例5((D)成分の添加量:(A)成分および(B)成分の合計量100重量部に対して0.3重量部)のコノスコープ画像を図24(e)~(h)、図25(e)~(h)および図26(e)~(h)に示し、比較例1((D)成分の添加量:0重量部)のコノスコープ画像を図24(i)~(l)、図25(i)~(l)および図26(i)~(l)に示す。
 さらに、図27における特性曲線Aが実施例4((D)成分の添加量:(A)成分および(B)成分の合計量100重量部に対して0.6重量部)における出射角-輝度チャートであり、特性曲線Bが実施例5((D)成分の添加量:(A)成分および(B)成分の合計量100重量部に対して0.3重量部)における出射角-輝度チャートであり、特性曲線Cが比較例1((D)成分の添加量:0重量部)における出射角-輝度チャートである。
[実施例5]
 実施例5では、光拡散フィルム用組成物を調製する際に、(D)成分としての紫外線吸収剤を前記式(8)~(9)で表わされる化合物の混合品であるBASF(株)製のTINUVIN 400に変えるとともに、その添加量を0.75重量部((A)成分および(B)成分の合計量(100重量部)に対して0.3重量部)としたほかは、実施例1と同様に光拡散フィルムを製造し、評価した。得られた結果を、表1、図28~29および図24~27に示す。
 なお、図28(a)は、得られた光拡散フィルムを、塗布層の移動方向に平行かつフィルム面と直交する面で切断した断面の模式図であり、図28(b)は、その断面写真である。
 また、図28(c)は、得られた光拡散フィルムを、塗布層の移動方向に垂直かつフィルム面と直交する面で切断した断面の断面写真である。
 また、図29(a)は、図28(b)に示す断面写真における屈曲部付近を拡大した写真であり、図29(b)は、屈曲部よりも下方部分を拡大した写真である。
 また、図24(e)~(h)、図25(e)~(h)および図26(e)~(h)が実施例5におけるコノスコープ画像であり、図27における特性曲線Bが実施例5における出射角-輝度チャートである。
[実施例6]
 実施例6では、光拡散フィルム用組成物を調製する際に、(D)成分としての紫外線吸収剤を前記式(10)で表わされるBASF(株)製のTINUVIN 384-2に変えるとともに、その添加量を0.5重量部((A)成分および(B)成分の合計量(100重量部)に対して0.2重量部)としたほかは、実施例1と同様に光拡散フィルムを製造し、評価した。得られた結果を、表1および図30~35に示す。
 なお、図30(a)は、得られた光拡散フィルムを、塗布層の移動方向に平行かつフィルム面と直交する面で切断した断面の模式図であり、図30(b)は、その断面写真である。
 また、図30(c)は、得られた光拡散フィルムを、塗布層の移動方向に垂直かつフィルム面と直交する面で切断した断面の断面写真である。
 また、図31(a)は、図30(b)に示す断面写真における屈曲部分付近を拡大した写真であり、図31(b)は、屈曲部よりも下方部分を拡大した写真である。
 また、図32(a)~(d)、図33(a)~(d)および図34(a)~(d)が実施例6におけるコノスコープ画像である。
 また、比較のために、実施例7((D)成分の添加量:(A)成分および(B)成分の合計量100重量部に対して0.1重量部)のコノスコープ画像を図32(e)~(h)、図33(e)~(h)および図34(e)~(h)に示し、比較例1((D)成分の添加量:0重量部)のコノスコープ画像を図32(i)~(l)、図33(i)~(l)および図34(i)~(l)に示す。
 さらに、図35における特性曲線Aが実施例6((D)成分の添加量:(A)成分および(B)成分の合計量100重量部に対して0.2重量部)における出射角-輝度チャートであり、特性曲線Bが実施例7((D)成分の添加量:(A)成分および(B)成分の合計量100重量部に対して0.1重量部)における出射角-輝度チャートであり、特性曲線Cが比較例1((D)成分の添加量:0重量部)における出射角-輝度チャートである。
 なお、図35に示す出射角-輝度チャートは、入射角θ1を10°に変えて測定した。
[実施例7]
 実施例7では、光拡散フィルム用組成物を調製する際に、(D)成分としての紫外線吸収剤を前記式(10)で表わされるBASF(株)製のTINUVIN 384-2に変えるとともに、その添加量を0.25重量部((A)成分および(B)成分の合計量(100重量%)に対して0.1重量%)としたほかは、実施例1と同様に光拡散フィルムを製造し、評価した。得られた結果を、表1、図36~37および図32~35に示す。
 なお、図36(a)は、得られた光拡散フィルムを、塗布層の移動方向に平行かつフィルム面と直交する面で切断した断面の模式図であり、図36(b)は、その断面写真である。
 また、図36(c)は、得られた光拡散フィルムを、塗布層の移動方向に垂直かつフィルム面と直交する面で切断した断面の断面写真である。
 また、図37(a)は、図36(b)に示す断面写真における屈曲部付近を拡大した写真であり、図37(b)は、屈曲部よりも下方部分を拡大した写真である。
 また、図32(e)~(h)、図33(e)~(h)および図34(e)~(h)が実施例7におけるコノスコープ画像であり、図35における特性曲線Bが実施例7における出射角-輝度チャートである。
[実施例8]
 実施例8では、塗布層に対して活性エネルギー線を照射する前に、塗布層を5℃の環境下に15分間放置し、その後、5℃に冷却された状態の塗布層に対し、直ちに活性エネルギー線を照射したほかは、実施例1と同様に光拡散フィルムを製造し、評価した。得られた結果を、表1および図38~41に示す。
 なお、図38(a)は、得られた光拡散フィルムを、塗布層の移動方向に平行かつフィルム面と直交する面で切断した断面の模式図であり、図38(b)は、その断面写真である。
 また、図39(a)~(d)、図40(a)~(d)および図41(a)~(d)が実施例8におけるコノスコープ画像である。
 また、比較のために、実施例1((D)成分の添加量:(A)成分および(B)成分の合計量100重量部に対して0.1重量部)のコノスコープ画像を図39(e)~(h)、図40(e)~(h)および図41(e)~(h)に示し、比較例1((D)成分の添加量:0重量部)のコノスコープ画像を図39(i)~(l)、図40(i)~(l)および図41(i)~(l)に示す。
[比較例1]
 比較例1では、光拡散フィルム用組成物を調製する際に、(D)成分としての紫外線吸収剤を添加しなかったほかは、実施例1と同様に光拡散フィルムを製造し、評価した。得られた結果を、表1、図42、図14~17、図24~27、図32~35および図39~41等に示す。
 なお、図42(a)は、得られた光拡散フィルムを、塗布層の移動方向に平行かつフィルム面と直交する面で切断した断面の模式図であり、図42(b)は、その断面写真である。
 また、図42(c)は、得られた光拡散フィルムを、塗布層の移動方向に垂直かつフィルム面と直交する面で切断した断面の断面写真である。
 また、図14(m)~(p)、図15(m)~(p)、図16(m)~(p)、図24(i)~(l)、図25(i)~(l)、図26(i)~(l)、図32(i)~(l)、図33(i)~(l)および図34(i)~(l)、図39(i)~(l)、図40(i)~(l)および図41(i)~(l)等が比較例1におけるコノスコープ画像であり、図17における特性曲線D、図27における特性曲線Cおよび図35における特性曲線Cが比較例1における出射角-輝度チャートである。
[比較例2]
 比較例2では、光拡散フィルム用組成物を調製する際に、(D)成分としての紫外線吸収剤の添加量を7.5重量部((A)成分および(B)成分の合計量(100重量部)に対して3重量部)に変えたほかは、実施例1と同様に光拡散フィルムの製造を試みた。
 その結果、フィルムが全く硬化しなかった。
[比較例3]
 比較例3では、塗布層に対して活性エネルギー線を照射する際に、紫外線スポット平行光源と、塗布層との間に、波長370nm付近の紫外線のみを透過させる特性を有するバンドバスフィルター(Edmund Optics(株)製、B-370)を配置して活性エネルギー線を照射したほかは、比較例1と同様に光拡散フィルムを製造し、評価した。得られた結果を、表1および図43~46に示す。
 なお、図43(a)は、得られた光拡散フィルムを、塗布層の移動方向に平行かつフィルム面と直交する面で切断した断面の模式図であり、図43(b)は、その断面写真である。
 また、図44(a)~(d)、図45(a)~(d)および図46(a)~(d)が比較例3におけるコノスコープ画像である。
 また、比較のために、実施例1(D)成分の添加量:(A)成分および(B)成分の合計量100重量部に対して0.1重量部)のコノスコープ画像を図44(e)~(h)、図45(e)~(h)および図46(e)~(h)に示し、比較例1((D)成分の添加量:0重量部)のコノスコープ画像を図44(i)~(l)、図45(i)~(l)および図46(i)~(l)に示す。
 さらに、使用したバンドパスフィルターの光透過特性を示す波長-透過率チャートを図47に示す。
[比較例4]
 比較例4では、塗布層に対して活性エネルギー線を照射する際に、紫外線スポット平行光源と、塗布層との間に、波長370nm付近の紫外線のみを透過させる特性を有するバンドパスフィルター(Edmund Optics(株)製、B-370)を配置して活性エネルギー線を照射したほかは、実施例1と同様に光拡散フィルムを製造した。
 その結果、図48に示すように、フィルムの表面のみが硬化して収縮シワが発生しており、フィルム内にカラム構造は形成されていなかった。
[参考例1]
 参考例1では、塗布層に対する活性エネルギー線の照射を、紫外線スポット平行光源の代わりに線状の高圧水銀ランプを用いて、以下のように行った。
 すなわち、線状の高圧水銀ランプに集光用のコールドミラーが付属した紫外線照射装置(アイグラフィックス(株)製、ECS-4011GX)を準備した。
 次いで、熱線カットフィルター枠上に遮光版を配置し、塗布層の表面に照射される紫外線が、線状光源の長軸方向から眺めたときの塗布層表面の法線を0°とした場合に、線状光源からの直接の紫外線の照射角(図7のθ3)が16°となるように設定した。
 このとき、塗布層表面から線状光源までの高さは500mmとし、ピーク照度は2.0mW/cm2、積算光量は50mJ/cm2となるように設定した。
 また、遮光板等での反射光が、照射機内部で迷光となり、塗布層の光硬化に影響を及ぼすことを防ぐため、コンベア付近にも遮光板を設け、線状光源から直接発せられる紫外線のみが塗布層に対して照射されるように設定した。
 次いで、コンベアにより、塗布層を0.2m/分の速度にて移動させながら紫外線を照射した。
 そのほかは、実施例1と同様に光拡散フィルムを製造し、評価した。得られた結果を、表1および図49~51に示す。
 なお、図49(a)は、得られた光拡散フィルムを、塗布層の移動方向に平行かつフィルム面と直交する面で切断した断面の模式図であり、図49(b)は、その断面写真であり、図49(c)は、図49(b)に示す断面写真における屈曲部付近を拡大した写真である。
 また、図50(a)~(c)および図51(a)~(b)に参考例1におけるコノスコープ画像を示す。
 これらのコノスコープ画像は、光拡散フィルムに対して、入射角θ1(°)を10°、20°、30°、40°、50°に変えながら光を入射して得た。
 また、比較のために、実施例1((D)成分の添加量:(A)成分および(B)成分の合計量100重量部に対して0.1重量部)のコノスコープ画像を図50(d)~(f)および図51(c)~(d)に示す。
 以上の実施例1~9および比較例1~2より、所定の光拡散フィルム用組成物に対し、所定の範囲で紫外線吸収剤を添加することで、屈曲部を有する柱状物等からなる所定のカラム構造を形成することができ、ひいては、拡散光の開き角を効果的に拡大した光拡散フィルムを得られることが理解される。
 また、比較例3および4より、バンドパスフィルターを用いて紫外線を照射した場合には、屈曲部を有する柱状物等からなる所定のカラム構造を形成できないことが理解される。
 さらに、参考例1より、屈曲部を有する板状領域からなる所定のルーバー構造を形成してなる光拡散フィルムでは、拡散光の開き角を効果的に拡大できるものの、光拡散入射角度領域と、非光拡散入射角度領域との間における光の拡散具合の切り替わりが急峻になるばかりか、板状領域の延び方向における拡散光の開き角が著しく小さくなることが理解される。
Figure JPOXMLDOC01-appb-T000013
*1カッコ内の数値は、(A)成分および(B)成分の合計量(100重量部)に対する(D)成分の添加量(重量部)を示す。
*2比較例2では、活性エネルギー線を照射しても塗布層が硬化せず、フィルムを得ることができなかった。
*3比較例4では、フィルムの表面のみが硬化して収縮シワが発生し、フィルムを得ることができなかった。
 以上、詳述したように、本発明によれば、フィルム内に、屈曲部を有する柱状物等からなる所定のカラム構造を形成することにより、拡散光の開き角を効果的に拡大した光拡散フィルムを得ることができるようになった。
 したがって、本発明の光拡散フィルム等は、反射型液晶表示装置における光制御膜の他、視野角制御フィルム、視野角拡大フィルム、さらにはプロジェクション用スクリーンにも適用することができ、これらの高品質化に著しく寄与することが期待される。
1:塗布層、2:工程シート、10:等方性光拡散フィルム、10´:屈曲カラム構造を有する等方性光拡散フィルム、12:屈折率が相対的に高い柱状物、13:カラム構造、13´:屈曲カラム構造、13a:カラム構造の境界面、14:屈折率が相対的に低い領域、50:光源からの照射光、60:平行光、125:線状光源、200:照射光平行化部材、202:点光源、204:レンズ、210:遮光部材、210a:板状部材、210b:筒状部材

Claims (9)

  1.  屈折率が相対的に低い領域中に、屈折率が相対的に高い複数の柱状物をフィルム膜厚方向に林立させてなるカラム構造を有する光拡散フィルムであって、
     前記屈折率が相対的に高い複数の柱状物が、当該柱状物の途中において屈曲部を有していることを特徴とする光拡散フィルム。
  2.  前記カラム構造のうち、前記屈曲部よりも上方部分における前記柱状物のフィルム面の法線に対する傾斜角θaを0~30°の範囲内の値とするとともに、前記屈曲部よりも下方部分における前記柱状物のフィルム面の法線に対する傾斜角θbを1~60°の範囲内の値とすることを特徴とする請求項1に記載の光拡散フィルム。
  3.  前記傾斜角θaおよびθbが、下記関係式(1)を満足することを特徴とする請求項2に記載の光拡散フィルム。
    1≦|θb-θa|≦30    (1)
  4.  前記カラム構造の厚さLを50~700μmの範囲内の値とすることを特徴とする請求項1~3のいずれか一項に記載の光拡散フィルム。
  5.  前記カラム構造のうち、前記屈曲部よりも上方部分における前記柱状物の長さLaを5~200μmの範囲内の値とするとともに、前記屈曲部よりも下方部分における前記柱状物の長さLbを20~400μmの範囲内の値とすることを特徴とする請求項1~4のいずれか一項に記載の光拡散フィルム。
  6.  前記長さLaおよびLbが、下記関係式(2)を満足することを特徴とする請求項5に記載の光拡散フィルム
    0.01≦La/Lb≦10    (2)
  7.  屈折率が相対的に低い領域中に、屈折率が相対的に高い複数の柱状物をフィルム膜厚方向に林立させてなるカラム構造であって、前記屈折率が相対的に高い複数の柱状物が、当該柱状物の途中において屈曲部を有するカラム構造を有する光拡散フィルムの製造方法であって、
     下記工程(a)~(c)を含むことを特徴とする光拡散フィルムの製造方法。
    (a)(A)成分としての複数の芳香環を含有する(メタ)アクリル酸エステルと、(B)成分としてのウレタン(メタ)アクリレートと、(C)成分としての光重合開始剤と、(D)成分としての紫外線吸収剤と、を含む光拡散フィルム用組成物であって、前記(A)成分の含有量を、前記(B)成分100重量部に対して、25~400重量部の範囲内の値とするとともに、前記(C)成分の含有量を、前記(A)成分および(B)成分の合計量(100重量部)に対して、0.2~20重量部の範囲内の値とし、かつ、前記(D)成分の含有量を、前記(A)成分および(B)成分の合計量(100重量部)に対して、2重量部未満の値(但し、0重量部を除く。)とする光拡散フィルム用組成物を準備する工程
    (b)前記光拡散フィルム用組成物を工程シートに対して塗布し、塗布層を形成する工程
    (c)前記塗布層に対して活性エネルギー線を照射する工程
  8.  前記(D)成分として、波長330~380nmの光に対して吸収ピークを有する紫外線吸収剤を用いることを特徴とする請求項7に記載の光拡散フィルムの製造方法。
  9.  前記(D)成分として、ヒドロキシフェニルトリアジン系紫外線吸収剤、ベンゾトリアゾール系紫外線吸収剤、ベンゾフェノン系紫外線吸収剤およびヒドロキシベンゾエート系紫外線吸収剤からなる群から選択される少なくとも一種を用いることを特徴とする請求項7または8に記載の光拡散フィルムの製造方法。
PCT/JP2014/054397 2013-03-29 2014-02-25 光拡散フィルムおよび光拡散フィルムの製造方法 WO2014156421A1 (ja)