WO2014133102A1 - Polymère biocompatible en tant que matière antithrombogène, carbonate cyclique utile comme précurseur correspondant et procédé pour sa production - Google Patents

Polymère biocompatible en tant que matière antithrombogène, carbonate cyclique utile comme précurseur correspondant et procédé pour sa production Download PDF

Info

Publication number
WO2014133102A1
WO2014133102A1 PCT/JP2014/054948 JP2014054948W WO2014133102A1 WO 2014133102 A1 WO2014133102 A1 WO 2014133102A1 JP 2014054948 W JP2014054948 W JP 2014054948W WO 2014133102 A1 WO2014133102 A1 WO 2014133102A1
Authority
WO
WIPO (PCT)
Prior art keywords
group
polymer
compound
ether
bond
Prior art date
Application number
PCT/JP2014/054948
Other languages
English (en)
Japanese (ja)
Inventor
賢 田中
和樹 福島
千香子 佐藤
彩乃 佐々木
裕人 井上
Original Assignee
国立大学法人山形大学
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from JP2013037994A external-priority patent/JP6226357B2/ja
Priority claimed from JP2013111270A external-priority patent/JP6320688B2/ja
Application filed by 国立大学法人山形大学 filed Critical 国立大学法人山形大学
Publication of WO2014133102A1 publication Critical patent/WO2014133102A1/fr

Abstract

L'invention concerne une composition de polymère biocompatible comprenant une structure présentant au moins un groupe éther de chaîne latérale et une chaîne principale formée à partir d'un squelette polymère biodégradable ainsi qu'un composé intermédiaire pour la production de la composition de polymère et un procédé pour sa production. Le composé intermédiaire est produit par l'exposition d'un composé diol présentant des groupes carboxyle à une source de carbone pour la cyclisation du fragment diol du composé diol en présence d'un solvant organique tout en protégeant les groupes carboxyle à l'aide d'une base organique, puis un polymère biocompatible est produit par la polymérisation avec ouverture de cycle du composé intermédiaire. Un dispositif médical présentant un caractère antithrombogène supérieur peut être obtenu à l'aide de cette composition de polymère.
PCT/JP2014/054948 2013-02-27 2014-02-27 Polymère biocompatible en tant que matière antithrombogène, carbonate cyclique utile comme précurseur correspondant et procédé pour sa production WO2014133102A1 (fr)

Applications Claiming Priority (4)

Application Number Priority Date Filing Date Title
JP2013037994A JP6226357B2 (ja) 2013-02-27 2013-02-27 抗血栓性材料としての生体親和性ポリマー
JP2013-037994 2013-02-27
JP2013-111270 2013-05-27
JP2013111270A JP6320688B2 (ja) 2013-05-27 2013-05-27 環状カーボネートの製造方法

Publications (1)

Publication Number Publication Date
WO2014133102A1 true WO2014133102A1 (fr) 2014-09-04

Family

ID=51428361

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2014/054948 WO2014133102A1 (fr) 2013-02-27 2014-02-27 Polymère biocompatible en tant que matière antithrombogène, carbonate cyclique utile comme précurseur correspondant et procédé pour sa production

Country Status (1)

Country Link
WO (1) WO2014133102A1 (fr)

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2017535633A (ja) * 2014-10-06 2017-11-30 インターナショナル・ビジネス・マシーンズ・コーポレーションＩｎｔｅｒｎａｔｉｏｎａｌ Ｂｕｓｉｎｅｓｓ Ｍａｃｈｉｎｅｓ Ｃｏｒｐｏｒａｔｉｏｎ 医用水溶性ポリカルボナート
WO2018008662A1 (fr) * 2016-07-08 2018-01-11 国立大学法人東京農工大学 Nouveau polycarbonate aliphatique et composition de résine liante contenant ledit polycarbonate
CN116284763A (zh) * 2023-02-23 2023-06-23 华南理工大学 一种含环状/线性结构的聚烯胺类化合物及其制备方法与应用

Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20100305281A1 (en) * 2009-06-02 2010-12-02 International Business Machines Corporation Polymers bearing pendant pentafluorophenyl ester groups, and methods of synthesis and functionalization thereof
WO2011078804A1 (fr) * 2009-12-23 2011-06-30 International Business Machines Corporation Polymères antimicrobiens et procédés de fabrication de ceux-ci
WO2011078805A1 (fr) * 2009-12-23 2011-06-30 International Business Machines Corporation Polymères biodégradables, complexes de ceux-ci pour la thérapie génique et l'administration de médicament, et procédés associés à ceux-ci
JP2012232909A (ja) * 2011-04-28 2012-11-29 Osaka Univ 新規トリメチレンカーボネート誘導体および該ポリマー

Patent Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20100305281A1 (en) * 2009-06-02 2010-12-02 International Business Machines Corporation Polymers bearing pendant pentafluorophenyl ester groups, and methods of synthesis and functionalization thereof
WO2011078804A1 (fr) * 2009-12-23 2011-06-30 International Business Machines Corporation Polymères antimicrobiens et procédés de fabrication de ceux-ci
WO2011078805A1 (fr) * 2009-12-23 2011-06-30 International Business Machines Corporation Polymères biodégradables, complexes de ceux-ci pour la thérapie génique et l'administration de médicament, et procédés associés à ceux-ci
JP2012232909A (ja) * 2011-04-28 2012-11-29 Osaka Univ 新規トリメチレンカーボネート誘導体および該ポリマー

Cited By (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2017535633A (ja) * 2014-10-06 2017-11-30 インターナショナル・ビジネス・マシーンズ・コーポレーションＩｎｔｅｒｎａｔｉｏｎａｌ Ｂｕｓｉｎｅｓｓ Ｍａｃｈｉｎｅｓ Ｃｏｒｐｏｒａｔｉｏｎ 医用水溶性ポリカルボナート
WO2018008662A1 (fr) * 2016-07-08 2018-01-11 国立大学法人東京農工大学 Nouveau polycarbonate aliphatique et composition de résine liante contenant ledit polycarbonate
KR20190028420A (ko) * 2016-07-08 2019-03-18 고꾸리쯔 다이가꾸호우징 도쿄노우코우다이가쿠 신규 지방족 폴리카보네이트 및 해당 폴리카보네이트를 포함하는 바인더 수지 조성물
JPWO2018008662A1 (ja) * 2016-07-08 2019-04-25 国立大学法人東京農工大学 新規脂肪族ポリカーボネート、および、該ポリカーボネートを含むバインダー樹脂組成物
US10787540B2 (en) 2016-07-08 2020-09-29 National University Corporation Tokyo University Of Agriculture And Technology Aliphatic polycarbonate and binder resin composition containing said polycarbonate
KR102331102B1 (ko) 2016-07-08 2021-11-26 고꾸리쯔 다이가꾸호우징 도쿄노우코우다이가쿠 신규 지방족 폴리카보네이트 및 해당 폴리카보네이트를 포함하는 바인더 수지 조성물
CN116284763A (zh) * 2023-02-23 2023-06-23 华南理工大学 一种含环状/线性结构的聚烯胺类化合物及其制备方法与应用
CN116284763B (zh) * 2023-02-23 2024-06-04 华南理工大学 一种含环状/线性结构的聚烯胺类化合物及其制备方法与应用

Similar Documents

Publication Publication Date Title
JP5599712B2 (ja) オリゴフッ素化架橋ポリマーおよびそれの使用
JP5671024B2 (ja) ポリマー、好ましくは（アルキル）アクリロイルポリカーボネートを作る方法、得られるポリマーおよび（アルキル）アクリロイルポリカーボネート、ならびにこれを含むバイオデバイス
JP5346333B2 (ja) ポリアミド及びポリカーボネートジアミンからなるコポリマーを含む医療機器
EP1803754B1 (fr) Copolymères en séquence actifs biologiquement et article revêtu
JP5346334B2 (ja) 変性ポリアミド及びポリエーテルからなるコポリマーを含む医療機器
JP5255627B2 (ja) 変性ポリアミド及びポリカーボネートからなるコポリマーを含む医療機器
US20100076162A1 (en) Biodegradable nitric oxide generating polymers and related biomedical devices
Lopez‐Donaire et al. Surface modifying oligomers used to functionalize polymeric surfaces: Consideration of blood contact applications
JP2017082174A (ja) ポリマー、ポリマー溶液及びポリマー被覆基板
WO2014133102A1 (fr) Polymère biocompatible en tant que matière antithrombogène, carbonate cyclique utile comme précurseur correspondant et procédé pour sa production
JP6226357B2 (ja) 抗血栓性材料としての生体親和性ポリマー
WO2012173628A1 (fr) Copolymères et leurs procédés d'utilisation
WO2018061916A1 (fr) Copolymère et matériau médical l'utilisant
JP6320688B2 (ja) 環状カーボネートの製造方法
EP3219330B1 (fr) Synthèse d'un nano-agrégat de chitosane modifié par un peptide à auto-assemblage et son application au transport de protéines
WO2015170769A1 (fr) Polymère antibactérien, son procédé de production, et utilisation associée
EP3342795B1 (fr) Gel injectable biodégradable
Ghosh et al. Recent Development in Polyurethanes for Biomedical Applications
JP2017203062A (ja) 新規ポリマー
US20240165307A1 (en) Medical composition and use thereof
KR102687882B1 (ko) 카르보네이트-연결된 표면 개질 거대분자
JP2023026365A (ja) 医療用組成物及びその用途
Navarro Tissue Engineering Simplified: Biodegradable Polymers and Biomimetic Scaffolds Made Easy, Tailorable, and Economical for Tissue Engineering
EP2098256A1 (fr) Matériau inhibant la coagulation du sang, matériau de revêtement et éléments à demeure in vivo faits à l'aide du matériau, et procédé de traitement
JP2006271888A (ja) 抗血栓性医用材料及びその製造方法

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 14756260

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 14756260

Country of ref document: EP

Kind code of ref document: A1