WO2014087881A1 - Composition de résine à base de cellulose - Google Patents

Composition de résine à base de cellulose Download PDF

Info

Publication number
WO2014087881A1
WO2014087881A1 PCT/JP2013/081765 JP2013081765W WO2014087881A1 WO 2014087881 A1 WO2014087881 A1 WO 2014087881A1 JP 2013081765 W JP2013081765 W JP 2013081765W WO 2014087881 A1 WO2014087881 A1 WO 2014087881A1
Authority
WO
WIPO (PCT)
Prior art keywords
cellulose
group
acid
polyether
cardanol
Prior art date
Application number
PCT/JP2013/081765
Other languages
English (en)
Japanese (ja)
Inventor
曽山　誠
幸浩 木内
位地　正年
修吉 田中
清彦 當山
Original Assignee
日本電気株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 日本電気株式会社 filed Critical 日本電気株式会社
Priority to JP2014551047A priority Critical patent/JPWO2014087881A1/ja
Publication of WO2014087881A1 publication Critical patent/WO2014087881A1/fr

Abstract

La présente invention concerne une composition de résine à base de cellulose qui présente une résistance améliorée aux impacts, tout en présentant des propriétés améliorées de plasticité thermique, de résistance à la chaleur, de résistance, d'aptitude au moulage et de résistance à l'eau. Ladite composition de résine à base de cellulose contient : une résine à base de cellulose qui est obtenue en faisant réagir, par liaison chimique, une ou plusieurs substances choisies parmi des acides carboxyliques ayant de 1 à 32 atomes de carbone, des alcools, des phénols et des dérivés de ces substances avec un groupe hydroxy d'une cellulose ou d'un dérivé associé; et un polysiloxane modifié avec un polyéther comprenant un groupe polyéther représenté par -(CmH2mO)n- (dans lequel m représente un entier situé dans la plage allant de 2 à 4 et n représente un entier situé dans la plage allant de 1 à 80) ou le groupe polyéther comprenant un substituant.
PCT/JP2013/081765 2012-12-07 2013-11-26 Composition de résine à base de cellulose WO2014087881A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
JP2014551047A JPWO2014087881A1 (ja) 2012-12-07 2013-11-26 セルロース系樹脂組成物

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2012-268140 2012-12-07
JP2012268140 2012-12-07

Publications (1)

Publication Number Publication Date
WO2014087881A1 true WO2014087881A1 (fr) 2014-06-12

Family

ID=50883302

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2013/081765 WO2014087881A1 (fr) 2012-12-07 2013-11-26 Composition de résine à base de cellulose

Country Status (2)

Country Link
JP (1) JPWO2014087881A1 (fr)
WO (1) WO2014087881A1 (fr)

Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS6369846A (ja) * 1986-09-11 1988-03-29 Tsutsunaka Plast Kogyo Kk カレンダ−成形用セルロ−ス系樹脂組成物
JPH04370279A (ja) * 1991-06-20 1992-12-22 Achilles Corp スエード調皮革様シート状物およびその製造方法
JPH055281A (ja) * 1991-06-20 1993-01-14 Achilles Corp 皮革様シート状物およびその製造方法
JP2001139414A (ja) * 1999-11-11 2001-05-22 Kose Corp 皮膚化粧料
JP2006124491A (ja) * 2004-10-28 2006-05-18 Toray Ind Inc ポリエステル樹脂組成物および白色フィルム

Patent Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS6369846A (ja) * 1986-09-11 1988-03-29 Tsutsunaka Plast Kogyo Kk カレンダ−成形用セルロ−ス系樹脂組成物
JPH04370279A (ja) * 1991-06-20 1992-12-22 Achilles Corp スエード調皮革様シート状物およびその製造方法
JPH055281A (ja) * 1991-06-20 1993-01-14 Achilles Corp 皮革様シート状物およびその製造方法
JP2001139414A (ja) * 1999-11-11 2001-05-22 Kose Corp 皮膚化粧料
JP2006124491A (ja) * 2004-10-28 2006-05-18 Toray Ind Inc ポリエステル樹脂組成物および白色フィルム

Also Published As

Publication number Publication date
JPWO2014087881A1 (ja) 2017-01-05

Similar Documents

Publication Publication Date Title
KR101515692B1 (ko) 셀룰로오스 수지 및 그 제조 방법
JP5853698B2 (ja) セルロース系樹脂およびその製造方法
WO2014119657A1 (fr) Composition de résine de type cellulose, matériau de moulage et article moulé
JP5737280B2 (ja) カルダノール変性シランカップリング剤、カルダノール変性フィラー、およびセルロース系樹脂組成物
JP5786861B2 (ja) セルロース系樹脂組成物
JP5846120B2 (ja) セルロース系樹脂
US9458251B2 (en) Cellulose resin and process for producing the same
JP5928448B2 (ja) セルロース系樹脂およびその製造方法
WO2013180278A1 (fr) Procédé de production de dérivé cellulosique et dérivé cellulosique
WO2016067662A1 (fr) Dérivé de cellulose et composition de résine pour moulage
JP6528684B2 (ja) セルロース誘導体の製造方法、セルロース誘導体、成形用樹脂組成物および成形体
JP2012219112A (ja) セルロース系樹脂およびその製造方法
JP2015081326A (ja) カルダノール類縁体を用いたセルロース系樹脂およびその製造方法
JP2014162804A (ja) セルロース系樹脂組成物
WO2014087881A1 (fr) Composition de résine à base de cellulose

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 13859819

Country of ref document: EP

Kind code of ref document: A1

ENP Entry into the national phase

Ref document number: 2014551047

Country of ref document: JP

Kind code of ref document: A

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 13859819

Country of ref document: EP

Kind code of ref document: A1