WO2014057612A1 - グラフェン膜の製造方法およびグラフェン膜ならびにグラフェン膜を用いた透明導電膜 - Google Patents

グラフェン膜の製造方法およびグラフェン膜ならびにグラフェン膜を用いた透明導電膜 Download PDF

Info

Publication number
WO2014057612A1
WO2014057612A1 PCT/JP2013/005432 JP2013005432W WO2014057612A1 WO 2014057612 A1 WO2014057612 A1 WO 2014057612A1 JP 2013005432 W JP2013005432 W JP 2013005432W WO 2014057612 A1 WO2014057612 A1 WO 2014057612A1
Authority
WO
WIPO (PCT)
Prior art keywords
substrate
graphene
film
graphene film
contact
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/JP2013/005432
Other languages
English (en)
French (fr)
Inventor
健志 藤井
まり子 佐藤
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Fuji Electric Co Ltd
Original Assignee
Fuji Electric Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Fuji Electric Co Ltd filed Critical Fuji Electric Co Ltd
Publication of WO2014057612A1 publication Critical patent/WO2014057612A1/ja
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

　グラフェンと表面にテクスチャなどの凹凸のある表面との接触不良を削減または解消することにより、グラフェンと凹凸を持つ基板上に均一にグラフェン膜を転写することを課題とする。　遷移金属基板である第１基板の表面に凹凸を形成する工程と、前記第１基板に炭素を含む原料物質を供給することにより、１層以上の炭素原子のシート状の結晶構造を有するグラフェンを成長させる工程と、該グラフェンの表面に接して、樹脂の仮支持膜である第２基板を形成する工程と、前記第１基板を除去する工程と、前記第２基板と前記グラフェンとの積層体を第３基板の表面に対し前記グラフェンの前記第１基板に接していた側の表面を向けて前記積層体を貼り付ける工程と、前記第２基板を除去する工程と、を含む。

Description

グラフェン膜の製造方法およびグラフェン膜ならびにグラフェン膜を用いた透明導電膜
　本発明は、グラフェン膜の製造方法およびグラフェン膜に関する。さらに詳細には本発明は、表面に凹凸のある基板に転写することの出来るグラフェン膜の製造方法およびグラフェン膜に関する。
　従来、ｓｐ２結合で互いに結合して炭素原子のシート状の結晶構造を有するグラフェンにおいて、炭素原子の単層のシートからなるグラフェン（単層グラフェンという）が発見されている。単層グラフェンは、非特許文献１及び非特許文献２に記載のように、半整数ホール効果などの２次元性に由来する特異な量子伝導が報告され、物性物理の分野で注目されている。
　単層グラフェンでは、キャリア（電子）の移動度が約１５０００ｃｍ２／Ｖ・ｓであり、シリコンに比べ一桁以上高い値を示すことが知られている。この点に注目し単層グラフェンの各種の産業応用が提案されている。その応用先は多岐にわたり、Ｓｉを超えるトランジスタへの応用、スピン注入デバイス、単分子を検出するガスセンサーなどを含んでいる。なかでも、導電性薄膜や透明導電膜へのグラフェンの適用が注目されており活発に開発が行われている。
　グラフェンを、導電性薄膜または透明導電膜として利用する際の重要な特性の一つが、低いシート抵抗である。シート抵抗は、膜厚と導電率とに反比例することから、膜厚を厚くするほどシート抵抗は低い値が得られる。また、導電率は移動度に比例するため、良質な膜のグラフェンを成膜して、炭素原子の配列に不整合等を減らすことにより、移動度を高められれば、様々な応用の可能性が拓ける。
　また、グラフェンの典型的な製造方法の一つが、ＣＶＤ法である。例えば非特許文献３では、ＣＶＤ法によってＣｕフォイル上に膜質の良いグラフェン薄膜を均一に成膜できることが報告されている。具体的には、ＣＶＤ炉の内部にＣｕフォイルを配置して、１０００℃まで昇温しながら水素を導入しておき、そこにメタンなどの炭化水素系のガスを供給することにより、Ｃｕフォイル表面にグラフェンが成膜される。
　こうして形成されたグラフェンを導電性薄膜や透明導電膜の用途として用いるためには、Ｃｕ表面から剥離して目的の基板に形成する必要がある。その手法の典型的なものでは、形成されたグラフェンの上に、樹脂の仮支持膜としてＰＭＭＡ（Polymethyl methacrylate）を形成する。その後、Ｃｕフォイルをエッチングにより取り除く。次いで、グラフェン／ＰＭＭＡ膜を、最終的な基板に対して、グラフェンがその基板に接する向きに貼り付ける。その後にアセトンなどの有機溶媒にてＰＭＭＡを溶解させれば、グラフェンを当該最終的な基板の面の上に形成することができる。実際、この手法（以下、従来の転写法と呼ぶ）により形成したグラフェンにおいては、結晶の欠陥に起因するといわれるラマン分光法のＤピークが観測されず、非常に良質な結晶性を示す。つまり、従来の転写法は平坦な基板に転写する場合には有効な手法といえる。
特開平８－２８８５２９号公報
K. S. Novoselov, A. K. Geim, S. V. Morozov,D. Jiang, Y. Zhang, S. V. Dubonos, I. V. Grigorieva, A. A. Firsov, Science 306(2004)666. K. S. Novoselov, D. Jiang, F. Schedin, T. J.Booth, V. V. Khotkevich, S. V. Morozov and K. Geim, Proc. Natl. Acad. Sci.U.S.A. 102 (2005) 10451. Xuesong Li, et al., "Transferof Large-Area Graphene Films for High-Performance Transparent ConductiveElectrodes", Nano Lett. 9, (2009) 4359-4362.
　そこで、本願の発明者らも、非特許文献３と同様の従来の転写法を用いて、太陽電池上へのグラフェン膜の作製を試みた。その結果、太陽電池上には、グラフェンを転写できなかった。本願の発明者は、転写できなかった原因としては、太陽電池では、基板表面や基板上に接して形成される電極に、光の閉じ込め効率を向上させるために、３０ｎｍ程度以上の凹凸であるテクスチャと呼ばれる構造を用いており、転写対象の太陽電池表面（受光面側半導体層表面）にも３０ｎｍ程度のテクスチャ構造が有るためと考える。従来の転写法ではグラフェンの平坦性が１ｎｍ程度であり、転写の際にテクスチャの凸の部分にはグラフェンは接触できるが、凹の部分にはグラフェンは接触せず、結果としてＰＭＭＡを除去した際に、グラフェンと基板との接触が不十分でグラフェンは剥離してしまったと推測される。
　本発明は、上記課題の解決することを目的とする。すなわち本発明は、グラフェンと、表面にテクスチャなどの凹凸のある表面との接触不良を削減または解消することにより、グラフェンと凹凸を持つ基板上に均一にグラフェン膜を転写することを提供し、太陽電池などの用途へのグラフェン膜の適用の可能性を拓くものである。
　本願の発明者は、上述したように、太陽電池などのテクスチャ構造を持つ、凹凸のある表面上に、グラフェンを転写すると、表面の凹凸が転写の能率を低下させる要因になりかねないことに気づいた。そこで、本願の発明者らは、凹凸のある表面に効率良くグラフェンが密着する方法を探索した。そして、グラフェン自体を凹凸構造とすることで、転写の際にグラフェンが転写対象の表面の凹凸にフィットとし、グラフェンの付着の効率が向上し転写能率が向上することを確認した。
　すなわち、本発明のある態様においては、遷移金属基板である第１基板の表面に凹凸を形成する工程と、前記第１基板に炭素を含む原料物質を供給することにより、１層以上の炭素原子のシート状の結晶構造を有するグラフェンを成長させる工程と、該グラフェンの表面に接して樹脂の仮支持膜である第２基板を形成する工程と、前記第１基板を除去する工程と、前記第２基板と前記グラフェンとの積層体を第３基板の表面に対し前記グラフェンの前記第１基板に接していた側の表面を向けて前記積層体を貼り付ける工程と、前記第２基板を除去する工程と、を含むグラフェン膜の製造方法が提供される。
　第２基板がＰＭＭＡ（ポリメチルメタクリレート）またはＰＤＭＳ（ポリジメチルシロキサン）であることが好ましい。
　また、本発明のある態様においては、凹凸のある遷移金属基板上にグラフェンを成長することで、基板の凹凸を引き継いだ、１層以上の炭素原子がシート状に形成された結晶構造を有する膜である、グラフェン膜が提供される。
　本発明の各態様において、第１基板および第２基板は、それぞれ、遷移金属基板および樹脂の仮支持膜を互いに、または他の基板から区別するために本出願で用いる呼称である。これに対し、第３基板は、第１基板とも第２基板とも別の基板である限り、任意の材質の任意の基板である。つまり、第３基板は、第１および第２基板の材質も含めて任意の材質により作製された基板または基体とする物体である。通常は、第３基板の面の上に形成されたグラフェン膜を、その後に支持する基板とて使用し続ける。その場合、第３基板はグラフェン膜が適用される用途の観点から決定される。
　第３基板の例としては、薄膜太陽電池の受光面側の層が挙げられる。
この層も、基板などに形成された凹凸を引き継いで、３０ｎｍ程度、またはそれ以上の凹凸を、表面に有するものである。この場合、グラフェン膜は、薄膜太陽電池の透明電極層として用いられる。
例えば、特許文献１には、アモルファス系材料から成る薄膜太陽電池において、基板に接する電極である、下部電極層表面の山谷（凹凸）の高低差が５０ｎｍ～１５０ｎｍであることが記載されている。この下部電極層表面の凹凸を、太陽電池の最上層が引き継ぎ、最上層にも３０ｎｍ程度の凹凸が出来る。このとき、凹凸を有したグラフェン膜は、太陽電池の透明導電膜として用いることができる。
　ただ、太陽電池の表面層が有する凹凸には、ランダムネスが有る。このため、単に第１基板に、規則的な凹凸を設けて転写しても、太陽電池の表面層に、グラフェン膜が、上手くフィットしない場合がある。この場合には、予め、太陽電池の受光面側の表面層に存在している凹凸の型を取り、この型を用いて、第１基板の表面に凹凸を設ければ、グラフェン膜の凹凸が、太陽電池の表面層の凹凸にフィットする。
　グラフェンは原子層１層で約２．３％もの高い光吸収を示すため、本発明で透明導電膜としてグラフェン膜を採用すると、１０層を上限とすると好適である。その場合、本発明において提供されるグラフェン膜の膜厚方向の光透過率が７０％以上であると有利である。
　さて、グラフェンとは、ｓｐ２結合で互いに結合して炭素原子が１原子層以上の膜状または層状に形成されている状態の物質を指す。したがって、本出願において、グラフェンという文言の意味としては、単層グラフェンだけではなく、複数の原子層で成る炭素原子のシートも含む。なお、本出願においてグラフェン膜と呼ぶときは、例えば第３基板などの、何らかの基板または基体に支持された状態のグラフェンを意図している。
　凹凸とは、平坦な状態から隆起した構造を呼ぶ。したがって、隆起の仕方にはさまざまな形状があり、限定されるものでは無い。本出願においては、概ね３０ｎｍ以上の高さとなっている部分を指している。
　なお、本発明において、「接して」や「貼り付ける」とは、必ずしも全面的に密着しているものだけを含むものではない。例えば基板の凹凸を引き継いで基板上に載置または支持または配置されているものも、「接して」や「貼り付ける」に含まれる。
　本発明のいずれかの態様においては、転写能率の低下の原因である表面の凹凸に対し、凹凸を有するグラフェン膜を使用することにより、グラフェン膜の付着効率が向上し、転写能率の高いグラフェン膜が提供され、導電性を利用する任意の用途へのグラフェン膜の適用の可能性が拓ける。
本発明のある実施形態におけるグラフェン膜の製造方法の工程の各段階の様子を示す説明図である。
　以下、本発明に係るグラフェン膜の製造方法およびグラフェン膜を、図面を参照して説明する。当該説明に際し特に言及がない限り、全図にわたり共通する部分または要素には共通する参照符号が付されている。また、図中、各実施形態の要素のそれぞれは、必ずしも互いの縮尺比を保って示してはいない。
＜実施の形態１＞
　本実施形態においては、グラフェン膜の製造方法およびグラフェン膜が提供される。図１は、本実施形態のグラフェン膜の製造方法の工程の各段階の説明図である。
　図１（ａ）に示すようにまず、遷移金属基板である第１基板１１の表面をエッチングすることにより図１（ｂ）に示す、表面１１ａのように３０ｎｍ程度、またはそれ以上の凹凸を持つ表面を形成する。次いで、図１（ｃ）に示すように、表面１１ａに炭素を含む原料物質を供給することにより、１層以上の炭素原子のシート状の結晶構造を有するグラフェン１０を成長させる。
　具体的には、グラフェン１０の成長法としては、ＣＶＤ法またはＰＶＤ法（物理的気相堆積）により成膜することができる。このうちＣＶＤ法では、１×１０－７Ｐａ以下の超高真空中や、１０～１００００Ｐａ程度の低圧や大気圧などの、さまざまな条件下に維持した遷移金属基板を６００～１２００℃程度に加熱する。その状態の遷移金属基板に対して、炭素原子を含むメタンなどの炭化水素ガスを吹き付ける。この処理によりメタンガスはクラッキング（解離吸着）される。供給されたガスに由来する炭素原子は、遷移金属基板の表面の触媒効果を受け、長い距離をマイグレーションすることで、グラフェンの核に到達し、グラフェンが成長してゆく。なお、遷移金属基板は、表面を単結晶の表面とし、薄膜により形成されていてもよい。
　一方、ＰＶＤ法によるグラフェンの成長方法としては、ＭＢＥ（分子線エピタキシー法）やＰＬＤ（パルスレーザー堆積）などにより、グラフェンを成長させることが可能である。ＭＢＥでは超高真空中でグラファイトを１２００～２０００℃に加熱することで原子状の炭素を発生させ、分子線となった原子状炭素を、加熱した遷移金属基板表面上に供給する。これにより、遷移金属基板の触媒効果によってグラフェンが成膜される。これに対しＰＬＤでは、超高真空中でグラファイトをＫｒＦのエキシマレーザーにてアブレーションすることで、瞬時に蒸発した炭素が分子線の状態で供給される。この炭素の分子線を加熱された遷移金属基板に供給すると、遷移金属基板の表面にグラフェンが成膜される。
　なお、上述した第１基板のための遷移金属には、Ｆｅ、Ｃｏ、Ｎｉ、Ｃｕ、Ｍｏ、Ｒｕ、Ｒｈ、Ｐｄ、Ｗ、Ｒｅ、Ｉｒ、Ｐｔまたはこれらの合金を採用することが可能である。また、遷移金属基板の形態は、フォイル、薄膜、バルク、およびそれらの単結晶、多結晶などとすることができる。これらのうち最も典型的な遷移金属基板は銅箔である。遷移金属基板は、グラフェンの支持基板となるとともに、上述したとおり、供給された炭素を含有するガスをクラッキング（分解）する触媒となり、炭素原子がシート状の結晶構造のグラフェンの成長を促進する作用を示す。
　次に図１（ｄ）のように、樹脂支持膜である第２基板１２を、グラフェン１０の表面に接するように形成する。具体的には、第１基板の面の上に形成されているグラフェン１０を、その状態を維持しつつ第２基板１２を形成する。この際、第２基板１２は、グラフェン１０を保持することが可能な材質により作製する。例えばグラフェン１０に接した状態で、液状の材質から固化させることが可能で、その後にグラフェン１０を保持しうる材質が、この第２基板１２に適している。最も典型的な第２基板１２は、溶媒に溶けている状態の溶媒可溶性の樹脂や、高分子となる前のプレポリマーなどの前駆体から、溶媒を揮発させたり、前駆体を重合させることによって固化したものである。この第２基板１２となる樹脂支持膜は、例えば、ある程度の支持機能を発揮することができること、後の第１基板１１の除去の際に影響を受けないこと、さらに、必要に応じて最終的にグラフェン１０に影響を与えずに除去可能であること、という条件を満たす材質から選択される。この段階のグラフェン１０は、第１基板１１（遷移金属基板）と第２基板１２（樹脂支持基板）とに挟まれた状態となっている（図１（ｄ））。
　次いで図１（ｅ）のように、第１基板１１である遷移金属基板を除去する。遷移金属基板を除去するためには、例えば酸によるエッチングを採用することが可能である。この除去の処理は、グラフェン１０を変質させない手法から選択される。第１基板が完全に除去されると、グラフェン１０が第２基板１２に付着して表面を露出させている状態になる。
　その後、図１（ｆ）のように、グラフェン１０の第１基板１１に接していた側の表面を、他の基板である第３基板１３に向けて、第３基板１３の表面１３ａに対して貼り付ける。第３基板１３の表面１３ａにはテクスチャと呼ばれる凹凸が形成されている。なお、第３基板１３は、第１基板１１とも第２基板１２とも別の基板である。
　最後に図１（ｇ）のように第２基板１２を除去する。この手法としては、グラフェン１０および第３基板１３に対して影響を及ぼしにくい任意の手法を採用することができる。例えば、第３基板１３がシリコン基板やガラス基板などの無機物であるなら、樹脂支持基板の材質を溶解させる有機溶媒によって第２基板１２を除去することができる。第２基板１２（樹脂支持膜）の材質や性状は、本工程において除去可能なものを採用しておく。
　以上の工程により、グラフェン１０を第３基板１３の面の上に形成してグラフェン膜を製造することができる。次に、より詳細な製造条件について説明する。
　本実施形態においては、第１基板である遷移金属をエッチングするためには、金属を均一かつランダムに削り取る手法が最適である。その方法としては酸などによるウエットエッチングや反応性イオンエッチングなどによるドライエッチングを使用することが望ましい。このときエッチングの高さは転写対象である、第３基板の凹凸よりも大きい必要があり、一般的に太陽電池などのテクスチャと呼ばれる構造では３０nm以上の凹凸があるため、本エッチングによる高さは３０nm以上が望ましい。
　本実施形態において採用する第２基板１４（樹脂支持基板）は、上述した条件を満たすことが可能な任意の材質のものとすることができる。第２基板１２として好適なものは、ＰＭＭＡ（ポリメチルメタクリレート）またはＰＤＭＳ（ポリジメチルシロキサン）である。ＰＭＭＡやＰＤＭＳは、溶媒に溶解させた状態の溶液により、容易に塗布することが可能であり、また、その溶媒を揮発させて樹脂の仮支持膜を形成することも容易である。さらに、第１基板１１の除去のための処理（エッチング処理）にも耐えられる上、第２基板自体を除去することも容易に実施することができる。そしてさらに、グラフェン１０を転写するために要する程度の膜を形成することができる。これらの条件を満たすＰＭＭＡやＰＤＭＳは、本実施形態において第２基板１２（樹脂支持基板）として採用する材質の好適なものである。
　本実施形態において提供されるグラフェン膜では、第１基板の凹凸の形状を引き継ぎ、同じく３０ｎｍ程度の凹凸を有しており、そのため、凹凸のある第３基板上に転写した際には、グラフェン膜の凹凸と第３基板の凹凸が互い違いに入り込み形状にフィットするとともに、グラフェン膜が第３基板に付着することが出来、効率良くグラフェン膜を転写することが出来る。
　ここで、凹凸の高さ指標は例えば走査電子顕微鏡、透過電子顕微鏡、原子間力顕微鏡などによって測定される高低差から算出できる。この方法を用いた一般的な第３基板のテクスチャ構造の凹凸は、例えば太陽電池の受光面側の半導体層では３０ｎｍ程度である。したがって、グラフェン膜の好ましい構成では、好ましくは、凹凸が３０ｎｍ以上とされる。
　本実施形態において提供されるグラフェン膜は、グラフェンの原子層数が１層以上１０層以下であると好適である。その理由は、グラフェン膜の適用用途に関係している。グラフェンは、特に単層グラフェンにおいて高い移動度を示すことが知られている。他方、グラフェン膜が、光の透過が要求される用途において透明導電膜などとして利用される場合、透過率の点から層数には上限が存在する。具体的には、グラフェンは原子層１層で約２．３％もの高い光吸収を示すため、本実施形態で例えば、透明導電膜としてグラフェン膜を採用すると、１０層を上限とすることが好適である。その場合、本実施形態において提供されるグラフェン膜の膜厚方向の光透過率が７０％以上とすると有利である。
［実施例］
　次に、本実施形態のグラフェン膜の実施例について説明する。実施例１は上述した実施形態に従って作製したグラフェン膜のサンプルである。以下の実施例に示す材料、使用量、割合、処理内容、処理手順、要素または部材の向きや具体的配置等は本発明の趣旨を逸脱しない限り適宜変更することかできる。したがって、本発明の範囲は以下の具体例に限定されるものではない。また、既に説明した図面を引き続き参照する。
　まず、第１基板１１としては１０ｍｍ角のＣＭＰ研磨（化学的機械研磨）したＣｕフォイル（膜厚１００μｍ）を採用した。この基板の算術平均粗さＲａは、１ｎｍ程度である。この第１基板１１を、塩酸５ｍｌ、過酸化水素５ｍｌ、水２５ｍｌの混合液に１０秒浸漬した後、５分間の流水洗浄し、乾燥させることで、第１基板１１の表面に３０ｎｍの凹凸１１ａを形成した。この第１基板１１をＣＶＤの反応炉に配置し、１×１０－３Ｐａまで真空引きを行った。そして、水素を５Ｐａ（３．８×１０－２Ｔｏｒｒ）導入した状態で、第１基板１１を５０℃／ｍｉｎの昇温レートで１０００℃まで加熱した。その後、第１基板１１を１０００℃に保持した状態で水素の供給を停止し、原料ガスとしてメタンを約４．０×１０２Ｐａ（約３Ｔｏｒｒ）導入した。第１基板１１の基板温度とガス圧を保持した状態で１０ｍｉｎ成膜を行った。成膜後は１００℃／ｓｅｃの冷却レートにて急冷し、第１基板１１にグラフェン１０を成長させた。
　次に、グラフェン１０の表面に、ジククロベンゼンで１０ｗｔ％に溶解したＰＭＭＡ溶液を２０μｌ滴下し、回転数４０００ｒｐｍ、６０秒の条件で、スピンコートした。その後４０℃、３０分間の条件で乾燥させ、ＰＭＭＡ膜による樹脂支持基板として第２基板１２を形成した。
　次いで、塩酸１０ｍｌ、過酸化水素１０ｍｌ、純水５０ｍｌの混合液に浸漬し、第１基板１１としたＣｕフォイルが完全になくなるまでエッチングした。その後、５分間の流水洗浄し、乾燥させることで３０ｎｍの凹凸が付いたグラフェン１０と第２基板１２の積層体を形成した。
　その後、第３基板１３であるテクスチャ付きＳｎＯ/ｇｌａｓｓ（旭硝子製Ａｓａｈｉ－Ｕ）の表面に押し付け、１８０℃、３０分間の条件で加熱した。この加熱により、ＰＭＭＡが軟化し、グラフェン１０を、ＳｎＯ/ｇｌａｓｓ基板である第３基板１３のＳｎＯ表面に密着させた。
　最後に、アセトンにて５分間浸漬することにより、第２基板１２のＰＭＭＡをグラフェン１０の表面から除去した。さらに超純水にて５分間洗浄して、図４のようにグラフェン１０を第３基板１３に配置した、グラフェン膜のサンプルを得た。
　本実施形態に従って作製したグラフェン膜である実施例１サンプルの走査電子顕微鏡像を観察した。グラフェンが均一に転写されていることが判った。ただ顕微鏡写真では、グラフェンと下地との濃淡差が小さく、白黒２値で図示するのは困難なので、図示は省略する。以上により本発明の効果が実証された。
　以上、本発明の実施形態を具体的に説明した。上述の実施形態および実施例は、発明を説明するために記載されたものであり、本出願の発明の範囲は、特許請求の範囲の記載に基づいて定められるべきものである。また、各実施形態の他の組合せを含む本発明の範囲内に存在する変形例もまた、特許請求の範囲に含まれるものである。
　　１０　グラフェン
　　１１　第１基板
　　１１ａ　表面
　　１２　第２基板
　　１３　第３基板
　　１３ａ　表面
　

Claims (8)

  1. 遷移金属基板である第１基板の表面に凹凸を形成する工程と、前記第１基板に炭素を含む原料物質を供給することにより、１層以上の炭素原子のシート状の結晶構造を有するグラフェンを成長させる工程と、該グラフェンの表面に接して、樹脂の仮支持膜である第２基板を形成する工程と、前記第１基板を除去する工程と、前記第２基板と前記グラフェンとの積層体を第３基板の表面に対し前記グラフェンの前記第１基板に接していた側の表面を向けて前記積層体を貼り付ける工程と、前記第２基板を除去する工程と、を含むグラフェン膜の製造方法。
  2. 第１基板の表面に凹凸を形成する工程が、ウエットエッチングまたはドライエッチングによって形成される請求項１に記載のグラフェン膜の製造方法。
  3. 第１基板の表面の凹凸が３０ｎｍ以上である請求項１または請求項２のいずれか１項に記載のグラフェン膜の製造方法。
  4. 前記第２基板がＰＭＭＡまたはＰＤＭＳである請求項１に記載のグラフェン膜の製造方法。
  5. 　前記第３基板が、薄膜太陽電池の受光面側に位置する層である請求項１に記載のグラフェン膜の製造方法。
  6. 遷移金属基板が表面に３０ｎｍ以上の凹凸を有し、その形状を引き継ぐことにより、高さ３０ｎｍ以上の凹凸を有して当該基板の表面に接して配置されているグラフェン膜。
  7. グラフェンの層数が１層以上１０層以下であることを特徴とする請求項６に記載のグラフェン膜。
  8. 請求項６または請求項７に記載のグラフェンを少なくとも１層有し、膜厚方向の光透過率が７０％以上であるグラフェン膜を用いた透明導電膜。








    　
PCT/JP2013/005432 2012-10-09 2013-09-13 グラフェン膜の製造方法およびグラフェン膜ならびにグラフェン膜を用いた透明導電膜 Ceased WO2014057612A1 (ja)