Classifications

• • A—HUMAN NECESSITIES
  • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
  • A61L—METHODS OR APPARATUS FOR STERILISING MATERIALS OR OBJECTS IN GENERAL; DISINFECTION, STERILISATION OR DEODORISATION OF AIR; CHEMICAL ASPECTS OF BANDAGES, DRESSINGS, ABSORBENT PADS OR SURGICAL ARTICLES; MATERIALS FOR BANDAGES, DRESSINGS, ABSORBENT PADS OR SURGICAL ARTICLES
  • A61L15/00—Chemical aspects of, or use of materials for, bandages, dressings or absorbent pads
  • A61L15/16—Bandages, dressings or absorbent pads for physiological fluids such as urine or blood, e.g. sanitary towels, tampons
  • A61L15/42—Use of materials characterised by their function or physical properties
  • A61L15/44—Medicaments
• • A—HUMAN NECESSITIES
  • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
  • A61F—FILTERS IMPLANTABLE INTO BLOOD VESSELS; PROSTHESES; DEVICES PROVIDING PATENCY TO, OR PREVENTING COLLAPSING OF, TUBULAR STRUCTURES OF THE BODY, e.g. STENTS; ORTHOPAEDIC, NURSING OR CONTRACEPTIVE DEVICES; FOMENTATION; TREATMENT OR PROTECTION OF EYES OR EARS; BANDAGES, DRESSINGS OR ABSORBENT PADS; FIRST-AID KITS
  • A61F13/00—Bandages or dressings; Absorbent pads
  • A61F13/02—Adhesive bandages or dressings
  • A61F13/0203—Adhesive bandages or dressings with fluid retention members
  • A61F13/0213—Adhesive bandages or dressings with fluid retention members the fluid retention member being a layer of hydrocolloid, gel forming material
• • A—HUMAN NECESSITIES
  • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
  • A61F—FILTERS IMPLANTABLE INTO BLOOD VESSELS; PROSTHESES; DEVICES PROVIDING PATENCY TO, OR PREVENTING COLLAPSING OF, TUBULAR STRUCTURES OF THE BODY, e.g. STENTS; ORTHOPAEDIC, NURSING OR CONTRACEPTIVE DEVICES; FOMENTATION; TREATMENT OR PROTECTION OF EYES OR EARS; BANDAGES, DRESSINGS OR ABSORBENT PADS; FIRST-AID KITS
  • A61F13/00—Bandages or dressings; Absorbent pads
• • A—HUMAN NECESSITIES
  • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
  • A61F—FILTERS IMPLANTABLE INTO BLOOD VESSELS; PROSTHESES; DEVICES PROVIDING PATENCY TO, OR PREVENTING COLLAPSING OF, TUBULAR STRUCTURES OF THE BODY, e.g. STENTS; ORTHOPAEDIC, NURSING OR CONTRACEPTIVE DEVICES; FOMENTATION; TREATMENT OR PROTECTION OF EYES OR EARS; BANDAGES, DRESSINGS OR ABSORBENT PADS; FIRST-AID KITS
  • A61F13/00—Bandages or dressings; Absorbent pads
  • A61F13/00051—Accessories for dressings
  • A61F13/00063—Accessories for dressings comprising medicaments or additives, e.g. odor control, PH control, debriding, antimicrobic
• • A—HUMAN NECESSITIES
  • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
  • A61F—FILTERS IMPLANTABLE INTO BLOOD VESSELS; PROSTHESES; DEVICES PROVIDING PATENCY TO, OR PREVENTING COLLAPSING OF, TUBULAR STRUCTURES OF THE BODY, e.g. STENTS; ORTHOPAEDIC, NURSING OR CONTRACEPTIVE DEVICES; FOMENTATION; TREATMENT OR PROTECTION OF EYES OR EARS; BANDAGES, DRESSINGS OR ABSORBENT PADS; FIRST-AID KITS
  • A61F13/00—Bandages or dressings; Absorbent pads
  • A61F13/01—Non-adhesive bandages or dressings
  • A61F13/01034—Non-adhesive bandages or dressings characterised by a property
  • A61F13/01042—Absorbency
• • A—HUMAN NECESSITIES
  • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
  • A61F—FILTERS IMPLANTABLE INTO BLOOD VESSELS; PROSTHESES; DEVICES PROVIDING PATENCY TO, OR PREVENTING COLLAPSING OF, TUBULAR STRUCTURES OF THE BODY, e.g. STENTS; ORTHOPAEDIC, NURSING OR CONTRACEPTIVE DEVICES; FOMENTATION; TREATMENT OR PROTECTION OF EYES OR EARS; BANDAGES, DRESSINGS OR ABSORBENT PADS; FIRST-AID KITS
  • A61F13/00—Bandages or dressings; Absorbent pads
  • A61F13/02—Adhesive bandages or dressings
  • A61F13/0203—Adhesive bandages or dressings with fluid retention members
  • A61F13/0206—Adhesive bandages or dressings with fluid retention members with absorbent fibrous layers, e.g. woven or non-woven absorbent pads or island dressings
• • A—HUMAN NECESSITIES
  • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
  • A61F—FILTERS IMPLANTABLE INTO BLOOD VESSELS; PROSTHESES; DEVICES PROVIDING PATENCY TO, OR PREVENTING COLLAPSING OF, TUBULAR STRUCTURES OF THE BODY, e.g. STENTS; ORTHOPAEDIC, NURSING OR CONTRACEPTIVE DEVICES; FOMENTATION; TREATMENT OR PROTECTION OF EYES OR EARS; BANDAGES, DRESSINGS OR ABSORBENT PADS; FIRST-AID KITS
  • A61F13/00—Bandages or dressings; Absorbent pads
  • A61F13/05—Bandages or dressings; Absorbent pads specially adapted for use with sub-pressure or over-pressure therapy, wound drainage or wound irrigation, e.g. for use with negative-pressure wound therapy [NPWT]
• • A—HUMAN NECESSITIES
  • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
  • A61F—FILTERS IMPLANTABLE INTO BLOOD VESSELS; PROSTHESES; DEVICES PROVIDING PATENCY TO, OR PREVENTING COLLAPSING OF, TUBULAR STRUCTURES OF THE BODY, e.g. STENTS; ORTHOPAEDIC, NURSING OR CONTRACEPTIVE DEVICES; FOMENTATION; TREATMENT OR PROTECTION OF EYES OR EARS; BANDAGES, DRESSINGS OR ABSORBENT PADS; FIRST-AID KITS
  • A61F13/00—Bandages or dressings; Absorbent pads
  • A61F13/15—Absorbent pads, e.g. sanitary towels, swabs or tampons for external or internal application to the body; Supporting or fastening means therefor; Tampon applicators
• • A—HUMAN NECESSITIES
  • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
  • A61L—METHODS OR APPARATUS FOR STERILISING MATERIALS OR OBJECTS IN GENERAL; DISINFECTION, STERILISATION OR DEODORISATION OF AIR; CHEMICAL ASPECTS OF BANDAGES, DRESSINGS, ABSORBENT PADS OR SURGICAL ARTICLES; MATERIALS FOR BANDAGES, DRESSINGS, ABSORBENT PADS OR SURGICAL ARTICLES
  • A61L15/00—Chemical aspects of, or use of materials for, bandages, dressings or absorbent pads
  • A61L15/16—Bandages, dressings or absorbent pads for physiological fluids such as urine or blood, e.g. sanitary towels, tampons
  • A61L15/18—Bandages, dressings or absorbent pads for physiological fluids such as urine or blood, e.g. sanitary towels, tampons containing inorganic materials
• • A—HUMAN NECESSITIES
  • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
  • A61L—METHODS OR APPARATUS FOR STERILISING MATERIALS OR OBJECTS IN GENERAL; DISINFECTION, STERILISATION OR DEODORISATION OF AIR; CHEMICAL ASPECTS OF BANDAGES, DRESSINGS, ABSORBENT PADS OR SURGICAL ARTICLES; MATERIALS FOR BANDAGES, DRESSINGS, ABSORBENT PADS OR SURGICAL ARTICLES
  • A61L15/00—Chemical aspects of, or use of materials for, bandages, dressings or absorbent pads
  • A61L15/16—Bandages, dressings or absorbent pads for physiological fluids such as urine or blood, e.g. sanitary towels, tampons
  • A61L15/22—Bandages, dressings or absorbent pads for physiological fluids such as urine or blood, e.g. sanitary towels, tampons containing macromolecular materials
• • A—HUMAN NECESSITIES
  • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
  • A61L—METHODS OR APPARATUS FOR STERILISING MATERIALS OR OBJECTS IN GENERAL; DISINFECTION, STERILISATION OR DEODORISATION OF AIR; CHEMICAL ASPECTS OF BANDAGES, DRESSINGS, ABSORBENT PADS OR SURGICAL ARTICLES; MATERIALS FOR BANDAGES, DRESSINGS, ABSORBENT PADS OR SURGICAL ARTICLES
  • A61L15/00—Chemical aspects of, or use of materials for, bandages, dressings or absorbent pads
  • A61L15/16—Bandages, dressings or absorbent pads for physiological fluids such as urine or blood, e.g. sanitary towels, tampons
  • A61L15/22—Bandages, dressings or absorbent pads for physiological fluids such as urine or blood, e.g. sanitary towels, tampons containing macromolecular materials
  • A61L15/28—Polysaccharides or their derivatives
• • A—HUMAN NECESSITIES
  • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
  • A61L—METHODS OR APPARATUS FOR STERILISING MATERIALS OR OBJECTS IN GENERAL; DISINFECTION, STERILISATION OR DEODORISATION OF AIR; CHEMICAL ASPECTS OF BANDAGES, DRESSINGS, ABSORBENT PADS OR SURGICAL ARTICLES; MATERIALS FOR BANDAGES, DRESSINGS, ABSORBENT PADS OR SURGICAL ARTICLES
  • A61L15/00—Chemical aspects of, or use of materials for, bandages, dressings or absorbent pads
  • A61L15/16—Bandages, dressings or absorbent pads for physiological fluids such as urine or blood, e.g. sanitary towels, tampons
  • A61L15/42—Use of materials characterised by their function or physical properties
• • A—HUMAN NECESSITIES
  • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
  • A61L—METHODS OR APPARATUS FOR STERILISING MATERIALS OR OBJECTS IN GENERAL; DISINFECTION, STERILISATION OR DEODORISATION OF AIR; CHEMICAL ASPECTS OF BANDAGES, DRESSINGS, ABSORBENT PADS OR SURGICAL ARTICLES; MATERIALS FOR BANDAGES, DRESSINGS, ABSORBENT PADS OR SURGICAL ARTICLES
  • A61L15/00—Chemical aspects of, or use of materials for, bandages, dressings or absorbent pads
  • A61L15/16—Bandages, dressings or absorbent pads for physiological fluids such as urine or blood, e.g. sanitary towels, tampons
  • A61L15/42—Use of materials characterised by their function or physical properties
  • A61L15/46—Deodorants or malodour counteractants, e.g. to inhibit the formation of ammonia or bacteria
• • A—HUMAN NECESSITIES
  • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
  • A61L—METHODS OR APPARATUS FOR STERILISING MATERIALS OR OBJECTS IN GENERAL; DISINFECTION, STERILISATION OR DEODORISATION OF AIR; CHEMICAL ASPECTS OF BANDAGES, DRESSINGS, ABSORBENT PADS OR SURGICAL ARTICLES; MATERIALS FOR BANDAGES, DRESSINGS, ABSORBENT PADS OR SURGICAL ARTICLES
  • A61L15/00—Chemical aspects of, or use of materials for, bandages, dressings or absorbent pads
  • A61L15/16—Bandages, dressings or absorbent pads for physiological fluids such as urine or blood, e.g. sanitary towels, tampons
  • A61L15/42—Use of materials characterised by their function or physical properties
  • A61L15/60—Liquid-swellable gel-forming materials, e.g. super-absorbents
• • A—HUMAN NECESSITIES
  • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
  • A61L—METHODS OR APPARATUS FOR STERILISING MATERIALS OR OBJECTS IN GENERAL; DISINFECTION, STERILISATION OR DEODORISATION OF AIR; CHEMICAL ASPECTS OF BANDAGES, DRESSINGS, ABSORBENT PADS OR SURGICAL ARTICLES; MATERIALS FOR BANDAGES, DRESSINGS, ABSORBENT PADS OR SURGICAL ARTICLES
  • A61L2300/00—Biologically active materials used in bandages, wound dressings, absorbent pads or medical devices
  • A61L2300/10—Biologically active materials used in bandages, wound dressings, absorbent pads or medical devices containing or releasing inorganic materials
  • A61L2300/102—Metals or metal compounds, e.g. salts such as bicarbonates, carbonates, oxides, zeolites, silicates
  • A61L2300/104—Silver, e.g. silver sulfadiazine

Definitions

• the present invention relates to wound dressings having antibacterial, antiviral and/or antifungal activity, to a method of producing such dressings and the use of such dressings in the treatment of wounds.
• the invention relates to the dressings for use in the treatment of infected or dehydrated wounds or wounds with scant exudate.
• Silver sulfadiazine is used extensively in the treatment of wounds, and particularly burns, and is incorporated in a cream base and sold under the trademark Flamazine or Silvadene. As the silver is present in such products as a complex, its solubility in wound fluid is low and hence the quantity of active silver present is also low. It is also known to deliver silver ions from a wound dressing such as those comprising a gelling fibre as found in AQUACEL®Ag. These dressings comprise gel forming fibres which have been ion exchanged with for instance silver nitrate to incorporate silver ions into the fibres. When in contact with an exuding wound, the dressing takes up moisture and releases the silver to the exudate and the wound itself.
• the state of hydration of the dressing would affect the duration for which silver is available and the quantity of silver that is available. It could be expected that on application of the dressing to the wound, the release of silver ions from the dressing would be initially high but tail off over time as the dressing dehydrates. This could happen for instance if the amount of exudate produced by the wound is insufficient to maintain hydration in the dressing, or if the rate of evaporation of moisture from the dressing is high or at least exceeds the rate of absorption from the wound.
• a dry dressing therefore not only limits the supply of silver ions to the wound from a silver containing dressing, it also deprives the wound of the benefits of moist wound healing.
• a dry dressing may adhere to the wound causing tissue damage on removal.
• wound dressings can be prepared which give a controlled, sustained release of silver ions within the dressing and into the adjacent wound fluid to give antimicrobial activity and moist wound healing over the wear time.
• the required hydration property is provided by a dressing comprising an open structure of woven or nonwoven gel forming fibres.
• open structure is meant a regular or irregular, two or three dimensional construct with a large volume for a given mass in which the free internal fabric volume exceeds the solid fibre volume.
• the invention provides for a wound dressing comprising a mat of gel forming fibres comprising silver, the mat having an open structure reinforced with textile fibres or fibres or threads of limited absorbency for use in the treatment of infected wounds.
• Such dressings may have the advantage that hydration is maintained over the wear time of the dressing so that a prolonged delivery of silver ions is experienced by the wound. This is thought to be due to the combination of the open structure of the fibrous mat and the non-gel forming fibres providing the necessary integrity to allow the dressing to be removed from the wound in one piece at the end of its wear time.
• the open structure of the fibrous mat is provided by a nonwoven fibrous mat that has been entangled by fluid jet entanglement such as hydro entanglement or needle punching.
• the open structure may be defined by the extent of entanglement in the dressing.
• the extent of entanglement maybe expressed as the number of entanglements per square centimetre or more usually by a punch density.
• the nonwoven fibrous mat is needle punched or entangled to a punch density of less than 60 per cm 2 , and more preferably from 50 to 10 per cm 2 . Most preferably the punch density is from 40 to 10 per cm 2
• the jet pressure, diameter and spacing also give a density of entanglement equivalent to a needle punch density in that they give a number of entanglements per square centimetre.
• the fibrous mat of gel forming fibres preferably has a basis weight of from 30 to 1000 grams per square meter. More preferably the basis weight is from 100 to 200 grams per square meter and most preferably from 150 to 200 grams per square meter.
• the dressing has a rate of moisture loss at least 25% lower than a dressing made from a mat with a needle punch density of 60 per cm 2 or higher. More preferably the rate of moisture loss is from 30% to 60% lower than that from a dressing with a needle punch density of 60 per cm 2 or higher.
• the dressing maintains the hydration of the wound by having a rate of moisture loss (as measured by the percentage weight loss from the dressing) of less than 75% over the first 48 hours of wear. More preferably the rate of moisture loss is from 70% to 50% over the first 48 hours of wear.
• the nonwoven fibrous mat is reinforced with textile fibres blended with the gel-forming fibres during the formation of the mat.
• the textile fibres are present as a thread or yarn stitch-bonded on the fibrous mat for instance as described
• a desired final concentration of silver in the dry wound dressing is between about 0.1% and 20% by weight, for example. Preferably between 0.1% to 10% by weight and more preferably between 0.5% and 5% by weight of the dressing. Such concentrations can be achieved by the preparation method described in
• a desired concentration of ionic silver released by the dressing into water is preferably less than 1.5 ppm and, more preferably, between 1.5 ppm and 0.5 ppm. Most preferably the concentration of ionic silver released by the dressing into water is about 1 ppm.
• gel forming fibres By gel forming fibres is meant hygroscopic fibres which upon the uptake of wound exudate become moist slippery or gelatinous and thus reduce the tendency for the surrounding fibres to adhere to the wound.
• the gel forming fibres can be of the type which retain their structural integrity on absorption of exudate or can be of the type which lose their fibrous form and become a structureless gel.
• the gel forming fibres are preferably spun sodium carboxymethylcellulose fibres, chemically modified cellulosic fibres, cellulose ethyl sulphonate fibres, pectin fibres, alginate fibres, chitosan fibres, hyaluronic acid fibres, or other polysaccharide fibres or fibres derived from gums.
• the cellulosic fibres preferably have a degree of substitution of at least 0.05 carboxymethyl groups per glucose unit or equivalent ethyl sulphonate.
• the gel forming fibres preferably have an absorbency of at least 5 grams 0.9% saline solution per gram of fibre (as measured by the free swell absorbency method BS EN 13726-1:2002 Test methods for primary wound dressings - Part 1 : Aspects of absorbency, Method 3.2 free swell absorptive capacity ).
• the gel forming fibres have an absorbency of at least 10 g/g as measured in the free swell absorbency method, more preferably between 15 g/g and 30 g/g.
• the textile fibres have an absorbency of less than log/g as measured by the free swell method and more preferably less than 5 g/g.
• the dressing may for instance comprise non gel forming fibres and in particular textile fibres such as Lyocell
• the wound dressing may comprise a fibrous mat in the form of a strip or a roll with an open structure and comprising gel forming fibres, the strip having longitudinal lines of stitches formed from a thread and optionally transverse lines of stitches formed from a thread.
• the longitudinal stitching is longitudinal in that it is generally parallel to the long dimension of the strip.
• the transverse stitching is transverse in that it joins the longitudinal lines of stitches together and in some embodiments is generally perpendicular to the long dimension of the strip.
• the thread maybe a single filament or multiple filament yarn or a staple fibre yarn.
• the thread can be cellulosic, elastane, nylon, polyester or polyurethane.
• the thread can be impregnated with an active agent for example with an antimicrobial agent or confer other properties such as radio-opaque qualities.
• the dressing maybe stitched with lines of longitudinal stitching from imm to lomm apart and preferably from 2 mm to 5 mm apart.
• the lines of longitudinal stitching may be a lock stitch and may typically be crochet or chain stitch but other stitch patterns may also be used.
• the dressing may also comprise rows of transverse stitches; the rows of transverse stitching may be from 1 to lomm apart and preferably from 2 to 5 mm apart.
• the transverse lines of stitches may be a pattern stitch and may be crocheted or may be a basting stitch between two layers of superposed gel forming fibres.
• the lines of stitching are made in a thread such as lyocell.
• the transverse stitches serve to link adjacent longitudinal lines of stitches together to add strength to the dressing in a transverse direction.
• Modification of cellulose fibres can be achieved, for example, by sequential or simultaneous treatment of the cellulosic material with a strong alkali, such as aqueous sodium hydroxide, and monochloroacetic acid or a salt thereof.
• a strong alkali such as aqueous sodium hydroxide, and monochloroacetic acid or a salt thereof.
• the appropriate reaction conditions will depend upon the composition of the fabric and the degree of carboxymethylation or ethyl sulphonation required and will be readily apparent to the person skilled in the art. They may be identical or similar to those described in WO 93/12275, WO 94/16746 or WO 00/01425 to which the reader is directed for further detail.
• the chemical modification is carried out in the presence of industrial methylated spirits (IMS), and IMS is preferably also used in a subsequent washing step, suitably along with water, as a cleaner and steriliser.
• IMS industrial methylated spirits
• the degree of substitution is desirably such that upon absorption of exudate the fibres at the skin-contacting surface of the dressing form a gel.
• the open structure of the fibrous mat may be provided by a nonwoven mat of gel- forming fibres made by a needle felting/ carding technique to form a web.
• the mat may have an antimicrobial material incorporated into it and in particular silver by the method described in WO 02/43743.
• the roll may be stitched in the longitudinal direction with lines of stitching in lyocell yarn.
• the longitudinal lines of stitches may be supplemented by transverse lines of stitching in the form of continuous, angular zigzags which extend between adjacent longitudinal lines of stitches. In this way stitch free gaps are left between columns of longitudinal stitching.
• the roll may be slit in the longitudinal direction in the stitch free gaps to form dressings of various sizes. For instance strips of 1 cm x 45 cm, squares of 5 cm x 5 cm or rectangles of 20 cm x 30 cm.
• Figure 1 is a table showing results from Example 1 below.
• Figure 1 shows how the different degrees of needle punch density affected the hydration performance of the mats.
• prototype mats that managed to retain the fluid for longer are:
• Table 2 shows the needle punch density against the % weight loss on drying for the samples in Table 1.
• the mats to be used in dressings according to the invention demonstrated that they can maintain a moist wound environment for a sustained period of time. It can be concluded, that a low needle punch density, provides a "loftier" structure which allows more space between the fibres to expand and gel, thus, increasing the absorption capacity. This structure also contributes to retaining the fluid for a longer time, therefore, drying out at a slower rate.
• a wound dressing according to the invention was made by preparing two mats of gel- forming fibres (carboxymethylcellulose) by carding, cross-lapping and needle punching to a needle punch density of 22 to make a mat of 70 gsm.
• the mats were impregnated with silver ions by the method described in WO/0243743A to give a total silver content of around 1.18% based on the anhydrous dressing.
• the mats were placed one on top of the other and stitch-bonded by the method described in PCT/GB2009/001138 so that the weft stitches were in between the mats.
• the release of silver from such a wound dressing was measured by silver assay using atomic absorption spectrophotometer (AAS) equipped with a silver hollow cathode lamp.
• AAS atomic absorption spectrophotometer
• a dialysis membrane was pre-soaked in water for a minimum of 16 hours. Samples of the dressing are cut into 5 cm x 5 cm squares and weighed. Each sample is placed into a pouch created from the prehydrated dialysis membrane and placed into 200 ml of isotonic saline at 37 °C contained within a suitable screw topped glass vessel and stirred by magnetic stirrer.
• a 10.0 ml aliquot from each vessel was taken at the following time-points: 3 h, 6 h, 24 h, 48 h, 72 h and 96 h and replaced with 10.0 ml of fresh saline in order to maintain the dissolution volume of 200 ml.
• the liquid samples were then assayed by AAS comparing to standard silver solutions of known concentration.
• This example shows the relationship between the hydration state of the optimized open structure fibrous mat and antimicrobial effectiveness.
• An optimized open structure fibrous mat according to the invention consists of two gel forming 77 gsm mats stitch-bonded together following the method described in PCT/GB2009/001138. Each mat being comprised of carded, cross-lapped and needled punched sodium carboxymethylcellulose fibres (at a needle punch density of 22 per cm 2 ) which have been previously impregnated with silver ions as described in WO02/ 43743A.
• TSA Tryptone Soy Agar
• This example shows the relationship between the rate of dehydration of optimized open structure fibrous mats and the ease of their removal from a fragile surface.
• Fibrous mat 5cm x 5cm samples of conventional loogsm fibre mats with a needle punch density of 60 per cm 2 and optimized open structure mats according to the invention as described in example 3 were fully hydrated by immersion in isotonic saline. Drained samples were placed on agar plates (tryptone 15 g/1, soy peptone 5 g/1, sodium chloride 5 g/1 & Agar No.2 12 g/1). Mats were then left to dehydrate in a forced- air cabinet for 24 hours at ambient room temperature ( ⁇ 22°C). At this point, sample mats had become adhered to the agar surface and could not be removed without disrupting the agar.
• the conventional fibre mats had a drier appearance after 24 hrs on the agar surface and rehydration was visibly slower when compared to the optimized open structured mats.
• dressings are likely to be changed at fixed intervals rather than when absorption capacity is reached or the dressing begins to adhere due to a reduction in the rate of exudation. There may also be limited time available to make dressing changes. Waiting for rehydration may not therefore be an option. Given these circumstances, the invention offers a distinct advantage in that tissue damage caused by dressing change is less likely to occur with the optimized open structure mat according to the invention.

Landscapes

• Health & Medical Sciences (AREA)
• Public Health (AREA)
• Veterinary Medicine (AREA)
• Engineering & Computer Science (AREA)
• Life Sciences & Earth Sciences (AREA)
• Animal Behavior & Ethology (AREA)
• General Health & Medical Sciences (AREA)
• Chemical & Material Sciences (AREA)
• Epidemiology (AREA)
• Materials Engineering (AREA)
• Hematology (AREA)
• Biomedical Technology (AREA)
• Heart & Thoracic Surgery (AREA)
• Vascular Medicine (AREA)
• Dispersion Chemistry (AREA)
• Inorganic Chemistry (AREA)
• Medicinal Chemistry (AREA)
• Materials For Medical Uses (AREA)
• Nonwoven Fabrics (AREA)

Priority Applications (18)

Applications Claiming Priority (2)

Publications (1)

Family

ID=46582175

Family Applications (1)

Country Status (21)

Cited By (2)

Families Citing this family (28)

Citations (6)

Family Cites Families (18)

• 2012
  • 2012-05-31 GB GB201209745A patent/GB201209745D0/en not_active Ceased
• 2013
  • 2013-05-30 US US14/403,954 patent/US10350326B2/en active Active
  • 2013-05-30 KR KR1020147036277A patent/KR102152480B1/ko not_active Expired - Fee Related
  • 2013-05-30 NZ NZ702489A patent/NZ702489A/en not_active IP Right Cessation
  • 2013-05-30 SG SG11201407876TA patent/SG11201407876TA/en unknown
  • 2013-05-30 EP EP13726839.7A patent/EP2854881B1/en active Active
  • 2013-05-30 CA CA 2875133 patent/CA2875133A1/en not_active Abandoned
  • 2013-05-30 JP JP2015514591A patent/JP6621328B2/ja active Active
  • 2013-05-30 MX MX2014014377A patent/MX355182B/es active IP Right Grant
  • 2013-05-30 GB GB1421899.4A patent/GB2517620B/en active Active
  • 2013-05-30 MY MYPI2014003333A patent/MY166594A/en unknown
  • 2013-05-30 BR BR112014029931A patent/BR112014029931A2/pt not_active Application Discontinuation
  • 2013-05-30 WO PCT/GB2013/051443 patent/WO2013179047A1/en not_active Ceased
  • 2013-05-30 AU AU2013269330A patent/AU2013269330B2/en active Active
  • 2013-05-30 EP EP20189013.4A patent/EP3750566A1/en not_active Withdrawn
  • 2013-05-30 RU RU2014153900A patent/RU2663457C2/ru not_active IP Right Cessation
  • 2013-05-30 IN IN10234DEN2014 patent/IN2014DN10234A/en unknown
  • 2013-05-30 CN CN201380028751.8A patent/CN105007953B/zh active Active
• 2014
  • 2014-11-23 IL IL235857A patent/IL235857A0/en unknown
  • 2014-11-27 ZA ZA2014/08742A patent/ZA201408742B/en unknown
  • 2014-11-28 DO DO2014000275A patent/DOP2014000275A/es unknown
  • 2014-11-28 PH PH12014502658A patent/PH12014502658A1/en unknown
  • 2014-11-28 CL CL2014003240A patent/CL2014003240A1/es unknown
• 2018
  • 2018-06-19 JP JP2018116036A patent/JP2018187403A/ja active Pending

Patent Citations (6)

Also Published As

Similar Documents

Legal Events