WO2013122873A1 - Powder metal with solid lubricant and powder metal scroll compressor made therefrom - Google Patents

Powder metal with solid lubricant and powder metal scroll compressor made therefrom Download PDF

Info

Publication number
WO2013122873A1
WO2013122873A1 PCT/US2013/025576 US2013025576W WO2013122873A1 WO 2013122873 A1 WO2013122873 A1 WO 2013122873A1 US 2013025576 W US2013025576 W US 2013025576W WO 2013122873 A1 WO2013122873 A1 WO 2013122873A1
Authority
WO
WIPO (PCT)
Prior art keywords
powder
powder metal
scroll compressor
solid lubricant
graphite
Prior art date
Application number
PCT/US2013/025576
Other languages
English (en)
French (fr)
Inventor
Ian William Donaldson
John David S. GUROSIK
Original Assignee
Gkn Sinter Metals, Llc
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Gkn Sinter Metals, Llc filed Critical Gkn Sinter Metals, Llc
Priority to BR112014017956A priority Critical patent/BR112014017956A8/pt
Priority to JP2014557709A priority patent/JP2015528850A/ja
Priority to CN201380009465.7A priority patent/CN104114306A/zh
Priority to US14/377,218 priority patent/US20150017043A1/en
Priority to DE112013000990.0T priority patent/DE112013000990T5/de
Publication of WO2013122873A1 publication Critical patent/WO2013122873A1/en

Links

Classifications

    • CCHEMISTRY; METALLURGY
    • C22METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22CALLOYS
    • C22C33/00Making ferrous alloys
    • C22C33/02Making ferrous alloys by powder metallurgy
    • C22C33/0257Making ferrous alloys by powder metallurgy characterised by the range of the alloying elements
    • C22C33/0264Making ferrous alloys by powder metallurgy characterised by the range of the alloying elements the maximum content of each alloying element not exceeding 5%
    • BPERFORMING OPERATIONS; TRANSPORTING
    • B22CASTING; POWDER METALLURGY
    • B22FWORKING METALLIC POWDER; MANUFACTURE OF ARTICLES FROM METALLIC POWDER; MAKING METALLIC POWDER; APPARATUS OR DEVICES SPECIALLY ADAPTED FOR METALLIC POWDER
    • B22F1/00Metallic powder; Treatment of metallic powder, e.g. to facilitate working or to improve properties
    • B22F1/09Mixtures of metallic powders
    • BPERFORMING OPERATIONS; TRANSPORTING
    • B22CASTING; POWDER METALLURGY
    • B22FWORKING METALLIC POWDER; MANUFACTURE OF ARTICLES FROM METALLIC POWDER; MAKING METALLIC POWDER; APPARATUS OR DEVICES SPECIALLY ADAPTED FOR METALLIC POWDER
    • B22F1/00Metallic powder; Treatment of metallic powder, e.g. to facilitate working or to improve properties
    • B22F1/10Metallic powder containing lubricating or binding agents; Metallic powder containing organic material
    • B22F1/105Metallic powder containing lubricating or binding agents; Metallic powder containing organic material containing inorganic lubricating or binding agents, e.g. metal salts
    • FMECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
    • F04POSITIVE - DISPLACEMENT MACHINES FOR LIQUIDS; PUMPS FOR LIQUIDS OR ELASTIC FLUIDS
    • F04CROTARY-PISTON, OR OSCILLATING-PISTON, POSITIVE-DISPLACEMENT MACHINES FOR LIQUIDS; ROTARY-PISTON, OR OSCILLATING-PISTON, POSITIVE-DISPLACEMENT PUMPS
    • F04C18/00Rotary-piston pumps specially adapted for elastic fluids
    • F04C18/02Rotary-piston pumps specially adapted for elastic fluids of arcuate-engagement type, i.e. with circular translatory movement of co-operating members, each member having the same number of teeth or tooth-equivalents
    • F04C18/0207Rotary-piston pumps specially adapted for elastic fluids of arcuate-engagement type, i.e. with circular translatory movement of co-operating members, each member having the same number of teeth or tooth-equivalents both members having co-operating elements in spiral form
    • FMECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
    • F04POSITIVE - DISPLACEMENT MACHINES FOR LIQUIDS; PUMPS FOR LIQUIDS OR ELASTIC FLUIDS
    • F04CROTARY-PISTON, OR OSCILLATING-PISTON, POSITIVE-DISPLACEMENT MACHINES FOR LIQUIDS; ROTARY-PISTON, OR OSCILLATING-PISTON, POSITIVE-DISPLACEMENT PUMPS
    • F04C18/00Rotary-piston pumps specially adapted for elastic fluids
    • F04C18/02Rotary-piston pumps specially adapted for elastic fluids of arcuate-engagement type, i.e. with circular translatory movement of co-operating members, each member having the same number of teeth or tooth-equivalents
    • F04C18/0207Rotary-piston pumps specially adapted for elastic fluids of arcuate-engagement type, i.e. with circular translatory movement of co-operating members, each member having the same number of teeth or tooth-equivalents both members having co-operating elements in spiral form
    • F04C18/0215Rotary-piston pumps specially adapted for elastic fluids of arcuate-engagement type, i.e. with circular translatory movement of co-operating members, each member having the same number of teeth or tooth-equivalents both members having co-operating elements in spiral form where only one member is moving
    • FMECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
    • F04POSITIVE - DISPLACEMENT MACHINES FOR LIQUIDS; PUMPS FOR LIQUIDS OR ELASTIC FLUIDS
    • F04CROTARY-PISTON, OR OSCILLATING-PISTON, POSITIVE-DISPLACEMENT MACHINES FOR LIQUIDS; ROTARY-PISTON, OR OSCILLATING-PISTON, POSITIVE-DISPLACEMENT PUMPS
    • F04C18/00Rotary-piston pumps specially adapted for elastic fluids
    • F04C18/02Rotary-piston pumps specially adapted for elastic fluids of arcuate-engagement type, i.e. with circular translatory movement of co-operating members, each member having the same number of teeth or tooth-equivalents
    • F04C18/0207Rotary-piston pumps specially adapted for elastic fluids of arcuate-engagement type, i.e. with circular translatory movement of co-operating members, each member having the same number of teeth or tooth-equivalents both members having co-operating elements in spiral form
    • F04C18/0246Details concerning the involute wraps or their base, e.g. geometry
    • F04C18/0253Details concerning the base
    • FMECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
    • F04POSITIVE - DISPLACEMENT MACHINES FOR LIQUIDS; PUMPS FOR LIQUIDS OR ELASTIC FLUIDS
    • F04CROTARY-PISTON, OR OSCILLATING-PISTON, POSITIVE-DISPLACEMENT MACHINES FOR LIQUIDS; ROTARY-PISTON, OR OSCILLATING-PISTON, POSITIVE-DISPLACEMENT PUMPS
    • F04C29/00Component parts, details or accessories of pumps or pumping installations, not provided for in groups F04C18/00 - F04C28/00
    • F04C29/02Lubrication; Lubricant separation
    • FMECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
    • F01MACHINES OR ENGINES IN GENERAL; ENGINE PLANTS IN GENERAL; STEAM ENGINES
    • F01CROTARY-PISTON OR OSCILLATING-PISTON MACHINES OR ENGINES
    • F01C17/00Arrangements for drive of co-operating members, e.g. for rotary piston and casing
    • F01C17/06Arrangements for drive of co-operating members, e.g. for rotary piston and casing using cranks, universal joints or similar elements
    • F01C17/066Arrangements for drive of co-operating members, e.g. for rotary piston and casing using cranks, universal joints or similar elements with an intermediate piece sliding along perpendicular axes, e.g. Oldham coupling
    • FMECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
    • F04POSITIVE - DISPLACEMENT MACHINES FOR LIQUIDS; PUMPS FOR LIQUIDS OR ELASTIC FLUIDS
    • F04CROTARY-PISTON, OR OSCILLATING-PISTON, POSITIVE-DISPLACEMENT MACHINES FOR LIQUIDS; ROTARY-PISTON, OR OSCILLATING-PISTON, POSITIVE-DISPLACEMENT PUMPS
    • F04C2230/00Manufacture
    • F04C2230/20Manufacture essentially without removing material
    • F04C2230/22Manufacture essentially without removing material by sintering

Definitions

  • This disclosure relates to powder metal formulations including solid lubricants and further relates to powder metal parts, such as scroll compressors, made using these powder metal formulations.
  • scroll portions may be shaped as involutes, spirals, or other such curves.
  • one of the scroll portions is gyrated relative to the other scroll portion. This movement of the scroll portions relative to one another causes the points of contact between the two scroll portions to vary. These changing points of contact between the scrolls, when made over a continuous length, can result in the forced movement and the compression of gases and/or refrigerants between the two parts.
  • the parts for a scroll compressor can have relatively complex geometries (i.e., may have an involute or a spiral shape) and can present fabrication challenges. Because powder metallurgy is well adapted to handle certain complex geometries and high part volumes, powder metal processes have been explored as one means to make the scroll portion of a scroll compressor or, more ambitiously, all of a scroll compressor.
  • Powder metal parts may be fabricated in the
  • a powder metal starting material is compacted under pressure using a die and tool set to form the loose powder metal into a powder metal compact.
  • This powder metal compact has a shape that is relatively close to, but slightly larger than, the shape of the final desired part.
  • This powder metal compact is then sintered to cause the adjacent powder metal particles to diffuse into one another and to neck together thereby bonding the particles together. This sintering is typically done at just below the melting temperature of the powder metal material but, in some
  • a liquid phase may also be developed during sintering.
  • the sintered powder metal forms a much stronger sintered part that might be subjected to any of a number of finishing processes (e.g., machining, grinding, deburring, and so forth) , reworking (e.g., forging or coining), or simply used as -sintered.
  • a powder metal formulation is disclosed which is particularly useful in the production of powder metal scroll compressors.
  • This powder metal formulation includes a solid lubricant such as, for example, talc or boron nitride which is carried through the powder metal formation process such that the solid lubricant is part of the final powder metal scroll compressor.
  • the solid lubricant is a nickel -coated graphite powder.
  • the solid lubricant is admixed with the other constituents of the powder metal material.
  • a scroll compressor can be made that includes a solid lubricant.
  • this solid lubricant helps promote smooth contact between the scrolls with reduced amounts of friction.
  • the solid lubricant is also inert such that it does not present any concerns when it is used to compress, for example, a refrigerant.
  • a powder metal scroll compressor includes a hub and a scroll adjoined to one another in which a powder metal forms at least a portion of the powder metal scroll compressor including the scroll .
  • the powder metal includes iron powder, carbon in an amount of less than 0.9% by weight of the powder metal, and a solid lubricant in the powder metal .
  • the iron powder and solid lubricant may be admixed with one another prior to compaction and sintering of the powder metal scroll compressor.
  • the solid lubricant may be 0.25% to 3.0% by weight of the powder metal and the powder metal may include only iron powder, carbon, the solid lubricant and be substantially free of other constituents.
  • the powder metal may contain other constituents.
  • the powder metal may further include copper powder (which may be elemental copper powder) in an amount of less than 3.0% by weight of the powder metal.
  • the iron powder, the copper powder, and the solid lubricant may be admixed with one another prior to compaction and sintering of the powder metal scroll compressor and the powder metal may include only iron powder, carbon, copper powder, and the solid lubricant and be substantially free of other constituents.
  • the solid lubricant should be capable of surviving the compaction and sintering process (for example, not burn off at sintering temperatures) .
  • the solid lubricants being referred to are not typical lubricants, waxes, or binders that are conventionally used to help the compacted powder metal parts retain their shape or be ejected from the compaction tooling, as those conventional lubricants, waxes, or binders are consumed and lost during any initial burn off and/or sintering operations. Accordingly, many of the solid lubricants described herein remain inert and stable in an Fe-C or an Fe- Cu-C system through processing of temperatures up to 1080 degrees Centigrade, for example.
  • One solid lubricant that may be used is talc
  • the talc may have a nominal 15 to 25 micron mean particle size (d50) .
  • hexagonal boron nitride (BN) .
  • the hexagonal boron nitride may have a nominal 5 to 30 micron mean particle size (d50) .
  • the solid lubricant may be provided in the form of a nickel-coated graphite powder.
  • the carbon may be present in an amount of less than ⁇ 0.9% by weight of the powder metal material, exclusive of the graphite of the nickel -coated graphite powder (as this graphite powder does not significantly contribute to the carbon content in the iron) .
  • a nickel coating of the nickel -coated graphite powder may substantially surround the graphite to protect the graphite during sintering of the powder metal scroll
  • a nickel content of the nickel -coated graphite powder may be in a range of 55 to 80 wt% with the remainder being graphite.
  • a total amount of graphite in the powder metal scroll compressor may be in the range of 0.5 to 5.0 wt%, or more narrowly 1.0 to 3.0 wt%, exclusive of the carbon in an amount of less than 0.9% by weight of the powder metal material.
  • the nickel-coated graphite powder may have an average particle size of approximately 100 microns.
  • a powder metal is provided, such as a powder metal that may be used for a powder metal scroll compressor of the type described above.
  • the powder metal includes iron powder, carbon in an amount of less than 0.9% by weight of the powder metal material, and a solid lubricant .
  • the iron powder and solid lubricant are admixed with one another.
  • the powder metal may include iron powder, carbon, the solid lubricant and be substantially free of other constituents.
  • the powder metal may further include a copper powder (such as an elemental copper powder) in an amount of less than 3.0% by weight of the powder metal.
  • the iron powder, the copper powder, and the solid lubricant may be admixed with one another, and the powder metal may include iron powder, carbon, copper powder, and the solid lubricant and be substantially free of other constituents.
  • the solid lubricant may be 0.25% to 3.0% by weight of the powder metal.
  • the solid lubricant may remain inert and stable in an Fe-C or an Fe-Cu-C system through processing of temperatures up to 1080 degrees Centigrade.
  • the solid lubricant may be talc (Mg 3 Si O 10 (OH) 2 ) .
  • the talc may have a nominal 15 to 25 micron mean particle size (d50) .
  • the solid lubricant may be any suitable lubricant.
  • hexagonal boron nitride (BN) .
  • the hexagonal . boron nitride may have a nominal 5 to 30 micron mean particle size (d50) .
  • the solid lubricant may be a nickel -coated graphite powder and in which the carbon in an amount of less than 0.9% by weight of the powder metal material is exclusive of the graphite of the nickel-coated graphite powder.
  • a nickel coating of the nickel -coated graphite powder may substantially surround the graphite to protect the graphite during sintering of the powder metal scroll compressor and to prevent the graphite from combining with the iron powder.
  • a nickel content of the nickel-coated graphite powder may be in a range of 55 to 80 wt% with the remainder being graphite.
  • a total amount of graphite in the powder metal scroll compressor may be in the range of 0.5 to 5.0 wt%, or more narrowly 1.0 to 3.0 wt%, exclusive of the carbon in an amount of less than 0.9% by weight of the powder metal material.
  • the nickel-coated graphite powder may be an average particle size of approximately 100 microns.
  • a part may be made using any of the powder metal formulations described herein by compacting and sintering the powder metal to form the part.
  • the solid lubricant is retained throughout the process and is dispersed throughout the part including the surface of the part. It may be particularly advantageous when this surface of the part is a bearing surface such that the solid lubricant can serve as a lubricant on this surface.
  • FIG. 1 is a top perspective view of a one-piece scroll compressor showing the hub side.
  • FIG. 2 is a bottom perspective view of the scroll compressor of FIG. 1 showing the scroll side.
  • FIG. 3 is a top plan view of the scroll compressor of FIG. 1.
  • FIG. 4 is a cross-sectional side view of the scroll compressor taken along line 4-4 of FIG. 3.
  • FIGS. 1 through 4 a one-piece scroll compressor 100 is shown.
  • the powder metal scroll compressor 100 can be produced from a single powder metal compact using the powder metal processes according to the method described in PCT International Publication No.
  • the powder metal formulation could be used to separately make one or more portions of the part or the entirety of the part using, for example, the methods described in PCT International
  • the scroll compressor 100 is a powder metal part which is formed by compression along an axis of compaction A- A.
  • the scroll compressor 100 includes a flange 102, a hub 104, and a scroll 106.
  • the flange 102 has a top face 108 and a bottom face 110 which extend in a direction perpendicular to the axis A-A and which are essentially planar and parallel to one another.
  • Two mounting slots 112 are formed around an outer periphery of the flange 102 for mounting the scroll compressor 100 to another item in a refrigeration assembly or the like .
  • the hub 104 axially extends from the top face 108 of the flange 102.
  • the hub 104 is generally cylindrically- shaped and has a radially outward facing surface 114, a radially inward facing surface 116, and a top axial face 118. Both the radially outward facing surface 114 and the radially inward facing surface 116 may have a slight taper as they extend away from the top face 108 of the flange 102 towards the top axial face 118. By having a taper, the scroll compressor 100 can be more easily separated from the tool members during the ejection process.
  • the scroll 106 extends axially from the bottom face 110 of the flange 102.
  • the scroll 106 is a spiraling wall that spirals relative to the axis A-A.
  • the scroll 106 includes an inner wall end 120 and an outer wall end 122 with a generally radially outward facing surface 124 and a generally radially inward facing surface 126 extending between the ends 120 and 122. These surfaces 124 and 126 run
  • a bottom axial face 128 of the scroll 106 is also spiral -shaped.
  • the generally radially outward facing surface 124 and the generally radially inward facing surface 126 may have a taper to ease the ejection process from the tool and die set during compaction of the powder metal.
  • the spiral is similar to an Archimedean spiral, meaning that if a radial line is drawn relative to the axis A-A, a channel 130 formed between the generally radially outward and inward facing surfaces 124 and 126 is also of substantially constant width regardless of the distance from the axis A-A.
  • other involute is also of substantially constant width regardless of the distance from the axis A-A.
  • top features such as the hub 104 are formed by transferring powder metal within the die cavity by a powder transfer motion of the lower tool members. As the powder is transferred, the powder fill to final part ratio along the vertical columns of the part must be approximately 2:1 to provide a part that is relatively uniformly dense after the compaction process.
  • the powder metal used to make this powder metal scroll compressor includes iron powder (either elemental or prealloyed iron) , carbon in an amount less than 0.9 wt% of the powder metal, and solid lubricant in an amount between 0.25 wt% and 3.0 wt% of the powder metal.
  • iron powder either elemental or prealloyed iron
  • carbon in an amount less than 0.9 wt% of the powder metal
  • solid lubricant in an amount between 0.25 wt% and 3.0 wt% of the powder metal.
  • Other elemental additions could also be included such as, for example, copper (Cu) and nickel (Ni) .
  • the powder metal formulation is relatively simplistic in that it does not require more than these listed
  • Mixing of the various constituent powders may be performed using conventional means such as v-blenders or double cone mixers.
  • the various constituent powders can be admixed together along with pressing lubricants (e.g., lithium stearate, Licowax, etc.) in addition to the solid lubricant.
  • pressing lubricants e.g., lithium stearate, Licowax, etc.
  • the solid lubricant for this powder metal formulation may be talc, which is also known as hydrated magnesium silicate and has the chemical formula of Mg 3 Si 4 Oio (OH) 2 ⁇
  • talc When used as a solid lubricant, some amount of quartz impurity may exist within the talc.
  • the talc When talc is used as the solid lubricant, the talc may be preferably provided in a powder form having a nominal 15 to 25 micron mean particle size (d50) .
  • the solid lubricant for this powder formulation may be a hexagonal boron nitride (BN) .
  • BN hexagonal boron nitride
  • the boron nitride may be preferably provided in a powder form having a nominal 5 to 30 micron mean particle size (d50) .
  • nickel-coated graphite powder As the solid lubricant.
  • the nickel coating protects the graphite during sintering and prevents the graphite from combining with the iron powder. In the finished product, the coating protects and preserves the graphite until rupture of the nickel coating during use of the component (e.g., rupture due to wear on surfaces), to release the graphite lubricant.
  • the nickel-coated graphite has nickel content ranging from 55 to 80 wt% with the remainder being graphite.
  • the nickel-coated graphite powder may have an average particle size of approximately 100 microns.
  • Graphite size may be coarse (Tyler mesh size -120/+230 at 88-98% or a range of 115 to 65 microns) to fine (Tyler mesh size -120/+270 at > 85% and -270/+325 ⁇ 15% or a range of 115 to 43 microns) with both having a small amount of more coarse and finer particle sizes ( ⁇ 5 wt%) .
  • the solid lubricant is added to the mix to provide a graphite level of 0.5 wt% to 5 wt%, although a graphite range of 1 wt% to 3 wt% is believed to be typical for most applications. This graphite is exclusive of the carbon content in the powder metal which is used to alter the metallurgical properties of the iron powder.
  • this powder metal formulation incorporates the powder for the solid lubricant as an admixed constituent in the powder metal.
  • the admixed solid lubricant is inert in Fe-C, Fe-Cu-C and other powder metal mixtures processed at temperatures around 1180 degrees Centigrade. This means that even after the powder metal has been compacted and sintered into a final part, all or a substantial portion of the solid lubricant remains present.
  • the solid lubricant assists in reducing frictional heat and spalling/galling in a system with reciprocal motion under a mechanical load such as that in which a scroll compressor is used (and, in particular, in the scroll section of the scroll compressor) .
  • the solid lubricant is resistant to adhesion and does not create significant resistance to motion of the scroll compressor.
  • the inclusion of the solid lubricant may be best implemented in powder metal parts that have ferritic/pearlitic microstructures and its inclusion can also be used for improving machinability .
  • the powder metal formulation can be formulated to have less than 0.9 wt% carbon, less than 3.0% copper, and between 0.25 to 3.0 wt% of solid lubricant with the remainder of the powder being elemental iron with no other substantial additions. Again, this is a relatively simple powder formula that does not contain a large number of alloying elements.
  • Powder metal formulations such as those described above can be prepared and then processed into a sintered powder metal part by compacting the powder into a powder metal compact and then sintering the powder. It is contemplated that such parts might be compacted as unitary bodies or might be formed from separately compacted components that are subsequently joined together to form a single final part.
  • any section of a part made from various joined sections may have the powder metal containing the solid lubricant in those sections in which the solid lubricant will be most desirable.
  • the scroll section of a scroll compressor may be made using the powder described above, while the other section to which the scroll section is joined may be made of a powder metal material that does not include the solid lubricant.
  • the other section to which the scroll section is joined may be made of a powder metal material that does not include the solid lubricant.

Landscapes

  • Engineering & Computer Science (AREA)
  • Mechanical Engineering (AREA)
  • General Engineering & Computer Science (AREA)
  • Chemical & Material Sciences (AREA)
  • Inorganic Chemistry (AREA)
  • Materials Engineering (AREA)
  • Metallurgy (AREA)
  • Organic Chemistry (AREA)
  • Powder Metallurgy (AREA)
  • Rotary Pumps (AREA)
  • Applications Or Details Of Rotary Compressors (AREA)
  • Lubricants (AREA)
PCT/US2013/025576 2012-02-15 2013-02-11 Powder metal with solid lubricant and powder metal scroll compressor made therefrom WO2013122873A1 (en)

Priority Applications (5)

Application Number Priority Date Filing Date Title
BR112014017956A BR112014017956A8 (pt) 2012-02-15 2013-02-11 Metal em pó com lubrificante sólido e compressor em espiral de metal em pó feito do mesmo
JP2014557709A JP2015528850A (ja) 2012-02-15 2013-02-11 固体潤滑剤を含む粉末金属及びそれで作られた粉末金属スクロール圧縮機
CN201380009465.7A CN104114306A (zh) 2012-02-15 2013-02-11 具有固体润滑剂的粉末金属及由该粉末金属制成的粉末金属涡旋式压缩机
US14/377,218 US20150017043A1 (en) 2012-02-15 2013-02-11 Powder metal with solid lubricant and powder metal scroll compressor made therefrom
DE112013000990.0T DE112013000990T5 (de) 2012-02-15 2013-02-11 Pulvermetall mit Festschmierstoff und ein daraus hergestellter Pulvermetallscrollverdichter

Applications Claiming Priority (4)

Application Number Priority Date Filing Date Title
US201261599042P 2012-02-15 2012-02-15
US61/599,042 2012-02-15
US201261720226P 2012-10-30 2012-10-30
US61/720,226 2012-10-30

Related Child Applications (2)

Application Number Title Priority Date Filing Date
US14/378,297 A-371-Of-International US9350942B2 (en) 2012-02-13 2013-02-12 Video session manager and method for enabling and managing video calling and telepresence communications sessions across multiple domains
US15/141,566 Continuation US9641802B2 (en) 2012-02-13 2016-04-28 Video session manager and method for enabling and managing video calling and telepresence communications sessions across multiple domains

Publications (1)

Publication Number Publication Date
WO2013122873A1 true WO2013122873A1 (en) 2013-08-22

Family

ID=47827425

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US2013/025576 WO2013122873A1 (en) 2012-02-15 2013-02-11 Powder metal with solid lubricant and powder metal scroll compressor made therefrom

Country Status (6)

Country Link
US (1) US20150017043A1 (de)
JP (1) JP2015528850A (de)
CN (1) CN104114306A (de)
BR (1) BR112014017956A8 (de)
DE (1) DE112013000990T5 (de)
WO (1) WO2013122873A1 (de)

Families Citing this family (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE102017125096B4 (de) * 2017-10-26 2022-05-19 Hanon Systems Verfahren zum Herstellen eines Scrollverdichters und mit dem Verfahren hergestellter Scrollverdichter

Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP1002883A1 (de) * 1998-11-19 2000-05-24 Eaton Corporation Ventilsitz aus Metallpulver
EP1331395A2 (de) * 2002-01-24 2003-07-30 Copeland Corporation Spiralmaschinerotor aus Metallpulver
EP1985393A1 (de) * 2006-02-15 2008-10-29 JFE Steel Corporation Mischpulver auf eisenbasis und verfahren zur herstellung von pulverpresslingen und gesinterten pulverpresslingen auf eisenbasis
US20100229386A1 (en) * 2009-03-11 2010-09-16 Emerson Climate Technologies, Inc. Powder metal scrolls and sinter-brazing methods for making the same
WO2010135232A1 (en) 2009-05-18 2010-11-25 Gkn Sinter Metals, Llc Powder metal die filling

Family Cites Families (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
BE755697A (fr) * 1969-09-03 1971-03-03 Int Nickel Ltd Fabrication de produits metalliques frittes
JPS58133347A (ja) * 1982-01-30 1983-08-09 Oiles Ind Co Ltd 高温用焼結摺動部材ならびにその製造方法
GB9207139D0 (en) * 1992-04-01 1992-05-13 Brico Eng Sintered materials
JPH06192710A (ja) * 1992-12-25 1994-07-12 Toshiba Corp 圧縮機用摺動部材およびその製造方法
JP4215285B2 (ja) * 1995-08-08 2009-01-28 株式会社小松製作所 自己潤滑性焼結摺動材およびその製造方法
SE0203134D0 (sv) * 2002-10-22 2002-10-22 Hoeganaes Ab Method of preparing iron-based components

Patent Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP1002883A1 (de) * 1998-11-19 2000-05-24 Eaton Corporation Ventilsitz aus Metallpulver
EP1331395A2 (de) * 2002-01-24 2003-07-30 Copeland Corporation Spiralmaschinerotor aus Metallpulver
EP1985393A1 (de) * 2006-02-15 2008-10-29 JFE Steel Corporation Mischpulver auf eisenbasis und verfahren zur herstellung von pulverpresslingen und gesinterten pulverpresslingen auf eisenbasis
US20100229386A1 (en) * 2009-03-11 2010-09-16 Emerson Climate Technologies, Inc. Powder metal scrolls and sinter-brazing methods for making the same
WO2010135232A1 (en) 2009-05-18 2010-11-25 Gkn Sinter Metals, Llc Powder metal die filling
US20120118104A1 (en) 2009-05-18 2012-05-17 Gurosik John D Powder Metal Die Filling

Also Published As

Publication number Publication date
BR112014017956A2 (de) 2017-06-20
DE112013000990T5 (de) 2015-04-09
JP2015528850A (ja) 2015-10-01
BR112014017956A8 (pt) 2017-07-11
US20150017043A1 (en) 2015-01-15
CN104114306A (zh) 2014-10-22

Similar Documents

Publication Publication Date Title
JP4480084B2 (ja) 鉄基焼結合金部材およびその製造方法
US7854995B1 (en) High density dual helical gear
EP2524749B1 (de) Metallurgische Zusammensetzung von Partikelmaterialien, selbstschmierendes, gesintertes Produkt und Verfahren zum Erhalten von selbstschmierenden gesinterten Produkten
CN104755775B (zh) 烧结轴承
JP5147184B2 (ja) 鉄基焼結合金およびその製造方法
US20050034559A1 (en) Sinterable metal powder mixture for the production of sintered components
WO2010080064A1 (en) Multilevel parts from agglomerated spherical metal powder
KR101061346B1 (ko) 분말 야금용 혼합 분말, 그 압분체 및 소결체
JP2007138226A (ja) 鉄系焼結部品、鉄系焼結部品の製造方法、アクチェエータ
JP4964126B2 (ja) 成形生成物を製造する方法
JP2002504188A (ja) 高密度の高炭素焼結金属粉末鋼部品の製造法
Simchi et al. Warm compaction of metallic powders
MX2007008208A (es) Metodo de formacion de componentes de polvo de metal con densificacion de superficie.
US7364803B1 (en) High density dual helical gear and method for manufacture thereof
US20150017043A1 (en) Powder metal with solid lubricant and powder metal scroll compressor made therefrom
JP2001523763A (ja) 粉末ブレンドによる高密度成形方法
EP1545816A1 (de) Hochdichte materialien auf metallbasis mit niedrigen reibungskoeffizienten und verschleissraten
WO2011040242A1 (ja) 動力伝達部品
EP3052808B1 (de) Pulvermetallspiralen mit modifizierter spitzenkonstruktion
KR101650174B1 (ko) 구리-탄소결합분말 및 이를 이용하여 제조되는 압분체 및 슬라이드재.
JP5177787B2 (ja) Fe基焼結合金の製造方法とそのFe基焼結合金
Kandavel et al. Experimental Investigations on Plastic Deformation and Densification Characteristics of P/M Fe–C–Cu–Mo Alloy Steels Under Cold Upsetting
KR101650173B1 (ko) 구리-탄소결합분말의 제조방법 및 이를 이용하여 제조된 구리-탄소결합분말
CN112166001B (zh) 粉末冶金用粉末混合物及其制造方法
US11850662B1 (en) High strength part having powder metal internal ring

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 13707737

Country of ref document: EP

Kind code of ref document: A1

ENP Entry into the national phase

Ref document number: 2014557709

Country of ref document: JP

Kind code of ref document: A

WWE Wipo information: entry into national phase

Ref document number: 112013000990

Country of ref document: DE

Ref document number: 1120130009900

Country of ref document: DE

REG Reference to national code

Ref country code: BR

Ref legal event code: B01A

Ref document number: 112014017956

Country of ref document: BR

122 Ep: pct application non-entry in european phase

Ref document number: 13707737

Country of ref document: EP

Kind code of ref document: A1

ENP Entry into the national phase

Ref document number: 112014017956

Country of ref document: BR

Kind code of ref document: A2

Effective date: 20140722