WO2013080949A1 - Dispositif d'affichage à cristaux liquides, plaque polarisante et film protecteur de polariseur - Google Patents

Dispositif d'affichage à cristaux liquides, plaque polarisante et film protecteur de polariseur Download PDF

Info

Publication number
WO2013080949A1
WO2013080949A1 PCT/JP2012/080562 JP2012080562W WO2013080949A1 WO 2013080949 A1 WO2013080949 A1 WO 2013080949A1 JP 2012080562 W JP2012080562 W JP 2012080562W WO 2013080949 A1 WO2013080949 A1 WO 2013080949A1
Authority
WO
WIPO (PCT)
Prior art keywords
film
liquid crystal
polarizer
retardation
crystal display
Prior art date
Application number
PCT/JP2012/080562
Other languages
English (en)
Japanese (ja)
Inventor
村田 浩一
佐々木 靖
Original Assignee
東洋紡株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Family has litigation
First worldwide family litigation filed litigation Critical https://patents.darts-ip.com/?family=48535404&utm_source=google_patent&utm_medium=platform_link&utm_campaign=public_patent_search&patent=WO2013080949(A1) "Global patent litigation dataset” by Darts-ip is licensed under a Creative Commons Attribution 4.0 International License.
Application filed by 東洋紡株式会社 filed Critical 東洋紡株式会社
Priority to CN201280058785.7A priority Critical patent/CN103959148B/zh
Priority to KR1020147016784A priority patent/KR101737679B1/ko
Priority to JP2013547152A priority patent/JP5804079B2/ja
Publication of WO2013080949A1 publication Critical patent/WO2013080949A1/fr

Abstract

Le but de la présente invention est de diminuer encore l'apparition d'irrégularités spectrales dans un dispositif d'affichage à cristaux liquides qui utilise une diode électroluminescente comme source de lumière et utilise un film polyester orienté ayant un retard donné comme film protecteur de polariseur. Ce dispositif d'affichage à cristaux liquides comprend une source lumineuse de rétroéclairage, deux plaques polarisantes et une cellule à cristaux liquides disposée entre les deux plaques polarisantes. La source lumineuse de rétroéclairage est une source de lumière blanche ayant un spectre d'émission continu. Les deux plaques polarisantes sont chacune formées à partir d'un polariseur et de films protecteurs des deux côtés du polariseur. Au moins l'un des films protecteurs situés de chaque côté est un film polyester orienté ayant un retard de 3 000 à 30 000 nm. L'axe de polarisation du polariseur et l'axe d'orientation principal du film polyester orienté, qui est un film protecteur du polariseur, sont sensiblement parallèles.
PCT/JP2012/080562 2011-11-29 2012-11-27 Dispositif d'affichage à cristaux liquides, plaque polarisante et film protecteur de polariseur WO2013080949A1 (fr)

Priority Applications (3)

Application Number Priority Date Filing Date Title
CN201280058785.7A CN103959148B (zh) 2011-11-29 2012-11-27 液晶显示装置、偏光板和偏振片保护膜
KR1020147016784A KR101737679B1 (ko) 2011-11-29 2012-11-27 액정표시장치, 편광판 및 편광자 보호 필름
JP2013547152A JP5804079B2 (ja) 2011-11-29 2012-11-27 液晶表示装置、偏光板および偏光子保護フィルム

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2011-259849 2011-11-29
JP2011259849 2011-11-29

Publications (1)

Publication Number Publication Date
WO2013080949A1 true WO2013080949A1 (fr) 2013-06-06

Family

ID=48535404

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2012/080562 WO2013080949A1 (fr) 2011-11-29 2012-11-27 Dispositif d'affichage à cristaux liquides, plaque polarisante et film protecteur de polariseur

Country Status (5)

Country Link
JP (5) JP5804079B2 (fr)
KR (1) KR101737679B1 (fr)
CN (1) CN103959148B (fr)
TW (1) TWI515485B (fr)
WO (1) WO2013080949A1 (fr)

Cited By (14)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2015055680A (ja) * 2013-09-10 2015-03-23 大日本印刷株式会社 偏光板、偏光板の製造方法、画像表示装置、画像表示装置の製造方法及び偏光板の光透過率改善方法
JP2015055679A (ja) * 2013-09-10 2015-03-23 大日本印刷株式会社 偏光板、偏光板の製造方法、画像表示装置、画像表示装置の製造方法及び偏光板の光透過率改善方法
JP2015135404A (ja) * 2014-01-17 2015-07-27 東洋紡株式会社 偏光子保護フィルム、偏光板及び液晶表示装置
JP2015141260A (ja) * 2014-01-28 2015-08-03 東洋紡株式会社 偏光子保護フィルム、偏光板及液晶表示装置
WO2015122520A1 (fr) * 2014-02-17 2015-08-20 大日本印刷株式会社 Stratifié, méthode de fabrication de stratifié, dispositif d'affichage d'image, méthode de fabrication de dispositif d'affichage d'image, et méthode d'amélioration de transmittance de lumière de plaque polarisante
JP2017062500A (ja) * 2016-12-06 2017-03-30 大日本印刷株式会社 偏光板、偏光板の製造方法、画像表示装置、画像表示装置の製造方法及び偏光板の光透過率改善方法
US9798189B2 (en) 2010-06-22 2017-10-24 Toyobo Co., Ltd. Liquid crystal display device, polarizer and protective film
JP2018077529A (ja) * 2018-01-22 2018-05-17 大日本印刷株式会社 偏光板、偏光板の製造方法、画像表示装置、画像表示装置の製造方法及び偏光板の光透過率改善方法
US10054816B2 (en) 2009-11-12 2018-08-21 Toyo Boseki Kabushiki Kaisha Method for improving visibility of liquid crystal display device, and liquid crystal display device using same
JP2018145298A (ja) * 2017-03-06 2018-09-20 凸版印刷株式会社 フィルム及び画像表示装置
US10175494B2 (en) 2011-05-18 2019-01-08 Toyobo Co., Ltd. Polarizing plate suitable for liquid crystal display device capable of displaying three-dimensional images, and liquid crystal display device
US10180597B2 (en) 2011-05-18 2019-01-15 Toyobo Co., Ltd. Liquid crystal display device, polarizing plate, and polarizer protection film
JP2021157196A (ja) * 2016-03-16 2021-10-07 東洋紡株式会社 液晶表示装置
JP2021165846A (ja) * 2016-03-16 2021-10-14 東洋紡株式会社 液晶表示装置および偏光板

Families Citing this family (10)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2014171386A1 (fr) * 2013-04-19 2014-10-23 東洋紡株式会社 Écran à cristaux liquides, plaque de polarisation, et film de protection de polariseur
WO2016068102A1 (fr) * 2014-10-30 2016-05-06 東洋紡株式会社 Dispositif d'affichage à cristaux liquides et plaque de polarisation
CN107003562B (zh) * 2014-11-25 2021-07-23 东洋纺株式会社 液晶显示装置和偏光板
KR101813438B1 (ko) * 2015-03-04 2018-01-30 도요보 가부시키가이샤 액정표시장치
KR20180023953A (ko) * 2015-07-16 2018-03-07 도요보 가부시키가이샤 액정 표시 장치 및 편광판
CN108139628A (zh) * 2015-10-16 2018-06-08 东洋纺株式会社 液晶显示装置和偏光板
CN106019689B (zh) * 2016-07-20 2019-07-19 京东方科技集团股份有限公司 显示模组及其制造方法、显示装置
CN106597730A (zh) * 2016-12-27 2017-04-26 深圳市华星光电技术有限公司 液晶显示面板及液晶显示器
JP7187937B2 (ja) * 2018-09-27 2022-12-13 大日本印刷株式会社 意匠材
KR102362364B1 (ko) * 2019-01-23 2022-02-11 삼성에스디아이 주식회사 액정표시장치

Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS58143305A (ja) * 1982-02-22 1983-08-25 Hitachi Ltd 表示パネル
JPS6026304A (ja) * 1983-07-22 1985-02-09 Nitto Electric Ind Co Ltd 偏光板
JP2010096948A (ja) * 2008-10-16 2010-04-30 Seiko Epson Corp 光学フィルム、液晶装置の製造方法
JP2010243630A (ja) * 2009-04-02 2010-10-28 Mitsubishi Plastics Inc 偏光板保護用ポリエステルフィルム

Family Cites Families (10)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS5977401A (ja) * 1982-09-22 1984-05-02 Nitto Electric Ind Co Ltd 偏光板
JP4328243B2 (ja) * 2004-03-16 2009-09-09 富士フイルム株式会社 液晶表示装置
CN100443933C (zh) * 2004-05-18 2008-12-17 富士胶片株式会社 光学补偿起偏振板、图像显示单元和液晶显示单元
US7898628B2 (en) * 2007-08-29 2011-03-01 Mitsubishi Electric Corporation Liquid crystal display device
JP2010079287A (ja) * 2008-08-28 2010-04-08 Fujifilm Corp 液晶表示装置
JP5451215B2 (ja) * 2009-06-29 2014-03-26 帝人デュポンフィルム株式会社 偏光子支持基材用フィルム
JP5568808B2 (ja) * 2009-10-20 2014-08-13 住友化学株式会社 バックライトを備える液晶表示装置および液晶表示装置用光学部材セット
JP4888853B2 (ja) * 2009-11-12 2012-02-29 学校法人慶應義塾 液晶表示装置の視認性改善方法、及びそれを用いた液晶表示装置
JP5307758B2 (ja) * 2010-04-12 2013-10-02 西部自動機器株式会社 超仕上げ装置
JP5885447B2 (ja) * 2011-09-30 2016-03-15 大日本印刷株式会社 積層体及び偏光板保護フィルム

Patent Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS58143305A (ja) * 1982-02-22 1983-08-25 Hitachi Ltd 表示パネル
JPS6026304A (ja) * 1983-07-22 1985-02-09 Nitto Electric Ind Co Ltd 偏光板
JP2010096948A (ja) * 2008-10-16 2010-04-30 Seiko Epson Corp 光学フィルム、液晶装置の製造方法
JP2010243630A (ja) * 2009-04-02 2010-10-28 Mitsubishi Plastics Inc 偏光板保護用ポリエステルフィルム

Cited By (25)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US10948764B2 (en) 2009-11-12 2021-03-16 Keio University Method for improving visibility of liquid crystal display device, and liquid crystal display device using the same
US10054816B2 (en) 2009-11-12 2018-08-21 Toyo Boseki Kabushiki Kaisha Method for improving visibility of liquid crystal display device, and liquid crystal display device using same
US9798189B2 (en) 2010-06-22 2017-10-24 Toyobo Co., Ltd. Liquid crystal display device, polarizer and protective film
US10503016B2 (en) 2010-06-22 2019-12-10 Toyobo Co., Ltd. Liquid crystal display device, polarizer and protective film
US9897857B2 (en) 2010-06-22 2018-02-20 Toyobo Co., Ltd. Liquid crystal display device, polarizer and protective film
US10180597B2 (en) 2011-05-18 2019-01-15 Toyobo Co., Ltd. Liquid crystal display device, polarizing plate, and polarizer protection film
US10175494B2 (en) 2011-05-18 2019-01-08 Toyobo Co., Ltd. Polarizing plate suitable for liquid crystal display device capable of displaying three-dimensional images, and liquid crystal display device
CN105518496A (zh) * 2013-09-10 2016-04-20 大日本印刷株式会社 偏光片、偏光片的制造方法、图像显示装置、图像显示装置的制造方法以及偏光片的透光率改善方法
US10310153B2 (en) 2013-09-10 2019-06-04 Dai Nippon Printing Co., Ltd. Polarizing plate, method for manufacturing polarizing plate, image display device, method for manufacturing image display device, and method for improving transmittance of polarizing plate
JP2015055679A (ja) * 2013-09-10 2015-03-23 大日本印刷株式会社 偏光板、偏光板の製造方法、画像表示装置、画像表示装置の製造方法及び偏光板の光透過率改善方法
JP2015055680A (ja) * 2013-09-10 2015-03-23 大日本印刷株式会社 偏光板、偏光板の製造方法、画像表示装置、画像表示装置の製造方法及び偏光板の光透過率改善方法
CN107765358A (zh) * 2013-09-10 2018-03-06 大日本印刷株式会社 偏光片和图像显示装置及其制造方法、透光率改善方法
JP2015135404A (ja) * 2014-01-17 2015-07-27 東洋紡株式会社 偏光子保護フィルム、偏光板及び液晶表示装置
JP2015141260A (ja) * 2014-01-28 2015-08-03 東洋紡株式会社 偏光子保護フィルム、偏光板及液晶表示装置
WO2015122520A1 (fr) * 2014-02-17 2015-08-20 大日本印刷株式会社 Stratifié, méthode de fabrication de stratifié, dispositif d'affichage d'image, méthode de fabrication de dispositif d'affichage d'image, et méthode d'amélioration de transmittance de lumière de plaque polarisante
JP2015152837A (ja) * 2014-02-17 2015-08-24 大日本印刷株式会社 積層体、積層体の製造方法、画像表示装置、画像表示装置の製造方法及び偏光板の光透過率改善方法
KR102220271B1 (ko) * 2014-02-17 2021-02-25 다이니폰 인사츠 가부시키가이샤 적층체, 적층체의 제조 방법, 화상 표시 장치, 화상 표시 장치의 제조 방법 및 편광판의 광투과율 개선 방법
KR20160120749A (ko) * 2014-02-17 2016-10-18 다이니폰 인사츠 가부시키가이샤 적층체, 적층체의 제조 방법, 화상 표시 장치, 화상 표시 장치의 제조 방법 및 편광판의 광투과율 개선 방법
JP2021157196A (ja) * 2016-03-16 2021-10-07 東洋紡株式会社 液晶表示装置
JP2021165846A (ja) * 2016-03-16 2021-10-14 東洋紡株式会社 液晶表示装置および偏光板
JP7201026B2 (ja) 2016-03-16 2023-01-10 東洋紡株式会社 液晶表示装置
JP7230953B2 (ja) 2016-03-16 2023-03-01 東洋紡株式会社 液晶表示装置および偏光板
JP2017062500A (ja) * 2016-12-06 2017-03-30 大日本印刷株式会社 偏光板、偏光板の製造方法、画像表示装置、画像表示装置の製造方法及び偏光板の光透過率改善方法
JP2018145298A (ja) * 2017-03-06 2018-09-20 凸版印刷株式会社 フィルム及び画像表示装置
JP2018077529A (ja) * 2018-01-22 2018-05-17 大日本印刷株式会社 偏光板、偏光板の製造方法、画像表示装置、画像表示装置の製造方法及び偏光板の光透過率改善方法

Also Published As

Publication number Publication date
KR101737679B1 (ko) 2017-05-18
TW201329569A (zh) 2013-07-16
JP6761381B2 (ja) 2020-09-23
CN103959148A (zh) 2014-07-30
TWI515485B (zh) 2016-01-01
KR20140097413A (ko) 2014-08-06
JP2015166875A (ja) 2015-09-24
JP6179548B2 (ja) 2017-08-16
JP5804079B2 (ja) 2015-11-04
JPWO2013080949A1 (ja) 2015-04-27
JP2017215596A (ja) 2017-12-07
JP2017201417A (ja) 2017-11-09
JP2019174822A (ja) 2019-10-10
CN103959148B (zh) 2016-08-17

Similar Documents

Publication Publication Date Title
JP6179548B2 (ja) 液晶表示装置、偏光板および偏光子保護フィルム
JP5472519B2 (ja) 液晶表示装置、偏光板および偏光子保護フィルム
JP5614506B2 (ja) 液晶表示装置、偏光板および偏光子保護フィルム
JP6443048B2 (ja) 液晶表示装置、偏光板及び偏光子保護フィルム
WO2017010444A1 (fr) Dispositif d'affichage à cristaux liquides et plaque polarisante
JP2015111207A (ja) 偏光子保護フィルム、偏光板及び液晶表示装置
JP6337481B2 (ja) 偏光子保護フィルム、偏光板及液晶表示装置
JP2018028612A (ja) 液晶表示装置
JP6521216B2 (ja) 液晶表示装置及び偏光板
JP6337474B2 (ja) 偏光子保護フィルム、偏光板及び液晶表示装置
JP2015079129A (ja) 液晶表示装置、偏光板及び偏光子保護フィルム
JP2015111206A (ja) 偏光子保護フィルム、偏光板及び液晶表示装置

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 12853966

Country of ref document: EP

Kind code of ref document: A1

ENP Entry into the national phase

Ref document number: 2013547152

Country of ref document: JP

Kind code of ref document: A

NENP Non-entry into the national phase

Ref country code: DE

ENP Entry into the national phase

Ref document number: 20147016784

Country of ref document: KR

Kind code of ref document: A

122 Ep: pct application non-entry in european phase

Ref document number: 12853966

Country of ref document: EP

Kind code of ref document: A1