WO2013009750A2

WO2013009750A2 - Novel separators for electrochemical systems

Info

Publication number: WO2013009750A2
Application number: PCT/US2012/046067
Authority: WO
Inventors: Farshid Roumi
Original assignee: California Institute Of Technology
Priority date: 2011-07-11
Filing date: 2012-07-10
Publication date: 2013-01-17
Also published as: JP2014528139A; US10158110B2; EP2732487A2; EP2732487A4; KR101950975B1; CN103650204A; JP2018067543A; JP6270718B2; US20130017432A1; KR20140048197A; WO2013009750A3; CN103650204B; JP6592055B2

Abstract

In an aspect, the invention provides separator systems for electrochemical systems providing electronic, mechanical and chemical properties useful for a range of electrochemical storage and conversion applications. Separator systems of some embodiments, for example, provide structural, physical and electrostatic attributes useful for managing and controlling dendrite formation in lithium and zinc based batteries. In an embodiment, for example, separator systems of the invention have a multilayer, porous geometry supporting excellent ion transport properties while at the same time providing a barrier effective to prevent dendrite initiated mechanical failure, shorting and/or thermal runaway.

Description

NOVEL SEPARATORS FOR ELECTROCHEMICAL SYSTEMS

CROSS REFERENCE TO RELATED APPLICATION

[0001] This application claims the benefit of and priority to United States Provisional Application No. 61/506,489 filed on July 1 1 , 201 1 and United States Provisional

Application No. 61/622,371 filed on April 10, 2012, each of which is hereby incorporated by reference in its entirety.

BACKGROUND

[0002] Over the last few decades revolutionary advances have been made in electrochemical storage and conversion devices expanding the capabilities of these systems in a variety of fields including portable electronic devices, air and space craft technologies, passenger vehicles and biomedical instrumentation. Current state of the art electrochemical storage and conversion devices have designs and performance attributes that are specifically engineered to provide compatibility with a diverse range of application requirements and operating environments. For example, advanced electrochemical storage systems have been developed spanning the range from high energy density batteries exhibiting very low self-discharge rates and high discharge reliability for implanted medical devices to inexpensive, light weight rechargeable batteries providing long runtimes for a wide range of portable electronic devices to high capacity batteries for military and aerospace applications capable of providing extremely high discharge rates over short time periods.

[0003] Despite the development and widespread adoption of this diverse suite of advanced electrochemical storage and conversion systems, significant pressure continues to stimulate research to expand the functionality of these systems, thereby enabling an even wider range of device applications. Large growth in the demand for high power portable electronic products, for example, has created enormous interest in developing safe, light weight primary and secondary batteries providing higher energy densities. In addition, the demand for miniaturization in the field of consumer electronics and instrumentation continues to stimulate research into novel design and material strategies for reducing the sizes, masses and form factors of high performance batteries. Further, continued development in the fields of electric vehicles and aerospace engineering has also created a need for mechanically robust, high reliability, high energy density and high power density batteries capable of good device performance in a useful range of operating environments.

[0004] Many recent advances in electrochemical storage and conversion technology are directly attributable to discovery and integration of new materials for battery components. Lithium battery technology, for example, continues to rapidly develop, at least in part, due to the discovery of novel electrode and electrolyte materials for these systems. The element lithium has a unique combination of properties that make it attractive for use in an electrochemical cell. First, it is the lightest metal in the periodic table having an atomic mass of 6.94 AMU. Second, lithium has a very low

electrochemical oxidation/reduction potential (i.e., - 3.045 V vs. NHE (normal hydrogen reference electrode)). This unique combination of properties enables lithium based electrochemical cells to have very high specific capacities. State of the art lithium ion secondary batteries provide excellent charge-discharge characteristics, and thus, have also been widely adopted as power sources in portable electronic devices, such as cellular telephones and portable computers. U.S. Patent Nos. 6,852,446, 6,306,540, 6,489,055, and "Lithium Batteries Science and Technology" edited by Gholam-Abbas Nazri and Gianfranceo Pistoia, Kluer Academic Publishers, 2004, which are hereby incorporated by reference in their entireties, are directed to lithium and lithium ion battery systems.

[0005] Advances in electrode materials, electrolyte compositions and device

geometries continue to support the further development of Li based electrochemical systems. For example, U.S. Patent Application Publication US2012/0077095, published on March 29, 2012, and International Patent Application publication WO 2012/034042, published on March 15, 2012, disclose three-dimensional electrode array structures for electrochemical systems including lithium batteries.

[0006] Despite substantial advances, practical challenges remain in connection with the continued development of Li based electrochemical systems. A significant issue, for example, relates to dendrite formation in primary and secondary lithium and lithium ion batteries. It is generally known that Li deposition in many electrolytes is highly dendridic which make these systems susceptible to problems involving shorting, mechanical failure and thermal runaway. Safety concerns relating to dendrite formation are currently a barrier to implementation of metal Li anodes in rechargeable systems. A number of strategies have been pursued to address safety in connection with dendrite formation, particularly in the context of secondary batteries, including development of non-lithium anodes and internal safety systems able to monitor in real time problems associated with dendrite formation.

[0007] As will be generally recognized from the foregoing, a need currently exists for lithium based electrochemical systems exhibiting electrochemical properties useful for a range of applications. Specifically, lithium electrochemical systems capable of good electrochemical performance and high versatility for both primary and secondary lithium based batteries are needed.

SUMMARY

[0008] In an aspect, the invention provides separator systems for electrochemical systems providing electronic, mechanical and chemical properties useful for a range of electrochemical storage and conversion applications. Separator systems of some embodiments, for example, provide structural, physical and electrostatic attributes useful for preventing catastrophic failure in electrochemical cells and useful for increasing the performance such as cycle life and energy and power. One series of examples are separators for managing and controlling dendrite formation in metal based batteries, such as lithium based, alkaline based, zinc based and lead based batteries. In an embodiment, for example, separator systems of the invention have a multilayer, porous geometry supporting excellent ion transport properties while at the same time providing a barrier effective to prevent dendrite initiated mechanical failure, electronic internal shorting and/or thermal runaway. Another series of examples are multilayer separators consisting of several porous/perforated layers and an impervious yet ion-selective conductive membrane in which the porous layers provide a barrier effective to prevent internal shorting failure, such as dendrite shorting failure, and/or thermal runaway; and the membrane layer provide a barrier effective to separate the electrolyte next to the anode from that next to the cathode which can prevent the contamination of either of the electrodes and their surfaces and their electrolytes and thus increase the performance of the cell, such as energy, power and life cycle; this is especially useful in metal air and flow batteries and semi-solid batteries, some examples are lithium-air, lithium water and zinc-air cells.

[0009] In an embodiment, the invention provides a separator system for an

electrochemical system comprising: (i) a first high mechanical strength layer having a plurality of apertures extending entirely through the first high mechanical strength layer and provided in a first pattern; and (ii) a second high mechanical strength layer having a plurality of apertures extending entirely through the second high mechanical strength layer and provided in a second pattern; the second pattern having an off-set alignment relative to the first pattern such that an overlap of the apertures of the first high mechanical strength layer and the apertures of the second high mechanical strength layer along axes extending perpendicularly from the first high mechanical strength layer to the second high mechanical strength layer is less than or equal to 20%; wherein the first high mechanical strength layer and the second high mechanical strength layer are positioned such that ions of an electrolyte provided in contact with the first high mechanical strength layer and the second high mechanical strength layer are able to be transported through the first high mechanical strength layer and the second high mechanical strength layer. In an embodiment, for example, the first high mechanical strength layer and the second high mechanical strength layer are not in direct physical contact with each other. In an embodiment of this aspect, the overlap of the apertures of the first high mechanical strength layer and the apertures of the second high mechanical strength layer along axes extending perpendicularly from the first high mechanical strength layer to the second high mechanical strength layer is less than or equal to 10%. In an embodiment, for example, the separator system of the invention further comprises one or more electrolytes provided between, and optionally in contact, with the first high mechanical strength layer the second high mechanical strength layer or both, wherein the first and second high mechanical strength layers are ionically conductive and optionally allow transport of the electrolyte of an electrochemical system.

[0010] In an embodiment, the invention provides a separator system for an

electrochemical system comprising: (i) a first high mechanical strength layer having a plurality of apertures extending entirely through the first high mechanical strength layer and provided in a first pattern; (ii) a second high mechanical strength layer having a plurality of apertures extending entirely though the second high mechanical strength layer and provided in a second pattern, the second pattern having an off-set alignment relative to the first pattern such that an overlap of the apertures of the first high mechanical strength layer and the apertures of the second high mechanical strength layer along axes extending perpendicularly from the first high mechanical strength layer to the second high mechanical strength layer is less than or equal to 20%; and (iii) a third high mechanical strength layer having a plurality of apertures extending entirely through the third high mechanical strength layer and provided in a third pattern having the same spatial arrangement of apertures as the first pattern; wherein the first high mechanical strength layer, the second high mechanical strength layer and the third high mechanical strength layer are positioned such that ions of an electrolyte provided in contact with the first high mechanical strength layer, the second high mechanical strength layer and the third high mechanical strength layer are able to be transported through the first high mechanical strength layer, the second high mechanical strength layer and the third high mechanical strength layer. In an embodiment of this aspect, the overlap of the apertures of the first high mechanical strength layer and the apertures of the second high mechanical strength layer along axes extending perpendicularly from the first high mechanical strength layer to the second high mechanical strength layer is less than or equal to 10%. As used throughout this description, the "same spatial arrangement of apertures" refers to the positions of apertures of two or more high mechanical strength layers such that they are aligned along axes extending

perpendicularly between the high mechanical strength layers. In an embodiment, for example, the same spatial arrangement of apertures" refers to the positions of apertures of two or more high mechanical strength layers such that they overlap by a factor of 90% or more along axes extending perpendicularly between the high mechanical strength layers.

[0011] In an embodiment, the invention provides a separator system for an

electrochemical system comprising: (i) a first high mechanical strength layer having a plurality of apertures extending entirely through the first high mechanical strength layer and provided in a first pattern; (ii) a second high mechanical strength layer having a plurality of apertures extending entirely through the second high mechanical strength layer and provided in a second pattern, the second pattern having an off-set alignment relative to the first pattern such that an overlap of the apertures of the first high mechanical strength layer and the apertures of the second high mechanical strength layer along axes extending perpendicularly from the first high mechanical strength layer to the second high mechanical strength layer is less than or equal to 20%; (iii) a third high mechanical strength layer having a plurality of apertures extending entirely through the third high mechanical strength layer and provided in a third pattern having the same spatial arrangement of apertures as that of the first pattern; and (iv) a fourth high mechanical strength layer having a plurality of apertures extending entirely through the fourth high mechanical strength layer and provided in a fourth pattern having the same spatial arrangement of apertures as that of the second pattern; wherein the first high mechanical strength layer, the second high mechanical strength layer, the third high mechanical strength layer and the fourth high mechanical strength layer are positioned such that ions of an electrolyte provided in contact with the first high mechanical strength layer, the second high mechanical strength layer, the third high mechanical strength layer and the fourth high mechanical strength layer are able to be transported through the first high mechanical strength layer, the second high mechanical strength layer, the third high mechanical strength layer and the fourth high mechanical strength layer. In an embodiment of this aspect, the overlap of the apertures of the first high mechanical strength layer and the apertures of the second high mechanical strength layer along axes extending perpendicularly from the first high mechanical strength layer to the second high mechanical strength layer is less than or equal to 10%.

[0012] In an embodiment, the invention provides a separator system for an

electrochemical system comprising: (i) a first high mechanical strength layer having a plurality of apertures extending entirely through the first high mechanical strength layer and provided in a first pattern; (ii) a second high mechanical strength layer having a plurality of apertures extending entirely through the second high mechanical strength layer and provided in a second pattern, the second pattern having an off-set alignment relative to the first pattern such that an overlap of the apertures of the first high mechanical strength layer and the apertures of the second high mechanical strength layer along axes extending perpendicularly from the first high mechanical strength layer to the second high mechanical strength layer is less than or equal to 40%; and (iii) a third high mechanical strength layer having a plurality of apertures extending entirely through the third high mechanical strength layer and provided in a third pattern; the third pattern having an off-set alignment relative to the first pattern and the second pattern such that an overlap of the apertures of the first high mechanical strength layer, the apertures of the second high mechanical strength layer and the apertures of the third high mechanical strength layer along axes extending perpendicularly from the first layer or the second layer to the third layer is less than or equal to 20%; wherein the first high mechanical strength layer, the second high mechanical strength layer and the third high mechanical strength layer are positioned such that ions of an electrolyte provided in contact with the first high mechanical strength layer, the second high mechanical strength layer and the third high mechanical strength layer are able to be transported through the first high mechanical strength layer, the second high mechanical strength layer and the third high mechanical strength layer. In an embodiment of this aspect, the overlap of the apertures of the first high mechanical strength layer and the apertures of the second high mechanical strength layer along axes extending perpendicularly from the first high mechanical strength layer to the second high mechanical strength layer is less than or equal to 20% and the overlap of the apertures of the first high mechanical strength layer, the apertures of the second high mechanical strength layer and the apertures of the third high mechanical strength layer along axes extending

perpendicularly from the first high mechanical strength layer or the second high mechanical strength layer to the third high mechanical strength layer is less than or equal to 10%.

[0013] In an embodiment, the invention provides a separator system for an

electrochemical system comprising: (i) a first high mechanical strength layer having a plurality of apertures extending entirely through the first high mechanical strength layer and provided in a first pattern; (ii) a second high mechanical strength layer having a plurality of apertures extending entirely through the second high mechanical strength layer and provided in a second pattern, the second pattern having an off-set alignment relative to the first pattern such that an overlap of the apertures of the first high mechanical strength layer and the apertures of the second high mechanical strength layer along axes extending perpendicularly from the first high mechanical strength layer to the second high mechanical strength layer is less than or equal to 50%; (iii) a third high mechanical strength layer having a plurality of apertures extending entirely through the third high mechanical strength layer and provided in a third pattern; the third pattern having an off-set alignment relative to the first pattern and the second pattern such that an overlap of the apertures of the first high mechanical strength layer, the apertures of the second high mechanical strength layer and the apertures of the third high

mechanical strength layer along axes extending perpendicularly from the first high mechanical strength layer or the second high mechanical strength layer to the third high mechanical strength layer is less than or equal to 30%; and (iv) a fourth high mechanical strength layer having a plurality of apertures extending entirely through the fourth high mechanical strength layer and provided in a fourth pattern; the fourth pattern having an off-set alignment relative to the first pattern, the second pattern and the third pattern such that an overlap of the apertures of the first high mechanical strength layer, the apertures of the second high mechanical strength layer, the apertures of the third high mechanical strength layer and the apertures of the fourth high mechanical strength layer along axes extending perpendicularly from the first high mechanical strength layer or the second high mechanical strength layer to the fourth high mechanical strength layer is less than or equal to 20%; wherein the first high mechanical strength layer, the second high mechanical strength layer, the third high mechanical strength layer and the fourth high mechanical strength layer are positioned such that ions of an electrolyte provided in contact with the first high mechanical strength layer, the second high mechanical strength layer, the third high mechanical strength layer and the fourth high mechanical strength layer are able to be transported through the first high mechanical strength layer, the second high mechanical strength layer, the third high mechanical strength layer and the fourth high mechanical strength layer. In an embodiment of this aspect, the overlap of the apertures of the first high mechanical strength layer and the apertures of the second high mechanical strength layer along axes extending perpendicularly from the first high mechanical strength layer to the second high mechanical strength layer is less than or equal to 30%, and the off-set alignment relative to the first pattern and the second pattern such that an overlap of the apertures of the first high mechanical strength layer, the apertures of the second high mechanical strength layer and the apertures of the third high mechanical strength layer along axes extending

perpendicularly from the first layer or the second layer to the third layer is less than or equal to 20%, and off-set alignment relative to the first pattern, the second pattern and the third pattern such that an overlap of the apertures of the first high mechanical strength layer, the apertures of the second high mechanical strength layer, the apertures of the third high mechanical strength layer and the apertures of the fourth high

mechanical strength layer along axes extending perpendicularly from the first high mechanical strength layer or the second high mechanical strength layer to the third layer is less than or equal to 10%.

[0014] In some embodiments, for example, the second high mechanical strength layer is provided between the first high mechanical strength layer and the third high

mechanical strength layer. In some embodiments, for example, the first high

mechanical strength layer is provided between the second high mechanical strength layer and the fourth high mechanical strength layer or wherein the third high mechanical strength layer is provided between the second high mechanical strength layer and the fourth high mechanical strength layer. In an embodiment, first and second mechanical strength layers are not provided in physical contact, or first, second and third

mechanical strength layers are not provided in physical contact, or first, second, third and fourth mechanical strength layers are not provided in physical contact. [0015] Some separators of this aspect, for example, provide a multilayer structure for managing dendrite formation in an electrochemical system, wherein multiple separator layers (e.g., first, second, third, fourth, etc. high mechanical strength layers) have complementary patterns of apertures, such as micro- or nano-channels, that establish ion conductivity between positive and negative electrodes in a manner that dendrite growth between positive and negative electrodes is kinetically and/or thermodynamically unfavorable. Some separators of this aspect, for example, provide a barrier having a multilayer geometry and physical properties preventing a direct, linear pathway for dendrite growth between positive and negative electrodes, for example, by providing a multilayer structure wherein the only pathway(s) for ion transport between positive a negative electrodes requires curved trajectories that are kinetically and/or

thermodynamically unfavorable to dendrite growth. In an embodiment, the first high mechanical strength layer, the second high mechanical strength layer, the third high mechanical strength layer and/or the fourth high mechanical strength layer are planar and provided in a substantially parallel orientation with respect to each other, for example, wherein planar surfaces of the first, second, third and/or fourth high

mechanical strength layers are provided in parallel planes. In an embodiment, the first high mechanical strength layer, the second high mechanical strength layer, the third high mechanical strength layer and/or the fourth high mechanical strength layer are hollow cylindrical structures and provided in a substantially concentric orientation, for example, wherein curved surfaces of cylindrical first and second layers are provided in a concentric orientation. As used herein, axes extending perpendicularly from a

concentric orientation are perpendicular to a central axis and extend radially from the central axis.

[0016] The multilayer geometry of some separator systems of the invention provides an off-set alignment providing a selected overlap of apertures of the first pattern and the apertures of the second pattern along axes extending perpendicularly from the first layer to the second layer. This aspect of the invention is useful for accessing useful ion transport properties while at the same time preventing dendrite formation between positive and negative electrodes of an electrochemical cell. In some embodiments, the term "off-set" refers to a configuration wherein the apertures of one high mechanical strength layer of the separator are off-set relative to the positions of apertures of another high mechanical strength layer along axes extending from the one layer to the another layer, such as axes extending perpendicularly from a first high mechanical strength layer to a second high mechanical strength layer. In some embodiments, the term "off-set" refers to a relative configuration of patterns of apertures in high mechanical strength layers, such as wherein the apertures of a first pattern of the first high mechanical strength layer are off-set relative to the positions of apertures of the second pattern of the second high mechanical strength layer such that the apertures of the first high mechanical strength layer are not entirely superimposable onto the apertures of the second high mechanical strength layer along the axes extending perpendicularly from the first high mechanical strength layer to the second high mechanical strength layer. In an embodiment, for example, the first and second high mechanical strength layers are nano- and/or micro-porous and aligned such that the apertures of the first high mechanical strength layer are not superimposable at all onto the apertures of the second high mechanical strength layer along the axes extending perpendicularly from the first high mechanical strength layer to the second high mechanical strength layer. In an embodiment, for example, the overlap of the apertures of two or more of the first pattern, the second pattern, the third pattern and the fourth pattern along the axes extending perpendicularly from the first high mechanical strength layer to the second high mechanical strength layer is less than or equal to 10%, and optionally for some applications less than or equal to 1 %. In an embodiment, for example, the overlap of the apertures of two or more of the first pattern, the second pattern, the third pattern and the fourth pattern along the axes extending perpendicularly from the first high

mechanical strength layer to the second high mechanical strength layer is selected from the range of 0 to 5%, and optionally for some applications selected from the range of 0 to 1 %. In an embodiment, for example, the overlap of the apertures of two or more of the first pattern, the second pattern, the third pattern and the fourth pattern along the axes extending perpendicularly from the first high mechanical strength layer to the second high mechanical strength layer is equal to 0, for example equal to 0 by a good precision. In an embodiment, for example, the overlap of the apertures of the first pattern, the second pattern, and the third pattern along the axes extending

perpendicularly from the first high mechanical strength layer to the second high mechanical strength layer is less than or equal to 10%. In an embodiment, for example, the overlap of the apertures of the first pattern, the second pattern, and the third pattern along the axes extending perpendicularly from the first high mechanical strength layer to the second high mechanical strength layer is selected from the range of 0 to 5%. In an embodiment, for example, the overlap of the apertures of the first pattern, the second pattern, the third pattern and the fourth pattern along the axes extending perpendicularly from the first high mechanical strength layer to the second high mechanical strength layer is less than or equal to 10%. In an embodiment, for example, the overlap of the apertures of the first pattern, the second pattern, the third pattern and the fourth pattern along the axes extending perpendicularly from the first high mechanical strength layer to the second high mechanical strength layer is selected from the range of 0 to 5%.

[0017] In an embodiment, for example, two or more of the first pattern, the second pattern, the third pattern and the fourth pattern comprise substantially complementary patterns. In an embodiment, for example, the substantially complementary patterns correspond to substantially negative images of one another. As used herein, a complementary pattern refers to a configuration wherein the relative positions of apertures of one pattern of a high mechanical strength layer and the apertures of one or more other pattern or one or more other high mechanical strength layers are selected to prevent dendrite growth between positive and negative electrodes of an electrochemical cell. In an embodiment, for example, the substantially complementary patterns of the first and second patterns are negative images of one another, for example, wherein the positions of apertures of the first pattern correspond to regions of the second layer not having an aperture. As an example of a complementary pattern of the invention, the first layer may be characterized by a pattern of apertures corresponding to the black squares of a chess board and the second layer may be characterized by a pattern of apertures corresponding to the red squares of the chess board. As an example of a complementary pattern of the invention, the first high mechanical strength layer may have a first periodic pattern of apertures characterized by a first pitch and aperture spacing, wherein the second high mechanical strength layer has a second periodic pattern of apertures characterized by a the same pitch and aperture spacing but offset or translated from the positions of the apertures of the first pattern such that the apertures of the first high mechanical strength layer are not superimposable on the apertures of the second high mechanical strength layer along axes extend

perpendicularly from first and second high mechanical strength layers.

[0018] In an embodiment, a separator system having three or more high mechanical strength layers may include some high mechanical strength layers having identical patterns (i.e. non-complementary patterns), so long as at least one layer having a complementary pattern is positioned between the high mechanical strength layers having identical patterns. For example, a separator system may be characterized by one or more high mechanical strength layers having a pattern A and one or more high mechanical strength layers having a pattern B, where A and B are complementary patterns, arranged according to a repeating sequence of ABA, with longer sequences possible for multilayer systems containing four or more high mechanical strength layers, e.g., ABABAB.

[0019] In another embodiment, a separator system having three or more high mechanical strength layers may include only high mechanical strength layers having complementary patterns. For example, a separator system may be characterized by one or more high mechanical strength layers having a pattern A, one or more high mechanical strength layers having a pattern B, and one or more high mechanical strength layers having a pattern C, where A, B and C are each complementary to the other two patterns, arranged according to a repeating sequence of ABC, with longer sequences (e.g. ABCABC) and varied sequences (e.g. ABCBA, ABCA) possible for multilayer systems containing four or more high mechanical strength layers.

[0020] In another aspect, the invention provides separator systems further comprising one or more low ionic resistance layers provided on a side of at least one of the first high mechanical strength layer, the second high mechanical strength layer, the third high mechanical strength layer and the fourth high mechanical strength layer. In an embodiment, for example, each of the one or more low ionic resistance layers is an electrolyte containing layer providing a reservoir for the electrolyte, for example of an electrochemical cell. In an embodiment, for example, each of the one or more low ionic resistance layers independently has an ionic resistance less than or equal to 20 ohm- cm², and preferably for some embodiments less than or equal to 2 ohm-cm² , and preferably for some embodiments less than or equal to 1 ohm-cm² _. In an embodiment, for example, at least one of said one or more low ionic resistance layers is a pressure buffer providing space for an electrolyte provided between at least two of the first high mechanical strength layer, the second high mechanical strength layer, the third high mechanical strength layer and the fourth high mechanical strength layer.

[0021] In an embodiment, for example, at least one of the high mechanical strength layers and the one or more low ionic resistance layers is a deposited layer that is deposited on at least one of the high mechanical strength layers and the one or more low ionic resistance layers. In an embodiment, for example, at least one of the high mechanical strength layers and the one or more low ionic resistance layers is a deposited layer that is deposited on an electrode of an electrochemical cell, such as a layer deposited directly on the surface of a positive or negative electrode presented to an electrolyte of an electrochemical cell. In an embodiment, for example, at least one of the one or more low ionic resistance layers, and optionally all, is adhered by pressure, heat or chemical adhering to at least one side of any of the first high mechanical strength layer, the second high mechanical strength layer, the third high mechanical strength layer and the fourth high mechanical strength layer. In an embodiment, for example, at least one of the one or more low ionic resistance layers, and optionally all, is adhered by a resin polymer to at least one side of any of the first high mechanical strength layer, the second high mechanical strength layer, the third high mechanical strength layer and the fourth high mechanical strength layer. In an embodiment, for example, at least one of the one or more low ionic resistance layers, and optionally all, comprises a microporous material, a woven material, or a nonwoven material.

[0022] In an embodiment, for example, at least one of the one or more low ionic resistance layers, and optionally all, comprises a ceramic or a glass electrolyte, a polymer electrolyte or another solid electrolyte. In an embodiment, for example, the low ionic resistance layers comprise a glass electrolyte, such as LISICON or LIPON, or a polymer electrolyte such as PEO. In an embodiment, for example, at least one of the one or more low ionic resistance layers, and optionally all, comprises a perforated ceramic separator, a porous ceramic separator, a perforated glass separator, a porous glass separator or a perforated metal or perforated alloy separator or perforated rubber or a rubber mesh or a metal mesh or an alloy mesh.

[0023] In an embodiment, for example, at least one of the one or more low ionic resistance layers comprises a ring or a frame having a central aperture, such as a ring or frame structure providing a mechanically supporting structure, an electrolyte reservoir structure and/or a spacer structure in an electrochemical cell. In an embodiment, for example, the one or more low ionic resistance layers comprise one or more frame layers in contact with at least one of the first high mechanical strength layer, the second high mechanical strength layer, the third high mechanical strength layer and the fourth high mechanical strength layer. In an embodiment, for example, the first high mechanical strength layer is provided between first and second frame layers and wherein the second high mechanical strength layer is provided between third and fourth frame layers or the first high mechanical strength layer is provided between first and second frame layers and wherein the second high mechanical strength layer is provided between second and third frame layers. In an embodiment, for example, the one or more low ionic resistance layers comprise one or more frame layers in physical contact with at least one of the electrodes of an electrochemical system, such as the positive and/or negative electrodes of an electrochemical cell. In an embodiment, for example, the one or more low ionic resistance layers comprise a spacer provided between the first and second layers, the spacer separating the first and second layers by a selected distance selected from the range of 10 nm to 1000 μιτι, and optionally for some applications selected from the range of 1 μιτι to 1000 μιτι. In an embodiment, for example, the spacer of this aspect comprises: a ring for establishing the selected distance between the first high mechanical strength layer and the second high mechanical strength layer; a frame structure having a porous wall component, a material layer, or an arrangement of discrete material elements.

[0024] In an embodiment, for example, each of the low ionic resistance layers, and optionally all, is independently a polymer, a ceramic, a wood, glass, a mineral, a metal, an alloy, a woven material, a nonwoven material, cellulose, wood fiber, sponge or a combination thereof. In an embodiment, for example, the one or more low ionic resistance layers each independently have porosity greater than or equal to 50%, and preferably for some applications greater than 70%, and preferably for some applications greater than 90%. In an embodiment, for example, the one or more low ionic resistance layers each independently have a porosity selected from the range of 50% to 95%, preferably for some applications a porosity selected from the range of 70% to 95%.

[0025] In an embodiment, for example, at least one side of one of the high mechanical strength layers is wet-able, for example wet-able with electrolyte of an electrochemical cell. In an embodiment, for example, a separator configuration is characterized by the wet-able side of a high mechanical strength layer is placed next to another high mechanical strength layer with no low ionic resistance layer provided between them. In an embodiment, for example, a separator configuration is characterized by the wet-able side of the high mechanical strength layer is placed next to an electrode with no low ionic resistance layer between them. In an embodiment, for example, a separator includes one or more low ionic resistance layers or high mechanical strength layers coated on another low ionic resistance layer or a high mechanical strength layer or coated on an electrode in a chemical cell, such as on the positive electrode or negative electrode of an electrochemical system. [0026] In another aspect, the invention provides a separator further comprising one or more chemical barrier layers provided on a side of at least one of the first high mechanical strength layer, the second high mechanical strength layer, the third high mechanical strength layer, the fourth high mechanical strength layer or the one or more low ionic resistance layers. Separators having one or more chemical barriers are useful in electrochemical systems wherein positive and negative electrodes are provided in contact with different electrolytes and, thus, the chemical barrier(s) allow transport of charge carriers but prevents transport of electrolytes. In such configurations, the chemical barriers are useful for protecting the electrodes from degradation and/or enabling the use of different electrolytes for positive and negative electrodes of an electrochemical cell. In an embodiment, for example, the one or more chemical barrier layers independently prevents transportation of unwanted chemical components through the one or more chemical barrier layers to a positive electrode or a negative electrode of an electrochemical cell. In an embodiment, for example, the one or more chemical barrier layers prevents transport of an electrolyte solvent through the one or more chemical barrier layers to a positive electrode or a negative electrode of an

electrochemical cell. In an embodiment, for example, the one or more chemical barrier layers comprises a solid electrolyte or a solid polymer electrolyte disposed on at least one side of an electrode of an electrochemical cell. In an embodiment, for example, the one or more chemical barrier layers comprise a solid electrolyte from LISICON or NASICON or a polymer electrolyte comprising polyethylene oxide (PEO).

[0027] In an embodiment, for example, the separator system is a component of an electrochemical cell having a negative electrode and a positive electrode, wherein the one or more chemical barrier layer comprise an ion conductive protective membrane, wherein the protective membrane provides a barrier between a first electrolyte in contact with the positive electrode and a second electrode in contact with the negative electrode, wherein the ion conductive protective membrane prevents contact between the negative electrode and the first electrolyte. In an embodiment, for example, the negative electrode is a lithium metal electrode, wherein the ion conductive protective membrane conducts lithium ion charge carriers and prevents contact between the lithium metal electrode and the first electrolyte.

[0028] In an embodiment, for example, the ion conductive protective membrane comprising a material selected from the group consisting of glassy or amorphous active metal ion conductors, ceramic active metal ion conductors, and glass-ceramic active metal ion conductors. In an embodiment, for example, the one or more chemical barrier layers further comprises a solid polymer electrolyte disposed between a surface of the protective membrane and the positive electrode or negative electrode. In an

embodiment, for example, at least one of the high mechanical strength layers, one or more low ionic resistance layers and the one or more chemical barrier layers is a deposited layer that is deposited on at least one of the high mechanical strength layers, one or more low ionic resistance layers and the one or more chemical barrier layers. In an embodiment, for example, at least one of the high mechanical strength layers, one or more low ionic resistance layers and the one or more chemical barrier layers is a deposited layer that is deposited on an electrode of an electrochemical cell. In an embodiment, for example, a separator comprises a combination of at least two of the first high mechanical strength layer, the second high mechanical strength layer, the third high mechanical strength layer and the fourth high mechanical strength layer and the one or more chemical barrier layers without any of the low ionic resistance layers.

[0029] In an aspect, a separator further comprises a third high mechanical strength layer having a plurality of apertures extending entirely through the third high mechanical strength layer and provided in a third pattern; the third high mechanical strength layer positioned between the first high mechanical strength layer and the second high mechanical strength layer; the third pattern having an off-set alignment relative to the first pattern or the second pattern such that an overlap of the apertures of the first pattern or the second pattern and the apertures of the third pattern along axes extending perpendicularly from the first high mechanical strength layer or the second high mechanical strength layer to the third high mechanical strength layer is less than or equal to 20%. In an aspect, a separator further comprises a fourth high mechanical strength layer having a plurality of apertures extending entirely through the fourth high mechanical strength layer and provided in a fourth pattern; the fourth high mechanical strength layer positioned between the first high mechanical strength layer and the second high mechanical strength layer, the fourth pattern having an off-set alignment relative to the first pattern, the second pattern or the third pattern such that an overlap of the apertures of the first pattern, the second pattern or the third pattern and the apertures of the fourth pattern along axes extending perpendicularly from the first high mechanical strength layer or the second high mechanical strength layer to said fourth high mechanical strength layer is less than or equal to 20%. [0030] The layers of multilayer separator systems of the invention may be configured and attached via a variety of mechanisms and device arrangements to provide mechanical properties useful for specific applications. In an embodiment, for example, at least a portion, and optionally all, of the first high mechanical strength layer, the second high mechanical strength layer, the third high mechanical strength layer, the fourth high mechanical strength layer, low ionic resistance layers, frame layers, spacer, chemical barrier layers, or any combination of these are at least partially attached to each other via a pressure, heating, an adhesive coating, a chemical adherent, plasma treating or any combination of these. In an embodiment, for example, at least a portion, and optionally all, of the first high mechanical strength layer, the second high

mechanical strength layer, the third high mechanical strength layer, the fourth high mechanical strength layer, low ionic resistance layers, frame layers, spacer, chemical barrier layers, or any combination of these are at least partially attached to each other via glue, epoxy, cement, PTFE, a solid electrolyte, a gel electrolyte, a polymer electrolyte, a silicone adhesive, acrylic adhesive, cyanacrylate, stycast 1266, deltabond 151 , PVDF, PVA, LIPON, LISICON, PE-PP-PVDF, tetramethylammonium hydroxide pentahydrate (CH₃)₄NOH-5H₂O , poly(ethylene oxide) (PEO), copolymer of

epichlorohydrin and ethylene oxide P(ECH-co-EO) and poly(vinylalcohol), glassfibre polymer electrolyte, zinc sulfide, silicon dioxide, Kapton Tape, polyethylene oxide or polypropylene oxide, or a copolymer, PVDF-co-HFP Bi₂O₃, a non-fluorine-containing binder or an aromatic binder, lithium polyacrylate or a combination thereof.

[0031] In an embodiment, the invention provides a separator system further comprising one or more solid electrolyte layers that prevent water molecules, CO₂, O₂ or air from transporting through said separator system, for example, wherein said one or more solid electrolyte layers comprise LISICON or NASICON.

[0032] In an aspect, a separator of the invention further comprises one or more electrolytes, such as an electrolyte of an electrochemical cell, which is optionally in physical contact with at least a portion of the first high mechanical strength layer, the second high mechanical strength layer, the third high mechanical strength layer, the fourth high mechanical strength layer, low ionic resistance layers, frame layers, spacer, chemical barrier layers, or any combination of these. In an embodiment, for example, the separator system is a component of an electrochemical cell having a positive electrode and a negative electrode, the separator further comprising an electrolyte provided between the positive electrode and the negative electrode; wherein the electrolyte is in contact with any of the first high mechanical strength layer, the second high mechanical strength layer, the third high mechanical strength layer, and the fourth high mechanical strength layer. In an embodiment, for example, the separator system is a component of an electrochemical cell having a positive electrode and a negative electrode, the separator further comprising a first electrolyte and a second electrolyte provided between the positive electrode and the negative electrode; wherein the first electrolyte has a different composition than the second electrolyte; wherein the first electrolyte is in contact with any of the first high mechanical strength layer, the second high mechanical strength layer, the third high mechanical strength layer, and the fourth high mechanical strength layer, and wherein the second electrolyte is in contact with any of the first high mechanical strength layer, the second high mechanical strength layer, the third high mechanical strength layer, and the fourth high mechanical strength layer; where the first electrolyte and the second electrolyte do not mix with each other because of the presence of an impervious ion conducting layer between them or because of different chemistry and physics such as hydrophilic or hydrophobic behavior or density.

[0033] Selection of the physical, chemical and electronic properties of the components of the separator system, such as the first high mechanical strength layer, the second high mechanical strength layer, the third high mechanical strength layer, and the fourth high mechanical strength layer, are selected to provide net separator properties useful for applications in electrochemical cells, such as to provide the combination of high electrical resistance, high ion conductivity and useful mechanical attributes.

[0034] In an embodiment, for example, the first pattern of apertures provides a first porosity of the first high mechanical strength layer greater than or equal to 30% and preferably for some applications more than 40%, and/or wherein the second pattern of apertures provides a second porosity of the second high mechanical strength layer greater than or equal to 30%, and preferably for some applications more than 40%. In an embodiment, for example, the first pattern of apertures provides a first porosity of the first high mechanical strength layer greater than or equal to 30% and preferably for some applications more than 40%, or wherein the second pattern of apertures provides a second porosity of the second high mechanical strength layer greater than or equal to 30% and preferably for some applications more than 40%; or wherein the third pattern of apertures provides a third porosity of the third high mechanical strength layer greater than or equal to 30% and preferably for some applications more than 40%; or wherein the fourth pattern of apertures provides a fourth porosity of the fourth high mechanical strength layer greater than or equal to 30% and preferably for some applications more than 40%. In an embodiment, for example, the first pattern of apertures provides a porosity of the first high mechanical strength layer selected from the range of 30% to 70% and preferably for some applications 40% to 70%; and wherein the second pattern of apertures provides a porosity of the second high mechanical strength layer selected from the range of 30% to 70% and preferably for some applications 40% to 70%. In an embodiment, for example, the first pattern of apertures provides a porosity of the first high mechanical strength layer selected from the range of 30% to 70% and preferably for some applications 40% to 70%; or wherein the second pattern of apertures provides a porosity of the second high mechanical strength layer selected from the range of 30% to 70% and preferably for some applications 40% to 70%; or wherein the third pattern of apertures provides a porosity of the third high mechanical strength layer selected from the range of 30% to 70% and preferably for some applications 40% to 70%; or wherein the fourth pattern of apertures provides a porosity of the fourth high mechanical strength layer selected from the range of 30% to 70% and preferably for some applications 40% to 70%.

[0035] A range of geometries, shapes, orientations and patterns for apertures of the high mechanical strength layers are useful in the separator systems of the invention. In an embodiment, for example, the apertures of any of the first high mechanical strength layer, the second high mechanical strength layer, the third high mechanical strength layer or the fourth high mechanical strength layer independently have cross sectional shapes selected from the group consisting of a circle, parallelogram, rectangle, square, triangle, ellipse, tetragon, pentagon, hexagon and any combinations thereof. In an embodiment, for example, the apertures of the high mechanical strength layers have at least one lateral dimension (e.g., length, width, diameter, etc.) greater than or equal to 20 μητι, optionally for some embodiments greater than or equal to 50 μητι, optionally for some embodiments greater than or equal to 200 μηη; optionally for some embodiments greater than or equal to 500 μηη. In an embodiment, for example, the apertures of the high mechanical strength layers have at least one lateral dimension between 1 μηη and 1 mm, and optionally for some applications 200 μηη and 1 mm. In an embodiment, for example, the apertures of the high mechanical strength layers have at least one lateral dimension less than or equal to 200 μηη and optionally for some applications less than or equal to 10 μηη; and optionally for some applications less than or equal to 1 μηη. In an embodiment, for example, any of the first pattern, the second pattern, the third pattern or the fourth pattern is independently a symmetrical pattern of apertures or an asymmetrical pattern of apertures. In an embodiment, for example, any of the first pattern, the second pattern, the third pattern or the fourth pattern independently comprise a pattern of apertures that is not random.

[0036] In an embodiment, for example, any of the first pattern of apertures, second pattern of apertures, third pattern of apertures or the fourth pattern of apertures are independently made by a process selected from the group consisting of laser cutting, lithography, etching, casting, drilling, molding, punching, patterning, coating and any combinations of these.

[0037] In an embodiment, the first high mechanical strength layer; and/or second high mechanical strength layer; and/or third high mechanical strength layer; and/or fourth high mechanical strength layer are electrically non-conductive, for example, one or more of these layers comprising an electrically insulating material so as to prevent direct electrical contact between positive and negative electrodes of an electrochemical system such as an electrochemical cell. Electrically insulating high mechanical strength layers may comprise a range of electrical insulating materials such as Kapton, polyethylene, Polypropylene, fibrous cellulose, and/or metal layers coated with electrical insulators such as PE and PP coatings. In an embodiment, at least one of the first high mechanical strength layer; and/or second high mechanical strength layer; and/or third high mechanical strength layer; and/or fourth high mechanical strength layer are electrically conductive, for example, wherein one or more of these layers comprises an electrically insulating material and one or more of these layers comprises an electrically conductive material, the first high mechanical strength layer; and/or second high mechanical strength layer; and/or third high mechanical strength layer; and/or fourth high mechanical strength layer comprise a material characterized by a shape memory property, such as a shape memory polymer, or a materials characterized by the property of super elasticity.

[0038] In an embodiment, for example, the first high mechanical strength layer and the second high mechanical strength layer are not in complete physical contact with each other, such as provided in a configuration wherein there is at least some space between first high mechanical strength layer and the second high mechanical strength layer for electrolyte to have ionic transport, such as provided by first and second high mechanical strength layers having rough surfaces in contact with each other such that at some points they are physically attached but at some other points there is some space between them. In an embodiment, the first high mechanical strength layer and the second high mechanical strength layer are not in physical contact. In an embodiment, for example, the first high mechanical strength layer and the second high mechanical strength layer are separated by a distance selected from the range of 20 nm to 2 mm. . In an embodiment, for example, the first high mechanical strength layer or the second high mechanical strength layer is separated from the third high mechanical strength layer or the fourth high mechanical strength layer by a distance selected from the range of 20 nm to 2 mm.

[0039] In an embodiment, for example, any of, and optionally all of, the first high mechanical strength layer, the second high mechanical strength layer, the third high mechanical strength layer, the fourth high mechanical strength layer, the one or more low ionic resistance layers, and the one or more chemical barrier layers independently have an average thickness selected over the range of 10 nm to 1 mm, and optionally for some applications selected over the range of 1 μηη to 500 μητι, and optionally for some applications selected over the range of 10 nm to 50 μηη. In an embodiment, for example, any of, and optionally all of, the first high mechanical strength layer, the second high mechanical strength layer, the third high mechanical strength layer, the fourth high mechanical strength layer, the one or more low ionic resistance layers, and the one or more chemical barrier layers independently have an average thickness selected over the range 5 μηη to 1 mm, optionally for some applications selected over the range 25 μηη to 5 mm, and optionally for some applications selected over the range of Ι ΟΟμΐη to 2 mm, and optionally for some applications selected over the range of δθθμΐη to 1 mm. In an embodiment, for example, any of, and optionally all of, the first high mechanical strength layer, the second high mechanical strength layer, the third high mechanical strength layer, the fourth high mechanical strength layer, the one or more low ionic resistance layers, and the one or more chemical barrier layers

independently have an average thickness selected over the range 10 nm to 2 μηη or selected over the range 2 μηη to 50 μηη.

[0040] In an embodiment, for example, any of, and optionally all of, the first high mechanical strength layer, the second high mechanical strength layer, the third high mechanical strength layer and the fourth high mechanical strength layer independently have a Young's modulus selected over the range of 500 MPa to 500 GPa. In an embodiment, for example, any of, and optionally all of, the first high mechanical strength layer, the second high mechanical strength layer, the third high mechanical strength layer and the fourth high mechanical strength layer independently have a yield strength selected over the range of 5 MPa to 1000 MPa. In an embodiment, for example, any of, and optionally all of, the first high mechanical strength layer, the second high

mechanical strength layer, the third high mechanical strength layer and the fourth high mechanical strength layer independently have a propagating tear strength selected over the range of 0.005 N to 10 N, preferably for some applications a propagating tear strength more than 0.01 N. In an embodiment, for example, any of, and optionally all of, the first high mechanical strength layer, the second high mechanical strength layer, the third high mechanical strength layer and the fourth high mechanical strength layer independently have an initiating tear strength selected over the range of 10 N to 500 N, preferably for some applications an initiating tear strength more than 50N. In an embodiment, for example, any of, and optionally all of, the first high mechanical strength layer, the second high mechanical strength layer, the third high mechanical strength layer and the fourth high mechanical strength layer independently have a tensile strength selected over the range of 50 MPa to 2GPa. In an embodiment, for example, any of, and optionally all of, the first high mechanical strength layer, the second high mechanical strength layer, the third high mechanical strength layer and the fourth high mechanical strength layer independently have an impact strength selected over the range of 10 N cm to 1000 N cm.

[0041] In an embodiment, for example, any of, and optionally all of, the first high mechanical strength layer, the second high mechanical strength layer, the third high mechanical strength layer and the fourth high mechanical strength layer independently comprise planar layers provided in a parallel configuration. In an embodiment, for example, any of, and optionally all of, the first high mechanical strength layer, the second high mechanical strength layer, the third high mechanical strength layer and the fourth high mechanical strength layer independently comprise hollow cylindrical layers provided in a concentric configuration. In an embodiment, for example, any of, and optionally all of, the first high mechanical strength layer, the second high mechanical strength layer, the third high mechanical strength layer, the fourth high mechanical strength layer, the one or more low ionic resistance layers, and the one or more chemical barrier layers comprise chemically resistant materials. In an embodiment, the first high mechanical strength layer, the second high mechanical strength layer, the third high mechanical strength layer, the fourth high mechanical strength layer, the one or more low ionic resistance layers, and the one or more chemical barrier layers are independently chemically compatible with an electrolyte it is provided in contact with and/or independently chemically compatible with an electrode it is provided in contact with.

[0042] In an embodiment, for example, any of, and optionally all of, the first high mechanical strength layer, the second high mechanical strength layer, the third high mechanical strength layer and the fourth high mechanical strength layer independently comprise a material having a melting point greater than or equal to 100 Celsius. In an embodiment, for example, at least two of the high mechanical strength layers have different melting temperature with the difference of at least 30 Celsius, optionally wherein the difference in melting temperatures of the high mechanical strength layers provides a shutdown mechanism that by melting one of the layers the ionic path between two electrodes of an electrochemical cell closes; or alternatively wherein the difference in melting temperatures of the high mechanical strength layers result does not provide a shutdown mechanism that by melting one of the layers the ionic path between two electrodes of an electrochemical cell closes. In an embodiment, for example, any of, and optionally all of, the first high mechanical strength layer, the second high mechanical strength layer, the third high mechanical strength layer and the fourth high mechanical strength layer independently comprise a material having a thermal coefficient of thermal expansion is less than or equal to 50ppm/°C.

[0043] The first high mechanical strength layer, the second high mechanical strength layer, the third high mechanical strength layer and the fourth high mechanical strength layer of separator systems of the invention may comprise a range of materials selected for a particular application, such as type of electrochemical cell. In an embodiment, for example, first high mechanical strength layer, the second high mechanical strength layer, the third high mechanical strength layer and the fourth high mechanical strength layer independently comprise chemically resistant materials. In an embodiment, for example, first high mechanical strength layer, the second high mechanical strength layer, the third high mechanical strength layer and the fourth high mechanical strength layer independently comprise thermally stable materials. In an embodiment, for example, any of, and optionally all of, the first high mechanical strength layer, the second high mechanical strength layer, the third high mechanical strength layer and the fourth high mechanical strength layer independently comprise one or more materials selected from the group consisting of a polymer, a metal, an alloy, a ceramic, a wood, a glass, a semiconductor, a woven material, and a nonwoven material. In an

embodiment, for example, any of, and optionally all of, the first high mechanical strength layer, the second high mechanical strength layer, the third high mechanical strength layer and the fourth high mechanical strength layer independently comprise a material having a dielectric constant greater than or equal to 50. In an embodiment, for example, any of, and optionally all of, the first high mechanical strength layer, the second high mechanical strength layer, the third high mechanical strength layer and the fourth high mechanical strength layer independently comprise a conductive material. In an embodiment, for example, any of, and optionally all of, the first high mechanical strength layer, the second high mechanical strength layer, the third high mechanical strength layer and the fourth high mechanical strength layer independently comprise one or more materials selected from the group consisting of a gel electrolyte, a solid electrolyte and a polymer electrolyte. In an embodiment, for example, any of, and optionally all of, the first high mechanical strength layer, the second high mechanical strength layer, the third high mechanical strength layer and the fourth high mechanical strength layer

independently comprise one or more materials selected from the group consisting of Polyacrylic acid (PAA), Cross-linked polyethylene (PEX, XLPE) , Polyethylene (PE), Polyethylene terephthalate (PET, PETE), Polyphenyl ether (PPE), Polyvinyl chloride (PVC), Polyvinylidene chloride (PVDC), Polylactic acid (PLA), Polypropylene (PP), Polybutylene (PB), Polybutylene terephthalate (PBT), Polyamide (PA), Polyimide (PI), Polycarbonate (PC), Polytetrafluoroethylene (PTFE), Polystyrene (PS), Polyurethane (PU), Polyester (PE), Acrylonitrile butadiene styrene (ABS), Poly(methyl methacrylate) (PMMA), Polyoxymethylene (POM), Polysulfone (PES), Styrene-acrylonitrile (SAN), Ethylene vinyl acetate (EVA), Styrene maleic anhydride (SMA), PVDF, PEO PVDF, LIPON PVDF, LISICON PVDF, tetramethylammonium hydroxide pentahydrate

(CH₃)₄NOH-5H₂O, poly(ethylene oxide) (PEO), copolymer of epichlorohydrin and ethylene oxide P(ECH-co-EO) and poly(vinylalcohol), PEO- PVA- glassfibre polymer electrolyte, zinc sulfide, silicon dioxide, PVA and PSA, PVA/V6/PSS;

PVAN6/(PSS+PAA); V6/PVA/(PSS+PAA); PVMPSS+PAA(35%))/(PSS+PAA(35%)); (PSS+PAA(35%))/PVA/(PSS+PAA(35%)); or (PSS+PAA (35%))/(PVA(10%)+PSS (20% vs. PVA))/(PSS+PAA (35%)) polyethylene glycol, polypropylene glycol, polybutylene glycol, alkyl-polyethylene glycol, alkyl-polypropylene glycol, alkyl-polybutylene glycol, a copolymer thereof, a PEO material or a PVA material and any combination thereof. [0044] In an embodiment, for example, a surface of any of the first high mechanical strength layer, the second high mechanical strength layer, the third high mechanical strength layer and the fourth high mechanical strength layer is wet-able with an electrolyte. In an embodiment, for example, a surface of any of the first high mechanical strength layer, the second high mechanical strength layer, the third high mechanical strength layer and the fourth high mechanical strength layer is coated with a coating that is wet-able with an electrolyte. In an embodiment, for example, at least a portion of a surface of any of the first high mechanical strength layer, the second high mechanical strength layer, the third high mechanical strength layer and the fourth high mechanical strength layer is coated with an adhesive coating, optionally covering less than 10% of the surface. In an embodiment, for example, at least a portion of a surface of any of the first high mechanical strength layer, the second high mechanical strength layer, the third high mechanical strength layer and the fourth high mechanical strength layer is coated with an adhesive coating having a thickness less than 5 μηη . In an embodiment, for example, at least one surface of any of the first high mechanical strength layer, the second high mechanical strength layer, the third high mechanical strength layer and the fourth high mechanical strength layer has a surface roughness, such as a surface roughness characterized by a rms (root mean square) selected from the range of 1 nm to 1000 nm, providing a space for an electrolyte between at least a portion of the first high mechanical strength layer, the second high mechanical strength layer, the third high mechanical strength layer or the fourth high mechanical strength layer. In an embodiment, for example, the separator system is a component in an electrochemical cell having a positive electrode and a negative electrode; wherein at least one surface of any of the first high mechanical strength layer, the second high mechanical strength layer, the third high mechanical strength layer and the fourth high mechanical strength layer has a surface roughness such as a surface roughness characterized by a rms selected from the range of 1 nm to 1000 nm, providing a space for an electrolyte between the first high mechanical strength layer, the second high mechanical strength layer, the third high mechanical strength layer or the fourth high mechanical strength layer and the positive electrode or the negative electrode of the electrochemical cell. In an embodiment, for example, the surface roughness provides a distance between at least a portion of two of the high mechanical strength layers or between at least a portion of a high mechanical strength layer and the positive electrode or negative electrode selected from the range of 5 nm and 5micrometers. [0045] In an aspect, the invention provides a separator system wherein at least some of the first high mechanical strength layer, the second high mechanical strength layer, the third high mechanical strength layer, the fourth high mechanical strength layer, low ionic resistance layers, frame layers, spacer, chemical barrier layers, or any combination of these have a high surface energy, preferably for some applications a surface energy greater than or equal to 10mJ/m². In an embodiment, for example, the surface energy of any of these components facilitates the wettability of the layers with the electrolyte. In an embodiment, for example, the surface energy of any of these components helps with the attachment of the layers to each other or to the electrodes of an electrochemical cell.

[0046] In an aspect, the separator further comprises one or more coatings provided on any of the first high mechanical strength layer, the second high mechanical strength layer, the third high mechanical strength layer and the fourth high mechanical strength layer. In an embodiment, for example, the one or more coatings independently comprises one or more non-conductive coatings. In an embodiment, for example, the one or more coatings independently comprises one or more hydrophobic coatings and/or hydrophilic coatings. In an embodiment, for example, the one or more coatings independently comprises polyethylene glycol. In an embodiment, for example, the one or more coatings prevent material transport from a positive electrode to a negative electrode of an electrochemical cell. In an embodiment, for example, the one or more coatings independently have a thickness selected from the range of 10 nm to 2 μηη . In an embodiment, for example, the separator is for an electrochemical cell having a sulfur- based cathode, wherein the one or more coating repels hydrophobic polysulfides and increases the performance and cycle life of the electrochemical cell. In an embodiment, the hydroponic or hydrophobic coating is provided for a sulfur based cathode Li- battery. A problem with state of the art for a sulfur based cathode Li- batteries is that the electrochemical reactions are solvable in the electrolyte and, thus there may be a significant capacity loss due to the passage of the materials (inter-medially poly sulfides) from the sulfur electrode to the Li electrode through the electrolyte. To prevent this problem, a separator of a specific embodiment is coated with polyethylene glycol material (hydrophilic) which repels the hydrophobic poly sulfides and, thus hinders the materials passage and capacity loss. Use of a coating in embodiments of the invention is also useful in protecting a Li anode from moisture, say a by a hydrophobic coating on the separator, for example in a lithium-air and lithium water electrochemical cell. [0047] In an embodiment, for example, any of the first high mechanical strength layer, the second high mechanical strength layer, the third high mechanical strength layer and the fourth high mechanical strength layer is independently a metal layer, optionally selected from the group consisting of Al, Ni, Cu and stainless steel. In an embodiment, for example, the coating is a non-conductive coating, optionally comprising PTFE, PE, PP, PVC, or a polyimide.

[0048] The invention includes separator systems useful for with a range of

electrochemical systems. In an embodiment, for example, the invention provides a separator system for a primary electrochemical cell or secondary electrochemical cell. In an embodiment, for example, the invention provides a separator system for a lithium battery, an alkaline battery, zinc battery or a lead acid battery. In an embodiment, for example, the invention provides a separator system for a lithium metal-air battery, a lithium ion battery, a lithium air battery, a Fe-air battery, a Al-air battery, or a zinc-air battery. In an embodiment, for example, the invention provides a separator system for a fuel cell, a flow battery system, a semisolid battery, a 3-D battery, a nano-battery, a micro-battery or an electrochemical capacitor.

[0049] In another aspect, the invention provides an electrochemical cell comprising: (i) a negative electrode; (ii) a positive electrode; (iii) a first electrolyte provided between the positive electrode and the negative electrode; and (iv) a separator system of the invention provided in contact with the electrolyte and between the negative electrode and the positive electrode; wherein the separator system is positioned such that ions of the electrolyte are able to be transported between the positive electrode and the negative electrode. In an aspect, the separator system prevents electrical contact between the positive electrode and the negative electrode. As will be understood by one of skill in the art, any of the separator systems described herein can be used for electrochemical systems of the invention, such as electrochemical cells.

[0050] In an embodiment, for example, the separator system is provided in physical contact with the positive electrode and the negative electrode. In an embodiment, for example, the separator system provides an ionic conductivity between the positive electrode and the negative electrode equal to or greater than 1 x10^"3 S/cm, optionally for some applications preferably greater than 1 x10^"2 S/cm. In an embodiment, for example, the separator system provides a net ionic resistance from the positive electrode to the negative electrode selected over the range of 0.5 ohm cm² to 25 ohm cm², and preferably for some applications less than 5 ohm cm².

[0051] In an embodiment, the electrochemical cell further comprises a chemical barrier layer provided between the positive electrode and the negative electrode; the electrochemical cell further comprising a second electrolyte provided between the positive electrode and the negative electrode, wherein the chemical barrier layer prevents mixing of the first electrolyte and the second electrolyte.

[0052] In an embodiment, for example, the off-set alignment of the high mechanical strength layers provides no direct, linear path between the positive and negative electrodes. In an embodiment, for example, the off-set alignment prevents shorting via electrical contact between the positive electrode and the negative electrode by manufacturing defects, external objects or the formation of dendrites on the positive electrode or negative electrode. Embodiments of this aspect are beneficial, for example, for minimizing or preventing electrical shorting from the positive electrode to the negative electrode or thermal runaway issues arising from the formation of dendrites. Embodiments of this aspect are beneficial, for example, for providing electrochemical cells capable of enhanced cycling and/or high discharge rate

performance.

[0053] In an embodiment, for example, at least one of the first high mechanical strength layer, the second high mechanical strength layer, the third high mechanical strength layer, the fourth high mechanical strength layer, the low ionic resistance layers, the frame layers, the spacer, the chemical barrier layers, or any combination of these are at least partially attached the positive electrode or the negative electrode by via pressure, heating, an adhesive coating, a chemical adherent, plasma treating or by depositing or coating one layer on another layer or on an electrode or any combination of these. In an embodiment, for example, at least one of the first high mechanical strength layer, the second high mechanical strength layer, the third high mechanical strength layer, the fourth high mechanical strength layer, the low ionic resistance layers, the frame layers, the spacer, the chemical barrier layers, or any combination of these are at least partially attached to the positive electrode or the negative electrode by via a glue, epoxy, cement, a Telfon coating, a solid electrolyte, a gel electrolyte or a polymer electrolyte. In an embodiment, for example, at least one of the first high mechanical strength layer, the second high mechanical strength layer, the third high mechanical strength layer, the fourth high mechanical strength layer, low ionic resistance layers, frame layers, spacer, chemical barrier layers, or any combination of these comprise a coating deposited on a surface of the positive electrode or the negative electrode.

[0054] In an embodiment, for example, the invention provides an electrochemical cell incorporating the present separator system having a cycle capacity at least 300 cycles, and preferably for some applications at least 500 cycles. In an embodiment, for example, the invention provides an electrochemical cell incorporating the present separator system having a specific capacity equal to or greater than 100 mAh g^"1 at a discharge rate equal to or greater than C/5. In an embodiment, for example, the invention provides an electrochemical cell having

[0055] Electrochemical cells and separator systems of the invention are compatible with a range of electrolytes, including liquid electrolytes, solid, electrolytes, gel electrolytes, aprotic electrolytes, aqueous electrolytes and nonaqueous electrolytes. In an embodiment, for example, the electrolyte comprises a solid charge carrying media or a gel electrode. In an embodiment, for example, the electrolyte comprises a polymeric media. In an embodiment, for example, the electrolyte comprises polyethylene oxide, polytetrafluoroethylene, polyvinylidene fluoride, fluorine-containing copolymers, polyacrylonitrile, and any combinations thereof.

[0056] In an embodiment, for example, the electrolyte comprises an alkali metal salt at least partially dissolved in one or more nonaqueous solvents. In an embodiment, for example, the electrolyte comprises a solvent and a supporting salt; wherein the solvent is selected from the group consisting of organic carbonates, ethers, esters, formates, lactones, sulfones, sulfolane, 1 ,3-dioxolane, ethylene carbonate, propylene carbonate, dimethyl carbonate, diethyl carbonate, ethyl methyl carbonate, butylene carbonate, vinylene carbonate, fluoroethylene carbonate, fluoropropylene carbonate, y- butylrolactone, methyl difluoroacetate, ethyl difluoroacetate, dimethoxyethane, diglyme (bis(2-methoxyethyl)ether), tetrahydrofuran, dioxolane, 2MeTHF, 1 ,2-DME or higher glymes, sufolane, methyl formate, methyl acetate, and any combinations thereof; and wherein the supporting salt is selected from the group consisting of LiPF₆, LiBF , LiAsF₆, LiCIO₄, L1SO3CF3, LiN(CF₃SO₂)2, LiN(SO₂C₂F₅)2 an any combinations thereof. In an embodiment, for example, the electrolyte comprises a golfing agent selected from the group consisting of PVdF, PVdF— HFP copolymer, PAN, and PEO and mixtures thereof; a plasticizer selected from the group consisting of EC, PC, DEC, DMC, EMC, THE, 2MeTHF, 1 ,2-DME and mixtures thereof; and a Li salt selected from the group consisting of LiPF6, LiBF₄, LiAsF₆, LiCIO₄, LiSO₃CF₃, LiN(CF₃SO₂)₂ and LiN(SO₂C₂F5)₂.

[0057] In an aspect, the invention provides an electrochemical cell having a first electrolyte on a first side of the cell including the positive electrode and a second electrolyte on a second side of the cell including the negative electrode, wherein the first electrolyte has a different composition than the second electrolyte, and wherein the electrochemical cell further comprises one or more chemical barrier layers comprising an ion conductive protective membrane positioned between the positive electrode and the negative electrode. In an embodiment of this aspect, the first electrolyte is an aqueous electrolyte and the second electrolyte is an aprotic electrolyte. In an

embodiment of this aspect, at least one of the first electrolyte and the second electrolyte is a solid electrolyte.

[0058] Electrochemical cells and separator systems of the invention are compatible with electrodes having a range of compositions, form factors and device geometries. In an embodiment, for example, the negative electrode, the positive electrode or both comprise a micro-sized material of a nano-sized material. As used herein, nano-sized refers to a structure, such as a particle or thin film, having at least one physical dimension (e.g., length, height, width, diameter, etc.) that is selected over the range of 1 nm to 1000 nm. As used herein, micro-sized refers to a structure, such as a particle or thin film, having at least one physical dimension (e.g., length, height, width, diameter, etc.) that is selected over the range of 1 μηη to 1000 μηη . In an embodiment, for example, the negative electrode or the positive electrode is in the form of a powder, such as a mixture of active electrode particles and conductive particles. In an

embodiment, for example, the negative electrode or the positive electrode is in the form of a thin film. In an embodiment, for example, the invention provides an electrochemical cell wherein at least one of the positive electrode or negative electrode in the form of a solvated metal, such as solvated lithium or a solvated lithium alloy. In an embodiment, for example, the invention provides an electrochemical cell wherein at least one of the positive electrode or negative electrode in the form of a molten metal.

[0059] In an embodiment, for example, the invention provides an electrochemical cell wherein the negative electrode comprises a material selected from the group consisting of lithium, zinc, aluminum, silicon, tin, antimony, lead, germanium, magnesium, , cadmium, bismuth, indium, molybdenum, niobium, tungsten, tantalum, iron, nickel, manganese, copper, a sodium transition metal phosphate, a sodium mixed metal phosphate; Li₄/3Ti5/3O₄, graphite, an alloy of tin, cobalt, carbon, L1VO₂, Li₄Ti₅Oi₂, Li4/3Ti5/3O TiO₂, WO₂, and MoO₂. In an embodiment, for example, the invention provides an electrochemical cell wherein the positive electrode comprises a material selected from the group consisting of graphite, LiCoO_2NiO_8O₂ , LiNiO2 , LiFePO₄ , LiMnPO₄ , LiCoPO₄ , LiMn₂O₄ , LiCoO₂, LiNiO _5Mn l.5O₄, LiVPO₄ F, silver oxide, nickel oxide, cobalt oxide, manganese oxide, AgO, Ag₂O₃, Zn, ZnO AgO, Ag₂O, Ag₂O₃, HgO, Hg₂O, CuO, CdO, NiOOH, Pb₂O₄, PbO₂, LiFePO₄, Li₃V₂(PO₄)₃, V₆O₁₃, V₂O₅, Fe₃O₄, Fe₂O₃, MnO₂, LiCoO₂, LiNiO₂, LiMn₂O₄,. LiVO₂, Li₄Ti₅Oi₂, TiO₂, WO₂, and MoO₂. In an embodiment, for example, the invention provides an electrochemical cell wherein the positive electrode comprises a material selected from the group consisting of a (i) lithiated metal oxide based cathode selected from the group consisting of LixCoO₂, Li_xNiO₂, LixMn₂O₄ and LiFePO₄; (ii) an unlithiated metal oxide based cathode selected from the group consisting of Ag_xV₂O5, Cu_xV₂O5, V2O5, V₆O-i₃, MnO2, CuO, Ag₂CrO₄ and MoO₃, wherein x ranges from 0 to 2; (iii) a lithiated metal oxide based cathode selected from the group consisting of FeS₂,TiS₂, FeS and CuS; (iv) an active sulfur cathode selected from the group consisting of elemental sulfur, polysulfides and combinations thereof; and (v) a PEO/carbon/metal-oxide type cathode structure comprising an aqueous electrochemically active component such as water or a water soluble oxidant selected from the group consisting of gaseous, liquid and solid oxidants and

combinations thereof such as peroxide, hydrogen peroxide, O₂, SO₂ and NO₂, and the water soluble solid oxidants are selected from the group consisting of NaNO₂, KNO₂, Na₂SO₃ and K₂SO₃ wherein the cathode structure electronically conductive component is a porous catalytic support such as nickel and wherein said cathode structure electrochemically active material comprises air.

[0060] Electrochemical cells of the invention include primary electrochemical cells and secondary electrochemical cells. In an embodiment, for example, the invention provides an electrochemical cell comprising a lithium battery, an alkaline battery, zinc battery, a lead acid battery, a lithium metal -air battery, a lithium ion battery, a lithium air battery, a Fe-air battery, a Al-air battery, or a zinc-air battery. In an embodiment, for example, the invention provides an electrochemical cell comprising a fuel cell, a flow battery system, a semisolid battery, a 3-D battery, a nano-battery, a micro-battery, or an electrochemical capacitor. In an embodiment, for example, the invention provides an electrochemical cell comprising a thin film battery. In an embodiment, for example, the invention provides an electrochemical cell that is an alkaline metal ion battery.

[0061] In an embodiment, for example, the invention provides a battery pack comprising a one or more electrochemical cells, such as one or more lithium ion electrochemical cells. As will be understood by one of skill in the art, any of the separator systems and electrochemical cells described herein can be used for alkali metal fuel cells of the invention.

[0062] In an aspect, the invention provides an alkali metal fuel cell, comprising: (i) a renewable anode comprising solid alkali metal and alkali metal dissolved in a solvent as fuel; (ii) a cathode structure comprising a static electronically conductive component, an ionically conductive component comprising an electrolyte for ions of the alkali metal, and a fluid oxidant obtained from an operating environment of the cell; and (iii) a separator system of the invention provided between the anode and cathode structure. As will be understood by one of skill in the art, any of the separator systems described herein can be used for alkali metal fuel cells of the invention.

[0063] In an aspect, the invention provides a method of making an electrochemical cell, the method comprising the steps of: (i) providing a negative electrode; (ii) providing a positive electrode; (iii) providing an electrolyte between the positive electrode and the negative electrode; and (iv) providing a separator system positioned between the positive electrode and the negative electrode, wherein the separator system comprises (i) a first high mechanical strength layer having a plurality of apertures extending entirely through the first high mechanical strength layer and provided in a first pattern; and (ii) a second high mechanical strength layer having a plurality of apertures extending entirely through the second high mechanical strength layer and provided in a second pattern; the second pattern having an off-set alignment relative to the first pattern such that an overlap of the apertures of the first high mechanical strength layer and the apertures of the second high mechanical strength layer along axes extending perpendicularly from the first high mechanical strength layer to the second high mechanical strength layer is less than or equal to 20%; wherein the first high mechanical strength layer and the second high mechanical strength layer are positioned such that ions of an electrolyte provided in contact with the first high mechanical strength layer and the second high mechanical strength layer are able to be transported through the first high mechanical strength layer and the second high mechanical strength layer. In an embodiment, the separator system is at least partially in physical contact with the electrolyte. In an embodiment, the method further comprises providing an ion conductive chemical barrier between the positive electrode and the negative electrode; wherein the ion conductive chemical barrier separates a first electrolyte in contact with the positive electrode from a second electrolyte that is in connect with the negative electrode; wherein the first electrolyte has a different composition from the second electrolyte; and wherein the ion conductive chemical barrier prevents mixing of the first electrolyte and the second electrolyte. As will be generally understood by one of skill in the art, any of the present separator systems and systems of the invention, including all specific embodiments and combinations of components, materials and properties described herein, may be used in the present methods of making an electrochemical cell.

[0064] In an aspect, the invention provides a method of generating an electrical current, the method comprising the steps of: (i) providing an electrochemical cell, wherein the electrochemical cell comprises: (1 ) a first high mechanical strength layer having a plurality of apertures extending entirely through the first high mechanical strength layer and provided in a first pattern; and (2) a second high mechanical strength layer having a plurality of apertures extending entirely through the second high mechanical strength layer and provided in a second pattern; the second pattern having an off-set alignment relative to the first pattern such that an overlap of the apertures of the first high mechanical strength layer and the apertures of the second high mechanical strength layer along axes extending perpendicularly from the first high mechanical strength layer to the second high mechanical strength layer is less than or equal to 20%; wherein the first high mechanical strength layer and the second high mechanical strength layer are positioned such that ions of an electrolyte provided in contact with the first high mechanical strength layer and the second high mechanical strength layer are able to be transported through the first high mechanical strength layer and the second high mechanical strength layer; and (ii) discharging the electrochemical cell. In an embodiment, the method of this aspect further includes the step of charging the electrochemical cell. In an embodiment, the method of this aspect further includes the step of cycling the electrochemical cell through a plurality of charge and discharge cycles. As will be generally understood by one of skill in the art, any of the present separator systems and systems of the invention, including all specific embodiments and combinations of components, materials and properties described herein, may be used in the present methods of generating an electrical current. [0065] Without wishing to be bound by any particular theory, there can be discussion herein of beliefs or understandings of underlying principles or mechanisms relating to the invention. It is recognized that regardless of the ultimate correctness of any explanation or hypothesis, an embodiment of the invention can nonetheless be operative and useful.

BRIEF DESCRIPTION OF THE DRAWINGS

[0066] Figure 1 provides a side perspective view of a multilayer separator system for an electrochemical system comprising parallel first and second high mechanical strength layers having complementary patterns of apertures, wherein the second pattern of apertures has an off-set alignment relative to the first pattern such that there is no overlap of the apertures of the first pattern and the apertures of the second pattern along axes extending perpendicularly from the first high mechanical strength layer to the second high mechanical strength layer.

[0067] Figure 2 provides a side perspective view of a multilayer separator system for an electrochemical system comprising parallel first and second high mechanical strength layers having complementary patterns of apertures, wherein the second pattern of apertures has an off-set alignment relative to the first pattern such that there is a selected extent of overlap of the apertures of the first pattern and the apertures of the second pattern along axes extending perpendicularly from the first high mechanical strength layer to the second high mechanical strength layer, for example, a selected extent of overlap minimizing or avoid dendrite growth through the separator system.

[0068] Figure 3 provides a schematic diagram illustrating a cross sectional view of a multilayer separator system of the invention having first and second patterned high mechanical strength layers separated by an electrolyte-containing layer.

[0069] Figure 4 provides a schematic diagram illustrating a cross sectional view of a multilayer separator system of the invention having first, second and third patterned high mechanical strength layers separated by electrolyte-containing layers.

[0070] Figure 5 provides a schematic diagram illustrating a cross sectional view of a multilayer separator system of the invention showing the orientation of apertures and solid regions of the first and second patterned high mechanical strength layers separated by electrolyte-containing layers. [0071] Figure 6 provides a schematic diagram illustrating a cross sectional view of a multilayer separator system of the invention showing the orientation of apertures and solid regions of the first, second and third patterned high mechanical strength layers separated by electrolyte-containing layers.

[0072] Figure 7 provides a schematic diagram providing a cross sectional view of a lithium battery of the invention comprising a separator system with two patterned high mechanical strength layers having complementary patterns of apertures.

[0073] Figure 8 provides a schematic diagram providing a cross sectional view of a lithium battery of the invention comprising a separator system with four patterned high mechanical strength layers having complementary patterns of apertures.

[0074] Figure 9 provides a schematic diagram providing a cross sectional view of an electrochemical cell of the invention comprising a separator system with three patterned high mechanical strength layers having complementary patterns of apertures.

[0075] Figure 10A provides a schematic diagram providing a cross sectional view of an electrochemical cell of the invention comprising a lithium metal anode, cathode and a separator system comprising three high mechanical strength layers having

complementary patterns of apertures, two low ionic resistance layers, two electrolyte containing voids and a frame component.

[0076] Figure 10B provides a schematic diagram providing a cross sectional view of an electrochemical cell (e.g. useful for Li-air, Li-water batteries) having a separator with a protective solid electrolyte, wherein the solid electrolyte conducts the desired ions (such as Li⁺) but is impermeable to water, air, CO₂, contaminations and materials that deteriorate the performance of the electrochemical cell.

[0077] Figure 10C provides a schematic diagram providing a cross sectional view of an electrochemical cell (e.g., useful for Li-air, Li-water batteries) having a separator with a protective solid electrolyte, wherein the solid electrolyte conducts the desired ions (such as Li⁺) but is impermeable to water, air, CO2, contaminations and materials that deteriorate the performance of the electrochemical cell.

[0078] Figure 10D provides a schematic diagram providing a cross sectional view of an electrochemical cell (e.g., useful for Li-Sulfur batteries) having separator with a protective solid electrolyte, wherein the solid electrolyte conducts the desired ions (such as Li⁺) but is impermeable to particle passage between cathode and anode that deteriorate the performance of the electrochemical cell.

[0079] Figure 10E provides a schematic diagram providing a cross sectional view of an electrochemical cell having a separator wherein the conductive side of the separator next to the anode reduces anode loss; e.g., by stopping the dendrite growth, reducing anode loss such as in mossy deposition and stop the passage of cathode materials to the anode upon cycling which breaks the electronic contact between anode particles and the current collector and deteriorate the performance of the electrochemical cell.

[0080] Figure 10F provides a schematic diagram providing a cross sectional view of an electrochemical cell having a separator wherein the perforated separator plates and the porous layers act as a separator by providing electronic insulation between the electrodes, yet providing ionic connection between the electrodes via a fluid electrolyte (aqueous or aprotic).

[0081] Figure 10G provides a schematic diagram providing a cross sectional view of an electrochemical cell having a separator wherein shape memory effect of the two high mechanical strength layers results in a very good mechanical contact between the separator and the electrodes.

[0082] Figure 10H provides a schematic diagram providing a cross sectional view of an electrochemical cell having a separator wherein the super elasticity and/or shape memory effect of the two high mechanical strength layers results in a very good mechanical contact between the separator and the electrodes.

[0083] Figure 101 provides a schematic diagram providing a cross sectional view of an electrochemical cell having a separator wherein the super elasticity and/or shape memory effect of two high mechanical strength layers results in a very good mechanical contact between the separator and the electrodes.

[0084] Figure 10J provides a schematic diagram providing a cross sectional view of an electrochemical cell having a separator wherein the conductive side of the separator reduces anode loss such as in silicon large deformations upon cycling which breaks the electronic contact between anode particles and the current collector and deteriorate the performance of the electrochemical cell. [0085] Figure 10K provides a schematic diagram providing a cross sectional view of an electrochemical cell having a separator wherein the conductive side of the separator next to the anode reduces anode loss such as in silicon large deformations upon cycling which breaks the electronic contact between anode particles and the current collector and deteriorate the performance of the electrochemical cell.

[0086] Figures 1 1 A and 1 1 B provide examples of the designs of porous, patterned layers of some separator systems of the invention.

[0087] Figure 12 provides a schematic diagram of a cross sectional view of an electrochemical cell including a separator system of the invention.

[0088] Figure 13 provides a schematic diagram illustrating a potential trajectory of dendrite growth in an electrochemical system of the invention.

[0089] Figure 14 (Panels A - M) provides examples of complementary patterns of apertures useful in the patterned high mechanical strength layers of separator systems of the invention.

[0090] Figure 15 provides a plot of charge and discharge capacities (mAh/g) as a function of number of cycles for an electrochemical cell having: (A) a multilayer separator system of the invention having an overall thickness of 125 microns and (B) a Celgard separator having a thickness of 25 microns.

[0091] Figure 16 provides a plot of charge and discharge capacities (mAh/g) as a function of number of cycles for: (A, lines 1 , 5 and 6)) an electrochemical cell having a multilayer separator system of the invention, a Li metal anode and a UC0O2 cathode as compared to (B, lines 2 and 3) an electrochemical cell having a conventional separator.

[0092] Figure 17 provides a plot of charge and discharge capacities (mAh/g) as a function of number of cycles for: (lines A, B and C) an electrochemical cell having a multilayer separator system of the invention, a Li metal anode and a L1C0O2 cathode as compared to (lines F and D) show a reference electrode made with a perforated Kapton between two Celgard layers and (lines H and I) a Celgard separator having a thickness of 25 microns. [0093] Figure 18 provides a schematic diagram illustrating an electrochemical cell of the invention having a multilayer separator comprising three high mechanical strength layers with complementary patterns of apertures.

[0094] Figure 19 provides a schematic diagram illustrating the trajectory of Li⁺ ions passing through the multilayer separator shown in Figure 18.

[0095] Figure 20 provides a plot of cell voltage (V vs Li) versus cycling time (h) for the galvanostatic lithium stripping from two symmetrical (5/9)" lithium chips.

[0096] Figure 21 provides plots of the current [milliA mper] vs. time [hr] and voltage [v] vs. time [hr].

[0097] Figure 22 provides a plot of current [A] (on top) and voltage [v] (on bottom) as a function of time [s] in a CR2032 cell made with Li-metal , LiFePO cathode.

[0098] Figures 23 and 24 provide photographs of perforated layers useful in separator systems of some embodiments.

[0099] Figures 25, 26, 27, 28, 29 and 30 provide photographs of perforated layers useful in separator systems of some embodiments.

DETAILED DESCRIPTION

[00100] In general the terms and phrases used herein have their art-recognized meaning, which can be found by reference to standard texts, journal references and contexts known to those skilled in the art. The following definitions are provided to clarify their specific use in the context of the invention.

[00101] Referring to the drawings, like numerals indicate like elements and the same number appearing in more than one drawing refers to the same element. In addition, hereinafter, the following definitions apply:

[00102] The term "electrochemical cell" refers to devices and/or device

components that convert chemical energy into electrical energy or electrical energy into chemical energy. Electrochemical cells have two or more electrodes (e.g., positive and negative electrodes) and an electrolyte, wherein electrode reactions occurring at the electrode surfaces result in charge transfer processes. Electrochemical cells include, but are not limited to, primary batteries, secondary batteries and electrolysis systems. In certain embodiments, the term electrochemical cell includes fuel cells, supercapacitors, capacitors, flow batteries, metal-air batteries and semi-solid batteries. General cell and/or battery construction is known in the art, see e.g., U.S. Pat. Nos. 6,489,055, 4,052,539, 6,306,540, Seel and Dahn J. Electrochem. Soc. 147(3) 892-898 (2000).

[00103] The term "capacity" is a characteristic of an electrochemical cell that refers to the total amount of electrical charge an electrochemical cell, such as a battery, is able to hold. Capacity is typically expressed in units of ampere-hours. The term "specific capacity" refers to the capacity output of an electrochemical cell, such as a battery, per unit weight. Specific capacity is typically expressed in units of ampere-hours kg^"1.

[00104] The term "discharge rate" refers to the current at which an electrochemical cell is discharged. Discharge rate can be expressed in units of ampere. Alternatively, discharge rate can be normalized to the rated capacity of the electrochemical cell, and expressed as C/(X t), wherein C is the capacity of the electrochemical cell, X is a variable and t is a specified unit of time, as used herein, equal to 1 hour.

[00105] "Current density" refers to the current flowing per unit electrode area.

[00106] Electrode refers to an electrical conductor where ions and electrons are exchanged with electrolyte and an outer circuit. "Positive electrode" and "cathode" are used synonymously in the present description and refer to the electrode having the higher electrode potential in an electrochemical cell (i.e. higher than the negative electrode). "Negative electrode" and "anode" are used synonymously in the present description and refer to the electrode having the lower electrode potential in an electrochemical cell (i.e. lower than the positive electrode). Cathodic reduction refers to a gain of electron(s) of a chemical species, and anodic oxidation refers to the loss of electron(s) of a chemical species. Positive electrodes and negative electrodes of the present electrochemical cell may further comprise a conductive diluent, such as acetylene black, carbon black, powdered graphite, coke, carbon fiber, graphene, and metallic powder, and/or may further comprises a binder, such as a polymer binder.

Useful binders for positive electrodes in some embodiments comprise a fluoropolymer such as polyvinylidene fluoride (PVDF). Positive and negative electrodes of the present invention may be provided in a range of useful configurations and form factors as known in the art of electrochemistry and battery science, including thin electrode designs, such as thin film electrode configurations. Electrodes are manufactured as disclosed herein and as known in the art, including as disclosed in, for example, U.S. Pat. Nos.

4,052,539, 6,306,540, and 6,852,446. For some embodiments, the electrode is typically fabricated by depositing a slurry of the electrode material, an electrically conductive inert material, the binder, and a liquid carrier on the electrode current collector, and then evaporating the carrier to leave a coherent mass in electrical contact with the current collector.

[00107] "Electrode potential" refers to a voltage, usually measured against a reference electrode, due to the presence within or in contact with the electrode of chemical species at different oxidation (valence) states.

[00108] "Electrolyte" refers to an ionic conductor which can be in the solid state, the liquid state (most common) or more rarely a gas (e.g., plasma).

[00109] "Standard electrode potential" (E°) refers to the electrode potential when concentrations of solutes are 1 M, the gas pressures are 1 atm and the temperature is 25 degrees Celsius. As used herein standard electrode potentials are measured relative to a standard hydrogen electrode.

[00110] "Active material" refers to the material in an electrode that takes part in electrochemical reactions which store and/or deliver energy in an electrochemical cell.

[00111] "Cation" refers to a positively charged ion, and "anion" refers to a negatively charged ion.

[00112] "Electrical contact" and "electrical communication" refer to the

arrangement of one or more objects such that an electric current efficiently flows from one object to another. For example, in some embodiments, two objects having an electrical resistance between them less than 100 Ω are considered in electrical communication with one another. An electrical contact can also refer to a component of a device or object used for establishing electrical communication with external devices or circuits, for example an electrical interconnection. "Electrical communication" also refers to the ability of two or more materials and/or structures that are capable of transferring charge between them, such as in the form of the transfer of electrons. In some embodiments, components in electrical communication are in direct electrical communication wherein an electronic signal or charge carrier is directly transferred from one component to another. In some embodiments, components in electrical communication are in indirect electrical communication wherein an electronic signal or charge carrier is indirectly transferred from one component to another via one or more intermediate structures, such as circuit elements, separating the components.

[00113] "Thermal contact" and "thermal communication" are used synonymously and refer to an orientation or position of elements or materials, such as a current collector or heat transfer rod and a heat sink or a heat source, such that there is more efficient transfer of heat between the two elements than if they were thermally isolated or thermally insulated. Elements or materials may be considered in thermal

communication or contact if heat is transported between them more quickly than if they were thermally isolated or thermally insulated. Two elements in thermal communication or contact may reach thermal equilibrium or thermal steady state and in some

embodiments may be considered to be constantly at thermal equilibrium or thermal steady state with one another. In some embodiments, elements in thermal

communication with one another are separated from each other by a thermally conductive material or intermediate thermally conductive material or device component. In some embodiments, elements in thermal communication with one another are separated by a distance of 1 μιτι or less. In some embodiments, elements in thermal communication with one another are provided in physical contact.

[00114] "High mechanical strength" refers to a property of components of separator systems of the invention, such as first, second, third and fourth high mechanical strength layers, having a mechanical strength sufficient to prevent growth of dendrites between positive and negative electrodes of an electrochemical cell, for example, during charge and discharge cycles of a secondary electrochemical cell. In an embodiment, for example, a high mechanical strength layer has a mechanical strength sufficient to prevent piercing due to the growth of dendrites between electrodes. In an embodiment, for example, a high mechanical strength layer has a mechanical strength sufficient to prevent shorting between the positive electrode and the negative electrode of an electrochemical cell due to the growth of dendrites between electrodes. In an embodiment, for example, a high mechanical strength layer is characterized by a Young's modulus greater than or equal to 500 MPa, and optionally for some applications a Young's modulus greater than or equal to 1 GPa, and optionally for some applications a Young's modulus greater than or equal to 10 GPa, and optionally for some

applications a Young's modulus greater than or equal to 100 GPa. In an embodiment, for example, a high mechanical strength layer is characterized by a yield strength greater than or equal to 5 MPa, and optionally for some applications a yield strength greater than or equal to 50 MPa, and optionally for some applications a yield strength greater than or equal to 100 MPa, and optionally for some applications a yield strength greater than or equal to 500 MPa. In an embodiment, for example, a high mechanical strength layer is characterized by a propagating tear strength greater than or equal to 0.005 N, and optionally for some applications a propagating tear strength greater than or equal to 0.05 N, a propagating tear strength greater than or equal to 0.5 N, a

propagating tear strength greater than or equal to 1 N. In an embodiment, for example, a high mechanical strength layer is characterized by an initiating tear strength greater than or equal to 10 N, and optionally for some applications an initiating tear strength greater than or equal to 100 N. In an embodiment, for example, a high mechanical strength layer is characterized by a tensile strength greater than or equal to 50 MPa, and optionally for some applications a tensile strength greater than or equal to 100 MPa, and optionally for some applications a tensile strength greater than or equal to 500 MPa, and optionally for some applications a tensile strength greater than or equal to 1 GPa. In an embodiment, for example, a high mechanical strength layer is characterized by an impact strength greater than or equal to 10 N cm, and optionally for some applications to an impact strength greater than or equal to 50 N cm, and optionally for some

applications to an impact strength greater than or equal to 100 N cm, and optionally for some applications to an impact strength greater than or equal to 500 N cm.

[00115] "Chemically resistant" refers a property of components, such as layers, of separators and electrochemical systems of the invention wherein the tensile retention and elongation retention is at least 90% in the working environment of an

electrochemical system, such as an electrochemical cell.

[00116] "Thermally stable" refers a property of components, such as layers, of separators and electrochemical systems of the invention wherein the melting point is more than 100 Celsius, and preferably for some embodiments more than 300 Celsius, and optionally the coefficient of thermal expansion is less than 50ppm/Celsius. In an embodiment, thermally stable refers to a property of a component of the separator system such that it may perform in a rechargeable electrochemical cell without undergoing a change size or shape with the temperature that significantly degrades the performance of the electrochemical cell. [00117] "Porosity" refers to the amount of a material or component, such as a high mechanical strength layer, that corresponds to pores, such as apertures, channels, voids, etc. Porosity may be expressed as the percentage of the volume of a material, structure or device component, such as a high mechanical strength layer, that corresponds to pores, such as apertures, channels, voids, etc., relative to the total volume occupied by the material, structure or device component.

[00118] Figure 1 provides a side perspective view of a multilayer separator system 100(1) for an electrochemical system comprising parallel first and second high

mechanical strength layers having complementary patterns of apertures, wherein the second pattern of apertures has an off-set alignment relative to the first pattern such that there is no overlap of the apertures of the first pattern and the apertures of the second pattern along axes extending perpendicularly from the first high mechanical strength layer to the second high mechanical strength layer. As shown in Figure 1 , separator system 100(1) comprises a first high mechanical strength layer 102(1) having a first pattern comprising a plurality of apertures, e.g. 104(1) and 104(4), and a second high mechanical strength layer 102(2) having a second pattern comprising a second plurality of apertures, e.g. 104(2) and 104(3). First and second layers are characterized by a planar geometry and lateral dimensions, such as height, H, length, L, and width or thickness, W. As shown in Figure 1 , apertures 104 extend entirely through the thickness of either first high mechanical strength layer 102(1) or second high

mechanical strength layer 102(2). Each aperture 104 is also characterized by lateral dimensions, such as height, h, length, I, and width or thickness (not shown).

[00119] The superposition of the pattern of first high mechanical strength layer 102(1) onto the second high mechanical strength layer 102(2) is schematically presented as a plurality of off-set dashed areas 106(1) on second high mechanical strength layer 102(2), and the superposition of the pattern of second high mechanical strength layer 102(2) on first high mechanical strength layer 102(1) is schematically presented as a plurality of off-set dashed areas 106(2) on first high mechanical strength layer 102(1). In the embodiment shown in Figure 1 , the first and second patterns resemble checkerboard patterned, for example where the first pattern corresponds to the back squares and the second pattern corresponds to the red squares of a checker board. As will be apparent to one of skill in the art, however, other patterns, such as honeycomb patterns, close-packed circle patterns, brick patterns, triangular patterns and the like, are also possible, so long as the first and second patterns have off-set alignments relative to one another, for example, such that an overlap of apertures 104 along axes extending perpendicularly from first high mechanical strength layer 102(1) to second high mechanical strength layer 102(2) is less than or equal to 50%, 40%, 30%, 20%, 10%, 5%, 2% or 0%. In the embodiment shown in Figure 1 , there is no overlap of the apertures of the first pattern and the apertures of the second pattern along axes extending perpendicularly from the first high mechanical strength layer to the second high mechanical strength layer. The arrows 108(1) and 108(2) shown in Figure 1 are provided so as to illustrate regions of the apertures that do not overlap along axes extending perpendicularly from first high mechanical strength layer 102(1) to second high mechanical strength layer 102(2). The off-set alignment of the first pattern of apertures of the first high mechanical strength layer and the second pattern of apertures of the second high mechanical strength layer prevents growth of dendrites through the combination of first and second high mechanical strength layers, for example, by mechanically blocking growing dendrites and/or requiring a pathway involving curved trajectories which are thermodynamically and/or kinetically unfavorable. For example, a dendrite may only pass through aperture 104(3) of second high mechanical strength layer 102(2), as shown by arrow A, because it is physically blocked by first high mechanical strength layer 102(1) at point 110(1). Similarly, a dendrite may only pass through aperture 104(4) of first high mechanical strength layer 102(1), as shown by arrow B, because it is physically blocked by second high mechanical strength layer

102(2) at point 110(2).

[00120] Figure 2 provides a side perspective view of a multilayer separator system 100(2) for an electrochemical system comprising parallel first and second high

mechanical strength layers having complementary patterns of apertures, wherein the second pattern of apertures has an off-set alignment relative to the first pattern such that there is a selected extent of overlap of the apertures of the first pattern and the apertures of the second pattern along axes extending perpendicularly from the first high mechanical strength layer to the second high mechanical strength layer. As shown in Figure 2, separator system 100(2) comprises a first high mechanical strength layer

102(3) having a first pattern comprising a plurality of apertures, e.g. 104(5) and 104(9), and a second high mechanical strength layer 102(4) having a second pattern comprising a second plurality of apertures, e.g. 104(6), 104(7) and 104(8). First and second high mechanical strength layers 102 are characterized by lateral dimensions, such as height, H, length, L, and width or thickness, W. As shown in Figure 1 , apertures 104 extend entirely through the thickness of either first high mechanical strength layer 102(3) or second high mechanical strength layer 102(4). Each aperture 104 is also characterized by lateral dimensions, such as height, h, length, I, and width or thickness (not shown).

[00121] The superposition of the first pattern of first high mechanical strength layer 102(3) on the second high mechanical strength layer 102(4) is schematically presented as a plurality of dashed areas 106(3) on second high mechanical strength layer 102(4), and the superposition of the second pattern of second high mechanical strength layer 102(4) on the first high mechanical strength layer 102(3) is schematically presented as a plurality of dashed areas 106(4) on first layer 102(3). In the embodiment shown in Figure 2, the first and second patterns have off-set alignments relative to one another such that there is a selected overlap of apertures 104 along axes extending

perpendicularly from first high mechanical strength layer 102(3) to second high mechanical strength layer 102(4). In an embodiment, for example, the selected overlap is less than or equal to 50%, 40%, 30%, 20%, 10%, 5%, or 2%. In the embodiment shown in Figure 2, the overlap of the apertures of the first pattern and the apertures of the second pattern along axes extending perpendicularly from the first high mechanical strength layer to the second high mechanical strength layer is greater than zero. The arrows shown in Figure 2 are provided so as to illustrate the overlapping regions 112 of the apertures and regions of the apertures that do not overlap along axis extending perpendicularly from first high mechanical strength layer 102(3) to second high mechanical strength layer 102(4). The off-set alignment of the pattern of apertures of the first high mechanical strength layer and the pattern of apertures of the second high mechanical strength layer prevents growth of dendrites through the combination of the first and second high mechanical strength layers, for example, by blocking dendrite growth and/or requiring a pathway involving curved trajectories which are

thermodynamically and/or kinetically unfavorable.

[00122] The invention may be further understood by the following non-limiting examples.

EXAMPLE 1 : Novel Separators for Electrochemical and Chemical Systems, such as for batteries, such as for rechargeable lithium batteries and especially to prevent dendrite short circuits in Li-metal batteries

[00123] Figure 3 provides a schematic diagram illustrating a cross sectional view of a multilayer separator system of the invention having first and second high mechanical strength layers (layers R and F) having complementary patterns of apertures separated by an electrolyte-containing layer (layer M). Figure 4 provides a schematic diagram illustrating a cross sectional view of a multilayer separator system of the invention having first, second and third high mechanical strength layers (layers R and F) with complementary patterns of apertures separated by electrolyte-containing layers (layer M). In Figures 3 and 4, layers (R) and layers (F) are high mechanical strength layers having patterns of apertures that when provided in combination prevent dendrite growth through the separator system, for example, when incorporated into an electrochemical system, such as an electrochemical cell. In Figures 3 and 4,

electrolyte-containing layer(s) M is provided between layers F and R and, in some embodiments, electrolyte-containing layer(s) M is preferably thicker than layers F and R. In an electrochemical system, for example, layer(s) M acts as an reservoir for an electrolyte. In an electrochemical system, for example, layer(s) M acts as a separator, thereby, preventing electrical and/or physical contact between the positive electrode and negative electrode while allowing ion transport between positive and negative electrodes so that the electrochemical cell can undergo efficient discharge and charging

characteristics. In an embodiment, for example, layer M is a low ionic resistance layer, such as a conductive microporous membrane. In an embodiment, for example, layer M is a polyethylene (PE) membrane or a polypropylene (PP) membrane or a combination of both.

[00124] In some embodiments, high mechanical strength layers F and R function to prevent dendrite growth in an electrochemical cell such to prevent electrical shorting, thermal runaway and/or mechanical failure of the cell. As an example, high mechanical strength layers F and R may be configured to prevent the short circuit and capacity losses in lithium metal batteries by preventing dendrite growth between positive and negative electrodes. In some embodiments, high mechanical strength layers F and R provide complementary barriers each having a mechanical strength sufficient to prevent piercing or mechanical failure of the barrier when in contact with a growing dendrite.

[00125] In some embodiments, high mechanical strength layers F and R are provided with complementary patterns of apertures extending through the entire thickness of the layers. Figure 5 provides a schematic diagram illustrating a cross sectional view of a multilayer separator system of the invention illustrating apertures (schematically illustrated as the dotted regions) and solid regions (schematically illustrated as the filled regions) of the first and second high mechanical strength layers separated by one or more low ionic resistance layers, such as an electrolyte-containing layer M. Figure 6 provides a schematic diagram illustrating a cross sectional view of a multilayer separator system of the invention illustrating apertures and solid regions of the first, second and third high mechanical strength layers separated by one or more low ionic resistance layers, such as an electrolyte-containing layer M. As an example, high mechanical strength layer(s) F may be characterized by a preselected first pattern of apertures and solid regions, and high mechanical strength layer(s) R may be

characterized by a second preselected pattern of apertures and solid regions that is different from that of high mechanical strength layer F. In an embodiment, for example, the two patterns are complementary such that each of the high mechanical strength layers F and R have apertures (e.g., through-holes, nanopores, micropores, channels, etc.) that allow the transport of ions and electrolyte from either side of the high

mechanical strength layer, but alignment of high mechanical strength layers F and R in the multilayer separator system geometry provides apertures of high mechanical strength layer F to match the solid regions of high mechanical strength layer R and the solid regions of high mechanical strength layer F to match the holes of high mechanical strength layer R, for example along axes extending perpendicularly from said high mechanical strength layer(s) R to high mechanical strength layer(s) F. In an

embodiment, for example, the apertures of high mechanical strength layers F and R are off-set with respect to each other such that no straight line can go through the holes of both layers F and R when they are provided in combination, for example in a parallel or concentric orientation. This spatial arrangement can be visualized, for example, by considering a periodic pattern, such as a chess board having white and black squares, wherein the white squares correspond to the apertures and wherein the black squares correspond to the solid regions of the high mechanical strength layer. In an example, high mechanical strength layer F can be in the format of a typical chess board, and high mechanical strength layer R is in the format of a reverse one, misplaced chess board, in which the white blocks (corresponding to the apertures) are in the place of black squares (solid part of layer F) and black blocks (corresponding to the solid regions) are in the place of white squares (holes of layer F). This off-set alignment results in at least two high mechanical strength layers wherein all the holes are blocked by solid regions of a neighboring layer when provided in a multilayer geometry.

[00126] Placement of the low ionic resistance layer M (typical separator) between high mechanical strength layers F and R provides a separator system which prevents the unwanted growth of dendrites extending through the separator system. In order to minimize the effect of the separator system on the resistance of the cell, however, it is desirable for some embodiments to minimize the thickness of high mechanical strength layers F and R while at least maintaining a thickness that is necessary to provide sufficient mechanical strength to block growing dendrites.

[00127] In an embodiment, for example, high mechanical strength layers F and R are very thin (e.g., thickness less than or equal to 100 μηη and optionally for some embodiments thickness less than or equal to 20 μηη) and, thus, can optionally be in the form of one or more coatings on the front and/or back sides of the layer M. The volume fraction and surface fraction of holes in high mechanical strength layers F and R are selected for a given application, and for some applications it is preferable that at least a quarter, and optionally half, of the surface-volume comprises apertures and the remainder comprising impermeable solid regions. In an embodiment, high mechanical strength layers F and R comprise materials that do not react with other components of an electrochemical cell and are chemically resistant and thermally stable. In an embodiment, high mechanical strength layers F and R comprise electrical insulators.

[00128] In specific embodiments useful for a lithium-metal battery, high mechanical strength layers F and R comprise a polyethylene membrane or polypropylene

membrane or Teflon or a mixture of these materials having complementary patterns of apertures allowing the passage of ions and electrolyte but preventing the passage of electrical current directly between positive and negative electrodes of an

electrochemical cell. In an embodiment, for example, low ionic resistance layer M is a porous polyethylene membrane or a porous polypropylene membrane or a mixture of these. In an embodiment, low ionic resistance layer M has a thickness selected from the range of 10-200 micrometers, preferably for some applications equal to 80 - 120 micrometers, and high mechanical strength layers F and R each independently have a thickness selected from the range of 5-200 micrometers, preferably for some

applications equal to 10 - 30 micrometers. In an embodiment, high mechanical strength layers L and M have complementary periodic patterns of apertures and solid regions, wherein one or more lateral dimensions of the unit cell characterizing the apertures and/or solid regions is, for example, selected over the range of 1 micrometer and 1 millimeter, preferably 10 - 30 micrometers for some applications. Smaller sizes of the lateral dimensions of the unit cell of the apertures, as small as 10 times the average aperture size of layer M, are preferred for some embodiments; but it is acknowledged that there may be practical advantages of large apertures with respect to fabrication, so there can be a compromise in the selection of the physical dimensions of the apertures.

[00129] As will be apparent to one of skill in the art, the composition, physical dimensions (e.g., thicknesses) and mechanical properties (e.g., porosity) of the components of the separator systems may depend on the type of electrochemical or chemical cells and/or application. In an embodiment, for example, separator systems for lead-acid batteries may employ thicker high mechanical strength layers having larger hole sizes than in separator systems for lithium-metal batteries.

[00130] Other separator geometries, besides the described R-M-F and F-M-R-M-F systems shown in Figures 3 and 5, are also useful for some applications. As an example, the invention includes multilayer systems with 3, 4, 5, 6, 7, 8, etc. high mechanical strength layers having patterns of apertures selected to prevent dendrite growth. Multilayer systems having more than two high mechanical strength layers, such corresponding to the F-M-R-M-F system shown in Figures 4 and 6, are preferred for some applications as they may be configured to efficiently prevent growth of dendrites from positive to negative electrodes and yet the added resistance to the cell can still be maintained low enough to provide useful discharge and charging performance.

[00131] As an example, a high energy rechargeable lithium battery of the invention comprises: (1 ) an anode comprising lithium metal or lithium-alloy or mixtures of lithium metal and/or lithium alloy and another material; (2) a cathode; (3) a separator system of the invention disposed between the anode and the cathode; and (4) one or more electrolytes in ionic communication, optionally in physical contact, with the anode and the cathode via the separator. In an embodiment, for example, the electrolyte is either solid, gel or liquid (e.g. a fluid). In some embodiments, the electrodes are solid materials or are semi-solid particles (e.g., small solid particles in liquids) such as what is used in semi-solid batteries or in flow batteries or in flow cells. The cross sectional geometry of the separator system can be a range of shapes including rectangular, circular, square, etc.

[00132] Figure 7 provides a schematic diagram providing a cross sectional view of a lithium battery of the invention comprising a separator system with two high

mechanical strength layers having complementary patterns of apertures. The

electrochemical cell comprises an anode (e.g., lithium metal) and cathode that are separated by a multilayer separator system including an electrolyte reservoir. The multilayer separator comprises two high mechanical strength layers having complementary patterns of apertures separated by a low ionic resistance layer such as an electrolyte-containing separator and/or spacer. In addition, very porous media is provided between the high mechanical strength layers and the anode and cathode components. As shown in Figure 7, the high mechanical strength layers have patterns comprising alternating apertures and solid regions (e.g., in Figure 7 the filled-in regions correspond to solid regions of the high mechanical strength layer and dotted regions correspond to apertures extending through the high mechanical strength layer). In the embodiment shown, the high mechanical strength layers have complementary patterns of apertures capable of preventing growth of dendrites between cathode and anode, wherein open regions (e.g., apertures) of a first high mechanical strength layer correspond to solid regions of the second high mechanical strength layer along axes extending perpendicularly from the layers, as shown in Figure 7.

[00133] Figures 8 - 10 provide examples of other embodiments of lithium batteries illustrating additional device configurations and device components of the invention. Figure 8 provides a schematic diagram providing a cross sectional view of a lithium battery of the invention comprising a separator system with four high mechanical strength layers having complementary patterns of apertures. In the device illustrated in Figure 8, high mechanical strength layer R is provided in direct physical contact with the anode and high mechanical strength L is provided in direct physical contact with the cathode. In the embodiment shown in Figure 8, the two layers R have the same pattern of apertures and the two layers F have the same pattern of apertures. Together the patterns in layers R and F comprise complementary patterns that eliminate any direct linear pathway between the anode and the cathode along axis extending

perpendicularly from cathode to anode, thereby preventing dendrite growth related shorting. In the embodiment shown in Figure 8, a high mechanical strength layer R is provided in physical contact with the anode so as to allow ions to pass through layer R and interact with the anode surface; and a high mechanical strength layer F is provided in physical contact with the cathode so as to allow ions to pass through layer F and interact with the cathode surface.

[00134] Figure 9 provides a schematic diagram providing a cross sectional view of an electrochemical cell of the invention comprising a separator system with three high mechanical strength layers having complementary patterns of apertures. In the device illustrated in Figure 9, a very porous layer (e.g., porosity > 80%) is provided between the high mechanical strength layer F and the anode and a very porous layer (e.g., porosity > 80%) is provided between high mechanical strength layer F and the cathode. In the device illustrated in Figure 9, high mechanical strength layer R has a pattern of apertures that is complementary to the pattern of apertures of high mechanical strength layers F, and a porous layer (e.g., porosity > 50%) is provided between high mechanical strength layer R and the high mechanical strength layers F. In an embodiment, for example, the two high mechanical strength layers F are characterized by the same pattern of apertures. In the embodiment shown in Figure 9, the two layers F have the same pattern of apertures. Together the patterns in layer R and the two layers F comprise complementary patterns that eliminate any direct linear pathway between the anode and the cathode along axis extending perpendicularly from cathode to anode, thereby preventing dendrite growth related shorting. In the embodiment shown in Figure 9, a very porous layer (e.g., porosity > 80%) is provided in physical contact with the anode so as to allow ions to pass through this porous layer and interact with the anode surface; and a very porous layer (e.g., porosity > 80%) is provided in physical contact with the cathode so as to allow ions to pass through this porous layer and interact with the cathode surface.

[00135] Figure 10A provides a schematic diagram providing a cross sectional view of an electrochemical cell of the invention comprising a lithium metal anode, cathode and a separator system comprising three high mechanical strength layers having complementary patterns of apertures, two low ionic resistance layers, two electrolyte containing voids and a frame component. In some embodiments, for example, the frame layer(s) provides a means of physically integrating, attaching and/or mechanically supporting the components of the overall multilayer arrangement. In the lithium battery shown in Figure 10, an electrolyte containing void is provided between the anode and a first high mechanical strength layer having a pattern of apertures and an electrolyte containing void is provided between the cathode and a second high mechanical strength layer having a pattern of apertures. In some embodiments, for example, incorporation of an electrolyte containing void between the electrode and the high mechanical strength layer is useful to avoid reducing the electrode surface area so as to access useful discharge and charge characteristics of the cell. In the device illustrated in Figure 10, high mechanical strength layer R has a pattern of apertures that is complementary to the pattern of apertures of high mechanical strength layers F, and a low ionic resistance layer (e.g., porosity > 50%) is provided between high mechanical strength layer R and the high mechanical strength layers F.

[00136] Figure 10B provides a schematic diagram providing a cross sectional view of an electrochemical cell (e.g. useful for Li-air, Li-water batteries) having a separator with a protective solid electrolyte, wherein the solid electrolyte conducts the desired ions (such as Li⁺) but is impermeable to water, air, CO2, contaminations and materials that deteriorate the performance of the electrochemical cell. The electrochemical cell comprises a anode such as a lithium anode; a cathode such as a carbon-water cathode or carbon-air cathode; a separator system comprising two high mechanical strength layers having complementary patterns of apertures, three low ionic resistance layers, and a solid electrolyte layer, such as a LISICON layer. In the device illustrated in Figure 10B, the high mechanical strength layers are optionally chemically resistant and thermally stable perforated layers that are also electronically insulating, such as perforated Kapton layers. Use of complementary high mechanical strength layers comprising Kapton is useful in some embodiments for preventing dendrite growth. As shown in Figure 10B, a first low ionic resistance layer, such as a very porous layer (e.g., > 80%), is provided between the anode and a first high mechanical strength layer and a second low ionic resistance layer, such as a very porous layer (e.g., > 80%), is provided between the first high mechanical strength layer and a second high mechanical strength layer, and a third low ionic resistance layer, such as a very porous layer (e.g., > 80%), is provided between the second high mechanical strength layer and the cathode. As shown in Figure 10B, a solid electrolyte layer, such as a LISICON layer, is provided between the third low ionic resistance layer and the cathode such that ions are able to be transported to the cathode surface. In an embodiment, for example, the solid electrolyte layer is provided in physical contact with a surface of the cathode. In some embodiments, incorporation of the solid electrolyte layer (e.g., LISICON layer) is useful to protect the cathode, for example, to protect against unwanted chemical reactions with the cathode surface and components of the electrochemical cell, such as electrolyte components other than the solid electrolyte. In some embodiments, the solid electrolyte layer (e.g., LISICON layer) provides a chemical barrier layer separating a first side of the electrochemical cell having a first electrolyte from a second side of the electrochemical cell having a second electrolyte that is different from the first electrolyte. Embodiments of this aspect, therefore, may provide a means for integrating two separate electrolytes each tailored specifically for selected anode and cathode compositions. [00137] Figure 10C provides a schematic diagram providing a cross sectional view of an electrochemical cell (e.g., useful for Li-air, Li-water batteries) having a separator with a protective solid electrolyte, wherein the solid electrolyte conducts the desired ions (such as Li⁺) but is impermeable to water, air, CO2, contaminations and materials that deteriorate the performance of the electrochemical cell. The electrochemical cell comprises a lithium anode; a cathode such as a carbon-water cathode or carbon-air cathode; a separator system comprising two high mechanical strength layers having complementary patterns of apertures, three low ionic resistance layers; and a solid electrolyte layer, such as a LISICON layer. The overall electrochemical cell geometry in Figure 10C is similar to that shown in Figure 10B, wherein a first low ionic resistance layer, such as a very porous layer (e.g., > 80%), is provided between the anode and a first high mechanical strength layer and a second low ionic resistance layer, such as a very porous layer (e.g., > 80%), is provided between the first high mechanical strength layer and a second high mechanical strength layer, and a third low ionic resistance layer, such as a very porous layer (e.g., > 80%), is provided between the second high mechanical strength layer and the cathode, and wherein a solid electrolyte layer, such as a LISICON layer, is provided between the third low ionic resistance layer and the cathode such that ions are able to be transported to the cathode surface. In the electrochemical cell of Figure 10C, however, the high mechanical strength layers are perforated metal layers having complementary patterns of apertures that are useful in some embodiments for preventing dendrite growth and reducing anode loss such as in mossy deposition. Similar to the discussion in connection with Figure 10B, incorporation of the solid electrolyte layer (e.g., LISICON layer) is useful to protect the cathode, for example, to protect against unwanted chemical reactions with the cathode surface and components of the electrochemical cell, such as electrolyte components other than the solid electrolyte. In some embodiments, the solid electrolyte layer (e.g., LISICON layer) provides a chemical barrier layer separating a first side of the electrochemical cell having a first electrolyte from a second side of the electrochemical cell having a second electrolyte that is different from the first electrolyte, and therefore, may provide a means for integrating two separate electrolytes each tailored specifically for selected anode and cathode compositions.

[00138] Figure 10D provides a schematic diagram providing a cross sectional view of an electrochemical cell (e.g., useful for Li-Sulfur batteries) having separator with a protective solid electrolyte, wherein the solid electrolyte conducts the desired ions (such as Li⁺) but is impermeable to particle passage between cathode and anode that deteriorate the performance of the electrochemical cell. The electrochemical cell comprises an anode such as a lithium anode; a cathode such as a sulfur-based cathode; a separator system comprising two high mechanical strength layers having complementary patterns of apertures, three low ionic resistance layers; and a solid electrolyte layer, such as a LISICON layer. The overall electrochemical cell geometry in Figure 10C is similar to that shown in Figures 10B and 10C, wherein a first low ionic resistance layer, such as a very porous layer (e.g., > 80%), is provided between the anode and a first high mechanical strength layer and a second low ionic resistance layer, such as a very porous layer (e.g., > 80%), is provided between the first high mechanical strength layer and a second high mechanical strength layer, and a third low ionic resistance layer, such as a very porous layer (e.g., > 80%), is provided between the second high mechanical strength layer and the cathode, and wherein a solid electrolyte layer, such as a LISICON layer, is provided between the third low ionic resistance layer and the cathode such that ions are able to be transported to the cathode surface. In the electrochemical cell of Figure 10D, however, the high

mechanical strength layers are perforated metal layers having complementary patterns of apertures and the cathode is optionally a sulfur-based cathode. Incorporation of high mechanical strength metal layers in the present separators are useful in some

embodiments for preventing dendrite growth, reducing anode loss such as in mossy deposition and stopping the passage of cathode materials to the anode. Similar to the discussion in connection with Figure 10B, incorporation of the solid electrolyte layer (e.g., LISICON layer) is useful to protect the cathode, for example, to protect against unwanted chemical reactions with the cathode surface and components of the

electrochemical cell, such as electrolyte components other than the solid electrolyte. In some embodiments, the solid electrolyte layer (e.g., LISICON layer) provides a chemical barrier layer separating a first side of the electrochemical cell having a first electrolyte from a second side of the electrochemical cell having a second electrolyte that is different from the first electrolyte, and, therefore, may provide a means for integrating two separate electrolytes each tailored specifically for selected anode and cathode compositions

[00139] Figure 10E provides a schematic diagram providing a cross sectional view of an electrochemical cell having a separator wherein the conductive side of the separator next to the anode reduces anode loss; e.g., by stopping the dendrite growth, reducing anode loss such as in mossy deposition and stop the passage of cathode materials to the anode upon cycling which breaks the electronic contact between anode particles and the current collector and deteriorate the performance of the

electrochemical cell. For example, the conductive side next to the cathode increases the electronic conductivity of the cathode which can result in longer life cycle, higher power and thicker cathode, and higher energy cathode and thus a better

electrochemical cell. The electrochemical cell comprises a anode, such as a lithium anode; a cathode, such as a LiFePO₄, LiCoO₂ cathode; a separator system comprising two high mechanical strength layers having complementary patterns of apertures, three low ionic resistance layers; and a mechanically, chemically and heat resistant ionic conductive layer such as a carbon black layer. The overall electrochemical cell geometry in Figure 10C is similar to that shown in Figures 10B, 10C and 10D, wherein a first low ionic resistance layer, such as a very porous layer (e.g., > 80%), is provided between the anode and a first high mechanical strength layer and a second low ionic resistance layer, such as a very porous layer (e.g., > 80%), is provided between the first high mechanical strength layer and a second high mechanical strength layer, and a third low ionic resistance layer, such as a very porous layer (e.g., > 80%), is provided between the second high mechanical strength layer and the cathode. In the

electrochemical cell of Figure 10D, however, a first high mechanical strength layer comprises a perforated metal layer and a second high mechanical strength layer comprises a perforated electronically insulating layer, such as a perforated Kapton layer. In this embodiment, the perforated metal layer and the perforated Kapton layer have complementary patterns of apertures to prevent dendrite growth. In addition, a mechanically, chemically and heat resistant ionic conductive carbon black layer is provided adjacent to, and optionally in electrical contact and/or physical contact with, the cathode.

[00140] Figure 10F provides a schematic diagram providing a cross sectional view of an electrochemical cell having a separator wherein the perforated separator plates and the porous layers act as a separator by providing electronic insulation between the electrodes, yet providing ionic connection between the electrodes via a fluid electrolyte (aqueous or aprotic). The electrochemical cell comprises an anode, such as a silicon, Li, Zn, ZnO, Graphite or LTO anode; a cathode, such as a LiFePO4, LiCoO2, Sulfur, or Ag cathode; and a separator system comprising two high mechanical strength layers having complementary patterns of apertures and three low ionic resistance layers. As shown in Figure 10F, a first low ionic resistance layer, such as a very porous layer (e.g., > 80%), is provided between the anode and a first high mechanical strength layer and a second low ionic resistance layer, such as a very porous layer (e.g., > 80%), is provided between the first high mechanical strength layer and a second high mechanical strength layer, and a third low ionic resistance layer, such as a very porous layer (e.g., > 80%), is provided between the second high mechanical strength layer and the cathode. In the electrochemical cell of Figure 10F, first and second high mechanical strength layers independently comprise a mechanically, chemically and heat resistant electronically insulating layers, such as perforated metal layers having one or more insulating coatings such as a PE or PP coating.

[00141] Figure 10G provides a schematic diagram providing a cross sectional view of an electrochemical cell having a separator wherein shape memory effect of the two high mechanical strength layers results in a very good mechanical contact between the separator and the electrodes. The electrochemical cell comprises a anode, such as a silicon, Li, Zn, ZnO, Graphite or LTO anode; a cathode, such as a LiFePO4, LiCoO2, Sulfur, or Ag cathode; and a separator system comprising two high mechanical strength layers having complementary patterns of apertures and three low ionic resistance layers. The overall electrochemical cell geometry in Figure 10G is similar to that shown in Figure 10F, wherein a first low ionic resistance layer, such as a very porous layer (e.g., > 80%), is provided between the anode and a first high mechanical strength layer and a second low ionic resistance layer, such as a very porous layer (e.g., > 80%), is provided between the first high mechanical strength layer and a second high mechanical strength layer, and a third low ionic resistance layer, such as a very porous layer (e.g., > 80%), is provided between the second high mechanical strength layer and the cathode. In the electrochemical cell of Figure 10G, however, first and second high mechanical strength layers independently comprise a mechanically, chemically and heat resistant electronically insulating layers exhibiting a shape memory effect, such as perforated Nitnonol layers that are optionally coated with PE or PP.

[00142] Figure 10H provides a schematic diagram providing a cross sectional view of an electrochemical cell having a separator wherein the super elasticity and/or shape memory effect of the two high mechanical strength layers results in a very good mechanical contact between the separator and the electrodes. In an embodiment, of this aspect for example, enhanced electrical contact is provided between the solid electrolyte and the cathode. The electrochemical cell comprises a anode such as a silicon, Li, Zn, ZnO, Graphite, or LTO anode; a cathode such as a LiFePO₄, L1C0O2, Sulfur, Ag, Carbon-Air, Carbon-Water cathode; a separator system comprising two high mechanical strength layers having complementary patterns of apertures, three low ionic resistance layers; and a solid electrolyte layer, such as a LISICON or PEO (polyethylene oxide) layer. The overall electrochemical cell geometry in Figure 10H is similar to that shown in Figures 10B, 10C and 10D, wherein a first low ionic resistance layer, such as a very porous layer (e.g., > 80%), is provided between the anode and a first high mechanical strength layer and a second low ionic resistance layer, such as a very porous layer (e.g., > 80%), is provided between the first high mechanical strength layer and a second high mechanical strength layer, and a third low ionic resistance layer, such as a very porous layer (e.g., > 80%), is provided between the second high mechanical strength layer and the cathode, and wherein a solid electrolyte layer, such as a LISICON or PEO layer, is provided between the third low ionic resistance layer and the cathode such that ions are able to be transported to the cathode surface. In the electrochemical cell of Figure 10H, however, the high mechanical strength layers are mechanically, chemically and heat resistant electronically insulating layers with super- elasticity or shape memory effect such as perforated Nitonol layers that may optionally be coated with PE or PP. Similar to the discussion in connection with Figure 10B, incorporation of the solid electrolyte layer (e.g., LISICON or PEO layer) is useful to protect the cathode, for example, to protect against unwanted chemical reactions with the cathode surface and components of the electrochemical cell, such as electrolyte components other than the solid electrolyte. In some embodiments, the solid electrolyte layer (e.g., LISICON layer) provides a chemical barrier layer separating a first side of the electrochemical cell having a first electrolyte from a second side of the electrochemical cell having a second electrolyte that is different from the first electrolyte, and, therefore, may provide a means for integrating two separate electrolytes each tailored specifically for selected anode and cathode compositions

[00143] Figure 101 provides a schematic diagram providing a cross sectional view of an electrochemical cell having a separator wherein the super elasticity and/or shape memory effect of two high mechanical strength layers results in a very good mechanical contact between the separator and the electrodes. In an embodiment of this aspect, for example, enhanced electrical contact is provided between the solid electrolyte and the cathode. The electrochemical cell comprises a anode such as a silicon, Li, Zn, ZnO, Graphite, or LTO anode; a cathode such as a LiFePO₄, L1C0O2, Sulfur, Ag, Carbon-Air, Carbon-Water cathode; ; a separator system comprising two high mechanical strength layers having complementary patterns of apertures, three low ionic resistance layers; and a solid electrolyte layer, such as a LISICON or PEO layer. The overall

electrochemical cell geometry in Figure 10I is similar to that shown in Figures 10B, 10C and 10D, wherein a first low ionic resistance layer, such as a very porous layer (e.g., > 80%), is provided between the anode and a first high mechanical strength layer and a second low ionic resistance layer, such as a very porous layer (e.g., > 80%), is provided between the first high mechanical strength layer and a second high mechanical strength layer, and a third low ionic resistance layer, such as a very porous layer (e.g., > 80%), is provided between the second high mechanical strength layer and the cathode, and wherein a solid electrolyte layer, such as a LISICON layer, is provided between the third low ionic resistance layer and the cathode such that ions are able to be transported to the cathode surface. In the electrochemical cell of Figure 101, however, the high mechanical strength layers are mechanically, chemically and heat resistant

electronically insulating layers exhibiting a super-elasticity and/or shape memory effect such as a perforated shape memory polymer layer. Similar to the discussion in connection with Figure 10B, incorporation of the solid electrolyte layer (e.g., LISICON or PEO layer) is useful to protect the cathode, for example, to protect against unwanted chemical reactions with the cathode surface and components of the electrochemical cell, such as electrolyte components other than the solid electrolyte. In some

embodiments, the solid electrolyte layer (e.g., LISICON or PEO layer) provides a chemical barrier layer separating a first side of the electrochemical cell having a first electrolyte from a second side of the electrochemical cell having a second electrolyte that is different from the first electrolyte, and, therefore, may provide a means for integrating two separate electrolytes each tailored specifically for selected anode and cathode compositions.

[00144] Figure 10J provides a schematic diagram providing a cross sectional view of an electrochemical cell having a separator wherein the conductive side of the separator reduces anode loss such as in silicon large deformations upon cycling which breaks the electronic contact between anode particles and the current collector and deteriorate the performance of the electrochemical cell. The electrochemical cell comprises an anode, such as a silicon anode; a cathode, such as a LiFePO₄ or LiCoO₂ cathode; and a separator system comprising two high mechanical strength layers having complementary patterns of apertures and three low ionic resistance layers. The overall electrochemical cell geometry in Figure 10J is similar to that shown in Figure 10F, wherein a first low ionic resistance layer, such as a very porous layer (e.g., > 80%), is provided between the anode and a first high mechanical strength layer and a second low ionic resistance layer, such as a very porous layer (e.g., > 80%), is provided between the first high mechanical strength layer and a second high mechanical strength layer, and a third low ionic resistance layer, such as a very porous layer (e.g., > 80%), is provided between the second high mechanical strength layer and the cathode. In the electrochemical cell of Figure 10J, however, the first high mechanical strength layer comprises a mechanically, chemically and heat resistant ionically conductive and electrically conductive layer positioned proximate to the anode, such as a perforated metal layer; and the second high mechanical strength layer comprises a mechanically, chemically and heat resistant nonconductive perforated layer positioned proximate to the cathode, such as a perforated Kapton layer.

[00145] Figure 10K provides a schematic diagram providing a cross sectional view of an electrochemical cell having a separator wherein the conductive side of the separator next to the anode reduces anode loss such as in silicon large deformations upon cycling which breaks the electronic contact between anode particles and the current collector and deteriorate the performance of the electrochemical cell. In an embodiment of this aspect, the conductive side next to the cathode increases the electronic conductivity of the cathode which can result in longer life cycle, higher power and thicker cathode, and higher energy cathode and thus a better electrochemical cell. The electrochemical cell comprises an anode, such as a silicon anode; a cathode, such as a LiFePO or LiCoO₂ cathode; and a separator system comprising thee high mechanical strength layers having complementary patterns of apertures and three low ionic resistance layers. As shown in Figure 10K a first low ionic resistance layer, such as a very porous layer (e.g., > 80%), is provided between the anode and a first high mechanical strength layer, a second low ionic resistance layer, such as a very porous layer (e.g., > 80%), is provided between the first high mechanical strength layer and a second high mechanical strength layer, a third low ionic resistance layer, such as a very porous layer (e.g., > 80%), is provided between the second and third high mechanical strength layers. In the electrochemical cell of Figure 10K, the first and third high mechanical strength layers positioned proximate to anode and cathode, respectively, comprises a mechanically, chemically and heat resistant layers, such as a perforated metal layers; and the second high mechanical strength layer provide between said first and second high mechanical strength layers comprises a mechanically, chemically and heat resistant electronically insulating and ionically conductive layer, such as a perforated Kapton layer.

[00146] Figures 1 1A and 1 1 B provide examples of the designs of porous, patterned layers of the some separator systems of the invention, such as layers F in Figures 2 - 10. In the embodiments shown in Figure 1 1A and 1 1 B, for example, there are alternating porous regions (schematically shown as dotted regions) and solid regions (schematically shown as filled-in regions). In these embodiments, the layer(s) R may provide the reverse patterned of apertures of the designs of the layers F. In Figure 1 1 A and 1 1 B, the pattern is characterized by alternating rectangular porous regions and solid regions.

EXAMPLE 2: High Performance Inexpensive Rechargeable Lithium Batteries:

Engineering the Separator and Electrodes

[00147] The highest energy batteries known so far use metals such as zinc and lithium, which are inexpensive, and have very high energy/power densities. Meanwhile, recharging these batteries poses major safety hazards. A requirement for mitigating the safety problems is very strong yet highly conductive separators that can resist dendrite formation, accidents and thermal runaway.

[00148] Using engineering methods in building separators and electrodes, the separator systems of this example provide a significant improvement of safety, durability, power and energy performance in a variety of battery chemistries. One approach of the invention is to apply engineering knowledge and methods to the most efficient chemistries used in the battery industry. As shown in this example, the invention provides manufacturing friendly methods to make ultra-safe, high-capacity separators. Coin cells made of commercial lithium metal, LiFePO₄ and the present separator systems demonstrate conductivities comparable to conventional Celgard separators, the mechanical strength of solids and a working temperature range of - 40 to 200 Celsius. The separator systems of this example can be an essential part of Li- Sulfur, Li-air, Zn-Manganese or Zn-air batteries.

[00149] A goal of certain aspects of the invention is to enhance rechargeability, safety and high cycle life of the existing non-rechargeable high-energy chemistries such as lithium metal and zinc batteries and provide advanced electrochemical systems for high-energy rechargeable metal-air batteries which provide economic solutions to energy storage challenges, especially in utility-scale batteries.

[00150] Current state of the art lithium metal batteries are not rechargeable, mostly due to dendrite formation which may result in internal shorts and in fires and explosions. At the same time, silicon as a potential high-energy anode undergoes very large shape changes and loses its electronic contact with the current collector, unless one uses very expensive nano-silicone grown carefully in preferred directions (not scalable). Many different electrolytes and additives have been tested and failed to be useful in an industrial level system. Recently, various solid electrolytes have been introduced to enhance the safety, but they have orders of magnitude lower conductivity compared to liquid electrolyte-separator systems, and lose their performance after very few cycles due to fatigue, cracks and lost electrode-electrolyte contacts.

[00151] Using a novel and scalable process, aspects of the invention provide highly porous separator systems (e.g., greater than or equal to than 10^~2 S/cm

conductivity with liquid electrolyte, at room temperature) with mechanically rigid materials (e.g., more than 1 GPa elastic modulus, and temperature range of -200 to 400 Celsius) that resist the growth of dendrites. Embodiments of the present separator systems provide a new device architecture that enables high-energy, low-cost utility- scale batteries for a variety of chemistries. Embodiments of the present separator systems also provide accident safe transportation batteries. Experimental results indicate, for example, batteries integrating the present separator systems may achieve more than 5,000 cycles with no or minimal capacity loss. In addition, some of the separator systems are able to be readily implemented into casting and roll-to-roll processing methodologies, already used in current lithium battery manufacturing.

[00152] An important feature of certain embodiments of the invention is a multilayer separator system that provides high conductivity and high safety at the same time. Figure 12 provides a schematic diagram of a cross sectional view of an

electrochemical cell including a separator system of the invention. As shown in Figure 12, the electrochemical cell comprises anode (3) and cathode (4) separated from each other by a separator system (5). In this embodiment, the separator system (5) comprises a plurality of layers including perforated layers (1 and 1 ') comprising a strong material and having a pattern of apertures and frame and/or very porous layers (2). The high elastic modulus of the perforated layers of the separator material prevents dendrites from directly piercing the barrier. Figure 14 provides examples of patterns of apertures useful in the perforated layers of separator systems of the invention. As shown in Figure 14, perforated layers of the separator systems may have apertures with circular shapes. Figure 14 also illustrates complementary patterns for perforated layers useful for preventing dendrite growth, shorting and mechanical failure. For example, panels A and B provide complementary patterns of apertures which do not overlap when provided in the off-set alignment of certain separator systems. Panel C provides a schematic illustrating the superposition of the patterns in panels A and B showing that the off-set alignment results in no overlap of the apertures. Similarly, panels F and G provide complementary patterns of apertures which do not overlap when provided in the off-set alignment of certain separator systems. Similarly, panels H and I provide complementary patterns of apertures which do not overlap when provided in the off-set alignment of certain separator systems. Similarly, panels J and K provide

complementary patterns of apertures which do not overlap when provided in the off-set alignment of certain separator systems. Similarly, panels L and M provide

complementary patterns of rectangular apertures which do not overlap when provided in the off-set alignment of certain separator systems.

[00153] The large number of apertures in the perforated layer ensures high conductivity of the separator and the offset alignment of the pores in the successive layers ensures that there is no direct path between the electrodes. The force from the high mechanical strength layers on the dendrites slows down or stops the dendrite growth. In an electrochemical cell this significantly improves the performance of the cell. Figure 13 provides a schematic diagram illustrating a potential trajectory of dendrite growth in an electrochemical system of the invention. In this figure, the dendrite is shown as a curved line extending from anode to cathode. As shown in Figure 13, dendrites would have to make several curvatures to pass through the perforated layers and create a short. From a strictly mechanical view, the elastic modulus of lithium (5GPa) is orders of magnitude too high to allow successive curvatures of dendrites in a small length (less than 0.1 mm); the required energy to bend a straight beam is

u =

where E is the elastic modulus, I is the moment of inertia, and R(x) is the radius of the curvature at each point, finally, L is the length of the element. From a chemical engineering standpoint, the dendrites have too much kinetic frustration to overcome such a convoluted growth path. The layered separator system including perforated layers having complementary patterns of apertures effectively prevents dendrite fornnation and therefore prevents shorts. The materials and fabrication methods necessary for such a composite separator system are compatible with the present battery fabrication infrastructure, allowing low-cost implementation into current battery manufacturing. The invention provides cost-effective, safe and high-energy lithium batteries well suited for load leveling in a power grid with very slow charging (e.g., C/10) and very fast discharging (e.g., 4C). The invention also provides a process of making layered separators resulting in industrially friendly batteries characterized by the conductivity of liquid electrolytes, the safety of solid electrolytes, high cycle life and low cost.

[00154] The electrochemical systems of the invention are also compatible with the use of engineered electrodes such as pre-stressed electrodes. Lithium metal when compressed in an out-of-plane direction performs significantly better by leveling its surface (less mossy and less dendrites). Also, out-of-plane compression in silicon anodes results in much better contacts with the current collectors and much higher life cycle. This aspect of the invention can also be helpful in solid state batteries by maintaining a good contact between the electrodes and the solid electrolyte and increasing the cycle life and performance.

[00155] To further demonstrate the beneficial attributes of the present invention, over 100 coin-cells incorporating a composite layer separator system have been made and evaluated. Some of the tested separators are currently 0.125mm thick and keep 75% capacity at C/2 compared to 0.025 mm Celgard. Safety tests including blunt nail and high current cycling, 55 mA/cm2 for 300 cycles, show that the separator system is robust and the battery does not internally short. Furthermore, there is no measurable degradation or capacity loss after several hundred cycles, in contrast to 5-layer Celgard separators (0.125mm thick) which were completely destroyed. The invention includes separator systems having an overall thickness of 0.075 mm. The invention includes 0.025mm thick rolls of the separator system useful for 10kWh packs of cylindrical 18650 lithium metal batteries with 400 Wh/kg energy and 5000 cycles.

[00156] Grid level energy storage is currently dominated by pumped hydro, over 99% of current storage, which is only possible at a very few limited sites and

applications, is not suitable for society's growing storage needs. Other solutions have significant shortcomings. Compressed air technology suffers from very low round trip efficiency of less than 20%. Electrochemical capacitors and flywheels have very low energy/cost ratios. Flow batteries, used as a combination of high-power and high- energy, are very complicated and expensive. Current batteries also suffer from high cost/energy and cost/power ratios (at about $1/Wh). The state-of-the-art high energy lithium-metal, metal-air, and nano-silicon chemistries have major safety/cost problems as mentioned earlier.

[00157] In some embodiments, the separator-electrodes design of the invention enables a range of rechargeable high-energy chemistries that are currently not considered safe and/or have short cycle life. Using industrial methods of manufacturing (e.g., CNC, molding, casting) the invention combines electrochemistry with engineering to address safety issues with state of the art battery technologies. The present separator systems combined with high-energy electrodes, provide safe, long cycle life, high energy batteries at industrial scale for grid storage and also electric vehicles.

[00158] The present systems and methods are scalable and industrially friendly. Enhancing separator performance may be achieved via several approaches amenable with the present systems and methods. Improving the conductivity by making smaller holes (0.010 to 0.100 mm) and using thinner layers (0.005 mm) are useful approaches for accessing high performance systems. In addition, maintaining the required offset alignment and attaching the layers by thermal heating at the boundaries and other selected areas may be used to access separator systems providing enhanced safety.

[00159] Figure 15 provides a plot of charge and discharge capacities (mAh/g) as a function of number of cycles for an electrochemical cell having: (A) a multilayer separator system of the invention having an overall thickness of 125 microns and (B) a Celgard separator having a thickness of 25 microns. The CR2032 coincell evaluated is made of Li foil 0.5mm thick anode, LiFePO4 (0.0142g) cathode, 1 M LiPF6 in

EC:DEC:DMC (1 :1 :1 ). The voltage limits are 3v (discharge) and 4v (charge). Formation, 3 cycles at C/24, and the C/2 cycling are distinguishable from the sharp drop in the capacity. The top line shows a separator made with two perforated Kapton layers as mechanical strong layers and 3 perforated Celgard 2325 layers as low resistance layers. The bottom line shows a separator made with two perforated Kapton layers as mechanical strong layers and 3 Celgard 2325 layers as low resistance layers. The cells are tested in room temperature. No measurable capacity drop was observed after 40-50 cycles. The experimental results shown in Figure 15 indicate that the present separators provide low resistance, and thus, are compatible with a range of electrochemical systems.

[00160] Figure 16 provides a plot of charge and discharge capacities (mAh/g) as a function of number of cycles for: (A) an electrochemical cell having a multilayer separator system of the invention, a Li metal anode and a UC0O₂ cathode as compared to (B) an electrochemical cell having a conventional separator. The electrochemical cells were coin cells and evaluated at a discharge rate of C/2. The CR2032 coincell evaluated is made of Li foil, 0.5mm thick anode, LiCoO₂, 0.1 mm thick cathode, 1 M LiPF6 in EC:DEC:DMC (1 :1 :1 ). The voltage limits are 3v (discharge) and 4.2v (charge). Formation, 5 cycles at C/24, and the C/2 cycling are distinguishable from the sharp drop in the capacity. The red lines (indicated by the letter B), 1 , 5, 6 show cells made with a separator made with two perforated Kapton layers (2mm diameter holes) as mechanical strong layers and 3 Celgard 2325 layers as low resistance layers. The blue lines

(indicated by the letter A), 2, 3 show a reference electrode made with a perforated Kapton between two Celgard layers. The cells are tested in room temperature. The cells were cycled at C/2 and then were cycled at C/24 for a few cycles and then again at C/2. The experimental results show that the capacity loss was not due to any chemical reactions in the cell, and were likely due to the resistance of the perforated Kapton layers in the electrochemical cells evaluated. Figure 16 shows that a homogenous distribution of holes, and thus smaller holes, are necessary to reach a good capacity in the cell under some experimental conditions.

[00161] Figure 17 provides a plot of charge and discharge capacities (mAh/g) as a function of number of cycles for: (A) an electrochemical cell having a multilayer separator system of the invention, a Li metal anode and a LiFePO cathode as compared to (B) an electrochemical cell having a conventional separator having a thickness of 75 microns and (c) a Celgard separator having a thickness of 25 microns. The electrochemical cells were coin cells and evaluated at a discharge rate of C/2. The CR2032 coincell evaluated is made of Li foil, 0.5mm thick anode, LiFePO4, 0.1 mm thick cathode, 1 M LiPF6 in EC:DEC:DMC (1 :1 :1 ). The voltage limits are 3v (discharge) and 4v (charge). Formation, 5 cycles at C/24, and the C/2 cycling are distinguishable from the sharp drop in the capacity. The lines I, H show cells made with single Celgard layers. The lines, A, B, C, show cells with a separator made with two perforated Kapton layers as mechanical strong layers and 3 Celgard 2325 layers as low resistance layers. The lines F and D, show a reference electrode made with a perforated Kapton between two Celgard layers. The cells are tested in room temperature. The test demonstrate the importance of having thin separators to reach high capacity in the cells.

[00162] Figure 18 provides a schematic diagram illustrating an electrochemical cell of the invention having a multilayer separator comprising three high mechanical strength layers with complementary patterns of apertures, an anode and a cathode. Figure 19 provides a schematic diagram illustrating the trajectory of Li⁺ ions passing through the multilayer separator shown in Figure 18. While Li⁺ ions are able to efficiently pass through the multilayer separator as shown in Figure 19, dendrites are not able to make the same trajectory and, thus are prevented in certain embodiments of the invention. Further, the force from the high mechanical strength layers slows down or even stops the dendrite growth.

[00163] Figure 20 provides a plot of cell voltage (V vs Li) versus cycling time (h) for the galvanostatic lithium stripping from two symmetrical (5/9)" lithium chips.

[00164] Figure 22 shows the current [amper] vs. time [s] (top plot) and voltage [v] vs. time [s] (bottom plot) for the experiment of Figure 15. This shows the top red line.

[00165] Figures 23 - 30 provide photographs of perforated layers useful in separator systems of some embodiments. Figure 23, for example, provides pictures of the different separator materials (5-Celgard separator: a) and new separator b) - d) after cycling a few days at high current: a) 5-Celgard separator (from top-left to bottom-right: Li+Celgard, Li+Celgard, Stainless steel current collector; b) Celgard layer between the two perforated Kapton layers; c) Celgard in contact with the lithium electrode; d) perforated Kapton. Figure 24, for example, provides pictures of: Top) A typical separator (Celgard) punctured by lithium dendrites and destroyed. As can be seen the separator is not recognizable anymore. Bottom) Lithium dendrites could not penetrate the new separator. Shown here, a Kapton layer of the new separator is intact, though the Celgard on the right side of the Kapton layer is destroyed. Figures 25 and 26, for example, are pictures of a 1 mil kapton film prepared with laser cutting for use in a separator system of the invention.

[00166] Figure 23 shows the layers of a novel separator (0.125 mm thick) made with 2 Kapton layers as the high strength layers and 3 Celgard layers next to them as low resistance layers in comparison with 5 Celgard layers (0.125mm thick) as a reference separator in a house made cell of ½" diameter. Celgard 2325 is used. The cells are made with 0.75mm Li foils as electrodes and 1 M LiPF6 in EC:DEC:DMC (1 :1 :1 ) from Novolte, as electrolyte. The Kapton holes are each 2mm diameter. Cells are tested at room temperature and are cycled at 55 mA for 45 minute charge-discharge cycles in an Argon-filled dry box (H2O <0.5 ppm) (a) Reference separator: shows 5- Celgard reference separator: the cell is shorted; (b) shows the new separator. The cell is not shorted. (b1 ) New separator: Celgard in contact with the lithium electrode shows severe damage; (b2) new separator: Celgard layer between the two perforated Kapton layers is intact; (b3) new separator: perforated Kapton is intact and maintains its structural integrity, preventing any short. This figure shows that the multilayered separator can safely stop dendrite shorting and prevent catastrophic failure even at very high currents. Figure 24 (zoom out) is the same as figure 23 (zoom in). The top and bottom graphs show two adjacent layers in each design. Figure 25-30 show several examples of the strong layer design made of Kapton. The holes are made with Laser cutting. The size of each of the layers is ½ inch. The holes are 1 mm diameter and 2 mm diameter. Figure 21 provides plots of the current [milliA mper] vs. time [hr] and voltage vs Li [v] vs. time [hr].

EXAMPLE 3: Lithium Batteries Having a Multilayer Separator System

[00167] This Example provides description of examples of lithium batteries comprising a multilayer separator system of the present invention.

[00168] Example A: In this example, two layers of Kapton films, each 25 micrometers thick, are used for the separator system. Each layer is perforated with Cartesian (vertical-horizontal) periodic holes, each 1 mm diameter, and with 1 mm distance between the walls. A layer of Celgard 25 micrometers is placed in between the two Kapton layers. A layer of Celgard 25 micrometers is placed in between each Kapton layer and the adjacent electrode. The electrodes are L1C0O2 and Lithium metal films. The electrolyte is LiPF₆ in a combination of EC-DMC-PC-DME.

[00169] Example B: In this example, two layers of Kapton films, each 25 micrometers thick, are used for the separator system. Each layer is perforated with Cartesian (vertical-horizontal) periodic holes, each 1 mm diameter, and with 1 mm distance between the walls are used for the separator system. A layer of Celgard, 25 micrometers, is placed in between the two Kapton layers. A layer of Celgard 25 micrometers is placed in between each Kapton layer and the adjacent electrode. The electrodes are LiFePO₄ and Lithium metal films. The electrolyte is LiPF₆ in a combination of EC-DMC-PC-DME.

[00170] Example C: In this example, two layers of Kapton films, each 25 micrometers thick, are used for the separator system. Each layer is perforated with Cartesian (vertical-horizontal) periodic holes, each 1 mm diameter, and with 1 mm distance between the walls are used for the separator system. A layer of perforated Celgard, 25 micrometers thick with 3 holes each 1/8 inch, is placed in between the two Kapton layers. A layer of perforated Celgard, 25 micrometers thick with 3 holes each 1/8 inch, is placed in between each Kapton layer and the adjacent electrode. The electrodes are LiFePO₄ and Lithium metal films. The electrolyte LiPF₆ in is a combination of EC- DMC-PC-DME.

[00171] Example D: In this example, two layers of Kapton films, each 25 micrometers thick and 3/4 inch diameter, are used for the separator system. Each layer is perforated with Cartesian (vertical-horizontal) periodic holes, each 1 mm diameter, and with 1 mm distance between the walls. A ring of Celgard, 25 micrometers thick, is placed in between the two Kapton layers. A ring of Celgard, 25 micrometers thick and 3/4 inch outside diameter and 1/2 inch inside diameter, is placed in between each Kapton layer and the adjacent electrode. The electrodes are LiFePO₄ and Lithium metal films. The electrolyte is LiPF₆ in a combination of EC-DMC-PC-DME.

[00172] Example E: In this example, two layers of Kapton films, each 5

micrometers thick and 3/4 inch diameter, are used for the separator system. Each layer is perforated with Cartesian (vertical-horizontal) periodic holes, each 1 mm diameter, and with 1 mm distance between the walls. A ring of Celgard, 5 micrometers thick, is placed in between the two Kapton layers. A ring of Celgard, 5 micrometers thick and 3/4 inch outside diameter and 1/2 inch inside diameter, is placed in between each Kapton layer and the adjacent electrode. The electrodes are LiFePO₄ and Lithium metal films. The electrolyte is LiPF₆ in a combination of EC-DMC-PC-DME.

[00173] Example F: In this example, two layers of stainless steel, each 5 micrometers thick, are used. The steel layers are coated with a very thin electronically isolating layer (here 1 micrometer thick Teflon. Kapton can be used too). Each layer is perforated with Cartesian (vertical-horizontal) periodic holes, each 0.5 mm diameter, and with 0.5 mm distance between the walls. A layer of Celgard, 5 micrometers, is placed in between the two stainless steel layers. A layer of Celgard 5 micrometers is placed in between each stainless steel layer and the adjacent electrode. The electrodes are LiFePO₄ and Lithium metal films. The electrolyte is LiPF₆ in a combination of EC- DMC-PC-DME.

[00174] Example G: In this example, two layers of Kapton films, each 5 micrometers thick and 3/4 inch diameter, are used for the separator system. Each layer is perforated with Cartesian (vertical-horizontal) periodic holes, each 1 mm diameter, and with 1 mm distance between the walls. A ring of Celgard, 5 micrometers thick, is placed in between the two Kapton layers. A ring of Celgard, 5 micrometers thick and 3/4 inch outside diameter and 1/2 inch inside diameter, is placed in between the Kapton layer next to lithium metal film anode and the Li electrode. A LISICON layer, 25 micrometer thick and ¾ inch diameter is placed between the second Kapton and the air carbon- cathode. The electrolyte on the Li side of the LISICON is LiCIO in a combination of EC- DMC-PC-DME. The electrolyte on the air cathode side of LISICON is an aqueous electrolyte.

[00175] Example H: In this example, two layers of PE films, each 5 micrometers thick and 3/4 inch diameter are used for the separator system. Each layer is perforated with Cartesian (vertical-horizontal) periodic holes, each 0.1 mm diameter, and with 0.1 mm distance between the walls. A LISICON layer, 25 micrometer thick and ¾ inch diameter is placed between the second PE and the air carbon-cathode. The electrolyte on the Li side of the LISICON is LiPF6 in a combination of EC-DMC-PC-DME. The electrolyte on the air cathode side of LISICON is an aqueous electrolyte.

[00176] Example I: In this example, two layers of stainless steel, each 5 micrometers thick, are used. The steel layers are coated with a very thin electronically isolating layer (here 1 micrometer thick Teflon) on the inside faces (sides against the closer electrode). Each layer is perforated with Cartesian (vertical-horizontal) periodic holes, each 0.1 mm diameter, and with 0.1 mm distance between the walls. A layer of Celgard, 5 micrometers, is placed in between the two stainless steel layers. A layer of Celgard 5 micrometers is placed in between each stainless steel layer and the adjacent electrode. The electrodes are partially lithiated Si and partially lithiated sulfur. The battery with this separator is expected to show higher cycle life and charge-discharge (power) rates.

[00177] Example J: In this example, two layers of stainless steel, each 5 micrometers thick, are used. The steel layers are coated with a very thin electronically isolating layer of 1 micrometer thick Teflon on the inside surfaces (the sides against the closer electrodes) and with a 1 micrometer thick polyethylene glycol on the outside surface (the sides facing the closer electrodes). Each layer is perforated with Cartesian (vertical-horizontal) periodic holes, each 0.1 mm diameter, and with 0.1 mm distance between the walls. A layer of cellulose separator, 5 micrometers, is placed in between the two stainless steel layers. A layer of cellulose separator, 5 micrometers, is placed in between each stainless steel layer and the adjacent electrode. The electrodes are Li metal and sulfur. It is expected that the polyethylene glycol coating increases the cycle life of the battery.

[00178] Example K: In this example, two layers of Kapton films, each 5

micrometers thick and 3/4 inch diameter, are used for the separator system. Each layer is perforated with Cartesian (vertical-horizontal) periodic holes, each 0.1 mm diameter, and with 0.1 mm distance between the walls. A ring of Celgard, 5 micrometers thick, is placed in between the two Kapton layers. A ring of Celgard, 5 micrometers thick and 3/4 inch outside diameter and 1/2 inch inside diameter, is placed in between each Kapton layer and the adjacent electrode. The electrodes are Zinc anode and carbon based air cathode. The electrolyte is aqueous 6M KOH.

[00179] Example L: In this example, two layers of PP films, each 5 micrometers thick and 3/4 inch diameter, are used for the separator system. Each layer is perforated with Cartesian (vertical-horizontal) periodic holes, each 0.1 mm diameter, and with 0.1 mm distance between the walls. The electrodes are Zinc anode and carbon based air cathode. The electrolyte is aqueous 6M KOH.

[00180] Example M: In this example, two layers of Kapton films, each 5

micrometers thick and 3/4 inch diameter, are used for the separator system. Each layer is perforated with an arbitrary pattern of holes that are each 40% porous and when put on top of each other give less than 5% overlap of the hole patterns, each 0.1 mm diameter, and with 0.1 mm distance between the walls. A ring of Celgard, 5 micrometers thick, is placed in between the two Kapton layers. A ring of Celgard, 5 micrometers thick and 3/4 inch outside diameter and 1/2 inch inside diameter, is placed in between each Kapton layer and the adjacent electrode. The electrodes are Zinc anode and carbon based air cathode. The electrolyte is aqueous 6M KOH.

[00181] Example N: In this example, two layers of Kapton films, each 25 micrometers thick and 3/4 inch diameter, are used for the separator system. Each layer is perforated with an arbitrary pattern of holes that are each 40% porous and when put on top of each other give less than 5% overlap of the hole patterns, each 1 mm diameter, and with 1 mm distance between the walls. A ring of Celgard, 25 micrometers thick, is placed in between the two Kapton layers. A ring of Celgard, 25 micrometers thick and 3/4 inch outside diameter and 1/2 inch inside diameter, is placed in between each Kapton layer and the adjacent electrode. The electrodes are LiFePO₄ and Lithium metal films. The electrolyte is LiPF6 in a combination of EC-DMC-PC-DME.

[00182] Example O: In this example, two layers of Kapton films, each 5

micrometers thick and 3/4 inch diameter, are used for the separator system. Each layer is perforated with Cartesian (vertical-horizontal) periodic holes, each 0.01 mm diameter, and with 0.01 mm distance between the walls. A ring of Celgard, 5 micrometers thick, is placed in between the two Kapton layers. A ring of Celgard, 5 micrometers thick and 3/4 inch outside diameter and 1/2 inch inside diameter, is placed in between each Kapton layer and the adjacent electrode. The electrodes are LiFePO₄ and Lithium metal films. The electrolyte is LiPF6 in a combination of EC-DMC-PC-DME.

[00183] Example P: In this example, two layers of Kapton films, each 5

micrometers thick and 3/4 inch diameter, are used for the separator system. Each layer is perforated with Cartesian (vertical-horizontal) periodic holes, each 0.001 mm diameter, and with 0.001 mm distance between the walls. A ring of Celgard, 5 micrometers thick, is placed in between the two Kapton layers. A ring of Celgard, 5 micrometers thick and 3/4 inch outside diameter and 1/2 inch inside diameter, is placed in between each Kapton layer and the adjacent electrode. The electrodes are LiFePO₄ and Lithium metal films. The electrolyte is LiPF6 in a combination of EC-DMC-PC-DME.

[00184] Example Q. same as any of the above examples when the layers are attache to each other by PEO and PvDFat some areas such as the outer part of each side.

[00185] Example R corresponds to Example G when the LISICON is 5

micrometers and is deposited on the Kapton layer on the air cathode side of the lithium- air cell.

[00186] In another Example, the porous patterned layers have the following physical dimensions, compositions and mechanical properties: • Thickness: 125 micron, 75 micron, 50 micron or 25 microns.

• Tensile strength: 150 MPa isotropic (Celgard: 15 MPa TD; 150 MPA MD)

• Porosity: 45%

• Elastic modulus: 2GPa

• Yield strength: 50 MPa

• Density: ~1 .3 g/cm³

• MIT Folding Endurance: 10000 cycles

• Elmendorf tear strength: 0.1 N

• Graves tear strength: 15 N

• Impact strength: 50 N.cm

• 30 mins @ 150Celsius Shrinkage: 0.2 (Celgard: 5-10%)

• Dielectric Strength ASTM D-149-91 : 250 V/m

• Dielectric constant: 3.5

• Thermal coefficient of expansion: 20 ppm/Celsius.

[00187] Electrochemical cells comprising multilayer separators having porous patterned layers with these properties exhibit useful performance characteristics. When tested a half cell [coin cells]: LiFePO₄|LP71 |Li, for example, after 200 cycles: @ C/5 the capacity was -140 mAh/g; @C/2 -120 mAh/g. Force-displacement testing using external pressure showed that the cell did not short but stopped functioning. Analysis of the separator system after 300 cycles at C/2 showed little to no degradation and the separator system was able to be used in another cell.

[00188] Tables 1 and 2 provides summary of the physical dimensions and properties of high mechanical strength layers and separator systems of certain embodiments of the invention. Table 1 : Physical dimensions and properties of the high mechanical strength layers

Table 2: Physical dimensions and properties of the separator systems

[00189] The resistivities of the separators were tested in 1 M LiPF₆ EC:EMC (30:70 by volume. For electrochemical evaluation, ½" coincell electrochemical cells with AI-AI electrodes were used to characterize the separators. The separators are made as celgard/perforated Kapton/celgard/perforated kapton/celgard, each 25 μηη thick.

Example 4: Separators Comprising Coated Metal Mesh

[00190] In some aspects, separator systems of the invention comprise one or more porous patterned layers that are a coated metal layer, such as a metal mesh having an external insulating coating. Embodiments of this aspect are beneficial for increasing the life of a battery significantly. In an embodiment, for example, the metal mesh (Al, nickel, copper, stainless steel) has very high mechanical strength over a very wide temperature range; the metal separator is a thermally conductive material that homogenizes the temperature of the cell and significantly enhances the safety and the life of the cell. In an embodiment, the microporous layers of the separator are PTFE coated aluminum mesh layers (e.g. Al mesh, 40% opening: 3 layers, 5 micrometers each or 2 layers 1/3 mil each; in one embodiment, Al layers are coated with PTFE, e.g. 2 micrometers thick on each side. In another embodiment only the Al layer next to the anode is coated. In an another embodiment, the Al layers are coated and the sides are provided in contact with the electrodes.

STATEMENTS REGARDING INCORPORATION BY REFERENCE AND VARIATIONS

[00191] All references throughout this application, for example patent documents including issued or granted patents or equivalents; patent application publications; and non-patent literature documents or other source material; are hereby incorporated by reference herein in their entireties, as though individually incorporated by reference, to the extent each reference is at least partially not inconsistent with the disclosure in this application (for example, a reference that is partially inconsistent is incorporated by reference except for the partially inconsistent portion of the reference).

[00192] The terms and expressions which have been employed herein are used as terms of description and not of limitation, and there is no intention in the use of such terms and expressions of excluding any equivalents of the features shown and described or portions thereof, but it is recognized that various modifications are possible within the scope of the invention claimed. Thus, it should be understood that although the present invention has been specifically disclosed by preferred embodiments, exemplary embodiments and optional features, modification and variation of the concepts herein disclosed may be resorted to by those skilled in the art, and that such modifications and variations are considered to be within the scope of this invention as defined by the appended claims. The specific embodiments provided herein are examples of useful embodiments of the present invention and it will be apparent to one skilled in the art that the present invention may be carried out using a large number of variations of the devices, device components, methods steps set forth in the present description. As will be obvious to one of skill in the art, methods and devices useful for the present methods can include a large number of optional composition and processing elements and steps.

[00193] All patents and publications mentioned in the specification are indicative of the levels of skill of those skilled in the art to which the invention pertains. References cited herein are incorporated by reference herein in their entirety to indicate the state of the art, in some cases as of their filing date, and it is intended that this information can be employed herein, if needed, to exclude (for example, to disclaim) specific

embodiments that are in the prior art. For example, when a compound is claimed, it should be understood that compounds known in the prior art, including certain compounds disclosed in the references disclosed herein (particularly in referenced patent documents), are not intended to be included in the claim.

[00194] When a group of substituents is disclosed herein, it is understood that all individual members of those groups and all subgroups and classes that can be formed using the substituents are disclosed separately. When a Markush group or other grouping is used herein, all individual members of the group and all combinations and subcombinations possible of the group are intended to be individually included in the disclosure. As used herein, "and/or" means that one, all, or any combination of items in a list separated by "and/or" are included in the list; for example "1 , 2 and/or 3" is equivalent to "Ί ' or '2' or '3' or Ί and 2' or Ί and 3' or '2 and 3' or Ί , 2 and 3"'.

[00195] Every formulation or combination of components described or exemplified can be used to practice the invention, unless otherwise stated. Specific names of materials are intended to be exemplary, as it is known that one of ordinary skill in the art can name the same material differently. One of ordinary skill in the art will appreciate that methods, device elements, starting materials, and synthetic methods other than those specifically exemplified can be employed in the practice of the invention without resort to undue experimentation. All art-known functional equivalents, of any such methods, device elements, starting materials, and synthetic methods are intended to be included in this invention. Whenever a range is given in the specification, for example, a temperature range, a time range, or a composition range, all intermediate ranges and subranges, as well as all individual values included in the ranges given are intended to be included in the disclosure.

[00196] It must be noted that as used herein and in the appended claims, the singular forms "a", "an", and "the" include plural reference unless the context clearly dictates otherwise. Thus, for example, reference to "a cell" includes a plurality of such cells and equivalents thereof known to those skilled in the art, and so forth. As well, the terms "a" (or "an"), "one or more" and "at least one" can be used interchangeably herein. It is also to be noted that the terms "comprising", "including", and "having" can be used interchangeably. The expression "of any of claims XX- YY" (wherein XX and YY refer to claim numbers) is intended to provide a multiple dependent claim in the alternative form, and in some embodiments is interchangeable with the expression "as in any one of claims XX- YY."

[00197] Unless defined otherwise, all technical and scientific terms used herein have the same meanings as commonly understood by one of ordinary skill in the art to which this invention belongs. Although any methods and materials similar or equivalent to those described herein can be used in the practice or testing of the present invention, the preferred methods and materials are now described. Nothing herein is to be construed as an admission that the invention is not entitled to antedate such disclosure by virtue of prior invention.

[00198] Whenever a range is given in the specification, for example, a range of integers, a temperature range, a time range, a composition range, or concentration range, all intermediate ranges and subranges, as well as all individual values included in the ranges given are intended to be included in the disclosure. As used herein, ranges specifically include the values provided as endpoint values of the range. As used herein, ranges specifically include all the integer values of the range. For example, a range of 1 to 100 specifically includes the end point values of 1 and 100. It will be understood that any subranges or individual values in a range or subrange that are included in the description herein can be excluded from the claims herein.

[00199] As used herein, "comprising" is synonymous with "including," "containing," or "characterized by," and is inclusive or open-ended and does not exclude additional, unrecited elements or method steps. As used herein, "consisting of excludes any element, step, or ingredient not specified in the claim element. As used herein,

"consisting essentially of does not exclude materials or steps that do not materially affect the basic and novel characteristics of the claim. Any recitation herein of the term "comprising", particularly in a description of components of a composition or in a description of elements of a device, is understood to encompass those compositions and methods consisting essentially of and consisting of the recited components or elements. The invention illustratively described herein suitably may be practiced in the absence of any element or elements, limitation or limitations which is not specifically disclosed herein. [00200] The terms and expressions which have been employed are used as terms of description and not of limitation, and there is no intention in the use of such terms and expressions of excluding any equivalents of the features shown and described or portions thereof, but it is recognized that various modifications are possible within the scope of the invention claimed. Thus, it should be understood that although the present invention has been specifically disclosed by preferred embodiments and optional features, modification and variation of the concepts herein disclosed may be resorted to by those skilled in the art, and that such modifications and variations are considered to be within the scope of this invention as defined by the appended claims.

Claims

We claim:

1 . A separator system for an electrochemical system comprising: a first high mechanical strength layer having a plurality of apertures extending entirely through said first high mechanical strength layer and provided in a first pattern; and a second high mechanical strength layer having a plurality of apertures extending entirely through said second high mechanical strength layer and provided in a second pattern; said second pattern having an off-set alignment relative to said first pattern such that an overlap of said apertures of said first high mechanical strength layer and said apertures of said second high mechanical strength layer along axes extending perpendicularly from said first high mechanical strength layer to said second high mechanical strength layer is less than or equal to 20%; wherein said first high mechanical strength layer and said second high

mechanical strength layer are positioned such that ions of an electrolyte provided in contact with the first high mechanical strength layer and said second high mechanical strength layer are able to be transported through the first high mechanical strength layer and said second high mechanical strength layer.

2. A separator system for an electrochemical system comprising: a first high mechanical strength layer having a plurality of apertures extending entirely through said first high mechanical strength layer and provided in a first pattern; a second high mechanical strength layer having a plurality of apertures extending entirely though said second high mechanical strength layer and provided in a second pattern, said second pattern having an off-set alignment relative to said first pattern such that an overlap of said apertures of said first high mechanical strength layer and said apertures of said second high mechanical strength layer along axes extending perpendicularly from said first high mechanical strength layer to said second high mechanical strength layer is less than or equal to 20%; and a third high mechanical strength layer having a plurality of apertures extending entirely through said third high mechanical strength layer and provided in a third pattern having the same spatial arrangement of apertures as said first pattern; wherein said first high mechanical strength layer, said second high

mechanical strength layer and said third high mechanical strength layer are positioned such that ions of an electrolyte provided in contact with said first high mechanical strength layer, said second high mechanical strength layer and said third high mechanical strength layer are able to be transported through the first high mechanical strength layer, said second high mechanical strength layer and said third high mechanical strength layer.

3. A separator system for an electrochemical system comprising: a first high mechanical strength layer having a plurality of apertures extending entirely through said first high mechanical strength layer and provided in a first pattern; a second high mechanical strength layer having a plurality of apertures extending entirely through said second high mechanical strength layer and provided in a second pattern, said second pattern having an off-set alignment relative to said first pattern such that an overlap of said apertures of said first high mechanical strength layer and said apertures of said second high mechanical strength layer along axes extending perpendicularly from said first high mechanical strength layer to said second high mechanical strength layer is less than or equal to 20%; a third high mechanical strength layer having a plurality of apertures extending entirely through said third high mechanical strength layer and provided in a third pattern having the same spatial arrangement of apertures as that of said first pattern; and a fourth high mechanical strength layer having a plurality of apertures extending entirely through said fourth high mechanical strength layer and provided in a fourth pattern having the same spatial arrangement of apertures as that of said second pattern; wherein said first high mechanical strength layer, said second high

mechanical strength layer, said third high mechanical strength layer and said fourth high mechanical strength layer are positioned such that ions of an electrolyte provided in contact with said first high mechanical strength layer, said second high mechanical strength layer, said third high mechanical strength layer and said fourth high mechanical strength layer are able to be transported through said first high mechanical strength layer, said second high mechanical strength layer, said third high mechanical strength layer and said fourth high mechanical strength layer.

4. A separator system for an electrochemical system comprising: a first high mechanical strength layer having a plurality of apertures extending entirely through said first high mechanical strength layer and provided in a first pattern; a second high mechanical strength layer having a plurality of apertures extending entirely through said second high mechanical strength layer and provided in a second pattern, said second pattern having an off-set alignment relative to said first pattern such that an overlap of said apertures of said first high mechanical strength layer and said apertures of said second high mechanical strength layer along axes extending perpendicularly from said first high mechanical strength layer to said second high mechanical strength layer is less than or equal to 40%; and a third high mechanical strength layer having a plurality of apertures extending entirely through said third high mechanical strength layer and provided in a third pattern; said third pattern having an off-set alignment relative to said first pattern and said second pattern such that an overlap of said apertures of said first high mechanical strength layer, said apertures of said second high mechanical strength layer and said apertures of said third high mechanical strength layer along axes extending perpendicularly from said first high mechanical strength layer or said second high mechanical strength layer to said third layer is less than or equal to 20%; wherein said first high mechanical strength layer, said second high

5. A separator system for an electrochemical system comprising: a first high mechanical strength layer having a plurality of apertures extending entirely through said first high mechanical strength layer and provided in a first pattern; a second high mechanical strength layer having a plurality of apertures extending entirely through said second high mechanical strength layer and provided in a second pattern, said second pattern having an off-set alignment relative to said first pattern such that an overlap of said apertures of said first high mechanical strength layer and said apertures of said second high mechanical strength layer along axes extending perpendicularly from said first high mechanical strength layer to said second high mechanical strength layer is less than or equal to 50%; a third high mechanical strength layer having a plurality of apertures extending entirely through said third high mechanical strength layer and provided in a third pattern; said third pattern having an off-set alignment relative to said first pattern and said second pattern such that an overlap of said apertures of said first high mechanical strength layer, said apertures of said second high mechanical strength layer and said apertures of said third high mechanical strength layer along axes extending perpendicularly from said first high mechanical strength layer or said second high mechanical strength layer to said third layer is less than or equal to 30%; and a fourth high mechanical strength layer having a plurality of apertures extending entirely through said fourth high mechanical strength layer and provided in a fourth pattern; said fourth pattern having an off-set alignment relative to said first pattern, said second pattern and said third pattern such that an overlap of said apertures of said first high mechanical strength layer, said apertures of said second high mechanical strength layer, said apertures of said third high mechanical strength layer and said apertures of said fourth high mechanical strength layer along axes extending perpendicularly from said first high mechanical strength layer or said second high mechanical strength layer to said fourth high mechanical strength layer is less than or equal to 20%; wherein said first high mechanical strength layer, said second high

6. The separator system of any of claims 1 -5, wherein the overlap of said apertures of two or more of said first pattern, said second pattern, said third pattern and said fourth pattern along said axes extending perpendicularly from said first high mechanical strength layer to said second high mechanical strength layer is less than or equal to 10%.

7. The separator system of any of claims 1 -6, wherein the overlap of said apertures of two or more of said first pattern, said second pattern, said third pattern and said fourth pattern along said axes extending perpendicularly from said first high mechanical strength layer to said second high mechanical strength layer is selected from the range of 0 to 5%.

8. The separator system of any of claims 1 -7, wherein the overlap of said apertures of two or more of said first pattern, said second pattern, said third pattern and said fourth pattern along said axes extending perpendicularly from said first high mechanical strength layer to said second high mechanical strength layer is equal to O.

9. The separator system of claim 4, wherein the overlap of said apertures of said first pattern, said second pattern, and said third pattern along said axes extending perpendicularly from said first high mechanical strength layer to said second high mechanical strength layer is less than or equal to 10%.

10. The separator system of claim 4, wherein the overlap of said apertures of said first pattern, said second pattern, and said third pattern along said axes extending perpendicularly from said first high mechanical strength layer to said second high mechanical strength layer is selected from the range of 0 to 5%.

1 1 .The separator system of claim 5, wherein the overlap of said apertures of said first pattern, said second pattern, said third pattern and said fourth pattern along said axes extending perpendicularly from said first high mechanical strength layer to said second high mechanical strength layer is less than or equal to 10%.

12. The separator system of claim 5, wherein the overlap of said apertures of said first pattern, said second pattern, said third pattern and said fourth pattern along said axes extending perpendicularly from said first high mechanical strength layer to said second high mechanical strength layer is selected from the range of 0 to 5%.

13. The separator system of any of claims 1 -12, wherein two or more of said first pattern, said second pattern, said third pattern and said fourth pattern comprise substantially complementary patterns.

14. The separator system of claim 13, wherein said substantially complementary patterns correspond to substantially negative images of one another.

15. The separator system of any of claims 1 -14, further comprising one or more low ionic resistance layers provided on a side of at least one of the first high mechanical strength layer, the second high mechanical strength layer, the third high mechanical strength layer and the fourth high mechanical strength layer.

16. The separator system of claim 15, wherein each of said one or more low ionic resistance layers is an electrolyte containing layer providing a reservoir for said electrolyte.

17. The separator system of any of claims 15-16, wherein each of said one or more low ionic resistance layers independently has an ionic resistance less than or equal to 20 ohm-cm².

18. The separator system of any of claims 15-17, wherein at least one of said one or more low ionic resistance layers is a pressure buffer providing space for an electrolyte provided between at least two of the first high mechanical strength layer, the second high mechanical strength layer, the third high mechanical strength layer and the fourth high mechanical strength layer.

19. The separator system of any of claims 15-18, wherein at least one of said high mechanical strength layers and said one or more low ionic resistance layers is a deposited layer that is deposited on at least one of said high mechanical strength layers and said one or more low ionic resistance layers.

20. The separator system of any of claims 15-19, wherein at least one of said high mechanical strength layers and said one or more low ionic resistance layers is a deposited layer that is deposited on an electrode of an electrochemical cell.

21 .The separator system of any of claims 15-20, wherein at least one of said one or more low ionic resistance layers is adhered by pressure, heat or chemical adhering to at least one side of any of the first high mechanical strength layer, the second high mechanical strength layer, the third high mechanical strength layer and the fourth high mechanical strength layer.

22. The separator system of any of claims 15-21 , wherein at least one of said one or more low ionic resistance layers is adhered by a resin polymer to at least one side of any of the first high mechanical strength layer, the second high

mechanical strength layer, the third high mechanical strength layer and the fourth high mechanical strength layer.

23. The separator system of any of claims 15-22, wherein at least one of said one or more low ionic resistance layers comprises a microporous material, a woven material, or a nonwoven material.

24. The separator system of any of claims 15-22, wherein at least one of said one or more low ionic resistance layers comprises a ceramic or a glass electrolye, a polymer electrolyte or a solid electrolyte.

25. The separator system of any of claims 15-22, wherein at least one of said one or more low ionic resistance layers comprises a perforated ceramic separator, a porous ceramic separator, a perforated glass separator, a porous glass separator, a perforated metal, a perforated alloy separator, a perforated rubber, a rubber mesh, a metal mesh or an alloy mesh.

26. The separator system of any of claims 15-25, wherein at least one of said one or more low ionic resistance layers comprises a ring or a frame having a central aperture.

27. The separator system of any of claims 15-26, wherein said one or more low ionic resistance layers comprise one or more frame layers in physical contact with at least one of said first high mechanical strength layer, the second high mechanical strength layer, the third high mechanical strength layer and the fourth high mechanical strength layer or wherein said one or more low ionic resistance layers comprise one or more frame layers in contact with at least one electrode of an electrochemical cell.

28. The separator system of claim 27, wherein said first high mechanical strength layer is provided between first and second frame layers and wherein said second high mechanical strength layer is provided between third and fourth frame layers.

29. The separator system of claim 27, wherein said first high mechanical strength layer is provided between first and second frame layers and wherein said second high mechanical strength layer is provided between second and third frame layers.

30. The separator system of any of claims 15-29, wherein said one or more low ionic resistance layers comprise one or more frame layers in contact with at least one of said electrodes of an electrochemical cell.

31 .The separator system of any of claims 15-30, wherein said one or more low ionic resistance layers comprise a spacer provided between said first and second layers, said spacer separating said first and second layers by a selected distance selected from the range of 10 nm to 1000 μιτι.

32. The separator system of claim 15-31 , wherein said spacer comprises: a ring for establishing said selected distance between said first high mechanical strength layer and said second high mechanical strength layer; a frame structure having a porous wall component, a material layer, or an arrangement of discrete material elements.

33. The separator system of any of claims 15 - 32, wherein each of said low ionic resistance layers is independently a polymer, a ceramic, a wood, glass, a mineral, a metal, an alloy, a woven material, a nonwoven material, cellulose, wood fiber, sponge or a combination thereof.

34. The separator system of any of claims 15 - 33, wherein said one or more low ionic resistance layers each independently have porosity greater than or equal to 50%.

35. The separator system of any of claims 15 - 34, wherein said one or more low ionic resistance layers each independently have a porosity selected from the range of 50% to 95%.

36. The separator system of any of claims 1 - 35, wherein said one or more low ionic resistance layers or high mechanical strength layers is coated on another low ionic resistance layer or a high mechanical strength layer or is coated on an electrode in a chemical cell.

37. The separator system of any of claims 1 - 36, wherein at least one side of one of said high mechanical strength layers is wet-able.

38. The separator system of claim 37, wherein said wet-able side of the high

mechanical strength layer is placed next to another high mechanical strength layer with no low ionic resistance layer provided between them.

39. The separator system of claim 37, wherein said wet-able side of the high

mechanical strength layer is placed next to an electrode with no low ionic resistance layer between them.

40. The separator system of any of claims 1 -39, further comprising one or more

chemical barrier layers provided on a side of at least one of the first high mechanical strength layer, the second high mechanical strength layer, the third high mechanical strength layer, the fourth high mechanical strength layer or said one or more low ionic resistance layers.

41 .The separator system of claim 40, wherein said one or more chemical barrier layers independently prevents transportation of unwanted chemical components through said one or more chemical barrier layers to a positive electrode or a negative electrode of an electrochemical cell.

42. The separator system of any of claims 40-41 , wherein said one or more chemical barrier layers prevents transport of an electrolyte solvent through said one or more chemical barrier layers to a positive electrode or a negative electrode of an electrochemical cell.

43. The separator system of any of claims 40-42, wherein said one or more chemical barrier layers comprises a solid electrolyte or a solid polymer electrolyte disposed on at least one side of an electrode of an electrochemical cell.

44. The separator system of any of claims 40-43, wherein said one or more chemical barrier layers comprise a solid electrolyte from LISICON or NASICON or a polymer electrolyte comprising polyethylene oxide (PEO).

45. The separator system of any of claims 40-44, wherein the separator system is a component of an electrochemical cell having a negative electrode and a positive electrode, wherein said one or more chemical barrier layer comprise an ion conductive protective membrane, wherein said ion conductive protective membrane provides a barrier between a first electrolyte in contact with said positive electrode and a second electrode in contact with said negative electrode, wherein said ion conductive protective membrane prevents contact between said negative electrode and said first electrolyte.

46. The separator system of claims 45, wherein said negative electrode is a lithium metal electrode, wherein said ion conductive protective membrane conducts lithium ion charge carriers and prevents contact between said lithium metal electrode and said first electrolyte.

47. The separator system of claim 45, wherein said ion conductive protective

membrane comprising a material selected from the group consisting of glassy or amorphous active metal ion conductors, ceramic active metal ion conductors, and glass-ceramic active metal ion conductors.

48. The separator system of any of claims 40-47, wherein said one or more chemical barrier layers further comprises a solid polymer electrolyte disposed between a surface of the protective membrane and the positive electrode or the negative electrode.

49. The separator system of any of claims 40-48, wherein at least one of said high mechanical strength layers, one or more low ionic resistance layers and said one or more chemical barrier layers is a deposited layer that is deposited on at least one of said high mechanical strength layers, one or more low ionic resistance layers and said one or more chemical barrier layers.

50. The separator system of any of claims 40-49, wherein at least one of said high mechanical strength layers, one or more low ionic resistance layers and said one or more chemical barrier layers is a deposited layer that is deposited on an electrode of an electrochemical cell.

51 .The separator system of any of claims 40-47, comprising a combination of at least two of the first high mechanical strength layer, the second high mechanical strength layer, the third high mechanical strength layer and the fourth high mechanical strength layer and said one or more chemical barrier layers without any of said low ionic resistance layers.

52. The separator system of claim 1 , further comprising a third high mechanical

strength layer having a plurality of apertures extending entirely through said third high mechanical strength layer and provided in a third pattern; said third high mechanical strength layer positioned between said first high mechanical strength layer and said second high mechanical strength layer; said third pattern having an off-set alignment relative to said first pattern or said second pattern such that an overlap of said apertures of said first pattern or said second pattern and said apertures of said third pattern along axes extending perpendicularly from said first high mechanical strength layer or said second high mechanical strength layer to said third high mechanical strength layer is less than or equal to 20%.

53. The separator system of claim 52, further comprising a fourth high mechanical strength layer having a plurality of apertures extending entirely through said fourth high mechanical strength layer and provided in a fourth pattern; said fourth high mechanical strength layer positioned between said first high mechanical strength layer and said second high mechanical strength layer, said fourth pattern having an off-set alignment relative to said first pattern, said second pattern or said third pattern such that an overlap of said apertures of said first pattern, said second pattern or said third pattern and said apertures of said fourth pattern along axes extending perpendicularly from said first high mechanical strength layer or said second high mechanical strength layer to said fourth high

mechanical strength layer is less than or equal to 20%.

54. The separator system of any of claims 1 - 53, wherein at least a portion of said first high mechanical strength layer, said second high mechanical strength layer, said third high mechanical strength layer, said fourth high mechanical strength layer, low ionic resistance layers, frame layers, spacer, chemical barrier layers, or any combination of these are at least partially attached to each other via a pressure, heating, an adhesive coating, a chemical adherent, plasma treating or any combination of these.

55. The separator system of any of claims 1 - 54, wherein at least a portion of said first high mechanical strength layer, said second high mechanical strength layer, said third high mechanical strength layer, said fourth high mechanical strength layer, low ionic resistance layers, frame layers, spacer, chemical barrier layers, or any combination of these are at least partially attached to each other via glue, epoxy, cement, PTFE, a solid electrolyte, a gel electrolyte, a polymer electrolyte, a silicone adhesive, acrylic adhesive, cyanacrylate, stycast 1266, deltabond 151 , PVDF, PVA, LIPON, LISICON, PE-PP-PVDF, tetramethylammonium hydroxide pentahydrate (CH₃)₄NOH-5H₂O , poly(ethylene oxide) (PEO), copolymer of epichlorohydrin and ethylene oxide P(ECH-co-EO) and poly(vinylalcohol), glassfibre polymer electrolyte, zinc sulfide, silicon dioxide, Kapton Tape, polyethylene oxide or polypropylene oxide, or a copolymer, PVDF-co-HFP Bi₂O₃, a non-fluorine-containing binder or an aromatic binder, lithium polyacrylate or a combination thereof.

56. The separator system of any of claims 1 -55, wherein the separator system is a component of an electrochemical cell having a positive electrode and a negative electrode, said separator further comprising an electrolyte provided between said positive electrode and said negative electrode; wherein said electrolyte is in contact with any of said first high mechanical strength layer, said second high mechanical strength layer, said third high mechanical strength layer, and said fourth high mechanical strength layer.

57. The separator system of any of claims 1 -56, wherein the separator system is a component of an electrochemical cell having a positive electrode and a negative electrode, said separator further comprising a first electrolyte and a second electrolyte provided between said positive electrode and said negative electrode; wherein said first electrolyte has a different composition than said second electrolyte; wherein said first electrolyte is in contact with any of said first high mechanical strength layer, said second high mechanical strength layer, said third high mechanical strength layer, and said fourth high mechanical strength layer, and wherein said second electrolyte is in contact with any of said first high mechanical strength layer, said second high mechanical strength layer, said third high mechanical strength layer, and said fourth high mechanical strength layer; where the first electrolyte and the second electrolyte do not mix with each other because of the presence of an impervious ion conducting layer between them or because of different chemistry and physics such as hydrophilic or hydrophobic behavior or density.

58. The separator system of any of claims 1 -57, wherein said first pattern of

apertures provides a first porosity of said first high mechanical strength layer greater than or equal to 30% and wherein said second pattern of apertures provides a second porosity of said second high mechanical strength layer greater than or equal to 30%.

59. The separator system of any of claims 1 -58, wherein said first pattern of

apertures provides a first porosity of said first high mechanical strength layer greater than or equal to 30%, or wherein said second pattern of apertures provides a second porosity of said second high mechanical strength layer greater than or equal to 30%; or wherein said third pattern of apertures provides a third porosity of said third high mechanical strength layer greater than or equal to 30%; or wherein said fourth pattern of apertures provides a fourth porosity of said fourth high mechanical strength layer greater than or equal to 30%.

60. The separator system of any of claims 1 -59, wherein said first pattern of

apertures provides a porosity of said first high mechanical strength layer selected from the range of 30% to 70% and wherein said second pattern of apertures provides a porosity of said second high mechanical strength layer selected from the range of 30% to 70%.

61 .The separator system of any of claims 1 -59, wherein said first pattern of

apertures provides a porosity of said first high mechanical strength layer selected from the range of 30% to 70%; or wherein said second pattern of apertures provides a porosity of said second high mechanical strength layer selected from the range of 30% to 70%; or wherein said third pattern of apertures provides a porosity of said third high mechanical strength layer selected from the range of 30% to 70%; or wherein said fourth pattern of apertures provides a porosity of said fourth high mechanical strength layer selected from the range of 30% to 70%

62. The separator systems of claim 2 or 4 wherein said second high mechanical strength layer is provided between said first high mechanical strength layer and said third high mechanical strength layer.

63. The separator systems of claim 3 or 5 wherein said first high mechanical strength layer is provided between said second high mechanical strength layer and said fourth high mechanical strength layer or wherein said third high mechanical strength layer is provided between said second high mechanical strength layer and said fourth high mechanical strength layer.

64. The separator system of any of claims 1 -63, wherein said apertures of any of said first high mechanical strength layer, said second high mechanical strength layer, said third high mechanical strength layer or said fourth high mechanical strength layer independently have cross sectional shapes selected from the group consisting of a circle, parallelogram, rectangle, square, triangle, ellipse, tetragon, pentagon, hexagon and any combinations thereof.

65. The separator system of any of claims 1 -64, wherein said apertures of said high mechanical strength layers have at least one lateral dimension greater than or equal to 20 μηη .

66. The separator system of any of claims 1 -64, wherein said apertures of said high mechanical strength layers have at least one lateral dimension selected from the range of 200 μηη and 1 mm.

67. The separator system of any of claims 1 -64, wherein said apertures of said high mechanical strength layers have at least one lateral dimension less than or equal to 200 μηη.

68. The separator system of any of claims 1 -64, wherein said apertures of said high mechanical strength layers have at least one lateral dimension less than or equal to 10 μηη.

69. The separator system of any of claims 1 -64, wherein said apertures of said high mechanical strength layers have at least one lateral dimension less than or equal to 1 μηη .

70. The separator system of any of claims 1 -64, wherein any of said first pattern, said second pattern, said third pattern or said fourth pattern is independently a symmetrical pattern of apertures or an asymmetrical pattern of apertures.

71 .The separator system of any of claims 1 -70, wherein any of said first pattern, said second pattern, said third pattern or said fourth pattern independently comprise a pattern of apertures that is not random.

72. The separator system of any of claims 1 -71 , wherein any of said first pattern of apertures, second pattern of apertures, third pattern of apertures or said fourth pattern of apertures are independently made by a process selected from the group consisting of laser cutting, lithography, etching, casting, drilling, molding, punching, patterning, coating and any combinations of these.

73. The separator system of any of claims 1 -72, wherein said first high mechanical strength layer and said second high mechanical strength layer are not in complete physical contact.

74. The separator system of any of claims 1 -73, wherein said first high mechanical strength layer and said second high mechanical strength layer are separated by a distance selected from the range of 20 nm to 2 mm.

75. The separator system of any of claims 1 -74, wherein said first high mechanical strength layer or said second high mechanical strength layer is separated from said third high mechanical strength layer or said fourth high mechanical strength layer by a distance selected from the range of 20 nm to 2 mm.

76. The separator system of any of claims 1 -75, wherein any of said first high

mechanical strength layer, said second high mechanical strength layer, said third high mechanical strength layer, said fourth high mechanical strength layer, said one or more low ionic resistance layers, and said one or more chemical barrier layers independently have an average thickness selected over the range of 10 nm to 25 μηη .

77. The separator system of any of claims 1 -75, wherein any of said first high

mechanical strength layer, said second high mechanical strength layer, said third high mechanical strength layer, said fourth high mechanical strength layer, said one or more low ionic resistance layers, and said one or more chemical barrier layers independently have an average thickness selected over the range 5 μηη to 1 mm.

78. The separator system of any of claims 1 -75, wherein any of said first high

mechanical strength layer, said second high mechanical strength layer, said third high mechanical strength layer, said fourth high mechanical strength layer, said one or more low ionic resistance layers, and said one or more chemical barrier layers independently have an average thickness selected over the range 10 nm to 2 μηη or selected over the range 2 μηη to 50 μηη

79. The separator system of any of claims 1 -78, wherein any of said first high

mechanical strength layer, said second high mechanical strength layer, said third high mechanical strength layer and said fourth high mechanical strength layer independently have a Young's modulus selected over the range of 500 MPa to 500 GPa.

80. The separator system of any of claims 1 -79, wherein any of said first high mechanical strength layer, said second high mechanical strength layer, said third high mechanical strength layer and said fourth high mechanical strength layer independently have a yield strength selected over the range of 5 MPa to 1000 MPa.

81 .The separator system of any of claims 1 -80, wherein any of said first high

mechanical strength layer, said second high mechanical strength layer, said third high mechanical strength layer and said fourth high mechanical strength layer independently have a propagating tear strength selected over the range of 0.005 N to 10 N.

82. The separator system of any of claims 1 -81 , wherein any of said first high

mechanical strength layer, said second high mechanical strength layer, said third high mechanical strength layer and said fourth high mechanical strength layer independently have an initiating tear strength selected over the range of 10 N to 500 N.

83. The separator system of any of claims 1 -82, wherein any of said first high

mechanical strength layer, said second high mechanical strength layer, said third high mechanical strength layer and said fourth high mechanical strength layer independently have a tensile strength selected over the range of 50 MPa to 2GPa.

84. The separator system of any of claims 1 -83, wherein any of said first high

mechanical strength layer, said second high mechanical strength layer, said third high mechanical strength layer and said fourth high mechanical strength layer independently have an impact strength selected over the range of 10 N cm to 1000 N cm.

85. The separator system of any of claims 1 -84, wherein any of said first high

mechanical strength layer, said second high mechanical strength layer, said third high mechanical strength layer and said fourth high mechanical strength layer independently comprise planar layers or hollow cylindrical layers.

86. The separator system of any of claims 1 -85, wherein any of said first high

mechanical strength layer, said second high mechanical strength layer, said third high mechanical strength layer, said fourth high mechanical strength layer, said one or more low ionic resistance layers, and said one or more chemical barrier layers comprise chemically resistant materials.

87. The separator system of any of claims 1 -86, wherein any of said first high

mechanical strength layer, said second high mechanical strength layer, said third high mechanical strength layer and said fourth high mechanical strength layer independently comprise a material having a melting point greater than or equal to 100 Celsius.

88. The separator system of claim 87, wherein at least two of said high mechanical strength layers have different melting temperature with a difference of at least 30 Celsius.

89. The separator system of claim 88, wherein the difference in melting temperatures of said high mechanical strength layers provides in a shutdown mechanism that by melting one of the layers the ionic path between two electrodes of an electrochemical cell closes.

90. The separator system of claim 88, wherein the difference in melting temperatures of said high mechanical strength layers result does not provide a shutdown mechanism that by melting one of the layers the ionic path between two electrodes of an electrochemical cell closes.

91 .The separator system of any of claims 1 -90, wherein any of said first high

mechanical strength layer, said second high mechanical strength layer, said third high mechanical strength layer and said fourth high mechanical strength layer independently comprise a material having a thermal coefficient of thermal expansion is less than or equal to 50ppm/°C.

92. The separator system of any of claims 1 -91 , wherein any of said first high

mechanical strength layer, said second high mechanical strength layer, said third high mechanical strength layer and said fourth high mechanical strength layer independently comprise one or more materials selected from the group consisting of a polymer, a metal, an alloy, a ceramic, a wood, a glass, a semiconductor, a woven material, and a nonwoven material.

93. The separator system of any of claims 1 -92, wherein any of said first high mechanical strength layer, said second high mechanical strength layer, said third high mechanical strength layer and said fourth high mechanical strength layer independently comprise one or more materials selected from the group consisting of a gel electrolyte, a solid electrolyte and a polymer electrolyte.

94. The separator system of any of claims 1 -93, wherein any of said first high

mechanical strength layer, said second high mechanical strength layer, said third high mechanical strength layer and said fourth high mechanical strength layer independently comprise one or more materials selected from the group consisting of Polyacrylic acid (PAA), Cross-linked polyethylene (PEX, XLPE) , Polyethylene (PE), Polyethylene terephthalate (PET, PETE), Polyphenyl ether (PPE), Polyvinyl chloride (PVC), Polyvinylidene chloride (PVDC), Polylactic acid (PLA),

Polypropylene (PP), Polybutylene (PB), Polybutylene terephthalate (PBT), Polyamide (PA), Polyimide (PI), Polycarbonate (PC), Polytetrafluoroethylene (PTFE), Polystyrene (PS), Polyurethane (PU), Polyester (PE), Acrylonitrile butadiene styrene (ABS), Poly(methyl methacrylate) (PMMA), Polyoxymethylene (POM), Polysulfone (PES), Styrene-acrylonitrile (SAN), Ethylene vinyl acetate (EVA), Styrene maleic anhydride (SMA), PVDF, PEO PVDF, LIPON PVDF, LISICON PVDF, tetramethylammonium hydroxide pentahydrate

(CH₃)₄NOH-5H₂O, poly(ethylene oxide) (PEO), copolymer of epichlorohydrin and ethylene oxide P(ECH-co-EO) and poly(vinylalcohol), PEO- PVA- glassfibre polymer electrolyte, zinc sulfide, silicon dioxide, PVA and PSA, PVAV6/PSS; PVAN6/(PSS+PAA); V6/PVA/(PSS+PAA);

PVMPSS+PAA(35%))/(PSS+PAA(35%));

(PSS+PAA(35%))/PVA/(PSS+PAA(35%)); or (PSS+PAA

(35%))/(PVA(10%)+PSS (20% vs. PVA))/(PSS+PAA (35%)) polyethylene glycol, polypropylene glycol, polybutylene glycol, alkyl-polyethylene glycol, alkyl- polypropylene glycol, alkyl-polybutylene glycol, a copolymer thereof, a PEO material, a PVA material and any combination thereof.

95. The separator system of any of claims 1 -94, wherein a surface of any of said first high mechanical strength layer, said second high mechanical strength layer, said third high mechanical strength layer and said fourth high mechanical strength layer is wet-able with an electrolyte.

96. The separator system of any of claims 1 -94, wherein a surface of any of said first high mechanical strength layer, said second high mechanical strength layer, said third high mechanical strength layer and said fourth high mechanical strength layer is coated with a coating that is wet-able with an electrolyte.

97. The separator system of any of claims 1 -94, wherein at least a portion of a

surface of any of said first high mechanical strength layer, said second high mechanical strength layer, said third high mechanical strength layer and said fourth high mechanical strength layer is coated with an adhesive coating.

98. The separator system of any of claims 96 - 97, wherein said coating has a

thickness less than 5 μηη or wherein said coating covers less than 10% of said surface or wherein said coating has a thickness less than 5 μηη and covers less than 10% of said surface

99. The separator system of any of claims 1 -98, wherein at least one surface of any of said first high mechanical strength layer, said second high mechanical strength layer, said third high mechanical strength layer and said fourth high mechanical strength layer has a surface roughness providing a space for an electrolyte between at least a portion of said first high mechanical strength layer, said second high mechanical strength layer, said third high mechanical strength layer or said fourth high mechanical strength layer.

100. The separator system of any of claims 1 -99, wherein the separator system is a component in an electrochemical cell having a positive electrode and a negative electrode; wherein at least one surface of any of said first high

mechanical strength layer, said second high mechanical strength layer, said third high mechanical strength layer and said fourth high mechanical strength layer has a surface roughness providing a space for an electrolyte between said first high mechanical strength layer, said second high mechanical strength layer, said third high mechanical strength layer or said fourth high mechanical strength layer and said positive electrode or said negative electrode of said electrochemical cell.

101 . The separator system of any of claims 99-100, wherein said surface

roughness provides a distance between at least a portion of two of said high mechanical strength layers or between at least a portion of a high mechanical strength layer and the positive electrode or negative electrode selected from the range of 5 nm and 5 micrometers.

102. The separator system of any of claims 1 -94, further comprising one or more coatings provided on any of said first high mechanical strength layer, said second high mechanical strength layer, said third high mechanical strength layer and said fourth high mechanical strength layer.

103. The separator system of claim 102, wherein said one or more coatings independently comprises a non-conductive coating.

104. The separator system of claim 102, wherein said one or more coatings independently comprises a hydrophobic coating or a hydrophilic coating.

105. The separator system of claim 102, wherein said one or more coatings independently comprises polyethylene glycol.

106. The separator system of claim 102, wherein said one or more coatings prevent material transport from a positive electrode to a negative electrode of an electrochemical cell.

107. The separator system of claim 102, wherein said one or more coatings independently have a thickness selected from the range of 10 nm to 2 μηη .

108. The separator system of claim 102 for an electrochemical cell having a sulfur-based cathode, wherein said one or more coating repels hydrophobic polysulfides and increases the performance and cycle life of the electrochemical cell.

109. The separator system of any of claims 1 -108, wherein any of said first high mechanical strength layer, said second high mechanical strength layer, said third high mechanical strength layer and said fourth high mechanical strength layer is independently a metal layer.

1 10. The separator system of claim 109, wherein any of said first high

mechanical strength layer, said second high mechanical strength layer, said third high mechanical strength layer and said fourth high mechanical strength layer is independently a metal selected from the group consisting of Al, Ni, Cu and stainless steel.

1 1 . The separator system of claim 109, wherein said coating is a non- conductive coating. 12. The separator system of claim 1 1 1 , wherein said non-conductive coating is PTFE, PE, PP, PVC, or a polyimide. 13. The separator system of any of claims 1 -1 12, comprising a separator in a primary electrochemical cell or secondary electrochemical cell. 14. The separator system of any of claims 1 -1 13, comprising a separator in a lithium battery, an alkaline battery, zinc battery or a lead acid battery. 15. The separator system of any of claims 1 -1 13, comprising a separator in a lithium metal-air battery, a lithium ion battery, a lithium air battery, a Fe-air battery, a Al-air battery, or a zinc-air battery. 16. The separator of system of any of claims 1 -1 13, comprising a separator in a fuel cell, a flow battery system, a semisolid battery, a 3-D battery, a nano- battery, a micro-battery or an electrochemical capacitor. 17. An electrochemical cell comprising: a negative electrode; a positive electrode; a first electrolyte provided between said positive electrode and said negative electrode; and the separator system of any of claims 1 -1 16 provided in contact with said electrolyte and between said negative electrode and said positive electrode; wherein said separator system is positioned such that ions of said electrolyte are able to be transported between said positive electrode and said negative electrode. 18. The electrochemical cell of claim 1 17, further comprising a chemical barrier layer provided between said positive electrode and said negative electrode; said electrochemical cell further comprising a second electrolyte provided between said positive electrode and said negative electrode, wherein said chemical barrier layer prevents mixing of said first electrolyte and said second electrolyte.

1 19. The electrochemical cell of any of claims 1 17-1 18, wherein said off-set alignment provides no direct linear path between the positive electrode and the negative electrode.

120. The electrochemical cell of any of claims 1 17-1 19, wherein said off-set alignment prevents shorting via electrical contact between said positive electrode and said negative electrode by manufacturing defects, external objects or the formation of dendrites on said positive electrode or negative electrode.

121 . The electrochemical cell of any of claims 1 17-120, wherein at least one of said first high mechanical strength layer, said second high mechanical strength layer, said third high mechanical strength layer, said fourth high mechanical strength layer, said low ionic resistance layers, said frame layers, said spacer, said chemical barrier layers, or any combination of these are at least partially attached said positive electrode or said negative electrode by via pressure, heating, an adhesive coating, a chemical adherent, plasma treating or by depositing or coating one layer on another layer or on an electrode or any combination of these.

122. The electrochemical cell of any of claims 1 17-121 , wherein at least one of said first high mechanical strength layer, said second high mechanical strength layer, said third high mechanical strength layer, said fourth high mechanical strength layer, said low ionic resistance layers, said frame layers, said spacer, said chemical barrier layers, or any combination of these are at least partially attached to said positive electrode or said negative electrode by via a glue, epoxy, cement, a Telfon coating, a solid electrolyte, a gel electrolyte or a polymer electrolyte.

123. The electrochemical cell of any of claims 1 17-122, wherein at least one of said first high mechanical strength layer, said second high mechanical strength layer, said third high mechanical strength layer, said fourth high mechanical strength layer, low ionic resistance layers, frame layers, spacer, chemical barrier layers, or any combination of these comprise a coating deposited on a surface of said positive electrode or said negative electrode.

124. The electrochemical cell of any of claims 1 17 - 123, wherein said separator system prevents electrical contact between said positive electrode and said negative electrode.

125. The electrochemical cell of any of claims 1 17 - 124, wherein said

separator system provides an ionic conductivity between said positive electrode and said negative electrode equal to or greater than 1 x10^"3 S/cm.

126. The electrochemical cell of any of claims 1 17 - 124, wherein said

separator system provides an ionic conductivity between said positive electrode and said negative electrode equal to or greater than 1 x10^"2 S/cm.

127. The electrochemical cell of any of claims 1 17 - 126, wherein said

separator system is provided in physical contact with said positive electrode and said negative electrode.

128. The electrochemical cell of any of claims 1 17 - 127 having a cycle

capacity of at least 300 cycles.

129. The electrochemical cell of any of claims 1 17-128, wherein said separator system provides a net ionic resistance from said positive electrode to said negative electrode selected over the range of 0.5 ohm cm² to 25 ohm cm².

130. The electrochemical cell of any of claims 1 17-128, wherein said separator system provides a net ionic resistance from said positive electrode to said negative electrode less than or equal to 5 ohm cm².

131 . The electrochemical cell of any of claims 1 17-130, wherein said

electrochemical cell provides a specific capacity equal to or greater than 100 mAh g^"1 at a discharge rate equal to or greater than C/5.

132. The electrochemical cell of any of claims 1 17-131 , wherein said electrolyte is aqueous.

133. The electrochemical cell of any of claims 1 17-131 , wherein said electrolyte is aprotic.

134. The electrochemical cell of any of claims 1 17-131 , wherein said electrolyte comprises an alkali metal salt at least partially dissolved in one or more

nonaqueous solvents.

135. The electrochemical cell of any of claims 1 17-131 , wherein said electrolyte comprises a solvent and a supporting salt; wherein said solvent is selected from the group consisting of organic carbonates, ethers, esters, formates, lactones, sulfones, sulfolane, 1 ,3-dioxolane, ethylene carbonate, propylene carbonate, dimethyl carbonate, diethyl carbonate, ethyl methyl carbonate, butylene carbonate, vinylene carbonate, fluoroethylene carbonate, fluoropropylene carbonate, y-butylrolactone, methyl difluoroacetate, ethyl difluoroacetate, dimethoxyethane, diglyme (bis(2-methoxyethyl)ether), tetrahydrofuran, dioxolane, 2MeTHF, 1 ,2-DME or higher glymes, sufolane, methyl formate, methyl acetate, and any combinations thereof; and wherein said supporting salt is selected from the group consisting of LiPF₆, LiBF₄, LiAsF₆, LiCIO₄, LiSO₃CF₃, LiN(CF₃SO₂)2, LiN(SO2C₂F₅)2 and any combinations thereof.

136. The electrochemical cell of any of claims 1 17-131 , wherein said electrolyte comprises a golfing agent selected from the group consisting of PVdF, PVdF— HFP copolymer, PAN, and PEO and mixtures thereof; a plasticizer selected from the group consisting of EC, PC, DEC, DMC, EMC, THE, 2MeTHF, 1 ,2-DME and mixtures thereof; and a Li salt selected from the group consisting of LiPF6, LiBF₄, LiAsFe, LiCIO₄, LiSO₃CF₃, LiN(CF₃SO₂)₂ and LiN(SO₂C₂F5)₂.

137. The electrochemical cell of any of claims 1 17-131 , wherein said electrolyte comprises a solid charge carrying media or a gel electrode.

138. The electrochemical cell of any of claims 1 17-131 , wherein said electrolyte comprises a polymeric media.

139. The electrochemical cell of any of claims 1 17-131 , wherein said electrolyte comprises polyethylene oxide, polytetrafluoroethylene, polyvinylidene fluoride, fluorine-containing copolymers, polyacrylon itrile, or any combinations thereof

140. The electrochemical cell of any of claims 1 17-139, wherein said negative electrode or said positive electrode comprise a nano-sized material.

141 . The electrochemical cell of any of claims 1 17-139, wherein said negative electrode or said positive electrode is in the form of a powder.

142. The electrochemical cell of any of claims 1 17-141 , wherein said negative electrode comprises a material selected from the group consisting of lithium, zinc, aluminum, silicon, tin, antimony, lead, germanium, magnesium, , cadmium, bismuth, indium, molybdenum, niobium, tungsten, tantalum, iron, nickel, manganese, copper, a sodium transition metal phosphate, a sodium mixed metal phosphate; Li₄/3Ti5/3O₄, graphite, an alloy of tin, cobalt, carbon, LiVO₂, Li₄Ti₅Oi₂, Li4/3Ti5/3O₄ TiO₂, WO₂, and MoO₂.

143. The electrochemical cell of any of claims 1 17-142, wherein said positive electrode comprises a material selected from the group consisting of graphite, LiCoO_2NiO_8O₂ , LiNiO2 , LiFePO₄ , LiMnPO₄ , LiCoPO₄ , LiMn₂O₄ , LiCoO₂, LiNiO _5Mn l.5O₄, LiVPO₄ F, silver oxide, nickel oxide, cobalt oxide, manganese oxide, AgO, Ag₂O₃, Zn, ZnO AgO, Ag₂O, Ag₂O₃, HgO, Hg₂O, CuO, CdO, NiOOH, Pb₂O₄, PbO₂, LiFePO₄, Li₃V₂(PO₄)₃, V₆O₁₃, V₂O₅, Fe₃O₄, Fe₂O₃, MnO₂, LiCoO₂, LiNiO₂, LiMn₂O₄,. LiVO₂, Li₄Ti₅O ₂, TiO₂, WO₂, and MoO₂.

144. The electrochemical cell of any of claims 1 17- 142, wherein said positive electrode comprises a material selected from the group consisting of a lithiated metal oxide based cathode selected from the group consisting of LixCoO₂, Li_xNiO₂, LixMn₂O and LiFePO ; an unlithiated metal oxide based cathode selected from the group consisting of Ag_xV₂Os, Cu_xV₂O5, V₂Os, V₆O-i₃, MnO₂, CuO, Ag₂CrO₄ and MoO₃, wherein x ranges from 0 to 2; a lithiated metal oxide based cathode selected from the group consisting of FeS₂,TiS₂, FeS and CuS; an active sulfur cathode selected from the group consisting of elemental sulfur, polysulfides and combinations thereof; and a PEO/carbon/metal-oxide type cathode structure comprising an aqueous electrochemically active component such as water or a water soluble oxidant selected from the group consisting of gaseous, liquid and solid oxidants and combinations thereof such as peroxide, hydrogen peroxide, O₂, SO₂ and NO₂, and the water soluble solid oxidants are selected from the group consisting of NaNO₂, KNO₂, Na₂SO₃ and K₂SO₃ wherein the cathode structure electronically conductive component is a porous catalytic support such as nickel and wherein said cathode structure electrochemically active material comprises air.

145. The electrochemical cell of any of claims 1 17-144, comprising a primary electrochemical cell or secondary electrochemical cell.

146. The electrochemical cell of any of claims 1 17-144, comprising a lithium battery, an alkaline battery, zinc battery, a lead acid battery, a lithium metal -air battery, a lithium ion battery, a lithium air battery, a Fe-air battery, a Al-air battery, or a zinc-air battery.

147. The electrochemical cell of system of any of claims 1 17-144, comprising a fuel cell, a flow battery system, a semisolid battery, a 3-D battery, a nano-battery, a micro-battery or an electrochemical capacitor.

148. The electrochemical cell of any of claims 1 17-144, wherein said

electrochemical cell is a thin film battery.

149. A battery pack comprising at least one electrochemical cell of any of

claims 1 17-144, wherein said at least one electrochemical cell includes a lithium ion electrochemical cell.

150. An electronic device comprising the battery pack of claim 149.

151 . An alkali metal fuel cell comprising: a renewable anode comprising solid alkali metal and alkali metal dissolved in a solvent as fuel; a cathode structure comprising a static electronically conductive component, an ionically conductive component comprising an electrolyte for ions of the alkali metal, and a fluid oxidant obtained from an operating environment of the cell; and a separator system of any of claims 1 -1 12 provided between the anode and cathode structure.

152. The electrochemical cell of any of claims 1 17 - 151 , wherein said

electrochemical cell has at least one of its electrodes in the form of a solvated metal.

153. The electrochemical cell of claim 152, wherein the metal is lithium or a lithium alloy.

154. The electrochemical cell of any of claims 1 17 - 151 , wherein said electrochemical cell has at least one of its electrodes in the form of a molten metal.

155. The electrochemical cell of claim 152, wherein the electrochemical cell is an alkaline metal ion battery.

156. The electrochemical cell of any of claims 1 17 - 151 , wherein said

electrochemical cell has a first electrolyte on a first side of the cell including the positive electrode and a second electrolyte on a second side of the cell including the negative electrode, wherein the first electrolyte has a different composition than the second electrolyte; and wherein said electrochemical cell further comprises one or more chemical barrier layers comprising an ion conductive protective membrane positioned between the positive electrode and the negative electrode.

157. The electrochemical cell of claim 156, wherein the first electrolyte is an aqueous electrolyte and the second electrolyte is an aprotic electrolyte.

158. The electrochemical cell of claim 156, wherein at least one of the first electrolyte and the second electrolyte is a solid electrolyte.

159. The separator system of any of claims 1 - 1 16, further comprising one or more solid electrolyte layers that prevent water molecules, CO₂, O₂ or air from transporting through said separator system.

160. The separator system of claim 159, wherein said one or more solid

electrolyte layers comprise LISICON or NASICON.

161 . The separator system of any of claims 1 -1 16, wherein at least one of the high mechanical strength layers has a dielectric constant greater than or equal to 50.

162. The separator system of any of claims 1 -1 16, wherein at least one of the high mechanical strength layers comprises a conductive material.

163. The separator system of any of claims 1 -1 16, wherein at least one of said first high mechanical strength layer, said second high mechanical strength layer, said third high mechanical strength layer, said fourth high mechanical strength layer, said low ionic resistance layers, said frame layers, said spacer, said chemical barrier layers, or any combination of these have a high surface energy.

164. The separator system of claim 163, wherein the surface energy is greater than or equal to 10mJ/m2.

165. The separator system any of claims 163 - 164, wherein the surface energy helps with the wettability of the layers with an electrolyte.

166. The separator system any of claims 163 - 165, wherein the surface energy helps with the attachment of the layers to each other or to one or more electrodes of an electrochemical cell.