WO2012114980A1 - Ébauche de masque réfléchissant pour lithographie euv - Google Patents

Ébauche de masque réfléchissant pour lithographie euv Download PDF

Info

Publication number
WO2012114980A1
WO2012114980A1 PCT/JP2012/053712 JP2012053712W WO2012114980A1 WO 2012114980 A1 WO2012114980 A1 WO 2012114980A1 JP 2012053712 W JP2012053712 W JP 2012053712W WO 2012114980 A1 WO2012114980 A1 WO 2012114980A1
Authority
WO
WIPO (PCT)
Prior art keywords
layer
film thickness
mask blank
euv
reflective
Prior art date
Application number
PCT/JP2012/053712
Other languages
English (en)
Japanese (ja)
Inventor
和幸 林
和伸 前重
俊之 宇野
Original Assignee
旭硝子株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 旭硝子株式会社 filed Critical 旭硝子株式会社
Priority to JP2013500989A priority Critical patent/JPWO2012114980A1/ja
Publication of WO2012114980A1 publication Critical patent/WO2012114980A1/fr

Abstract

La présente invention concerne une ébauche de masque EUV dans laquelle l'épaisseur de la couche absorbante est optimisée, l'épaisseur de la couche d'absorption pouvant être réduite en comparaison d'une épaisseur classique dans une plage n'altérant pas les caractéristiques du motif. Dans une ébauche de masque réfléchissant pour lithographie EUV, une couche réfléchissante pour la lumière EUV et une couche absorbante destinée à absorber la lumière EUV sont formées dans l'ordre indiqué, l'ébauche de masque réfléchissant pour la lithographie EUV étant caractérisée en ce que l'épaisseur de la couche absorbante est définie de manière à se situer dans une plage de ±2,0 % d'épaisseur minimale et de sorte que le pouvoir réfléchissant du faisceau soit inférieur ou égal à 4,0 % dans une plage de longueur d'onde de 13,3 à 13,7 nm.
PCT/JP2012/053712 2011-02-24 2012-02-16 Ébauche de masque réfléchissant pour lithographie euv WO2012114980A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
JP2013500989A JPWO2012114980A1 (ja) 2011-02-24 2012-02-16 Ｅｕｖリソグラフィ用反射型マスクブランク

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2011-038428 2011-02-24
JP2011038428 2011-02-24

Publications (1)

Publication Number Publication Date
WO2012114980A1 true WO2012114980A1 (fr) 2012-08-30

Family

ID=46720761

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2012/053712 WO2012114980A1 (fr) 2011-02-24 2012-02-16 Ébauche de masque réfléchissant pour lithographie euv

Country Status (3)

Country Link
JP (1) JPWO2012114980A1 (fr)
TW (1) TWI582530B (fr)
WO (1) WO2012114980A1 (fr)

Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2005268255A (ja) * 2004-03-16 2005-09-29 Toppan Printing Co Ltd 極限紫外線露光用マスクブランク及びマスク並びに転写方法
JP2008118143A (ja) * 2002-04-11 2008-05-22 Hoya Corp 反射型マスクブランクス及び反射型マスク及びそれらの製造方法並びに半導体の製造方法

Family Cites Families (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP4540267B2 (ja) * 2001-07-30 2010-09-08 Ｈｏｙａ株式会社 Ｅｕｖ光露光用反射型マスクブランクおよびｅｕｖ光露光用反射型マスク
JP3674591B2 (ja) * 2002-02-25 2005-07-20 ソニー株式会社 露光用マスクの製造方法および露光用マスク
DE102007028172B3 (de) * 2007-06-20 2008-12-11 Advanced Mask Technology Center Gmbh & Co. Kg EUV-Maske und Verfahren zur Reparatur einer EUV-Maske
JP4602430B2 (ja) * 2008-03-03 2010-12-22 株式会社東芝 反射型マスク及びその作製方法
WO2010020337A1 (fr) * 2008-08-21 2010-02-25 Asml Holding Nv Substrats de réticule pour ultraviolet extrême à conductivité thermique élevée
JP2010062244A (ja) * 2008-09-02 2010-03-18 Renesas Technology Corp 半導体装置の製造方法
CN102203906B (zh) * 2008-10-30 2013-10-09 旭硝子株式会社 Euv光刻用反射型掩模坯料

Patent Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2008118143A (ja) * 2002-04-11 2008-05-22 Hoya Corp 反射型マスクブランクス及び反射型マスク及びそれらの製造方法並びに半導体の製造方法
JP2005268255A (ja) * 2004-03-16 2005-09-29 Toppan Printing Co Ltd 極限紫外線露光用マスクブランク及びマスク並びに転写方法

Also Published As

Publication number Publication date
JPWO2012114980A1 (ja) 2014-07-07
TW201243492A (en) 2012-11-01
TWI582530B (zh) 2017-05-11

Similar Documents

Publication Publication Date Title
US8828627B2 (en) Reflective mask blank for EUV lithography and reflective mask for EUV lithography
US9423684B2 (en) Reflective mask blank for EUV lithography and process for its production
JP5018789B2 (ja) Ｅｕｖリソグラフィ用反射型マスクブランク
JP5067483B2 (ja) Ｅｕｖリソグラフィ用反射型マスクブランク
US9097976B2 (en) Reflective mask blank for EUV lithography
JP6287099B2 (ja) Ｅｕｖリソグラフィ用反射型マスクブランク
US8927181B2 (en) Reflective mask blank for EUV lithography
JP5590113B2 (ja) Ｅｕｖリソグラフィ用反射型マスクブランクおよびその製造方法
JP5040996B2 (ja) Ｅｕｖリソグラフィ用反射型マスクブランク
JP5348141B2 (ja) Ｅｕｖリソグラフィ用反射型マスクブランク
JPWO2011004850A1 (ja) Ｅｕｖリソグラフィ用反射型マスクブランク
KR102476861B1 (ko) Euv 리소그래피용 반사형 마스크 블랭크 및 그 제조 방법, 그리고 그 마스크 블랭크용의 반사층이 부착된 기판 및 그 제조 방법
JP2015073013A (ja) Ｅｕｖリソグラフィ用反射型マスクブランクの製造方法
JP6186996B2 (ja) Ｅｕｖリソグラフィ用反射型マスクブランク、および、ｅｕｖリソグラフィ用反射型マスク
JP2014160752A (ja) Ｅｕｖリソグラフィ用反射型マスクブランクおよび該マスクブランク用反射層付基板
JP2009210802A (ja) Ｅｕｖリソグラフィ用反射型マスクブランク
JP5333016B2 (ja) Ｅｕｖリソグラフィ用反射型マスクブランク
JP6044213B2 (ja) Ｅｕｖリソグラフィ用反射型マスクブランクおよびその製造方法、ならびに該マスクブランク用の反射層付基板およびその製造方法
JP6288327B2 (ja) Ｅｕｖリソグラフィ用反射型マスクブランク、および、ｅｕｖリソグラフィ用反射型マスク
WO2012114980A1 (fr) Ébauche de masque réfléchissant pour lithographie euv
JP2009252788A (ja) Ｅｕｖリソグラフィ用反射型マスクブランク

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 12749543

Country of ref document: EP

Kind code of ref document: A1

ENP Entry into the national phase

Ref document number: 2013500989

Country of ref document: JP

Kind code of ref document: A

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 12749543

Country of ref document: EP

Kind code of ref document: A1