WO2012057073A1 - Organe collecteur de chaleur solaire et son procédé de fabrication - Google Patents

Organe collecteur de chaleur solaire et son procédé de fabrication Download PDF

Info

Publication number
WO2012057073A1
WO2012057073A1 PCT/JP2011/074424 JP2011074424W WO2012057073A1 WO 2012057073 A1 WO2012057073 A1 WO 2012057073A1 JP 2011074424 W JP2011074424 W JP 2011074424W WO 2012057073 A1 WO2012057073 A1 WO 2012057073A1
Authority
WO
WIPO (PCT)
Prior art keywords
solar heat
heat collecting
collecting member
layer
metal layer
Prior art date
Application number
PCT/JP2011/074424
Other languages
English (en)
Japanese (ja)
Inventor
箕浦　潔
彰信 石動
千明 三成
貴文 端山
Original Assignee
シャープ株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by シャープ株式会社 filed Critical シャープ株式会社
Publication of WO2012057073A1 publication Critical patent/WO2012057073A1/fr

Abstract

La présente invention concerne un organe collecteur de chaleur solaire (10A, 10B) doté d'une couche métallique (M) ayant une surface. La surface de la couche métallique (M) possède une structure d'œil de papillon de nuit contenant une pluralité de convexités (10p) ou une structure inversée d'œil de papillon de nuit contenant une pluralité de concavités (10q), et vue depuis la direction normale, la taille bidimensionnelle de la pluralité de convexités (10p) ou de la pluralité de concavités (10q) est comprise entre 50 nm et 380 nm. Grâce à cette structure, l'organe collecteur de chaleur solaire est capable de collecte efficace de chaleur.
PCT/JP2011/074424 2010-10-25 2011-10-24 Organe collecteur de chaleur solaire et son procédé de fabrication WO2012057073A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2010-238423 2010-10-25
JP2010238423 2010-10-25

Publications (1)

Publication Number Publication Date
WO2012057073A1 true WO2012057073A1 (fr) 2012-05-03

Family

ID=45993781

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2011/074424 WO2012057073A1 (fr) 2010-10-25 2011-10-24 Organe collecteur de chaleur solaire et son procédé de fabrication

Country Status (1)

Country Link
WO (1) WO2012057073A1 (fr)

Cited By (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
FR3014177A1 (fr) * 2013-12-04 2015-06-05 Commissariat Energie Atomique Structure de surface pour les absorbeurs solaires thermiques et leur procede de realisation.
FR3016875A1 (fr) * 2014-01-30 2015-07-31 Commissariat Energie Atomique Structure photonique de surface en materiau refractaire et son procede de realisation.
WO2016060198A1 (fr) * 2014-10-16 2016-04-21 富士フイルム株式会社 Module de caméra et dispositif électronique
EP4164353A1 (fr) * 2018-11-13 2023-04-12 GE Aviation Systems LLC Procédé et appareil de dissipation de chaleur dans des dispositifs électroniques

Citations (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS61119948A (ja) * 1984-11-14 1986-06-07 Hitachi Ltd 太陽熱集熱器
JP2004285422A (ja) * 2003-03-24 2004-10-14 Kanagawa Acad Of Sci & Technol 金属モールド及びその製造方法並びに陽極酸化ポーラスアルミナとその製造方法
WO2006059686A1 (fr) * 2004-12-03 2006-06-08 Sharp Kabushiki Kaisha Materiau empechant la reflexion, element optique, dispositif d’affichage, procede de fabrication d’une matrice et procede de fabrication d’un materiau empechant la reflexion a l’aide de la matrice
JP2006214654A (ja) * 2005-02-03 2006-08-17 Nippon Electric Glass Co Ltd 太陽熱集熱板、選択吸収膜及び太陽熱温水器
JP2006287027A (ja) * 2005-04-01 2006-10-19 Sharp Corp 太陽電池
JP2007156017A (ja) * 2005-12-02 2007-06-21 Nagaoka Univ Of Technology 透明膜、光学部材及び透明膜の製造方法
JP2009103808A (ja) * 2007-10-22 2009-05-14 Asahi Kasei Corp 反射防止フィルム
JP2010219495A (ja) * 2009-02-18 2010-09-30 Nagaoka Univ Of Technology 太陽電池用透明部材および太陽電池
WO2010116728A1 (fr) * 2009-04-09 2010-10-14 シャープ株式会社 Matrice et procédé de fabrication de celle-ci

Patent Citations (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS61119948A (ja) * 1984-11-14 1986-06-07 Hitachi Ltd 太陽熱集熱器
JP2004285422A (ja) * 2003-03-24 2004-10-14 Kanagawa Acad Of Sci & Technol 金属モールド及びその製造方法並びに陽極酸化ポーラスアルミナとその製造方法
WO2006059686A1 (fr) * 2004-12-03 2006-06-08 Sharp Kabushiki Kaisha Materiau empechant la reflexion, element optique, dispositif d’affichage, procede de fabrication d’une matrice et procede de fabrication d’un materiau empechant la reflexion a l’aide de la matrice
JP2006214654A (ja) * 2005-02-03 2006-08-17 Nippon Electric Glass Co Ltd 太陽熱集熱板、選択吸収膜及び太陽熱温水器
JP2006287027A (ja) * 2005-04-01 2006-10-19 Sharp Corp 太陽電池
JP2007156017A (ja) * 2005-12-02 2007-06-21 Nagaoka Univ Of Technology 透明膜、光学部材及び透明膜の製造方法
JP2009103808A (ja) * 2007-10-22 2009-05-14 Asahi Kasei Corp 反射防止フィルム
JP2010219495A (ja) * 2009-02-18 2010-09-30 Nagaoka Univ Of Technology 太陽電池用透明部材および太陽電池
WO2010116728A1 (fr) * 2009-04-09 2010-10-14 シャープ株式会社 Matrice et procédé de fabrication de celle-ci

Cited By (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
FR3014177A1 (fr) * 2013-12-04 2015-06-05 Commissariat Energie Atomique Structure de surface pour les absorbeurs solaires thermiques et leur procede de realisation.
WO2015083051A1 (fr) * 2013-12-04 2015-06-11 Commissariat A L'energie Atomique Et Aux Energies Alternatives Structure de surface pour les absorbeurs solaires thermiques et leur procédé de réalisation
FR3016875A1 (fr) * 2014-01-30 2015-07-31 Commissariat Energie Atomique Structure photonique de surface en materiau refractaire et son procede de realisation.
WO2015114519A1 (fr) 2014-01-30 2015-08-06 Commissariat A L'energie Atomique Et Aux Energies Alternatives Structure photonique de surface en materiau refractaire et son procede de realisation
WO2016060198A1 (fr) * 2014-10-16 2016-04-21 富士フイルム株式会社 Module de caméra et dispositif électronique
JP2016080865A (ja) * 2014-10-16 2016-05-16 富士フイルム株式会社 カメラモジュール及び電子機器
EP4164353A1 (fr) * 2018-11-13 2023-04-12 GE Aviation Systems LLC Procédé et appareil de dissipation de chaleur dans des dispositifs électroniques

Similar Documents

Publication Publication Date Title
Verma et al. Self-cleaning and antireflective packaging glass for solar modules
JP3472838B2 (ja) 波長選択性太陽光吸収材料及びその製造方法
Jeong et al. Absorption mechanism and performance characterization of CuO nanostructured absorbers
CN102033255B (zh) 一种宽谱广角增透亚波长结构的制备方法
JP6224345B2 (ja) 熱吸収材及びその製造方法
JPS6148124B2 (fr)
EP2830098A1 (fr) Absorbeur plasmonique à large bande film mince
KR20110113189A (ko) 투명 유리 기재 및 이러한 기재의 제조 방법
EP3375912B1 (fr) Dispositif en matériau composite
WO2012057073A1 (fr) Organe collecteur de chaleur solaire et son procédé de fabrication
US20110185728A1 (en) High efficiency solar thermal receiver
Li et al. Transparent selective photothermal coatings for antifogging applications
WO2010065635A2 (fr) Structures coniques métalliques à sous-longueur d'onde comme absorbeur solaire sélectif
US20160298875A1 (en) Surface structure for solar heat absorbers and method for the production thereof
Zheng et al. Research status and application prospects of manufacturing technology for micro–nano surface structures with low reflectivity
CN101592777A (zh) 基于纳米结构的全光谱广角聚光器的制作方法
Wang et al. Broadband antireflective subwavelength structures for infrared detection
Berger et al. Controlling the optical performance of transparent conducting oxides using direct laser interference patterning
US20120273041A1 (en) Light concentrator with tapered dichroic materials
Thirunaukkarasu et al. Mechanically and thermally stable thin sheets of broadband antireflection surfaces fabricated by femtosecond lasers
Baryshnikova et al. Nanostructural antireflecting coatings: Classification analysis (A review)
CN104900292A (zh) 一种基于半导体工艺的平面型龙虾眼聚焦镜头的制备方法
Chiadini et al. Analysis of prismatic bioinspired texturing of the surface of a silicon solar cell for enhanced light-coupling efficiency
US11402132B2 (en) Solar energy converter and related methods
ES2648262T3 (es) Un procedimiento de fabricación de una superficie a base de aluminio altamente reflectante resistente a la temperatura para aplicaciones de reflector solar y partes reflectoras fabricadas de ese modo

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 11836207

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 11836207

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: JP