WO2012047359A1 - Thin film composite membranes incorporating carbon nanotubes - Google Patents
Thin film composite membranes incorporating carbon nanotubes Download PDFInfo
- Publication number
- WO2012047359A1 WO2012047359A1 PCT/US2011/045140 US2011045140W WO2012047359A1 WO 2012047359 A1 WO2012047359 A1 WO 2012047359A1 US 2011045140 W US2011045140 W US 2011045140W WO 2012047359 A1 WO2012047359 A1 WO 2012047359A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- carbon nanotubes
- thin film
- membrane
- film composite
- organic solution
- Prior art date
Links
- 239000012528 membrane Substances 0.000 title claims abstract description 147
- 239000002131 composite material Substances 0.000 title claims abstract description 54
- 239000010409 thin film Substances 0.000 title claims abstract description 42
- OKTJSMMVPCPJKN-UHFFFAOYSA-N Carbon Chemical compound [C] OKTJSMMVPCPJKN-UHFFFAOYSA-N 0.000 title claims abstract description 34
- 239000002041 carbon nanotube Substances 0.000 title claims abstract description 26
- 229910021393 carbon nanotube Inorganic materials 0.000 title claims abstract description 22
- 239000000243 solution Substances 0.000 claims abstract description 99
- 238000000034 method Methods 0.000 claims abstract description 44
- 230000008569 process Effects 0.000 claims abstract description 36
- 239000007864 aqueous solution Substances 0.000 claims abstract description 24
- 238000012695 Interfacial polymerization Methods 0.000 claims abstract description 15
- 238000004519 manufacturing process Methods 0.000 claims abstract description 11
- 229920000768 polyamine Polymers 0.000 claims abstract description 9
- 229910052799 carbon Inorganic materials 0.000 claims abstract description 8
- 238000000576 coating method Methods 0.000 claims description 40
- 239000011248 coating agent Substances 0.000 claims description 39
- 239000002048 multi walled nanotube Substances 0.000 claims description 37
- 239000002904 solvent Substances 0.000 claims description 35
- -1 saturated polycyclic compound Chemical class 0.000 claims description 32
- 239000000203 mixture Substances 0.000 claims description 30
- XLYOFNOQVPJJNP-UHFFFAOYSA-N water Substances O XLYOFNOQVPJJNP-UHFFFAOYSA-N 0.000 claims description 28
- 239000004952 Polyamide Substances 0.000 claims description 20
- 229920002647 polyamide Polymers 0.000 claims description 20
- UWCPYKQBIPYOLX-UHFFFAOYSA-N benzene-1,3,5-tricarbonyl chloride Chemical group ClC(=O)C1=CC(C(Cl)=O)=CC(C(Cl)=O)=C1 UWCPYKQBIPYOLX-UHFFFAOYSA-N 0.000 claims description 12
- 125000004122 cyclic group Chemical group 0.000 claims description 10
- 229930195733 hydrocarbon Natural products 0.000 claims description 10
- 239000004215 Carbon black (E152) Substances 0.000 claims description 9
- 150000004820 halides Chemical class 0.000 claims description 9
- 239000013535 sea water Substances 0.000 claims description 7
- CBCKQZAAMUWICA-UHFFFAOYSA-N 1,4-phenylenediamine Chemical group NC1=CC=C(N)C=C1 CBCKQZAAMUWICA-UHFFFAOYSA-N 0.000 claims description 5
- 238000010612 desalination reaction Methods 0.000 claims description 5
- 150000002430 hydrocarbons Chemical class 0.000 claims description 5
- 125000002015 acyclic group Chemical group 0.000 claims description 2
- 229920006395 saturated elastomer Polymers 0.000 claims 2
- 150000001335 aliphatic alkanes Chemical class 0.000 claims 1
- 150000001924 cycloalkanes Chemical class 0.000 claims 1
- 239000006185 dispersion Substances 0.000 description 38
- 230000000052 comparative effect Effects 0.000 description 28
- 238000001223 reverse osmosis Methods 0.000 description 28
- 239000002071 nanotube Substances 0.000 description 25
- 239000000178 monomer Substances 0.000 description 24
- JHIVVAPYMSGYDF-UHFFFAOYSA-N cyclohexanone Chemical compound O=C1CCCCC1 JHIVVAPYMSGYDF-UHFFFAOYSA-N 0.000 description 22
- 150000003839 salts Chemical class 0.000 description 20
- 238000012360 testing method Methods 0.000 description 17
- VLKZOEOYAKHREP-UHFFFAOYSA-N n-Hexane Chemical compound CCCCCC VLKZOEOYAKHREP-UHFFFAOYSA-N 0.000 description 15
- 229920002492 poly(sulfone) Polymers 0.000 description 14
- 239000000047 product Substances 0.000 description 14
- NNBZCPXTIHJBJL-UHFFFAOYSA-N trans-decahydronaphthalene Natural products C1CCCC2CCCCC21 NNBZCPXTIHJBJL-UHFFFAOYSA-N 0.000 description 13
- 239000000463 material Substances 0.000 description 12
- WZCQRUWWHSTZEM-UHFFFAOYSA-N 1,3-phenylenediamine Chemical compound NC1=CC=CC(N)=C1 WZCQRUWWHSTZEM-UHFFFAOYSA-N 0.000 description 10
- FAPWRFPIFSIZLT-UHFFFAOYSA-M Sodium chloride Chemical compound [Na+].[Cl-] FAPWRFPIFSIZLT-UHFFFAOYSA-M 0.000 description 10
- 238000000527 sonication Methods 0.000 description 10
- 239000012466 permeate Substances 0.000 description 9
- 229920000642 polymer Polymers 0.000 description 9
- 125000004855 decalinyl group Chemical group C1(CCCC2CCCCC12)* 0.000 description 8
- 229940018564 m-phenylenediamine Drugs 0.000 description 8
- 239000002109 single walled nanotube Substances 0.000 description 8
- VZSRBBMJRBPUNF-UHFFFAOYSA-N 2-(2,3-dihydro-1H-inden-2-ylamino)-N-[3-oxo-3-(2,4,6,7-tetrahydrotriazolo[4,5-c]pyridin-5-yl)propyl]pyrimidine-5-carboxamide Chemical compound C1C(CC2=CC=CC=C12)NC1=NC=C(C=N1)C(=O)NCCC(N1CC2=C(CC1)NN=N2)=O VZSRBBMJRBPUNF-UHFFFAOYSA-N 0.000 description 7
- 239000010408 film Substances 0.000 description 7
- 238000002156 mixing Methods 0.000 description 7
- 230000000269 nucleophilic effect Effects 0.000 description 7
- 239000011148 porous material Substances 0.000 description 7
- 238000005204 segregation Methods 0.000 description 7
- CSNNHWWHGAXBCP-UHFFFAOYSA-L Magnesium sulfate Chemical compound [Mg+2].[O-][S+2]([O-])([O-])[O-] CSNNHWWHGAXBCP-UHFFFAOYSA-L 0.000 description 6
- GLUUGHFHXGJENI-UHFFFAOYSA-N Piperazine Chemical compound C1CNCCN1 GLUUGHFHXGJENI-UHFFFAOYSA-N 0.000 description 6
- BGTOWKSIORTVQH-UHFFFAOYSA-N cyclopentanone Chemical compound O=C1CCCC1 BGTOWKSIORTVQH-UHFFFAOYSA-N 0.000 description 6
- 230000004907 flux Effects 0.000 description 6
- 239000010410 layer Substances 0.000 description 6
- 238000001728 nano-filtration Methods 0.000 description 6
- PXXNTAGJWPJAGM-UHFFFAOYSA-N vertaline Natural products C1C2C=3C=C(OC)C(OC)=CC=3OC(C=C3)=CC=C3CCC(=O)OC1CC1N2CCCC1 PXXNTAGJWPJAGM-UHFFFAOYSA-N 0.000 description 6
- 230000002776 aggregation Effects 0.000 description 5
- 238000004220 aggregation Methods 0.000 description 5
- 230000015572 biosynthetic process Effects 0.000 description 5
- 239000000975 dye Substances 0.000 description 5
- 239000011521 glass Substances 0.000 description 5
- 230000035699 permeability Effects 0.000 description 5
- 239000011780 sodium chloride Substances 0.000 description 5
- IAZDPXIOMUYVGZ-UHFFFAOYSA-N Dimethylsulphoxide Chemical compound CS(C)=O IAZDPXIOMUYVGZ-UHFFFAOYSA-N 0.000 description 4
- UFWIBTONFRDIAS-UHFFFAOYSA-N Naphthalene Chemical compound C1=CC=CC2=CC=CC=C21 UFWIBTONFRDIAS-UHFFFAOYSA-N 0.000 description 4
- YGYAWVDWMABLBF-UHFFFAOYSA-N Phosgene Chemical compound ClC(Cl)=O YGYAWVDWMABLBF-UHFFFAOYSA-N 0.000 description 4
- 239000005708 Sodium hypochlorite Substances 0.000 description 4
- 239000000654 additive Substances 0.000 description 4
- 239000002245 particle Substances 0.000 description 4
- SUKJFIGYRHOWBL-UHFFFAOYSA-N sodium hypochlorite Chemical compound [Na+].Cl[O-] SUKJFIGYRHOWBL-UHFFFAOYSA-N 0.000 description 4
- UHOVQNZJYSORNB-UHFFFAOYSA-N Benzene Chemical compound C1=CC=CC=C1 UHOVQNZJYSORNB-UHFFFAOYSA-N 0.000 description 3
- YXFVVABEGXRONW-UHFFFAOYSA-N Toluene Chemical compound CC1=CC=CC=C1 YXFVVABEGXRONW-UHFFFAOYSA-N 0.000 description 3
- 239000002253 acid Substances 0.000 description 3
- FDQSRULYDNDXQB-UHFFFAOYSA-N benzene-1,3-dicarbonyl chloride Chemical compound ClC(=O)C1=CC=CC(C(Cl)=O)=C1 FDQSRULYDNDXQB-UHFFFAOYSA-N 0.000 description 3
- KKEYFWRCBNTPAC-UHFFFAOYSA-N benzene-dicarboxylic acid Natural products OC(=O)C1=CC=C(C(O)=O)C=C1 KKEYFWRCBNTPAC-UHFFFAOYSA-N 0.000 description 3
- 238000006243 chemical reaction Methods 0.000 description 3
- 238000005660 chlorination reaction Methods 0.000 description 3
- 239000008367 deionised water Substances 0.000 description 3
- 229910021641 deionized water Inorganic materials 0.000 description 3
- 239000012527 feed solution Substances 0.000 description 3
- 229910002804 graphite Inorganic materials 0.000 description 3
- 239000010439 graphite Substances 0.000 description 3
- 150000002500 ions Chemical class 0.000 description 3
- 150000002576 ketones Chemical class 0.000 description 3
- 239000002346 layers by function Substances 0.000 description 3
- 238000011068 loading method Methods 0.000 description 3
- 229910052943 magnesium sulfate Inorganic materials 0.000 description 3
- 235000019341 magnesium sulphate Nutrition 0.000 description 3
- 239000001044 red dye Substances 0.000 description 3
- PYWVYCXTNDRMGF-UHFFFAOYSA-N rhodamine B Chemical compound [Cl-].C=12C=CC(=[N+](CC)CC)C=C2OC2=CC(N(CC)CC)=CC=C2C=1C1=CC=CC=C1C(O)=O PYWVYCXTNDRMGF-UHFFFAOYSA-N 0.000 description 3
- CXWXQJXEFPUFDZ-UHFFFAOYSA-N tetralin Chemical compound C1=CC=C2CCCCC2=C1 CXWXQJXEFPUFDZ-UHFFFAOYSA-N 0.000 description 3
- UMFBMIMWJUUXLR-UHFFFAOYSA-N (3,5-dicarbonochloridoylphenyl) carbonochloridate Chemical compound ClC(=O)OC1=CC(C(Cl)=O)=CC(C(Cl)=O)=C1 UMFBMIMWJUUXLR-UHFFFAOYSA-N 0.000 description 2
- UIMAOHVEKLXJDO-UHFFFAOYSA-N (7,7-dimethyl-3-oxo-4-bicyclo[2.2.1]heptanyl)methanesulfonate;triethylazanium Chemical compound CCN(CC)CC.C1CC2(CS(O)(=O)=O)C(=O)CC1C2(C)C UIMAOHVEKLXJDO-UHFFFAOYSA-N 0.000 description 2
- GWHJZXXIDMPWGX-UHFFFAOYSA-N 1,2,4-trimethylbenzene Chemical compound CC1=CC=C(C)C(C)=C1 GWHJZXXIDMPWGX-UHFFFAOYSA-N 0.000 description 2
- LFSAPCRASZRSKS-UHFFFAOYSA-N 2-methylcyclohexan-1-one Chemical compound CC1CCCCC1=O LFSAPCRASZRSKS-UHFFFAOYSA-N 0.000 description 2
- RSCMSACQRPYYRN-UHFFFAOYSA-N 3,5-diaminobenzamide Chemical compound NC(=O)C1=CC(N)=CC(N)=C1 RSCMSACQRPYYRN-UHFFFAOYSA-N 0.000 description 2
- QYAMZFPPWQRILI-UHFFFAOYSA-N 5-isocyanatobenzene-1,3-dicarbonyl chloride Chemical compound ClC(=O)C1=CC(N=C=O)=CC(C(Cl)=O)=C1 QYAMZFPPWQRILI-UHFFFAOYSA-N 0.000 description 2
- XMWRBQBLMFGWIX-UHFFFAOYSA-N C60 fullerene Chemical compound C12=C3C(C4=C56)=C7C8=C5C5=C9C%10=C6C6=C4C1=C1C4=C6C6=C%10C%10=C9C9=C%11C5=C8C5=C8C7=C3C3=C7C2=C1C1=C2C4=C6C4=C%10C6=C9C9=C%11C5=C5C8=C3C3=C7C1=C1C2=C4C6=C2C9=C5C3=C12 XMWRBQBLMFGWIX-UHFFFAOYSA-N 0.000 description 2
- VEXZGXHMUGYJMC-UHFFFAOYSA-M Chloride anion Chemical compound [Cl-] VEXZGXHMUGYJMC-UHFFFAOYSA-M 0.000 description 2
- XDTMQSROBMDMFD-UHFFFAOYSA-N Cyclohexane Chemical compound C1CCCCC1 XDTMQSROBMDMFD-UHFFFAOYSA-N 0.000 description 2
- YNQLUTRBYVCPMQ-UHFFFAOYSA-N Ethylbenzene Chemical compound CCC1=CC=CC=C1 YNQLUTRBYVCPMQ-UHFFFAOYSA-N 0.000 description 2
- SECXISVLQFMRJM-UHFFFAOYSA-N N-Methylpyrrolidone Chemical compound CN1CCCC1=O SECXISVLQFMRJM-UHFFFAOYSA-N 0.000 description 2
- MKYBYDHXWVHEJW-UHFFFAOYSA-N N-[1-oxo-1-(2,4,6,7-tetrahydrotriazolo[4,5-c]pyridin-5-yl)propan-2-yl]-2-[[3-(trifluoromethoxy)phenyl]methylamino]pyrimidine-5-carboxamide Chemical compound O=C(C(C)NC(=O)C=1C=NC(=NC=1)NCC1=CC(=CC=C1)OC(F)(F)F)N1CC2=C(CC1)NN=N2 MKYBYDHXWVHEJW-UHFFFAOYSA-N 0.000 description 2
- 239000004695 Polyether sulfone Substances 0.000 description 2
- 239000002202 Polyethylene glycol Substances 0.000 description 2
- 230000000996 additive effect Effects 0.000 description 2
- 230000001464 adherent effect Effects 0.000 description 2
- 125000001931 aliphatic group Chemical group 0.000 description 2
- 150000001338 aliphatic hydrocarbons Chemical class 0.000 description 2
- RDOXTESZEPMUJZ-UHFFFAOYSA-N anisole Chemical compound COC1=CC=CC=C1 RDOXTESZEPMUJZ-UHFFFAOYSA-N 0.000 description 2
- 230000008901 benefit Effects 0.000 description 2
- RPHKINMPYFJSCF-UHFFFAOYSA-N benzene-1,3,5-triamine Chemical compound NC1=CC(N)=CC(N)=C1 RPHKINMPYFJSCF-UHFFFAOYSA-N 0.000 description 2
- HDPRVQJRZUJZPT-UHFFFAOYSA-N benzene-1,3,5-trisulfonyl chloride Chemical compound ClS(=O)(=O)C1=CC(S(Cl)(=O)=O)=CC(S(Cl)(=O)=O)=C1 HDPRVQJRZUJZPT-UHFFFAOYSA-N 0.000 description 2
- 150000001555 benzenes Chemical class 0.000 description 2
- 238000009835 boiling Methods 0.000 description 2
- 125000003178 carboxy group Chemical group [H]OC(*)=O 0.000 description 2
- 239000003054 catalyst Substances 0.000 description 2
- MVPPADPHJFYWMZ-UHFFFAOYSA-N chlorobenzene Chemical compound ClC1=CC=CC=C1 MVPPADPHJFYWMZ-UHFFFAOYSA-N 0.000 description 2
- 239000008199 coating composition Substances 0.000 description 2
- 150000001875 compounds Chemical class 0.000 description 2
- 238000009833 condensation Methods 0.000 description 2
- 230000005494 condensation Effects 0.000 description 2
- 229920001577 copolymer Polymers 0.000 description 2
- RWGFKTVRMDUZSP-UHFFFAOYSA-N cumene Chemical compound CC(C)C1=CC=CC=C1 RWGFKTVRMDUZSP-UHFFFAOYSA-N 0.000 description 2
- 150000003997 cyclic ketones Chemical class 0.000 description 2
- SHQSVMDWKBRBGB-UHFFFAOYSA-N cyclobutanone Chemical compound O=C1CCC1 SHQSVMDWKBRBGB-UHFFFAOYSA-N 0.000 description 2
- CGZZMOTZOONQIA-UHFFFAOYSA-N cycloheptanone Chemical compound O=C1CCCCCC1 CGZZMOTZOONQIA-UHFFFAOYSA-N 0.000 description 2
- FWFSEYBSWVRWGL-UHFFFAOYSA-N cyclohex-2-enone Chemical compound O=C1CCCC=C1 FWFSEYBSWVRWGL-UHFFFAOYSA-N 0.000 description 2
- IIRFCWANHMSDCG-UHFFFAOYSA-N cyclooctanone Chemical compound O=C1CCCCCCC1 IIRFCWANHMSDCG-UHFFFAOYSA-N 0.000 description 2
- 230000007547 defect Effects 0.000 description 2
- 150000004985 diamines Chemical class 0.000 description 2
- 238000003618 dip coating Methods 0.000 description 2
- WJJMNDUMQPNECX-UHFFFAOYSA-N dipicolinic acid Chemical compound OC(=O)C1=CC=CC(C(O)=O)=N1 WJJMNDUMQPNECX-UHFFFAOYSA-N 0.000 description 2
- 230000000694 effects Effects 0.000 description 2
- 238000005516 engineering process Methods 0.000 description 2
- 239000004744 fabric Substances 0.000 description 2
- 239000013505 freshwater Substances 0.000 description 2
- 238000010438 heat treatment Methods 0.000 description 2
- 230000006872 improvement Effects 0.000 description 2
- 239000002198 insoluble material Substances 0.000 description 2
- KQNPFQTWMSNSAP-UHFFFAOYSA-N isobutyric acid Chemical compound CC(C)C(O)=O KQNPFQTWMSNSAP-UHFFFAOYSA-N 0.000 description 2
- 238000012986 modification Methods 0.000 description 2
- 230000004048 modification Effects 0.000 description 2
- 239000002086 nanomaterial Substances 0.000 description 2
- LQNUZADURLCDLV-UHFFFAOYSA-N nitrobenzene Chemical compound [O-][N+](=O)C1=CC=CC=C1 LQNUZADURLCDLV-UHFFFAOYSA-N 0.000 description 2
- 239000002736 nonionic surfactant Substances 0.000 description 2
- 230000003204 osmotic effect Effects 0.000 description 2
- JLPJFSCQKHRSQR-UHFFFAOYSA-N oxolan-3-one Chemical compound O=C1CCOC1 JLPJFSCQKHRSQR-UHFFFAOYSA-N 0.000 description 2
- 229920006393 polyether sulfone Polymers 0.000 description 2
- 229920001223 polyethylene glycol Polymers 0.000 description 2
- 229920005597 polymer membrane Polymers 0.000 description 2
- 238000006116 polymerization reaction Methods 0.000 description 2
- 229920000036 polyvinylpyrrolidone Polymers 0.000 description 2
- 239000001267 polyvinylpyrrolidone Substances 0.000 description 2
- 235000013855 polyvinylpyrrolidone Nutrition 0.000 description 2
- UOHMMEJUHBCKEE-UHFFFAOYSA-N prehnitene Chemical compound CC1=CC=C(C)C(C)=C1C UOHMMEJUHBCKEE-UHFFFAOYSA-N 0.000 description 2
- CYIDZMCFTVVTJO-UHFFFAOYSA-N pyromellitic acid Chemical compound OC(=O)C1=CC(C(O)=O)=C(C(O)=O)C=C1C(O)=O CYIDZMCFTVVTJO-UHFFFAOYSA-N 0.000 description 2
- 241000894007 species Species 0.000 description 2
- 230000003068 static effect Effects 0.000 description 2
- 239000000126 substance Substances 0.000 description 2
- 239000004094 surface-active agent Substances 0.000 description 2
- 238000003786 synthesis reaction Methods 0.000 description 2
- LXEJRKJRKIFVNY-UHFFFAOYSA-N terephthaloyl chloride Chemical compound ClC(=O)C1=CC=C(C(Cl)=O)C=C1 LXEJRKJRKIFVNY-UHFFFAOYSA-N 0.000 description 2
- DSXFPRKPFJRPIB-UHFFFAOYSA-N thiolan-3-one Chemical compound O=C1CCSC1 DSXFPRKPFJRPIB-UHFFFAOYSA-N 0.000 description 2
- MIOPJNTWMNEORI-GMSGAONNSA-N (S)-camphorsulfonic acid Chemical compound C1C[C@@]2(CS(O)(=O)=O)C(=O)C[C@@H]1C2(C)C MIOPJNTWMNEORI-GMSGAONNSA-N 0.000 description 1
- RQHPYGROUIBUSW-UHFFFAOYSA-N 1,2,3-trimethylnaphthalene Chemical class C1=CC=C2C(C)=C(C)C(C)=CC2=C1 RQHPYGROUIBUSW-UHFFFAOYSA-N 0.000 description 1
- WQONPSCCEXUXTQ-UHFFFAOYSA-N 1,2-dibromobenzene Chemical class BrC1=CC=CC=C1Br WQONPSCCEXUXTQ-UHFFFAOYSA-N 0.000 description 1
- MOXLHAPKZWTHEX-UHFFFAOYSA-N 1,2-dichloronaphthalene Chemical class C1=CC=CC2=C(Cl)C(Cl)=CC=C21 MOXLHAPKZWTHEX-UHFFFAOYSA-N 0.000 description 1
- MTZUIIAIAKMWLI-UHFFFAOYSA-N 1,2-diisocyanatobenzene Chemical class O=C=NC1=CC=CC=C1N=C=O MTZUIIAIAKMWLI-UHFFFAOYSA-N 0.000 description 1
- QNLZIZAQLLYXTC-UHFFFAOYSA-N 1,2-dimethylnaphthalene Chemical class C1=CC=CC2=C(C)C(C)=CC=C21 QNLZIZAQLLYXTC-UHFFFAOYSA-N 0.000 description 1
- KPZGRMZPZLOPBS-UHFFFAOYSA-N 1,3-dichloro-2,2-bis(chloromethyl)propane Chemical compound ClCC(CCl)(CCl)CCl KPZGRMZPZLOPBS-UHFFFAOYSA-N 0.000 description 1
- FQUYSHZXSKYCSY-UHFFFAOYSA-N 1,4-diazepane Chemical compound C1CNCCNC1 FQUYSHZXSKYCSY-UHFFFAOYSA-N 0.000 description 1
- RXYPXQSKLGGKOL-UHFFFAOYSA-N 1,4-dimethylpiperazine Chemical compound CN1CCN(C)CC1 RXYPXQSKLGGKOL-UHFFFAOYSA-N 0.000 description 1
- AMBFNDRKYCJLNH-UHFFFAOYSA-N 1-(3-piperidin-1-ylpropyl)piperidine Chemical compound C1CCCCN1CCCN1CCCCC1 AMBFNDRKYCJLNH-UHFFFAOYSA-N 0.000 description 1
- PVOAHINGSUIXLS-UHFFFAOYSA-N 1-Methylpiperazine Chemical compound CN1CCNCC1 PVOAHINGSUIXLS-UHFFFAOYSA-N 0.000 description 1
- DLKQHBOKULLWDQ-UHFFFAOYSA-N 1-bromonaphthalene Chemical class C1=CC=C2C(Br)=CC=CC2=C1 DLKQHBOKULLWDQ-UHFFFAOYSA-N 0.000 description 1
- JTPNRXUCIXHOKM-UHFFFAOYSA-N 1-chloronaphthalene Chemical class C1=CC=C2C(Cl)=CC=CC2=C1 JTPNRXUCIXHOKM-UHFFFAOYSA-N 0.000 description 1
- JIMRSFDTUBLGOO-UHFFFAOYSA-N 1-chlorosulfonylcyclohexa-3,5-diene-1,3-dicarbonyl chloride Chemical compound ClC(=O)C1=CC=CC(S(Cl)(=O)=O)(C(Cl)=O)C1 JIMRSFDTUBLGOO-UHFFFAOYSA-N 0.000 description 1
- HYFLWBNQFMXCPA-UHFFFAOYSA-N 1-ethyl-2-methylbenzene Chemical compound CCC1=CC=CC=C1C HYFLWBNQFMXCPA-UHFFFAOYSA-N 0.000 description 1
- KGRVJHAUYBGFFP-UHFFFAOYSA-N 2,2'-Methylenebis(4-methyl-6-tert-butylphenol) Chemical compound CC(C)(C)C1=CC(C)=CC(CC=2C(=C(C=C(C)C=2)C(C)(C)C)O)=C1O KGRVJHAUYBGFFP-UHFFFAOYSA-N 0.000 description 1
- VVJIVFKAROPUOS-UHFFFAOYSA-N 2,2-bis(aminomethyl)propane-1,3-diamine Chemical compound NCC(CN)(CN)CN VVJIVFKAROPUOS-UHFFFAOYSA-N 0.000 description 1
- NSMWYRLQHIXVAP-UHFFFAOYSA-N 2,5-dimethylpiperazine Chemical compound CC1CNC(C)CN1 NSMWYRLQHIXVAP-UHFFFAOYSA-N 0.000 description 1
- UTESMPAHZRAKMZ-UHFFFAOYSA-N 2,7-dinitropyrene Chemical class C1=C([N+]([O-])=O)C=C2C=CC3=CC([N+](=O)[O-])=CC4=CC=C1C2=C43 UTESMPAHZRAKMZ-UHFFFAOYSA-N 0.000 description 1
- PXBFMLJZNCDSMP-UHFFFAOYSA-N 2-Aminobenzamide Chemical class NC(=O)C1=CC=CC=C1N PXBFMLJZNCDSMP-UHFFFAOYSA-N 0.000 description 1
- NGNBDVOYPDDBFK-UHFFFAOYSA-N 2-[2,4-di(pentan-2-yl)phenoxy]acetyl chloride Chemical compound CCCC(C)C1=CC=C(OCC(Cl)=O)C(C(C)CCC)=C1 NGNBDVOYPDDBFK-UHFFFAOYSA-N 0.000 description 1
- UENRXLSRMCSUSN-UHFFFAOYSA-N 3,5-diaminobenzoic acid Chemical compound NC1=CC(N)=CC(C(O)=O)=C1 UENRXLSRMCSUSN-UHFFFAOYSA-N 0.000 description 1
- YLZOPXRUQYQQID-UHFFFAOYSA-N 3-(2,4,6,7-tetrahydrotriazolo[4,5-c]pyridin-5-yl)-1-[4-[2-[[3-(trifluoromethoxy)phenyl]methylamino]pyrimidin-5-yl]piperazin-1-yl]propan-1-one Chemical compound N1N=NC=2CN(CCC=21)CCC(=O)N1CCN(CC1)C=1C=NC(=NC=1)NCC1=CC(=CC=C1)OC(F)(F)F YLZOPXRUQYQQID-UHFFFAOYSA-N 0.000 description 1
- QIKYZXDTTPVVAC-UHFFFAOYSA-N 4-Aminobenzamide Chemical compound NC(=O)C1=CC=C(N)C=C1 QIKYZXDTTPVVAC-UHFFFAOYSA-N 0.000 description 1
- VZNUCJOYPXKLTA-UHFFFAOYSA-N 5-chlorobenzene-1,3-diamine Chemical compound NC1=CC(N)=CC(Cl)=C1 VZNUCJOYPXKLTA-UHFFFAOYSA-N 0.000 description 1
- JPPYSPAXPNNOBC-UHFFFAOYSA-N 5-chlorosulfonylbenzene-1,3-dicarbonyl chloride Chemical compound ClC(=O)C1=CC(C(Cl)=O)=CC(S(Cl)(=O)=O)=C1 JPPYSPAXPNNOBC-UHFFFAOYSA-N 0.000 description 1
- ZOXJGFHDIHLPTG-UHFFFAOYSA-N Boron Chemical compound [B] ZOXJGFHDIHLPTG-UHFFFAOYSA-N 0.000 description 1
- PZNSFCLAULLKQX-UHFFFAOYSA-N Boron nitride Chemical compound N#B PZNSFCLAULLKQX-UHFFFAOYSA-N 0.000 description 1
- 239000005057 Hexamethylene diisocyanate Substances 0.000 description 1
- NIPNSKYNPDTRPC-UHFFFAOYSA-N N-[2-oxo-2-(2,4,6,7-tetrahydrotriazolo[4,5-c]pyridin-5-yl)ethyl]-2-[[3-(trifluoromethoxy)phenyl]methylamino]pyrimidine-5-carboxamide Chemical compound O=C(CNC(=O)C=1C=NC(=NC=1)NCC1=CC(=CC=C1)OC(F)(F)F)N1CC2=C(CC1)NN=N2 NIPNSKYNPDTRPC-UHFFFAOYSA-N 0.000 description 1
- AFCARXCZXQIEQB-UHFFFAOYSA-N N-[3-oxo-3-(2,4,6,7-tetrahydrotriazolo[4,5-c]pyridin-5-yl)propyl]-2-[[3-(trifluoromethoxy)phenyl]methylamino]pyrimidine-5-carboxamide Chemical compound O=C(CCNC(=O)C=1C=NC(=NC=1)NCC1=CC(=CC=C1)OC(F)(F)F)N1CC2=C(CC1)NN=N2 AFCARXCZXQIEQB-UHFFFAOYSA-N 0.000 description 1
- WWEXBGFSEVKZNE-UHFFFAOYSA-N N=C=O.N=C=O.C1=CC=CC2=CC=CC=C21 Chemical class N=C=O.N=C=O.C1=CC=CC2=CC=CC=C21 WWEXBGFSEVKZNE-UHFFFAOYSA-N 0.000 description 1
- BDJRBEYXGGNYIS-UHFFFAOYSA-N Nonanedioid acid Natural products OC(=O)CCCCCCCC(O)=O BDJRBEYXGGNYIS-UHFFFAOYSA-N 0.000 description 1
- CTQNGGLPUBDAKN-UHFFFAOYSA-N O-Xylene Chemical compound CC1=CC=CC=C1C CTQNGGLPUBDAKN-UHFFFAOYSA-N 0.000 description 1
- REYJJPSVUYRZGE-UHFFFAOYSA-N Octadecylamine Chemical compound CCCCCCCCCCCCCCCCCCN REYJJPSVUYRZGE-UHFFFAOYSA-N 0.000 description 1
- 239000002033 PVDF binder Substances 0.000 description 1
- 229920002873 Polyethylenimine Polymers 0.000 description 1
- 239000004743 Polypropylene Substances 0.000 description 1
- 229920002396 Polyurea Polymers 0.000 description 1
- 239000004372 Polyvinyl alcohol Substances 0.000 description 1
- ZMANZCXQSJIPKH-UHFFFAOYSA-N Triethylamine Chemical class CCN(CC)CC ZMANZCXQSJIPKH-UHFFFAOYSA-N 0.000 description 1
- 241000212749 Zesius chrysomallus Species 0.000 description 1
- FHKPLLOSJHHKNU-INIZCTEOSA-N [(3S)-3-[8-(1-ethyl-5-methylpyrazol-4-yl)-9-methylpurin-6-yl]oxypyrrolidin-1-yl]-(oxan-4-yl)methanone Chemical compound C(C)N1N=CC(=C1C)C=1N(C2=NC=NC(=C2N=1)O[C@@H]1CN(CC1)C(=O)C1CCOCC1)C FHKPLLOSJHHKNU-INIZCTEOSA-N 0.000 description 1
- ISKQADXMHQSTHK-UHFFFAOYSA-N [4-(aminomethyl)phenyl]methanamine Chemical compound NCC1=CC=C(CN)C=C1 ISKQADXMHQSTHK-UHFFFAOYSA-N 0.000 description 1
- 235000011037 adipic acid Nutrition 0.000 description 1
- 239000001361 adipic acid Substances 0.000 description 1
- 150000001298 alcohols Chemical class 0.000 description 1
- 150000001408 amides Chemical class 0.000 description 1
- 150000001412 amines Chemical class 0.000 description 1
- 125000003277 amino group Chemical group 0.000 description 1
- 150000004945 aromatic hydrocarbons Chemical class 0.000 description 1
- YCOXTKKNXUZSKD-UHFFFAOYSA-N as-o-xylenol Natural products CC1=CC=C(O)C=C1C YCOXTKKNXUZSKD-UHFFFAOYSA-N 0.000 description 1
- 230000004888 barrier function Effects 0.000 description 1
- RUOKPLVTMFHRJE-UHFFFAOYSA-N benzene-1,2,3-triamine Chemical class NC1=CC=CC(N)=C1N RUOKPLVTMFHRJE-UHFFFAOYSA-N 0.000 description 1
- CJPIDIRJSIUWRJ-UHFFFAOYSA-N benzene-1,2,4-tricarbonyl chloride Chemical compound ClC(=O)C1=CC=C(C(Cl)=O)C(C(Cl)=O)=C1 CJPIDIRJSIUWRJ-UHFFFAOYSA-N 0.000 description 1
- ALIQZUMMPOYCIS-UHFFFAOYSA-N benzene-1,3-disulfonyl chloride Chemical compound ClS(=O)(=O)C1=CC=CC(S(Cl)(=O)=O)=C1 ALIQZUMMPOYCIS-UHFFFAOYSA-N 0.000 description 1
- GCAIEATUVJFSMC-UHFFFAOYSA-N benzenetetracarboxylic acid Natural products OC(=O)C1=CC=C(C(O)=O)C(C(O)=O)=C1C(O)=O GCAIEATUVJFSMC-UHFFFAOYSA-N 0.000 description 1
- UJMDYLWCYJJYMO-UHFFFAOYSA-N benzenetricarboxylic Acid Natural products OC(=O)C1=CC=CC(C(O)=O)=C1C(O)=O UJMDYLWCYJJYMO-UHFFFAOYSA-N 0.000 description 1
- 238000009529 body temperature measurement Methods 0.000 description 1
- 229910052796 boron Inorganic materials 0.000 description 1
- 150000004768 bromobenzenes Chemical class 0.000 description 1
- 229920002678 cellulose Polymers 0.000 description 1
- 239000000919 ceramic Substances 0.000 description 1
- 150000001805 chlorine compounds Chemical class 0.000 description 1
- NNBZCPXTIHJBJL-AOOOYVTPSA-N cis-decalin Chemical compound C1CCC[C@H]2CCCC[C@H]21 NNBZCPXTIHJBJL-AOOOYVTPSA-N 0.000 description 1
- 239000012141 concentrate Substances 0.000 description 1
- 239000002826 coolant Substances 0.000 description 1
- ZOLLIQAKMYWTBR-UHFFFAOYSA-N cyclododeca-1,5,9-triene Chemical compound C1CC=CCCC=CCCC=C1 ZOLLIQAKMYWTBR-UHFFFAOYSA-N 0.000 description 1
- ZZLVWYATVGCIFR-UHFFFAOYSA-N cyclohexane-1,1,2-triamine Chemical class NC1CCCCC1(N)N ZZLVWYATVGCIFR-UHFFFAOYSA-N 0.000 description 1
- YMHQVDAATAEZLO-UHFFFAOYSA-N cyclohexane-1,1-diamine Chemical class NC1(N)CCCCC1 YMHQVDAATAEZLO-UHFFFAOYSA-N 0.000 description 1
- SSJXIUAHEKJCMH-UHFFFAOYSA-N cyclohexane-1,2-diamine Chemical compound NC1CCCCC1N SSJXIUAHEKJCMH-UHFFFAOYSA-N 0.000 description 1
- UYAUGHKQCCCFDK-UHFFFAOYSA-N cyclohexane-1,3,5-triamine Chemical compound NC1CC(N)CC(N)C1 UYAUGHKQCCCFDK-UHFFFAOYSA-N 0.000 description 1
- WLPXOECYEATUCV-UHFFFAOYSA-N cyclohexane-1,3-dicarbonyl chloride Chemical compound ClC(=O)C1CCCC(C(Cl)=O)C1 WLPXOECYEATUCV-UHFFFAOYSA-N 0.000 description 1
- VKIRRGRTJUUZHS-UHFFFAOYSA-N cyclohexane-1,4-diamine Chemical compound NC1CCC(N)CC1 VKIRRGRTJUUZHS-UHFFFAOYSA-N 0.000 description 1
- HXTYZWJVMWWWDK-UHFFFAOYSA-N cyclohexane-1,4-dicarbonyl chloride Chemical compound ClC(=O)C1CCC(C(Cl)=O)CC1 HXTYZWJVMWWWDK-UHFFFAOYSA-N 0.000 description 1
- QECQLMGRLZYSEW-UHFFFAOYSA-N decoxybenzene Chemical compound CCCCCCCCCCOC1=CC=CC=C1 QECQLMGRLZYSEW-UHFFFAOYSA-N 0.000 description 1
- 238000011033 desalting Methods 0.000 description 1
- 238000007607 die coating method Methods 0.000 description 1
- 239000012971 dimethylpiperazine Substances 0.000 description 1
- ZZTCPWRAHWXWCH-UHFFFAOYSA-N diphenylmethanediamine Chemical class C=1C=CC=CC=1C(N)(N)C1=CC=CC=C1 ZZTCPWRAHWXWCH-UHFFFAOYSA-N 0.000 description 1
- KWKXNDCHNDYVRT-UHFFFAOYSA-N dodecylbenzene Chemical compound CCCCCCCCCCCCC1=CC=CC=C1 KWKXNDCHNDYVRT-UHFFFAOYSA-N 0.000 description 1
- 239000002079 double walled nanotube Substances 0.000 description 1
- 230000035622 drinking Effects 0.000 description 1
- 238000001035 drying Methods 0.000 description 1
- 230000002708 enhancing effect Effects 0.000 description 1
- 150000002148 esters Chemical class 0.000 description 1
- 150000002170 ethers Chemical class 0.000 description 1
- 229940058172 ethylbenzene Drugs 0.000 description 1
- 239000012467 final product Substances 0.000 description 1
- 235000013305 food Nutrition 0.000 description 1
- ANSXAPJVJOKRDJ-UHFFFAOYSA-N furo[3,4-f][2]benzofuran-1,3,5,7-tetrone Chemical compound C1=C2C(=O)OC(=O)C2=CC2=C1C(=O)OC2=O ANSXAPJVJOKRDJ-UHFFFAOYSA-N 0.000 description 1
- 238000007429 general method Methods 0.000 description 1
- RRAMGCGOFNQTLD-UHFFFAOYSA-N hexamethylene diisocyanate Chemical compound O=C=NCCCCCCN=C=O RRAMGCGOFNQTLD-UHFFFAOYSA-N 0.000 description 1
- WNLRTRBMVRJNCN-UHFFFAOYSA-N hexanedioic acid Natural products OC(=O)CCCCC(O)=O WNLRTRBMVRJNCN-UHFFFAOYSA-N 0.000 description 1
- 239000007970 homogeneous dispersion Substances 0.000 description 1
- 239000008240 homogeneous mixture Substances 0.000 description 1
- 125000002887 hydroxy group Chemical group [H]O* 0.000 description 1
- 239000012535 impurity Substances 0.000 description 1
- 238000013101 initial test Methods 0.000 description 1
- SNHMUERNLJLMHN-UHFFFAOYSA-N iodobenzene Chemical compound IC1=CC=CC=C1 SNHMUERNLJLMHN-UHFFFAOYSA-N 0.000 description 1
- 230000001788 irregular Effects 0.000 description 1
- 230000002262 irrigation Effects 0.000 description 1
- 238000003973 irrigation Methods 0.000 description 1
- 238000005259 measurement Methods 0.000 description 1
- AUHZEENZYGFFBQ-UHFFFAOYSA-N mesitylene Substances CC1=CC(C)=CC(C)=C1 AUHZEENZYGFFBQ-UHFFFAOYSA-N 0.000 description 1
- 125000001827 mesitylenyl group Chemical group [H]C1=C(C(*)=C(C([H])=C1C([H])([H])[H])C([H])([H])[H])C([H])([H])[H] 0.000 description 1
- 229910052751 metal Inorganic materials 0.000 description 1
- 239000002184 metal Substances 0.000 description 1
- 150000002739 metals Chemical class 0.000 description 1
- UZKWTJUDCOPSNM-UHFFFAOYSA-N methoxybenzene Substances CCCCOC=C UZKWTJUDCOPSNM-UHFFFAOYSA-N 0.000 description 1
- PYLWMHQQBFSUBP-UHFFFAOYSA-N monofluorobenzene Chemical compound FC1=CC=CC=C1 PYLWMHQQBFSUBP-UHFFFAOYSA-N 0.000 description 1
- ZCCWXQXXLXZMIG-UHFFFAOYSA-N n'-[amino(phenyl)methyl]-n',1-diphenylmethanediamine Chemical compound C=1C=CC=CC=1C(N)N(C=1C=CC=CC=1)C(N)C1=CC=CC=C1 ZCCWXQXXLXZMIG-UHFFFAOYSA-N 0.000 description 1
- CXMXRPHRNRROMY-UHFFFAOYSA-N n-Decanedioic acid Natural products OC(=O)CCCCCCCCC(O)=O CXMXRPHRNRROMY-UHFFFAOYSA-N 0.000 description 1
- TVIDDXQYHWJXFK-UHFFFAOYSA-N n-Dodecanedioic acid Natural products OC(=O)CCCCCCCCCCC(O)=O TVIDDXQYHWJXFK-UHFFFAOYSA-N 0.000 description 1
- 239000002105 nanoparticle Substances 0.000 description 1
- 239000007783 nanoporous material Substances 0.000 description 1
- ZBJSGOMTEOPTBH-UHFFFAOYSA-N naphthalene-1,3,6-trisulfonyl chloride Chemical compound ClS(=O)(=O)C1=CC(S(Cl)(=O)=O)=CC2=CC(S(=O)(=O)Cl)=CC=C21 ZBJSGOMTEOPTBH-UHFFFAOYSA-N 0.000 description 1
- 150000002790 naphthalenes Chemical class 0.000 description 1
- WSVDSBZMYJJMSB-UHFFFAOYSA-N octadecylbenzene Chemical compound CCCCCCCCCCCCCCCCCCC1=CC=CC=C1 WSVDSBZMYJJMSB-UHFFFAOYSA-N 0.000 description 1
- CDKDZKXSXLNROY-UHFFFAOYSA-N octylbenzene Chemical compound CCCCCCCCC1=CC=CC=C1 CDKDZKXSXLNROY-UHFFFAOYSA-N 0.000 description 1
- 239000003960 organic solvent Substances 0.000 description 1
- 230000001590 oxidative effect Effects 0.000 description 1
- HFPZCAJZSCWRBC-UHFFFAOYSA-N p-cymene Chemical compound CC(C)C1=CC=C(C)C=C1 HFPZCAJZSCWRBC-UHFFFAOYSA-N 0.000 description 1
- BEZDDPMMPIDMGJ-UHFFFAOYSA-N pentamethylbenzene Chemical compound CC1=CC(C)=C(C)C(C)=C1C BEZDDPMMPIDMGJ-UHFFFAOYSA-N 0.000 description 1
- DLRJIFUOBPOJNS-UHFFFAOYSA-N phenetole Chemical compound CCOC1=CC=CC=C1 DLRJIFUOBPOJNS-UHFFFAOYSA-N 0.000 description 1
- DGTNSSLYPYDJGL-UHFFFAOYSA-N phenyl isocyanate Chemical class O=C=NC1=CC=CC=C1 DGTNSSLYPYDJGL-UHFFFAOYSA-N 0.000 description 1
- 150000004986 phenylenediamines Chemical class 0.000 description 1
- GHAIYFTVRRTBNG-UHFFFAOYSA-N piperazin-1-ylmethanamine Chemical compound NCN1CCNCC1 GHAIYFTVRRTBNG-UHFFFAOYSA-N 0.000 description 1
- LTEKQAPRXFBRNN-UHFFFAOYSA-N piperidin-4-ylmethanamine Chemical compound NCC1CCNCC1 LTEKQAPRXFBRNN-UHFFFAOYSA-N 0.000 description 1
- 229920000090 poly(aryl ether) Polymers 0.000 description 1
- 229920000509 poly(aryleneethynylene) polymer Polymers 0.000 description 1
- 229920000553 poly(phenylenevinylene) Polymers 0.000 description 1
- 229920002239 polyacrylonitrile Polymers 0.000 description 1
- 125000003367 polycyclic group Chemical group 0.000 description 1
- 229920000728 polyester Polymers 0.000 description 1
- 229920006149 polyester-amide block copolymer Polymers 0.000 description 1
- 229920001155 polypropylene Polymers 0.000 description 1
- 229920002635 polyurethane Polymers 0.000 description 1
- 239000004814 polyurethane Substances 0.000 description 1
- 229920002451 polyvinyl alcohol Polymers 0.000 description 1
- 229920000915 polyvinyl chloride Polymers 0.000 description 1
- 239000004800 polyvinyl chloride Substances 0.000 description 1
- 229920002981 polyvinylidene fluoride Polymers 0.000 description 1
- 230000002035 prolonged effect Effects 0.000 description 1
- 238000005086 pumping Methods 0.000 description 1
- 238000000746 purification Methods 0.000 description 1
- WPNXWWLAOCWIDT-UHFFFAOYSA-N pyridine-2,3-dicarbonyl chloride Chemical compound ClC(=O)C1=CC=CN=C1C(Cl)=O WPNXWWLAOCWIDT-UHFFFAOYSA-N 0.000 description 1
- GJAWHXHKYYXBSV-UHFFFAOYSA-N pyridinedicarboxylic acid Natural products OC(=O)C1=CC=CN=C1C(O)=O GJAWHXHKYYXBSV-UHFFFAOYSA-N 0.000 description 1
- 238000011084 recovery Methods 0.000 description 1
- 230000000717 retained effect Effects 0.000 description 1
- 239000000523 sample Substances 0.000 description 1
- 238000000926 separation method Methods 0.000 description 1
- 239000002356 single layer Substances 0.000 description 1
- 238000007764 slot die coating Methods 0.000 description 1
- 239000011877 solvent mixture Substances 0.000 description 1
- 238000005507 spraying Methods 0.000 description 1
- 238000010186 staining Methods 0.000 description 1
- 229910001220 stainless steel Inorganic materials 0.000 description 1
- 239000010935 stainless steel Substances 0.000 description 1
- 238000003860 storage Methods 0.000 description 1
- HXJUTPCZVOIRIF-UHFFFAOYSA-N sulfolane Chemical compound O=S1(=O)CCCC1 HXJUTPCZVOIRIF-UHFFFAOYSA-N 0.000 description 1
- JOUDBUYBGJYFFP-FOCLMDBBSA-N thioindigo Chemical compound S\1C2=CC=CC=C2C(=O)C/1=C1/C(=O)C2=CC=CC=C2S1 JOUDBUYBGJYFFP-FOCLMDBBSA-N 0.000 description 1
- DVKJHBMWWAPEIU-UHFFFAOYSA-N toluene 2,4-diisocyanate Chemical compound CC1=CC=C(N=C=O)C=C1N=C=O DVKJHBMWWAPEIU-UHFFFAOYSA-N 0.000 description 1
- NNBZCPXTIHJBJL-MGCOHNPYSA-N trans-decalin Chemical compound C1CCC[C@@H]2CCCC[C@H]21 NNBZCPXTIHJBJL-MGCOHNPYSA-N 0.000 description 1
- KNXVOGGZOFOROK-UHFFFAOYSA-N trimagnesium;dioxido(oxo)silane;hydroxy-oxido-oxosilane Chemical compound [Mg+2].[Mg+2].[Mg+2].O[Si]([O-])=O.O[Si]([O-])=O.[O-][Si]([O-])=O.[O-][Si]([O-])=O KNXVOGGZOFOROK-UHFFFAOYSA-N 0.000 description 1
- SRPWOOOHEPICQU-UHFFFAOYSA-N trimellitic anhydride Chemical compound OC(=O)C1=CC=C2C(=O)OC(=O)C2=C1 SRPWOOOHEPICQU-UHFFFAOYSA-N 0.000 description 1
- 150000005199 trimethylbenzenes Chemical class 0.000 description 1
- 239000008096 xylene Substances 0.000 description 1
- 150000003738 xylenes Chemical class 0.000 description 1
- GKXVJHDEWHKBFH-UHFFFAOYSA-N xylylenediamine group Chemical group C=1(C(=CC=CC1)CN)CN GKXVJHDEWHKBFH-UHFFFAOYSA-N 0.000 description 1
Classifications
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01D—SEPARATION
- B01D69/00—Semi-permeable membranes for separation processes or apparatus characterised by their form, structure or properties; Manufacturing processes specially adapted therefor
- B01D69/12—Composite membranes; Ultra-thin membranes
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01D—SEPARATION
- B01D67/00—Processes specially adapted for manufacturing semi-permeable membranes for separation processes or apparatus
- B01D67/0079—Manufacture of membranes comprising organic and inorganic components
- B01D67/00793—Dispersing a component, e.g. as particles or powder, in another component
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01D—SEPARATION
- B01D69/00—Semi-permeable membranes for separation processes or apparatus characterised by their form, structure or properties; Manufacturing processes specially adapted therefor
- B01D69/14—Dynamic membranes
- B01D69/141—Heterogeneous membranes, e.g. containing dispersed material; Mixed matrix membranes
- B01D69/148—Organic/inorganic mixed matrix membranes
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01D—SEPARATION
- B01D71/00—Semi-permeable membranes for separation processes or apparatus characterised by the material; Manufacturing processes specially adapted therefor
- B01D71/02—Inorganic material
- B01D71/021—Carbon
- B01D71/0212—Carbon nanotubes
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B82—NANOTECHNOLOGY
- B82Y—SPECIFIC USES OR APPLICATIONS OF NANOSTRUCTURES; MEASUREMENT OR ANALYSIS OF NANOSTRUCTURES; MANUFACTURE OR TREATMENT OF NANOSTRUCTURES
- B82Y30/00—Nanotechnology for materials or surface science, e.g. nanocomposites
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B82—NANOTECHNOLOGY
- B82Y—SPECIFIC USES OR APPLICATIONS OF NANOSTRUCTURES; MEASUREMENT OR ANALYSIS OF NANOSTRUCTURES; MANUFACTURE OR TREATMENT OF NANOSTRUCTURES
- B82Y40/00—Manufacture or treatment of nanostructures
-
- C—CHEMISTRY; METALLURGY
- C01—INORGANIC CHEMISTRY
- C01B—NON-METALLIC ELEMENTS; COMPOUNDS THEREOF; METALLOIDS OR COMPOUNDS THEREOF NOT COVERED BY SUBCLASS C01C
- C01B32/00—Carbon; Compounds thereof
- C01B32/15—Nano-sized carbon materials
- C01B32/158—Carbon nanotubes
- C01B32/168—After-treatment
- C01B32/174—Derivatisation; Solubilisation; Dispersion in solvents
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01D—SEPARATION
- B01D61/00—Processes of separation using semi-permeable membranes, e.g. dialysis, osmosis or ultrafiltration; Apparatus, accessories or auxiliary operations specially adapted therefor
- B01D61/02—Reverse osmosis; Hyperfiltration ; Nanofiltration
- B01D61/025—Reverse osmosis; Hyperfiltration
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01D—SEPARATION
- B01D67/00—Processes specially adapted for manufacturing semi-permeable membranes for separation processes or apparatus
- B01D67/0002—Organic membrane manufacture
- B01D67/0006—Organic membrane manufacture by chemical reactions
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01D—SEPARATION
- B01D71/00—Semi-permeable membranes for separation processes or apparatus characterised by the material; Manufacturing processes specially adapted therefor
- B01D71/06—Organic material
- B01D71/56—Polyamides, e.g. polyester-amides
-
- C—CHEMISTRY; METALLURGY
- C01—INORGANIC CHEMISTRY
- C01B—NON-METALLIC ELEMENTS; COMPOUNDS THEREOF; METALLOIDS OR COMPOUNDS THEREOF NOT COVERED BY SUBCLASS C01C
- C01B2202/00—Structure or properties of carbon nanotubes
- C01B2202/20—Nanotubes characterized by their properties
- C01B2202/28—Solid content in solvents
-
- C—CHEMISTRY; METALLURGY
- C01—INORGANIC CHEMISTRY
- C01B—NON-METALLIC ELEMENTS; COMPOUNDS THEREOF; METALLOIDS OR COMPOUNDS THEREOF NOT COVERED BY SUBCLASS C01C
- C01B2202/00—Structure or properties of carbon nanotubes
- C01B2202/20—Nanotubes characterized by their properties
- C01B2202/36—Diameter
Definitions
- Reverse osmosis (RO) desalination uses membrane technology to transform seawater and brackish water into fresh water for drinking, irrigation and industrial applications. Reverse osmosis desalination processes require substantially less energy than thermal desalination processes. As a result, the majority of recent commercial projects use more cost-effective reverse osmosis membranes to produce fresh water from seawater or brackish water. Over the years, advances in membrane technology and energy recovery devices have made reverse osmosis more affordable and efficient. Despite its capacity to efficiently remove ionic species at as high as99.8% salt rejection, there remains a need for reverse osmosis membranes that possess improved flux characteristics while maintaining useful rejection characteristics.
- Reverse osmosis is the process of forcing a solvent from a region of high solute concentration through a membrane to a region of low solute concentration by applying a pressure in excess of the osmotic pressure. This is the reverse of the normal osmosis process, which is the natural movement of solvent from an area of low solute concentration, through a membrane, to an area of high solute
- the membrane here is semipermeable, meaning it allows the passage of solvent but not of solute.
- the membranes used for reverse osmosis have a dense barrier layer where most separation occurs. In most cases the membrane is designed to allow only water to pass through this dense layer while preventing the passage of solutes (such as salt ions). Examples of reverse osmosis processes are the purification of brackish water and seawater, where often less than 1% of the impurity species in the seawater or brackish water are found in the permeate.
- the reverse osmosis process requires that a high pressure be exerted on the high concentration side of the membrane, usually 2-17 bar (30-250 psi) for fresh and brackish water, and 40-70 bar (600-1000 psi) for seawater, which has around 24 bar (350 psi) natural osmotic pressure which must be overcome.
- Nanofiltration in concept and operation, is much the same as reverse osmosis.
- the key difference is the degree of removal of monovalent ions such as chlorides.
- Reverse osmosis removes about 99% of the monovalent ions.
- Nanofiltration membranes removal of monovalent ions varies between 50% to 90% depending on the material and manufacture of the membrane. Nanofiltration membranes and systems are used for water softening, food and pharmaceutical applications.
- An example of a nanofiltration process is the desalting of a sugar solution, where 80% of the salt passes through the membrane with the water and 95% of the sugar is retained by the membrane.
- Nanotubes such as carbon and boron nanotubes are fundamentally new nanoporous materials that have great potential for membrane applications.
- the current methods of synthesis of CNT membranes involve multiple steps and are limited to making membrane samples of extremely small area. They are not scalable to large surface areas necessary for the fabrication of commercial membranes for practical applications.
- Membranes containing carbon nanotubes have been disclosed for use in purifying water.
- WO 2006/060721 assigned to National University of Singapore, describes thin film composite (TFC) membranes containing multi-walled carbon nanotubes (MWNT) in an active layer prepared by interfacial polymerization.
- the WNTs are characterized as having an outside diameter of 30-50 nm.
- further improvements in the performance of TFC membranes for reverse osmosis applications are desirable.
- the present invention relates to processes for manufacturing a thin film composite membrane comprising multi-walled carbon nantubes.
- the processes include contacting under interfacial polymerization conditions an organic solution comprising a polyacid halide with an aqueous solution comprising a polyamine to form a thin film composite membrane on a surface of a porous base membrane; at least one of the organic solution and the aqueous solution further including multi-walled carbon nanotubes having an outside diameter of less than about 30 nm.
- solvents for use in compositions containing nanotubes may have density greater than about 0.8 and solubility in water of less than about 100 g/L.
- the solvent may be a single compound or a mixture having the specified density and water solubility.
- Particularly suitable solvents having these properties are cis- and frans-decalin, and mixtures thereof.
- Solvents for use in the processes of the present invention may additionally be insoluble in the polysulfone base membranes commonly used in preparing reverse osmosis membranes.
- polysulfone insoluble and “insoluble in polysulfones” means that such materials swell or dissolve polysulfone.
- Polysulfone insoluble materials may be included in compositions of the present invention in minor amounts, that is, less than about 50% by weight, based on total weight of the composition. In some embodiments, the polysulfone insoluble materials are present at less than or equal to about 10% by weight, in others at less than or equal to about 5% by weight, and in still others, less than or equal to about 3% by weight.
- the solvent is a saturated cyclic C 5 -C 20 hydrocarbon solvent.
- the saturated cyclic C 5 -C 2 o hydrocarbon solvent is a saturated polycyclic compound, or a mixture or one or more saturated polycyclic compounds, for example, cis-decalin, trans-decalin, cyclohexyl halides, and 1 ,5,9- cyclododecatrien and derivatives or a mixture thereof.
- compositions of the present invention and organic solutions for use in the processes of the present invention may also include at least one saturated acyclic C4-C30 alkane compound, such as hexane or one or more isoparaffins.
- Suitable isoparaffins include the ISOPARTM series from ExxonMobil (including, but not limited to, ISOPARTM E, ISOPARTM G, ISOPARTM H, ISOPARTM L, and ISOPARTM M).
- the saturated cyclic C5-C20 hydrocarbon loading in the organic solution is greater than about 20% w w (weight of saturated cyclic C5-C20 hydrocarbon/total weight of solvent, not including monomer or nanotubes); in some embodiments, greater than about 50% w/w, and in other embodiments, greater than about 80% w/w.
- the organic solution may additionally include a cyclic ketone such as cyclooctanone, cycloheptanone, 2 methylcyclohexanone, cyclohexanone, cyclohexene-3-one, cyclopentanone, cyclobutanone, 3-ketotetrahydrofuran, 3- ketotetrahydrothiophene, or 3-ketoxetane, particularly, cyclohexanone.
- Aqueous dispersions may include dispersing aids such as polyvinylpyrrolidone, or surfactants, particularly non-ionic surfactants.
- compositions of the present invention and organic solutions for use in the processes of the present invention may also include other additives.
- the additive loading in the solvent mixture is in the range of 0.1 to 20 wt%, preferably in the range of 0.5% to 10%, and more preferably in the range of 1 to 10%.
- These other additives include the following compounds with molar volumes in the range of 50 cm3/mol-1 or higher (preferably 80 or higher) and Hildebrand solubility parameters in the range of 8.5 to 10.5 cal n cm .
- aromatic hydrocarbons such as tetralin, dodecylbenzene, octadecylbenzene, benzene, toluene, xylene, mesitylene, anisole, dimethylbenzenes, trimethylbenzenes, tetramethylbenzene, ethyl-benzene .fluorobenzene, chlorobenzene, bromobenzenes, dibromobenzenes, iodobenzene, nitrobenzene, ethyl-toluene, pentamethyl-benzene, octyl-benzene, cumene, pseudo- cumene, para-cymene, phenetole, and phenoxy-decane; naphthalenes such as methylnaphtha!enes, dimethylnaphthalenes, trimethylnaphthalenes, ethylnaphthalenes phen
- Nanotubes for use with solvents having density greater than about 0.8 and solubility in water of less than about 100 g/L include single wall, double wall, and multiwall carbon nanotubes and boron nitride nanotubes with various internal and external diameters and length.
- Nanotubes with carboxyl (COOH), hydroxyl (OH) carbonyl chloride (-COCI), functionalized with octadecylamine, functionalized with PEG (polyethylene glycol) may be used.
- Nanotubes with carbonyl chloride (-COCI) may be covalently bonded to polyamide thin film to avoid the leach out of nanotubes during membrane service.
- the nanotubes typically have a cylindrical nanostructure with an inside diameter (ID) and outside diameters (OD).
- Concentration of the nanotubes in the organic solution or the aqueous solution is at least 0.025% w/w, and may range from about 0.025% w/w to about 10% w/w in some embodiments, and in others, ranges from about 0.025% w/w to about 5% w/w. In yet other embodiments, the concentration of the nanotubes ranges from about 0.05% w/w to about 1% w/w.
- the thin film composite (TFC) membranes that may be prepared by a process according to the present invention are composed of a separating functional layer formed on a porous base support.
- the separating functional layer is thin in order to maximize membrane flux performance, and is formed on a porous support or base membrane to provide mechanical strength.
- TFC membranes that may be prepared include, but are not limited to, reverse osmosis membranes composed of a polyamide separating functional layer formed on a porous polysulfone support, nanofiltration membranes, and other thin film composite membrane.
- Interfacial polymerization includes contacting an aqueous solution of one or more nucleophilic monomers onto a porous support membrane; followed by coating an organic solution, generally in an aliphatic solvent, containing one or more electrophilic monomers.
- a thin film polymer is formed from condensation of the electrophilic and nucleophilic monomers and is adherent to the porous support. The rate of thin film formation may be accelerated by heating or addition of catalysts.
- the polyacid halide monomer on contact with the polyamine monomer reacts on the surface of the porous base membrane to afford a polyamide disposed on the surface of the porous support membrane. Suitable monomers useful in the present invention are described below.
- the membrane comprises a polymer having an amine group.
- the polymer may be produced by interfacial polymerization.
- Interfacial polymerization includes a process widely used for the synthesis of thin film membranes for reverse osmosis, hyperfiltration, and nanofiltration.
- Interfacial polymerization includes coating a first solution, generally aqueous, of one or more nucleophilic monomers onto a porous base support; followed by coating a second solution, generally in an aliphatic solvent, containing one or more electrophilic monomers. The second solution is immiscible with the first solution.
- a thin film polymer is formed from condensation of the electrophilic and nucleophilic monomers and is adherent to the porous base support.
- the rate of thin film formation may be accelerated by heating or addition of catalysts.
- nucleophilic monomers include, but are not limited to, amine containing monomers such as polyethylenimines; cyclohexanediamines; 1 ,2- diaminocyclohexane; 1 ,4-diaminocyclohexane; piperazine; methyl piperazine;
- dimethylpiperazine e.g. 2,5-dimethyl piperazine
- homopiperazine 1,3- bis(piperidyl)propane
- 4-aminomethylpiperazine cyclohexanetriamines (e.g. 1,3,5- triaminocyclohexane)
- xylylenediamines o-, m-, p-xylenediamine
- phenylenediamines ⁇ e.g. m-phenylene diamine and p-phenylenediamine, 3,5- diaminobenzoic acid, 3,5-diamonsulfonic acid); chloropheny!enediamines (e.g. 4- or 5-chloro-m-phenylenediamine); benzenetriamines (e.g. 1 ,3,5-benzenetriamine, 1,2,4- triamino enzene); bis(aminobenzyl) aniline; tetraaminobenzenes; diaminobiphenyls (e.g. 4,4,'-diaminobiphenyl; tetrakis(aminomethyl)methane;
- chloropheny!enediamines e.g. 4- or 5-chloro-m-phenylenediamine
- benzenetriamines e.g. 1 ,3,5-benzenetriamine, 1,2,4- triamino
- diaminodiphenylmethanes ⁇ , ⁇ '-diphenylethylenediamine
- aminobenzamides e.g. 4- aminobenzamide, 3,3'-diaminobenzamide; 3,5-diaminobenzamide; 3,5- diaminobenzamide; 3,3'5,5'-tetraaminobenzamide); either individually or in any combinations thereof.
- nucleophilic monomers for the present invention include m-phenylenediamine, p-phenylenediamine, 1 ,3,5-triaminobenzene, piperazine, 4- aminomethylpiperidine, and either individually or in any combinations thereof. More particularly, nucleophilic monomer useful in the present invention includes m- phenylene diamine.
- electrophilic monomers include, but are not limited to, acid halide-terminated polyamide oligomers (e.g. copolymers of piperazine with an excess of isophthaloyl chloride); benzene dicarboxylic acid halides (e.g. isophthaloyl chloride or terephthaloyl chloride); benzene tricarboxylic acid halides (e.g. trimesoyl chloride or trimellitic acid trichloride); cyclohexane dicarboxylic acid halides (e.g.
- cyclohexane tricarboxylic acid halides e.g.cis-1 ,3,5-cyclohexane tricarboxylic acid trichloride
- pyridine dicarboxylic acid halides e.g. quinolinic acid dichloride or dipicolinic acid dichloride
- trimellitic anhydride acid halides benzene tetra carboxylic acid halides (e.g. pyromellitic acid tetrachloride); pyromellitic acid dianhydride;
- pyridine tricarboxylic acid halides sebacic acid halides; azelaic acid halides; adipic acid halides; dodecanedioic acid halides; toluene diisocyanate; methylenebis(phenyl isocyanates); naphthalene diisocyanates; bitolyl diisocyanates; hexamethylene diisocyanate; phenylene diisocyanates; isocyanato benzene dicarboxylic acid halides (e.g. 5-isocyanato isophthaloyl chloride); haloformyloxy benzene dicarboxylic acid halides (e.g.
- 5-chloroformyloxy isophthaloyl chloride dihalosulfonyl benzenes (e.g. 1 ,3-benzenedisulfonic acid chloride); halosulfonyl benzene dicarboxylic acid halides (e.g. 3-chlorosulfonyl isophthaloyl chloride); 1,3,6-tri(chlorosulfonyl)naphthalene; 1 ,3,7 tri(chlorosulfonyl)napthalene; trihalosulfonyl benzenes (e.g.
- Particular electrophilic monomers include, but are not limited to, terephthaloyl chloride, isophthaloyl chloride, 5-isocyanato isophthaloyl chloride, 5-chloroformyloxy isophthaloyl chloride, 5-chlorosulfonyl isophthaloyl chloride, 1 ,3,6- (trichlorosutfonyl)naphthalene, 1 ,3,7-(trichlorosulfonyl)napthalene, 1 ,3,5- trichlorosulfonyl benzene, either individually or in any combinations thereof. More particular electrophilic monomers include trimesoyl chloride acid chloride
- the interfacial polymerization reaction may be carried out at a temperature ranging from about 5°C to about 60°C, preferably from about 10°C to about 40°C to produce an interfacial polymer membrane.
- interfacial polymers produced thereform include polyamide, polysulfonamide, polyurethane, polyurea, and polyesteramides, either individually or in any combinations thereof.
- a porous base support includes a support material having a surface pore size in the approximate range from about 50 Angstroms to about 5000 Angstroms.
- the pore sizes should be sufficiently large so that a permeate solvent can pass through the support without reducing the flux of the composite.
- the pores should not be so large that the permselective polymer membrane will either be unable to bridge or form across the pores, or tend to fill up or penetrate too far into the pores, thus producing an effectively thicker membrane than 200 nanometers.
- U.S. Pat. No. 4,814,082 W. J. Wrasidlo
- U.S. Pat. No. 4,783,346 S. A. Sundet
- Non-limiting examples of the material forming the porous base support include polysulfone, polyether sulfone, polyacrylonitrile, cellulose ester,
- porous base membranes are either available commercially or may be prepared using techniques known to those of ordinary skill in the art.
- a porous base membrane which is a polysulfone membrane or a porous polyethersulfone membrane are used because of their desirable mechanical and chemical properties. Those of ordinary skill in the art will be able to make the selection from among the suitable materials.
- the thickness of the material forming the porous base support may be between about 75 and about 250 microns thick, although other thicknesses may be used. For example, a 25 microns thick porous base support permits production of higher flux films.
- the porous base support may be relatively thick, for example, 2.5 cm or more, where aqueous solution is applied to only one side, which is subsequently contacted with the organic solution, forming the interface at which polymerization occurs.
- the polymeric porous base support may be reinforced by backing with a fabric or a non-woven web material. Non-limiting examples include films, sheets, and nets such as a nonwoven polyester cloth.
- the polymer of the porous base support may permeate through the pores, be attached on both sides of the support, or be attached substantially on one side of the support.
- the thin film composite membrane may be post-treated with an oxidizing solution, such as a sodium hypochlorite solution.
- an oxidizing solution such as a sodium hypochlorite solution.
- concentration of sodium hypochlorite in the solution may range from about 50 ppm to about 4000 ppm, and, in some embodiments, from about 50 ppm to about 500 ppm.
- the organic solution or the aqueous solution, or both the organic solution and the aqueous solution may include, in addition to the polyacid halide monomer or the polyamine monomer, multi- walled carbon nanotubes dispersed therein.
- Suitable organic solvents include aliphatic hydrocarbons, alcohols, ketones, esters, ethers, amides, and mixtures thereof.
- aliphatic hydrocarbons such as decalins, and isoparaffins, and mixtures thereof may be used.
- the organic solution may additionally include a cyclic ketone such as cyclooctanone, cycloheptanone, 2 methylcyclohexanone, cyclohexanone, cyclohexene-3-one, cyclopentanone, cyclobutanone, 3-ketotetrahydrofuran, 3-ketotetrahydrothiophene, or 3-ketoxetane, particularly, cyclohexanone.
- Aqueous dispersions may include dispersing aids such as polyvinylpyrrolidone, or surfactants, particularly non-ionic surfactants.
- Carbon nanotubes have a cylindrical nanostructure with an inside diameter (ID) and outside diameters (OD). While single-walled carbon nanotubes (SWNT) are composed of a single layer of graphite in the shape of a tube or cylinder, multiwalled nanotubes (MWNT) are made up of a single rolled layer of graphite or multiple layers of graphite, arranged in concentric cylinders. The MWNTs for use in the processes and membranes of the present invention have an outside diameter of less than about 30 nm, particularly less than about 8 nm. The inner diameter of the multi-walled carbon nanotubes is less than about 8 nm, and particularly useful are nanotubes with inner diameters ranging from about 2 to about 5 nm.
- a WNT designated as having an outside diameter of less than about 30 nm this means that greater than about 50% of the MWNT particles have an outer diameter of less than about 30 nm, in some embodiments, more than about 75% of the MWNT particles have an outer diameter of less than about 30 nm.
- MWNTs are designated as having an outer diameter of less than about 8 nm, it means that more than about 50% of the MWNT particles have an outer diameter of less than about 8 nm, in some embodiments, more than about 75% of the MWNT particles have an outer diameter of less than about 8 nm.
- Concentration of the multi-walled carbon nanotubes in the organic solution or the aqueous solution is at least 0.025% w/w, and may range from about 0.025% w/w to about 10% w/w in some embodiments, and in others, ranges from about 0.025% w/w to about 5% w/w. In yet other embodiments, the concentration of the multi- walled carbon nanotubes ranges from about 0.05% w/w to about 1 % w/w. In yet other embodiments, the concentration of the multi-walled carbon nanotubes ranges from about 0.1 % w/w to about 1 % w/w.
- the concentration of the multi-walled carbon nanotubes ranges from about 0.1 % w/w to about 0.5% w/w.
- the amount of carbon nanotubes contained in the final product ranges from about 0.1%-30% by weight in some embodiments; in other embodiments, from about 1 %-10% by weight, and in still other embodiments, from about 0.5%-5% by weight.
- dispersions of carbon nanotubes in non-polar hydrocarbons such as hexane, cydohexane, and isoparaffins are stable only for short periods, even after prolonged sonication. Dispersion instability may be minimized by incorporating an in-line, continuous mixer/ homogenizer. A dispersion of nanotubes may be mixed with the monomer-containing solutions prior to use in the coating operation using an in-line, continuous mixer/homogenizer in the processes of the present invention in order to maximize stability of the nanotube dispersions.
- a higher-volume stream of a solution of one of the monomers is mixed with a lower volume stream of a carbon nanotube dispersion to form a new dispersion containing both nanotubes and one of the monomers just before the combined coating solution mixture is dispensed on the porous support membrane.
- Suitable mixing/homogenizing devices include static mixers, ultrasonic mixers, dynamic mixers, and other mechanical devices such as industrial mixers and blenders with various types of blades, shafts, and impellers. Static mixers and ultrasonic mixers are examples of preferred devices due to their simplicity and effectiveness.
- the nanotubes dispersion may be under constant or intermittent mixing during the coating operation to ensure the homogeneous dispersion of nanotubes in the coating solution(s).
- the mixing device includes (but not limited to) ultrasonic mixing device, dynamic mixer, and other mechanical devices such as industrial mixers and blenders with various types of blades, shafts, and impellers to make a good quality homogeneous mixture. Ultrasonic mixing is one of the preferred methods.
- the advantage of separating the nanotube dispersion from the monomer solution is that it decouples the various (and often conflicting) requirements of nanotube dispersion stability and solvent compatibility with the porous support.
- conventional coating formulation including conventional solvents such as hexane and ISOPARTM G
- more aggressive solvents that are better at dispersing nanotubes may be used in making the nanotube dispersion prior to combining the two. Since the residence time between the in-line mixing and the coating is minimized, the nanotubes in the dispersion do not have time to agglomerate and segregate. Also, since the solvent used in dispersing nanotubes is typically a minor fraction in the final coating formulation after the in-line mixing, the problem of solvent attacking the porous support is resolved.
- Coating methods typically include dip coating, slot die coating, and spray coating.
- the coating tanks may be used as catch pans to recycle the unused coating solutions.
- the nanotube dispersions may be in-line homogenized outside the coating tanks and recirculated andreplenished during the coating operation.
- the treated surface of the porous base membrane was then contacted with 100 grams of an organic solution containing trimesoyl chloride (0.16% by weight) and carbon nanotubes (type and amount shown in examples) in ISOPARTM G solvent.
- an organic solution containing trimesoyl chloride 0.16% by weight
- carbon nanotubes type and amount shown in examples
- Membrane Performance Testing Membrane tests were carried out on composite membranes configured as a flat sheet in a cross-flow test cell apparatus (Sterlitech Corp., Kent WA) (model CF042) with an effective membrane area of 35.68 cm 2 .
- the test cells were plumbed two in series in each of 6 parallel test lines. Each line of cells was equipped with a valve to turn feed flow on/off and regulate concentrate flow rate, which was set to 1 gallon per minute (gpm) in all tests.
- the test apparatus was equipped with a temperature control system that included a temperature measurement probe, a heat exchanger configured to remove excess heat caused by pumping, and an air-cooled chiller configured to reduce the temperature of the coolant circulated through the heat exchanger.
- rhodamine WT from Cole-Parmer
- a dye solution comprising 1% rhodamine red dye was sprayed on the polyamide surface of the composite membrane and allowed to stand for 1 minute, after which time the red dye was rinsed off. Since rhodamine red dye does not stain polyamide, but stains polysulfone strongly, a defect-free membrane should show no dye stain after thorough rinse.
- dye stain patterns e.g. red spots or other irregular dye staining patterns
- the membranes were cut into 2 inch x 6 inch rectangular coupons, and loaded into cross flow test cells.
- test coupons were exposed to a 70 ppm aqueous solution of sodium hypochlorite at 25°C for 30 minutes. The test coupons were then rinsed with deionized water for 1 hour. [0039] Following the "chlorination" procedure, the test coupons were again tested for reverse osmosis membrane performance with the synthetic feed solution containing 500 ppm sodium chloride used before as described herein. Solution conductivities and temperatures were measured with a CON 11 conductivity meter (Oakton Instruments). Conductivites were compensated to measurement at 25°C. The pH was measured with a Russell RL060P portable pH meter (Thermo Electron Corp). Permeate was collected in a graduated cylinder.
- Permeability or "A value" of each membrane was determined at standard temperatures (77°F or 25°C). Permeability is defined as the rate of flow through the membrane per unit area per unit pressure. Avalues were calculated from permeate weight, collection time, membrane area, and transmembrane pressure. A values reported herein have units of 10 -5 cm 3 /s-cm 2 -atm. Salt concentrations determined from the conductivities of permeate and feed solutions were used to calculate salt rejection values. Conductivitiesof the permeate and feed solutions were measured, and salt concentrations calculated from the conductivity values, to yield salt rejection values.
- the product composite membrane was rinsed with hot deionized water and stored in a refrigerator before until testing or element fabrication.
- the product composite membrane was treated with a solution containing polyvinyl alcohol solution and then dried before storage, testing, or element fabrication.
- a polyamide coated thin film com osite RO membrane was fabricated using a handframe coating apparatus
- An aqueous coating solution (Solution A) was prepared and contained 2.6 wt% m-phenylene diamine (mPD) and 6.6 wt% triethylammonium camphorsulfonate (TEACSA).
- An organic coating solution (Solution B) was prepared and contained 0.16 wt% trimesoyl chloride (TMC) in ISOPARTM G.
- a wet polysulfone porous support film was first coated with the aqueous solution containing the m-phenylenediamine (Solution A) and then coated with the organic solution comprising the trimesoyl chloride (Solution B) to effect an interfacial polymerization reaction between the diamine and the triacid chloride at one surface of the polysulfone porous support film, thereby producing a thin film composite reverse osmosis membrane.
- the product membrane was tested in triplicate using a solution of magnesium sulfate (500 ppm in NaCl) at an applied operating pressure of 115 pounds per square inch (psi) and operating crossflow rate of 1.0 gram per minute (grams per mole), at pH 7.0.
- the permeability and salt passage results are shown in Table 1.
- Comparative Example 1-1 with the exception that the organic coating solution (Solution A) also contained 0.1 wt% fullerene C60 (BU-602-BuckyUSA, Houston TX).
- the product composite membranes were tested and membrane A-values and salt passage properties were measured. Data are shown in Table 1. The data show that coating solution contains fullerene C60 nano-particles showed no significant increase in performance relative to a control (Comparative Example 1-1 ).
- Comparative Example 1 -1 Comparative Example 1 -1 with the exception that the organic coating solution (Solution A) also included 0.1 % w/w single-walled carbon nanotubes (SWNT, P-3, Carbon Solutions, Inc. Riverside, CA, I.D. -1.4 nm, O.D. ⁇ 2 nm.
- the product composite membranes were tested and membrane A-values and salt passage properties were measured. Data are presented in Table 1 -1.
- Comparative Example 1-1 Comparative Example 1-1 with the exception that the organic coating solution (Solution A) further comprised 0.1 wt% multi-walled carbon nanotubes (1238YJS, Nanostructured & Amorphous Materials, Inc., Houston, TX) with inner diameters of 5- 15 nm, outside diameters of 30-50 nm, and 0.5-2 ⁇ in length.
- the product composite membranes were tested and membrane A-values and salt passage properties were measured. Data is shown in Table 1.
- Polyamide thin film composite RO membranes were fabricated as in Comparative Example 1-1 with the exception that the organic coating solution (Solution A) further comprised 0.05% or 0.1 wt% w/w multi-walled carbon nanotubes (1225YJS, Nanostructured & Amorphous Materials, Inc., Houston, TX) I.D.2-5 nm, O.D. ⁇ 8 nm, and 0.5-2 ⁇ in length.
- the product composite membranes were tested and membrane A-values and salt passage properties were measured. Data are gathered in Table 1-1.
- coating solution contains SWNT showed had a significant increase in performance relative to the control without CNTs (Comparative Example 1-1 ), controls with SWNTs (Comparative Example 1-3), and controls with large OD (30-50 nm) MWNT (Comparative Example 1-4).
- Comparative Example 2-1 Instability of CNT dispersions in ISOPARTM G, hexane, and cyclohexane
- 0.01 % single wall carbon nanotubes (P-3 from Carbon Solutions) were dispersed in ISOPARTM G by first sonicating for 60 minutes using a bath sonicator (Branson 5510 model) in a glass vial with screw cap.
- 0.01 wt% multiwall carbon nanotubes with inside diameters of 2-5 nm and outside diameters of less than 8 nm, and a length of 0.5 to 2 mm (1225YJS from Nanostructured and Amorphous Materials, Inc) were dispersed in ISOPARTM G, hexane, and cyclohexane.
- Example 2-3 Stability of CNTs dispersions in decalin , cyclohexanone, and their mixtures.
- 0.1 wt% multiwall carbon nanotubes (1225YJS) were dispersed in a variety of decalins ISOPARTM G mixtures by first sonicating for 60 minutes using a bath sonicator (Branson 5510 model) in a glass vial. After the sonication stopped, the dispersion stability was observed. The dispersions in these decalin mixtures showed fair stability.
- Multiwall carbon nanotubes (1225YJS) at 0.01 wt% loading were dispersed in a variety of cyclohexanone/ ISOPARTM G, mixtures by first sonicating for 60 minutes using a bath sonicator (Branson 5510 model) inside a glass vial with screw cap. After the sonication stopped, the dispersion instability was observed. These carbon nanotube dispersions showed no visible segregation within 30 minutes. Thus the carbon nanotube dispersions in these decalin mixtures showed excellent stability ⁇ Table 5).
- a polyamide coated thin film composite RO membrane was fabricated using a handframe apparatus.
- An aqueous coating solution (Solution A, nominally 90.8 wt% water) was prepared and contained 2.6 wt% meta-phenylene diamine (mPD), and 6.6 wt% triethylammonium camphorsulfonate (TEACSA).
- An organic coating solution (Solution B) was prepared and contained 0.16 wt% trimesoyl chloride (TMC) in ISOPARTM G.
- a wet polysulfone porous support film was first coated with the aqueous solution containing the m-phenylenediamine (Solution A) and then coated with the organic solution comprising the trimesoyl chloride (Solution B) to effect an interfacial polymerization reaction between the diamine and the triacid chloride at one surface of the polysulfone porous support film, thereby producing a thin film composite reverse osmosis membrane.
- the product membrane was tested in triplicate as described in this section using a solution of magnesium sulfate (2000 ppm in NaCl) at an applied operating pressure of 225 pounds per square inch (psi) and operating crossflow rate of 1.0 gallons per minute (gpm), at pH 7.0.
- the test results are shown in Table 6.
- the membrane was contacted with an aqueous solution containing to 70 parts per million (ppm) of sodium hypochlorite at 25 °C for 30 minutes.
- the membrane was then rinsed with water for 1 hour, and then tested again with the magnesium sulfate solution under the same conditions used previously (2000 ppm NaCl, operating pressure 225 psi and operating crossflow rate of 1.0 gpm, pH 7.0, ambient temperature to provide the data in Table 6 labeled "Membrane A Value (after chlorination)" and "% Salt Passage (after chlorination)".
- Polyamide thin film composite RO membranes were fabricated as in Comparative Example 2-1 with the exception that the organic coating solvent (Solution B) were made of decalins, 50:50 decalin/ ISOPARTM G mixture, and 97:3 decalins/cyclohexanone mixture, respectively.
- the product composite membranes were tested and membrane A-values and salt passage properties were measured. Data are gathered in Table 7. The data show that when the organic coating solution contains carbon nanotubes performance is enhanced relative to a control (Comparative Example 2-6)
- Polyamide thin film composite RO membranes were fabricated as in Comparative Example 2-1 with the exception that the organic coating solution (Solution B) further comprised 0.025, 0.05, and 0.1 wt% multiwall carbon nanotubes (1225YJS).
- the product composite membranes were tested and membrane A-values and salt passage properties were measured. Data are gathered in Table 8. The data show that when the organic coating solution contains carbon nanotubes performance was enhanced relative to a control (Comparative Example 2-6)
Landscapes
- Chemical & Material Sciences (AREA)
- Engineering & Computer Science (AREA)
- Nanotechnology (AREA)
- Chemical Kinetics & Catalysis (AREA)
- Inorganic Chemistry (AREA)
- Materials Engineering (AREA)
- Manufacturing & Machinery (AREA)
- Physics & Mathematics (AREA)
- Organic Chemistry (AREA)
- Condensed Matter Physics & Semiconductors (AREA)
- General Physics & Mathematics (AREA)
- Crystallography & Structural Chemistry (AREA)
- Composite Materials (AREA)
- Dispersion Chemistry (AREA)
- Water Supply & Treatment (AREA)
- Separation Using Semi-Permeable Membranes (AREA)
- Carbon And Carbon Compounds (AREA)
- Manufacture Of Porous Articles, And Recovery And Treatment Of Waste Products (AREA)
- Laminated Bodies (AREA)
Priority Applications (6)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
KR1020137010422A KR20130100318A (ko) | 2010-09-30 | 2011-07-25 | 탄소 나노튜브를 포함하는 박막 복합체 막 |
AU2011312781A AU2011312781A1 (en) | 2010-09-30 | 2011-07-25 | Thin film composite membranes incorporating carbon nanotubes |
JP2013531575A JP2014500131A (ja) | 2010-09-30 | 2011-07-25 | カーボンナノチューブを組み込んだ複合薄膜 |
CN2011800468571A CN103124590A (zh) | 2010-09-30 | 2011-07-25 | 结合碳纳米管的薄膜复合膜 |
EP11749977.2A EP2621614A1 (en) | 2010-09-30 | 2011-07-25 | Thin film composite membranes incorporating carbon nanotubes |
CA2811723A CA2811723A1 (en) | 2010-09-30 | 2011-07-25 | Thin film composite membranes incorporating carbon nanotubes |
Applications Claiming Priority (4)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
US12/895,365 US20120080381A1 (en) | 2010-09-30 | 2010-09-30 | Thin film composite membranes incorporating carbon nanotubes |
US12/895,353 | 2010-09-30 | ||
US12/895,365 | 2010-09-30 | ||
US12/895,353 US8591741B2 (en) | 2010-09-30 | 2010-09-30 | Thin film composite membranes incorporating carbon nanotubes |
Publications (1)
Publication Number | Publication Date |
---|---|
WO2012047359A1 true WO2012047359A1 (en) | 2012-04-12 |
Family
ID=45928040
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/US2011/045140 WO2012047359A1 (en) | 2010-09-30 | 2011-07-25 | Thin film composite membranes incorporating carbon nanotubes |
Country Status (7)
Country | Link |
---|---|
EP (1) | EP2621614A1 (zh) |
JP (1) | JP2014500131A (zh) |
KR (1) | KR20130100318A (zh) |
CN (1) | CN103124590A (zh) |
AU (1) | AU2011312781A1 (zh) |
CA (1) | CA2811723A1 (zh) |
WO (1) | WO2012047359A1 (zh) |
Cited By (9)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
FR2996780A1 (fr) * | 2012-10-16 | 2014-04-18 | Univ Claude Bernard Lyon | Procede et dispositif de production d'energie |
WO2014118639A2 (en) * | 2013-01-31 | 2014-08-07 | American University Of Cairo (Auc) | Polymer-carbon nanotube nanocomposite porous membranes |
WO2014168629A1 (en) * | 2013-04-12 | 2014-10-16 | General Electric Company | Membranes comprising graphene |
CN110252155A (zh) * | 2019-06-20 | 2019-09-20 | 西华大学 | 一种抗污染功能化多壁碳纳米管复合膜及其制备方法 |
US10442709B2 (en) | 2015-12-17 | 2019-10-15 | Nitto Denko Corporation | Selectively permeable graphene oxide membrane |
US11000811B2 (en) | 2015-03-31 | 2021-05-11 | Shinshu University | Reverse osmosis composite membrane and method for manufacturing reverse osmosis composite membrane |
US11517861B2 (en) | 2018-07-09 | 2022-12-06 | Lg Chem, Ltd. | Water treatment separation membrane, water treatment module comprising same, and manufacturing method therefor |
US11724234B2 (en) | 2016-08-31 | 2023-08-15 | South Dakota Board Of Regents | Multilayer thin film nanocomposite membranes prepared by molecular layer-by-layer assembly |
EP4146376A4 (en) * | 2020-05-04 | 2024-03-13 | Atom H20, LLC | CARBON NANOTUBE-BASED MEMBRANE AND ITS MANUFACTURING PROCESSES |
Families Citing this family (11)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JP6029156B2 (ja) * | 2012-11-21 | 2016-11-24 | エルジー・ケム・リミテッド | 耐塩素性に優れた高流量水処理分離膜 |
CN105080366B (zh) * | 2014-04-22 | 2017-05-31 | 中国石油化工股份有限公司 | 一种反渗透膜及其制备方法 |
CN105498547B (zh) * | 2015-11-26 | 2018-05-22 | 中国科学院生态环境研究中心 | 一种低压正电荷中空纤维纳滤膜的制备方法 |
JP6733959B2 (ja) * | 2016-09-29 | 2020-08-05 | 国立大学法人信州大学 | 逆浸透複合膜 |
CN107398188A (zh) * | 2017-07-19 | 2017-11-28 | 浙江工业大学 | 接枝有机硅烷多壁碳纳米管嵌入聚酰胺分离层的纳米复合正渗透的制备方法 |
KR102046818B1 (ko) * | 2017-10-16 | 2019-12-02 | 한국과학기술연구원 | 질화 붕소 나노 물질을 이용한 가열 재생 가능한 한외여과막과 그 제조 및 재생 방법 |
CN108114614A (zh) * | 2017-12-21 | 2018-06-05 | 天津工业大学 | 一种含zsm-5沸石的高通量复合反渗透膜及其制备方法 |
WO2020056414A1 (en) * | 2018-09-14 | 2020-03-19 | Ohio State Innovation Foundation | Membranes for gas separation |
JP6999958B2 (ja) * | 2019-12-03 | 2022-02-10 | 国立大学法人信州大学 | 半透複合膜の製造方法及び半透複合膜 |
KR102623644B1 (ko) * | 2021-11-18 | 2024-01-10 | 이화여자대학교 산학협력단 | 고안정성의 보론나이트라이드 세라믹 멤브레인 및 그 제조방법 |
CN116061510B (zh) * | 2022-12-07 | 2023-12-05 | 南通大学 | 一种基于多层自我调节复合非织造材料及制备方法与应用 |
Citations (9)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US4783346A (en) | 1987-12-10 | 1988-11-08 | E. I. Du Pont De Nemours And Company | Process for preparing composite membranes |
US4814082A (en) | 1986-10-20 | 1989-03-21 | Memtec North America Corporation | Ultrafiltration thin film membranes |
EP1362938A1 (en) * | 2002-05-17 | 2003-11-19 | Kabushiki Kaisha Toyota Jidoshokki | Method for refining inorganic short fiber |
US20050244650A1 (en) * | 2004-04-29 | 2005-11-03 | Compagnic Plastic Omnium | Electrically conductive PTFE tape |
US7001556B1 (en) * | 2001-08-16 | 2006-02-21 | The Board Of Regents University Of Oklahoma | Nanotube/matrix composites and methods of production and use |
WO2006060721A1 (en) | 2004-12-03 | 2006-06-08 | William Marsh Rice University | Well-dispersed polymer nanocomposites via interfacial polymerization |
US20060257638A1 (en) * | 2003-01-30 | 2006-11-16 | Glatkowski Paul J | Articles with dispersed conductive coatings |
US20090283475A1 (en) * | 2005-03-11 | 2009-11-19 | New Jersey Institute Of Technology | Carbon Nanotube Mediated Membrane Extraction |
US20090321355A1 (en) * | 2008-06-30 | 2009-12-31 | NANOASIS TECHNOLOGIES, INC., a corporation of the state of Delaware | Membranes with embedded nanotubes for selective permeability |
Family Cites Families (3)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US5234598A (en) * | 1992-05-13 | 1993-08-10 | Allied-Signal Inc. | Thin-film composite membrane |
KR101389656B1 (ko) * | 2005-12-06 | 2014-04-28 | 미츠비시 레이온 가부시키가이샤 | 카본 나노튜브 함유 조성물, 복합체, 및 그것들의 제조방법 |
CN101797522A (zh) * | 2009-02-09 | 2010-08-11 | 乌鲁木齐现代石油化工有限公司 | 蜡油非临氢降凝催化剂再生烧焦的装置及方法 |
-
2011
- 2011-07-25 WO PCT/US2011/045140 patent/WO2012047359A1/en active Application Filing
- 2011-07-25 KR KR1020137010422A patent/KR20130100318A/ko not_active Application Discontinuation
- 2011-07-25 CN CN2011800468571A patent/CN103124590A/zh active Pending
- 2011-07-25 JP JP2013531575A patent/JP2014500131A/ja not_active Withdrawn
- 2011-07-25 EP EP11749977.2A patent/EP2621614A1/en not_active Withdrawn
- 2011-07-25 AU AU2011312781A patent/AU2011312781A1/en not_active Abandoned
- 2011-07-25 CA CA2811723A patent/CA2811723A1/en not_active Abandoned
Patent Citations (9)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US4814082A (en) | 1986-10-20 | 1989-03-21 | Memtec North America Corporation | Ultrafiltration thin film membranes |
US4783346A (en) | 1987-12-10 | 1988-11-08 | E. I. Du Pont De Nemours And Company | Process for preparing composite membranes |
US7001556B1 (en) * | 2001-08-16 | 2006-02-21 | The Board Of Regents University Of Oklahoma | Nanotube/matrix composites and methods of production and use |
EP1362938A1 (en) * | 2002-05-17 | 2003-11-19 | Kabushiki Kaisha Toyota Jidoshokki | Method for refining inorganic short fiber |
US20060257638A1 (en) * | 2003-01-30 | 2006-11-16 | Glatkowski Paul J | Articles with dispersed conductive coatings |
US20050244650A1 (en) * | 2004-04-29 | 2005-11-03 | Compagnic Plastic Omnium | Electrically conductive PTFE tape |
WO2006060721A1 (en) | 2004-12-03 | 2006-06-08 | William Marsh Rice University | Well-dispersed polymer nanocomposites via interfacial polymerization |
US20090283475A1 (en) * | 2005-03-11 | 2009-11-19 | New Jersey Institute Of Technology | Carbon Nanotube Mediated Membrane Extraction |
US20090321355A1 (en) * | 2008-06-30 | 2009-12-31 | NANOASIS TECHNOLOGIES, INC., a corporation of the state of Delaware | Membranes with embedded nanotubes for selective permeability |
Non-Patent Citations (3)
Title |
---|
FORNASIERO, PNAS, 2008 |
HINDS ET AL., SCIENCE, 2004 |
HOLT, SCIENCE, 2006 |
Cited By (16)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
FR2996780A1 (fr) * | 2012-10-16 | 2014-04-18 | Univ Claude Bernard Lyon | Procede et dispositif de production d'energie |
WO2014060690A1 (fr) * | 2012-10-16 | 2014-04-24 | Universite Claude Bernard Lyon I | Procede et dispositif de production d'energie |
US9564652B2 (en) | 2012-10-16 | 2017-02-07 | Universite Claude Bernard Lyon I | Method and device for producing energy |
WO2014118639A3 (en) * | 2013-01-31 | 2014-12-04 | American University Of Cairo (Auc) | Polymer-carbon nanotube nanocomposite porous membranes |
WO2014118639A2 (en) * | 2013-01-31 | 2014-08-07 | American University Of Cairo (Auc) | Polymer-carbon nanotube nanocomposite porous membranes |
WO2014168629A1 (en) * | 2013-04-12 | 2014-10-16 | General Electric Company | Membranes comprising graphene |
CN105073235A (zh) * | 2013-04-12 | 2015-11-18 | 通用电气公司 | 包含石墨烯的膜 |
JP2016522737A (ja) * | 2013-04-12 | 2016-08-04 | ゼネラル・エレクトリック・カンパニイ | グラフェンを含む膜 |
US20160354729A1 (en) * | 2013-04-12 | 2016-12-08 | General Electric Company | Membranes comprising graphene |
CN105073235B (zh) * | 2013-04-12 | 2018-02-06 | 通用电气公司 | 包含石墨烯的膜 |
US11000811B2 (en) | 2015-03-31 | 2021-05-11 | Shinshu University | Reverse osmosis composite membrane and method for manufacturing reverse osmosis composite membrane |
US10442709B2 (en) | 2015-12-17 | 2019-10-15 | Nitto Denko Corporation | Selectively permeable graphene oxide membrane |
US11724234B2 (en) | 2016-08-31 | 2023-08-15 | South Dakota Board Of Regents | Multilayer thin film nanocomposite membranes prepared by molecular layer-by-layer assembly |
US11517861B2 (en) | 2018-07-09 | 2022-12-06 | Lg Chem, Ltd. | Water treatment separation membrane, water treatment module comprising same, and manufacturing method therefor |
CN110252155A (zh) * | 2019-06-20 | 2019-09-20 | 西华大学 | 一种抗污染功能化多壁碳纳米管复合膜及其制备方法 |
EP4146376A4 (en) * | 2020-05-04 | 2024-03-13 | Atom H20, LLC | CARBON NANOTUBE-BASED MEMBRANE AND ITS MANUFACTURING PROCESSES |
Also Published As
Publication number | Publication date |
---|---|
CN103124590A (zh) | 2013-05-29 |
KR20130100318A (ko) | 2013-09-10 |
JP2014500131A (ja) | 2014-01-09 |
EP2621614A1 (en) | 2013-08-07 |
CA2811723A1 (en) | 2012-04-12 |
AU2011312781A1 (en) | 2013-04-04 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
EP2621614A1 (en) | Thin film composite membranes incorporating carbon nanotubes | |
US8591741B2 (en) | Thin film composite membranes incorporating carbon nanotubes | |
US20120080381A1 (en) | Thin film composite membranes incorporating carbon nanotubes | |
CA2729737C (en) | Membranes with embedded nanotubes for selective permeability | |
Lin et al. | Thin film nanocomposite hollow fiber membranes incorporated with surface functionalized HKUST-1 for highly-efficient reverses osmosis desalination process | |
Haghighat et al. | Fouling decline and retention increase of polyvinyl chloride nanofiltration membranes blended by polypyrrole functionalized multiwalled carbon nanotubes | |
Vatanpour et al. | Fabrication and characterization of novel antifouling nanofiltration membrane prepared from oxidized multiwalled carbon nanotube/polyethersulfone nanocomposite | |
Arthanareeswaran et al. | Fabrication of cellulose acetate–zirconia hybrid membranes for ultrafiltration applications: Performance, structure and fouling analysis | |
Yuan et al. | Hydrophilic nanofiltration membranes with reduced humic acid fouling fabricated from copolymers designed by introducing carboxyl groups in the pendant benzene ring | |
US20130146530A1 (en) | Membrane, water treatment system, and method of making | |
US20090321355A1 (en) | Membranes with embedded nanotubes for selective permeability | |
US11000811B2 (en) | Reverse osmosis composite membrane and method for manufacturing reverse osmosis composite membrane | |
Lim et al. | Feasibility and performance of a thin-film composite seawater reverse osmosis membrane fabricated on a highly porous microstructured support | |
EP3181215A1 (en) | Forward osmosis membrane and forward osmosis treatment system | |
US20140209539A1 (en) | Polymer-carbon nanotube nanocomposite porous membranes | |
Mansourpanah et al. | Self-antifouling properties of magnetic Fe2O3/SiO2-modified poly (piperazine amide) active layer for desalting of water: Characterization and performance | |
US20160158707A1 (en) | Novel membranes | |
Ansari et al. | Fabrication of novel poly (phenylene ether ether sulfone) based nanocomposite membrane modified by Fe2NiO4 nanoparticles and ethanol as organic modifier | |
Liu et al. | Boron substituted MFI-type zeolite-coated mesh for oil-water separation | |
Kato et al. | Single-step preparation of nanocomposite polyamide 6 hollow fiber membrane with integrally skinned asymmetric structure for organic solvent nanofiltration | |
CN111437736A (zh) | 含有氧化石墨烯的有机复合膜及其制备方法 | |
Tewfik et al. | Assessment of interfacial polymerization modalities on the performance of polyaniline doped polyethersulphone hollow fiber membranes |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
WWE | Wipo information: entry into national phase |
Ref document number: 201180046857.1 Country of ref document: CN |
|
121 | Ep: the epo has been informed by wipo that ep was designated in this application |
Ref document number: 11749977 Country of ref document: EP Kind code of ref document: A1 |
|
WWE | Wipo information: entry into national phase |
Ref document number: 12013500444 Country of ref document: PH |
|
WWE | Wipo information: entry into national phase |
Ref document number: 2011749977 Country of ref document: EP |
|
ENP | Entry into the national phase |
Ref document number: 2811723 Country of ref document: CA |
|
ENP | Entry into the national phase |
Ref document number: 2013531575 Country of ref document: JP Kind code of ref document: A |
|
NENP | Non-entry into the national phase |
Ref country code: DE |
|
ENP | Entry into the national phase |
Ref document number: 2011312781 Country of ref document: AU Date of ref document: 20110725 Kind code of ref document: A |
|
ENP | Entry into the national phase |