WO2011077804A1 - 透明電極および有機電子デバイス - Google Patents

透明電極および有機電子デバイス Download PDF

Info

Publication number
WO2011077804A1
WO2011077804A1 PCT/JP2010/067218 JP2010067218W WO2011077804A1 WO 2011077804 A1 WO2011077804 A1 WO 2011077804A1 JP 2010067218 W JP2010067218 W JP 2010067218W WO 2011077804 A1 WO2011077804 A1 WO 2011077804A1
Authority
WO
WIPO (PCT)
Prior art keywords
transparent
conductive layer
polymer
binder
electrode
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/JP2010/067218
Other languages
English (en)
French (fr)
Inventor
孝敏 末松
博和 小山
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Konica Minolta Inc
Original Assignee
Konica Minolta Inc
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Konica Minolta Inc filed Critical Konica Minolta Inc
Publication of WO2011077804A1 publication Critical patent/WO2011077804A1/ja
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

　本発明は、フレキシブル透明基板上に、導電性ポリマーとバインダーとを有してなる透明導電層を有する透明電極であって、前記透明導電層の該バインダー同士が架橋構造を有するかまたは、該バインダーと該導電性ポリマーとが架橋構造を有しており、該バインダーが下記一般式（Ａ）で表されるポリマー（Ａ）であり、かつ前記透明導電層のナノインデンテーション弾性率が４ＧＰａ以上１０ＧＰａ以下であることを特徴とし、有機ＥＬ素子、有機太陽電池といった有機電子デバイスに用いることのできる、透明性、平滑性、導電性、可撓性、耐水性に優れた透明電極、および該透明電極を用いた有機電子デバイスが提供できる。　

Description

透明電極および有機電子デバイス
　本発明は、透明電極および有機電子デバイスに関し、詳しくは平滑性、導電性、透明性、可撓性、耐水性に優れた透明電極および該透明電極を用いた有機電子デバイスに関する。
　近年、薄型ＴＶ等の需要の高まりに伴い、液晶、プラズマ、有機ＥＬ、フィールドエミッションなど、各種方式のディスプレイ技術の開発が盛んになされている。これら表示方式がそれぞれ異なる各種ディスプレイにおいても、透明電極は必須の構成技術となっている。また、ＴＶ以外でもタッチパネルや携帯電話、電子ペーパー、各種太陽電池、各種エレクトロルミネッセンス調光素子においても、透明電極は欠くことのできない技術要素となっている。特に、有機ＥＬや有機薄膜太陽電池といった有機電子デバイス用途では、透明電極表面の凹凸による電流のリークや層形成の歪みにより、発光不良、発電不良等が発生しやすく、透明電極表面に対しては高度な平滑性が要求されている。
　有機ＥＬや有機薄膜太陽電池などの有機電子デバイスに用いられる透明電極は、ガラスや透明なプラスチックフィルム等の基材上に、インジウム－スズの複合酸化物（ＩＴＯ）膜に代表される金属酸化物が主に使用されている。しかし、金属酸化物を用いた透明電極は可撓性に劣るため、折り曲げを繰り返すと透明電極表面に微小な亀裂が入るという問題があった。
　この問題を解決する方法としてπ共役系高分子に代表される導電性ポリマーを適当な溶媒に溶解または分散した塗液を用い、塗布や印刷によって透明導電体層を形成する方法（特許文献１参照）が提案されている。しかし、この方法では、ＩＴＯ電極と比較して可撓性が改善されるものの、透明性、導電性が著しく低下するという課題があった。また、異物除去や不純物の除去を目的として導電性ポリマー層を水洗処理すると、導電性ポリマー層が膨潤や溶解することにより、平滑性が損なわれるという課題があった。
　また、ＩＴＯ電極の平滑性向上のため、導電性ポリマーをＩＴＯ電極上に積層する方法も知られている（特許文献２参照）。しかし、この構成では、ＩＴＯ電極上に不純物などの突起が存在すると、導電性ポリマー層の弾性が低いため、電極を折り曲げたときに、導電性ポリマー層が突起部分とともに変形し、有機電子デバイスの機能不良の原因となる。また、これを防ぐために導電性ポリマー層を厚くすると、透明電極の透明性が損なわれ、これらを両立させることは難しい。
　これに対して、ＩＴＯ電極上に導電性ポリマーと非水系バインダーからなる透明導電層を作製する方法（特許文献３参照）が提案されている。非水系バインダー添加により、透明性を損なうことなく、ＩＴＯ電極の可撓性を補うのに必要な透明導電層の強度と厚みを得られるが、導電性ポリマー比率の低下により、透明導電層の導電性が著しく低下するという課題があった。また、特許文献３ではバインダーが非水系であるので、水洗処理によりバインダー中の不純物を取り除くことができず有機電子デバイスの機能が低下するという課題があった。
特開平６－２７３９６４号公報 特開２００３－４５６６５号公報 特表２００８－５３３７０１号公報
　本発明は、上記課題に鑑みなされたものであり、本発明の目的は、有機ＥＬ素子、有機太陽電池といった有機電子デバイスに用いることのできる、透明性、平滑性、導電性、可撓性、耐水性に優れた透明電極、および該透明電極を用いた有機電子デバイスを提供することにある。特に、透明導電層のナノインデンテーション弾性率を制御することにより、可撓性に優れた透明電極および該透明電極を用いた有機電子デバイスを提供することにある。
　本発明の上記目的は、下記の構成により達成される。
　１．フレキシブル透明基板上に、導電性ポリマーとバインダーとを有してなる透明導電層を有する透明電極において、前記透明導電層の該バインダー同士が架橋構造を有するかまたは、該バインダーと該導電性ポリマーとが架橋構造を有しており、該バインダーが下記一般式（Ａ）で表されるポリマー（Ａ）であり、かつ前記透明導電層のナノインデンテーション弾性率が４ＧＰａ以上１０ＧＰａ以下であることを特徴とする透明電極。
Figure JPOXMLDOC01-appb-C000002
　（式中、Ｘ１～Ｘ３はそれぞれ独立に、水素原子またはメチル基を表し、Ｒ１～Ｒ３はそれぞれ独立に、炭素数５以下のアルキレン基を表す。ｌ、ｍ、ｎは構成率（ｍｏｌ％）を表し、５０≦ｌ＋ｍ＋ｎ≦１００である。）
　２．前記透明導電層のナノインデンテーション弾性率が５．５ＧＰａ以上７．０ＧＰａ以下であることを特徴とする前記１に記載の透明電極。
　３．前記導電性ポリマーが、π共役系導電性高分子成分とポリ陰イオン成分とを有してなる導電性ポリマーであることを特徴とする前記１または２に記載の透明電極。
　４．前記ポリ陰イオン成分がポリスルホン酸であることを特徴とする前記３に記載の透明電極。
　５．前記１から４のいずれか１項に記載の透明電極を用いたことを特徴とする有機電子デバイス。
　本発明によれば、有機ＥＬ素子、有機太陽電池といった有機電子デバイスに用いることのできる、透明性、平滑性、導電性、可撓性、耐水性に優れた透明電極、および該透明電極を用いた有機電子デバイスを提供することにある。特に、透明導電層のナノインデンテーション弾性率を制御することにより、可撓性に優れた透明電極および該透明電極を用いた有機電子デバイスを提供することができる。
　以下、本発明を実施するための形態について説明するが、本発明はこれらに限定されない。
　本発明は、フレキシブル透明基板上に、導電性ポリマーとバインダーとを有してなる透明導電層を有する透明電極において、前記透明導電層の該バインダー同士が架橋構造を有するかまたは、該バインダーと該導電性ポリマーとが架橋構造を有しており、該バインダーが上記一般式（Ａ）で表されるポリマー（Ａ）であり、かつ前記透明導電層のナノインデンテーション弾性率が４ＧＰａ以上１０ＧＰａ以下であることを特徴とする。
　本発明においては、特に前記透明導電層のバインダー同士または導電性ポリマーとバインダーとが架橋されており、バインダーが上記ポリマー（Ａ）であり、かつ前記透明導電層のナノインデンテーション弾性率が４ＧＰａ以上１０ＧＰａ以下であることで、透明性、平滑性、導電性、可撓性、耐水性に優れた透明電極が得られる。
　また、本発明において導電性ポリマーとしてπ共役系導電性高分子成分とポリ陰イオン成分とを有してなる導電性ポリマーを用い、バインダーとしてポリマー（Ａ）を用いることにより、より透明性、導電性の優れた透明電極が得られる。
　以下、本発明とその構成要素、及び本発明を実施するための形態・態様等について詳細な説明をする。
　［導電性ポリマー］
　本発明の導電性ポリマーはπ共役系導電性高分子成分とポリ陰イオン成分とを有してなる導電性ポリマーである。
　こうした導電性ポリマーは、後述するπ共役系導電性高分子を形成する前駆体モノマーを、適切な酸化剤と酸化触媒と後述のポリ陰イオンの存在下で化学酸化重合することによって容易に製造できる。
　［π共役系導電性高分子］
　本発明に用いるπ共役系導電性高分子としては、特に限定されず、ポリチオフェン（基本のポリチオフェンを含む、以下同様）類、ポリピロール類、ポリインドール類、ポリカルバゾール類、ポリアニリン類、ポリアセチレン類、ポリフラン類、ポリパラフェニレンビニレン類、ポリアズレン類、ポリパラフェニレン類、ポリパラフェニレンサルファイド類、ポリイソチアナフテン類、ポリチアジル類、の鎖状導電性ポリマーを利用することができる。中でも、導電性、透明性、安定性等の観点からポリチオフェン類やポリアニリン類が好ましい。ポリエチレンジオキシチオフェンであることが最も好ましい。
　［π共役系導電性高分子前駆体モノマー］
　π共役系導電性高分子の形成に用いられる前駆体モノマーは、分子内にπ共役系を有し、適切な酸化剤の作用によって高分子化した際にもその主鎖にπ共役系が形成されるものである。例えば、ピロール類及びその誘導体、チオフェン類及びその誘導体、アニリン類及びその誘導体等が挙げられる。
　該前駆体モノマーの具体例としては、ピロール、３－メチルピロール、３－エチルピロール、３－ｎ－プロピルピロール、３－ブチルピロール、３－オクチルピロール、３－デシルピロール、３－ドデシルピロール、３，４－ジメチルピロール、３，４－ジブチルピロール、３－カルボキシルピロール、３－メチル－４－カルボキシルピロール、３－メチル－４－カルボキシエチルピロール、３－メチル－４－カルボキシブチルピロール、３－ヒドロキシピロール、３－メトキシピロール、３－エトキシピロール、３－ブトキシピロール、３－ヘキシルオキシピロール、３－メチル－４－ヘキシルオキシピロール、チオフェン、３－メチルチオフェン、３－エチルチオフェン、３－プロピルチオフェン、３－ブチルチオフェン、３－ヘキシルチオフェン、３－ヘプチルチオフェン、３－オクチルチオフェン、３－デシルチオフェン、３－ドデシルチオフェン、３－オクタデシルチオフェン、３－ブロモチオフェン、３－クロロチオフェン、３－ヨードチオフェン、３－シアノチオフェン、３－フェニルチオフェン、３，４－ジメチルチオフェン、３，４－ジブチルチオフェン、３－ヒドロキシチオフェン、３－メトキシチオフェン、３－エトキシチオフェン、３－ブトキシチオフェン、３－ヘキシルオキシチオフェン、３－ヘプチルオキシチオフェン、３－オクチルオキシチオフェン、３－デシルオキシチオフェン、３－ドデシルオキシチオフェン、３－オクタデシルオキシチオフェン、３，４－ジヒドロキシチオフェン、３，４－ジメトキシチオフェン、３，４－ジエトキシチオフェン、３，４－ジプロポキシチオフェン、３，４－ジブトキシチオフェン、３，４－ジヘキシルオキシチオフェン、３，４－ジヘプチルオキシチオフェン、３，４－ジオクチルオキシチオフェン、３，４－ジデシルオキシチオフェン、３，４－ジドデシルオキシチオフェン、３，４－エチレンジオキシチオフェン、３，４－プロピレンジオキシチオフェン、３，４－ブテンジオキシチオフェン、３－メチル－４－メトキシチオフェン、３－メチル－４－エトキシチオフェン、３－カルボキシチオフェン、３－メチル－４－カルボキシチオフェン、３－メチル－４－カルボキシエチルチオフェン、３－メチル－４－カルボキシブチルチオフェン、アニリン、２－メチルアニリン、３－イソブチルアニリン、２－アニリンスルホン酸、３－アニリンスルホン酸等が挙げられる。
　［ポリ陰イオン］
　本発明に用いるポリ陰イオンは、置換若しくは未置換のポリアルキレン、置換若しくは未置換のポリアルケニレン、置換若しくは未置換のポリイミド、置換若しくは未置換のポリアミド、置換若しくは未置換のポリエステル及びこれらの共重合体であって、アニオン基を有する構成単位とアニオン基を有さない構成単位とからなるものである。
　このポリ陰イオンは、π共役系導電性高分子を溶媒に可溶化させる可溶化高分子である。
　また、ポリ陰イオンのアニオン基は、π共役系導電性高分子に対するドーパントとして機能して、π共役系導電性高分子の導電性と耐熱性を向上させる。
　ポリ陰イオンのアニオン基としては、π共役系導電性高分子への化学酸化ドープが起こりうる官能基であればよいが、中でも、製造の容易さ及び安定性の観点からは、一置換硫酸エステル基、一置換リン酸エステル基、リン酸基、カルボキシ基、スルホ基等が好ましい。さらに、官能基のπ共役系導電性高分子へのドープ効果の観点より、スルホ基、一置換硫酸エステル基、カルボキシ基がより好ましい。
　ポリ陰イオンの具体例としては、ポリビニルスルホン酸、ポリスチレンスルホン酸、ポリアリルスルホン酸、ポリアクリル酸エチルスルホン酸、ポリアクリル酸ブチルスルホン酸、ポリ－２－アクリルアミド－２－メチルプロパンスルホン酸、ポリイソプレンスルホン酸、ポリビニルカルボン酸、ポリスチレンカルボン酸、ポリアリルカルボン酸、ポリアクリルカルボン酸、ポリメタクリルカルボン酸、ポリ－２－アクリルアミド－２－メチルプロパンカルボン酸、ポリイソプレンカルボン酸、ポリアクリル酸等が挙げられる。これらの単独重合体であってもよいし、２種以上の共重合体であってもよい。
　また、化合物内に更にＦ（フッ素原子）を有するポリ陰イオンであっても良い。具体的には、パーフルオロスルホン酸基を含有するナフィオン（Ｄｕｐｏｎｔ社製）、カルボン酸基を含有するパーフルオロ型ビニルエーテルからなるフレミオン（旭硝子社製）などを挙げることができる。
　これらのうち、スルホン酸を有する化合物であると、導電性ポリマー含有層を塗布、乾燥することによって形成した後に、１００℃以上２００℃以下の温度で５分以上の加熱処理を施した場合、架橋反応が促進するため、塗布膜の洗浄耐性や溶媒耐性が著しく向上することから、特に好ましい。
　さらに、これらの中でも、ポリスチレンスルホン酸、ポリイソプレンスルホン酸、ポリアクリル酸エチルスルホン酸、ポリアクリル酸ブチルスルホン酸が好ましい。これらのポリ陰イオンは、バインダーとの相溶性が高く、また、得られる導電性ポリマーの導電性をより高くできる。
　ポリ陰イオンの重合度は、モノマー単位が１０～１０００００個の範囲であることが好ましく、溶媒溶解性及び導電性の点からは、５０～１００００個の範囲がより好ましい。
　ポリ陰イオンの製造方法としては、例えば、酸を用いてアニオン基を有さないポリマーにアニオン基を直接導入する方法、アニオン基を有さないポリマーをスルホ化剤によりスルホン酸化する方法、アニオン基含有重合性モノマーの重合により製造する方法が挙げられる。
　アニオン基含有重合性モノマーの重合により製造する方法は、溶媒中、アニオン基含有重合性モノマーを、酸化剤及び／又は重合触媒の存在下で、酸化重合又はラジカル重合によって製造する方法が挙げられる。具体的には、所定量のアニオン基含有重合性モノマーを溶媒に溶解させ、これを一定温度に保ち、それに予め溶媒に所定量の酸化剤及び／又は重合触媒を溶解した溶液を添加し、所定時間で反応させる。その反応により得られたポリマーは溶媒によって一定の濃度に調整される。この製造方法において、アニオン基含有重合性モノマーにアニオン基を有さない重合性モノマーを共重合させてもよい。
　アニオン基含有重合性モノマーの重合に際して使用する酸化剤及び酸化触媒、溶媒は、π共役系導電性高分子を形成する前駆体モノマーを重合する際に使用するものと同様である。
　得られたポリマーがポリ陰イオン塩である場合には、ポリ陰イオン酸に変質させることが好ましい。アニオン酸に変質させる方法としては、イオン交換樹脂を用いたイオン交換法、透析法、限外ろ過法等が挙げられ、これらの中でも、作業が容易な点から限外ろ過法が好ましい。
　こうした導電性ポリマーは市販の材料も好ましく利用できる。例えば、ポリ（３，４－エチレンジオキシチオフェン）とポリスチレンスルホン酸からなる導電性ポリマー（ＰＥＤＯＴ－ＰＳＳと略す）が、Ｈ．Ｃ．Ｓｔａｒｃｋ社からＣｌｅｖｉｏｓシリーズとして、Ａｌｄｒｉｃｈ社からＰＥＤＯＴ－ＰＳＳの４８３０９５、５６０５９６として、Ｎａｇａｓｅ　Ｃｈｅｍｔｅｘ社からＤｅｎａｔｒｏｎシリーズとして市販されている。また、ポリアニリンが、日産化学社からＯＲＭＥＣＯＮシリーズとして市販されている。本発明において、こうした剤も好ましく用いることが出来る。
　２ｎｄ．ドーパントとして水溶性有機化合物を含有してもよい。本発明で用いることができる水溶性有機化合物には特に制限はなく、公知のものの中から適宜選択することができ、例えば、酸素含有化合物が好適に挙げられる。前記酸素含有化合物としては、酸素を含有する限り特に制限はなく、例えば、水酸基含有化合物、カルボニル基含有化合物、エーテル基含有化合物、スルホキシド基含有化合物などが挙げられる。前記水酸基含有化合物としては、例えば、エチレングリコール、ジエチレングリコール、プロピレングリコール、トリメチレングリコール、１，４－ブタンジオール、グリセリンなどが挙げられ、これらの中でも、エチレングリコール、ジエチレングリコールが好ましい。前記カルボニル基含有化合物としては、例えば、イソホロン、プロピレンカーボネート、シクロヘキサノン、γ－ブチロラクトンなどが挙げられる。前記エーテル基含有化合物としては、例えば、ジエチレングリコールモノエチルエーテル、などが挙げられる。前記スルホキシド基含有化合物としては、例えば、ジメチルスルホキシドなどが挙げられる。これらは、１種単独で使用してもよいし、２種以上を併用してもよいが、ジメチルスルホキシド、エチレングリコール、ジエチレングリコールから選ばれる少なくとも１種を用いることが好ましい。
　［バインダー］
　本発明のバインダーは、導電性ポリマーとともに透明導電層を形成し、バインダー同士で架橋した構造あるいは、バインダーと導電性ポリマーの少なくとも一部が架橋構造を有することを特徴とする。
　これにより、水洗処理を行っても、膜の溶解や膨潤をすることがなく水洗処理が可能となり、膜上の異物や膜中の不純物を取り除くことができ、有機電子デバイスの電流リークを抑制でき、寿命を向上することができる。
　さらに、バインダー同士あるいは、バインダーと導電性ポリマーの架橋には架橋剤を含んでいても良く、架橋剤は、樹脂との相溶性があり、架橋構造を作れば特に限定されない。例えば架橋剤としてオキサゾリン系架橋剤、カルボジイミド系架橋剤、ブロックイソシアネート系架橋剤、エポキシ系架橋剤、メラミン系架橋剤、ホルムアルデヒド系架橋剤等を単独あるいは複数併用して用いることができる。
　本発明において、バインダーは上記のポリマー（Ａ）であるが、前記導電性ポリマーの陰イオン成分がポリスルホン酸基であることが、ポリマー（Ａ）が導電性をアシストする効果が大きいことから、好ましい態様である。
　本発明に係る透明導電層は、バインダーとしてポリマー（Ａ）以外のバインダーを本発明の効果を損なわない範囲で含有してもよい。ポリマー（Ａ）以外のバインダーとしては、例えばポリエステル系樹脂、アクリル系樹脂、ポリウレタン系樹脂、アクリルウレタン系樹脂、ポリカーボネート系樹脂、セルロース系樹脂、ポリビニルアセタール系樹脂等が挙げられる。
　また、架橋は透明導電層のガラス転移温度やナノインデンテーション弾性率の変化、さらにＦＴＩＲ測定による官能基の変化により測定できる。
　［ナノインデンテーション弾性率］
　本発明におけるナノインデンテーション弾性率とは、透明導電層に微小な針を一定荷重で押し付けて、針のへこみ具合から、弾性率を算出する手法である。
　本発明では、ガラス基板上に作製した透明導電層を測定した値をナノインデンテーション弾性率とした。
　本発明における透明導電層のナノインデンテーション弾性率を１０ＧＰａ以下にすることで、透明導電層は適度な伸縮性をもつことができ、透明電極の折り曲げを繰り返しても、透明導電層表面にヒビが生じることがなく、透明導電層表面の平滑性が保持できる。
　一方、透明導電層のナノインデンテーション弾性率を４ＧＰａ以上にすることで、ＩＴＯ電極などの補助電極上に不純物などの突起が存在しても、電極を折り曲げたときに、突起周辺部の透明導電層の変形を防止できる。
　逆に、透明導電層のナノインデンテーション弾性率を４ＧＰａ以下のとき、補助電極上に不純物などの突起が存在すると、導電性ポリマー層の弾性が低いため、電極の折り曲げると、突起部分とともに透明導電層が変形し、有機電子デバイスの機能不良の原因となる。透明導電層のナノインデンテーション弾性率は５．５ＧＰａ以上、７．０ＧＰａ以下にすることが好ましい。
（ナノインデンテーション弾性率測定）
　ナノインデンテーション弾性率は以下のようにして測定することができる。
　Ｈｙｓｉｔｒｏｎ社製Ｔｒｉｂｏｓｃｏｐｅを用いて、エスアイアイナノテクノロジー社製ＳＰＩ３８００Ｎに装着し測定した。
　測定には、圧子としてベルコビッチ型圧子（先端稜角１４２．３°）と呼ばれる三角錘型ダイヤモンド製圧子で、先端曲率半径７５～１００ｎｍのものを用いた。
　表面に直角に当て、徐々に印加し、最大荷重到達後に荷重を０にまで徐々に戻す。
　この時の最大荷重Ｐを圧子接触部の投影面積Ａで除した値Ｐ／Ａを硬度として算出し、この値（硬度＝Ｐ／Ａ（ＧＰａ））を、ナノインデンテーション弾性率を表す指標として示す。
　［ポリマー（Ａ）］
　本発明に係るポリマー（Ａ）は、前記一般式（Ａ）で表されるポリマー（Ａ）である。一般式（Ａ）中、Ｘ１～Ｘ３はそれぞれ独立に、水素原子またはメチル基を表し、Ｒ１～Ｒ３はそれぞれ独立に、炭素数５以下のアルキレン基を表す。ｌ、ｍ、ｎは構成率（ｍｏｌ％）を表し、５０≦ｌ＋ｍ＋ｎ≦１００である。
　本発明に係るポリマー（Ａ）は、前記一般式（Ａ）で表されるポリマー（Ａ）であり、主たる共重合成分が下記一般式１～３で表されるモノマー（繰り返し単位）１～３であり、共重合成分の５０ｍｏｌ％以上の成分が下記一般式１～３で表されるモノマー１～３のいずれか、あるいは、下記一般式１～３で表されるモノマー１～３の成分の合計が５０ｍｏｌ％以上ある共重合ポリマーであることが好ましい。下記一般式１～３で表されるモノマー１～３の成分の合計が８０ｍｏｌ％以上であることがより好ましく、さらに、下記一般式１～３で表されるモノマー１～３いずれか単独のモノマーから形成されたホモポリマーであっても良く、また、好ましい実施形態である。即ち、一般式（Ａ）において、０≦ｌ≦１００であり、０≦ｍ≦１００であり、０≦ｎ≦１００である。
Figure JPOXMLDOC01-appb-C000003
　（式中、Ｘ１～Ｘ３はそれぞれ独立に、水素原子、またはメチル基を表す。Ｒ１～Ｒ３はそれぞれ独立に、炭素数が５以下のアルキレン基を表す。）
　ポリマー（Ａ）においては、他のモノマー成分が共重合されていてもかまわないが、親水性の高いモノマー成分であることがより好ましい。
　また、ポリマー（Ａ）は数平均分子量において、分子量１０００以下の含有量が０～５質量％以下であることが好ましい。低分子成分が少ないことで、素子の保存性や、導電層に対して垂直方向に電荷をやりとりする際の、層に対して垂直方向に障壁があるような挙動をより低下させることができる。
　このポリマー（Ａ）の数平均分子量において、分子量１０００以下の含有量が０～５質量％以下とする方法としては、再沈殿法、分取ＧＰＣに、リビング重合による単分散のポリマーを合成等により、低分子量成分を除去する、または低分子量成分の生成を抑制する方法を用いることができる。再沈殿法は、ポリマーが溶解可能な溶媒へ溶解し、ポリマーを溶解した溶媒より溶解性の低い溶媒中へ滴下することにより、ポリマーを析出させ、モノマー、触媒、オリゴマー等の低分子量成分を除去する方法である。また、分取ＧＰＣは例えばリサイクル分取ＧＰＣＬＣ－９１００（日本分析工業社製）、ポリスチレンゲルカラムで、ポリマーを溶解した溶液をカラムに通すことにより分子量で分けることができ、所望の低分子量をカットすることができる方法である。リビング重合は、開始種の生成が経時で変化せず、また停止反応等の副反応が少なく、分子量の揃ったポリマーが得られる。分子量はモノマーの添加量により調整できるため、例えば分子量を２万のポリマーを合成すれば、低分子量体の生成を抑制することができる。生産適性から、再沈殿法、リビング重合が好ましい。
　本発明のバインダーの数平均分子量、分子量分布の測定は、一般的に知られているゲルパーミエーションクロマトグラフィー（ＧＰＣ）により行うことができる。使用する溶媒は、水溶性バインダーが溶解すれば特に制限はなく、ＴＨＦ、ＤＭＦ、ＣＨ２Ｃｌ２が好ましく、より好ましくはＴＨＦ、ＤＭＦであり、更に好ましくはＤＭＦである。また、測定温度も特に制限はないが４０℃が好ましい。
　本発明のポリマー（Ａ）の数平均分子量は３，０００～２，０００，０００の範囲が好ましく、より好ましくは４，０００～５００，０００、更に好ましくは５０００～１０００００の範囲内である。
　本発明のポリマー（Ａ）の分子量分布は１．０１～１．３０が好ましく、より好ましくは１．０１～１．２５である。分子量分布は（重量平均分子量／数平均分子量）の比で表す。
　分子量１０００以下の含有量はＧＰＣにより得られた分布において、分子量１０００以下の面積を積算し、分布全体の面積で割ることで割合を換算した。
　リビングラジカル重合溶剤は、反応条件化で不活性であり、モノマー、生成するポリマーを溶解できれば特に制限はないが、アルコール系溶媒と水の混合溶媒が好ましい。リビングラジカル重合温度は、使用する開始剤によって異なるが、一般に－１０～２５０℃、好ましくは０～２００℃、より好ましくは１０～１００℃で実施される。
　本発明において、透明導電層のナノインデンテーション弾性率を４ＧＰａ以上１０ＧＰａ以下とするには、透明導電層の導電性ポリマーとポリマー（Ａ）の比率を調節し、フレキシブル透明基板にこれらを含む塗布液を塗布した後、１００℃以上２００℃以下で乾燥処理、または加熱処理を行えばよい。
　特に、導電性ポリマーとポリマー（Ａ）の含有量の比率（導電性ポリマー／ポリマー（Ａ）（質量比））を、概ね１０／９０～７０／３０の比率とし上記温度で乾燥することで、上記弾性率を本発明の範囲にすることができる。
　さらに乾燥温度としては、上記比率で、１２０℃から１５０℃の範囲にすることで、容易に上記弾性率の範囲を本発明の範囲とすることができる。
　本発明では、導電性ポリマーに対するポリマー（Ａ）の比率が３０％以下にすると、透明導電層に占める導電性ポリマーの量が多くなり、ナノインデンテーション弾性率の値が４．０以下になるとともに透明性も損なわれる。　また、導電性ポリマーに対するポリマー（Ａ）の比率が９００％以上にすると、透明導電層に占めるポリマー（Ａ）の量が多くなり、ナノインデンテーション弾性率の値が１０．０以上になるとともに導電性が悪くなる。
［透明導電層］
　本発明において、透明導電層は、少なくとも導電性ポリマーとバインダーを有してなる混合液を透明基板または補助電極を持つ透明基板上に塗布、乾燥することで形成することができる。また、塗布液中の固形分の濃度は０．５質量％から３０質量％であることが好ましく、１から２０質量％であることが、液の停滞安定性、塗布膜の平滑性や、リーク防止効果の発現の視点で、より好ましい。
　塗布法としては、ロールコート法、バーコート法、ディップコーティング法、スピンコーティング法、キャスティング法、ダイコート法、ブレードコート法、グラビアコート法、カーテンコート法、スプレーコート法、ドクターコート法、凸版（活版）印刷法、孔版（スクリーン）印刷法、平版（オフセット）印刷法、凹版（グラビア）印刷法、スプレー印刷法、インクジェット印刷法等を用いることができる。
　導電性ポリマー含有層の乾燥膜厚は３０ｎｍから２０００ｎｍであることが好ましい。本発明の導電層は１００ｎｍを切る領域では導電性の低下が大きくなることから１００ｎｍ以上であることがより好ましく、リーク防止効果をより高める視点からは２００ｎｍ以上であることがさらに好ましい。また、高い透過率を維持する視点から１０００ｎｍ以下であることがより好ましい。
　特に、ポリ陰イオンがポリスルホン酸である場合、塗布乾燥後に、さらに、１００℃以上２００℃以下の温度で５分以上の追加の加熱処理を施すことが好ましい。これにより、透明導電層の洗浄耐性、溶媒耐性を著しく向上できる。また、この透明導電層を用いた有機電子デバイスの保存性を向上できる。１００℃以上であると上記効果を奏することができる観点から好ましく、２００℃以下であると別な反応も抑制されて、上記効果を奏することができる観点から好ましい。処理温度としては１１０℃以上１８０℃以下であることがより好ましく、処理時間としては１５分以上であることがより好ましい。処理時間の上限は特にないが、生産性を考えると１２０分以下であることが好ましい。
　また、濡れ性の観点から、透明導電層は表面処理を施してもよく、表面処理については従来公知の技術を使用できる。例えば、表面処理としては、コロナ放電処理、火炎処理、紫外線処理、高周波処理、グロー放電処理、活性プラズマ処理、レーザー処理等の表面活性化処理を挙げることができる。
［透明電極］
　本発明において、少なくとも導電性ポリマーとバインダーからなる透明導電層を有する透明電極とは、少なくとも電極が本発明の導電性ポリマーとバインダーを有してなる透明導電層単体で形成されている、あるいは、補助電極として、ＩＴＯ、ＺｎＯなど、公知の他の導電性電極層に本発明の透明導電層が積層されている、あるいは、後述のストライプ状、あるいはメッシュ状、あるいは、ランダムな網目状電極等に本発明の透明導電層が積層されている、あるいは、本発明の透明導電層にストライプ状、あるいはメッシュ状、あるいは、ランダムな網目状電極等が少なくとも一部が埋め込まれている形態などを挙げることができるが、透明電極が少なくとも導電性ポリマーとバインダーを有してなる透明導電層を含んでいれば、これらに限定はされない。
［補助電極］
　大面積化に対応するためには、本発明の透明導電層を有する電極が、さらに、光不透過の導電部と透光性窓部とからなる補助電極を有することが好ましい。
　補助電極の光不透過の導電部は導電性が良い点で金属であることが好ましく、金属材料としては、例えば、金、銀、銅、鉄、ニッケル、クロム等が挙げられる。また導電部の金属は合金でも良く、金属層は単層でも多層でも良い。
　補助電極の形状は特に制限はないが、例えば、導電部がストライプ状、あるいはメッシュ状、あるいは、ランダムな網目状である。導電部がストライプ状、あるいはメッシュ状の補助電極を形成する方法としては、特に、制限はなく、従来公知な方法が利用できる。例えば、基材全面に金属層を形成し、公知のフォトリソ法によって形成できる。具体的には、基材上に全面に、蒸着、スパッタ、めっき等の１或いは２以上の物理的或いは化学的形成手法を用いて導電体層を形成する、あるいは、金属箔を接着剤で基材に積層した後、公知のフォトリソ法を用いて、エッチングすることにより、所望のストライプ状、あるいはメッシュ状に加工できる。
　別な方法としては、金属微粒子を含有するインクをスクリーン印刷により所望の形状に印刷する方法や、メッキ可能な触媒インクをグラビア印刷、あるいは、インクジェット方式で所望の形状に塗布した後、メッキ処理する方法、さらに別な方法としては、銀塩写真技術を応用した方法も利用できる。銀塩写真技術を応用した方法については、例えば、特開２００９－１４０７５０号公報の段落番号（００７６）～（０１１２）、および実施例を参考にして実施できる。触媒インクをグラビア印刷してメッキ処理する方法については、例えば、特開２００７－２８１２９０号公報を参考にして実施できる。
（ランダムな網目構造）
　ランダムな網目構造としては、例えば、特表２００５－５３０００５号公報に記載のような、金属微粒子を含有する液を塗布乾燥することにより、自発的に導電性微粒子の無秩序な網目構造を形成する方法を利用できる。別な方法としては、例えば、特表２００９－５０５３５８号公報に記載のような、金属ナノワイヤを含有する塗布液を塗布乾燥することで、金属ナノワイヤのランダムな網目構造を形成させる方法を利用できる。
　金属ナノワイヤとは、金属元素を主要な構成要素とする繊維状構造体のことをいう。特に、本発明において金属ナノワイヤとは、原子スケールからｎｍサイズの短径を有する多数の繊維状構造体を意味する。
　金属ナノワイヤとしては、１つの金属ナノワイヤで長い導電パスを形成するために、平均長さが３μｍ以上であることが好ましく、さらには３～５００μｍが好ましく、特に３～３００μｍであることが好ましい。併せて、長さの相対標準偏差は４０％以下であることが好ましい。また、平均短径には特に制限はないが、透明性の観点からは小さいことが好ましく、一方で、導電性の観点からは大きい方が好ましい。金属ナノワイヤの平均短径として１０～３００ｎｍが好ましく、３０～２００ｎｍであることがより好ましい。併せて、短径の相対標準偏差は２０％以下であることが好ましい。金属ナノワイヤの目付け量は０．００５ｇ／ｍ２～０．５ｇ／ｍ２であるのが好ましく、０．０１ｇ／ｍ２～０．２ｇ／ｍ２であるのがより好ましい。
　金属ナノワイヤに用いられる金属としては銅、鉄、コバルト、金、銀等を用いることができるが、導電性の観点から銀が好ましい。また、金属は単一で用いてもよいが、導電性と安定性（金属ナノワイヤの硫化や酸化耐性、及びマイグレーション耐性）を両立するために、主成分となる金属と１種類以上の他の金属を任意の割合で含んでもよい。
　金属ナノワイヤの製造手段には特に制限はなく、例えば、液相法や気相法等の公知の手段を用いることができる。また、具体的な製造方法にも特に制限はなく、公知の製造方法を用いることができる。例えば、銀ナノワイヤの製造方法としては、Ａｄｖ．Ｍａｔｅｒ．，２００２，１４，８３３～８３７；Ｃｈｅｍ．Ｍａｔｅｒ．，２００２，１４，４７３６～４７４５、金ナノワイヤの製造方法としては特開２００６－２３３２５２号公報等、銅ナノワイヤの製造方法としては特開２００２－２６６００７号公報等、コバルトナノワイヤの製造方法としては特開２００４－１４９８７１号公報等を参考にすることができる。特に、上述した銀ナノワイヤの製造方法は、水溶液中で簡便に銀ナノワイヤを製造することができ、また銀の導電率は金属中で最大であることから、好ましく適用することができる。
［水洗処理］
　透明電極はその表面や内部に異物や不純物があると、有機電子デバイスの寿命などの性能に大きく低下する。本発明においては水洗処理をすることが好ましい。本発明における水洗処理は水系溶媒の洗浄液を使って透明導電層を洗浄することをいう。水系溶媒とは５０質量％以上が水である溶媒を表す。もちろん、他の溶媒を含有しない純水であっても良い。さらに、洗浄液中の異物の少なさから、超純水であることが望ましい。超純水とは、水温が２５℃のとき、比抵抗が１８ＭΩ・ｃｍ程度で、ＪＩＳＫ０５５１に準じた方法で測定された全有機炭素ＴＯＣが０．０５ｍｇ／Ｌ未満である水のことをいう。水系溶媒の水以外の成分は、水に相溶する溶剤であれば特に制限はないが、アルコール系の溶媒を好ましく用いることができ、中でも、沸点が比較的水に近いイソプロピルアルコールを用いることが好ましい。さらに透明導電層の濡れ性を改善するため、洗浄液は界面活性剤を含んでいてもよい。また、洗浄液はフィルター成分が溶出しない限り、各種フィルターを介したものであることが、洗浄液中の異物が少なくなることから、好ましい。
〔フレキシブル透明基板〕
　本発明の電極に用いられるフレキシブル透明基板としては、高い光透過性を有し、フレキシブル性に優れていれば特に制限はない。例えば、表面への導電層の形成のし易さ等の点で、樹脂基板、樹脂フィルムなどが好適に挙げられるが、生産性の観点や軽量性と柔軟性といった性能の観点から透明樹脂フィルムを用いることが好ましい。
　本発明でフレキシブル透明基板としては、フレキシブルであることから、透明樹脂フィルムとするのが好ましい。透明樹脂フィルムであれば、外力による変形や衝撃に強く、割れにくい。好ましく用いることができる透明樹脂フィルムには特に制限はなく、その材料、形状、構造、厚み等については公知のものの中から適宜選択することができる。例えば、ポリエチレンテレフタレート（ＰＥＴ）、ポリエチレンナフタレート、変性ポリエステル等のポリエステル系樹脂フィルム、ポリエチレン（ＰＥ）樹脂フィルム、ポリプロピレン（ＰＰ）樹脂フィルム、ポリスチレン樹脂フィルム、環状オレフィン系樹脂等のポリオレフィン類樹脂フィルム、ポリ塩化ビニル、ポリ塩化ビニリデン等のビニル系樹脂フィルム、ポリエーテルエーテルケトン（ＰＥＥＫ）樹脂フィルム、ポリサルホン（ＰＳＦ）樹脂フィルム、ポリエーテルサルホン（ＰＥＳ）樹脂フィルム、ポリカーボネート（ＰＣ）樹脂フィルム、ポリアミド樹脂フィルム、ポリイミド樹脂フィルム、アクリル樹脂フィルム、トリアセチルセルロース（ＴＡＣ）樹脂フィルム、等を挙げることができるが、可視域の波長（３８０～７８０ｎｍ）における透過率が８０％以上である樹脂フィルムであれば、本発明に係る透明樹脂フィルムに好ましく適用することができる。中でも透明性、耐熱性、取り扱いやすさ、強度及びコストの点から、二軸延伸ポリエチレンテレフタレートフィルム、二軸延伸ポリエチレンナフタレートフィルム、ポリエーテルサルホンフィルム、ポリカーボネートフィルムであることが好ましく、二軸延伸ポリエチレンテレフタレートフィルム、二軸延伸ポリエチレンナフタレートフィルムであることがより好ましい。
　本発明に用いられる透明基板には、塗布液の濡れ性や接着性を確保するために、表面処理を施すことや易接着層を設けることができる。表面処理や易接着層については従来公知の技術を使用できる。例えば、表面処理としては、コロナ放電処理、火炎処理、紫外線処理、高周波処理、グロー放電処理、活性プラズマ処理、レーザー処理等の表面活性化処理を挙げることができる。
　また、易接着層としては、ポリエステル、ポリアミド、ポリウレタン、ビニル系共重合体、ブタジエン系共重合体、アクリル系共重合体、ビニリデン系共重合体、エポキシ系共重合体等を挙げることができる。易接着層は単層でもよいが、接着性を向上させるためには２層以上の構成にしてもよい。
　また、透明基板の表面または裏面には、無機物、有機物の被膜またはその両者のハイブリッド被膜が形成されていてもよく、ＪＩＳ　Ｋ　７１２９－１９９２に準拠した方法で測定された水蒸気透過度（２５±０．５℃、相対湿度（９０±２）％ＲＨ）が、１×１０－３ｇ／（ｍ２・２４ｈ）以下のバリア性フィルムであることが好ましく、さらには、ＪＩＳ　Ｋ　７１２６－１９８７に準拠した方法で測定された酸素透過度が、１×１０－３ｍｌ／ｍ２・２４ｈ・ａｔｍ以下、水蒸気透過度（２５±０．５℃、相対湿度（９０±２）％ＲＨ）が、１×１０－３ｇ／（ｍ２・２４ｈ）以下の高バリア性フィルムであることが好ましい。
　高バリア性フィルムとするために透明基板の表面または裏面に形成されるバリア膜を形成する材料としては、水分や酸素等素子の劣化をもたらすものの浸入を抑制する機能を有する材料であればよく、例えば、酸化珪素、二酸化珪素、窒化珪素等を用いることができる。さらに該膜の脆弱性を改良するためにこれら無機層と有機材料からなる層の積層構造を持たせることがより好ましい。無機層と有機層の積層順については特に制限はないが、両者を交互に複数回積層させることが好ましい。
　［有機電子デバイス］
　本発明における有機電子デバイスは基板上に対向する第一電極と第二電極を有し、第一電極と第二電極との電極間に少なくとも１層の有機機能層を有する。本発明において第一電極と第二電極の少なくとも一方の電極が本発明の透明電極層を含む電極である。有機機能層としては、有機発光層、有機光電変換層、液晶ポリマー層などが挙げられるが、特に限定されない。本発明は、機能層が薄膜でかつ電流駆動系のデバイスである有機発光層、有機光電変換層である場合において、特に有効である。
　以下、実施例を挙げて本発明を詳細に説明するが、本発明はこれらに限定されない。尚、特に断りない限り、実施例中の「部」あるいは「％」の表示は、「質量部」あるいは「質量％」を表す。
　実施例１
［本発明のバインダー：ポリマー（Ａ）の合成］
＜ＡＴＲＰ（Ａｔｏｍ　Ｔｒａｎｓｆｅｒ　Ｒａｄｉｃａｌ　Ｐｏｌｙｍｅｒｉｚａｔｉｏｎ）法を用いたリビングラジカル重合による本発明のバインダー：ポリマー（Ａ）の合成＞
「開始剤１の合成」
　合成例１　（メトキシキャップされたオリゴエチレングリコール・２－ブロモイソブチリレート（開始剤１）の合成）
　５０ｍｌ三口フラスコに２－ブロモイソブチリルブロミド（７．３ｇ、３５ｍｍｏｌ）とトリエチルアミン（２．４８ｇ、３５ｍｍｏｌ）及びＴＨＦ（２０ｍｌ）を加え、アイスバスにより内温を０℃に保持した。この溶液内にオリゴエチレングリコール（１０ｇ、２３ｍｍｏｌ、エチレングリコールユニット７～８、Ｌａｐｏｒｔｅ　Ｓｐｅｃｉａｌｔｉｅｓ社製）の３３％ＴＨＦ溶液３０ｍｌを滴下した。３０分攪拌後、溶液を室温にし、更に４時間攪拌した。ＴＨＦをロータリーエバポレーターにより減圧除去後、残渣をジエチルエーテルに溶解し、分駅ロートに移した。水を加えエーテル層を３回洗浄後、エーテル層をＭｇＳＯ４により乾燥させた。エーテルをロータリーエバポレーターにより減圧留去し、開始剤１を８．２ｇ（収率７３％）得た。
　合成例２　（ポリ（２－ヒドロキシエチルアクリレート）の合成）
　開始剤１（５００ｍｇ、１．０２ｍｍｏｌ）、２－ヒドロキシエチルアクリレート（４．６４ｇ、４０ｍｍｏｌ、東京化成社製）、５０：５０　ｖ／ｖ％　メタノール／水混合溶媒５ｍｌをシュレンク管に投入し、減圧下液体窒素に１０分間シュレンク管を浸した。シュレンク管を液体窒素から出し、５分後に窒素置換を行った。この操作を３回行った後、窒素下で、ビピリジン（４００ｍｇ、２．５６ｍｍｏｌ）、ＣｕＢｒ（１４７ｍｇ、１．０２ｍｍｏｌ）を加え、２０℃で攪拌した。３０分後、ろ紙とシリカを敷いた４ｃｍ桐山ロート上に反応溶液を滴下し、減圧で反応溶液を回収した。ロータリーエバポレーターにより溶媒を減圧留去後、５０℃で３時間減圧乾燥した。その結果、数平均分子量１３１００、分子量分布１．１７、分子量＜１０００の含量０質量％、の水溶性バインダー１を２．６０ｇ（収率８４％）得た。
　構造、分子量は各々１Ｈ－ＮＭＲ（４００ＭＨｚ、日本電子社製）、ＧＰＣ（Ｗａｔｅｒｓ２６９５、Ｗａｔｅｒｓ社製）で測定した。
＜ＧＰＣ測定条件＞
装置：Ｗａｇｅｒｓ２６９５（Ｓｅｐａｒａｔｉｏｎｓ　Ｍｏｄｕｌｅ）
検出器：Ｗａｔｅｒｓ　２４１４　（Ｒｅｆｒａｃｔｉｖｅ　Ｉｎｄｅｘ　Ｄｅｔｅｃｔｏｒ）
カラム：Ｓｈｏｄｅｘ　Ａｓａｈｉｐａｋ　ＧＦ－７Ｍ　ＨＱ
溶離液：ジメチルホルムアミド（２０ｍＭ　ＬｉＢｒ）
流速：１．０ｍｌ／ｍｉｎ
温度：４０℃
　合成例３　（ポリ（２－ヒドロキシエチルビニルエーテル）、ポリ（２－ヒドロキシエチルアクリルアミド）、の合成）
　合成例２の（ポリ（２－ヒドロキシエチルアクリレート）の合成）において、２－ヒドロキシエチルアクリレートを、それぞれ、下記の作製しようとするポリマーに対応するモノマーに代えた他は同様にして、ポリ（２－ヒドロキシエチルビニルエーテル）、ポリ（２－ヒドロキシエチルアクリルアミド）、（数平均分子量約２万、分子量＜１０００の含量０質量％）をそれぞれ得た。
［基板Ａ（フレキシブル透明基板Ａ、およびガラス基板Ａ）の作製］
《基板Ａ（フレキシブル透明基板Ａ）の作製》
　二軸延伸ＰＥＮフィルムに、大気圧プラズマ放電処理法を用いて、低密度層、中密度層、高密度層、のユニットを３層積層した透明ガスバリア性を持つ基板Ａ（フレキシブル透明基板Ａ）を作製した。
　ＪＩＳ　Ｋ　７１２９－１９９２に準拠した方法により水蒸気透過度を測定した結果、１０－３ｇ／（ｍ２・２４ｈ）以下であった。ＪＩＳ　Ｋ　７１２６－１９８７に準拠した方法により酸素透過度を測定した結果、１０－３ｍｌ／（ｍ２・２４ｈｒ・ＭＰａ）以下であった。
《基板Ａ（ガラス基板Ａ）の作製》
　ガラス基板を、基板Ａ（ガラス基板Ａ）として用意した。
［ＩＴＯ基板Ａ（ＩＴＯフレキシブル透明基板Ａ、およびＩＴＯガラス基板Ａ）の作製］
　基板Ａ（フレキシブル透明基板Ａ）のバリア層のない面に、および、基板Ａ（ガラス基板Ａ）の表の面に、ＩＴＯ（インジウムチンオキシド）をスパッタ法により１５０ｎｍ成膜した基板にフォトリソ法によりパターニングを行った後、イソプロピルアルコールに基板を浸漬し、超音波洗浄器ブランソニック３５１０Ｊ－ＭＴ（日本エマソン社製）により１０分間の超音波洗浄処理を施し、ＩＴＯ基板Ａ（ＩＴＯフレキシブル透明基板Ａ、およびＩＴＯガラス基板Ａ））を作製した。
［銀ナノワイヤ基板Ａ（銀ナノワイヤフレキシブル透明基板Ａ、および銀ナノワイヤガラス基板Ａ）の作製］
　また、基板Ａ（フレキシブル透明基板Ａ）のバリア層のない面に、および、基板Ａ（ガラス基板Ａ）の表面に、下記の銀ナノワイヤ分散液を、銀ナノワイヤの目付け量が０．０６ｇ／ｍ２となるように、銀ナノワイヤ分散液をバーコート法を用いて塗布し１２０℃、２０分乾燥加熱後、下記の金属微粒子除去液をスクリーン印刷を用いて、パターン印刷し、超純水で洗浄することにより金属微粒子除去液を除去し、銀ナノワイヤ基板Ａ（銀ナノワイヤフレキシブル透明基板Ａ、および銀ナノワイヤガラス基板Ａ）を作製した。
（銀ナノワイヤ分散液）
　銀ナノワイヤ分散液は、Ａｄｖ．Ｍａｔｅｒ．，２００２，１４，８３３～８３７に記載の方法を参考に、ＰＶＰ　Ｋ３０（数平均分子量５万；ＩＳＰ社製）を利用して、平均短径７５ｎｍ、平均長さ３５μｍの銀ナノワイヤを作製し、限外濾過膜を用いて銀ナノワイヤを濾別、洗浄処理した後、ヒドロキシプロピルメチルセルロース６０ＳＨ－５０（信越化学工業社製）を銀に対し２５質量％加えた水溶液に再分散し、銀ナノワイヤ分散液を調製した。
（金属微粒子除去液）
　また、金属微粒子除去液は以下の組成のものを使用した。
　〈金属微粒子除去液の作製〉
　エチレンジアミン４酢酸第２鉄アンモニウム　　　　　　　　　６０ｇ
　エチレンジアミン４酢酸　　　　　　　　　　　　　　　　　２．０ｇ
　メタ重亜硫酸ナトリウム　　　　　　　　　　　　　　　　　　１５ｇ
　チオ硫酸アンモニウム　　　　　　　　　　　　　　　　　　　７０ｇ
　マレイン酸　　　　　　　　　　　　　　　　　　　　　　　５．０ｇ
　純水で１Ｌに仕上げ、硫酸またはアンモニア水でｐＨを５．５に調整し、金属微粒子除去液を作製した。また、金属微粒子除去液ＢＦの粘度をカルボキシメチルセルロースナトリウム（ＳＩＧＭＡ－ＡＬＤＲＩＣＨ社製；Ｃ５０１３、以下ＣＭＣと略記する）で１０Ｐａ・ｓ（１００００ｃＰ）に調整した。
［透明導電層塗布液Ａ～Ｏの調製］
　下記の導電性ポリマーとバインダーの混合液である透明導電層塗布液Ａ～Ｏを調製した。
　（透明導電層塗布液Ａの調製）
　導電性ポリマー／バインダー＝１００／０（質量比）の混合液
　ＰＥＤＯＴ－ＰＳＳ　ＣＬＥＶＩＯＳ　ＰＨ５１０（固形分１．８９％）
（Ｈ．Ｃ．Ｓｔａｒｃｋ社製）（単独にて使用）
　（透明導電層塗布液Ｂの調製）
　導電性ポリマー／バインダー＝５／９５（質量比）の混合液
　ＰＥＤＯＴ－ＰＳＳ　ＣＬＥＶＩＯＳ　ＰＨ５１０（固形分１．８９％）
　　（Ｈ．Ｃ．Ｓｔａｒｃｋ社製）　　　　　　　　　　　０．２６５ｇ
　ポリヒドロキシエチルアクリレート（合成例２、固形分２０％水溶液）
　　　　　　　　　　　　　　　　　　　　　　　　　　　０．４７５ｇ
　（透明導電層塗布液Ｃの調製）
　導電性ポリマー／バインダー＝５／９５（質量比）の混合液
　ＰＥＤＯＴ－ＰＳＳ　ＣＬＥＶＩＯＳ　ＰＨ５１０（固形分１．８９％）
　　（Ｈ．Ｃ．Ｓｔａｒｃｋ社製）　　　　　　　　　　　０．２６５ｇ
　ポリヒドロキシエチルアクリレート（合成例２、固形分２０％水溶液）
　　　　　　　　　　　　　　　　　　　　　　　　　　　０．４７５ｇ
　ジメチルスルホキシド　　　　　　　　　　　　　　　　　０．１０ｇ
　（透明導電層塗布液Ｄの調製）
　導電性ポリマー／バインダー＝１０／９０（質量比）の混合液
　ＰＥＤＯＴ－ＰＳＳ　ＣＬＥＶＩＯＳ　ＰＨ５１０（固形分１．８９％）
　　（Ｈ．Ｃ．Ｓｔａｒｃｋ社製）　　　　　　　　　　　０．５２９ｇ
　ポリヒドロキシエチルアクリレート（合成例２、固形分２０％水溶液）
　　　　　　　　　　　　　　　　　　　　　　　　　　　　０．４５ｇ
　（透明導電層塗布液Ｅの調製）
　導電性ポリマー／バインダー＝３０／７０（質量比）の混合液
　ＰＥＤＯＴ－ＰＳＳ　ＣＬＥＶＩＯＳ　ＰＨ５１０（固形分１．８９％）
　　（Ｈ．Ｃ．Ｓｔａｒｃｋ社製）　　　　　　　　　　　１．５８７ｇ
　ポリヒドロキシエチルアクリレート（合成例２、固形分２０％水溶液）
　　　　　　　　　　　　　　　　　　　　　　　　　　　０．３５０ｇ
　（透明導電層塗布液Ｆの調製）
　導電性ポリマー／バインダー＝５０／５０（質量比）の混合液
　ＰＥＤＯＴ－ＰＳＳ　ＣＬＥＶＩＯＳ　ＰＨ５１０（固形分１．８９％）
　　（Ｈ．Ｃ．Ｓｔａｒｃｋ社製）　　　　　　　　　　　２．６４５ｇ
　ポリヒドロキシエチルアクリレート（合成例２、固形分２０％水溶液）
　　　　　　　　　　　　　　　　　　　　　　　　　　　０．２５０ｇ
　（透明導電層塗布液Ｇの調製）
　導電性ポリマー／バインダー＝７０／３０（質量比）の混合液
　ＰＥＤＯＴ－ＰＳＳ　ＣＬＥＶＩＯＳ、ＰＨ５１０（固形分１．８９％）
　　（Ｈ．Ｃ．Ｓｔａｒｃｋ社製）　　　　　　　　　　　３．７０４ｇ
　ポリヒドロキシエチルアクリレート（合成例２、固形分２０％水溶液）
　　　　　　　　　　　　　　　　　　　　　　　　　　　０．１５０ｇ
　（透明導電層塗布液Ｈの調製）
　導電性ポリマー／バインダー＝８０／２０（質量比）の混合液
　ＰＥＤＯＴ－ＰＳＳ　ＣＬＥＶＩＯＳ　ＰＨ５１０（固形分１．８９％）
　　（Ｈ．Ｃ．Ｓｔａｒｃｋ社製）　　　　　　　　　　　４．２３３ｇ
　ポリヒドロキシエチルアクリレート（合成例２、固形分２０％水溶液）
　　　　　　　　　　　　　　　　　　　　　　　　　　　０．１００ｇ
　（透明導電層塗布液Ｉの調製）
　導電性ポリマー／バインダー＝３０／７０（質量比）の混合液
　ＰＥＤＯＴ－ＰＳＳ　ＣＬＥＶＩＯＳ　ＰＨ５１０（固形分１．８９％）
　　（Ｈ．Ｃ．Ｓｔａｒｃｋ社製）　　　　　　　　　　　１．５８７ｇ
　ポリヒドロキシエチルアクリレート（合成例２、固形分２０％水溶液）
　　　　　　　　　　　　　　　　　　　　　　　　　　　０．３５０ｇ
　ジメチルスルホキシド　　　　　　　　　　　　　　　　　０．１０ｇ
　（透明導電層塗布液Ｊの調製）
　導電性ポリマー／バインダー＝３０／７０（質量比）の混合液
　ＰＥＤＯＴ－ＰＳＳ　ＣＬＥＶＩＯＳ　Ｐ　ＡＩ　４０８３
　　（固形分１．５％）（Ｈ．Ｃ．Ｓｔａｒｃｋ社製）　　２．０００ｇ
　ポリヒドロキシエチルアクリレート（合成例２、固形分２０％水溶液）
　　　　　　　　　　　　　　　　　　　　　　　　　　　０．３５０ｇ
　（透明導電層塗布液Ｋの調製）
　導電性ポリマー／バインダー＝３０／７０（質量比）の混合液
　ＰＥＤＯＴ－ＰＳＳ　ＣＬＥＶＩＯＳ　ＰＨ５１０（固形分１．８９％）
　　（Ｈ．Ｃ．Ｓｔａｒｃｋ社製）　　　　　　　　　　　１．５８７ｇ
　ポリヒドロキシエチルビニルエーテル
　　（数平均分子量２万、固形分２０％水溶液）　　　　　０．３５０ｇ
　（透明導電層塗布液Ｌの調製）
　導電性ポリマー／バインダー＝３０／７０（質量比）の混合液
　ＰＥＤＯＴ－ＰＳＳ　ＣＬＥＶＩＯＳ　ＰＨ５１０（固形分１．８９％）
　　（Ｈ．Ｃ．Ｓｔａｒｃｋ社製）　　　　　　　　　　　１．５８７ｇ
　ポリヒドロキシエチルアクリルアミド
　　（数平均分子量２万、固形分２０％水溶液）　　　　　０．３５０ｇ
　（透明導電層塗布液Ｏの調製）
　導電性ポリマー／バインダー＝１０／９０（質量比）の混合液
　ＰＥＤＯＴ－ＰＳＳ　ＣＬＥＶＩＯＳ　ＰＨ５１０（固形分１．８９％）
　　（Ｈ．Ｃ．Ｓｔａｒｃｋ社製）　　　　　　　　　　　０．５２９ｇ
　ポリビニルアルコール　ＰＶＡ－２３５（クレハ製）固形分２％水溶液
　　　　　　　　　　　　　　　　　　　　　　　　　　　４．５００ｇ
　ジメチルスルホキシド　　　　　　　　　　　　　　　　０．１００ｇ
　エポキシ系架橋剤　デナコールＥＸ－３１３
　　（ナガセケムテックス（株））　　　　　　　　　　　０．５００ｇ
　［透明電極の作製］
　《ＩＴＯ電極１（ＩＴＯフレキシブル透明電極１およびＩＴＯガラス電極１）の作製》
　作製したＩＴＯ基板Ａ（ＩＴＯフレキシブル透明基板ＡおよびＩＴＯガラス基板Ａ）にスピンコーターを用いて、乾燥膜厚３００ｎｍになるように回転数を調整して透明導電層塗布液Ａを塗布し、ふき取りにより不要部分をふき取った後、１２０℃、２０分で加熱乾燥し、ＩＴＯ電極１（ＩＴＯフレキシブル透明電極１およびＩＴＯガラス電極１）とした。ＩＴＯガラス電極１について、以下の方法で、透過率、導電性、ナノインデンテーション弾性率、洗浄耐性を測定した。また、ＩＴＯフレキシブル透明電極１について、内側と外側に４５°折り曲げる操作を１００回行い、操作前後での、平滑性を測定した。
　《ＩＴＯ電極２（ＩＴＯフレキシブル透明電極２、ＩＴＯガラス電極２、）の作製》
　乾燥温度１２０℃を１５０℃に変えた以外は、ＩＴＯ電極１（ＩＴＯフレキシブル透明電極１およびＩＴＯガラス電極１）と同様の方法で、ＩＴＯ電極２（ＩＴＯフレキシブル透明電極２およびＩＴＯガラス電極２）を作製し、同様の測定を行った。
　（ＩＴＯ電極３，４（ＩＴＯフレキシブル透明電極３，４、およびＩＴＯガラス電極３，４）の作製）
　透明導電層塗布液Ａを透明導電層塗布液Ｂ、Ｃに変え、乾燥温度１２０℃を１８０℃に変えた以外は、ＩＴＯ電極１（ＩＴＯフレキシブル透明電極１およびＩＴＯガラス電極１）と同様の方法で、ＩＴＯ電極３，４（ＩＴＯフレキシブル透明電極３，４、およびＩＴＯガラス電極３，４）を作製し、同様の測定を行った。
　《ＩＴＯ電極５～９（ＩＴＯフレキシブル透明電極５～９、およびＩＴＯガラス電極５～９）の作製》
　透明導電層塗布液Ａを透明導電層塗布液Ｄ～Ｈに変え、乾燥温度１２０℃を１５０℃に変えた以外は、ＩＴＯ電極１（ＩＴＯフレキシブル透明電極１およびＩＴＯガラス電極１）と同様の方法で、ＩＴＯ電極５～９（ＩＴＯフレキシブル透明電極５～９、ＩＴＯガラス電極５～９）を作製し、同様の測定を行った。
《ＩＴＯ電極１０～１４（ＩＴＯフレキシブル透明電極１０～１４、およびＩＴＯガラス電極１０～１４）の作製》
　透明導電層塗布液Ａを透明導電層塗布液Ｄ～Ｈに変えた以外は、ＩＴＯ電極１（ＩＴＯフレキシブル透明電極１およびＩＴＯガラス電極１）と同様の方法で、ＩＴＯ電極１０～１４（ＩＴＯフレキシブル透明電極１０～１４、ＩＴＯガラス電極１０～１４）を作製し、同様の測定を行った。
《ＩＴＯ電極１５～１９（ＩＴＯフレキシブル透明電極１５～１９、およびＩＴＯガラス電極１５～１９）の作製》
　透明導電層塗布液Ａを透明導電層塗布液Ｉ～Ｌ、Ｏに変え、乾燥温度１２０℃を１５０℃に変えた以外は、ＩＴＯ電極１（ＩＴＯフレキシブル透明電極１およびＩＴＯガラス電極１）と同様の方法で、ＩＴＯ電極１５～１９（ＩＴＯフレキシブル透明電極１５～１９、およびＩＴＯガラス電極１５～１９）を作製し、同様の測定を行った。
　《銀ナノワイヤ電極２０～２７（銀ナノワイヤフレキシブル透明電極２０～２７、および銀ナノワイヤガラス電極２０～２７）の作製》
　ＩＴＯ基板Ａ（ＩＴＯフレキシブル透明基板Ａ、およびＩＴＯガラス基板Ａ）を銀ナノワイヤ基板Ａ（銀ナノワイヤフレキシブル透明基板Ａ、および銀ナノワイヤガラス基板Ａ）に変えた以外は、ＩＴＯ電極２～９（ＩＴＯフレキシブル透明電極２～９、およびＩＴＯガラス電極２～９）と同様の方法で、銀ナノワイヤ電極２０～２７（銀ナノワイヤフレキシブル透明電極２０～２７、および銀ナノワイヤガラス電極２０～２７）、を作製した。
　《評価》
　作製した透明電極について以下の評価を行った。
（導電性）
　導電性の評価として、抵抗率計（ロレスタＧＰ（ＭＣＰ－Ｔ６１０型）：（株）ダイヤインスツルメンツ社製）を用いて表面抵抗を測定した。レンジオーバーで測定不可の試料については、３ｃｍ×３ｃｍの試料を作製して、導電性ポリマー含有層上の対向する２辺に端から約２ｍｍの幅で銀ペーストを塗布し、ＫＥＩＴＨＬＥＹ製ソースメジャーユニット２４００型を用いて、１Ｖの直流電圧を印加し、その時の電流値から１ｖ／電流値を面抵抗値とした。補助電極の構成にもよるが、１×１０７Ω／□以下であることが好ましい。下記評価基準に則り導電性を表す指標として評価した。
◎：表面抵抗が、１×１０６Ω／□未満である
○：表面抵抗が、１×１０６Ω／□以上、１×１０７Ω／□未満である
△：表面抵抗が、１×１０７Ω／□以上、１×１０８Ω／□未満である
×：表面抵抗が、１×１０８Ω／□以上、１×１０９Ω／□未満である
××：表面抵抗が、１×１０９Ω／□以上である
（透過率）
　透過率の評価として、東京電色社製　ＨＡＺＥ　ＭＥＴＥＲ　ＮＤＨ５０００を用いて、全光線透過率を測定した。素子での光ロスから、８０％以上であることが好ましい。下記評価基準に則り透過率を表す指標として評価した。
◎：全光線透過率が、８５％以上である
○：全光線透過率が、８０％以上、８５％未満である
△：全光線透過率が、７５％以上、８０％未満である
×：全光線透過率が、７０％以上、７５％未満である
××：全光線透過率が、０％以上、７０％未満である
（洗浄耐性）
　ビーカーに洗浄溶媒として、水：イソプロピルアルコール＝８：２（質量比）を投入し、スターラーで撹拌した。そこに、ＩＴＯガラス電極、または、銀ナノワイヤガラス電極、の試料を３分間浸漬し、さらに超純水の流水で５分間の水洗処理を実施した。そして、透明導電層表面に膨潤や膜剥がれなどの乱れがないか目視にて観察し、下記評価基準に則り洗浄耐性を表す指標として評価した。
○：透明導電層表面に膨潤や膜剥がれなどの乱れがない
×：透明導電層表面に膨潤や膜剥がれなどの乱れがある
（ナノインデンテーション弾性率測定）
　Ｈｙｓｉｔｒｏｎ社製Ｔｒｉｂｏｓｃｏｐｅを用いて、エスアイアイナノテクノロジー社製ＳＰＩ３８００Ｎに装着し測定した。測定には、圧子としてベルコビッチ型圧子（先端稜角１４２．３°）と呼ばれる三角錘型ダイヤモンド製圧子で、先端曲率半径７５～１００ｎｍのものを用いた。表面に直角に当て、徐々に印加し、最大荷重到達後に荷重を０にまで徐々に戻す。この時の最大荷重Ｐを圧子接触部の投影面積Ａで除した値Ｐ／Ａを硬度として算出し、この値（硬度＝Ｐ／Ａ（ＧＰａ））を、ナノインデンテーション弾性率を表す指標として示す。
　尚、圧子接触部の投影面積Ａは、押し込み試験によって得られた深さ－荷重曲線のうち、除荷曲線の初期３０％を直線に近似して外挿、深さ軸と交差する点を圧子接触部の接触深さｈとし、圧子の形状よりｈの関数として求められる。なお、標準試料として、溶融石英を押し込んだ結果得られる硬さが９ＧＰａとなるよう、事前に装置を校正して測定した。
　原理の詳細は、Ｈａｎｄｂｏｏｋ　ｏｆ　Ｍｉｃｒｏ／Ｎａｎｏ　Ｔｒｉｂｏｌｏｇｙ（Ｂｈａｒａｔ　Ｂｈｕｓｈａｎ編　ＣＲＣ）に記載されている。測定は最大荷重が３０μＮとして行った。測定時の温度は２０℃であった。
（平滑性）
　折り曲げ後の平滑性の評価として、原子間力顕微鏡（Ａｔｏｍｉｃ　Ｆｏｒｃｅ　Ｍｉｃｒｏｓｃｏｐｙ：ＡＦＭ）ＳＰＩ３８００Ｎプローブステーション及びＳＰＡ４００多機能型ユニット（セイコーインスツルメンツ社製）を用い、表面粗さＲａを測定した。
　カンチレバーは、ＳＩ－ＤＦ２０（セイコーインスツルメンツ社製）を用い、共振周波数１２０～１５０ｋＨｚ、バネ定数１２～２０Ｎ／ｍ、ＤＦＭモード（Ｄｙｎａｍｉｃ　Ｆｏｒｃｅ　Ｍｏｄｅ）にて、測定領域１０μｍ角を、走査周波数１Ｈｚで測定した。ＪＩＳ　Ｂ６０１（１９９４）に準じて求めた算術平均粗さＲａ値について、下記評価基準に基づいて平滑性を評価した。透明電極としては、５０ｎｍ以下であることが好ましい。尚、測定の結果、作製したすべての電極は、折り曲げ操作を行う前、Ｒａが２０ｎｍ未満であった。
◎：折り曲げ後のＲａ値が、２０ｎｍ未満である
○：折り曲げ後のＲａ値が、２０ｎｍ以上、５０ｎｍ未満である
△：折り曲げ後のＲａ値が、５０ｎｍ以上、１００ｎｍ未満である
×：折り曲げ後のＲａ値が、１００ｎｍ以上、３００ｎｍ未満である
××：折り曲げ後のＲａ値が、３００ｎｍ以上である
　以上の結果を表２に示す。
　（架橋の確認）
　フーリエ変換赤外分光装置（島津製作所製ＦＴＩＲ－８３００）にて、各サンプルのＩＲスペクトルを測定した。
　塗布液Ａを塗布した透明電極以外のすべて透明電極において、バインダーの水酸基に由来する３４００ｃｍ－１付近のピークが減少し、バインダー同士、架橋剤とバインダー、またはバインダーと導電性ポリマーとが脱水縮合することにより生成するエーテル由来のピークが１１４０ｃｍ－１に出現した。一方、塗布液Ａを塗布した透明電極では架橋は検出されなかった。また、ナノインデンテーション弾性率の増加も塗布液Ａを塗布した透明電極と比較して、すべての透明電極で増加がみられ、ポリマーＡや架橋剤の添加により透明導電層が架橋していることがわかる。
　［有機ＥＬデバイスの作製］
　上記で作製したＩＴＯフレキシブル透明電極１～１９、銀ナノワイヤフレキシブル透明電極２０～２７を用いて、以下の手順で有機ＥＬデバイス１～２７を作製した。水洗耐性のある電極については水洗処理を行ってから用いた。
　作製した各透明電極について、ＰＥＤＯＴ／ＰＳＳ〔ｐｏｌｙ（３，４－ｅｔｈｙｌｅｎｅｄｉｏｘｙｔｈｉｏｐｈｅｎｅ）－ｐｏｌｙ（ｓｔｙｒｅｎｅｓｕｌｆｏｎａｔｅ）〕＝１：２．５の分散液であるＢａｙｔｒｏｎ　ＰＨ５１０（Ｈ．Ｃ．Ｓｔａｒｃｋ社製）をスピンコーターで１０００ｒｐｍ、３分間塗布し、厚さ３０ｎｍの導電層を形成することで透明電極を面電極化して、アノード電極を形成した。
　次いで、市販の真空蒸着装置内の蒸着用るつぼの各々に、各層の構成材料を各々の素子作製に最適の量を充填した。蒸着用るつぼはモリブデン製またはタングステン製の抵抗加熱用材料で作製されたものを用いた。
　はじめに、真空度１×１０－４Ｐａまで減圧した後、α－ＮＰＤの入った前記蒸着用るつぼに通電して加熱し、蒸着速度０．１ｎｍ／秒で、アノード電極上に蒸着し、３０ｎｍの正孔輸送層を設けた。
　次いで、以下の手順で各発光層を設けた。
　Ｉｒ－１が１３質量％、Ｉｒ－２が３．７質量％の濃度になるように、Ｉｒ－１、Ｉｒ－２及び化合物１－１を蒸着速度０．１ｎｍ／秒で共蒸着し、発光極大波長が６２２ｎｍ、厚さ１０ｎｍの緑赤色燐光発光層を形成した。
　次いで、Ｅ－１が１０質量％になるように、Ｅ－１及び化合物１－１を蒸着速度０．１ｎｍ／秒で共蒸着し、発光極大波長が４７１ｎｍ、厚さ１５ｎｍの青色燐光発光層を形成した。
　その後、Ｍ－１を膜厚５ｎｍに蒸着して正孔阻止層を形成し、更にＣｓＦを膜厚比で１０％になるようにＭ－１と共蒸着し、厚さ４５ｎｍの電子輸送層を形成した。
　更に、アルミニウム１１０ｎｍを蒸着して陰極を形成した。
　次いで、ポリエチレンテレフタレートを基材とし、Ａｌ２Ｏ３を厚さ３００ｎｍで蒸着した可撓性封止部材を使用し、アノード電極及びカソード電極の外部取り出し端子が形成出来る様に端部を除きカソード電極の周囲に接着剤を塗り、可撓性封止部材を貼合した後、熱処理で接着剤を硬化させて、有機ＥＬデバイス１～２７を作製した。
Figure JPOXMLDOC01-appb-C000004
［有機ＥＬデバイスの評価］
　有機ＥＬデバイス１～２７について以下の方法で寿命の評価を行った。
（寿命）
　同一作製手順にて作製した１０素子のうち５素子を、初期の輝度を５０００ｃｄ／ｍ２で連続発光させて、輝度が半減するまでの時間を求め、その平均値を寿命とした。また、残りの５素子を内側と外側に４５°折り曲げる操作を１００回行い、寿命を求めた。折り曲げ前後での寿命の比率を求め、以下の評価基準に則り折り曲げ後の有機ＥＬデバイスの寿命として評価した。７０％以上であることが好ましい。
◎：折り曲げ前後での寿命の比率が、８５％以上、１００％未満である
○：折り曲げ前後での寿命の比率が、７０％以上、８５％未満である
×：折り曲げ前後での寿命の比率が、３０％以上、５０％未満である
××：折り曲げ前後での寿命の比率が、０％以上、３０％未満である
　結果を表２に示す。
Figure JPOXMLDOC01-appb-T000006
　表１中、
　※１：導電性ポリマー／バインダーの質量比
　※２：ナノインデンテーション弾性率［ＧＰａ］
　ＰＨ５１０：ＰＥＤＯＴ－ＰＳＳ　ＣＬＥＶＩＯＳ　ＰＨ５１０（固形分１．８９％）（Ｈ．Ｃ．Ｓｔａｒｃｋ社製）
　４０８３：ＰＥＤＯＴ－ＰＳＳ　ＣＬＥＶＩＯＳ　Ｐ　ＡＩ　４０８３（固形分１．５％）（Ｈ．Ｃ．Ｓｔａｒｃｋ社製）
Figure JPOXMLDOC01-appb-T000007
　表１、表２から明らかなように、表１、表２の有機ＥＬデバイス３、４、１９、２１、２２から透明導電層のナノインデンテーション弾性率が１０Ｇｐａ以上になると透明導電層表面に微細なひびが入り、平滑性が損なわれることがわかる。また、有機ＥＬデバイス１、２、９、１４、２７から補助電極上に不純物などの突起が存在すると、導電性ポリマー層の弾性が低いため、電極を折り曲げると突起周辺部で透明導電層の変形がし、有機機能層にダメージを与え、有機電子デバイスの寿命が大幅に低下したことがわかる。
　以上から、ナノインデンテーション弾性率を４ＧＰａ以上１０ＧＰａ以下（本発明の構成）にすることで、透明導電層は適度な伸縮性をもつことができ、透明電極の折り曲げを繰り返しても、透明導電層表面にヒビが生じることがなく、電極の折り曲げにより、補助電極の突起部分とともに透明導電層が変形することがなく有機電子デバイスの機能の低下を抑制できることがわかる。

Claims (5)

  1. 　フレキシブル透明基板上に、導電性ポリマーとバインダーとを有してなる透明導電層を有する透明電極において、前記透明導電層の該バインダー同士が架橋構造を有するかまたは、該バインダーと該導電性ポリマーとが架橋構造を有しており、該バインダーが下記一般式（Ａ）で表されるポリマー（Ａ）であり、かつ前記透明導電層のナノインデンテーション弾性率が４ＧＰａ以上１０ＧＰａ以下であることを特徴とする透明電極。
    Figure JPOXMLDOC01-appb-C000001
    　（式中、Ｘ１～Ｘ３はそれぞれ独立に、水素原子またはメチル基を表し、Ｒ１～Ｒ３はそれぞれ独立に、炭素数５以下のアルキレン基を表す。ｌ、ｍ、ｎは構成率（ｍｏｌ％）を表し、５０≦ｌ＋ｍ＋ｎ≦１００である。）
  2. 　前記透明導電層のナノインデンテーション弾性率が５．５ＧＰａ以上７．０ＧＰａ以下であることを特徴とする請求項１に記載の透明電極。
  3. 　前記導電性ポリマーが、π共役系導電性高分子成分とポリ陰イオン成分とを有してなる導電性ポリマーであることを特徴とする請求項１または２に記載の透明電極。
  4. 　前記ポリ陰イオン成分がポリスルホン酸であることを特徴とする請求項３に記載の透明電極。
  5. 　請求項１から４のいずれか１項に記載の透明電極を用いたことを特徴とする有機電子デバイス。
PCT/JP2010/067218 2009-12-22 2010-10-01 透明電極および有機電子デバイス Ceased WO2011077804A1 (ja)