WO2009025312A1 - ポリエステル製造用重縮合触媒とその製造方法とポリエステルの製造方法 - Google Patents
ポリエステル製造用重縮合触媒とその製造方法とポリエステルの製造方法 Download PDFInfo
- Publication number
- WO2009025312A1 WO2009025312A1 PCT/JP2008/064860 JP2008064860W WO2009025312A1 WO 2009025312 A1 WO2009025312 A1 WO 2009025312A1 JP 2008064860 W JP2008064860 W JP 2008064860W WO 2009025312 A1 WO2009025312 A1 WO 2009025312A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- polyester
- coating layer
- solid base
- catalyst
- compound
- Prior art date
Abstract
Description
Claims