WO2008083908A1 - Matériaux stratiformes à fort pouvoir respirant et procédé pour les produire - Google Patents

Matériaux stratiformes à fort pouvoir respirant et procédé pour les produire Download PDF

Info

Publication number
WO2008083908A1
WO2008083908A1 PCT/EP2007/064282 EP2007064282W WO2008083908A1 WO 2008083908 A1 WO2008083908 A1 WO 2008083908A1 EP 2007064282 W EP2007064282 W EP 2007064282W WO 2008083908 A1 WO2008083908 A1 WO 2008083908A1
Authority
WO
WIPO (PCT)
Prior art keywords
protein
thermoplastic polyurethane
polyurethane film
coated
layered
Prior art date
Application number
PCT/EP2007/064282
Other languages
German (de)
English (en)
Inventor
Guido Vandermeulen
Burghard Liebmann
Michael Schmitt
Harald Keller
Daniel HÜMMERICH
Original Assignee
Basf Se
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Basf Se filed Critical Basf Se
Publication of WO2008083908A1 publication Critical patent/WO2008083908A1/fr

Abstract

L'invention concerne des matériaux stratiformes comprenant un film polyuréthane thermoplastique, recouvert d'au moins une protéine, et au moins un matériau textile.
PCT/EP2007/064282 2007-01-08 2007-12-20 Matériaux stratiformes à fort pouvoir respirant et procédé pour les produire WO2008083908A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
EP07100223 2007-01-08
EP07100223.2 2007-01-08

Publications (1)

Publication Number Publication Date
WO2008083908A1 true WO2008083908A1 (fr) 2008-07-17

Family

ID=39323059

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/EP2007/064282 WO2008083908A1 (fr) 2007-01-08 2007-12-20 Matériaux stratiformes à fort pouvoir respirant et procédé pour les produire

Country Status (1)

Country Link
WO (1) WO2008083908A1 (fr)

Cited By (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2011069643A3 (fr) * 2009-12-08 2011-08-11 Amsilk Gmbh Revêtements à base de protéine de soie
CN107405277A (zh) * 2014-12-02 2017-11-28 丝绸医疗公司 丝性能服装和产品及其制备方法
CN108135975A (zh) * 2015-07-14 2018-06-08 丝绸医疗公司 丝性能服装和产品及其制备方法
WO2020250904A1 (fr) 2019-06-11 2020-12-17 Ｓｐｉｂｅｒ株式会社 Agent conférant des propriétés d'absorption d'eau et de séchage rapide, et procédé pour conférer des propriétés d'absorption d'eau et de séchage rapide
US11390988B2 (en) 2017-09-27 2022-07-19 Evolved By Nature, Inc. Silk coated fabrics and products and methods of preparing the same

Citations (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20060200232A1 (en) * 2005-03-04 2006-09-07 Phaneuf Matthew D Nanofibrous materials as drug, protein, or genetic release vehicles

Patent Citations (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20060200232A1 (en) * 2005-03-04 2006-09-07 Phaneuf Matthew D Nanofibrous materials as drug, protein, or genetic release vehicles

Cited By (13)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US10253213B2 (en) 2009-12-08 2019-04-09 Amsilk Gmbh Silk protein coatings
US20120252294A1 (en) * 2009-12-08 2012-10-04 Amsilk Gmbh Silk protein coatings
US9217017B2 (en) 2009-12-08 2015-12-22 Amsilk Gmbh Silk protein coatings
WO2011069643A3 (fr) * 2009-12-08 2011-08-11 Amsilk Gmbh Revêtements à base de protéine de soie
US11453975B2 (en) 2014-12-02 2022-09-27 Evolved By Nature, Inc. Silk performance apparel and products and methods of preparing the same
CN107405277A (zh) * 2014-12-02 2017-11-28 丝绸医疗公司 丝性能服装和产品及其制备方法
US11649585B2 (en) 2014-12-02 2023-05-16 Evolved By Nature, Inc. Silk performance apparel and products and methods of preparing the same
CN108135975A (zh) * 2015-07-14 2018-06-08 丝绸医疗公司 丝性能服装和产品及其制备方法
US11512425B2 (en) 2015-07-14 2022-11-29 Evolved By Nature, Inc. Silk performance apparel and products and methods of preparing the same
US11390988B2 (en) 2017-09-27 2022-07-19 Evolved By Nature, Inc. Silk coated fabrics and products and methods of preparing the same
WO2020250904A1 (fr) 2019-06-11 2020-12-17 Ｓｐｉｂｅｒ株式会社 Agent conférant des propriétés d'absorption d'eau et de séchage rapide, et procédé pour conférer des propriétés d'absorption d'eau et de séchage rapide
CN113994034A (zh) * 2019-06-11 2022-01-28 丝芭博株式会社 吸水速干剂和赋予吸水速干性能的方法
EP3985149A4 (fr) * 2019-06-11 2023-07-12 Spiber Inc. Agent conférant des propriétés d'absorption d'eau et de séchage rapide, et procédé pour conférer des propriétés d'absorption d'eau et de séchage rapide

Similar Documents

Publication Publication Date Title
JP6291011B2 (ja) 水性ポリウレタン尿素組成物含有分散体およびフィルム
DE2931125C2 (de) Verfahren zur Herstellung eines mit Polyurethan imprägnierten faserigen porösen Bahnmaterials
WO2008055860A2 (fr) Fibres notamment non-tissé à base de polyuréthane thermoplastique
EP2288493B1 (fr) Matériaux composites multicouches comportant un film de matière plastique perméable à la vapeur d'eau, ainsi que leurs procédés de fabrication et d'utilisation
DE1110607B (de) Verfahren zur Herstellung mikroporoeser Folien bzw. UEberzuege, insbesondere von wasserdampfdurchlaessigem Kunstleder
EP2202352B1 (fr) Tissu hydrofugé avec un composant végétal
WO2008083908A1 (fr) Matériaux stratiformes à fort pouvoir respirant et procédé pour les produire
EP1994212A1 (fr) Materiau non tisse a base de polyurethanne thermoplastique
JP5570428B2 (ja) 可塑剤含有熱活性化フィルムの接着
JP2010534573A (ja) 熱で賦活されたポリウレタン尿素組成物を有する積層化された繊維布構造物
EP2121312A1 (fr) Stratifié contenant une feuille et un non-tissé à base de polyuréthane thermoplastique
DE2948892A1 (de) Feuchtigkeitsdurchlaessiges, wasserdichtes beschichtetes textiles flaechengebilde und verfahren zu seiner herstellung
EP2337818A2 (fr) Compositions aqueuses de polyuréthane-urée comprenant des dispersions et des films
WO2007104640A2 (fr) Élément composite à base de polyuréthanne et de polyoléfine
EP3291986B1 (fr) Procédé de production de matériaux composites
KR20170016850A (ko) 수성 폴리우레탄우레아 조성물 함유 분산물 및 필름
EP0147668A1 (fr) Masses de revêtement de polyuréthane réticulables, procédé de leur préparation et leur utilisation
CN105452559B (zh) 片状物及其制造方法
JP3968736B2 (ja) ポリウレタン糸およびその製法
EP0122554B1 (fr) Utilisation de compositions de polyréthanes contenant des combinaisons de réticulants comme couches adhèsives thermo-actives
EP4021621B1 (fr) Matière composite perméable à la vapeur d'eau
JPH0299671A (ja) コーティング布帛の製造方法
JP2002212834A (ja) ポリウレタン糸およびその製造方法
DE2343295A1 (de) Poroeser flaechiger werkstoff
JPS6354829B2 (fr)

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 07857903

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase