Classifications

• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
  • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
  • B01J20/00—Solid sorbent compositions or filter aid compositions; Sorbents for chromatography; Processes for preparing, regenerating or reactivating thereof
  • B01J20/02—Solid sorbent compositions or filter aid compositions; Sorbents for chromatography; Processes for preparing, regenerating or reactivating thereof comprising inorganic material
  • B01J20/10—Solid sorbent compositions or filter aid compositions; Sorbents for chromatography; Processes for preparing, regenerating or reactivating thereof comprising inorganic material comprising silica or silicate
  • B01J20/103—Solid sorbent compositions or filter aid compositions; Sorbents for chromatography; Processes for preparing, regenerating or reactivating thereof comprising inorganic material comprising silica or silicate comprising silica
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
  • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
  • B01J20/00—Solid sorbent compositions or filter aid compositions; Sorbents for chromatography; Processes for preparing, regenerating or reactivating thereof
  • B01J20/02—Solid sorbent compositions or filter aid compositions; Sorbents for chromatography; Processes for preparing, regenerating or reactivating thereof comprising inorganic material
  • B01J20/10—Solid sorbent compositions or filter aid compositions; Sorbents for chromatography; Processes for preparing, regenerating or reactivating thereof comprising inorganic material comprising silica or silicate
  • B01J20/16—Alumino-silicates
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
  • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
  • B01J20/00—Solid sorbent compositions or filter aid compositions; Sorbents for chromatography; Processes for preparing, regenerating or reactivating thereof
  • B01J20/30—Processes for preparing, regenerating, or reactivating
  • B01J20/32—Impregnating or coating ; Solid sorbent compositions obtained from processes involving impregnating or coating
  • B01J20/3231—Impregnating or coating ; Solid sorbent compositions obtained from processes involving impregnating or coating characterised by the coating or impregnating layer
  • B01J20/3234—Inorganic material layers
  • B01J20/3236—Inorganic material layers containing metal, other than zeolites, e.g. oxides, hydroxides, sulphides or salts
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
  • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
  • B01J23/00—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00
  • B01J23/38—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00 of noble metals
  • B01J23/40—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00 of noble metals of the platinum group metals
  • B01J23/44—Palladium
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
  • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
  • B01J23/00—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00
  • B01J23/38—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00 of noble metals
  • B01J23/54—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00 of noble metals combined with metals, oxides or hydroxides provided for in groups B01J23/02 - B01J23/36
  • B01J23/66—Silver or gold
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
  • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
  • B01J23/00—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00
  • B01J23/70—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00 of the iron group metals or copper
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
  • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
  • B01J27/00—Catalysts comprising the elements or compounds of halogens, sulfur, selenium, tellurium, phosphorus or nitrogen; Catalysts comprising carbon compounds
  • B01J27/06—Halogens; Compounds thereof
  • B01J27/128—Halogens; Compounds thereof with iron group metals or platinum group metals
  • B01J27/13—Platinum group metals
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
  • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
  • B01J29/00—Catalysts comprising molecular sieves
  • B01J29/04—Catalysts comprising molecular sieves having base-exchange properties, e.g. crystalline zeolites
  • B01J29/049—Pillared clays
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
  • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
  • B01J35/00—Catalysts, in general, characterised by their form or physical properties
  • B01J35/20—Catalysts, in general, characterised by their form or physical properties characterised by their non-solid state
  • B01J35/23—Catalysts, in general, characterised by their form or physical properties characterised by their non-solid state in a colloidal state
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
  • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
  • B01J35/00—Catalysts, in general, characterised by their form or physical properties
  • B01J35/40—Catalysts, in general, characterised by their form or physical properties characterised by dimensions, e.g. grain size
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
  • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
  • B01J35/00—Catalysts, in general, characterised by their form or physical properties
  • B01J35/40—Catalysts, in general, characterised by their form or physical properties characterised by dimensions, e.g. grain size
  • B01J35/45—Nanoparticles
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
  • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
  • B01J37/00—Processes, in general, for preparing catalysts; Processes, in general, for activation of catalysts
  • B01J37/02—Impregnation, coating or precipitation
  • B01J37/03—Precipitation; Co-precipitation
  • B01J37/031—Precipitation
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
  • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
  • B01J37/00—Processes, in general, for preparing catalysts; Processes, in general, for activation of catalysts
  • B01J37/04—Mixing
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B82—NANOTECHNOLOGY
  • B82Y—SPECIFIC USES OR APPLICATIONS OF NANOSTRUCTURES; MEASUREMENT OR ANALYSIS OF NANOSTRUCTURES; MANUFACTURE OR TREATMENT OF NANOSTRUCTURES
  • B82Y30/00—Nanotechnology for materials or surface science, e.g. nanocomposites
• • C—CHEMISTRY; METALLURGY
  • C01—INORGANIC CHEMISTRY
  • C01B—NON-METALLIC ELEMENTS; COMPOUNDS THEREOF; METALLOIDS OR COMPOUNDS THEREOF NOT COVERED BY SUBCLASS C01C
  • C01B33/00—Silicon; Compounds thereof
  • C01B33/113—Silicon oxides; Hydrates thereof
  • C01B33/12—Silica; Hydrates thereof, e.g. lepidoic silicic acid
  • C01B33/14—Colloidal silica, e.g. dispersions, gels, sols
  • C01B33/141—Preparation of hydrosols or aqueous dispersions
• • C—CHEMISTRY; METALLURGY
  • C01—INORGANIC CHEMISTRY
  • C01B—NON-METALLIC ELEMENTS; COMPOUNDS THEREOF; METALLOIDS OR COMPOUNDS THEREOF NOT COVERED BY SUBCLASS C01C
  • C01B33/00—Silicon; Compounds thereof
  • C01B33/113—Silicon oxides; Hydrates thereof
  • C01B33/12—Silica; Hydrates thereof, e.g. lepidoic silicic acid
  • C01B33/14—Colloidal silica, e.g. dispersions, gels, sols
  • C01B33/146—After-treatment of sols
  • C01B33/151—After-treatment of sols by progressively adding a sol to a different sol, i.e. "build-up" of particles using a "heel"
• • C—CHEMISTRY; METALLURGY
  • C01—INORGANIC CHEMISTRY
  • C01G—COMPOUNDS CONTAINING METALS NOT COVERED BY SUBCLASSES C01D OR C01F
  • C01G55/00—Compounds of ruthenium, rhodium, palladium, osmium, iridium, or platinum
• • C—CHEMISTRY; METALLURGY
  • C01—INORGANIC CHEMISTRY
  • C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
  • C01P2002/00—Crystal-structural characteristics
  • C01P2002/70—Crystal-structural characteristics defined by measured X-ray, neutron or electron diffraction data
  • C01P2002/72—Crystal-structural characteristics defined by measured X-ray, neutron or electron diffraction data by d-values or two theta-values, e.g. as X-ray diagram
• • C—CHEMISTRY; METALLURGY
  • C01—INORGANIC CHEMISTRY
  • C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
  • C01P2004/00—Particle morphology
  • C01P2004/60—Particles characterised by their size
  • C01P2004/64—Nanometer sized, i.e. from 1-100 nanometer
• • C—CHEMISTRY; METALLURGY
  • C01—INORGANIC CHEMISTRY
  • C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
  • C01P2006/00—Physical properties of inorganic compounds
  • C01P2006/12—Surface area
• • C—CHEMISTRY; METALLURGY
  • C01—INORGANIC CHEMISTRY
  • C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
  • C01P2006/00—Physical properties of inorganic compounds
  • C01P2006/14—Pore volume

Definitions

• This invention relates generally to siliceous materials having incorporated metal particles and processes to produce such materials. More specifically, the invention relates to a process of adding a metal salt to a silicic acid solution to create a metal-rich siliceous material. The invention has particular relevance to preparing colloidal silica having reduced incorporated metal particles.
• colloidal materials such as colloidal silica
• colloidal silica with a metal-coated surface is generally known and used.
• the silica colloid is first synthesized.
• the colloid is then coated with a metal oxide.
• This coating procedure produces both negatively and positively charged surfaces, depending upon the properties of the metallic starting material and the coating method used.
• Metal-containing silica colloids are useful in various areas, such as chemical mechanical polishing agents in the electronics industry, coating applications, and as support materials in catalytic processes. Despite this versatility, conventional-type silica colloids have several disadvantages.
• Liquid suspended metal nanoparticles have several drawbacks in catalysis including difficulties in recycling the nanoparticle catalyst. Immobilization of the catalyst on a solid support makes it possible to recycle the catalyst via simple filtration. Synthesis of the immobilized catalyst (which involves infusing the solid support with metal nanoparticles), however, can be highly time consuming.
• palladium-catalyzed reaction for carbon-carbon bond formation (Heck Reaction) is a versatile industrial synthesis tool. It includes impregnating a solid support, such as precipitated silica, with Palladium (II) acetate, drying, and reducing with hydrogen gas or other suitable reducing agent.
• Impregnation involves taking a solid porous support and adding metal salt solutions to the support.
• the metal salt solutions intercalate through the structure of the porous support and form surface deposits upon drying.
• the metal particles have a tendency to migrate over the surface of the porous support and must make their way through the porous structure to disperse.
• the sol-gel technique ⁇ See Lopez et al, Pt/SiO 2 Sol-Gel Catalysts: Effects of pH and Platinum Precursor, J. Phys. Chem., 1993, pp. 1671 to 1677) involves mixing metal salts with a silane precursor, such as tetraethyl orthos ⁇ icate ("TEOS"). Over time, the TEOS hydrolyzes and its SiOH groups interact with the metal salts. Once the SiOH groups begin to condense and form a precipitate, the metals are dispersed within the SiO 2 matrix via terminating SiO " or SiOH groups. The metal salts in the sol-gel technique tend to become occluded within the structure during synthesis.
• a silane precursor such as tetraethyl orthos ⁇ icate
• synthesis methods for creating silica-based colloids or particles having more homogenously dispersed metal loads and enhanced stability over a greater pH range and/or other suitable characteristics are desirable.
• this invention provides a method of preparing a metal- rich siliceous material.
• the method includes mixing one or more salts of one or more metals with a silicic acid solution to form a blend.
• the blend is added to a basic heel solution for form colloidal silica particles in a suspension.
• One or more of the colloidal silica particles includes incorporated metal particles.
• the method includes concentrating the suspension, reducing the incorporated metal particles with a reducing agent, and/or further processing steps.
• the invention also provides a metal-rich siliceous composition comprising a plurality of settled silica particles.
• the particles are produced from a mixture of a silicic acid solution and one or more salts of one or more metals. From about 10 weight percent to about 50 weight percent metal is associated with the colloidal silica particles, based on total solids.
• the invention includes a metal-rich siliceous composition
• a metal-rich siliceous composition comprising a plurality of colloidal silica particles having an average diameter from about 1 to about 250 nanometers.
• the particles are produced from a mixture of a silicic acid solution and one or more salts of one or more metals. Up to about 10 weight percent metal is associated with the colloidal silica particles, based on total solids.
• a further advantage of the invention is to provide a method of forming metal-rich colloidal silica particles having essentially homogenously distributed or dispersed metal particles and a narrow particle size distribution.
• It is another advantage of the invention is to provide a cost-effective and efficient method of formulating colloidal materials with metal constituents and reducing the associated metals in the liquid state with reducing agents, such as hydrazine, after the catalyst is generated.
• Figure 1 depicts the PXRD pattern of the 5.28 weight percent Pd(O) before reduction.
• Figure 2 illustrates the PXRD pattern of 5.28 weight percent Pd(O) after reduction.
• Figure 3 shows the PXRD pattern of the (111) peak for the 0.55 ( — ),
• a modified sol-gel method to create metal-rich siliceous material such as colloidal silica or aluminosilicate is disclosed.
• the metal salt of choice is added to a silicic acid solution or a silicic acid solution containing aluminum salt.
• the aluminum is added to vary the metal-support interaction as it forms Al-O-Si linkages within the silica matrix.
• the metal salt containing colloidal particle is left as is to maximize colloidal stability or is reduced with hydrazine to produce the zero valence metal- containing colloidal particle.
• Keeping a particle colloidal before use may be an effective method of forming a catalyst material as it can be easily spray-dried or mixed with other materials for extruded catalyst particles.
• the invention provides a process to incorporate metal particles into siliceous materials, such as colloidal silica or metallosilicates.
• the metal particles may include a variety of metals, such as alkaline metals, alkaline earth metals, first row transition metals, second row transition metals, lanthanides, the like, and combinations thereof.
• the metals include palladium, platinum, iron, gold, aluminum, copper, nickel, iron, titanium, and combinations thereof.
• the metals include palladium, gold, aluminum, and combinations thereof.
• the process involves adding a salt of a metal, such as palladium acetate, to silicic acid to produce a mixture. Introducing this mixture to a basic heel solution (described below) leads to formation of colloidal silica particles. The palladium-containing colloidal silica particles are then reduced, in an embodiment, with a reducing agent (e.g., hydrazine or hydrogen gas) to form palladium particles with a zero valence. It is contemplated that in addition, metal oxides (e.g., alumina, titania, and the like) may be added to the silicic acid to produce metallosilicates that offer different metal-support interactions with the reduced metal.
• a reducing agent e.g., hydrazine or hydrogen gas
• metal salts may be used in the process of the invention.
• mixed metals such as gold and palladium
• gold chloride and palladium acetate may be added to the silicic acid to form the metal-rich colloidal silica.
• Other representative metal salts that may used include, copper chloride, iron trinitrate, nickel nitrate, cobalt chloride, the like, and combinations thereof.
• the colloidal compositions of the invention are stable to gelling or precipitation and typically remain in the colloidal state with concentrations from about 0.1 weight percent to about 40 weight percent total solids.
• the material Upon reduction of the metal salts to metal, the material remains stable at low concentrations of metal added, for example, up to about 2 weight percent reduced metal, based on solids. In one embodiment, some settling occurs at concentrations more than about 2 weight percent reduced metal, based on solids. In another embodiment, minimal settling occurs at concentrations up to about 40 weight percent reduced metal, based on solids.
• the metal-rich siliceous particles upon forming the metal-rich siliceous particles, they are subjected to a reducing agent to reduce the associated metal particles from salt form to zero valence form.
• the reducing agent is typically hydrazine if the metal is reduced while the particles are in solution and hydrogen gas if the material is dried (e.g., flash drying, spray drying, and the like) prior to reducing.
• the method includes preparing a silicic acid solution. It is contemplated that the silicic acid may be prepared using any suitable method.
• a representative method includes deionizing a sodium silicate, such as sodium orthosilicate (Na 4 SiO 4 ), sodium metasilicate (Na 2 SiOs), sodium polysilicate (Na 2 SiOa) n , sodium pyrosilicate Na 6 Si 2 O 7 , the like, and/or any combination thereof with an ion exchange resin.
• the sodium silicate is deionized with a strong acid ion exchange resin to produce the silicic acid or acid sol.
• An alternative method includes using the well-known St ⁇ ber process to produce the silicic acid.
• the basic heel solution used to synthesize the metal-rich siliceous material of the method acts as a catalyst for forming the material.
• the heel solution may be heated from about 6O 0 C to about 9O 0 C prior to adding the silicic acid/metal salts blend.
• the basic heel solution typically is in the range from about 10 milliequivalents ("meq") to about 200 meq and may alternatively include various types of bases.
• Representative bases include sodium hydroxide, lithium hydroxide, potassium hydroxide, ammonium hydroxide, primary amines, secondary amines, tertiary amines, quaternary amines, quaternary compounds, the like, and combinations thereof.
• Representative quaternary compounds include tetraethyl ammonium hydroxide, tetra-n-butyl ammonium hydroxide, tetra-n-propyl ammonium hydroxide, tetramethyl ammonium hydroxide, NNN-trimethyl-2-butyl ammonium hydroxide, NNN-trimethyl-propyl ammonium hydroxide, the like, and combinations thereof.
• the colloidal particles have an average diameter from about 1 nanometer to about 250 nanometers. In a more preferred embodiment, the particles have an average diameter from about 4 nanometers to about to about 150 nanometers.
• the metai-rich siliceous material of the invention may be used in a variety of industrial applications.
• Representative applications include dental applications, protein separation; molecular sieves, nanoporous membranes, wave guides, photonic crystals, refractory applications, clarification of wine and juice, chemical mechanical planarization of semiconductor and disk drive components, catalysts, catalyst supports, retention and drainage aids in papermaking, fillers, surface coatings, ceramic materials, investment casting binders, flattening agents, proppants, cosmetic formulations, and polishing abrasives. Certain of these industrial applications may require that the material of the invention be further processed prior to using it in the application. Possible processing steps include ultra-filtration, deionization, heating, drying, concentrating, surface functionalization, the like, and combinations thereof.
• the silica source for the below examples was silicic acid (or acid sol).
• the silicic acid was produced by passing a solution containing 25 grams of sodium silicate (R-570) in 57.37 grams deionized water through a cationic exchange resin.
• R-570 sodium silicate
• a cationic exchange resin any suitable column or resin may be used, in these examples, a column containing about 40 ml DowexTM 650C strong cationic exchange resin (available from Dow Chemical Company in Midland, MI) per 100 grams of diluted sodium silicate solution was used.
• the silicic acid/aluminum chlorohydrate/palladium acetate/HCl solution was dripped into the flask under stirring at a rate of about 10 ml/min for each reaction in Table I.
• the only preparation difference was the lack of aluminum chlorohydrate.
• a mixed metal silica colloid catalyst was also generated at a 1.07 weight percent total metal content with a palladium to gold molar ratio of 4. This mixed metal catalyst was then concentrated by ultrafiltration to 16.3% total solids.
• the color after addition to the silicic acid or silicic acid/aluminum chlorohydrate solution was light yellowish brown for the 0.55 wt% Pd(O) sample to dark brown for the 5.28 wt% Pd(O) sample.
• the solutions were very stable to gelling or precipitation and could be stored for hours before use to make the colloidal particles.
• the caustic heel was heated to 80 0 C and the silicic acid/palladium acetate or silicic acid/aluminum chlorohydrate/palladium acetate solution was dripped in at 10 ml/min to create for an intended silica colloid particle size of about 10 nanometers.
• Example I The samples from Example I were subsequently characterized as is or upon reduction with 1 ml of 10 wt% hydrazine solution in deionized water. Characterization of the metal-rich silica colloids included transmission electron microscopy ("TEM"), powder X-ray diffraction ("PXRD”), and nitrogen sorption. A Philips (FEI) EM208S TEM (100 kV) equipped with a thermionic tungsten filament or a JEOL 3010 TEM (300 kV) equipped with a LaB 6 filament were used. PXRD on the calcined samples was performed with a Philips PANalytical® X'Pert Pro 3040 using Co Ka radiation with a wavelength of 1.78897 A. Samples were washed with adequate amounts of deionized water to remove any NaCl that was present. Nitrogen sorption measurements were performed with an Autosorb-lC from Quantachrome®. Each sample was degassed for 3 hours at 300 0 C.
• TEM transmission electron micro
• FIG 2 depicts the PXRD pattern of the 5.28 wt% Pd(O) sample after reduction with hydrazine.
• the broad Pd(O) (111) peak at 2 ⁇ 46.71 can be seen.
• the PXRD patterns show the (111) peak associated with Pd(O). As with the 5.28 wt% Pd(O) sample, the peak is extremely broad for all three samples, with the average particle size as determined by the Scherer equation as shown in Table II.
• the lower 0.55 and 1.10 wt% Pd(O) samples have a larger average particle size of Pd(O), 4.24 and 4.60 nm, respectively, than the higher 1.82 wt% Pd(O) sample, which has an average particle size for Pd(O) of 2.87 nm.
• the 5.28 wt% Pd(O) sample has an even smaller particle size than the lower Pd(O) wt% samples, which is not typically observed by PXRD in the doping of metal particulates via previously known sol-gel synthesis techniques.
• the PXRD of the 1.10 wt% Pd(O) shown in FIG 3 gives a very distinct peak for the Pd(O) (111), whereas the 1.07 wt% (111) peak for both Au(O) and Pd(O) in FIG 4 are not seen.
• the extremely broad PXRD peak is an indication of the good dispersion of the Au(O) and Pd(O) particles through the aluminosilicate matrix and their extremely small particle size.
• the colloidal particle sizes associated with the surface areas are 12.3 nm for the 0.55 wt% Pd(O) sample, 10.5 nm for 1.10 wt% Pd(O) sample, and 10.8 nm for the 1.82 wt% Pd(O) sample.
• the particle size values for all three samples correlate well with the intended particle size of about 10 nm. All three samples exhibit Type IV isotherms with considerable hysteresis, while the adsorption portion of the isotherms gave pore size distributions from about 2 to about 30 nm.

Landscapes

• Chemical & Material Sciences (AREA)
• Organic Chemistry (AREA)
• Engineering & Computer Science (AREA)
• Chemical Kinetics & Catalysis (AREA)
• Materials Engineering (AREA)
• Inorganic Chemistry (AREA)
• Analytical Chemistry (AREA)
• Dispersion Chemistry (AREA)
• Nanotechnology (AREA)
• Crystallography & Structural Chemistry (AREA)
• Composite Materials (AREA)
• Condensed Matter Physics & Semiconductors (AREA)
• General Physics & Mathematics (AREA)
• Physics & Mathematics (AREA)
• Catalysts (AREA)
• Powder Metallurgy (AREA)
• Silicon Compounds (AREA)
• Manufacture Of Metal Powder And Suspensions Thereof (AREA)

Priority Applications (4)

Applications Claiming Priority (2)

Publications (2)

Family

ID=39360386

Family Applications (1)

Country Status (6)

Cited By (2)

Families Citing this family (23)

Family Cites Families (21)

• 2006
  • 2006-11-08 US US11/557,548 patent/US20080108497A1/en not_active Abandoned
• 2007
  • 2007-11-08 CN CN2007800411100A patent/CN101534944B/zh active Active
  • 2007-11-08 EP EP07864119.8A patent/EP2079546B1/en active Active
  • 2007-11-08 WO PCT/US2007/084095 patent/WO2008058240A2/en not_active Ceased
  • 2007-11-08 CA CA2669471A patent/CA2669471C/en active Active
  • 2007-11-08 JP JP2009535512A patent/JP5389660B2/ja active Active
• 2009
  • 2009-12-01 US US12/628,472 patent/US8003707B2/en active Active