WO2007030516A1 - Method of controlling solder deposition on heat spreader used for semiconductor package - Google Patents

Method of controlling solder deposition on heat spreader used for semiconductor package Download PDF

Info

Publication number
WO2007030516A1
WO2007030516A1 PCT/US2006/034678 US2006034678W WO2007030516A1 WO 2007030516 A1 WO2007030516 A1 WO 2007030516A1 US 2006034678 W US2006034678 W US 2006034678W WO 2007030516 A1 WO2007030516 A1 WO 2007030516A1
Authority
WO
WIPO (PCT)
Prior art keywords
heat spreader
flux
solder
preform
attaching
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/US2006/034678
Other languages
English (en)
French (fr)
Inventor
John N. Stipp
Brian T. Deram
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Kester LLC
Original Assignee
Kester LLC
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Kester LLC filed Critical Kester LLC
Priority to JP2008530160A priority Critical patent/JP5345848B2/ja
Publication of WO2007030516A1 publication Critical patent/WO2007030516A1/en
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Links

Classifications

    • BPERFORMING OPERATIONS; TRANSPORTING
    • B23MACHINE TOOLS; METAL-WORKING NOT OTHERWISE PROVIDED FOR
    • B23KSOLDERING OR UNSOLDERING; WELDING; CLADDING OR PLATING BY SOLDERING OR WELDING; CUTTING BY APPLYING HEAT LOCALLY, e.g. FLAME CUTTING; WORKING BY LASER BEAM
    • B23K1/00Soldering, e.g. brazing, or unsoldering
    • B23K1/20Preliminary treatment of work or areas to be soldered, e.g. in respect of a galvanic coating
    • B23K1/203Fluxing, i.e. applying flux onto surfaces
    • BPERFORMING OPERATIONS; TRANSPORTING
    • B23MACHINE TOOLS; METAL-WORKING NOT OTHERWISE PROVIDED FOR
    • B23KSOLDERING OR UNSOLDERING; WELDING; CLADDING OR PLATING BY SOLDERING OR WELDING; CUTTING BY APPLYING HEAT LOCALLY, e.g. FLAME CUTTING; WORKING BY LASER BEAM
    • B23K1/00Soldering, e.g. brazing, or unsoldering
    • B23K1/0008Soldering, e.g. brazing, or unsoldering specially adapted for particular articles or work
    • B23K1/0016Soldering of electronic components
    • BPERFORMING OPERATIONS; TRANSPORTING
    • B23MACHINE TOOLS; METAL-WORKING NOT OTHERWISE PROVIDED FOR
    • B23KSOLDERING OR UNSOLDERING; WELDING; CLADDING OR PLATING BY SOLDERING OR WELDING; CUTTING BY APPLYING HEAT LOCALLY, e.g. FLAME CUTTING; WORKING BY LASER BEAM
    • B23K1/00Soldering, e.g. brazing, or unsoldering
    • B23K1/20Preliminary treatment of work or areas to be soldered, e.g. in respect of a galvanic coating
    • B23K1/206Cleaning
    • HELECTRICITY
    • H05ELECTRIC TECHNIQUES NOT OTHERWISE PROVIDED FOR
    • H05KPRINTED CIRCUITS; CASINGS OR CONSTRUCTIONAL DETAILS OF ELECTRIC APPARATUS; MANUFACTURE OF ASSEMBLAGES OF ELECTRICAL COMPONENTS
    • H05K3/00Apparatus or processes for manufacturing printed circuits
    • H05K3/30Assembling printed circuits with electric components, e.g. with resistors
    • H05K3/32Assembling printed circuits with electric components, e.g. with resistors electrically connecting electric components or wires to printed circuits
    • H05K3/34Assembling printed circuits with electric components, e.g. with resistors electrically connecting electric components or wires to printed circuits by soldering
    • H05K3/3465Application of solder
    • HELECTRICITY
    • H10SEMICONDUCTOR DEVICES; ELECTRIC SOLID-STATE DEVICES NOT OTHERWISE PROVIDED FOR
    • H10WGENERIC PACKAGES, INTERCONNECTIONS, CONNECTORS OR OTHER CONSTRUCTIONAL DETAILS OF DEVICES COVERED BY CLASS H10
    • H10W40/00Arrangements for thermal protection or thermal control
    • H10W40/01Manufacture or treatment
    • H10W40/03Manufacture or treatment of arrangements for cooling
    • H10W40/037Assembling together parts thereof
    • HELECTRICITY
    • H05ELECTRIC TECHNIQUES NOT OTHERWISE PROVIDED FOR
    • H05KPRINTED CIRCUITS; CASINGS OR CONSTRUCTIONAL DETAILS OF ELECTRIC APPARATUS; MANUFACTURE OF ASSEMBLAGES OF ELECTRICAL COMPONENTS
    • H05K2203/00Indexing scheme relating to apparatus or processes for manufacturing printed circuits covered by H05K3/00
    • H05K2203/02Details related to mechanical or acoustic processing, e.g. drilling, punching, cutting, using ultrasound
    • H05K2203/0278Flat pressure, e.g. for connecting terminals with anisotropic conductive adhesive
    • HELECTRICITY
    • H05ELECTRIC TECHNIQUES NOT OTHERWISE PROVIDED FOR
    • H05KPRINTED CIRCUITS; CASINGS OR CONSTRUCTIONAL DETAILS OF ELECTRIC APPARATUS; MANUFACTURE OF ASSEMBLAGES OF ELECTRICAL COMPONENTS
    • H05K2203/00Indexing scheme relating to apparatus or processes for manufacturing printed circuits covered by H05K3/00
    • H05K2203/04Soldering or other types of metallurgic bonding
    • H05K2203/0415Small preforms other than balls, e.g. discs, cylinders or pillars
    • HELECTRICITY
    • H05ELECTRIC TECHNIQUES NOT OTHERWISE PROVIDED FOR
    • H05KPRINTED CIRCUITS; CASINGS OR CONSTRUCTIONAL DETAILS OF ELECTRIC APPARATUS; MANUFACTURE OF ASSEMBLAGES OF ELECTRICAL COMPONENTS
    • H05K2203/00Indexing scheme relating to apparatus or processes for manufacturing printed circuits covered by H05K3/00
    • H05K2203/04Soldering or other types of metallurgic bonding
    • H05K2203/0485Tacky flux, e.g. for adhering components during mounting
    • HELECTRICITY
    • H05ELECTRIC TECHNIQUES NOT OTHERWISE PROVIDED FOR
    • H05KPRINTED CIRCUITS; CASINGS OR CONSTRUCTIONAL DETAILS OF ELECTRIC APPARATUS; MANUFACTURE OF ASSEMBLAGES OF ELECTRICAL COMPONENTS
    • H05K3/00Apparatus or processes for manufacturing printed circuits
    • H05K3/0058Laminating printed circuit boards onto other substrates, e.g. metallic substrates
    • H05K3/0061Laminating printed circuit boards onto other substrates, e.g. metallic substrates onto a metallic substrate, e.g. a heat sink
    • HELECTRICITY
    • H05ELECTRIC TECHNIQUES NOT OTHERWISE PROVIDED FOR
    • H05KPRINTED CIRCUITS; CASINGS OR CONSTRUCTIONAL DETAILS OF ELECTRIC APPARATUS; MANUFACTURE OF ASSEMBLAGES OF ELECTRICAL COMPONENTS
    • H05K3/00Apparatus or processes for manufacturing printed circuits
    • H05K3/22Secondary treatment of printed circuits
    • H05K3/26Cleaning or polishing of the conductive pattern
    • HELECTRICITY
    • H05ELECTRIC TECHNIQUES NOT OTHERWISE PROVIDED FOR
    • H05KPRINTED CIRCUITS; CASINGS OR CONSTRUCTIONAL DETAILS OF ELECTRIC APPARATUS; MANUFACTURE OF ASSEMBLAGES OF ELECTRICAL COMPONENTS
    • H05K3/00Apparatus or processes for manufacturing printed circuits
    • H05K3/30Assembling printed circuits with electric components, e.g. with resistors
    • H05K3/32Assembling printed circuits with electric components, e.g. with resistors electrically connecting electric components or wires to printed circuits
    • H05K3/34Assembling printed circuits with electric components, e.g. with resistors electrically connecting electric components or wires to printed circuits by soldering
    • H05K3/3489Composition of fluxes; Application thereof; Other processes of activating the contact surfaces
    • HELECTRICITY
    • H10SEMICONDUCTOR DEVICES; ELECTRIC SOLID-STATE DEVICES NOT OTHERWISE PROVIDED FOR
    • H10WGENERIC PACKAGES, INTERCONNECTIONS, CONNECTORS OR OTHER CONSTRUCTIONAL DETAILS OF DEVICES COVERED BY CLASS H10
    • H10W72/00Interconnections or connectors in packages
    • H10W72/851Dispositions of multiple connectors or interconnections
    • H10W72/874On different surfaces
    • H10W72/877Bump connectors and die-attach connectors

Definitions

  • the present invention relates to a method of predepositing a specific amount of solder metal to a perform and heat spreader or heat sink thereby facilitating the removal of heat from the semiconductor or other element the heat spreader is attached to. More particularly, the present invention relates to a method of forming a solder deposit having desired dimensions of the final deposit directly on the heat spreader by reflowing the perform by use of an aggressive flux and preferably an application of a finishing flux. The deposit is preferably flattened or coined for an improved attachment to the semiconductor and coated with an additional attach flux.
  • soldering to a metal surface whether the purpose for soldering is to create electrical connections or non-electrical, mechanical connections, the solder must metalize, or bond to, the metal surface. Good electrical or thermal conduction by the solder is dependent on void-free solder bonding to the metal surface.
  • An example in the electronics assembly industry is to solder a metallic lid or cover onto an electronic device that must be cooled. The heat conducting lid can then radiate heat or transfer it to a thermal pipe for removing the heat, thereby cooling the device.
  • the soldering flux must be selected for its ability to remove contamination, mostly oxides, from the metal surface so the melted solder can properly bond to the metal.
  • soldering fluxes can be placed into groupings or categories by the corrosive nature of their residues as is done in IPC/EIA Standard J-STD-004 "Requirements for Soldering Fluxes".
  • This industry document classifies fluxes according to their basic composition and percent halides included in the composition.
  • ASTM B 32 Standard Specification for Solder Metals
  • ISO 9454 Soft Soldering Fluxes - Classification and Requirements
  • Inorganic Flux - A solution of inorganic acids and/or salts, including, but not limited to, halide salts of metals, such as zinc chloride, zinc bromide, stannous chloride, stannous bromide, stannous fluoride, sodium chloride, in water and optionally containing ammonium chloride, mineral acids, such as hydrochloric acid, hydrobromic acid, phosphoric acid.
  • halide salts of metals such as zinc chloride, zinc bromide, stannous chloride, stannous bromide, stannous fluoride, sodium chloride, in water and optionally containing ammonium chloride, mineral acids, such as hydrochloric acid, hydrobromic acid, phosphoric acid.
  • Organic Flux Primarily composed of organic materials other than rosin or resin, including, but not limited to, water soluble carboxylic acids, such as formic acid, acetic acid, propionic acid, malonic acid, glycolic acid, lactic acid, glyceric acid, malic acid, tartaric acid, and citric acid; water insoluble carboxylic acids, such as stearic acid, oleic acid, benzoic acid, salicylic acid, succinic acid, adipic acid, azelaic acid; optionally containing in admixture amines, amides, and hydrohalide derivatives of the amines and acids.
  • water soluble carboxylic acids such as formic acid, acetic acid, propionic acid, malonic acid, glycolic acid, lactic acid, glyceric acid, malic acid, tartaric acid, and citric acid
  • water insoluble carboxylic acids such as stearic acid, oleic acid, benzoic acid, salicylic acid, succ
  • the composition may also contain additives to increase activity, such as other organic acids and amine hydrohalides. Rosin fluxes are generally not water soluble. Additionally, the flux compositions may vary in activity as indicated by the level of halides included in the flux and by corrosion testing. Inorganic and Organic fluxes are generally water-soluble, while rosin fluxes are solvent-soluble. It is not the intention of the present invention to specify a flux type or composition, but rather to demonstrate the potential use of the variety of available fluxes.
  • High activity fluxes in particular the Inorganic and Organic water-soluble types, are very effective for soldering even the most difficult metals, but may cause the formation of harmful, insoluble, corrosive residues on the soldered assembly. If allowed to remain on the substrate, the residues can result in electrical or mechanical failure of the product.
  • the present invention utilizes a second flux to render the residues from the high activity flux soluble in water, or other suitable solvent, so they can be removed from the product by washing.
  • the second flux is a finishing flux that may or may not contain halides or other corrosive materials. If the finishing flux contains corrosives and/or halides, they must be cleanabJe after the reflow process.
  • Prior art processes to reduce the amount of residue formed on the metal after applying a deposition of solder on a base metal include using a less-active flux, which can result in poor solder joints, dewetting or incomplete soldering.
  • Another method utilizes a resist material to define the area of deposit on the metal substrate. The flux is applied and placed in the area bounded by the resist and, and then the metal substrate is dipped in molten solder or passed across a wave of solder. This method is undesirable because of the potential heat damage on the substrate and irregular solder deposit.
  • another prior art method utilizes a soldermask in an attempt to limit the spread of the solder deposit when solder paste is applied in the area defined by the soldermask. Though the solder deposit can be more uniform. The use of a soldermask would generally be expensive, time-consuming and inefficient.
  • the present invention comprises bonding a preformed solder deposit to a heat spreader wherein an attaching flux and finishing flux are utilized with the preform.
  • the preform and flux may be subjected to reflow condition one or two times.
  • an additional amount of attach flux may be added to the solder deposit before attachment to the back side of a microprocessor die.
  • the present invention is generally directed to methods of controlling solder deposition on a heat spreader or heat sink or conductive material.
  • the methods may be utilized with electrical connections and non-electrical connections, i.e., transporting thermal energy from the device via heat sinks.
  • the methods may also be used in forming connections for the transporting of electrical energy from one conductive metal to another metal. It will be described specifically for the controlled deposit of solder on heat spreaders or heat sinks used for semiconductor packages.
  • the first method comprises applying a sufficient amount of an attaching flux to a heat spreader or heat sink, placing a solder preform on the flux on the heat spreader, applying a sufficient amount of finishing flux onto the preform, subjecting the heat spreader, fluxes, and preform to reflow conditions, cooling, cleaning the substrate and preform, now the solder deposit, flattening the solder deposit and optionally applying an effective amount of second attach flux to the solder depositon for attachment to a back side of a microprocessor die.
  • An alternate method of the present invention comprises applying the attaching flux to a heat spreader or heat sink, placing a solder preform on the flux on the heat spreader, subjecting the heat spreader, attaching flux, and preform to reflow conditions, then applying a finishing flux to the heat spreader and preform, now the solder deposit, subjecting the heat spreader, solder deposit, and finishing flux to reflow conditions, cooling, cleaning the heat spreader and solder deposit, flattening the solder deposit and optionally applying a second attach flux for attachment to the back side of a microprocessor die.
  • Another alternative method of the present invention comprises applying an attaching flux with a solder perform to a first side of a heat spreader or heat sink, following the above steps for subjecting the flux, and perform to one or two reflow conditions with the application of a finishing flux as described. Then applying an attaching flux and solder perform having a lower melting point than the first solder perform on the second side of the heat spreader and apply a finishing flux before or after subjecting the pieces to reflow conditions.
  • the solder deposit on either side is flattened by conventional means and optionally coated with another attaching flux so the first side can be attached to the back side of a microprocessor die and the second side of the heat spreader to a heat sink.
  • Another object of the present invention to provide a method of using an aggressive flux with a solder without regard to the formation of harmful, insoluble, corrosive residues.
  • Figure 1 is a flow chart of the single reflow process of the present invention
  • Figure 2 is a flow chart of the double reflow process of the present invention.
  • Figure 3 shows a side elevation of the deposition of solder on a substrate
  • Figure 4 shows the flattening of the solder deposit prior to attachment to the back side of a microprocessor die
  • Figure 5 shows the application of a solder deposit on first and second sides of a heat spreader.
  • the heat spreader or heat sink dissipates heat. It is the metal surface being soldered or the metal material on which a preform may be attached by melting the preform.
  • the heat spreader for example, may be copper, nickel, brass, gold, or stainless steel.
  • the heat spreader may also be a metal or ceramic material that is plated with a solderable metal, such as copper, nickel, gold over nickel, tin-nickel, silver, or palladium.
  • Attaching flux is a material of sufficient activity to remove oxides and promote solder bonding on the substrate metal.
  • the attaching flux materials may be solid, liquid, viscous paste, or tacky.
  • the attaching flux may be mild or aggressive, depending on the tenacity of the oxidation or tarnish on the substrate surface. Aggressive attaching fluxes used for the solder bonding process could leave salt residue that is insoluble in water and most solvents. The amount and nature of the residue depends upon the chemical composition of the flux, the heat spreader, and the preform alloy used in the particular application.
  • a finishing flux is chosen by its compatibility with the attaching flux.
  • a finishing flux solubilizes residues and salts from an attaching flux and allows the residues to be washed away with an appropriate solvent.
  • the finishing flux leaves no corrosive residue or insoluble salt after washing.
  • the finishing flux preferably will be of a viscous nature, must have sufficient activity to solubilize salts of inorganic and organic acids, but not active enough to promote additional solder spreading on the base metal or substrate.
  • Preform is a pre-controlled amount of solder in a defined shape or matched to a dimension of the final desired solder deposit.
  • the ductility of the solder can be controlled by alloy selection so that a reliable interconnect is made with the two surfaces having dissimilar coefficients of thermal expansion (CTE).
  • Solders that are useful include alloys containing tin, lead, copper, silver, zinc and indium. Tin-lead alloys, having enough lead, are sufficiently ductile to withstand the stresses generated in the joint due to the CTE mismatch between the die and the heat spreader for a reliable joint.
  • Solvent is any suitable liquid that will dissolve and wash away the finishing flux from the surface of the substrate and solder deposit after reflow of the preform.
  • the solvent will be specific to the preform, flux, and substrate used.
  • the solvent may be any polar or non-polar solvent, water, alcohol, terpenes, aliphatic or aromatic petroleum hydrocarbon solvents, esters, ketones, glycol ethers, halogenated hydrocarbons, amines, etc.
  • Reflow is the act of heating the substrate and preform to a temperature that is greater than the liquidus of the preform.
  • preheating may be employed to evaporate the volatile solvents in the flux prior to the preform melting.
  • the wetting ability of the flux is directly related to the peak reflow temperature. The temperature must be high enough to allow good wetting by the solder preform, but not so high as to cause excessive degradation of the flux.
  • the reflow heat is accomplished by a combination of temperature and dwell time. The heat directly affects the activity of the flux and thus the solderability.
  • the preheating and peak temperature and time duration are parameters to be monitored.
  • the method of the present invention is advantageous because it allows for a controlled deposition of solder utilizing an aggressive flux, if necessary, to assure a strong attachment of the preform to the heat spreader.
  • Benefits of using a controlled amount of an aggressive flux include complete solder wetting of the heat spreader and elimination of voids between the solder and heat spreader. Voids are detrimental particularly in heat transfer assemblies because entrapped air and gases act as insulators, thus reducing the efficiency of heat transfer.
  • the method uses a highly aggressive flux with no concern about a corrosive residue because the residue can be effectively removed by the application of the finishing flux and washing.
  • the method of the present invention allows for soldering metals that are difficult to solder with mild, non-corrosive fluxes, by using an aggressive flux, followed by a finishing flux to solubilize the residues for washing away.
  • a controlled amount or sufficient or effective amount is the amount of attaching flux that will fill the capillary space between the preform and heat spreader. If too much attaching flux is used, it will be forced out of the edges of the preform covering the flux on the heat spreader when the preform is placed thereon.
  • a small amount of pressure is used to place the preform on the flux on the heat spreader. If too much pressure is used, some of the flux will be displaced from under the preform.
  • Solders used in the method of the present invention are conventional, for example, without being unduly limitative they may be tin-lead alloys, tin-silver alloys, tin- copper alloys, tin-silver-copper alloys, and 100% indium without or with tin additions.
  • Typical amounts of metals in the alloys are as follows: (Sn 63% Pb 37%), (Sn 50% Pb 50%), (Sn 60% Pb 40%), (Sn 95% Ag 5%), (Sn 96.5%% Ag 3.5%), In 100%, (In 95.5% Sn 0.5%), (In 99.75% Sn 0.25%).
  • the method of the present invention will function with essentially any solder that is compatible with the flux and metal heat spreader or heat sink.
  • indium and several of its alloys are preferred.
  • the thermal conductivity of indium can be enhanced by impregnation of the solder with copper, graphite, silicon carbide or diamond particles.
  • Solder performs are precise stampings of the described solders. They can be prepared in a conventional manner. The preforms are made by alloying the solder and pouring it into a billet. The billet is. compressed to extrude the solder in a wire or ribbon form. It can then be milled to the desired thickness. The ribbon can be cut or fed into a punch press and stamped to the desired dimensions.
  • heat spreaders which can be any solderable metal or plating, some are easier to solder to than others.
  • the heat spreader may be plated with a second metal to prevent corrosion such as nickel plated on copper, or to improve solderability such as palladium plated on nickel or nickel plated on aluminum.
  • Table I shows a lifting of metals for heat spreaders or platings in Groups 1-4 wherein the difficulty to solder increases as the number of the Group increases:
  • Group Heat Spreader Metals or Platings platinum, gold, copper, tin, solder, palladium, silver
  • Oxides on Group 1 metals can be removed with mild fluxes, such as rosin fluxes and many organic fluxes.
  • metals in Group 4 have tenacious oxides that require more aggressive fluxes such as the inorganic type.
  • the methods of the present invention can be utilized with all the foregoing metals. Nevertheless, often an easier to solder second metal may be plated on a metal surface that is more difficult to solder, for example, nickel plating on steel, gold plating on nickel, palladium plating on nickel, nickel plating on aluminum.
  • Table Il shows typical attaching fluxes used in the process of the present invention on three metals that can be used in heat spreaders that are increasingly difficult to solder.
  • the three metals are representative of the groups of metals in Table I.
  • the column "Fluxes” shows increased activity of the attaching fluxes listed from top to bottom, therefore, the IA or Inorganic Acid Flux has more activity and is more corrosive than type RMA or type RA rosin fluxes.
  • the designation of fluxes is conventional and known in the industry. Preferably the listing of fluxes corresponds to the ease of soldering.
  • X denotes the flux will cause the melted solder to wet the base metal of the heat spreader. Every flux type can be used with the metal substrate copper. Some more active, more aggressive, fluxes can be used on copper and nickel. The most aggressive fluxes are required for soldering stainless steel. While all fluxes identified in Table Il can be used for the present invention, the most aggressive are preferred as attaching fluxes, specifically the last three in the column under "Fluxes", Rosin highly activated (RA), organic acid (OA), and inorganic acid (IA). Some attaching fluxes, for example rosin mildly activated (RMA), may not be sufficiently active to adequately accomplish the soldering or bonding of the solder to the metal heat spreader.
  • RMA Rosin mildly activated
  • finishing flux can be applied on top of the preform, attaching flux and heat spreader and the steps of the single reflow process are followed.
  • the addition of the finishing flux provides for thermal insulation of the attaching flux which allows for reduction in the rate of temperature increase during reflow heating. This improves the heat stability of the attaching flux.
  • the foregoing fluxes may also be used as finishing fluxes, including rosin types (R), not listed above, as long as they are compatible and soluble with the specific attaching flux. Compatibility is primarily related to solubility. If the fluxes are soluble in the same solvents, they are considered compatible.
  • the cleaning solvent may be a polar or non-polar liquid.
  • Polar solvents include alcohols and preferably water.
  • Non-polar solvents include, but are not limited to, aliphatic or aromatic petroleum hydrocarbon solvents, esters, ketones, glycol ethers, halogenated hydrocarbons, amines and mixtures thereof.
  • FIG. 1 shows Method 1 , the Single Reflow Process.
  • a deposit of a high-activity flux or attach flux for example, an inorganic acid flux (IA)
  • IA inorganic acid flux
  • the flux may be sprayed on the substrate in a controlled area and thickness, or may be coated or sprayed on the preform prior to placing the preform on the substrate metal, or a controlled deposit of the flux in a quantity sufficient to fill the capillary space between the preform and substrate may be applied.
  • pressure may be applied on the preform 102 as it is placed on the substrate to be soldered.
  • a finishing flux is then added in a controlled amount 104.
  • the amount is dependent on the activity and consistency of the flux.
  • the sufficient or effective amount of the finishing flux in this process is an amount that will not flow underneath the preform and dilute the attaching flux.
  • the finishing fluxes as shown in Table Il as type RMA or Rosin Mildly Activated fluxes, may not be active enough to function as attaching fluxes and promote solder wetting on the substrate metal being used, but still may have sufficient activity to solubilize the residual salts of the inorganic acid, type IA, flux being used as the aggressive attaching flux.
  • the physical form of the finishing fluxes may be paste or a viscous gel or a liquid.
  • the viscosity characteristics of the fluxes are unique to the flux.
  • the reflow process 106 allows heating by various methods known in the art: induction heating, infrared, convection oven, hot gas heating, conduction, microwave energy, etc.
  • the temperature of the substrate being soldered is raised typically to about 20 0 C to about 40 0 C above the liquidus of the solder preform composition.
  • the heating and reflow may take place in an ambient air atmosphere or under nitrogen or other inert atmosphere.
  • the temperature and rate of heating depends upon the mass of the metal substrate and selected attaching flux. Conventional practices suggest that mild attaching fluxes such as rosin, mildly activated, are more susceptible to deterioration by high temperature and slow rate of heating. Therefore, the temperature and rate of heating should be adjusted for the selected flux type as known by skilled workers in the art. Cooling commences when the preform reaches liquidus and metal is wetted.
  • the solder deposition and heat spreader are cleaned with a solvent 108, wherein the solvent may be a polar or non-polar liquid, including but not limited to isopropanol, other alcohols, water, aliphatic or aromatic petroleum hydrocarbon solvents, esters, ketones, glycoi ethers, halogenated hydrocarbons, amines, and mixtures thereof.
  • the finished assembly may also be dried.
  • the solder deposit may be optionally flattened as shown in Figures 3 and 4. Flattening or "coining" of the solder deposit is accomplished by applying a large amount of physical pressure. This can be accomplished by conventional equipment, for example, an Arbor Press. The intent is to compress the top surface of the solder deposit to contrast the shape of the deposit.
  • the surface topography of the solder deposit can be modified by forming channels or other designs to provide less voiding when it is attached to a die or heat sink.
  • An attach flux 112 may optionally be applied to the solder deposit to aid in its attachment to a die or heat sink.
  • the solder deposit with the attach flux which preferably is Attach Flux A or B, is then attached to the back side of a microprocessor die 114. It may also be attached to a heat sink.
  • Figure 2 shows Method 2, a Two Reflow Process.
  • the attaching flux is deposited or placed on the heat spreader 200 as previously described and the preform is placed on the heat spreader 204.
  • Reflow 206 then occurs under conditions previously described, but dependent on the flux, metal heat spreader and preform being used.
  • the finishing flux 208 is applied over the former preform which is now a solder deposit, and reflow 210 takes place again under conditions previously described.
  • the amount of finishing flux is an amount that will cover the attaching flux and at least the edges of the solder deposit.
  • the solder deposit and substrate are then cleaned with a polar or non-polar solvent as previously described 214 and dried.
  • the solder deposit may be flattened 216, and covered with an attach flux 218 and attached to the back of a microprocessor die 220 as previously described.
  • Method I of the present invention provides an effective amount of attaching flux, which is limited to the capillary space between the substrate and preform so that even an aggressive flux can be applied and utilized in a controlled manner to provide a secure bond without concern about harmful residues.
  • the method of the present invention allows for a substantial deposition of flux and solder so that the solder can be fused to provide an intermetallic bond with the base metal.
  • the present invention allows for a controlled deposition of solder in the area.
  • the solder may be present in amounts ranging from a thickness of about 0.005 inch to about 0.012 inch preferably, and up to 0.200 inch.
  • the deposition of a typical amount of solder may fill an area on the base metal approximately in uniform dimensions without spreading beyond the area of deposition. After reflow on a substrate having dimensions of 1.5 inches by 1.5 inches the solder deposition after reflow would be present in an area of about 0.5 inch by 0.5 inch by 0.012 inch in a dome shape with defined boundaries.
  • Figure 3 is a representation of a sufficient amount of solder 300 bonded or deposited on a heat spreader 310 after reflow. The solder is mounded and retains its position on the metal substrate.
  • Figure 4 shows the deposition of solder 400 being flattened by an arm 410 on the heat spreader.
  • the flattening of solder deposit controls its dimensions. Channeling or other marking on the top surface 420 of the solder deposit 400 provides for less voiding when the deposit is attached to a die or heat sink.
  • the method of the present invention provides a void-free bond between the solder and the metal substrate.
  • Figure 5 shows a die 500 attached to a solder preform 510.
  • the die may be associated with various electrical devices and is made from conventional materials. It may include a microprocessor.
  • Electrical contacts 520 may comprise solder bumps that can be coupled to a substrate 530.
  • Substrate 530 may comprise any suitable material for carrying impulses between the die 500 and external devices.
  • Heat spreader 540 is coupled to heat sink 550 by solder deposit 560.
  • the first side 570 of the heat spreader may preferable be coupled with a solder preform containing pure indium to the die 500.
  • solder preform 560 Preferable, conventional solder performs containing silver-copper-tin alloys in solder preform 560 may couple the second side of the heat spreader 580 to heat sink 550. This arrangement is not intended to be unduly limitative for other arrangements of solders may be used to contact the die and heat sink.
  • the following non-limiting examples are presented to further illustrate the present invention. Variations include choice of substrates, solder preform composition, attaching and finishing fluxes, reflow oven speeds, and methods for applying the fluxes.
  • the heating method for melting the solder preform was to use a Sikama conveyorized reflow oven with the reflow zones set as follows: zone 1: 100 0 C, zone 2: 280 0 C, zone 3: 100 0 C 1 zone 4: off, zone 5: off. Each zone measures 6.25 inches in length and width, and the belt speed was varied to provide the heat required for the solder preform composition.
  • a droplet of Attach Flux (F) of sufficient quantity to wet the surface of the solder preform is added to the nickel coated copper heat spreader.
  • a solder preform of 100% Indium with dimensions of 0.5 inches x 0.5 inches x 0.012 inches is then placed onto the flux, and pressed down with sufficient pressure to displace any excess flux from under the preform. This excess flux was removed with a paper towel.
  • the Finishing Flux (5) was added to the top of the preform, and around the sides of the preform with an Asymtek Century Series automatic dispensing system.
  • zone 1 5O 0 C
  • zone 2 250 0 C
  • zone 3 54 0 C
  • zone 4 40°C
  • zone 5 26 0 C.
  • Each zone measures 6.25 inches in length, and the belt speed was ran at 50inches/minute.
  • the sample was rinsed with tap water, isopropanol, and dried with forced air. The resulting product was shiny and visually free of any residues.
  • a droplet of Attach Flux (G) of sufficient quantity to wet the surface of the solder preform is added to the nickel coated copper heat spreader.
  • a solder preform of 100% Indium with dimensions of 0.5 inches x 0.5 inches x 0.012 inches is then placed onto the flux, and pressed down with sufficient pressure to displace any excess flux from under the preform. This excess flux was removed with a paper towel.
  • the Finishing Flux (5) was added to the top of the preform, and around the sides of the preform with an Asymtek Century Series automatic dispensing system.
  • zone 1 off; zone 2: 280 0 C; zone 3: off; zone 4: off; zone 5: off.
  • zone 1 zone 1 : off; zone 2: 280 0 C; zone 3: off; zone 4: off; zone 5: off.
  • zone 1 zone 2: 280 0 C; zone 3: off; zone 4: off; zone 5: off.
  • zone 1 zone 2: 280 0 C; zone 3: off; zone 4: off; zone 5: off.
  • zone 3 off; zone 4: off; zone 5: off.
  • zone 5 off.
  • Each zone measures 6.25 inches in length, and the belt speed was ran at 60inches/minute.
  • the sample was rinsed with tap water, isopropanol, and dried with forced air.
  • the resulting product was shiny and visually free of any residues.
  • a droplet of Attach Flux (with same formula as in Example 1) of sufficient quantity to wet the surface of the solder preform is added to the gold coated nickel/copper heat spreader.
  • the Finishing Flux (with same formula as in Example 1) was added to the top of the preform, and around the sides of the preform with an Asymtek Century Series automatic dispensing system.
  • zone 1 off; zone 2: 28O 0 C; zone 3: off; zone 4: off; zone 5: off.
  • zone 1 zone 1 : off; zone 2: 28O 0 C; zone 3: off; zone 4: off; zone 5: off.
  • zone 1 zone 2: 28O 0 C; zone 3: off; zone 4: off; zone 5: off.
  • zone 1 zone 2: 28O 0 C; zone 3: off; zone 4: off; zone 5: off.
  • zone 3 off
  • zone 4 off
  • zone 5 off.
  • Each zone measures 6.25 inches in length, and the belt speed was ran at 60inches/minute.
  • the sample was rinsed with tap water, isopropanol, and dried with forced air.
  • the resulting product was shiny and visually free of any residues.
  • a droplet of Attach Flux (with same formula as Example 1) of sufficient quantity to wet the surface of the solder preform is added to the nickel coated popper heat spreader.
  • the resulting product was then reflowed on a Sikama reflow oven with the reflow zones as follows: zone 1: off; zone 2: 280 0 C; zone 3: off; zone 4: off; zone 5: off. Each zone measures 6.25 inches in length, and the belt speed was ran at ⁇ Oinches/minute.
  • the Finishing Flux (with same formula as Example 1) was added copiously by hand to the top of the preform, and around the sides of the preform and reflowed again with the same conditions mentioned previously. After the second reflow the sample was rinsed with tap water, isopropanol, and dried with forced air. The resulting product was shiny and visually free of any residues.
  • a droplet of Attach Flux (with same formula as Example 1) of sufficient quantity to wet the surface of the solder preform is added to the nickel coated copper heat spreader.
  • a solder preform of 0.5% Tin / 95.5% Indium with dimensions of 0.5 inches x 0.5 inches x 0.012 inches is then placed onto the flux, and pressed down with sufficient pressure to displace any excess flux from under the preform. This excess flux was removed with a paper towel.
  • the resulting product was then reflowed on a Sikama reflow oven with the reflow zones as follows: zone 1 : off; zone 2: 280 0 C; zone 3: off; zone 4: off; zone 5: off. Each zone measures 6.25 inches in length, and the belt speed was ran at 50inches/minute.
  • the Finishing Flux (with same formula as Example 1) was added copiously by hand to the top of the preform, and around the sides of the preform and reflowed again with the same conditions mentioned previously. After the second reflow the sample was rinsed with tap water, isopropanol, and dried with forced air. The resulting product was visually free of any residues.
  • a droplet of Attach Flux (with same formula as Example 1) of sufficient quantity to wet the surface of the solder preform is added to the nickel coated copper heat spreader.
  • a solder preform of 63% Tin / 37% Lead with dimensions of 0.6 inches x 0.6 inches x 0.012 inches is then placed onto the flux, and pressed down with sufficient pressure to displace any excess flux from under the preform. This excess flux was removed with a paper towel.
  • the resulting product was then reflowed on a Sikama reflow oven with the reflow zones as follows: zone 1: off; zone 2: 28O 0 C; zone 3: off; zone 4: off; zone 5: off. Each zone measures 6.25 inches in length, and the belt speed was ran at 50inches/minute.
  • the Finishing Flux (with same formula as Example 1) was added copiously by hand to the top of the preform, and around the sides of the preform and reflowed again with the same conditions mentioned previously. After the second reflow the sample was rinsed with tap water, isopropanol, and dried with forced air. The resulting product was visually free of any residues.
  • a droplet of Attach Flux (with same formula as Example 1) of sufficient quantity to wet the surface of the solder preform is added to the nickel coated copper heat spreader.
  • the resulting product was then reflowed on a Sikama reflow oven with the reflow zones as follows: zone 1 : off; zone 2: 28O 0 C; zone 3: off; zone 4: off; zone 5: off. Each zone measures 6.25 inches in length, and the belt speed was ran at 50inches/minute.
  • the Finishing Flux (with same formula as Example 1) was added copiously by hand to the top of the preform, and around the sides of the preform and reflowed again with the same conditions mentioned previously. After the second reflow the sample was rinsed with tap water, isopropanol, and dried with forced air. The resulting product was visually free of any residues.
  • a droplet of Attach Flux (with same formula as Example 1) of sufficient quantity to wet the surface of the solder preform is added to the nickel coated copper heat spreader.
  • a solder preform of 63% Tin / 37% Lead with dimensions of 0.6 inches x 0.6 inches x 0.012 inches is then placed onto the flux, and pressed down with sufficient pressure to displace any excess flux from under the preform. This excess flux was removed with a paper towel.
  • the resulting product was then reflowed on a Sikama reflow oven with the reflow zones as follows: zone 1 : off; zone 2: 280 0 C; zone 3: off; zone 4: off; zone 5: off. Each zone measures 6.25 inches in length, and the belt speed was ran at 50inches/minute.
  • the Finishing Flux (5) was added copiously by hand to the top of the preform, and around the sides of the preform and reflowed again with the same conditions mentioned previously. After the second reflow the sample was rinsed with tap water, isopropanol, and dried with forced air. The resulting product was visually free of any residues.
  • a droplet of Attach Flux (with the same formula as Example 1) of sufficient quantity to wet the surface of the solder perform is added to the nickel coated copper heat spreader.
  • the resulting product was then reflowed on a Sikama reflow oven with the reflow zones as follows: zone 1 : off; zone 2: 289 C; zone 3: off; zone 4: off; zone 5: off. Each zone measures 6.25 inches in length, and the belt speed was ran at 60 inches/minute.
  • the Finishing Flux (with the same formula as Example 1) was added copiously by hand to the top of the preform, and around the sides of the preform and reflowed again with the same conditions mentioned previously. After the second reflow the sample was rinsed with tap water, isopropanol, and dried with forced air. The resulting product was shiny and visually free of any residues.
  • the resulting assembly was placed in a die press, which was then placed in a hydraulic press to flatten or coin the indium deposit. The coin deposit was then coated with a low activity Attach Flux A and was readily available for coupling with the back of a microprocessor die.
  • a droplet of Attach Flux F of sufficient quantity to wet the surface of a solder perform is added to a first side of the nickel coated copper heat spreader.
  • a solder perform of 95.5% tin, 3.75% silver, 0.75% copper with dimensions of 0.5 inches by 0.5 inches by 0.012 inches is then placed onto the flux, and pressed down with sufficient pressure to displace any excess flux from under the preform. The excess flux was removed with a paper towel.
  • the resulting product was then reflowed on a Sikama reflow oven with reflow zones as follows: zone 1 : 70 C; zone 2: 100 C; zone 3: 176 C; zone 4: 250 C; zone 5: 500 C. Each zone measures 6.25 inches in length and the belt speed was run at 50 inches/minute.
  • the Finishing Flux 5 was added copiously by hand to the top of the preform, and around the sides of the perform and reflowed again with the same conductors mentioned previously. After the second reflow the sample was rinsed with tap water, isopropanol and dried with forced air. The resulting product was free of residues.
  • This first surface of the heat spreader can be attached to a heat sink.
  • a drop of Attach Flux F of sufficient quantity to wet the surface of the solder perform is added to the nickel coated copper heat spreader.
  • a solder perform of 100% indium with dimensions of 0.5 inches by 0.5 inches by 0.612 inches is then placed onto the flux, pressed down with sufficient pressure to displace any excess flux from under the perform.
  • the excess flux was removed with a paper towel.
  • the Finishing Flux 5 was added to the indium perform on the top and sides.
  • the resulting product was then reflowed on a Sikama reflow oven with the reflow zones as follows: zone 1: off; zone 2: 280 C; zone 3: off; zone 4: off; zone 5: off. Each zone measures 6.25 inches in length and the belt speed was run at 60 inches/minute. After reflow the sample was rinsed with tap water, isopropanol and dried with forced air. The resulting product was shiny and visually free of any residues.
  • the second side of the heat spreader can be attached to the back of a microprocessor die.
  • the respective solder deposits on the first and second sides of the heat spreader were individually flattened and channeled to increase the surface topography for !ess voiding when they are attached to a die or heat sink, respectively.
  • Attach Flux A a low activity flux

Landscapes

  • Engineering & Computer Science (AREA)
  • Mechanical Engineering (AREA)
  • Manufacturing & Machinery (AREA)
  • Microelectronics & Electronic Packaging (AREA)
  • Electric Connection Of Electric Components To Printed Circuits (AREA)
  • Cooling Or The Like Of Semiconductors Or Solid State Devices (AREA)
PCT/US2006/034678 2005-09-06 2006-09-05 Method of controlling solder deposition on heat spreader used for semiconductor package Ceased WO2007030516A1 (en)

Priority Applications (1)

Application Number Priority Date Filing Date Title
JP2008530160A JP5345848B2 (ja) 2005-09-06 2006-09-05 半導体パッケージに使用されるヒートスプレッダ上へのはんだの堆積を制御する方法

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US11/220,457 US20070051774A1 (en) 2005-09-06 2005-09-06 Method of controlling solder deposition on heat spreader used for semiconductor package
US11/220,457 2005-09-06

Publications (1)

Publication Number Publication Date
WO2007030516A1 true WO2007030516A1 (en) 2007-03-15

Family

ID=37622172

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US2006/034678 Ceased WO2007030516A1 (en) 2005-09-06 2006-09-05 Method of controlling solder deposition on heat spreader used for semiconductor package

Country Status (3)

Country Link
US (1) US20070051774A1 (https=)
JP (1) JP5345848B2 (https=)
WO (1) WO2007030516A1 (https=)

Families Citing this family (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US7319048B2 (en) * 2004-09-03 2008-01-15 Intel Corporation Electronic assemblies having a low processing temperature
US7968426B1 (en) * 2005-10-24 2011-06-28 Microwave Bonding Instruments, Inc. Systems and methods for bonding semiconductor substrates to metal substrates using microwave energy
DE102005053553A1 (de) * 2005-11-08 2007-05-16 Heraeus Gmbh W C Lotpasten mit harzfreien Flussmittel
US7651938B2 (en) * 2006-06-07 2010-01-26 Advanced Micro Devices, Inc. Void reduction in indium thermal interface material
US7829195B2 (en) * 2006-12-31 2010-11-09 Intel Corporation Fluorination pre-treatment of heat spreader attachment indium thermal interface material
US20080156635A1 (en) * 2006-12-31 2008-07-03 Simon Bogdan M System for processes including fluorination
US8728872B2 (en) * 2011-08-18 2014-05-20 DY 4 Systems, Inc. Manufacturing process and heat dissipating device for forming interface for electronic component
PL3834980T3 (pl) * 2019-12-10 2023-04-17 Heraeus Deutschland GmbH & Co. KG Pasta lutownicza

Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4752027A (en) * 1987-02-20 1988-06-21 Hewlett-Packard Company Method and apparatus for solder bumping of printed circuit boards
US5349495A (en) * 1989-06-23 1994-09-20 Vlsi Technology, Inc. System for securing and electrically connecting a semiconductor chip to a substrate
US20040074952A1 (en) * 2002-10-16 2004-04-22 Stipp John N. Method of controlling solder deposition utilizing two fluxes and preform

Family Cites Families (35)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US2149962A (en) * 1937-12-11 1939-03-07 Atlas Powder Co Soldering flux
US3855679A (en) * 1973-11-05 1974-12-24 Ford Motor Co Aluminum soldering
US4504007A (en) * 1982-09-14 1985-03-12 International Business Machines Corporation Solder and braze fluxes and processes for using the same
JPS60210844A (ja) * 1984-04-05 1985-10-23 Sanken Electric Co Ltd 半田接着方法
US4817854A (en) * 1985-03-11 1989-04-04 The United States Of America As Represented By The Secretary Of The Air Force LED soldering method utilizing a PT migration barrier
US5269453A (en) * 1992-04-02 1993-12-14 Motorola, Inc. Low temperature method for forming solder bump interconnections to a plated circuit trace
US5371404A (en) * 1993-02-04 1994-12-06 Motorola, Inc. Thermally conductive integrated circuit package with radio frequency shielding
KR970005712B1 (ko) * 1994-01-11 1997-04-19 삼성전자 주식회사 고 열방출용 반도체 패키지
US5543585A (en) * 1994-02-02 1996-08-06 International Business Machines Corporation Direct chip attachment (DCA) with electrically conductive adhesives
US5411199A (en) * 1994-03-07 1995-05-02 Motorola, Inc. Method for attaching a shield
US5492266A (en) * 1994-08-31 1996-02-20 International Business Machines Corporation Fine pitch solder deposits on printed circuit board process and product
KR0181615B1 (ko) * 1995-01-30 1999-04-15 모리시다 요이치 반도체 장치의 실장체, 그 실장방법 및 실장용 밀봉재
US5655703A (en) * 1995-05-25 1997-08-12 International Business Machines Corporation Solder hierarchy for chip attachment to substrates
US5985043A (en) * 1997-07-21 1999-11-16 Miguel Albert Capote Polymerizable fluxing agents and fluxing adhesive compositions therefrom
US6139336A (en) * 1996-11-14 2000-10-31 Berg Technology, Inc. High density connector having a ball type of contact surface
US6017634A (en) * 1997-07-21 2000-01-25 Miguel Albert Capote Carboxyl-containing polyunsaturated fluxing agent and carboxyl-reactive neutralizing agent as adhesive
US6367150B1 (en) * 1997-09-05 2002-04-09 Northrop Grumman Corporation Solder flux compatible with flip-chip underfill material
JP3311282B2 (ja) * 1997-10-13 2002-08-05 株式会社東芝 金属部材の接合方法及び接合体
WO1999035187A1 (en) * 1998-01-07 1999-07-15 Georgia Tech Research Corporation Reworkable epoxy underfill encapsulants
US6057381A (en) * 1998-07-02 2000-05-02 National Starch And Chemical Investment Holding Corporation Method of making an electronic component using reworkable underfill encapsulants
JP2000036518A (ja) * 1998-07-16 2000-02-02 Nitto Denko Corp ウェハスケールパッケージ構造およびこれに用いる回路基板
US6154364A (en) * 1998-11-19 2000-11-28 Delco Electronics Corp. Circuit board assembly with IC device mounted thereto
US6362435B1 (en) * 1999-12-20 2002-03-26 Delphi Technologies, Inc. Multi-layer conductor pad for reducing solder voiding
US6548790B1 (en) * 2000-02-24 2003-04-15 Trucco Horacio Andres Apparatus for manufacturing solid solder deposit PCBs
JP2001339011A (ja) * 2000-03-24 2001-12-07 Shinko Electric Ind Co Ltd 半導体装置およびその製造方法
JP2001332575A (ja) * 2000-05-19 2001-11-30 Sony Corp フラックス洗浄方法及び半導体装置の製造方法
JP4609617B2 (ja) * 2000-08-01 2011-01-12 日本電気株式会社 半導体装置の実装方法及び実装構造体
KR100371567B1 (ko) * 2000-12-08 2003-02-07 삼성테크윈 주식회사 Ag 선도금을 이용한 반도체 패키지용 리드프레임
JP2002273567A (ja) * 2001-03-16 2002-09-25 Nidec Tosok Corp スパンカツール
JP2003001408A (ja) * 2001-06-19 2003-01-08 Seiko Instruments Inc 基板同士のはんだ接合方法
US6800141B2 (en) * 2001-12-21 2004-10-05 International Business Machines Corporation Semi-aqueous solvent based method of cleaning rosin flux residue
US7846778B2 (en) * 2002-02-08 2010-12-07 Intel Corporation Integrated heat spreader, heat sink or heat pipe with pre-attached phase change thermal interface material and method of making an electronic assembly
US7182241B2 (en) * 2002-08-09 2007-02-27 Micron Technology, Inc. Multi-functional solder and articles made therewith, such as microelectronic components
JP2005007412A (ja) * 2003-06-17 2005-01-13 Sumitomo Metal Mining Co Ltd 半田クラッド片
US20050121776A1 (en) * 2003-12-05 2005-06-09 Deppisch Carl L. Integrated solder and heat spreader fabrication

Patent Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4752027A (en) * 1987-02-20 1988-06-21 Hewlett-Packard Company Method and apparatus for solder bumping of printed circuit boards
US5349495A (en) * 1989-06-23 1994-09-20 Vlsi Technology, Inc. System for securing and electrically connecting a semiconductor chip to a substrate
US20040074952A1 (en) * 2002-10-16 2004-04-22 Stipp John N. Method of controlling solder deposition utilizing two fluxes and preform

Also Published As

Publication number Publication date
JP5345848B2 (ja) 2013-11-20
US20070051774A1 (en) 2007-03-08
JP2009507395A (ja) 2009-02-19

Similar Documents

Publication Publication Date Title
US6786391B2 (en) Method of controlling solder deposition utilizing two fluxes and preform
US7344061B2 (en) Multi-functional solder and articles made therewith, such as microelectronic components
US6550667B2 (en) Flux composition and soldering method for high density arrays
CN100469222C (zh) 在电子元件上形成焊料区的方法和具有焊料区的电子元件
US6220501B1 (en) Method of joining metallic members, and joined metallic members
EP3038790B1 (en) Joining to aluminium
JPH0788680A (ja) 高温無鉛すずベースはんだの組成
JPH0788679A (ja) 無鉛すずアンチモン・ビスマス銅はんだ合金
US7740713B2 (en) Flux composition and techniques for use thereof
CN1122738A (zh) 焊剂配方及相应的焊接方法
US6871775B2 (en) Process for soldering and connecting structure
DE60300675T2 (de) Die Verwendung von Lötmetallen auf Nickel-plattierten stromlosen Oberflächen
JPH08164496A (ja) Sn−Zn系、Sn−Zn−Bi系はんだ及びその表面処理方法並びにそれを用いた実装品
KR20010012083A (ko) 무연 땜납
US20070051774A1 (en) Method of controlling solder deposition on heat spreader used for semiconductor package
JP2001274539A (ja) 電子デバイス搭載プリント配線板の電極接合方法
JPH1133776A (ja) 半田材料及びそれを用いた電子部品
JP6267427B2 (ja) はんだ付け方法及び実装基板
CN106112162B (zh) 一种用于减少锡铋焊点金属间化合物形成的方法
JP3684134B2 (ja) 電気又は電子部品及び電気又は電子組立体
CN102782189A (zh) Pd或以Pd为主成分的合金的表面处理剂、和铜表面的表面皮膜层构造
JP3592054B2 (ja) 電子回路及びその製造方法
CN115401364B (zh) 一种高活性水洗助焊剂及其制备工艺
JP2004156094A (ja) Sn又はSn合金に対する表面処理剤及び表面処理方法
JP4502430B2 (ja) はんだ濡れ性向上処理剤、及び錫及び錫合金のはんだ濡れ性の向上方法

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application
WWE Wipo information: entry into national phase

Ref document number: 2008530160

Country of ref document: JP

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 06814214

Country of ref document: EP

Kind code of ref document: A1