WO2007020818A1 - ポリウレタン・チオウレタン系光学用樹脂およびその製造方法 - Google Patents
ポリウレタン・チオウレタン系光学用樹脂およびその製造方法 Download PDFInfo
- Publication number
- WO2007020818A1 WO2007020818A1 PCT/JP2006/315486 JP2006315486W WO2007020818A1 WO 2007020818 A1 WO2007020818 A1 WO 2007020818A1 JP 2006315486 W JP2006315486 W JP 2006315486W WO 2007020818 A1 WO2007020818 A1 WO 2007020818A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- compound
- polyurethane
- molecule
- polyol
- component
- Prior art date
Abstract
Description
Claims