WO2006134860A1 - 合わせガラス - Google Patents

合わせガラス Download PDF

Info

Publication number
WO2006134860A1
WO2006134860A1 PCT/JP2006/311733 JP2006311733W WO2006134860A1 WO 2006134860 A1 WO2006134860 A1 WO 2006134860A1 JP 2006311733 W JP2006311733 W JP 2006311733W WO 2006134860 A1 WO2006134860 A1 WO 2006134860A1
Authority
WO
WIPO (PCT)
Prior art keywords
glass
laminated glass
glass plate
laminated
film
Prior art date
Application number
PCT/JP2006/311733
Other languages
English (en)
French (fr)
Inventor
Tadashi Marumoto
Kunio Mitoma
Original Assignee
Sekisui Chemical Co., Ltd.
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Sekisui Chemical Co., Ltd. filed Critical Sekisui Chemical Co., Ltd.
Priority to EP06766595A priority Critical patent/EP1908738A4/en
Priority to AU2006258682A priority patent/AU2006258682B2/en
Priority to US11/596,713 priority patent/US20080268236A1/en
Priority to CA002604634A priority patent/CA2604634A1/en
Priority to BRPI0611958A priority patent/BRPI0611958A2/pt
Publication of WO2006134860A1 publication Critical patent/WO2006134860A1/ja

Abstract

　合わせガラスとしての基本的性能を保持しつつ、室外側から見ると、鮮やかな色目を呈し、また、室内側から見ると、室内側ガラス板自体の色目とほとんど変わらない色目を呈するように構成された合わせガラスを提供することを目的とするものであり、２枚のガラス板が中間膜を介して積層されてなる合わせガラスであって、室外側に位置するように用いられる一方のガラス板が有色透明ガラス板であり、室内側に位置するように用いられる他方のガラス板が可視光線反射ガラス板であり、中間膜が錫ドープ酸化インジウム（ＩＴＯ）微粒子を含んでいることを特徴とする合わせガラスである。

Description

明 細 書
合わせガラス
技術分野
[0001] 本発明は、合わせガラスに関し、更に詳しくは、合わせガラスの基本的性能を保持 しつつ、室内と室外とを隔てるように窓などに設置したときに、室外から見ると鮮やか な色目を呈し、室内から見ると、中間膜や室外側ガラスの影響を受けにくぐ室内側 ガラス板自体の色目と実質的に変わらな 、色目を呈する、色目の調整が容易である 合わせガラスに関する。
背景技術
[0002] 従来より、合わせガラスは、透明性、耐候性、積層接着性および耐貫通性に優れ、 さらに、ガラス破片が飛散しにくいといった性能を基本性能として有しているため、例 えば、自動車などの車両や建築物の窓ガラスに広く使用されている。このような合わ せガラスとしては、例えば、少なくとも一対のガラス板間に、可塑剤により可塑化され たポリビニルブチラール榭脂等のポリビニルァセタール榭脂からなる合わせガラス用 中間膜を介在させ、一体化させたもの等が挙げられる。近年においては、熱遮蔽性 を高める目的で、熱遮蔽性合わせガラスが好適に用いられている。熱遮蔽性合わせ ガラスについては、中間膜に熱遮蔽性微粒子である錫ドープ酸化インジウム (ITO) 微粒子を添加した合わせガラスなどが従来カゝら用いられて ヽるが、 ITO微粒子を用 いて中間膜に熱遮蔽能を付与する場合、 ITO微粒子の配合量が多すぎると、中間 膜のヘイズ値が上昇するという問題が生じる。
[0003] また、このような熱遮蔽性合わせガラスは、中間膜に ITO微粒子が添加された場合 には、室内側力 見ると、中間膜に含まれる ITO微粒子の影響により、青味をおびる などして室内側力 見た色目が変わるため、別途室内側ガラス板の色目の調整など をしなければならなかった。この室内側ガラス板の色目の調整は、中間膜における IT o微粒子や室外側ガラス板に用いられるカラーガラスの影響などを考慮しなければ ならず、大変手間の力かるものであった。また、このような手間を省くために、中間膜 における ITO微粒子の含有量を少量にしたりすることなどが考えられる力 その場合 には、熱遮蔽性などの熱遮蔽性合わせガラスの基本性能が損なわれる恐れがあった 。さらに、中間膜における ITO微粒子の含有量を少量にした合わせガラスを室外から 見ると、可視光線の透過により色目が薄れ、鮮やかな色目を呈することが困難で、意 匠性を損なうという恐れもあった。
[0004] 上記のような理由から、合わせガラスの基本的性能を保持しつつ、室外から見ると 鮮やかな色目を呈し、室内から見る色目には中間膜や室外側ガラス力 の影響を受 けにく 、合わせガラスが待ち望まれて 、た。
[0005] なお、熱遮蔽性合わせガラス (特に、カラーガラス Ζιτο微粒子含有中間膜 Zカラ 一ガラス）については、例えば特許文献 1に記載されている。
特許文献 1：特開 2002— 326847号公報
発明の開示
発明が解決しょうとする課題
[0006] 本発明は、合わせガラスとしての基本的性能を保持しつつ、室外側から見ると、鮮 やかな色目を呈し、また、室内側から見ると、室内側ガラス板自体の色目とほとんど 変わらな 、色目を呈するように構成された合わせガラスを提供することを目的とする。 課題を解決するための手段
[0007] 本発明者らは、上記目的を達成すべく鋭意検討した結果、室内側となる一方に有 色透明のいわゆるカラーガラス板を配置し、他方に可視光線を反射するいわゆるミラ 一ガラスを配置し、さらに中間膜として錫ドープ酸化インジウム (ITO)微粒子を配合 した中間膜を用いることにより、熱遮蔽性などの合わせガラスの基本性能を損なうこと なぐ室外側力 該合わせガラスを見ると、カラーガラスに由来する鮮明な色目を呈し 、また、室内側から該合わせガラスを見ると、中間膜や室外側ガラス力もの色の影響 をあまり受けることなぐ室内側ガラス本来の色目とほとんど変わらない色目を呈する 合わせガラスが得られることを見出し、さらに検討を重ねて本発明を完成させるに至 つた o
[0008] すなわち、本発明は、
[1] 2枚のガラス板が中間膜を介して積層されてなる合わせガラスであって、一方 のガラス板が有色透明ガラス板であり、他方のガラス板が可視光線反射ガラス板であ り、中間膜が錫ドープ酸化インジウム (ITO)微粒子を含んで ヽることを特徴とする合 わせガラス、
[2] 有色透明ガラス板が室外側に位置し、可視光線反射ガラス板が室内側に位置 するようにして用いられる前項 [1]に記載の合わせガラス、
[3] 可視光線反射ガラス板が、ガラス板の片面または両面に金属膜を被覆してな る前記 [1ほたは [2]に記載の合わせガラス、
[4] 金属膜が Ag膜である前記 [3]に記載の合わせガラス、
[5] 中間膜が、ポリビニルァセタール榭脂を構成榭脂とする前記 [1]〜[4]のいずれ かに記載の合わせガラス、
[6] ポリビュルァセタール榭脂が、可塑剤により可塑ィ匕されたポリビュルプチラー ル榭脂である前記 [5]に記載の合わせガラス、
[7] 中間膜に含まれる錫ドープ酸化インジウム (ITO)微粒子の含有量が、中間膜 に対して、 0. 1〜1. 0質量％である前記 [1]〜[6]のいずれかに記載の合わせガラス 、および
[8] 車両のサイドガラス、リアガラスまたはルーフガラスに用いられる前記 [1]〜[7] の!、ずれかに記載の合わせガラス、
に関する。
発明の効果
[0009] 本発明の合わせガラスは、合わせガラスの基本性能を損なうことなく、該合わせガラ スを車両や建物の窓に設置して室外側力 該合わせガラスを見ると、室外側の有色 透明ガラス板による鮮やかな色目を呈し、また、室内側から該合わせガラスを見ると、 中間膜や室外側ガラスの色目の影響をあまり受けることなぐ室内側ガラス板の本来 の色目とほとんど変わらない色目を呈するので、従来の合わせガラスに比べて室内 側ガラス板の色目の調整に手間をかける必要がない。
発明を実施するための最良の形態
[0010] 本発明の合わせガラスは、 2枚のガラス板が中間膜を介して積層されてなる合わせ ガラスであって、一方のガラス板が有色透明ガラス板であり、他方のガラス板が可視 光線反射ガラス板であり、中間膜が錫ドープ酸化インジウム (ITO)微粒子を含んで 、ることを特徴とする。カゝかる構成を有する本発明の合わせガラスを車両や建物の窓 に設置するなどして使用する場合、通常は有色透明ガラス板の側を室外側とし、可 視光線反射ガラス板の側を室内側として使用する。以下に、本発明の合わせガラス の構成材料及び製造方法にっ ヽて順次説明する。
[0011] (有色透明ガラス板）
前記有色透明ガラス板は、有色透明ガラスで作られたガラス板であって、本発明の 目的を阻害しない限り特に限定されず、公知のものであってよい。前記有色透明ガラ スの種類としては、例えばグリーン色、ブロンド色、グレー色、ブルー色のソーダライ ムシリカガラスなどが挙げられる。前記有色透明ガラスとして、グリーン色ソーダライム シリカガラスを採用した場合には、その構成としては、質量百分率表示で Fe O換算
2 3 した全鉄 0. 3〜1%を含有するソーダライムシリカガラスが挙げられ、好適には、質量 百分率表示で Fe O換算した全鉄中の Fe O換算した FeOの質量が 20〜40%の
2 3 2 3
ソーダライムシリカガラスが挙げられる。さらに、合わせガラス力も切り出した lcm2の 合わせガラス片を構成する各ガラス板に含まれる Fe O換算した全鉄の含有量の総
2 3
和が、 2〜7mgであることが好ましい。
[0012] (可視光線反射ガラス板）
前記可視光線反射ガラス板は、本発明の目的を阻害しない限り特に限定されず、 常法に従い、ガラス板の片面または両面を金属膜で被覆することにより得られる。より 具体的には、例えば、ガラス板の少なくとも一つのガラス面を、スパッタリング法、真空 蒸着法、イオンプレーティング法等により、金属膜で被覆することにより得られる。な お、前記金属膜を構成する金属としては、 Ag (銀)、 Au (金）、 Cu (銅）、 Pd (パラジゥ ム）、 Rh (ロジウム)等の光線反射能を有する金属が挙げられる。前記金属膜としては 、 Ag膜が好ましい。また、ガラス板の片面に金属膜を被覆する場合、中間膜側の面 すなわち通常の使用時には室外に近い側となる面に被覆するのが好ましい。なお、 金属膜の厚さとしては、 2〜200nm程度が好ましい。
[0013] (中間膜）
前記中間膜は、錫ドープ酸化インジウム (ITO)微粒子を含む中間膜であれば特に 限定されない。中間膜中の錫ドープ酸化インジウム (ITO)微粒子の含有量は、本発 明の目的を阻害しない限り特に限定されないが、好ましくは 0. 1〜1. 0質量％である 。また、 ITO微粒子の粒子径としては、特に限定されないが、 10〜80nmが好ましい
[0014] 前記中間膜を主として構成する構成榭脂としては、本発明の目的を阻害しない限り 特に限定されず、公知のものが適宜採用され得る力 好ましくはポリビニルァセター ル榭脂であり、より好ましくは可塑剤により可塑ィ匕された可塑ィ匕ポリビュルァセタール 榭脂であり、最も好ましくは、可塑ィ匕ポリビニルブチラール榭脂である。
[0015] 前記可塑剤としては、合わせガラスの中間膜に用いられている公知の可塑剤、例え ば、一塩基酸エステル、多塩基酸エステルなどの有機エステル系可塑剤などが挙げ られる。力かる可塑剤の代表的なものとしては、例えば、（ィ）トリエチレングリコールと 有機酸との反応によって得られたグリコール系エステル、（口）有機酸と炭素数 4〜8 の直鎖状又は分岐状アルコールとのエステル、 （ハ）トリエチレングリコールジー 2— ェチルブチレート、トリエチレングリコールジー 2—ェチルへキソエート、トリエチレング リコールジカプリレート、トリエチレングリコールージーェチルへキサノエート（3GO)な どが挙げられる。可塑剤の使用量としては、本発明の目的を阻害しない限り特に限 定されないが、好ましくは構成榭脂 100質量部に対して 30〜70質量部であり、特に 好ましくは 35〜45質量部である。
[0016] 前記中間膜は、構成榭脂ゃ可塑剤以外に、例えば、紫外線吸収剤、酸化防止剤、 光安定化剤、界面活性剤などの公知の添加剤を含有して 、てもよ 、。
[0017] 前記中間膜は、上記の各材料力 常法に従い製膜して得られる。製膜方法として は、例えば、押し出し法、カレンダ一法、プレス法等の通常の製膜法によりシート状に 製膜する方法等が挙げられる。これらの製膜技術は従来十分に確立した技術なので 、本発明においてもこれら技術を適宜採用できる。
[0018] (製造方法）
本発明の合わせガラスは、常法に従い、前記有色透明ガラス板と前記可視光線反 射ガラス板とを前記中間膜を介して積層し、これを一体化することにより製造できる。 例えば、前記室外側ガラスと前記室内側ガラスの間に前記中間膜を挟み、これをゴ ムノッグに入れ、減圧吸引しながら約 70〜： L 10°Cで予備接着し、次いで、オートタレ ーブを用いるか、又は加熱機能を備えたプレス装置を用い、約 120〜150°Cで、約 1 〜1. 5MPaの圧力で本接着を行うことにより本発明の合わせガラスを製造することが できる。
[0019] 本発明の合わせガラスは、従来の合わせガラスと同様、自動車などの車両や建築 物の窓ガラスをはじめとする種々の用途に用いられる力 特に、車両のサイドガラス、 リァガラスまたはルーフガラスに好適に用いられる。
[0020] 本発明の合わせガラスを、車両のサイドガラス、リアガラス、ルーフガラスに用いる場 合には、軽量ィ匕を図るために合わせガラスの厚みを薄くすると遮音性が下がり、室内 の快適性が悪くなる恐れがあるため、前記合わせガラスに遮音膜を張り合わせて用 いるのが好ましい。また、前記遮音膜は、本発明の合わせガラスを製造する際に、前 記中間膜と 、ずれかのガラス板との間に積層して用いてもよぐ予め中間膜と遮音膜 とを張り合わせて力も用いてもょ 、。
なお、本発明の合わせガラスを構成する各ガラス板および中間膜の厚みとしては、 特に限定されるものではなぐ合わせガラスの用途に応じて公知のもしくは可能な範 囲で適宜設定すればよい。
実施例
[0021] (実施例 1〜2および比較例 1〜2)
(1)中間膜の調製
トリオクチルホスフェートをトリエチレングリコールージーェチルへキサノエート（3GO )に分散させて混合液とし、さらにこの混合液中に ITO微粒子 (平均粒径 35nm)を分 散させて ITO微粒子分散液を調製した。この ITO微粒子分散液をポリビュルブチラ ール榭脂に添加し、ミキシングロールで充分に溶融混練し、プレス成形機を用いて 1 50°Cで 30分間プレス成形することにより、厚さ 0. 8mmの中間膜 (SCF)を得た。な お、前記の ITO微粒子分散液の調製およびポリビュルプチラール榭脂への添加に 際しては、中間膜中の ITO微粒子含有量が 0. 2質量％となるよう、また、ポリビニル ブチラール榭脂 100質量部に対するトリオクチルホスフェートおよび 3GOの量がそれ ぞれ 0. 08質量部および 40質量部となるよう、混合比および添加量を調整した。
[0022] (2)合わせガラスの製造 前記（1)で得られた中間膜 (SCF)を、表 1に示される室外側ガラスとしての有色透 明ガラス板と室内側ガラスとしての可視光線反射ガラス板または有色透明ガラス板と で挟み込み、これをゴムバック内に入れ、 2. 6kPaの真空度で 20分間脱気した後、 脱気したままオーブンに移し、更に 90°Cで 30分間保持することにより予備接着した。 このようにして予備接着された積層物をオートクレープ中で 135°C、圧力 1. 2MPaの 条件で 20分間の圧着 (本接着)を行 ヽ、表 1に示される構成の合わせガラスを得た。
[0023] [表 1]
Figure imgf000008_0001
※ 室外側 （中間膜側） の面に A g膜が被覆されているガラスである。
[0024] (評価）
実施例 1〜2および比較例 1〜2で得られた合わせガラスについて以下の方法によ り評価を行った。結果を表 2に示した。
[0025] [可視光透過率 (Tv)、日射透過率 (Te)および日射反射率 (Re)の測定]
直記分光光度計（島津製作所社製「UV3100」）を使用して、 JIS Z 8722および JIS R 3106に従って、 380〜780 の可視光透過率 (Tv 300〜2100nmの 日射透過率 (Te)および 300〜2100nmの日射反射率 (Re)を求めた。
[0026] [表 2] T V T e R e
実施例 3 3 2 . 0 2 4 . 9 1 8 . 5
実施例 2 2 6 . 4 2 8 . 1 1 7 . 2
比較例 1 7 3 . 9 3 8 . 1 5 . 8
比較例 2 5 0 . 2 3 9 . 5 5 . 2
(単位 ： ％)
[0027] また、実施例および比較例の合わせガラスを窓ガラスとして設置して日中の晴天時 に色目を観察した。その結果、実施例 1〜2の合わせガラスは、室外側から該合わせ ガラスを目視で観察すると、室外側の有色透明ガラスによる鮮やかな色目を呈してお り、室内側力 該合わせガラスを目視で観察すると、室内側ガラス板の本来の色目と ほとんど変わらな 、色目を呈して!/、た。
一方、比較例 1〜2の合わせガラスは、室外側から該合わせガラスを目視で観察す ると、実施例のものと比べて色目が鮮やかでなぐまた、室内側カも該合わせガラスを 目視で観察すると、室内側ガラス板および室外側ガラス板を合わせた色目に中間膜 の ITO微粒子による色目（青味）が混ざったような色目を呈していた。
なお、表 2より、実施例 1〜2の合わせガラスは、比較例 1〜2のものと比べて、可視 光透過率 (Tv)および日射透過率 (Te)が低く、 日射反射率 (Re)が高 、ことが分力る 。これは、上記の観察結果を裏付けるものと思われる。
産業上の利用可能性
[0028] 本発明の合わせガラスは、従来の合わせガラス同様、種々の用途に用いられる力 特に、車両のサイドガラス、リアガラスまたはルーフガラスに有用である。

Claims

請求の範囲
[1] 2枚のガラス板が中間膜を介して積層されてなる合わせガラスであって、一方のガラ ス板が有色透明ガラス板であり、他方のガラス板が可視光線反射ガラス板であり、中 間膜が錫ドープ酸化インジウム (ITO)微粒子を含んで 、ることを特徴とする合わせガ ラス。
[2] 有色透明ガラス板が室外側に位置し、可視光線反射ガラス板が室内側に位置する ようにして用いられる請求の範囲第 1項に記載の合わせガラス。
[3] 可視光線反射ガラス板が、ガラス板の片面または両面に金属膜を被覆してなる請 求の範囲第 1項または第 2項に記載の合わせガラス。
[4] 金属膜が Ag膜である請求の範囲第 3項に記載の合わせガラス。
[5] 中間膜が、ポリビュルァセタール榭脂を構成榭脂とする請求の範囲第 1項〜第 4項 の!、ずれかに記載の合わせガラス。
[6] ポリビニルァセタール榭脂が、可塑剤により可塑ィ匕されたポリビュルプチラール榭 脂である請求の範囲第 5項に記載の合わせガラス。
[7] 中間膜に含まれる錫ドープ酸化インジウム (ITO)微粒子の含有量が、中間膜に対 して、 0. 1〜1. 0質量％である請求の範囲第 1項〜第 6項のいずれかに記載の合わ せガラス。
[8] 車両のサイドガラス、リアガラスまたはルーフガラスに用いられる請求の範囲第 1項 〜第 7項の 、ずれか〖こ記載の合わせガラス。
PCT/JP2006/311733 2005-06-12 2006-06-12 合わせガラス WO2006134860A1 (ja)