Classifications

• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
  • C08G65/00—Macromolecular compounds obtained by reactions forming an ether link in the main chain of the macromolecule
  • C08G65/02—Macromolecular compounds obtained by reactions forming an ether link in the main chain of the macromolecule from cyclic ethers by opening of the heterocyclic ring
  • C08G65/04—Macromolecular compounds obtained by reactions forming an ether link in the main chain of the macromolecule from cyclic ethers by opening of the heterocyclic ring from cyclic ethers only
  • C08G65/22—Cyclic ethers having at least one atom other than carbon and hydrogen outside the ring
  • C08G65/223—Cyclic ethers having at least one atom other than carbon and hydrogen outside the ring containing halogens
  • C08G65/226—Cyclic ethers having at least one atom other than carbon and hydrogen outside the ring containing halogens containing fluorine

Definitions

• the present invention relates to the polymerization of hexafluoropropylene oxide (HFPO).
• HFPO hexafluoropropylene oxide
• the present invention relates to a polymerization of HFPO that yields a desired degree of polymerization combined with a low amount of low molecular weight oligomers of HFPO.
• the present invention provides a process for oligomerization of hexafluoropropylene oxide, the process comprising polymerizing a mixture of hexafluoropropylene oxide and hexafluoropropene in the presence of an aprotic organic solvent using KF as a catalyst.
• the above process generally yields only a low amount of HFPO oligomers having a degree of polymerization of less than 5. It has further been found that generally, the degree of polymerization and molecular weight distribution shows little variation with changes in the weight ratio of catalyst to HFPO.
• the process can provide oligomers having a degree of polymerization of 6 to 10 with the amount of oligomers having a degree of polymerization of 4 or less being low, e.g. not more than 10% by weight, preferably not more than 5% by weight of the total weight of HFPO oligomers produced.
• the polymerization process can be carried out in a convenient, easy and cost effective way, yielding the desired HFPO oligomers in an economically effective way.
• the production of HFPO results in HFP/HFPO mixtures from which HFP needs to be separated, which is a costly process.
• the polymerization of HFPO according to the invention can use the crude mixture of HFP/HFPO without separation of the HFP.
• the polymerization of HFPO according to the present invention is carried out using a mixture of HFPO and HFP. While the amount of HFP may vary widely, the molar ratio of HFP to HFPO is typically between 4 and 0.05. In one embodiment, the molar ration may be between 3 and 0.2. In another embodiment, the molar ratio could be between 2 and 0.25.
• the polymerization of HFPO is started using KF as a catalyst.
• the KF catalyst is typically dissolved or dispersed in an aprotic polar organic solvent.
• Suitable solvents that can be used include crown ethers and glymes such as monoglyme, diglyme, triglyme and tetraflyme. Further suitable solvents include tetrahydrofuran and 1,4-dioxane. A mixture of solvents can be used as well.
• the solvents used in the polymerization should be dried. Typically, the solvents can be dried to a residual water content of not more than 500 ppm. In one embodiment the residual water content of a solvent used could be less than 200 ppm or less than 100 ppm. Solvents with even lower residual water content of for example less than 50 ppm may be used as well.
• the use of KF fluoride as a catalyst in the process according to the present invention can provide the advantage that the average degree of polymerization and molecular weight distribution is less dependent on the amount of catalyst used relative to the amount of HFPO fed to the polymerization. Accordingly, varying amounts of HFPO may be fed to the polymerization using a same amount of catalyst without substantially affecting the molecular weight and distribution of the corresponding oligomers produced.
• the weight percentage of KF catalyst is between 20 and 0.1 based on the amount of HFPO fed to the polymerization. In one embodiment, the weight percentage of KF catalyst is between 15 and 0.3. In another embodiment, the weight percentage of KF catalyst is between 10 and 0.5.
• the polymerization of HFPO is typically carried out at a temperature of-30°C to 5O 0 C.
• the polymerization temperature can be between -10 and 2O 0 C.
• Oligomers having an average polymerization degree of 6 to 10 while yielding low amounts of oligomers having a polymerization degree of less than 5 can typically be produced at a polymerization temperature between -10 and 1O 0 C. It will generally be beneficial to maintain the polymerization temperature constant during polymerization, e.g. within+/- 5 0 C.
• the reaction time is generally not critical and typically, the polymerization will be conducted for a time sufficient to convert most or all of the HFPO into oligomers.
• reaction time may vary between 10 minutes and 3 hours. In a typical embodiment, the reaction time is between Vz hour and 1 hour.
• the polymerization or oligomerization is typically carried out in a stainless steel vessel.
• the catalyst solution is typically added to the stainless steel vessel, which may then be brought under a vacuum.
• the mixture of HFPO and HFP is typically supplied to the vessel as a gas mixture. Once the feed of this gas mixture is complete, the reaction is generally continued until most or all of the HFPO is converted.
• the following general polymerization procedure was used in each of the examples: A stainless steel pressure vessel equipped with an effective stirrer and a baffle was used. The internal temperature was controlled by a heating-cooling jacket. A thermocouple in the reaction mixture served as reference for automatic temperature control.
• the dry reactor was filled with the catalyst consisting of dry KF and diglyme, inerted with dry nitrogen, and set under vacuum (450 to 500 hPa absolute).
• the mixer was started, the internal temperature was adjusted to the desired temperature, and the HFPO/HFP (1 to 1 by weight) feed was started. After the planned amount of the gas mixture was fed to the reactor, the feed line was closed and the batch was allowed to react at the preset temperature. Gas samples were taken on a regular basis to control the conversion. After conversion of most of the HFPO, the remaining HFP was evaporated.
• the batch was allowed to reach 20°C, the mixer was stopped and the lower phase was separated. A sample of the lower phase was converted to the methyl ester and analyzed by gas chromatography.
• Example 1 The following describes the input and process variables for each example: Example 1

Landscapes

• Chemical & Material Sciences (AREA)
• Health & Medical Sciences (AREA)
• Chemical Kinetics & Catalysis (AREA)
• Medicinal Chemistry (AREA)
• Polymers & Plastics (AREA)
• Organic Chemistry (AREA)
• Polyethers (AREA)
• Low-Molecular Organic Synthesis Reactions Using Catalysts (AREA)
• Epoxy Compounds (AREA)
• Organic Low-Molecular-Weight Compounds And Preparation Thereof (AREA)

Priority Applications (4)

Applications Claiming Priority (2)

Publications (1)

Family

ID=34938863

Family Applications (1)

Country Status (9)

Cited By (2)

Families Citing this family (10)

Citations (4)

Family Cites Families (2)

• 2005
  • 2005-03-02 EP EP05101610A patent/EP1698650A1/en not_active Withdrawn
• 2006
  • 2006-02-28 RU RU2007131789/04A patent/RU2007131789A/ru unknown
  • 2006-02-28 EP EP06736240A patent/EP1858952B1/en not_active Expired - Lifetime
  • 2006-02-28 PL PL06736240T patent/PL1858952T3/pl unknown
  • 2006-02-28 US US11/276,416 patent/US20060199942A1/en not_active Abandoned
  • 2006-02-28 CN CNA200680006740XA patent/CN101133101A/zh active Pending
  • 2006-02-28 WO PCT/US2006/006881 patent/WO2006093885A1/en not_active Ceased
  • 2006-02-28 JP JP2007558106A patent/JP2008531815A/ja not_active Withdrawn
  • 2006-02-28 AT AT06736240T patent/ATE406402T1/de not_active IP Right Cessation
  • 2006-02-28 DE DE602006002496T patent/DE602006002496D1/de not_active Expired - Fee Related

Patent Citations (4)

Also Published As

Similar Documents

Legal Events