WO2006092330A1 - Production de corps moules en materiaux finements divises a base de lignocellulose - Google Patents
Production de corps moules en materiaux finements divises a base de lignocellulose Download PDFInfo
- Publication number
- WO2006092330A1 WO2006092330A1 PCT/EP2006/001979 EP2006001979W WO2006092330A1 WO 2006092330 A1 WO2006092330 A1 WO 2006092330A1 EP 2006001979 W EP2006001979 W EP 2006001979W WO 2006092330 A1 WO2006092330 A1 WO 2006092330A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- finely divided
- lignocellulose
- urea
- urea compound
- aqueous composition
- Prior art date
Abstract
Priority Applications (8)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
US11/817,511 US20080246177A1 (en) | 2005-03-04 | 2006-03-03 | Production of Moulded Bodies From Lignocellulose-Based Fine Particle Materials |
JP2007557441A JP2008531800A (ja) | 2005-03-04 | 2006-03-03 | リグノセルロースをベースとする微粒状材料からなる成形体の製造 |
AU2006219948A AU2006219948A1 (en) | 2005-03-04 | 2006-03-03 | Production of moulded bodies from lignocellulose-based fine particle materials |
CA002599431A CA2599431A1 (fr) | 2005-03-04 | 2006-03-03 | Production de corps moules en materiaux finements divises a base de lignocellulose |
EP06707409A EP1858677A1 (fr) | 2005-03-04 | 2006-03-03 | Production de corps moules en materiaux finements divises a base de lignocellulose |
MX2007010009A MX2007010009A (es) | 2005-03-04 | 2006-03-03 | Preparacion de cuerpos moldeados de materiales de particulas finas a base de lignocelulosa. |
BRPI0608757A BRPI0608757A2 (pt) | 2005-03-04 | 2006-03-03 | uso de uma composição aquosa, processo para a produção de corpos moldados a partir de materiais finamente divididos à base de lignocelulose, corpo moldado, e, material finamente dividido à base de lignocelulose |
NO20074256A NO20074256L (no) | 2005-03-04 | 2007-08-21 | Fremstilling av stopte legemer fra ligocellulosebaserte finpartiklete materialer |
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
DE102005010042.2 | 2005-03-04 | ||
DE102005010042 | 2005-03-04 |
Publications (1)
Publication Number | Publication Date |
---|---|
WO2006092330A1 true WO2006092330A1 (fr) | 2006-09-08 |
Family
ID=36499429
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/EP2006/001979 WO2006092330A1 (fr) | 2005-03-04 | 2006-03-03 | Production de corps moules en materiaux finements divises a base de lignocellulose |
Country Status (14)
Country | Link |
---|---|
US (1) | US20080246177A1 (fr) |
EP (1) | EP1858677A1 (fr) |
JP (1) | JP2008531800A (fr) |
KR (1) | KR20080002805A (fr) |
CN (1) | CN101132892A (fr) |
AR (1) | AR054007A1 (fr) |
AU (1) | AU2006219948A1 (fr) |
BR (1) | BRPI0608757A2 (fr) |
CA (1) | CA2599431A1 (fr) |
MX (1) | MX2007010009A (fr) |
NO (1) | NO20074256L (fr) |
RU (1) | RU2007136554A (fr) |
WO (1) | WO2006092330A1 (fr) |
ZA (1) | ZA200708405B (fr) |
Cited By (5)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
WO2010001988A1 (fr) * | 2008-07-03 | 2010-01-07 | 国立大学法人京都大学 | Composition durcie par application de chaleur/pression à celle-ci |
US7939177B2 (en) | 2005-10-04 | 2011-05-10 | Basf Aktiengesellschaft | Lignocelluosic material which is low in formaldehyde and method for the production thereof |
WO2013026528A1 (fr) * | 2011-08-19 | 2013-02-28 | Rehau Ag + Co | Dispersion aqueuse destinée à traiter des fibres naturelles et procédé de traitement de fibres naturelles |
US8404312B2 (en) | 2006-06-28 | 2013-03-26 | Valspar Sourcing, Inc. | Method and system for edge-coating wood substrates |
DE102013016928A1 (de) * | 2013-10-11 | 2015-04-16 | Gustav Wilms Ohg | Verfahren zur Herstellung von synthetischen Produkten |
Families Citing this family (22)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US20100304126A1 (en) * | 2006-06-28 | 2010-12-02 | Valspar Sourcing, Inc. | Method and system for coating wood substrates using organic coagulants |
DE102007028374B4 (de) * | 2007-06-11 | 2009-04-23 | Ava - Anhaltinische Verfahrens- Und Anlagentechnik Gmbh | Verfahren zur Herstellung eines Holz-Kunststoff-Verbundwerkstoffes |
MX2011000937A (es) * | 2008-07-25 | 2011-03-04 | Basf Se | Productos lignocelulosicos y metodos para formar los mismos. |
US9986863B2 (en) | 2009-02-13 | 2018-06-05 | Koninklijke Philips N.V. | Floor construction with variable grade of resilience |
DE102009023643B4 (de) * | 2009-05-28 | 2016-08-18 | Fraunhofer-Gesellschaft zur Förderung der angewandten Forschung e.V. | Holzwerkstoffprodukt und Verfahren zu dessen Herstellung |
FI20096037A0 (fi) * | 2009-10-08 | 2009-10-08 | Upm Kymmene Wood Oy | Kemikaalien impregnointi puuhun |
JP2013123904A (ja) * | 2011-12-16 | 2013-06-24 | Okura Ind Co Ltd | パーティクルボード |
BR112014007761B1 (pt) * | 2011-12-23 | 2020-09-29 | Basf Se | Material de lignocelulose com um núcleo e duas camadas de cobertura, processo para produzir o mesmo e uso do mesmo |
HUE028569T2 (en) * | 2011-12-23 | 2016-12-28 | Basf Se | Lignocellulose-containing material, process containing lignocellulose fiber and expanded plastic particles in the outer layers of the outer layers |
US11472987B2 (en) * | 2012-06-07 | 2022-10-18 | Johns Manville | Formaldehyde free binder compositions with urea-aldehyde reaction products |
GB2511121B (en) * | 2013-02-26 | 2017-10-04 | Medite Europe Ltd | Process for manufacturing products from acetylated wood fibre |
AT514057B1 (de) * | 2013-05-16 | 2014-10-15 | Mandl Weiss Heike | Textile Fläche aus Schurwolle bzw. Seide und Zirbenholz |
WO2014204386A1 (fr) * | 2013-06-17 | 2014-12-24 | Välinge Innovation AB | Procédé de fabrication d'un panneau à base de bois et panneau à base de bois de ce type |
CN105479573B (zh) * | 2014-10-11 | 2019-03-12 | 彰武县寰宝木业有限公司 | 一种榆木家具板材的制备工艺 |
CN104960041B (zh) * | 2015-05-15 | 2017-03-15 | 福建省石狮市通达电器有限公司 | 一种竹纹外盖的生产工艺 |
DE102015119546A1 (de) * | 2015-11-12 | 2017-05-18 | Flooring Technologies Ltd. | Holzwerkstoffplatte aus einem Holz-Kunststoff-Verbundwerkstoff und Isocyanat, und ein Verfahren zu deren Herstellung |
US20190127653A1 (en) * | 2017-10-29 | 2019-05-02 | Eric James Brender | Shredable and splitable wax accelerant impregnated fire tinder |
US11878549B1 (en) * | 2018-09-17 | 2024-01-23 | John Sooklaris | Substrate for painting, particularly alcohol ink painting |
ES2802898A1 (es) * | 2019-07-17 | 2021-01-21 | Greenpoint Natura S L | Mezcla de fibra natural de cascara de coco particulada y/o madera de balsa particulada para la fabricacion de productos y procedimeinto de obtencion de dicha mezcla |
FI20205037A1 (en) * | 2020-01-15 | 2021-07-16 | Upm Kymmene Corp | Preparation of monoethylene glycol |
WO2023058088A1 (fr) * | 2021-10-04 | 2023-04-13 | 国立大学法人京都大学 | Solution de lignocellulose, article moulé et procédés de production s'y rapportant |
EP4364918A1 (fr) * | 2022-11-07 | 2024-05-08 | SWISS KRONO Tec AG | Procédé de fabrication d'un panneau de particules ainsi que panneau de particules |
Citations (8)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US3440135A (en) * | 1965-12-13 | 1969-04-22 | Kimberly Clark Co | Process for crosslinking cellulosic fibers during gas suspension of fibers |
US3811131A (en) * | 1968-09-24 | 1974-05-21 | Cotton Inc | Durable press process for treating cellulosic material with methylolamides and acetic acid or formic acid vapors |
US4409293A (en) * | 1982-09-10 | 1983-10-11 | Borden, Inc. | Wood composites of low formaldehyde emission |
DE3432135A1 (de) * | 1984-08-31 | 1986-03-13 | Blomberger Holzindustrie B. Hausmann GmbH & Co KG, 4933 Blomberg | Impraegnierte lagenholzplatte |
EP0401538A2 (fr) * | 1989-06-07 | 1990-12-12 | Chisso Corporation | Nappes à base de cellulose, inflammables, volumineuses et méthode pour fabriquer de telles nappes |
US5160679A (en) * | 1989-08-29 | 1992-11-03 | Greene Jack T | Process for making particle board including the use of acetoacetamide as a formaldehyde scavenger |
US5384012A (en) * | 1993-02-12 | 1995-01-24 | James River Corporation Of Virginia | Process for crosslinking of cellulosic fibers |
WO2004033171A1 (fr) * | 2002-10-04 | 2004-04-22 | Basf Aktiengesellschaft | Procede d'amelioration de la durete de la surface d'un corps en bois au moyen d'une solution aqueuse d'un agent d'impregnation |
Family Cites Families (3)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
BE513352A (fr) * | 1951-08-18 | |||
US2930715A (en) * | 1956-10-22 | 1960-03-29 | Ici Ltd | Surface treated rubber articles |
US4396391B2 (en) * | 1982-06-30 | 1993-03-16 | Treating cellulose textile fabrics with dimenthylol dihydroyethyleneuree-polyol |
-
2006
- 2006-03-03 RU RU2007136554/04A patent/RU2007136554A/ru not_active Application Discontinuation
- 2006-03-03 CA CA002599431A patent/CA2599431A1/fr not_active Abandoned
- 2006-03-03 EP EP06707409A patent/EP1858677A1/fr not_active Withdrawn
- 2006-03-03 JP JP2007557441A patent/JP2008531800A/ja not_active Withdrawn
- 2006-03-03 AR ARP060100813A patent/AR054007A1/es not_active Application Discontinuation
- 2006-03-03 KR KR1020077022663A patent/KR20080002805A/ko not_active Application Discontinuation
- 2006-03-03 AU AU2006219948A patent/AU2006219948A1/en not_active Abandoned
- 2006-03-03 BR BRPI0608757A patent/BRPI0608757A2/pt not_active IP Right Cessation
- 2006-03-03 MX MX2007010009A patent/MX2007010009A/es unknown
- 2006-03-03 US US11/817,511 patent/US20080246177A1/en not_active Abandoned
- 2006-03-03 WO PCT/EP2006/001979 patent/WO2006092330A1/fr active Application Filing
- 2006-03-03 CN CNA2006800071617A patent/CN101132892A/zh active Pending
-
2007
- 2007-08-21 NO NO20074256A patent/NO20074256L/no not_active Application Discontinuation
- 2007-10-02 ZA ZA200708405A patent/ZA200708405B/xx unknown
Patent Citations (8)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US3440135A (en) * | 1965-12-13 | 1969-04-22 | Kimberly Clark Co | Process for crosslinking cellulosic fibers during gas suspension of fibers |
US3811131A (en) * | 1968-09-24 | 1974-05-21 | Cotton Inc | Durable press process for treating cellulosic material with methylolamides and acetic acid or formic acid vapors |
US4409293A (en) * | 1982-09-10 | 1983-10-11 | Borden, Inc. | Wood composites of low formaldehyde emission |
DE3432135A1 (de) * | 1984-08-31 | 1986-03-13 | Blomberger Holzindustrie B. Hausmann GmbH & Co KG, 4933 Blomberg | Impraegnierte lagenholzplatte |
EP0401538A2 (fr) * | 1989-06-07 | 1990-12-12 | Chisso Corporation | Nappes à base de cellulose, inflammables, volumineuses et méthode pour fabriquer de telles nappes |
US5160679A (en) * | 1989-08-29 | 1992-11-03 | Greene Jack T | Process for making particle board including the use of acetoacetamide as a formaldehyde scavenger |
US5384012A (en) * | 1993-02-12 | 1995-01-24 | James River Corporation Of Virginia | Process for crosslinking of cellulosic fibers |
WO2004033171A1 (fr) * | 2002-10-04 | 2004-04-22 | Basf Aktiengesellschaft | Procede d'amelioration de la durete de la surface d'un corps en bois au moyen d'une solution aqueuse d'un agent d'impregnation |
Cited By (7)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US7939177B2 (en) | 2005-10-04 | 2011-05-10 | Basf Aktiengesellschaft | Lignocelluosic material which is low in formaldehyde and method for the production thereof |
US8404312B2 (en) | 2006-06-28 | 2013-03-26 | Valspar Sourcing, Inc. | Method and system for edge-coating wood substrates |
WO2010001988A1 (fr) * | 2008-07-03 | 2010-01-07 | 国立大学法人京都大学 | Composition durcie par application de chaleur/pression à celle-ci |
JP5472639B2 (ja) * | 2008-07-03 | 2014-04-16 | 国立大学法人京都大学 | 加熱・加圧により硬化する組成物 |
AU2009266708B2 (en) * | 2008-07-03 | 2014-06-05 | Kyoto University | Composition cured by applying heat/pressure thereto |
WO2013026528A1 (fr) * | 2011-08-19 | 2013-02-28 | Rehau Ag + Co | Dispersion aqueuse destinée à traiter des fibres naturelles et procédé de traitement de fibres naturelles |
DE102013016928A1 (de) * | 2013-10-11 | 2015-04-16 | Gustav Wilms Ohg | Verfahren zur Herstellung von synthetischen Produkten |
Also Published As
Publication number | Publication date |
---|---|
CN101132892A (zh) | 2008-02-27 |
US20080246177A1 (en) | 2008-10-09 |
EP1858677A1 (fr) | 2007-11-28 |
NO20074256L (no) | 2007-10-01 |
BRPI0608757A2 (pt) | 2016-11-08 |
AR054007A1 (es) | 2007-05-30 |
AU2006219948A1 (en) | 2006-09-08 |
KR20080002805A (ko) | 2008-01-04 |
CA2599431A1 (fr) | 2006-09-08 |
RU2007136554A (ru) | 2009-04-10 |
ZA200708405B (en) | 2009-11-25 |
JP2008531800A (ja) | 2008-08-14 |
MX2007010009A (es) | 2007-10-04 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
WO2006092330A1 (fr) | Production de corps moules en materiaux finements divises a base de lignocellulose | |
EP1858678B1 (fr) | Procede de production de materiaux a base de bois | |
DE69509546T2 (de) | Verfahren zur herstellung eines lignocellulosematerials, das zur herstellung eines fertigproduktes geeignet ist | |
DE3438735C2 (fr) | ||
EP1448733B1 (fr) | Liants thermodurcissables | |
Ayrilmis et al. | Flat-pressed wood plastic composite as an alternative to conventional wood-based panels | |
EP1716995B1 (fr) | Produit à base d'acides gras et de dérivés paraffiniques pour la protection des matériaux lignocellulosiques | |
EP2242797B1 (fr) | Liants exempts de formaldéhyde utilisés pour produire des matériaux ligneux | |
US6787590B2 (en) | Composites comprising plant material from Parthenium spp. and plastic | |
EP1877232A1 (fr) | Procede de traitement de surfaces de bois | |
EP3377283B1 (fr) | Plaque en matériau dérivé du bois osb (panneau de lamelles orientées) présentant des caractéristiques améliorées et son procédé de fabrication | |
EP1260530A1 (fr) | Liant thermodurcissable | |
CH542029A (de) | Verfahren zur Verbesserung der Zurückhaltung von Polyalkoholen oder deren Ester- oder Ätherderivaten in Holz, Mittel zur Durchführung dieses Verfahrens und nach diesem Verfahren erhaltenes Holz | |
EP1780243B2 (fr) | Composition de liant pour matériaux à base de bois | |
WO2006117159A1 (fr) | Compositions aqueuses durcissables pour l'impregnation de materiaux lignocellulosiques | |
DE10030254B4 (de) | Holz-Duroplast-Verbunde, Verfahren zu deren Herstellung und deren Verwendung | |
EP3733366B1 (fr) | Liant destiné à la fabrication de matériaux dérivé du bois | |
CA1241900A (fr) | Materiau composite a base de particules de biomasse et methode de fabrication connexe | |
WO2009080748A1 (fr) | Dérivés de glyoxal en tant que liants et agents de réticulation | |
AU736034B2 (en) | Impregnation of a lignocellulosic material | |
WO2007074136A1 (fr) | Procede pour produire des materiaux en contreplaque modifie | |
DE102006019819A1 (de) | Wässrige, härtbare Zusammensetzungen zum Imprägnieren von Lignocellulosematerialien | |
EP3581629A1 (fr) | Résines modifiées à base de formaldéhyde | |
Papadopoulos et al. | Bonding behaviour of chemically modified wood particles for board production | |
FI106300B (fi) | Menetelmä lignoselluloosapohjaisten komposiittituotteiden valmistamiseksi |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
121 | Ep: the epo has been informed by wipo that ep was designated in this application | ||
DPE1 | Request for preliminary examination filed after expiration of 19th month from priority date (pct application filed from 20040101) | ||
WWE | Wipo information: entry into national phase |
Ref document number: MX/a/2007/010009 Country of ref document: MX |
|
WWE | Wipo information: entry into national phase |
Ref document number: 560841 Country of ref document: NZ |
|
WWE | Wipo information: entry into national phase |
Ref document number: 2599431 Country of ref document: CA |
|
WWE | Wipo information: entry into national phase |
Ref document number: 11817511 Country of ref document: US |
|
WWE | Wipo information: entry into national phase |
Ref document number: 2006707409 Country of ref document: EP |
|
WWE | Wipo information: entry into national phase |
Ref document number: 200680007161.7 Country of ref document: CN Ref document number: 3850/CHENP/2007 Country of ref document: IN Ref document number: 2007557441 Country of ref document: JP |
|
NENP | Non-entry into the national phase |
Ref country code: DE |
|
WWE | Wipo information: entry into national phase |
Ref document number: 2006219948 Country of ref document: AU |
|
WWE | Wipo information: entry into national phase |
Ref document number: 1200701905 Country of ref document: VN |
|
ENP | Entry into the national phase |
Ref document number: 2006219948 Country of ref document: AU Date of ref document: 20060303 Kind code of ref document: A |
|
WWE | Wipo information: entry into national phase |
Ref document number: 1020077022663 Country of ref document: KR Ref document number: 2007136554 Country of ref document: RU |
|
WWP | Wipo information: published in national office |
Ref document number: 2006219948 Country of ref document: AU |
|
WWP | Wipo information: published in national office |
Ref document number: 2006707409 Country of ref document: EP |
|
ENP | Entry into the national phase |
Ref document number: PI0608757 Country of ref document: BR Kind code of ref document: A2 Effective date: 20070904 |